US 4,663,095 AGrant
Method of Making a Foamed Insulation Coaxial Cable for Hyperfrequencies Transmissions
Issue Date:1987-05-05
•16 Claims
Abstract
The invention concerns a method for producing a coaxial cable intended for the transmission of very high frequency signals. This coaxial cable comprises a dielectric insulating layer composed of foamed polytetrafluoroethylene or a composition comprising at least 80% of this product named hereinafter COMPOUND. The layer of insulating material is directly obtained by cold extrusion of a COMPOUND powder, the intimate mixing of a pore-forming agent and a foaming agent and a lubricating oil. The mixing of the COMPOUND powder, the pore-forming and foaming agents is effected dry or in aqueous dispersion. Principal application: Fields of use of ultra-high frequencies such as radars and transmissions.
Metadata
Assignee
- Habia Cable SA
Inventor
- Alain Battais
Application Information
Application Number:US 654309&
Filing Date:1984-09-25
Priority Date:1983-09-29
Art Unit:131
Classifications
IPC:
B29C 4702
Field of Search:
15617426442751;244.12110 F;110 FC45.9;46.1119
Patent Drawings
This patent does not have any drawings.
Description
The present invention relates to a coaxial cable intended for the transmission of very high frequency signals.
Signal propagation is ordered by electromagnetic rules which take into account in particular the frequency, the geometric appearance and the characteristics of the substance crossed, and the temperature.
Some transmission and detection systems require, notably for better performances, the use of very high frequency signals of which the attenuation is all the greater as the frequency is high.
Now, if it is considered that it is generally impossible to act on the temperature, it is consequently possible to intervene only on the physical and geometrical characteristics of the substance crossed, the most important of which is the dielectric constant of the insulation substance layer located between the central conductor and the shielding.
Different solutions, intended to decrease the value of the dielectric constant of the insulating substance layer located between the central conductor and the shielding, in order to bring it closer to that of the air (.epsilon.=1), have been considered. These solutions consist, mostly, in using a foamed material, in order to reduce the quantity of the basic insulating material per unit of volume, and to obtain a dielectric constant as near as possible to that of the gas confined in the cells of the foamed material.
Among these solutions, we can mention those described in French Patents:
FR-A-2 214 162, which describes a process for the production of wires and cables insulated with considerably expanded polyolefins. This process consists in mixing a polyolefin, a nucleation agent and a volatile agent in an extruder, with a view to covering, hot, the surface of the central conductor with a considerably expanded polyolefin foam layer (degree of expansion: 60%).
FR-A-2 240 507, which describes a coaxial cable and its process of production, which consists in using a dielectric in expanded ethylene of polypropylene polymer whose coating on the central conductor is made by extrusion with expansion by a swelling agent injected into the composition before extrusion.
Three solutions are at present used industrially in order to obtain an insulating material with low dielectric constant:
Extruded cellular polyethylene, whose dielectric constant is about 1.55, but whose poor temperature behaviour limits its use to a temperate environment. Further, its attenuation limits its use to frequencies lower than 1 GHZ.
Extruded foamed fluoroethylene-propylene (F.E.P.) whose dielectric constant is about 1.4 and service temperature is higher than that of the extruded cellular polyethylene, but whose attention limits its use to frequencies lower than 800 MHz.
Taped polytetrafluoroethylene (P.T.F.E.) whose dielectric constant is about 1.4, which offers characteristics adapted for the transmission of signals whose frequency can reach 10 GHz, but which necesitates a previous shaping and a delicate positioning by wrapping, which at present limit the lengths that can be used.
The coaxial cable of this invention intends to overcome the disadvantages shown by the solutions used at present, by making an insulating layer with a low dielectric constant, obtained in a continuous and homogeneous manner, and employing a conventional cold extrusion process.
The products and the process used make it possible to obtain a coaxial cable whose geometrical, electrical and thermal characteristics are superior to those of all the existing cables without limit due to manufacturing techniques, as is presently the case with the taped process, using production means very close to the conventional means used up to now in this type of manufacture.
This coaxial cable, whose insulating dielectric layer is composed of expanded polytetrafluoroethylene or of a composition comprising at least 80% of this product, named hereinafter COMPOUND, is mainly characterized in that this insulating layer is obtained directly by cold extrusion of a COMPOUND powder, an intimate mixture of a pore-forming agent and a foaming agent and a lubricating oil.
The COMPOUND powder has a granulometry lower than 500 microns, and preferably between 300 and 400 microns.
The pore-forming agent belongs to the aromatic series and may be composed of a compound such as benzene, toluene, naphthalene, benzaldehyde, aniline or one of their mono- or polyhalogenated derivatives or mixtures thereof and whose melting point is preferably comprised between 50.degree. and 100.degree. C. and boiling point is below 300.degree. C. This pore-forming agent is preferably chosen among products which have a tendency to sublimate.
According to the nature of the pore-forming agent, it may be necessary to use a foaming agent.
The foaming agent is activated or non-activated azodicarbonamide, modified azodicarbonamide, 5 phenyl tetrazol and its derivatives, or an aromatic derivative of hydrazines, whose decomposition point is between 200.degree. and 390.degree. C.
