US 4,925,512 AGrant
Method for Continuously Manufacturing Products of Thermoplastic Material and Equipment for Carrying Out Said Method
Issue Date:1990-05-15
•17 Claims
•4 Drawing Sheets
Abstract
The method ensures that the core of thermoplastic material of the product is completely enveloped by a continuous covering formed by at least one sheet of a flexible material. Equipment for carrying out the method comprises an extruder 7 for delivering the thermoplastic material in a pasty state and in the form of a rod 16-18 having a regular section, means 20 for unrolling under this rod a sheet 19 of a flexible material, means 34 and 41 for completely enveloping said rod with said flexible material, and means for pulling on said sheet of flexible material and conveying the rod to calendering rolls 43 and 44, and means 46 for forming and means 47 for cutting to the desired length said rod which is thus completely enveloped by said sheet of flexible material. This equipment is applicable to the manufacture of shapes and plates for in particular the packaging and transportation of products.
Metadata
Assignee
- Sonoco Gunther S.A.
Inventor
- Jean P. Briand
Application Information
Application Number:US 1054716
Filing Date:1987-09-30
Priority Date:1982-06-11
Art Unit:131
Classifications
IPC:
B32B 3120B32B 3130
Field of Search:
156425264145;199-202;244.11;244.12;244.18;244.19;244.22;244.27;242;243;277.2;273.7 ;459;465;461;466131.1212;145;148;151;157;160;171;175;176.1;211.12;211.21;212;239;280;284;293;299 ;285;210.2
Patent Drawings (4 sheets)
Description
In order to provide a better explanation of the present invention, there will now be described, merely by way of non-limiting examples, various embodiments of the invention with reference to the accompanying drawings in which:
FIG. 1 is a diagrammatic view of a first embodiment of equipment for carrying out the method of the invention, which embodiment is more particularly provided for manufacturing shapes enveloped in a sheet which is closed onto itself;
FIG. 2 is a diagrammatic view of a second embodiment of equipment for carrying out the method of the invention, which embodiment is more particularly provided for manufacturing plates enveloped by a first lower support and by a second upper support covering the rod, the longitudinally extending edge portions of the second support overlapping those of the first support after calendering;
FIGS. 3a to 3m represent various sections of the shapes and plates which may be made with either of the equipments of FIGS. 1 and 2 by the method according to the invention.
With reference to the drawings, the reference numeral 1 designates a supply hopper associated with a pressure-applying screw 2 which, in rotating at 3 about its vertical axis, drives in rotation fins or blades 4. The hopper 1 is fed with thermoplastic waste products of all kinds, films, packages, milk packages, various paper-making scrap products, which are reduced, above the hopper 1, to a sufficiently fine homogeneous state by means of a soundproof grinder having cutters diagrammatically represented by the rectangle 5.
The material fed into the hopper 1 may also be a virgin thermoplastic material, which may or may not contain a filler or fillers, in the form of textiles, paper, aluminium, wood sawdust or fine and long fibres of glass or fibres of metal.
The outlet of the hopper 1 directly feeds the product to the inlet 6 of an extruder 7 comprising a cylindrical barrel provided with heating resistances 8 and a central extrusion screw 9 driven in rotation as shown at 10 by a set of gears 11 which are driven in rotation as shown at 12 by a main motor 13.
The extruder 7 having a forced feed is associated with a degassing pump 14 driven by a motor 15.
The intimate mixture having a selected particle size comprising the thermoplastic material and its fillers is driven from the inlet to the outlet of the extruder 7 by the screw 9. By the combined action of the source of heat 8, the mixture is brought to a molten state which homogenizes it still further.
Under these conditions, the rod 16 of soft material is delivered at the outlet of the extruder at a temperature in the neigbourhood of 140.degree. C. and at a rate of at least .degree.m per minute. The section of this rod of soft and hot material depends on the shape of the die placed at the outlet of the extruder. This section may be that of a solid cylinder, a square, a relatively flat rectangle, such as 17, or be rounded on its small sides such as at 18.
