Multilayer Article of Microporous and Porous Materials

The present invention is directed to multilayer articles comprising microporous material characterized by a matrix consisting essentially of essentially linear ultrahigh molecular weight polyolefin, a very large proportion of finely-divided particulate filler, and a high void content, bonded to substantially porous material.

Accordingly, the invention is a multilayer article comprising at least one layer of porous material bonded to at least one layer of microporous material comprising (a) a matrix consisting essentially of essentially linear ultrahigh molecular weight polyolefin which is essentially linear ultrahigh molecular weight polyethylene having an intrinsic viscosity of at least about 18 deciliters/gram, essentially linear ultrahigh molecular weight polypropylene having an intrinsic viscosity of at least about 6 deciliters/gram, or a mixture thereof, the matrix comprising regions of stretch-induced molecularly oriented ultrahigh molecular weight polyolefin distributed throughout the matrix, (b) finely divided particulate substantially water-insoluble filler, of which at least about 50 percent by weight is siliceous, distributed throughout the matrix, the filler constituting from about 50 percent to about 90 percent by weight of the microporous material, and (c) a network of interconnecting pores communicating throughout the microporous material, the pores constituting more than 80 percent by volume of the microporous material.

The microporous material from which the multilayer articles are made, may be produced by stretching precursor microporous material in at least one stretching direction above the elastic limit, the precursor micrporous material comprising (a) a matrix consisting essentially of essentially linear ultrahigh molecular weight polyolefin which is essentially linear ultrahigh molecular weight polyethylene having an intrinsic viscosity of at least about 18 deciliters/gram, essentially linear ultrahigh molecular weight polypropylene having an intrinsic viscosity of at least about 6 deciliters/gram, or a mixture thereof, (b) finely divided particulate substantially water-insoluble filler, of which at least about 50 percent by weight is siliceous, distributed throughout the matrix, the filler constituting from about 50 percent to about 90 percent by weight of the microporous material, and (c) a network of interconnecting pores communicating throughout the precursor microporous material, the pores constituting from about 35 percent to about 80 percent by volume of the precursor microporous material, to produce stretched microporous material which is dimensionally stable at room temperature and which comprises (d) a matrix consisting essentially of the essentially linear ultrahigh molecular weight polyolefin, the matrix of the stretched microporous material comprising regions of stretch-induced molecularly oriented ultrahigh molecular weight polyolefin distributed throughout the matrix of the stretched microporous material, (e) the filler distributed throughout the matrix of the stretched microporous material, and (f) a network of interconnecting pores communicating throughout the stretched microporous material, the pores of the stretched microporous material constituting more than 80 percent by volume of the stretched microporous material.

It will be appreciated from the above that the stretching both increases the void volume of the material and induces regions of molecular orientation in the ultrahigh molecular weight (UHMW) polyolefin. As is well known in the art, many of the physical properties of molecularly oriented thermoplastic organic polymer, including tensile strength, tensile modulus, Young's modulus, and others, differ considerably from those of the corresponding thermoplastic organic polymer having little or no molecular orientation. Although it is not desired to be bound by any theory, it is believed that the properties of the UHMW polyolefin, the regions of molecular orientation, the high levels of filler loading, and the high degress of porosity cooperate to provide many of the desirable properties characteristic of the microporous material.

The microporous material is non-isotropic, that is, the pore or microvoid shapes and distributions of pore or microvoid sizes are not the same in planes perpendicular to the surface as in planes parallel to the surface.

The thickness across the microporous material may vary widely, but usually it is in the range of from about 0.03 to about 0.4 millimeter. In many cases, it is in the range of from about 0.05 to about 0.3 millimeter. From about 0.07 to about 0.25 millimeter is preferred.

Inasmuch as UHMW polyolefin is not a thermoset polymer having an infinite molecular weight, it is technically classified as a thermoplastic. However, because the molecules are essentially very long chains, UHMW polyolefin, and especially UHMW polyethylene, softens when heated but does not flow as a molten liquid in a normal thermoplastic manner. The very long chains and the peculiar properties they provide to UHMW polyolefin are believed to contribute in large measure to the desirable properties of the microporous material.

As indicated earlier, the intrinsic viscosity of the UHMW polyethylene is at least about 18 deciliters/gram. In many cases the intrinsic viscosity is at least about 19 deciliters/gram. Although there is no particular restriction on the upper limit of the intrinsic viscosity, the intrinsic viscosity is frequently in the range of from about 18 to about 39 deciliters/gram. An intrinsic viscosity in the range of from about 18 to about 32 deciliters/gram is preferred.

Also as indicated earlier the intrinsic viscosity of the UHMW polypropylene is at least about 6 deciliters/gram. In many cases the intrinsic viscosity is at least about 7 deciliters/gram. Although there is no particular restriction on the upper limit of the intrinsic viscosity, the intrinsic viscosity is often in the range of from about 6 to about 18 deciliters/gram. An intrinsic viscosity in the range of from about 7 to about 16 deciliters/gram is preferred.

As used herein and in the claims, intrinsic viscosity is determined by extrapolating to zero concentration the reduced viscosities or the inherent viscosities of several dilute solutions of the UHMW polyolefin where the solvent is freshly distilled decahydronaphthalene to which 0.2 percent by weight, 3,5-di-tert-butyl-4-hydroxyhydrocinnamic acid, neopentanetetrayl ester [CAS Registry No. 6683-19-8] has been added. The reduced viscosities or the inherent viscosities of the UHMW polyolefin are ascertained from relative viscosities obtained at 135.degree. C. using an Ubbelohde No. 1 viscometer in accordance with the general procedures of ASTM D 4020-81, except that several dilute solutions of differing concentration are employed. ASTM D 4020-81 is, in its entirety, incorporated herein by reference.

The nominal molecular weight of UHMW polyethylene is empirically related to the intrinsic viscosity of the polymer according to the equation:

where M is the nominal molecular weight and [.eta.] is the intrinsic viscosity of the UHMW polyethylene expressed in deciliters/gram. Similarly, the nominal molecular weight of UHMW polypropylene is empirically related to the intrinsic viscosity of the polymer according to the equation:

where M is the nominal molecular weight and [.eta.] is the intrinsic viscosity of the UHMW polypropylene expressed in deciliters/gram.

The essentially linear ultrahigh molecular weight polypropylene is most frequently essentially linear ultrahigh molecular weight isotactic polypropylene. Often the degree of isotacticity of such polymer is at least about 95 percent, while preferably it is at least about 98 percent.

