US 4,624,273 AGrant
Pigmented Composition
Issue Date:1986-11-25
•21 Claims
•1 Drawing Sheets
Abstract
Cosmetic pencils having cores consisting of water-set mixtures of plaster of paris, mica or other laminar material and pigment or color are disclosed. The mixtures are between 30 wgt % and 75 wgt % plaster of paris. The pencils may be made either by pouring water-based slurries of the mixtures into hollow pencil cases, or by introducing pre-formed cores into two-part cases which are subsequently secured together. The pencils can be easily sharpened and may contain a wide range of additives such as preservatives and bacterioistats.
Metadata
Assignee
- Atlas Pencil Company Limited
Inventor
- Raymond Carr
Application Information
Application Number:US 6709222
Filing Date:1984-11-13
Priority Date:1983-11-11
Art Unit:332
Classifications
IPC:
A45D 4026
Field of Search:
13240188.5;88.749;96
Patent Drawings (1 sheets)
Description
BACKGROUND TO THE INVENTION
1. Field of the Invention
This invention relates to pigmented compositions, for example compositions suitable for forming the core of a cosmetic pencil.
2. Description of Prior Art
A known cosmetic powder pencil core consists of pigment or colouring material, an extender such as a clay for modifying the intensity of the pigment or colouring material, a modifier such as a clay or zinc stearate for modification of the structure or other properties of the core, and a binder comprising a gum or gum-like material.
BRIEF SUMMARY OF THE INVENTION
The present invention provides a composition comprising a pigment or colouring material, plaster of paris (calcium sulphate hemihydrate) and mica or other material having a laminar structure, the composition containing 30 to 75 wgt %, preferably 35 to 70 wgt % and, more preferably, at least 40 wgt % plaster of paris. Most preferably, the composition contains about 45 wgt % plaster of paris.
The amount of laminar material may be as low as 10 wgt % of the composition but is preferably at least 20 wgt % of the composition. The preferred upper limit to the amount of laminar material is 50 wgt % of the composition. The particle size of the laminar material is preferably in the range of from 5 .mu.m to 100 .mu.m and more preferably in the range of from 5 .mu.m to 40 .mu.m.
The composition may also contain additives or modification agents, for example emollients, fillers, extenders, preservatives, bacteriostats and accelerators or retarders for the setting of the plaster of paris component. Preferably, the total amount of additives or modification agents is no more than 5 wgt % of the composition.
Compositions according to the invention may include some calcium sulphate dihydrate or barium sulphate in the dry mix of ingredients, the preferred amount being up to 20 wgt % of the composition.
The pigment or colouring material advantageously comprises an opacifying agent such as titanium dioxide or bismuth oxychloride. The mica or laminar material may conveniently be coated with opacifying agent and/or be pre-mixed with the pigment or colouring material. Alternatively, one or all of the opacifying agent, the pigment or colouring material and the laminar material can be added as separate ingredients to the plaster of paris. The preferred level of pigment or colouring material in the composition is from 5 to 30 wgt % of the composition.
To form the dry composition into a pencil core, a portion of the dry composition is mixed with water, formed into a desired core shape, caused or allowed to set and then dried. Accelerating or retarding agents for plaster of paris may be added to the dry composition or the mixture. Typically, the dry composition is mixed with approximately twice its weight of water.
Instead of introducing the additives or modification agents mentioned above into the dry mix of ingredients, these additives or agents may be first disolved in water to form an aqueous solution in which the other dry ingredients are subsequently disolved.
In one procedure for making a cosmetic pencil, after mixing and before setting, the wet material in the form of a slurry is poured or pumped directly into preformed wooden pencil cases, comprising wooden cylinders each with a longitudinal cylindrical bore. The cases are conveniently held in an upright position with an open end of the bore uppermost. When no accelerator or retardant is used setting may be achieved by allowing the filled case to stand for approximately 20 minutes at room temperature. This period may be lengthened to about 2 hours or shortened to about 3 minutes by use of a suitable retardant or accelerator. The set composition may then be dried at an elevated temperature of, say, 35.degree. to 60.degree. C. for a period of, for example, 24, 48 or 72 hours. Otherwise, drying may be achieved by allowing the filled cases to stand at room temperature for an appropriate time period, or by freeze or vacuum drying. During the drying process water from the mixture evaporates through the tip of the core exposed by the case and also through the wooden case material which is sufficiently porous to allow such evaporation. In the setting process, the calcium sulphate hemihydrate is converted to calcium sulphate dihydrate and the set composition therefore contains a stoichiometric amount of water. Apart from this water of crystallisation, the set compositions will contain little or no water.
In another procedure, the wet composition is moulded and set into rod-shaped pencil cores which are subsequently introduced into a two-part wooden block having a plurality of recesses which are opened longitudinally for introduction of the cores when the block parts are separated. After fitting of the cores to one block part, the two parts are united, the parts secured together and the block cut and shaped into a plurality of pencils. The cores are then allowed to dry.
