Thermochromic Particle Containing Linear Material
Issue Date:1989-07-25
•6 Claims
•1 Drawing Sheets
Abstract
Thermochromic particle-containing linear material product produced by the process characterized by dipping a core in the form of a monofilament or multifilament into a vinyl chloride resin sol composition having a thermochromic particulate material incorporated therein, the thermochromic particulate material being prepared by enclosing with a high polymer compound an electron-donating chromogenic substance, an electron-accepting substance for the chromogenic substance and a solvent having a boiling point of at least 150.degree. C. and selected from the group consisting of alcohols, amides, esters and azomethines and further covering the resulting product with a different high polymer compound; withdrawing the core from the sol composition; and heating the core to gel the sol composition and cover the core with the gelled composition.
Metadata
Assignee
- Matsui Shikiso Chemical Co., Ltd.
Inventors
- Goro Shimizu
- Masayasu Kamada
- Yoshimi Hayashi
Application Information
Application Number:US 1976087
Filing Date:1988-05-23
Priority Date:1987-02-25
Art Unit:158
Classifications
IPC:
B32B 516
Field of Search:
4281;283;403;379;375;378;380;383;392;394;395;396;406;407;913;402.24
Patent Drawings (1 sheets)
Description
BRIEF DESCRIPTION OF THE DRAWING
FIG. 1 is an enlarged sectional view showing a preferred linear material obtained by the process of the invention and comprising a core of multifilament;
FIG. 2 is an enlarged sectional view showing a linear material comprising a core of multifilament and obtained when the vinyl chloride resin sol composition used has an excessively high viscosity; and
FIG. 3 is an enlarged sectional view showing another preferred linear material obtained by the present process and comprising a core of monofilament.
FIG. 1 shows a linear material 1 having a multifilament core. The component filaments 3 of the multifilament are dispersed in a gel 2 of vinyl chloride resin sol composition, and the core is uniformly covered with the gel 2 as seen in the sectional view. This structure is desirable since the covering has good adhesion to the core. FIG. 3 shows another desirable linear material 1' wherein a monofilament 3' is used as the core. The monofilament core 3' is properly covered with a gel 2' having a uniform thickness.
EXAMPLE 1
To 100 parts of ZEON 101EP (brand name for a resin for vinyl chloride paste, product of Nippon Zeon Co., Ltd.) were added in divided portions 10 parts of DOP, 50 parts of TCP, 3 parts of epoxy plasticizer, 5 parts of tribasic zinc sulfate, 5 parts of dibasic lead phosphite, 10 parts of clay and 0.5 part of high-melting paraffin, and the mixture was fully kneaded in a Banbury mixer to obtain a sol mixture. To the mixture were further added in divided portions 10 parts of CHROMIC COLOR S-45 BLUE (brand name for a thermochromic particulate material, product of Matsui Shikiso Chemical Co., Ltd.) and O-Z-7721 PINK (brand name for a toner pigment, product of Resino Color Kogyo Co., Ltd.), and the mixture was stirred to obtain a pale purple vinyl chloride resin sol composition having a viscosity of about 12,000 cps (as measured by a B-type rotary viscometer at 20.degree. C. at 12 r.p.m.).
Next, the sol composition was placed into the extruder of an electric wire coating apparatus to coat a bare copper wire, 1.0 mm in outside diameter, in known manner to obtain a polyvinyl chloride coated electric wire, 2.8 mm in outside diameter. When usual rated current was passed through the wire, the wire appeared brilliant purple, whereas if an excessive current was passed, heat built up to change the color to pink. When the current value was then lowered, the color returned to the original purple color. The color change was reversible repeatedly. Thus, the wire had the function of detecting an abnormal current. Table 2 shows the properties of the wire determined.
EXAMPLE 2
To 100 parts of ALPHASOL LI (brand name for vinyl chloride plastisol, product of Alpha Kasei Co., Ltd.) were added in divided portions 5 parts of CHROMIC COLOR S-22 PINK (brand name for a thermochromic particulate material, product of Matsui Shikiso Chemical Co., Ltd.) and 1 part of GLOW YELLOW MF2G (brand name for a fluorescent pigment, product of Matsui Shikiso Chemical Co., Ltd.). The mixture was agitated to obtain a pale orange vinyl chloride plastisol having a viscosity of about 6,000 cps (as measured by B-type rotary viscometer at 20.degree. C. at 12 r.p.m.).