Sufficient UHMW polyolefin should be present in the matrix to provide its properties to the microporous material. Other thermoplastic organic polymer may also be present in the matrix so long as its presence does not materially affect the properties of the microporous material in an adverse manner. The amount of the other thermoplastic polymer which may be present depends upon the nature of such polymer. In general, a greater amount of other thermoplastic organic polymer may be used if the molecular structure contains little branching, few long sidechains, and few bulky side groups, than when there is a large amount of branching, many long sidechains, or many bulky side groups. For this reason, the preferred thermoplastic organic polymers which may optionally be present are low density polyethylene, high density polyethylene, poly(tetrafluoroethylene), polypropylene, copolymers of ethylene and propylene, copolymers of ethylene and acrylic acid, and copolymers of ethylene and methacrylic acid. If desired, all or a portion of the carboxyl groups of carboxyl-containing copolymers may be neutralized with sodium, zinc or the like. It is our experience that usually at least about 50 percent UHMW polyolefin, based on the weight of the matrix, will provide the desired properties to the microporous material. Often at least about 70 percent by weight of the matrix is UHMW polyolefin. In many cases the other thermoplastic organic polymer is substantially absent.

The finely divided substantially water-insoluble siliceous filler used in the present invention is particulate. As present in the microporous material, the siliceous filler may be in the form of ultimate particles, aggregates of ultimate particles, or a combination of both. In most cases, at least about 90 percent by weight of the siliceous filler used in preparing the microporous material has gross particle sizes in the range of from about 5 to about 40 micrometers as determined by use of a Model TAII Coulter Counter (Coulter Electronics, Inc.) according to ASTM C 690-80 but modified by stirring the filler for 10 minutes in Isoton II electrolyte (Curtin Matheson Scientific, Inc.) using a four-blade, 4.445 centimeter diameter propeller stirrer. Preferably at least about 90 percent by weight of the siliceous filler has gross particle sizes in the range of from about 10 to about 30 micrometers. It is expected that the sizes of filler agglomerates may be reduced during processing of the ingredients to prepare the microporous material. Accordingly, the distribution of gross particle sizes in the microporous material may be smaller than in the raw siliceous filler itself. ASTM C 690-80 is, in its entirety, incorporated herein by reference.

Examples of suitable siliceous fillers include silica, mica, montmorillonite, kaolinite, asbestos, talc, diatomaceous earth, vermiculite, natural and synthetic zeolites, cement, calcium silicate, aluminum silicate, sodium aluminum silicate, aluminum polysilicate, alumina silica gels, and glass particles. Silica and the clays are the preferred siliceous fillers. Of the silicas, precipitated silica, silica gel, or fumed silica is most often used.

In addition to the siliceous filler, finely divided particulate substantially water-insoluble non-siliceous fillers may also be employed. Examples of such optional non-siliceous fillers include carbon black, charcoal, graphite, titanium oxide, iron oxide, copper oxide, zinc oxide, antimony oxide, zirconia, magnesia, alumina, molybdenum disulfide, zinc sulfide, barium sulfate, strontium sulfate, calcium carbonate, magnesium carbonate, magnesium hydroxide, and finely divided particulate substantially water-insoluble flame retardant filler such as ethylenebis(tetrabromophthalimide), octabromodiphenyl oxide, decabromodiphenyl oxide, and ethylenebisdibromonorbornane dicarboximide.

The finely divided substantially water-insoluble non-siliceous filler used in the present invention is particulate. As present in the microporous material, the non-siliceous filler may be in the form of ultimate particles, aggregates of ultimate particles, or a combination of both. In most cases, at least about 75 percent by weight of the non-siliceous filler used in preparing the microporous material has gross particle sizes in the ranges of from about 0.1 to about 40 micrometers as determined by use of a Micromeretics Sedigraph 5000-D (Micromeretics Instrument Corp.) in accordance with the accompanying operating manual. The preferred ranges vary from filler to filler. For example, it is preferred that at least about 75 percent by weight of antimony oxide particles be in the range of from about 0.1 to about 3 micrometers, whereas it is preferred that at least about 75 percent by weight of barium sulfate particles be in the range of from about 1 to about 25 micrometers. It is expected that the sizes of filler agglomerates may be reduced during processing of the ingredients to prepare the microporous material. Therefore, the distribution of gross particle sizes in the microporous material may be smaller than in the raw non-siliceous filler itself.

The particularly preferred finely divided particulate substantially water-insoluble siliceous filler is precipitated silica. Although both are silicas, it is important to distinguish precipitated silica from silica gel inasmuch as these different materials have different properties. Reference in this regard is made to R. K. Iler, The Chemistry of Silica, John Wiley & Sons, New York (1979), Library of Congress Catalog No. QD 181.S6144, the entire disclosure of which is incorporated herein by reference. Note especially pages 15-29, 172-176, 218-233, 364-365, 462-465, 554-564, and 578-579. Silica gel is usually produced commercially at low pH by acidifying an aqueous solution of a soluble metal silicate, typically sodium silicate, with acid. The acid employed is generally a strong mineral acid such as sulfuric acid or hydrochloric acid although carbon dioxide is sometimes used. Inasmuch as there is essentially no difference in density between the gel phase and the surrounding liquid phase while the viscosity is low, the gel phase does not settle out, that is to say, it does not precipitate. Silica gel, then, may be described as a nonprecipitated, coherent, rigid, three-dimensional network of contiguous particles of colloidal amorphous silica. The state of subdivision ranges from large, solid masses to submicroscopic particles, and the degree of dehydration from almost anhydrous silica to soft gelatinous masses containing on the order of 100 parts of water per part of silica by weight, although the highly hydrated forms are only rarely used in the present invention.

Precipitated silica is usually produced commercially by combining an aqueous solution of a soluble metal silicate, ordinarily alkali metal silicate such as sodium silicate, and an acid so that colloidal particles will grow in weakly alkaline solution and be coagulated by the alkali metal ions of the resulting soluble alkali metal salt. Various acids may be used, including the mineral acids and carbon dioxide. In the absence of a coagulant, silica is not precipitated from solution at any pH. The coagulant used to effect precipitation may be the soluble alkali metal salt produced during formation of the colloidal silica particles, it may be added electrolyte such as a soluble inorganic or organic salt, or it may be a combination of both.

