US 4,896,044 AGrant
Scanning Tunneling Microscope Nanoetching Method
Issue Date:1990-01-23
•9 Claims
•3 Drawing Sheets
Abstract
A method is described for forming uniform nanometer sized depressions on the surface of a conducting substrate. A tunneling tip is used to apply tunneling current density sufficient to vaporize a localized area of the substrate surface. The resulting depressions or craters in the substrate surface can be formed in information encoding patterns readable with a scanning tunneling microscope.
Metadata
Assignee
- Purdue Research Foundation
Inventors
- Yun-Zhong Li
- Ronald G. Reifenberger
- Ronald P. Andres
Application Information
Application Number:US 3127680
Filing Date:1989-02-17
Priority Date:1989-02-17
Art Unit:256
Classifications
IPC:
H01J 37305
Field of Search:
250346369492.3;492.2158101
Patent Drawings (3 sheets)
Description
Brief Description of the Drawings
FIG. 1 is a graph showing the bias voltage V.sub.t (volts) vs. time (milliseconds) applied across a tunneling tip of a scanning tunneling microscope and a gold substrate;
FIG. 2 is a graph showing response of the tunneling current I.sub.t (nanoamperes) vs. time (milliseconds) applied between a tunneling tip of a scanning tunneling microscope and a gold substrate to an increase in bias voltage as shown in FIG. 1;
FIG. 3 is a graph showing the voltage V.sub.z (volts) applied to a z-piezo element vs. time (milliseconds) throughout the same time as shown in FIG. 1 and FIG. 2;
FIG. 4 is a scanning tunneling microscope image of a gold substrate with craters formed by the application of a transient current (10 indicates a crater 6 nm in diameter);
FIG. 5 is a graph showing the bias voltage V.sub.t (volts) vs. time (milliseconds) applied across a tunneling tip of a scanning tunneling microscope and a gold substrate;
FIG. 6 is a graph showing the saturated response of the tunneling current I.sub.t (nanoamperes) vs. time (millisecons) applied between a tunneling tip of a scanning tunneling microscope and a gold substrate to an increase in bias voltage as shown in FIG. 5;
FIG. 7 is a graph showing the voltage V.sub.z (volts) applied to a z-piezo element vs. time (milliseconds) throughout the same time as shown in FIG. 5 and FIG. 6; and
FIG. 8 is a scanning tunneling microscope image of the gold substrate in FIG. 4 with a hillock 20 (10 nm in diameter) formed by the application of a long term current.
Detailed Description of the Invention
A substrate suitable for the present method of nanoetching by creating topographical depressions is any conducting material that can be made essentially atomically flat. Non-atomically flat materials could be nanoetched by the present method, but there would exist a problem of distinguishing a nanoetched feature from a natural irregularity in the substrate. Because of their atomic scale regularity and high conductivity, metals are a preferred substrate for the method of the present invention. A most preferred substrate for use in this method is gold.
A tunneling tip can be positioned at a desired location over the substrate so that a tunneling current between the tunneling tip and the substrate will exist upon application of a predetermined bias voltage in any convenient manner. Excellent results are obtained if the tunneling tip is an integral part of a scanning tunneling microscope, which can not only precisely position the tunneling tip, but can also be used to image the substrate after nanoetching is completed to verify nanometer scale crater/depression formation in the substrate. Alternative devices such as a scanning tunneling microscope having multiple tips, with at least one tunneling tip suitable for positioning and additional tunneling tips suitable for nanoetching can be used. Another contemplated embodiment for positioning a tunneling tip for use in accordance with this method utilizes an atomic force microscope, such as that disclosed by Binnig in U.S. Pat. No. 4,724,318, incorporated herein by reference, with an attached tunneling tip.
In a preferred embodiment, the tunneling tip is part of a scanning tunneling microscope operated in constant current mode with a tunneling current of 1nA and a substrate bias voltage of 650 mV. The scanning tunneling microscope has a characteristic thermal drift of about 0.2 Angstroms per second and is capable of atomic resolution of carbon atoms in HOP graphite. The piezo elements are separately calibrated by measuring the periodicity of a 3600 line/mm holographic diffraction grating and the lattice constant of HOP graphite The device is operated in air, but the nanoetching according to the method of the present invention is also feasible in a vacuum or in liquids.