In the embodiment of the equipment shown in FIG. 1, which is more particularly intended for making shapes of small width, the rod 16 is immediately placed on a sheet 19 of a flexible material, for example paper, cardboard, or cloth, delivered by a reel 20 and if desired subjected to a pre-heating by infrared rays 21 so as to avoid, or at least limit, an excessive cooling of the rod 16.
As it is pulled forwardly by at least one of the rolls 22 of a calender 23, the paper 19 is formed by successive foldings, a first guide 24 raising the edge portions of the sheet, as diagrammatically represented at 25, and a second guide 26 folding the edge portions over onto each other so as to envelop completely and continuously the rod, as diagrammatically represented by the arrows 27.
The rod enveloped in this way is conveyed to a roll of the calender without having been subjected to the least mechanical stress, and consequently with no risk of distortion or tearing. To achieve this, it is quite obvious that the rate at which the protective sheet 19 is drawn along by the roll 22 is equal to the rate of extrusion of the rod 16.
As the distance between the die of the extruder 7 and the calendering line 23 is short and as the rod 16 is not subjected to any specific cooling, said rod enveloped by its protective sheet 19 is taken up by the rolls 22 of the calender while it is at a temperature of the order of 100.degree. to 120.degree. C., i.e. at a temperature suitable to enable it to be worked, compressed and formed.
In any case, the distance between the die of the extruder and the calendering line 23 may be determined, namely lengthened or shortened, in fact as a function of the ideal temperature at which the rod enveloped by its sheet must be presented at the entrance of the first calendering rolls.
When it passes between the rolls of the calender, the sheet 19 itself adheres to the core of thermoplastic material merely by the effect of the pressure exerted by the rolls.
If desired, in order to facilitate the adhesion, one or more of the rolls 22 are subjected to a continuous cooling by water.
As it emerges from the last pair of rolls of the calendering line, the flat composite structure 28 formed by the core of thermoplastic material, which may or may not contain a filler, completely enveloped by its protective sheet, is immediately conveyed to a forming line 29 in which the flat structure is progressively brought to the desired section or shape as diagrammatically represented at 31 and then 32, by passage between a plurality of successive pairs of rolls 30.
The flat composite structure 28 is easily worked, and therefore deformable, between the rolls, since it leaves the calendering line at a high temperature and it enters the forming line at an ideal working temperature which may be between 80.degree. and 100.degree. C.
After the composite structure has been formed into its final section, for example the L-section structure diagrammatically shown at 32, the composite structure is cut by cutters 33 into sections of the desired length.
As a concrete example, to manufacture an L-section element having a thickness of 3 mm and a developed length of 70 mm, which will therefore be folded to produce two flanges at a right angle and having a width of 35 mm each, there is extruded a mixture of 54% high-density polyethylene and 46% paper fibre associated with a minute amount of aluminium waste prodcts which is delivered at the rate of 20 m per minute in the form of a cylindrical rope or rod having a diameter of 8.17 mm.
This rod emerges from the extruder at the temperature of 140.degree. C. and is immediately placed on a sheet of kraft paper 160 mm wide which is pulled by the first pair of rolls of the calender at the rate of 20 m per minute.
After calendering and forming into the shape of an L-section element by the rolls of the forming line, the L-section element weighs 200 g per linear metre.
With the same mixture delivered by the same extruder in the form of a rod of the same diameter at the same temperature of 140.degree. C. and at the rate of 40 m per minute an L-section element can be manufactured which has the same width, half the thickness, 1.5 mm, and weighs 100 g per linear metre.
The two aforementioned L-section elements which are folded in the shape of an L after calendering, were obtained from the same mixture delivered by a conventional extruder whose production rate is 200 kg per hour.
In another manufacture, with again the same mixture achieved in in and delivered by another conventional extruder having a higher production rate of 800 kg per hour, a cylindrical rod having a diameter of 8.17 mm was delivered at the rate of 80 m per minute and had, after calendering, a flat shape 70 mm wide and 3 mm thick and weighing 200 g per linear metre.
At the end of the equipment, this flat strip was, as in the preceding examples, folded and formed into an L-section element of dimensions 35.times.35.times.3 mm.