Precipitated silica, then, may be described as precipitated aggregates of ultimate particles of colloidal amorphous silica that have not at any point existed as macroscopic gel during the preparation. The sizes of the aggregates and the degree of hydration may vary widely.

Precipitated silica powders differ from silica gels that have been pulverized in ordinarily having a more open structure, that is, a higher specific pore volume. However, the specific surface area of precipitated silica as measured by the Brunauer, Emmet, Teller (BET) method using nitrogen as the adsorbate, is often lower than that of silica gel.

Many different precipitated silicas may be employed in the present invention, but the preferred precipitated silicas are those obtained by precipitation from an aqueous solution of sodium silicate using a suitable acid such as sulfuric acid, hydrochloric acid, or carbon dioxide. Such precipitated silicas are themselves known and processes for producing them are described in detail in U.S. Pat. No. 2,940,830, and in U.S. Pat No. 4,681,750, the entire disclosures of which are incorporated herein by reference, including especially the processes for making precipitated silicas and the properties of the products.

In the case of the preferred filler, precipitated silica, the average ultimate particle size (irrespective of whether or not the ultimate particles are agglomerated) is less than about 0.1 micrometer as determined by transmission electron microscopy. Often the average ultimate particle size is less than about 0.05 micrometer. Preferably the average ultimate particle size of the precipitated silica is less than about 0.03 micrometer.

The finely divided particulate substantially water-insoluble filler constitutes from about 50 to 90 percent by weight of the microporous material. Frequently such filler constitutes from about 50 to about 85 percent by weight of the microporous material. From about 60 percent to about 80 percent by weight is preferred.

At least about 50 percent by weight of the finely divided particulate substantially water-insoluble filler is finely divided particulate substantially water-insoluble siliceous filler. In many cases at least about 65 percent by weight of the finely divided particulate substantially water-insoluble filler is siliceous. Often at least about 75 percent by weight of the finely divided particulate substantially water-insoluble filler is siliceous. Frequently at least about 85 percent by weight of the finely divided particulate water-insoluble filler is siliceous. In many instances all of the finely divided particulate water-insoluble filler is siliceous.

Minor amounts, usually less than about 5 percent by weight, of other materials used in processing such as lubricant, processing plasticizer, organic extraction liquid, surfactant, water, and the like, may optionally also be present. Yet other materials introduced for particular purposes may optionally be present in the microporous material in small amounts, usually less than about 15 percent by weight. Examples of such materials include antioxidants, ultraviolet light absorbers, dyes, pigments, and the like. The balance of the microporous material, exclusive of filler and any impregnant applied for one or more special purposes is essentially the thermoplastic organic polymer.

On an impregnant-free basis, pores constitute more than 80 percent by volume of the microporous material. In many instances the pores constitute at least about 85 percent by volume of the microporous material. Often the pores constitute from more than 80 percent to about 95 percent by volume of the microporous material. From about 85 percent to about 95 percent by volume is preferred. As used herein and in the claims, the porosity (also known as void volume) of the microporous material, expressed as percent by volume, is determined according to the equation:

where d.sub.1 is the density of the sample which is determined from the sample weight and the sample volume as ascertained from measurements of the sample dimensions and d.sub.2 is the density of the solid portion of the sample which is determined from the sample weight and the volume of the solid portion of the sample. The volume of the solid portion of the sample is determined using a Quantachrome Stereopycnometer (Quantachrome Corp.) in accordance with the accompanying operating manual.

The volume average diameter of the pores of the microporous material is determined by mercury porosimetry using an Autoscan mercury porosimeter (Quantachrome Corp.) in accordance with the accompanying operating manual. The volume average pore radius for a single scan is automatically determined by the porosimeter. In operating the porosimeter, a scan is made in the high pressure range (from about 138 kilopascals absolute to about 227 megapascals absolute). If about 2 percent or less of the total intruded volume occurs at the low end (from about 138 to about 250 kilopascals absolute) of the high pressure range, the volume average pore diameter is taken as twice the volume average pore radius determined by the porosimter. Otherwise, an additional scan is made in the low pressure range (from about 7 to about 165 kilopascals absolute) and the volume average pore diameter is calculated according to the equation: ##EQU1## where d is the volume average pore diameter, v.sub.1 is the total volume of mercury intruded in the high pressure range, v.sub.2 is the total volume of mercury intruded in the low pressure range, r.sub.1 is the volume average pore radius determined from the high pressure scan, r.sub.2 is the volume average pore radius determined from the low pressure scan, w.sub.1 is the weight of the sample subjected to the high pressure scan, and w.sub.2 is the weight of the sample subjected to the low pressure scan. Generally the volume average diameter of the pores is in the range of from about 0.6 to about 50 micrometers. Very often the volume average diameter of the pores is in the range of from about 1 to about 40 micrometers. From about 2 to about 30 micrometers is preferred.

In the course of determining the volume average pore diameter by the above procedure, the maximum pore radius detected is sometimes noted. This is taken from the low pressure range scan if run; otherwise it is taken from the high pressure range scan. The maximum pore diameter is twice the maximum pore radius.

The microporous sheet may be produced by stretching precursor microporous material according to the method described briefly above and in more detail below.

The precursor microporous material may be prodcued according to the general principles and procedures of U.S. Pat. No. 3,351,495, the entire disclosure of which is incorporated herein by reference, including especially the processes for making microporous materials and the properties of the products.

Preferably filler, thermoplastic organic polymer powder, processing plasticizer and minor amounts of lubricant and antioxidant are mixed until a substantially uniform mixture is obtained. The weight ratio of filler to polymer powder employed in forming the mixture is essentially the same as that of the microporous material to be produced. The mixture, together with additional processing plasticizer, is introduced to the heated barrel of a screw extruder. Attached to the extruder is a sheeting die. A continuous sheet formed by the die is forwarded without drawing to a pair of heated calender rolls acting cooperatively to form continuous sheet of lesser thickness than the continuous sheet exiting from the die. The continuous sheet from the calender then passes to a first extraction zone where the processing plasticizer is substantially removed by extraction with an organic liquid which is a good solvent for the processing plasticizer, a poor solvent for the organic polymer, and more volatile than the processing plasticizer. Usually, but not necessarily, both the processing plasticizer and the organic extraction liquid are substantially immiscible with water. The continuous sheet then passes to a second extraction zone where the residual organic extraction liquid is substantially removed by steam and/or water. The continuous sheet is then passed through a forced air dryer for substantial removal of residual water and remaining residual organic extraction liquid. From the dryer the continuous sheet, which is precursor microporous material, is passed to a take-up roll.