The formation of topographic depressions having the form of a crater is initiated by applying a computer controlled voltage pulse such as shown in FIG. 1 between the tunneling tip and a gold substrate at a predetermined point in a scanning tunneling microscope scan. For the gold substrate, step-pulsing the bias voltage to at least about 2.7 volts from an initial bias of 0.65 volts is sufficient to cause a transient increase in the tunneling current such that vaporative removal of substrate material in the region about the tunneling tip occurs. A transient tunneling current of between about 10 nanoamperes and about 100 nanoamperes for less than about 500 microseconds has been found to form reproducible craters in a gold substrate. power densities appropriate for other substrates can be determined empirically.
As shown in FIG. 2, a transient 100 nanoampere current applied for about 200 microseconds forms a crater 10 shown in FIG. 4. Because the constant current feedback loop to the z-piezo element is maintained during application of the bias voltage pulse, the tip initially moves away from the surface and then returns to its original position where the detected tunneling current is equivalent to a predetermined value at the applied bias voltage. FIG. 3 illustrates the adjustments in the voltage applied to the z-piezo element during the formation of the crater shown in FIG. 4. The magnitude of the applied bias voltage, the time over which the bias voltage is increased, the speed and sensitivity of the z-piezo feedback control circuit, and the inertial mass of the scanner assembly factors that can affect substrate etching in accordance with this invention. These parameters can be adjusted to decrease or lengthen the duration and intensity of tunneling current required to form uniform topographic depressions.
The transient increase in tunneling current causes an increase in power density sufficient to evaporate or vaporize a localized area of the substrate surface. A lower limit estimate of the transient current density needed to produce the crater 10 shown in FIG. 4 is about 5.times.10.sup.5 A/cm.sup.2. Such estimate was made by dividing the peak tunneling current by the area of the crater 10. The power applied to the gold substrate is greater than 2.times.10.sup.6 W/cm.sup.2, which results in an intense local heating that explosively evaporates (vaporizes) a portion of the substrate material.
Well defined craters with diameters as small as 1 nanometer can be reproducibly formed using this method. The depth of each crater is about one quarter its diameter, and there is generally no evidence of material about the rim of the crater. The craters produced by this nanoetching technique are stable, and are not filled by surface diffusion of gold atoms over long time periods. Individual craters have been observed for over two hours before drifting out of the field of view of the scanning tunneling microscope. A short (less than 1 millisecond) duration of the tunneling current pulse appears to be critical to crater formation in gold substrates.
Distinct and reproducible craters are not formed if the increase in tunneling current is of longer duration. Long term application (about 2 milliseconds) of a tunneling current greater than 100 na (shown in FIG. 6) between the tunneling tip and the substrate results in the formation of a hillock 20 shown in FIG. 8. Although hillock 20 was formed in response to current increase caused by a stepwise increase in bias voltage shown in FIG. 5, due to unknown interactions with the substrate a long duration current was created, causing local melting instead of explosive evaporation of the substrate. FIG. 7 illustrates the voltage app lied to the z-piezo element during formation of the hillock. III-defined craters and large mounds, of up to 20 nanometer diameter can be formed by a long term tunneling current. An important aspect of this invention is the ability to identify the size and morphology of the created marks by monitoring the tunneling current.
Formation of lines and two dimensional patterns on a nanometer scale is possible using the method of this invention. The patterns formed can be used to either store information or in the fabrication, modification, or repair of devices having nanometer scale features. For example, using a computer generated template for applying discrete voltage pulses while scanning a gold substrate a planck's constant symbol " n" has been formed. The figure was created by applying 201 voltage pulses out of a possible 10,000 which could be distinguishably applied during a scanning tunneling microscope scan. The complete figure is about 65 nanometers high by 40 nanometers wide and is about 2 nanometers deep. A minimum line width of 2 nanometers was achieved.
