Process for the Production of a Shaped Parts From Pieces of Sheet Metal of Different Thicknesses

The invention will now be described in greater detail with reference to the drawings, wherein:

FIGS. 1 to 4 are side views of welded joint zones of pieces of sheet metal of different thicknesses; and

FIG. 5 is a perspective view of pieces of metal of different thicknesses welded together, with a section shown along line A-B.

Referring to the embodiment illustrated in FIG. 1, surfaces 1,2 of pieces of sheet metal welded together lie in one plane on the welding side. In contrast, in the embodiment illustrated in FIG. 2 the surfaces 5,6 of the two pieces of sheet metal 7,8 lying on the welding side are offset in relation to one another. While in the embodiment illstrated in FIG. 1 welding is performed with a laser beam 9 directed perpendicularly to the surfaces 1,2, in the embodiment illustrated in FIG. 2 the laser beam 10 is directed at an inclination to the surfaces 5,6, one component of the beam direction being directed towards the exposed cut edge 11 of the thicker piece 7 of sheet metal, although the top corner 12 is not acted upon by the laser beam 10. A comparison of the shape and extent of the two welds 13,14 indicates that the weld 14 (embodiment illustrated in FIG. 2) is more favorable, since there is less risk that the toe cracks may occur more particularly in the root zone of the weld.

To prevent a root-side drop-through or root-side suckback at the underside of the joint 14, the joint 14 can be borne at that place on a gas cushion. To this end in the embodiment illustrated in FIG. 2 a cooling element 18 having a duct 21 is placed on the undersides 15,16 of the two pieces 7,8 of sheet metal. The duct 21 is in the zone of the jopint 14 and is filled with inert gas at excess pressure. The inert gas prevents a root-side drop-through on the underside 22 of the joint 14. Of course, it is possible for the joint to be borne on the rear side of the welding side with a suitably adapted cooling element in the embodiment illustrated in FIG. 1 also.

The embodiments illustrated in FIGS. 3 and 4 differ from those illustrated in FIGS. 1 and 2 by the feature that the surfaces 23-26,29-32 of the two pieces 27,28,33,34 of sheet metal are offset in relation to one another; another difference in the embodiment illustrated in FIG. 4 is that the corners at the cut edge of the thicker piece 33 of sheet metal are so chamfered that the height of the end face substantially corresponds to the thickness of the thinner piece 34 of sheet metal. A similar adaption of thickness may be convenient if there are considerable differences in thickness as between the two pieces of sheet metal.

FIG. 5 is a cross-section of a detail of a deep-drawn shaped part which is welded from pieces 37,38 of sheet metal of different thicknesses and in which the joint 39 is located in a portion shaped by deep drawing.