The processing plasticizer has little solvating effect on the thermoplastic organic polymer at 60.degree. C., only a moderate solvating effect at elevated temperatures on the order of about 100.degree. C., and a significant solvating effect at elevated temperatures on the order of about 200.degree. C. It is a liquid at room temperature and usually it is processing oil such as paraffinic oil, naphthenic oil, or aromatic oil. Suitable processing oils include those meeting the requirements of ASTM D 2226-82, Types 103 and 104. Preferred are those oils which have a pour point of less than 22.degree. C. according to ASTM D 97-66 (reapproved 1978). Particularly preferred are oils having a pour point of less than 10.degree. C. Examples of suitable oils include Shellflex.RTM. 412 and Shellflex.RTM. 371 oil (Shell Oil Co.) which are solvent refined and hydrotreated oils derived from naphthenic crude. ASTM D 2226-82 and ASTM D 97-66 (reapproved 1978) are, in their entireties, incorporated herein by reference. It is expected that other materials, including the phthalate ester plasticizers such as dibutyl phthalate, bis(2-ethylhexyl) phthalate, diisodecyl phthalate, dicyclohexyl phthalate, butyl benzyl phthalate, and ditridecyl phthalate will function satisfactorily as processing plasticizers.

There are many organic extraction liquids that can be used. Examples of suitable organic extraction liquids include 1,1,2-trichloroethylene, perchloroethylene, 1,2-dichloroethane, 1,1,1-trichloroethane, 1,1,2-trichloroethane, methylene chloride, chloroform, 1,1,2-trichloro-1,2,2-trifluoroethane, isopropyl alcohol, diethyl ether and acetone.

In the above described process for producing precursor microporous material, extrusion and calendering are facilitated when the substantially water-insoluble filler carries much of the processing plasticizer. The capacity of the filler particles to absorb and hold the processing plasticizer is a function of the surface area of the filler. It is therefore preferred that the filler have a high surface area. High surface area fillers are materials of very small particle size, materials having a high degree of porosity or materials exhibiting both characteristics. Usually the surface area of at least the siliceous filler is in the range of from about 20 to about 400 square meters per gram as determined by the Brunauer, Emmett, Teller (BET) method according to ATM C 819-77 using nitrogen as the adsorbate but modified by outgassing the system and the sample for one hour at 130.degree. C. Preferably the surface area is in the range of from about 25 to 350 square meters per gram. ASTM C 819-77 is, in its entirety, incorporated herein by reference. Preferably, but not necessarily, the surface area of any non-siliceous filler used is also in at least one of these ranges.

Inasmuch as it is desirable to essentially retain the filler in the precursor microporous material, it is preferred that the substantially water-insoluble filler be substantially insoluble in the processing plasticizer and substantially insoluble in the organic extraction liquid when precursor microporous material is produced by the above process.

The precursor microporous material comprises finely divided substantially water-insoluble filler of which at least about 50 percent by weight is siliceous, thermoplastic organic polymer which consists essentially of the UHMW polyolefin, and optional materials in essentially the same weight proportions as those discussed above in respect of the stretched sheet. The residual processing plasticizer content is usually less than 5 percent by weight of the precursor microporous sheet and this may be reduced even further by additional extractions using the same or a different organic extraction liquid.

Pores constitute from about 35 to about 80 percent by volume of the precursor microporous material. In many cases the pores constitute from about 60 to about 75 percent by volume of the precursor microporous material. The porosity of the precursor microporous material, expressed as percent by volume, is determined by the same procedure described above in respect of the stretched microporous material. In all cases, the porosity of the microporous material is, unless impregnated after stretching, greater than that of the precursor microporous material.

The volume average diameter of the pores of the precursor microporous material when made by the above-described process, is usually in the range of from about 0.02 to about 0.5 micrometers. Frequently the average diameter of the pores is in the range of from about 0.04 to about 0.3 micrometers. From about 0.05 to about 0.25 micrometers is preferred.

The microporous material may be produced by stretching the precursor microporous material in at least one stretching direction above the elastic limit. Usually the stretch ratio is at least about 1.5. In many cases the stretch ratio is at least about 1.7. Preferably it is at least about 2. Frequently the stretch ratio is in the range of from about 1.5 to about 15. Often the stretch ratio is in the range of from about 1.7 to about 10. Preferably the stretch ratio is in the range of from about 2 to about 6. As used herein, and in the claims, the stretch ratio is determined by the formula:

where S is the stretch ratio, L.sub.1 is the distance between two reference points located on the precursor microporous material and on a line parallel to the stretching direction, and L.sub.2 is the distance between the same two reference points located on the stretched microporous material.

The temperatures at which stretching is accomplished may vary widely. Stretching may be accomplished at about ambient room temperature, but usually elevated temperatures are employed. The intermediate product may be heated by any of a wide variety of techniques prior to, during, and/or after stretching. Examples of these techniques include radiative heating such as that provided by electrically heated or gas fired infrared heaters, convective heating such as that provided by recirculating hot air, and conductive heating such as that provided by contact with heated rolls. The temperatures which are measured for temperature control purposes may vary according to the apparatus used and personal preference. For example, temperature-measuring devices may be placed to ascertain the temperatures of the surfaces of infrared heaters, the interiors of infrared heaters, the air temperatures of points between the infrared heaters and the precursor microporous material, the temperatures of circulating hot air at points within the apparatus, the temperature of hot air entering or leaving the apparatus, the temperatures of the surfaces of rolls used in the stretching process, the temperature of heat transfer fluid entering or leaving such rolls, or film surface temperatures. In general, the temperature or temperatures are controlled such that the precursor microporous material is stretched about evenly so that the variations, if any, in film thickness of the stretched microporous material are within acceptable limits and so that the amount of stretched microporous material outside of those limits is acceptably low. It will be apparent that the temperatures used for control purposes may or may not be close to those of the precursor microporous material itself since they depend upon the nature of the apparatus used, the locations of the temperature-measuring devices, and the identities of the substances or objects whose temperatures are being measured.

In view of the locations of the heating devices and the line speeds usually employed during stretching, gradients of varying temperatures may or may not be present through the thickness of the precursor microporous material. Also because of such line speeds, it is impracticable to measure these temperature gradients. The presence of gradients of varying temperatures, when they occur, makes it unreasonable to refer to a singular film temperature. Accordingly, film surface temperatures, which can be measured, are best used for characterizing the thermal condition of the precursor microporous material. These are ordinarily about the same across the width of the precursor microporous material during stretching although they may be intentionally varied, as for example, to compensate for precursor microporous material having a wedge-shaped cross-section across the sheet. Film surface temperatures along the length of the sheet may be about the same or they may be different during stretching.