It has been found that the cores of cosmetic pencils made in accordance with the present invention can have excellent adhesion to their cases.
After drying, the pencils formed by either procedure are sharpened at one end to form and expose a conical tip of the core.
The composition of the invention has the advantages of inexpensiveness and simplicity compared with the known core composition. The finished pencil has an improved appearance compared with known cosmetic pencils and can contain a much wider range of additive materials, for example emollients, preservatives and bacteriostats. The pay-off properties of the pencils are also good.
BRIEF DESCRIPTION OF THE DRAWING
The sole FIGURE of the drawing of this specification shows a cosmetic powder pencil made in accordance with one aspect of the present invention.
DETAILED DESCRIPTION
The pencil comprises a cylindrical wooden pencil case 1 having a longitudinal cylindrical bore 2 into which has been poured or pumped a mixture of a composition according to the invention and water, the mixture having subsequently set to form a core 3 of the pencil. The core is about 12 cm long and about 6.9 mm in diameter. One end of the core 3 has been sharpened into a conical tip 4.
In a modified procedure, the tip 4 can be formed integrally with the remainder of the core 3 by moulding.
In a further modification, two pencils are formed simultaneously in a case of twice the length shown in the drawings which is subsequently cut into two equal-length parts.
Examples will now be given of compositions according to the invention:
EXAMPLE 1
Composition for Dark Blue Cosmetic Pencil
EXAMPLE 2
Composition for Light Blue Cosmetic Pencil
EXAMPLE 3
Composition for Green Cosmetic Pencil
In each Example, the ingredients listed above were thoroughly mixed together and then mixed with approximately twice their weight of water. The wet mixture could then be used in the manufacture of cosmetic pencils in a manner described hereinbefore.
For use in Examples 4 to 42 which follow, the following aqueous bacteriocide and fungicide solution was prepared;
2 parts by volume of a 1% sodium dehydroacetate solution in deionised water
4 parts by volume of 1% Germall 115 solution in deionised water
29 parts by volume of deionised water
Dry mixtures as specified in Examples 4 to 35 were then made up and 200 g portions of the mixtures were mixed with the volumes of the bacteriocide and fungicide solution stated in the individual examples. The mixtures were stirred gently to avoid aeration, sieved and then injected by means of an injection gun into empty wooden pencil cases in the form of hollow cylinders of 6.90 mm internal diameter and mm in length. The total time from mixing to injection did not exceed 12 minutes. Within 12 minutes of injection the pencils cores had solidified. The pencils were then transferred to a drying oven for a period of between 48 and 72 hours. After drying, one end of each pencil was sharpened with a pencil-sharpener to produce a finished make-up pencil.
In the following examples the figures in parentheses after certain pigments or colouring materials indicate that those materials contain mica in the indicated amounts by weight.
EXAMPLE 4
Composition for Highlighter Pencil
200 g of the mixture was mixed with 275 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 5
Composition for Golden Bronze Pencil
200 g of the mixture was mixed with 290 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 6
Composition for Green Pencil
200 g of the mixture was mixed with 225 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 7
Composition for Silver Grey Pencil
200 g of the mixture was mixed with 350 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 8
Composition for Blue Pencil
200 g of the mixture was mixed with cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 9
Composition for Dusty Pink Pencil
200 g of the mixture was mixed with 300 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 10
Composition for Green Pencil
200 g of the mixture was mixed with 250 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 11
Composition for Mulberry Pencil
200 g of the mixture was mixed with 280 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 12
Composition for Blue Pencil
200 g of the mixture was mixed with 270 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 13
Composition for Punk Pink Pencil
200 g of the mixture was mixed with 250 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 14
Composition for Silver Grey Pencil
200 g of the mixture was mixed with 350 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 15
Composition for Gold Pencil
200 g of the mixture was mixed with 300 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 16
Composition for Antique Bronze Pencil
200 g of the mixture was mixed with 270 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 17
Composition for Highlighter Pencil
200 g of the mixture was mixed with 360 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 18
Composition for Blue Highlighter Pencil
200 g of the mixture was mixed with 250 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 19
Composition for Apple Cordial Pencil
200 g of the mixture was mixed with 250 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 20
Composition for Sapphire Pencil
200 g of the mixture was mixed with 250 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 21
Composition for Sky Blue Pencil
EXAMPLE 22
Composition for Blue Mist Pencil
200 g of the mixture was mixed with 230 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 23
Composition for Jade Pencil
200 g of the mixture was mixed with 300 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 24
Composition for Mocca Pencil
200 g of the mixture was mixed with 340 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 25
Composition for Khaki Pencil
200 g of the mixture was mixed with 295 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 26
Composition for Baby Blue Pencil
200 g of the mixture was mixed with 300 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 27
Composition for Lilac Mist Pencil
200 g of the mixture was mixed with 330 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 28
Composition for Nearly Pink Pencil
200 g of the mixture was mixed with 320 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 29
Composition for Apricot Frost Pencil
200 g of the mixture was mixed with 330 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 30
Composition for Brick Red Pencil
200 g of the mixture was mixed with 270 cm.sup.3 bacteriocide and fungicide solution.