Next, an iron wire) 0.5 mm in diameter, was immersed in the sol for coating, then passed through a nozzle, 1.2 mm in orifice size, to remove an excess of the sol and passed through an oven at 180.degree. C. for 2 minutes to gel the coating, whereby a linear material, 1.2 mm in outside diameter was obtained. Although the wire appeared red at a temperature of not lower than about 17.degree. C., the color changed to bright yellow when the wire was heated to a temperature above about 22.degree. C. The color change was reversible repeatedly. Table 2 shows the properties of the linear material determined.
EXAMPLE 3
To 100 parts of P-440 (brand name for a vinyl chloride paste resin, product of Mitsubishi Monsanto Kogyo Co., Ltd.) were added in divided portions 30 parts of plasticizer DOP, 40 parts of TCP, 10 parts of DBP, 3 parts of stabilizer of the organotin laurate type and 1 part of TINUVIN 328 (brand name, a triazole ultraviolet absorber, product of Chiba-Geigy), and the mixture was fully kneaded in a planetary mixer. To the sol mixture obtained was added 10 parts of CHROMIC COLOR S-37 PINK (brand name for a thermochromic particulate material, product of Matsui Shikiso Chemical Co., Ltd.) in small portions. The mixture was thereafter stirred to obtain a pink vinyl chloride resin sol composition having a viscosity of about 6,100 cps (as measured by B-type rotary viscometer at 20.degree. C. at 12 r.p.m.).
The sol composition was placed into a container having a nozzle with an orifice diameter of 0.3 mm, and a nylon monofilament, about 70 denier and serving as a core, was passed through the container, whereby the core was impregnated with the sol composition. The core was then passed through a nozzle with an orifice diameter of 0.3 mm to regulate the fineness and then through an oven at about 200.degree. C. to gel the sol composition, and wound up after cooling. The linear material obtained was about 145 denier in fineness. When microscopically observed, the linear material was found to have a cross section as shown in FIG. 3. The linear material was pink at room temperature, i.e. 20.degree. C., but immediately turned colorless when placed into warm water at 40.degree. C. When removed from the water, the material resumed the original pink color at room temperature (20.degree. C.). This phenomenon was reversible repeatedly. Table 2 shows the properties of the material determined.
EXAMPLE 4
A pink linear material, about 138 denier, was prepared in the same manner as in Example 3 with the exception of using an approximately 70-denier nylon multifilament in place of the approximately 70-denier nylon monofilament. FIG. 1 shows the cross section of the linear material as observed microscopically. The material was superior to the one obtained in Example 3 in the adhesion of the covering to the core. Table 2 shows the properties of the linear material determined.
EXAMPLE 5
A blue vinyl chloride resin composition (about 5,800 cps in viscosity) was prepared in the same manner as in Example 3 except that 0.5 part of a non-thermochromic coloring agent, O-Z-7720 BLUE (brand name for a toner pigment, product of Resino Color Kogyo Co., Ltd.), was used in place of 10 parts of CHROMIC COLOR S-37 PINK. A 140-denier blue liner material was prepared in the same manner as in Example 3 using the composition. Next, using the pink sol composition prepared in Example 1, the blue linear material was treated in the same manner as in Example 1 except that the nozzle orifice diameter was 0.4 mm, whereby an approximately 265-denier pink linear material was obtained. Table 2 shows the properties of this material determined.
EXAMPLE 6
A brown vinyl chloride resin sol composition (about 6,200 cps in viscosity) was prepared by adding a non-thermochromic coloring agent,O-Z-7719 GREEN (brand name for a toner pigment, product of Resino Color Kogyo Co., Ltd.), to the sol composition obtained in Example 3. The coloring agent was used in an amount of 0.4 part per 100 parts of the vinyl chloride paste resin contained in the composition of Example 3. An approximately 4,240-denier brown linear material was prepared in the same manner as in Example 3 with the exception of using an approximately 1,280-denier nylon multifilament in place of the approximately 70-denier nylon monofilament, the above brown sol composition and a nozzle with an orifice diameter of 0.8 mm. Table 2 shows the properties of the linear material determined.