The film surface temperatures at which stretching is accomplished may vary widely, but in general they are such that the precursor microporous material is stretched about evenly, as explained above. In most cases, the film surface temperatures during stretching are in the range of form about 20.degree. C. to about 220.degree. C. Often such temperatures are in the range of from about 50.degree. C. to about 200.degree. C. From about 75.degree. C. to about 180.degree. C. is preferred.

Stretching may be accomplished in a single step or a plurality of steps as desired. For example, when the precursor microporous material is to be stretched in a single direction (uniaxial stretching), the stretching may be accomplished by a single stretching step or a sequence of stretching steps until the desired final stretch ratio is attained. Similarly, when the precursor microporous material is to be stretched in two directions (biaxial stretching), the stretching can be conducted by a single biaxial stretching step or a sequence of biaxial stretching steps until the desired final stretch ratios are attained. Biaxial stretching may also be accomplished by a sequence of one of more uniaxial stretching steps in one direction and one or more uniaxial stretching steps in another direction. Biaxial stretching steps where the precursor microporous material is stretched simultaneously in two directions and uniaxial stretching steps may be conducted in sequence in any order. Stretching in more than two directions is within contemplation. It may be seen that the various permutations of steps are quite numerous. Other steps, such as cooling, heating, sintering, annealing, reeling, unreeling, and the like, may optionally be included in the overall process as desired.

Various types of stretching apparatus are well known and may be used to accomplish stretching of the precursor microporous material. Uniaxial stretching is usually accomplished by stretching between two rollers wherein the second or downstream roller rotates at a greater peripheral speed than the first or upstream roller. Uniaxial stretching can also be accomplished on a standard tentering machine. Biaxial stretching may be accomplished by simultaneously stretching in two different directions on a tentering machine. More commonly, however, biaxial stretching is accomplished by first uniaxially stretching between two differentially rotating rollers as described above, followed by either uniaxially stretching in a different direction using a tenter machine or by biaxially stretching using a tenter machine. The most common type of biaxial stretching is where the two stretching directions are approximately at right angles to each other. In most cases where continuous sheet is being stretched, one stretching direction is at least approximately parallel to the long axis of the sheet (machine direction) and the other stretching direction is at least approximately perpendicular to the machine direction and is in the plane of the sheet (transverse direction).

After stretching has been accomplished, the microporous material may optionally be sintered, annealed, heat set and/or otherwise heat treated. During these optional steps, the stretched microporous material is usually held under tension so that it will not markedly shrink at the elevated temperatures employed, although some relaxation amounting to a small fraction of the maximum stretch ratio is frequently permitted.

Following stretching and any heat treatments employed, tension is released from the stretched microporous material after the microporous material has been brought to a temperature at which, except for a small amount of elastic recovery amounting to a small fraction of the stretch ratio, it is essentially dimensionally stable in the absence of tension. Elastic recovery under these conditions usually does not amount to more than about 10 percent of the stretch ratio.

The stretched microporous material may then be further processed as desired. Examples of such further processing steps include reeling, cutting, stacking, treatment to remove residual processing plasticizer or extraction solvent, and fabrication into shapes for various end uses.

Stetching is preferably accomplished after substantial removal of the processing plasticizer as described above. For purposes of this invention, however, the calendered sheet may be stretched in at least one stretching direction followed by substantial removal of the processing plasticizer by extraction and substantial removal of the residual organic extraction liquid. It will be appreciated that as stretching may be accomplished in a single step or a plurality of steps, so likewise extraction of the processing plasticizer may be accomplished in a single step or a plurality of steps and removal of the residual organic extraction liquid may be accomplished in a single step or a plurality of steps. The various combinations of the steps stretching partial stretching, processing plasticizer extraction, partial plasticizer extraction, removal of organic extraction liquid, and partial removal of organic extraction liquid are very numerous, and may be accomplished in any order, provided of course, that a step of processing plasticizer extraction (partial or substantially complete) precedes the first step of residual organic extraction liquid removal (partial or substantially complete). It is expected that varying the orders and numbers of these steps will produce variations in at least some of the physical properties of the stretched microporous product.

The stretched microporous material may be printed with a wide variety of printing inks using a wide variety of printing processes. Both the printing inks and the printing processes are themselves conventional. Printing may be accomplished before assembly of the microporous material into multilayer articles of the present invention or after assembly of such multilayer articles.

There are many advantages in using the microporous material described herein as a printing substrate.

One such advantage is that the substrate need not be pretreated with any of the pretreatments customarily used to improve adhesion between the printing ink and polyolefin substrate such as flame treatment, chlorination, or especially corona discharge treatment which is most commonly employed. This is surprising inasmuch as untreated polyolefins such as polyethylene and polypropylene cannot ordinarily be successfully printed because of a lack of adhesion between the polyolefin printing ink and the polyolefin substrate. The microporous material substrates used in the present invention may be pretreated to further improve ink-substrate adhesion, but commercially satisfactory results can ordinarily be attained without employing such methods.

Another advantage is that the microporous material substrates accept a wide variety of printing inks, including most organic solvent-based inks which are incompatible with water, organic solvent-based inks which are compatible with water, and water-based inks.

Yet another advantage is very rapid drying of most inks to the tack-free state upon printing the microporous material substrates. This advantage is quite important in high speed press runs, in multicolor printing, and in reducing or even eliminating blocking of stacks or coils of the printed substrate.

A further advantage is the sharpness of the printed image that can be attained. This is especially important in graphic arts applications where fine lines, detailed drawings, or halftone images are to be printed. Halftone images printed on the microporous material substrates ordinarily exhibit high degrees of dot resolution.

Ink jet printing, especially when a water-based ink jet printing ink is used, is particularly suitable for printing bar codes on microporous material substrates. The resulting bars are sharp and of high resolution, which are important factors in reducing errors when the codes are read by conventional methods and equipment. The ink dries very rapidly when applied, thereby minimizing loss of bar resolution due to smearing in subsequent handling operations.