Lithographic techniques are also possible if the substrate is coated with a covalently bound organic monolayer. Self-assembling monomolecular films comprising C.sub.12 -C.sub.18 carbon chains can be attached, for example, by means of a terminal thiol group to the surface of an atomically smooth gold substrate. Although the monomolecular film may not be sufficiently conductive to be a conducting substrate suitable for application of a substantial tunneling current, a transient increase in tunneling current such as previously described expIosiveIy vaporizes both the gold substrate and any attached organic molecules at a predetermined position.
Claims
We claim:
1. A method for creating topographic depressions on a conducting substrate by localized vaporization of the substrate surface on a nanometer scale comprising the steps of: positioning a tunneling tip over said surface so that a tunneling current is detectable in said tunneling tip upon application of a predetermined bias voltage; and transiently increasing the tunneling current to create a power density sufficient to cause localized evaporation of the substrate surface.
2. The method of claim 1 wherein the conducting substrate is atomically flat gold.
3. The method of claim 2 wherein the atomically flat gold has a surficial monolayer of a covalently bound organic compound.
4. The method of claim 3 wherein the organic compound comprises a C.sub.12 -C.sub.18 carbon chain with a terminal thiol group.
5. The method of claim 1 wherein the tunneling current is transiently increased by application of a stepped bias voltage pulse.
6. A method for electroetching a gold substrate on a nanometer scale utilizing a scanning tunneling microscope Comprising the steps of: positioning a tunneling tip of the scanning tunneling microscope over the surface of the gold substrate so that a tunnelrng current is detected in said tunneling tip upon application of a predetermined voltage bias; and transiently increasing the tunneling current to about 100 nanoamperes for less than about 500 microseconds.
7. The method of claim 6 wherein the tunneling current is transiently increased by application of a stepped bias voltage pulse.
8. A data storage method comprising the steps of: (1) positioning a tunneling tip over a conducting surface so that a tunneling current is detectable in said tunneling tip upon application of a predetermined bias voltage; (2) transiently increasing the tunneling current to create a power density sufficient to cause localized evaporation of the substrate surface; and (3) repeating steps (1) and (2) to create an information encoding pattern in the substrate surface.
9. A lithographic method utilizing localized vaporization of a resist layer on a conducting surface on a nanometer scale comprising the steps of: treating a substrate surface to form a resist layer comprising a covalently bound monomolecular layer of an organic compound; positioning a tunneling tip over a selected area of said resist layer bearing surface so that a tunneling current is detected in said tunneling tip upon application of a predetermined bias voltage; and transiently increasing the tunneling current to create a power density sufficient to cause localized vaporization of the resist layer.
Patent Citations (2)
Non-Patent Literature (6)
- McCord, M. A. and Pease, R. F. W., "Lithography with the Scanning Tunneling Microscope", J. Vac. Sci. Technol. B 4(1), Jan./Feb. 1986.
- Abraham, David W., Mamin, H. Jonathon, Ganz, Eric, and Clarke, John, "Surface Modification with the Scanning Tunneling Microscope", IBM J. Res. Develop., vol. 30, No. 5, Sep., 1986.
- McCord, M. A., and Pease, R. F. W., "Exposure of Calcium Fluoride Resist with the Scanning Tunneling Microscope", J. Vac. Sci. Technol. B 5(1), Jan./Feb., 1987.
- Schneir, J., Sonnenfeld, R., Marti, O., Hansma, P. K., Demuth, J. E., and Hamers, R. J., "Tunneling Microscopy, Lithography, and Surface Diffusion On An Easily Prepared Atomically Flat Gold Surface", J. Appl. Phys. 63, (3), 1 Feb. 1988.
- Schneir, J., Marti, O., Remmers, G., Glaser, D., Sonenfeld, R., Drake, B., Hansma, P. K., and Elings, V., "Scanning Tunneling Microscopy and Atomic Force Microscopy of the Liquid-Solid Inteface", J. Vac. Sci. Technol. A 6(2), Mar./Apr., 1988.
- McCord, M. A., Kern, D. P., and Chang, T. H. P., "Direct Deposition of 10nm Metallic Features with the Scanning Tunneling Microscope", RC 13840 (#62027) 6/22/88.