EXAMPLES 7 to 9
A dark brown vinyl chloride resin sol composition was prepared in the same manner as in Example 3 with the exception of using 8 parts of CHROMIC COLOR S-37 GREEN, 10 parts of CHROMIC COLOR S-37 FAST BLACK and 7 parts of CHROMIC COLOR S-37 GOLD in place of 10 parts of CHROMIC COLOR S-37 PINK and further using a non-thermochromic coloring agent-Z-7721PIN, in an amount of 0.5 part. The core used was a 75-denier acrylic multifilament (Example 7), about 75-denier polyester multifilament (Example 8) or about 202-denier glass fiber multifilament (Example 9). Approximately 140-, 143- and 316-denier dark brown linear materials were prepared in Examples 7, 8 and 9, respectively, in the same manner as in Example 3 using the above composition and above-mentioned different cores. Table 2 shows the properties of these materials determined.
EXAMPLE 10
A pink thermochromic linear material, about 60 denier, was prepared in the same manner as in Example 3 with the exception of using a nylon multifilament, 30 denier, as the core in place of the 70-denier nylon monofilament and using a nozzle with an orifice diameter of 0.15 mm. The linear material was cut to a length of 6 mm by a pile cutter to obtain short fiber for flocking. A laminate of polyurethane foam and polyester woven fabric was coated over the surface of the foam with an ink composed of 70 parts of BONCOAT ES-141 (brand name for an acrylic acid ester emulsion, product of Dainippon Ink & Chemicals Inc.), 3 parts of FIXER M-3 (brand name for a water-soluble melamine resin, product of Matsui Shikiso Chemical Co., Ltd.), 3 parts of YODOSOL KA-10 (brand name for an acrylic acid type thickener, product of Kanebo NSC Co., Ltd.) and 1 part of ammonia water, in an amount of 200 g/m.sup.2 using a knife coater. The coating was then electrostatically flocked with the short fiber and then heat-treated at 120.degree. C. for 5 minutes to obtain a thermochromic flocked sheet.
The flocked sheet obtained was pink at room temperature but turned colorless when heated to a temperature of over about 40.degree. C. The color change was reversible repeatedly.
The sheet can be used for making stuffed dolls, toy animals, etc. for infants by stitching. Such a toy may be used in a bathtub to enjoy the color change.
EXAMPLE 11
A scarlet thermochromic linear material, about 40 denier, was prepared in the same manner as in Example 3 with the exception of using a 20-denier nylon multifilament core in place of the 70-denier nylon monofilament, a thermochromic particulate material, CHROMIC COLOR S-32 MAGENTA (product of Matsui Shikiso Chemical Co., Ltd.) in place of CHROMIC COLOR S-37 and a nozzle having an orifice diameter of 0.1 mm. The linear material was cut to a length of about 17 mm by a cutting machine to obtain short fiber for napping. The short fiber was woven into the meshes of a polyester knitted fbric, to which an adhesive comprising an acrylic acid ester emulsion was applied over the rear surface. After drying, the fabric was treated by a raising machine in the known manner to obtain a thermochromic napped sheet. The sheet appeared purplish red at room temperature but turned colorless when heated to a temperature of above about 35.degree. C. The color change was reversible repeatedly.
The sheet can be used for making stuffed dolls, toy animals, etc. or clothes for dolls by stitching. Infants can enjoy the color change by touching these toys.
ADVANTAGE OF THE INVENTION
(1) The liner material of the present invention basically differs from those having an unchangeable color heretofore known and has thermochromic properties. The present material can also be colored with a conventional coloring agent in combination with the color afforded by the invention. These features give the material a remarkably increased commercial value and enhanced usefulness.
(2) A desired color change temperature is available by using various kinds of three components in the desired combination for the thermochromic particulate material for use in the invention. The present material will find very wide application.