Printing processes, printing equipment, and printing inks have been extensively discussed and documented. Examples of reference works that may be consulted include L. M. Larsen, Industrial Printing Ink, Reinhold Publishing Corp., (1962); Kirk-Othmer, Encyclopedia of Chemical Technology, 2d Ed., John Wiley & Sons, Inc., Vol. 11, pages 611-632 (1966) and Vol. 16, pages 494-546 (1968); and R. N. Blair, The Lithographers Manual, The Graphic Arts Technical Foundation, Inc., 7th Ed. (1983).

For a more detailed description of printing on microporous material of the kind employed in the present invention, see application Ser. No. 238,684, filed Aug. 30, 1988, which is a continuation-in-part of application Ser. No. 42,404, filed Apr. 24, 1987, now abandoned, the entire disclosures of which are incorporated herein by reference.

The microporous material is bonded to at least one layer of porous material. Porous materials are those which are generally pervious to gases and which have a large number of pores, passageways, or channels through which matter can pass. These materials are those customarily recognized and employed for their porous properties. Examples of suitable materials include porous thermoplastic polymeric sheet or film, porous thermoset polymeric sheet or film, porous elastomeric sheet or film, and open celled foams. Other examples include fabrics, such as woven fabrics, knitted fabrics, nonwoven fabrics, and scrims. Still other examples include fiber mats, paper, synthetic paper, felt, and the like. Further examples of suitable porous materials include materials which are microporous such as the stretched microporous materials and precursor microporous materials described herein, as well as other materials which are microporous. In the porous materials which are based on fibers, the fibers may be natural, such as wood fibers, cotton fibers, wool fibers, silk fibers, and the like; or they may be any of the artificial fibers such as polyester fibers, polyamide fibers, acrylic fibers, modacrylic fibers, rayon fibers, and the like; or they may be combinations of differing kinds of fibers. The fibers may be staple and/or they may be continuous. Metal fibers, carbon fibers, and glass fibers are within contemplation.

The multilayer article of the present invention may be constructed by bonding at least one layer of microporous material to at least one layer of porous material. The multilayer article may comprise one layer or more than one layer of microporous material and one layer or more than one layer of the porous material. The multilayer article may also optionally be bonded to one or more layers of porous material. For example, the microporous material may be bonded to a scrim which is bonded to a nonwoven fabric. In this case, the microporous material is often also bonded through the open areas of the scrim to the nonwoven fabric. As another example, the microporous material is bonded to a nonwoven fabric, the other side of which is bonded to a scrim. The combinations and permutations of possible layers are quite numerous. Most often, but not always, at least one exterior layer is microporous material.

Bonding may be made by conventional techniques such as for example fusion bonding and adhesive bonding. Examples of fusion bonding include sealing through use of heated rollers, heated bars, heated plates, heated bands, heated wires, flame bonding, radio frequency (RF) sealing, and ultrasonic sealing. Heat sealing is preferred. Solvent bonding may be used where the porous material is soluble in the applied solvent at least to the extent that the surface becomes tacky. After the microporous material has been brought into contact with the tacky surface, the solvent is removed to form a fusion bond.

Many adhesives which are well known may be used to accomplish bonding. Examples of suitable classes of adhesives include thermosetting adhesives, thermoplastic adhesive, adhesives which form the bond by solvent evaporation, adhesives which form the bond by evaporation of liquid nonsolvent, and pressure sensitive adhesives.

Foamable compositions may be foamed in contact with the microporous material to form a bond between the resulting porous foam and the microporous material.

Powder bonding is a technique which is particularly useful for bonding the microporous material to nonwoven webs of staple and/or continuous fibers and to woven or knitted fibers.

The bond may be permanent or peelable, depending upon the bonding technique employed, the adhesive employed, and/or the nature of the porous material used.

The microporous material may be essentially continuously bonded to the porous material, or it may be discontinuously bonded to the porous material. Examples of discontinuous bonds include bonding areas in the form of one or more spots, patches, strips, stripes, open-curved stripes, closed-curved stripes, irregular areas, and the like. When patterns of bonds are involved, they may be random, repetitive, or a combination of both.

The microporous material employed in the present invention is particularly useful for bonding to porous polyolefins such as polyethylene and polypropylene materials by heat sealing in the absence of extrinsic intervening adhesive. The bond obtained is ordinarily quite strong which is surprising inasmuch as the lamination of materials to polyolefins is usually difficult unless special adhesives are used.

The multilayer articles of the present invention have many and varied uses including filters, wipers, gaskets, cushion assemblies, signs, printing substrate, substrates for pen and ink drawings, maps (particularly maritime maps), wall coverings, and breathable fabrics for clothing. They are also useful as or as components of bandages, sanitary napkins, incontinence devices, diapers, and the like. They are also useful as the seams, joints, and seals of breathable packages, breathable wearing apparel and the like.

The invention is further described in conjunction with the following examples which are to be considered illustrative rather than limiting.

The preparation of the above described materials is illustrated by the following descriptive examples. Processing oil was used as the processing plasticizer. Silica, polymer, lubricant and antioxidant in the amount specified in Table I were placed in a high intensity mixer and mixed at high speed for 30 seconds to thoroughly blend the dry ingredients. The processing oil needed to formulate the batch was pumped into the mixer over a period of 2-3 minutes with low speed agitation. After the completion of the processing oil addition a 2 minute low speed mix period was used to distribute the processing oil uniformly throughout the mixture.

The batch was then conveyed to a ribbon blender where usually it was mixed with up to two additional batches of the same composition. Material was fed from the ribbon blender to a twin screw extruder by a variable rate screw feeder. Additional processing oil was added via a metering pump into the feed throat of the extruder. The extruder mixed and melted the formulation and extruded it through a 76.2 centimeter.times.0.3175 centimeter slot die. The extruded sheet was then calendered. A description of one type of calender that may be used may be found in U.S. Pat. No. 4,734,229, the entire disclosure of which is incorporated herein by reference, including the structures of the devices and their modes of operation. Other calenders of different design may alternatively be used; such calenders and their modes of operation are well known in the art. The hot, calendered sheet was then passed around a chill roll to cool the sheet. The rough edges of the cooled calendered sheet were trimmed by rotary knives to the desired width.

The oil filled sheet was conveyed to the extractor unit where it was contacted by both liquid and vaporized 1,1,2-trichloroethylene (TCE). The sheet was transported over a series of rollers in a serpentine fashion to provide multiple, sequential vapor/liquid/vapor contacts. The extraction liquid in the sump was maintained at a temperatue of 65.degree.-88.degree. C. Overflow from the sump of the TCE extractor was returned to a still which recovered the TCE and the processing oil for reuse in the process. The bulk of the TCE was extracted from the sheet by steam as the sheet was passed through a second extractor unit. A description of these types of extractors may be found in U.S. Pat. No. 4,648,417, the entire disclosure of which is incorporated herein by reference, including especially the structures of the devices and their modes of operation. The sheet was dried by radiant heat and convective air flow. The dried sheet was wound on cores to provide roll stock for further processing.