EXAMPLE 31
Composition for Stormy Black/Blue Pencil
100 g of the mixture was mixed with 290 cm.sup.3 bacteriocide and fungicide solution.
EXAMPLE 32
Composition for Twilight Pencil
200 g of the mixture was mixed with 300 cm.sup.3 bacteriocide and fungicide solution.
EXAMPLE 33
Composition for Earth Glow Pencil
200 g of the mixtures was mixed with 300 cm.sup.3 bacteriocide and fungicide solution.
EXAMPLE 34
Composition for Sunset Pencil
200 g of the mixture was mixed with 250 cm.sup.3 bacteriocide and fungicide solution.
EXAMPLE 35
Composition for Peacock Pencil
200 g of the mixture was mixed with 240 cm.sup.3 bacteriocide and fungicide solution.
EXAMPLE 36
Composition for Silver Pencil
200 g of the mixture was mixed with 450 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 37
Composition for Silver Pencil
200 g of the mixture was mixed with 475 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 38
Composition for Silver Pencil
200 g of the mixture was mixed with 400 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 39
Composition for Silver Pencil
200 g of the mixture was mixed with 325 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 40
Composition for Silver Pencil
200 g of the mixture was mixed with 300 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 41
Composition for Silver Pencil
200 g of the mixture was mixed with 300 cm.sup.3 of bacteriocide and fungicide solution.
EXAMPLE 42
Composition for Silver Pencil
200 g of the mixture was mixed with 275 cm.sup.3 of bacteriocide and fungicide solution.
Claims
I claim:
1. A pigmented or coloured composition which when mixed with water forms a set product adapted to be transferred to the skin as a cosmetic, the composition comprising a pigment or colouring material, plaster of paris and a material having a laminar structure, the composition containing from about 30 to about 75 wgt % plaster of paris.
2. The composition of claim 1, containing from about 35 to about 70 wgt % plaster of paris.
3. The composition of claim 1, containing from about 40 to about 70 wgt % plaster of paris.
4. The composition of claim 1, containing about 45 wgt % plaster of paris.
5. The composition of claim 1, containing at least about 10 wgt % material having a laminar structure.
6. The composition of claim 1, containing at least about 20 wgt % material having a laminar structure.
7. The composition of claim 1, containing no more than about 50 wgt % material having a laminar structure.
8. The composition of claim 1, wherein said material having a laminar structure is mica.
9. The composition of claim 1, wherein the particle size of said laminated material is in the range of from about 5 .mu.m to about 10 .mu.m.
10. The composition of claim 1, wherein the particle size of said laminar material is in the range of from about 5 .mu.m to about 40 .mu.m.
11. The composition of claim 1, containing from about 5 to about 30 wgt % pigment or colouring material.
12. The composition of claim 1, further comprising up to about 20 wgt % calcium sulphate dihydrate and/or barium sulphate.
13. The composition of claim 1, further comprising at least one additive material selected from emollients, fillers, extenders, preservatives, bacterioistats and accelerating and retarding agents for setting of plaster of paris.
14. The composition of claim 13, wherein the total amount of said additive material is less than about 5 wgt % of the composition.
15. The composition of claim 1, wherein said pigment or colouring material comprises an opacifying agent.
16. The composition of claim 15, wherein said material having a laminar structure is pre-coated with said opacifying agent before combination with the remainder of the composition.
17. The set product of a mixture of water and a composition according to claim 1.
18. A cosmetic pencil having a core comprising a set product as claimed in claim 17.
19. A method of making a cosmetic pencil, comprising the steps of forming a mixture of water and a pigmented composition as claimed in claim 1 into a pencil core, causing or allowing the mixture to set, assembling the set mixture with first and second pencil case parts and securing the parts together to form the pencil.
20. A method of making a cosmetic pencil, comprising the steps of forming a mixture of water and a pigmented composition as claimed in claim 1, introducing the mixture into a pre-formed pencil case and causing or allowing the mixture to set in the case to form the pencil.
21. The method of claim 20, further comprising the step of sharpening one end of the pencil.
Patent Citations (6)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2409000 | 1946-10-01 | Rubenstein | |
| US4413921 | 1983-11-01 | Fotiu | |
| JPX25368 | 1980-02-01 | ||
| JPX58067 | 1984-04-01 | ||
| JPX59759 | 1984-04-01 | ||
| WOXWO82/00444 | 1982-02-01 |
Non-Patent Literature (1)
- Sagarin, Cosmetics/Technology, 1957, pp. 403-404, 615-616 & 617.