(3) The thermochromic particulate material for use in this invention comprises the three components of electron-donating chromogenic substance, electron-accepting substance and solvent which are enclosed with a double film. The film is therefore tough, completely protects the three components enclosed and consequently eliminates the likelihood that the thermochromic function will be impaired or lost owing to the influence of heat, pressure, solvent, etc. although this probelm was encountered with the conventional three-component microcapsules.
(4) When multifilaments are used as cores according to the invention, the covering composition penetrates into the multifilament to cover the component filaments thereof as seen in FIG. 1. The increased covering area assures a tough bond, rendering the covering less susceptible to an external influence such as friction, tension or the like.
(5) The linear materials prepared by the process of the invention are usable for spinning, twisting, kitting, weaving, union cloth, flocking, etc. as required, for a wide variety of articles and products as given below.
Industrial materials: electric wires and cables, fences, protective netting, insect netting, etc.
Garments: sweaters, shirts, blouses, mufflers, gloves, caps, wigs, shoes, etc.
Interior furnishings: curtains, carpets, mats, bedclothes. etc.
Ornaments: artificial flowers, tablecloth, lace, pennants, etc.
Toys: stuffed dolls, doll hair, clothes for dolls, emblems, etc.
Claims
What is claimed is:
1. Thermochromic particle-containing linear material product, produced by the process characterized by applying onto a core in the form of a monofilament or multifilament, a vinyl chloride resin sol composition having a thermochromic particulate material incorporated therein, the thermochromic particulate material being prepared by enclosing with (1) a high polymer compound in the form of a thermosetting resin, an electron-donating chromogenic substance, an electron-accepting substance for the chromogenic substance and a solvent having a boiling point of at least 150.degree. C. and selected from the group consisting of alcohols, amides, esters and azomethines, and further covering the resulting product with (2) a different high polymer compound in the form of a hydrophilic high polymer compound, whereby to provide the particulate material as a double film of an inner thermosetting resin layer and an outer hydrophilic high polymer compound layer encapsulating said electron-donating chromogenic substance, said electron-accepting substance and said solvent, therewithin, and heating the core onto which said sol composition has been applied to gel the sol composition and cover the core with the gelled composition.
2. Product of claim 1, wherein said sol composition is applied by dipping the core into the sol composition, and withdrawing the core from the sol composition, and thereafter heating the core to gel the sol composition and cover the core with the gelled composition.
3. Product of claim 1, wherein the ratio of the core to the vinyl chloride resin sol composition is 70 to 20 parts by weight of the core to 30 to 80 parts by weight of the sol composition, and the vinyl chloride resin sol composition comprises the thermochromic particulate material, a plasticizer, a stabilizer, an auxiliary stabilizer and a gelling agent in a combined amount of 50 to 130 parts by weight per 100 parts by weight of a vinyl chloride resin, the combined amount including 0.5 to 40 parts by weight of the thermochromic particulate material.
4. Product of claim 1, wherein the core is a metal.
5. Product of claim 1, wherein the core is an organic fiber.
6. Product of claim 1, where in the core is an inorganic fiber.
Patent Citations (13)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3560229 | 1971-02-01 | Farnham et al. | |
| US4028118 | 1977-06-01 | Nakasuji et al. | |
| US4046577 | 1977-09-01 | Muzyczko et al. | |
| US4173677 | 1979-11-01 | Nakano et al. | |
| US4374670 | 1983-02-01 | Slocombe | |
| US4421560 | 1983-12-01 | Kito et al. | |
| US4425161 | 1984-01-01 | Shibahashi et al. | |
| US4441508 | 1984-04-01 | Buirley et al. | |
| US4490015 | 1984-12-01 | Kawarada et al. | |
| US4554189 | 1985-11-01 | Marshall | |
| US4554565 | 1985-11-01 | Kito et al. | |
| US4642250 | 1987-02-01 | Spector | |
| US4778244 | 1988-10-01 | Ryan |
Non-Patent Literature (1)
- Abstract of Japanese 58/032,671 (1983), AN-83-33274k/14.