Larger batch mixing equipment was employed than was used for Examples 1-4. Processing oil was used as the processing plasticizer. Silica, polymer, flame retardant concentrate, lubricant, and antioxidant in the amounts specified in Table II were placed in a high intensity mixer and mixed at high speed for 6 minutes. The processing oil needed to formulate the batch was pumped into the mixer over a period of 12-18 minutes with high speed agitation. After completion of the processing oil addition a 6 minute high speed mix period was used to complete the distribution of the processing oil uniformly throughout the mixture.

The batch was then processed according to the general procedures described in respect of Examples 1-4 to form precursor microporous sheets.

The five microporous sheets, as well as the hereinafter described biaxially stretched microporous sheets produced therefrom, were tested for various physical properties. Table III identifies the properties with the methods used for their determination. The various ASTM test methods and Method 502 C, referenced in Table III, are, in their entireties, incorporated herein by reference. The results of physical testing of the five precursor microporous sheets are shown in Table IV.

Property values indicated by MD (machine direction) were obtained on samples whose major axis was oriented along the length of the sheet. TD (transverse direction; cross machine direction) properties were obtained from samples whose major axis was oriented across the sheet.

Portions of the microporous materials produced in Examples 1-3, precursor material taken from a different roll of precursor material produced during the same production run as the precursor material of Example 4, and precursor material produced in Example 5 were unwound from cores and biaxially stretched by first uniaxially stretching in the machine direction using a single stage roll-to-roll machine direction stretching (MDS) unit and then essentially uniaxially stretching in the transverse direction using a moving clip tenter frame as a transverse direction stretching (TDS) unit. One or more preheat rolls were employed with the MDS unit to heat the sheet prior to stretching. In the TDS unit, the sheet was heated by banks of infrared radiant heaters. The Preheat and Stretch I Zones of the TDS unit each contained both upper and lower banks of such heaters. The upper banks were located about 10.16 centimeters above the precursor microporous material while the lower banks were located about 15.24 centimeters below the precursor microporous material. Electrical power to the heaters of each lower bank was controlled by an on-off controller in response to the difference between a set point and the signal provided by a thermocouple mounted in one heater of the bank. Autotransformers were used to adjust electrical power to the heaters of the upper banks. The Stretch II, Stretch III, Sinter I, and Sinter II Zones each contained upper banks of infrared radiant heaters located about 10.16 centimeters above the precursor microporous material. There were no lower banks in these zones. Electrical power to the heaters of each upper bank was controlled as described in respect of the heaters of each lower bank in the Preheat and Stretch I Zones. For a description of a typical TDS unit, see Figure 2 and column 2, lines 43-69, of U.S. Pat. No. 2,823,421, the entire disclosure of which is incorporated herein by reference.

The MDS stretch ratio was varied by controlling the relative peripheral speeds of the feed rolls and the takeoff rolls of the MDS unit. The chain track positions in the tenter frame were set to achieve the desired stretch ratio and then to essentially maintain that stretch ratio during sintering. For each of the Examples 6-27, the settings of one of the first four vertical columns under the heating "Approximate Transverse Stretch Ratio" in Table V were emplyed. The correct column may be ascertained by matching up the TD stretch ratio of the example with the final stretch ratio of the column. For Examples 28 and 29, the settings of the fifth vertical column under the same heading in Table V were used. For Example 30, the settings of the sixth vertical column under the same heading in Table V were employed. For Example 31, the settings of the seventh vertical column under the same heading in Table V were used.

The precursor sheet stock of Examples 1-3, precursor sheet stock taken from a different roll of precursor microporous material produced during the same production run as the precursor microporous material of Example 4, and precursor sheet stock of Example 5 were fed over the preheat roll of the MDS unit which was heated to the temperature indicated in Tables VI-X. The sheet was then stretched to the indicated stretch ratio by maintaining the relative peripheral speeds of the second and first stretch rolls at essentially the same ratio as the stretch ratio. The line speed given in Tables VI-X is the output speed of the MDS unit and the machine direction speed of the TDS unit. The linear feed rate from the roll stock of precursor microporous material to the MDS unit was set at a value given by the line speed divided by the MDS stretch ratio. Thus, with a line speed of 24 m/min and a MDS stretch ratio of 2, the linear feed rate from the roll stock of the MDS unit would be 12 m/min. The properties of several representative examples of biaxially stretched sheets are given in Tables VI-X.

The biaxially stetched microporous sheet of Example 12 was examined by scanning electron microscopy at a magnification of 430X. A section taken in a plane perpendicular to the sheet surface (viz., looking into the thickness) and along the machine direction showed substantial pore elongation. A section taken in a plane perpendicular to the sheet surface and along the transverse direction showed pore elongation which was not as pronounced as along the machined direction. A view of the sheet surface (not sectioned) showed that large void structures were not as numerous as in views of either of the sections looking into the thickness.

The biaxially stretched microporous sheet of Example 20 was examined by scanning electron microscopy at a magnification of 430X. A section taken in a plane perpendicular to the sheet surface and along the transverse direction showed pore elongation which was not as pronounced as that seen in a similar section taken along the machine direction. A view of the sheet surface (not sectioned) showed that large void structures were not as numerous as in views of either of the sections looking into the thickness.

A sample of the microporous material produced in Example 28 was cut into a rectangular sheet measuring about 15.2 centimeters by about 20.3 centimeters. The rectangle was folded in half so that the folded sheet measured about 7.6 centimeters by about 20.3 centimeters. A PAC Model 24PI Impulse Sealer (Packaging Aids Corporation) fitted with top and bottom heater bands 6.35 millimeters wide was used as a heat sealing unit. The surfaces of the heater bands were covered with polytetrafluoroethylene film to prevent sticking. This unit is an impulse sealer which clamps the heater bands around the package opening with full power to the heater bands for 1.5 seconds. The clamping force is then maintained for 9.5 seconds while the heater bands cool to about ambient temperature. The air pressure setting for providing clamping pressure was 413.7 kilopascals. The folded sheet was sealed along the unfolded 20.3 centimeter dimension and along one 7.6 centimeter dimension using the heat sealing unit to provide a pouch that was open at one end. The heat sealed seams were about 7 millimeters wide. No extraneous adhesive was employed in making the seams. About 300 milliliters of water was poured into the pouch to test the integrity of the bottom seam. Since the seam held, the top was sealed using the heat sealing unit to provide a totally enclosed pouch. The pouch retained its integrity for about 21/2 hours before one end seam failed due to tearing within one microporous layer rather than delamination at the interface of the seam. At the time of the failure most of the air had passed out of the pouch through the microporous material and water transport and/or water vapor transport had been established through the microporous material since water had collected on the inside of a plastic bag which had been placed around the pouch in case of failure.