The pore-forming agent and the foaming agent have a granulometry lower than 200 microns and preferably between 50 and 100 microns.
The lubricating oil is constituted by a mixture of aliphatic hydrocarbons whose evaporation temperature is lower than the sublimation or the decomposition temperature of the pore-forming and foaming agents.
The proportions used are from 30 to 85% for the COMPOUND, 10 to 50% for the intimate mixture of pore-forming and foaming agents and 5 to 20% for the lubricating oil.
According to a first process, the mixture of the components is made by a dry procedure.
According to a second, preferred process, the mixture is obtained by separate dispersion in a liquid of, on the one hand, the COMPOUND powder, and, on the other hand, the pore-forming and foaming agents. This operation is followed by a mixture of the whole and evaporation of the liquid. The powder obtained is lubricated with lubricating oil with a view to cold extrusion thereof directly around the central conductor. Extrusion is followed by evaporation and sintering.
Other characteristics and advantages will appear from the following description of a coaxial cable made according to the invention in accordance with the aqueous process.
The aqueous dispersion process makes it possible to obtain grains whose dimensions are much lower than those obtained by dry mixing, and to increase the homogeneity and regularity of the insulating layer which presents porosities of the order of one micron.
The principle consists in mixing with the COMPOUND powder, a product which sublimates or decomposes before or during the sintering, and which constitutes an unoccupied space whose volume is equal to or higher than that of the grain used.
Sublimation or decomposition temperature of the foaming agent must be higher than that of the lubricating oil, so that the COMPOUND is already agglomerated during sublimation or decomposition.
The mode of extrusion for the COMPOUND is a conventional one with, however, the necessity of using special equipment.
The sintering, because of the addition of a sublimating or decomposing product, must be made in three different zones, in a special oven in order to obtain successively: evaporation of the oils, sublimation or decomposition of the expansion product, then sintering of the COMPOUND.
The result obtained by using the expanded COMPOUND for making this coaxial cable makes it possible to obtain without major difficulty a dielectric constant 1.3.
The coaxial cable according to the invention is mainly intended for the fields of use of ultra high frequencies such as radar, electronics and transmissions. Its flexibility is an advantage over rigid wave guides.
Claims
I claim:
1. A method for producing a coaxial cable comprising a central conductor and a dielectric insulating layer which comprises preparing polytetrafluoroethylene powder composition in admixture with a pore-forming agent, cold extruding said mixture onto said central conductor so as to form said dielectric insulating layer thereon, said dielectric insulating layer comprising at least about 80% of said polytetrafluoroethylene, and expanding said dielectric insulating layer by sublimation of said pore-forming agent, whereby said dielectric insulating layer has a dielectric constant no greater than about 1.3.
2. The method of claim 1 wherein said polytetrafluoroethylene powder composition is in intimate mixture with said pre-forming agent and a framing agent.
3. The method of claim 2 wherein said polytetrafluoroethylene powder composition includes a lubricating oil.
4. The method of claim 1 wherein said polytetrafluoroethylene powder composition has a granulometry of lower than about 500 microns.
5. The method of claim 4 wherein said polytetrafluoroethylene powder composition has a granulometry of between about 300 and 400 microns.
6. The method of claim 1 wherein said pore-forming agent is selected from the group consisting of benzene, toluene, naphthalene, benzaldehye, aniline or one of the mono- or polyhalogenated derivatives thereof, and mixtures thereof.
7. The method of claim 2 wherein said foaming agent is selected from the group consisting of activated and non-activated azodicarbonamide, modified azodicarbonamide, 5 phenyl tetrazol and its derivatives, the aromatic derivatives of the hydrazines, and mixtures thereof.
8. The method of claim 2 wherein said foaming agent has a decomposition point of between about 200.degree. and 390.degree. C.
9. The method of claim 2 wherein said intimate mixture of said pore-forming agent and said foaming agent has a granulometry of less than about 200 microns.
10. The method of claim 9 wherein said intimate mixture of said pore-forming agent and said foaming agent has a granulometry of between about 50 and 100 microns.
11. The method of claim 3 wherein said lubricating oil has an evaporating temperature which is less than the sublimation temperature or the decomposition temperature of either of said pore-forming agent or said foaming agent.
12. The method of claim 2 wherein said step of preparing said expanded polytetrafluoroethylene comprises dry mixing said polytetrafluoroethylene powder, said pre-forming agent, and said foaming agent.
13. The method of claim 2 wherein said step of preparing said expanded polytetrafluoroethylene composition comprises preparing an acqueous dispersion of said polytetrafluoroethylene powder, said pore-forming agent and said foaming agent.
14. The method of claim 2 wherein said step of preparing said expanded polytetrafluoroethylene composition comprises dispersing said polytetrafluoroethylene powder in a first liquid, dispersing said pore forming agent and said foaming agent in a second liquid, mixing said first and second liquid mixtures, and evaporating said first and second liquids.
15. The method of claim 14 wherein said first and second liquids comprises the same liquid.
16. The method of claim 14 including the steps of lubricating said evaporated mixture by adding a lubricating oil thereto prior to said cold extruding step, and subsequently evaporating and sintering said extruded layer of expanded polytetrafluoroethylene.