In other words, the L-section element obtained in the 3rd example has the same technical properties as that obtained in the 1st example but is however produced four times quicker. This therefore shows that the limits of the practice of the invention are those of the production units (extruder) and not those of the materials employed for forming the core and the covering.
By way of example, it is recalled that the same L-section element made directly by extrusion from a V-section die can only emerge from the die at a rate in the neighbourhood of 5 m per minute, the L-section element produced having moreover a finish which is hardly aesthetic and mechanical properties which are distinctly inferior to those of the L-section element formed from the composite structure of the invention.
For example, a flat strip having a length of 380 mm supported only at its two ends is subjected in its middle part to vertical upward pressures (by means of weights) and the deflection of each specimen is measured in hundredths of a millimeter.
Various specimens were tested, the first having been manufactured according to the conventional direct extrusion technique, the others resulting from the carrying out of the invention with varying thicknesses of enveloping paper.
A deflection of 5 mm is reached with a weight of 50 grams for the conventional L-section element, which is consequently uncovered, with a weight of 160 grams for a covering 0.15 mm thick, with a weight of 300 grams for a covering 0.4 mm thick and lastly with a weight of 450 grams for a covering 0.6 mm thick.
The embodiment of the equipment shown in FIG. 2 is for the the manufacture of composite structures whose covering is formed by two sheets which overlap, and said equipment is consequently more particularly for the manufacture of plates of great width.
In this equipment, the units and elements having a reference numeral between 1 and 15 are identical to those of the equipment shown in FIG. 1.
The die of the extruder 7 delivers a hot rope or rod of softened material, either in the form of a cylinder 16 or in a more ovalized form 18, this rod being in any case immediately placed on a first protective support 19 delivered from a reel 20 and if desired pre-heated by infrared rays 21.
This rod-carrying support 19 is subjected to a first forming operation in a device 34 which raises the two edge portions of the sheet 19, as shown at 35, and folds them over at 36 onto the rod 8.
Immediately after, a second support 37 of the same type as the sheet 19 delivered by a reel 38 and if desired pre-heated by infrared rays 39, is applied at 40 on the partly covered rod.
By passing through a second forming device 41, the two sheets 19 and 37 are applied more closely against the rod 18 and are themselves in partly overlapping relation so as to provide the arrangement generally represented by the arrow 42.
The rod protected in this way is shifted to a calendering line 43 in which at least the first pair of rolls 44 pull on at least the lower sheet 19 at a rate equal to the rate of extrusion of the rod.
The pressure or pressures exerted by the rolls 44 render the rod thinner and the rod assumes the more flattened shape generally indicated by the arrow 45 and at the same time the sheets 19 and 37 adhere to the core of thermoplastic material.
It is clear that the width of the sheets 19 and 37 was in this respect determined as a function of the section, and more precisely as a function of the width of the object 45 to be delivered at the exit of the calender.
The width of the sheets 19 and 37 is indeed so chosen that in the final section of the plate 45 the longitudinally extending edge portions are covered with sheets 19 and 37 the edge portions of which overlap each other.
Consequently, the passage through the calender 43 will not result in any flow or seeping of the thermoplastic material since the latter remains constantly trapped between the sheets 19 and 37 which are always in overlapping relation at least partly.
After calendering, the plate may if desired be formed between the rolls of a forming line 46 and then it is cut to length by cutters 47.
In another embodiment, the plate 45 cut to length is then formed in a press device 48.
The shaping of the plate by forming or by pressing is still possible since, as in the equipment shown in FIG. 1, the plate 45 leaves the last pair of rolls of the calender at sufficiently high temperature to be worked and deformed.
All the products, shapes or plates, manufactured in one of the equipments shown in FIGS. 1 or 2 have the common feature of comprising a core of thermoplastic material, which may or may not contain a filler completely and continuously enveloped by one or two sheets of a flexible material which also covers the two longitudinally extending edges of the finished product.
This product therefore has a quite characteristic appearance in that the core of thermoplastic material is absolutely invisible under the protective sheet.