A piece of polyethylene bag stock was folded on itself and cut in the shape of a block letter "L" with the fold being located at the bottom. An aluminum foil strip was placed inside the fold and the superimposed portions of the polyethylene were heat sealed together. With the aluminum foil strip still in place, the resulting assembly was inserted into the failed seam of the pouch with the short arm of the assembly and a portion of the aluminum foil strip extending to the exterior of the pouch. The failed seam with the assembly in place was heat sealed to form a reinforced top seam. Upon cooling the aluminum foil strip was removed to thereby provide a spout for the otherwise sealed pouch. A binder clip was clamped onto the reinforced top seam, and the pouch was suspended via the binder clip over a 160 millimeter by 250 millimeter crystallizing dish. The pouch was slowly filled with approximately 400 milliliters of water. The filled pouch was weighed, hung in a hood and thereafter weighed periodically. The results are shown in Table XI.

There was no evidence of penetration by liquid water during this test.

The pouch was inflated with air via the spout and rate of air flow loss was measured. The results are shown in Table XII.

Two sheets were cut from a sample of the microporous material produced in Example 28. The sheets were superimposed. The electrically heated heat sealing unit of Example 32 was used to heat seal the sheets together along a seam in the outline of a large glove. The glove was completed by trimming away the material outside the seam. The glove could be used as an insert for a structurally stronger glove.

A portion of the microporous material produced in Example 29 was laminated to tissue paper under heat and pressure using Delnet low melting point adhesive. The laminate was subsequently embossed. Portions of the embossed laminate were used as wipers for absorption of various liquids. A unique feature of these wipers is their ability to absorb both oil and water.

The flame retardant microporous material of Example 30 and flame retardant polyester non-woven fabric were laminated together using dry powder bonding equipment commonly employed for producing laminated non-woven fabrics from staple fibers. The equipment comprised an unbailer, a carding machine, a shaker box dry powder applicator, an infrared oven 12.2 meters long, a nip comprising an upper heated roll and the final support roll for the conveyor belt of the oven, and a winder. In addition, provision was made for feeding microporous material under the upper nip roll for lamination to the web exiting from the oven.

Hoechst-Celanese Trivera.RTM. 271 flame retardant polyester staple fiber (1.5 denier; 4.8 centimeters in length) was fed to the unbailer. The unbailed fiber was forwarded to the carding machine which dispensed a staple fiber web about 2 meters wide and weighing about 33.9 grams/sqaure meter onto a conveyor belt operating at a line speed of about 45.7 meters/minute. The conveyor belt carried the web under the shaker box which dispensed Bostik FR 5178 flame retardant, hot melt polyester powder adhesive (Emhart Corp., Bostik Division) onto the web at a net rate of from 20.3 to 21.5 grams/square meter. A second conveyor belt then carried the web through the infrared oven where the web was heated so as to have a surface temperature of from about 166.degree. C. to about 177.degree. C. A roll of microporous material produced under the same conditions and during the same production run as that of Example 30 and having a width of 1.52 meters was unrolled, brought into contact with the upper nip roll located at the exit of the infrared oven, fed under the upper nip roll, and there brought into contact with the web exiting the oven. The upper nip roll was heated to about 99.degree. C. while the temperature of the conveyor belt upon exiting from the oven ranged from about 121.degree. C. to about 132.degree. C. During preheating of the microporous material by contact with the upper nip roll, some shrinkage of the microporous material in the transverse direction was noted. The nip consolidated the microporous material, the heated web, and the heated adhesive. The laminated web from the nip was wound on cores by the winder. As a finishing operation, the laminated web was unwound, trimmed to final widths of from 1.14 to 1.19 meters, and rewound on cores. The properties of the laminate are given in Table XIII.

The process and equipment of Example 35 were utilized to produce a laminate with a non-woven staple fiber weight of about 50.9 grams/square meter. All other settings of Example 35 were retained. The properties of this laminate are given in Table XIII.

The apparatus of Example 35, to which was added additional conveyor belts, a second shaker box, and a second infrared oven, was utilized to produce a three-layer laminate in which the order of the layers was microporous material--scrim--nonwoven web.

A nonwoven web of Trivera.RTM. 271 flame retardant polyester fiber was produced as described in Example 35. At the exit of the infrared oven of Example 35 a 4.times.4 (4 counts per inch, viz., 1.575 counts per centimeter, in both the machine and transverse directions) polyester scrim (Bayex, Inc.) rather than the microporous material was unrolled, brought into contact with the upper nip roll located at the exit of the infrared oven, fed under the upper nip roll, and there brought into contact with the web exiting the oven. The nip consolidated the scrim, the heated web, and the heated adhesive. The scrim-nonwoven web laminate was then passed under a second shaker box dry powder applicator which dispensed additional adhesive onto the laminate. The laminate was carried through a second infrared oven operating under conditions similar to the first infrared oven. A roll of the microporous material produced during the same production run as the micrporous material of Example 31 was unrolled, brought into contact with the upper nip roll located at the exit of the second infrared oven, fed under such upper nip roll, and there brought into contact with the two-layer laminate exiting the second oven. The nip consolidated the microporous material, the heated two-layer laminate, and the heated adhesive. The width of the three-layer laminate exiting the nip was 1.71 meters. The three-layer laminate was further processed as described in Example 35 to give a trimmed width of 1.52 meters.

The weight of the polyester staple fibers and the 4.times.4 scrim in the three-layer laminate was 27.5 grams/square meter. The toal weight of adhesive present was 31.5 grams/square meter. The properties of the three-layer laminate are given in Table XIII.

Although the present invention has been described with reference to specific details of certain embodiments thereof, it is not intended that such details should be regarded as limitations upon the scope of the invention except insofar as they are included in the accompanying claims.