US 4,687,893 AGrant
Method of Soldering a Metal Electrode to an Electrically Conductive Silicone Carbide Ceramic Element
Issue Date:1987-08-18
•5 Claims
•1 Drawing Sheets
Abstract
The invention relates to a method for soldering a metal electrode to an electrically conductive silicon carbide ceramic element and to a silicon carbide ceramic element made in accordance with the method. Silicon is used as the solder which provides a good electrical connection and, as the solder has approximately the same coefficient of expansion as the ceramic element mechanical stress due to temperature changes is minimized.
Metadata
Assignee
- Danfoss A/S
Inventors
- Hilmar O. Rasmussen
- Jorgen H. Petersen
- Ove S. Boe
- Peter J. M. Clausen
Application Information
Application Number:US 9369333
Filing Date:1986-11-28
Priority Date:1984-05-23
Art Unit:214
Classifications
IPC:
H05B 610
Field of Search:
21922843110.41;10.43;9.5;10.57;85 A;85 F;85 H;85 R121;122;123208
Patent Drawings (1 sheets)
Description
A preferred example of the invention will now be described in more detail with reference to the drawing, wherein:
FIG. 1 is a longitudinal section through a silicon carbide ceramic element according to the invention;
FIG. 2 is a partial longitudinal sectio through the ceramic element immediately prior to soldering;
FIG. 3 is a partial section through the soldered zone after the soldering step; and
FIG. 4 is a partial longitudinal section through the soldered zone after the application of the protective sleeve.
FIG. 1 shows a tubular ceramic element 1 of silicon carbide provided at both ends with a respective annular flange 2 and 3 which likewise consists of silicon carbide. The parts 1 to 3 are for example assembled prior to sintering and unified by sintering. They could also be assemblied after sintering and then, with the addition of liquid silicon, made integral to eath other. Such a tube can, especially when incorporating still further ceramic sections, be used as vaporisation burners as explained in prior Application No. P 32 43 397.2.
The annular flange 2 has an axial hole 4 in which a pin-shaped metal electrode 5 is secured. The annular flange 3 contains an axial hole 6 in which a pin-shaped metal electrode 7 is held. The metal electrodes consist of a metal having a coefficient of thermal expansion substantially equal to that of silicon carbide, i.e. for example molybdenum or tungsten. Both metal electrodes carry on the outside a respective protective sleeve 8 or 9 of stainless steel that also serves to secure a lead 10 or 11.
Manufacture takes place as follows. According to FIG. 2, the pin-shaped metal electrode 7 is inserted in the hole 6. At the mouth of the hole, an accumulation 12 of silicon powder or paste is provided around the electrode. A coil 13 with an axial length approximately the same as that of the annular flange 3 is arranged around the annular flange 3. Subsequently, the coil 13 is fed with high frequency current so that the zone of the annular flange is heated to a temperature at which the silicon in the accumlation 12 melts.
The liquid silicon coats the electrode 7 in the region of the accumulation 12 and penetrates into the gap between the electrode 7 and hole 6. The capillary effect can assist this. In this way, one obtains the silicon protective layer 14 which is shown in FIG. 3 and which surrounds the electrode 7 in the entire zone of the hole and somewhat beyond same. The coil current is switched off shortly after the silicon has melted. Since the ceramic element is only partially heated, the soldered zone cools off very quickly so that the silicon solidifies rapidly. Since the silicon will react with the metal of the electrode 7 only in the liquid state, only few harmful metal silicides can be formed.
To ensure that the remaining part of the metal electrode 7 is also protected against corrosion, the protective sleeve 9 of stainless steel is applied and secured, for example, by means of hard solder. It is pushed so far over the electrode 7 that it reaches up to the upper rim of the silicon protective layer 14 or even projects beyond same. In this way, one ensures that the metal electrode 7 will not corrode even under high temperature conditions such as those encountered in a vaporisation burner nor under the influence of oxygen in the air. The protective sleeve 9 has a depression 15 into which a lead 11 can be pushed. Fastening can likewise be effected by means of hard solder.
The soldered joints so produced are suitable not only for heating elements of silicon carbide but also for other applications, for example ignition electrodes or ionisation measuring electrodes.
Claims
We claim:
1. A method of soldering a metal rod electrode to an electrically conductive silicon carbide ceramic heating element, comprising the steps of providing a bore in a silicon carbide flange of a nominal diameter about the same as that of the electrode, mounting the flange on said element, inserting the rod electrode into said bore to have part extend outwardly of the bore, then applying silicon in one of a paste and powder form on the flange in surrounding relationship to the rod electrode in an amount that upon subsequently heating and cooling will fill the gap between the bore and the electrode and will extend somewhat outwardly of the flange, partially heating the flange to melt the silicon so that the silicon penetrates into the gap between the electrode and the bore, and terminating the heating shortly after the silicon melts so that upon cooling the silicon provides a protective layer on the part of the electrode that extends into the bore and somewhat outwardly of the bore, and applying and securing a corrosion resistant protective sleeve on the part of the electrode that extends from the protective layer andoutwardly of the flange, the protective layer outwardly of the flange and the protective sleeve protecting the electrode against corrosion under high temperatures such as in a vaporization burner.
2. A method according to claim 1, characterized in that the protective sleeve is made of stainless steel.
3. A method according to claim 2, characterized in that the protective sleeve is secured to the electrode by hard soldering.
4. A method according to claim 1, characterized in that the heating is by a high frequency current applied by a high frequency coil.
5. A method according to claim 4, characterized in that the axial length of the coil is substantially the same as that of the flange.