The finished shape may be delivered in the most varied sections, for example in the form of a flat strip 49 (FIG. 3a), an L-section element 50 (FIG. 3b), a U-section element 51 (FIG. 3c), a tube having a rectangular or square section 52 (FIGS. 3d and 3e respectively) the two edges of which remain free or are on the contrary fastened by adhesion or some other technique, a triangular beam 54 (FIG. 3f), a shock-absorbing L-section element 55 whose flanges are slightly formed over toward the centre of the L-section element (FIG. 3g), another shock absorbing L-section element 56, the flanges of which extend to the centre of the web (FIG. 3h), an L-section beam 57 (FIG. 3i), and the modification 58 of said beam with one edge bearing against the web (FIG. 3j), a modification of a beam of rectangular section in which a small side has a double thickness 61 (FIG. 3k).
The finished plate may have raised edge portions 59 (FIG. 3l) or have a crenellated section 60 (FIG. 3m).
The various aforementioned products may be used in different industries, such as those of wrapping, packing (shapes) and handling (plates and pallets for carrying loading crates and packages.)
It must be understood that the scope of the invention is not intended to be limited to the modes of application or to the embodiments mentioned and various modifications may be envisaged without departing from the scope of the invention as defined in the claims.
Claims
I claim:
1. A method for continuously manufacturing products having an inner core of thermoplastic material enveloped and protected by an outer sheet of a flexible material, said method comprising in combination the steps of: heating said thermoplastic material to its softening temperature in a heating means having an outlet for the softened thermoplastic material, supplying an elongated flexible and protective sheet means longitudinally adjacent to said outlet, said sheet having a longitudinally extending intermediate base portion and longitudinally extending lateral portions adjoining opposite sides of said base portion for supporting the thermoplastic material emerging from said outlet in the form of a rod on said base portion of said sheet as said rod emerges from said outlet, raising said longitudinally extending lateral portions of said sheet adjoining opposite sides of said base portion for arresting lateral flow of said softened thermoplastic material of said rod, enclosing said rod within said sheet by wrapping said sheet completely around said rod transversely of said rod and causing each longitudinally extending edge portions of said sheet to overlap each other on top of said rod for preventing escape of said thermoplastic material of said rod, conveying said rod and said sheet to calendering rolls by pulling on said sheet, calendering said rod and said sheet enveloping said rod, and cutting the rod and the sheet enveloping said rod.
2. A method for continuously manufacturing products having a core of thermoplastic material enveloped and protected by sheet means of a flexible material, said method comprising in combination the steps of: heating said thermoplastic material to its softening temperature in heating means having an outlet for the softened thermoplastic material, supplying upper and lower elongated flexible and protective sheets with at least said lower sheet longitudinally adjacent to said outlet, said lower sheet having a longitudinally extending intermediate base portion and longitudinally extending lateral portions adjoining opposite sides of said base portion, supporting the softened thermoplastic material which emerges from said outlet in the form of a rod onto said base portion of said lower sheet as said rod emerges from said outlet, raising said longitudinally extending lateral portions of said lower sheet adjoining opposite sides of said base portion for arresting lateral flow of said softened thermoplastic material of said rod, thereafter completely enveloping said rod with said sheets, with said upper sheet on top of said rod, and wrapping said sheets around said rod transversely of said rod and causing longitudinally extending portions of said sheets to overlap each other on top of and above said rod for preventing escape of said thermoplastic material of said rod, conveying said rod and said sheets to calendering rolls by pulling said lower sheet, calendering said rod and said sheets enveloping said rod, and cutting the rod and the sheets enveloping said rod.
3. A method according to claim 1, wherein said heating means comprises an extruder and said thermoplastic material is heated in the extruder to about 140.degree. C., and said calendering is effected on said rod at a temperature of said rod of about 100.degree. to 120.degree. C.
4. A method according to claim 2, wherein said heating means comprises an extruder and said thermoplastic material is heated in the extruder to about 140.degree. C. and said calendering is effected on said rod at a temperature of said rod of about 100.degree. to 120.degree. C., said overlapping portions overlapping one another to a sufficient extent transversely of said rod before said calendering to remain in overlapping relation to one another throughout the method notwithstanding manufacture of a wide product.
