US 4,619,733 AGrant
Pollution Free Pulping Process Using Recycled Wash Effluent From Multiple Bleach Stages to Remove Black Liquor and Recovering Sodium Hydroxide From the Black Liquor
Issue Date:1986-10-28
•3 Claims
•3 Drawing Sheets
Abstract
A pollution free pulping process wherein a lignocellulosic material is subjected to various pulping and bleaching steps without the use of sulphur and chlorine. The system is a closed one thus minimizing energy and chemical requirements while permitting one to obtain a product having excellent physical properties.
Metadata
Inventor
- Boon-Lam Kooi
Application Information
Application Number:US 7255063
Filing Date:1985-04-24
Priority Date:1983-11-30
Art Unit:133
Classifications
IPC:
D21C 9147D21C 9153D21C 916
Field of Search:
16219;65;30.1;60;30.11;33;37;40;78
Patent Drawings (3 sheets)
Description
Having thus generally described the invention, reference will be made to the accompanying drawings illustrating embodiments thereof, in which:
FIG. 1 is a flow chart of a first embodiment of a pulping process;
FIG. 2 is a flow chart of a second embodiment of a pulping process; and
FIG. 3 is a flow chart of a third embodiment of a pulping process.
Referring to FIG. 1 in greater detail, wood as indicated by arrow 10 is forwarded to a wood room 12. The wood may be softwood, hardwood or some other lignocellulosic material. Subsequently, delignification is commenced in a digester 14 wherein sodium hydroxide and anthraquinone (AQ) are added and the lignocellulosic material is cooked under pulping conditions as set forth hereinbelow. Subsequently, the precooked pulp is sent to a defiberizer 16 to mechanically treat the chips into a softened pulp mass.
The pulp from defiberizer 16 is then subjected to a washing treatment 18. Following the washing, a hydrogen peroxide and sodium hydroxide treatment is carried out as indicated by reference numeral 20. From hydrogen peroxide treatment 20, the pulp is forwarded to washer 22 and then subsequently to an oxygen bleach treatment 24. At this point, a magnesium salt is added in a small quantity to serve as a prohibitor to carbohydrate degradation. Sodium hydroxide is also added.
Subsequent to oxygen bleaching 24, the pulp is sent to washer 26 and is then subjected to an ozone bleach 28. A further washing step 30 follows before the pulp enters a caustic extraction stage identified by reference numeral 32. A further washing step 34 occurs and a final bleaching is carried out utilizing hydrogen peroxide bleaching 36 the pulp is then subjected to a final wash 38.
As indicated by line 40, the effluent from each washing stage or step is utilized in a countercurrent manner as wash water in the preceding washing stage. As a result, there is considerable savings in energy because the heat value in the washing effluent can be utilized and little or no fresh water is needed. This is not possible in a conventional bleach plant using chlorine and chlorine-containing bleaching chemicals. As will be appreciated by those skilled in the art, the effluent from any washing or wash and press step may be recycled not only in the immediately preceding wash step, but may go to any preceding wash treatment.
As may be seen from FIG. 1, the system will include an oxygen generating plant 42 and an ozone generator 44. From the flow diagram oxygen from plant 42 will flow to generator 44. Through line 46, ozone and oxygen will flow to the ozone bleaching stage 28. Oxygen from ozone bleaching step 28 is recycled via line 48 to oxygen plant 42. Oxygen plant 42 also supplies through line 50, oxygen to oxygen bleaching step 24.
Line 52 from oxygen plant 42 extends to a suitable hydrogen peroxide generator 54. This permits the supply of hydrogen peroxide via line 56 to hydrogen peroxide bleaching step 36. As previously mentioned, the pulp from defiberizer is subjected to a washing treatment 18. From washer 18, the black liquor is sent to an evaporator 58 for concentrating the sodium carbonate to a higher solid content. Subsequently, the liquor is forwarded to a suitable recovery furnace 60 to recover sodium hydroxide which is the main pulping chemical. Ferric oxide is conventionally added to react with the black liquor and burn in the furnace. A suitable furnace would be a direct alkali recovery system such as taught in U.S. Pat. No. 4,000,264.
The final step of the recovery of sodium hydroxide takes place with a leaching step designated by reference numeral 62 wherein sodium ferrate is treated with hot water to recover sodium hydroxide and ferric oxide. Sodium hydroxide, the main pulping chemical, is then recycled from leaching step 62 to digester 14 where any necessary sodium hydroxide make up is added. Ferric oxide recovered from leaching step 62 is recycled to furnace 60.
Referring to FIG. 2 a second embodiment of a pulping process is illustrated. This embodiment differs from that of FIG. 1 in that from defiberizer 116 the pulp is subjected to a wash and press operation 117 and a subsequent oxygen delignification as indicated by reference numeral 119. Following oxygen delignification 119, wherein magnesium and sodium hydroxide were added, a further wash and press step 121 is provided. The pulp, subsequent to washing and pressing, is then subjected to an ozone bleaching stage 123; a further wash 125; an oxygen bleach 127; and a further wash treatment 129. The benefits and advantages of the arrangement shown in FIG. 2 are similar to those of FIG. 1 with the elimination of air and water pollution, energy saving, water consumption reduction and savings in equipment construction cost. The various typical process variables are given hereinbelow.
Referring to FIG. 3 a process suitable for the pulping of hardwood is illustrated. In this process, a single stage soda-AQ delignification is carried out in digester 214. The pulp is then subjected to a screening and washing 215 and a pressing 270. Subsequently, the bleaching is similar to that of the embodiment of FIG. 2 as will be evident from the flow diagram of FIG. 3.