5. A method according to claim 4, further comprising degassing said thermoplastic material in said extruder.
6. A method according to claim 1, wherein the thermoplastic material is softened in an extruder comprising said heating means.
7. A method according to claim 6, wherein the thermoplastic material is extruded at a maximum temperature of about 140.degree. C.
8. A method according to claim 1, wherein the calendering of the enveloped rod is carried out at a temperature of about 100.degree. to 120.degree. C.
9. A method according to claim 1, further comprising imparting a cross-sectional shape to the rod and sheet assembly, after said calendering, said step being carried out at a temperature of about 80.degree. to 100.degree. C.
10. A method according to claim 6, wherein the rod is extruded at a rate of at least 20 m per minute.
11. A method according to claim 1, wherein said sheet means is of a material selected from the group comprising cardboard, cloth, a web of fibreglass, a web of a cardboard-polyethylene complex, and a web of cardboard-aluminium-polyethylene complex.
12. A method according to claim 1, wherein said thermoplastic core includes filler means selected from the group comprising fibres of cloth, paper, cardboard, other cellulosic fibres, fibres of glass, asbestos, wood, powder of talc, kaolin, or silica, aluminium, wood sawdust, and wherein said core is composed of at least 40% of thermoplastic material.
13. A method according to claim 3, wherein said calendering step is followed by a forming operation on said calendered rod and the enveloping sheet at a temperature of about 80.degree. to 100.degree. C. for imparting the cross-sectional shape to said rod and said sheet.
14. Equipment for continuously manufacturing products having a core of thermoplastic material enveloped and protected by sheet means of a flexible material, said equipment comprising in combination: an extruder having an outlet for delivering a thermoplastic material in the shape of a rod, said extruder including heating means for heating said thermoplastic material in said extruder to such temperature that said rod emerges from said outlet in a pasty state; means for supplying sheet means adjacent said outlet for receiving said rod as said rod emerges from said outlet; means for wrapping said sheet means completely around said rod transversely of said rod in such manner that longitudinally extending edge portions of said sheet means overlap each other on said rod; means for pulling on said sheet means at the rate of extrusion of said rod from said extruder; calendering rolls for calendering said rod and said sheet means when said pulling means have conveyed said rod and said sheet means to said calendering rolls; and means for cutting said rod and said sheet.
15. Equipment according to claim 14, wherein said sheet means is a single sheet of elongated shape and said means for supplying the sheet means supply said single sheet under said rod so as to support said rod, and said means for wrapping comprise means for raising lateral portions of said single sheet and folding said raised lateral portions onto the top of said rod in such manner that two edge portions of said sheet overlap each other on top of said rod.
16. Equipment according to claim 14, wherein said sheet means comprise an upper sheet of elongated shape and a lower sheet of elongated shape and said means for supplying the sheet means supplies said lower sheet under said rod to support said rod, and said means for wrapping comprise means for raising lateral portions of said lower sheet and folding said raised lateral portions over the top of said rod and causing edge portions of said upper sheet and said lower sheet to overlap one another on said rod.
17. Equipment according to claim, 14 further comprising forming means following on said calendering rolls for imparting the desired cross-sectional shape to said calendered rod and sheet means.
Patent Citations (16)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2620513 | 1952-12-01 | Cryor | |
| US3136676 | 1964-06-01 | Fisch | |
| US3174887 | 1965-03-01 | Voelkor | |
| US3454694 | 1969-07-01 | Delairie | |
| US3622418 | 1971-11-01 | Black | |
| US3655428 | 1972-04-01 | Geschwender | |
| US4056593 | 1977-11-01 | deNavas Albareda | |
| US4088721 | 1978-05-01 | Apicella, Jr. | |
| US4156752 | 1979-05-01 | Riccitiello | |
| US4234530 | 1980-11-01 | Thiel | |
| US4234536 | 1980-11-01 | Thiel | |
| US4302259 | 1981-11-01 | Steinberg et al. | |
| US4314867 | 1982-02-01 | Berger et al. | |
| US4612152 | 1986-09-01 | Kawabata | |
| FRX2455968 | 1980-12-01 | ||
| FRX2489211 | 1982-03-01 |