Table 1 hereinbelow gives typical process conditions for the pulping of softwood in a two-stage soda-AQ and hydrogen peroxide delignification. Table 2 gives the typical process conditions for pulping of hardwood with a two-stage soda-AQ and oxygen delignification such as shown in FIG. 2. It will be understood that the process conditions given therein are for purposes of illustration only and that variations of the operating conditions could be made depending on factors well known to those skilled in the art.
Table 3 hereinbelow sets forth process conditions for various bleaching stages as might be utilized in the embodiments of FIGS. 1, 2 and 3. Table 4 sets forth process conditions for a direct alkali recovery system such as recover furnace 60 in FIG. 1, while Table 5 gives typical process conditions for a single stage soda-AQ delignification.
It will be understood that the above-described embodiments are for purposes of illustration only and that changes and modifications may be made thereto without departing from the spirit and scope of the invention.
Claims
I claim:
1. A process for pulping lignocellulosic material comprising the steps of: (a) subjecting the lignocellulosic material to a digestion stage in the presence of NaOH as active alkali compound charged at between 20 to 25% and anthraquinone charged at between 0.1 to 0.4% at a temperature of between 160.degree. C. to 170.degree. C. for a time period of between 120 to 150 minutes to have a final K number of 40 to 60. (b) defiberizing the said pulp from step (a); (c) washing the defiberized pulp from step (b) and sending black liquor removed by the washing to an evaporator; (d) treating the washed pulp from step (c) with between 0.5 to 1.0% of hydrogen peroxide and 3 to 4% of sodium hydroxide for a period of between 60 to 90 minutes at a pulp consistency of between 15 to 25% to give a final K number of between 20 to 30 and subsequently washing the treated pulp; (e) subjecting the washed pulp from step (d) to an oxygen bleaching with oxygen charged at between 0.2 to 3% with a pulp consistency of between 3 to 30% at a temperature of between 80.degree. to 120.degree. C. at a pH of between 9 to 12 for a time period of 10 to 60 minuted with a magnesium ion present at between 0.1 to 0.3% and NaOH present at between 3-7% and subsequently washing said pulp; (f) further bleaching said pulp from step (e) in the presence of ozone at between 0.2 to 1% at a pulp consistency of between 1 to 40% for a time of between 5 to 300 minutes at a temperature of between 15.degree. to 60.degree. C. at a pH of between 2 to 7 and subsequently washing the pulp; (g) subjecting said washed pulp from step (f) to a sodium hydroxide extraction with sodium hydroxide being applied at between 1 to 3%, a pulp consistency of between 1 to 15%, a temperature of between 20.degree. to 60.degree. C., a pH of between 6 to 8 for a time period of between 70 to 90 minuted and subsequently washing the pulp; (h) further bleaching said pulp from step (g) in the presence of hydrogen peroxide charged at between 0.2 to 2% at a pulp consistency of between 10 to 25% for a time period of between 10 to 300 minutes at a temperature of between 20.degree. to 90.degree. C. with a pH of between 7 to 11 and subsequently washing the pulp; (i) the effluent from the washing of the said pulp in the above said steps (h), (g), (f) and (e) is counter-currently recycled to the said washing step in (c) and subsequently sent to the evaporator; all percentages being based on oven-dried pulp, the process being further characterized in that the black liquor from the evaporator in step (c) is forwarded to a recovery furnace to recover sodium hydroxide which is then utilized in step (a), the oxygen from the ozone bleaching in step (f) being recycled and utilized in step (e) and the process being further characterized in being free of sulphur and chlorine.
2. A process suitable for pulping lignocellulosic material comprising the steps of: (a) subjecting the lignocellulosic material to a digestion stage in the presence of NaOH as active alkali compund charged at between 13 to 15% and anthraquinone charged at between 0.01 to 0.05% at a temperature of between 160.degree. C. to 170.degree. C. for a time period of between 60 to 100 minutes to have a final K number of 40 to 50; (b) defiberizing the said pulp from step (a); (c) washing the defiberized pulp from step (b) and sending black liquor removed by the washing to an evaporator; (d) subjecting the washed pulp from step (c) to an oxygen delignification with oxygen being applied at between 0.5% to 2% at pressure of between 10 to 11 kg.sub.f /cm.sup.2 at an initial K number of between 40 to 50, a consistency of between 20 to 25% a temperature of between 110.degree. to 130.degree. C., an NaOH charged as active alkali of between 3 to 7%, a reaction time of between 25 to 35 minutes to have a final K number of between 15 to 25 then subsequently washing and pressing said pulp; (e) further bleaching said pulp from step (d) in the presence of ozone at between 0.2 to 1% at a pulp consistency of between 1 to 40% for a time of between 5 to 30 minutes at a temperature of between 15.degree. to 60.degree. C. at a pH of between 2 to 7 and subsequently washing the pulp; (f) subjecting the washed pulp from step (e) to an oxygen bleaching with oxygen charged at between 0.2 to 3% with a pulp consistency of between 3 to 30% at a temperature of between 80 to 120.degree. C. at pH of between 9 to 12 for a time period of 10 to 60 minutes with a magnesium ion present at between 0.1 to 0.3% and NaOH present at between 3-7% and subsequently washing said pulp; (g) further bleaching said pulp from step (f) In the presence of hydrogen peroxide charged at between 0.2 to 2% at a pulp consistency of between 10 to 25% for a time period of between 10 to 300 minutes at a temperature of between 20.degree. to 90.degree. C. with a pH of between 7 to 11 and subsequently washing the pulp; (h) the effluent from the washing of said pulp in the above said steps (g), (f), (e) and (d) is counter-currently recycled to the said washing step in (c) and subsequently sent to the evaporation; all percentages being based on oven-dried pulp, the process being characterized in being completely free of sulphur and chlorine, the black liquor from the evaporator in step (c) being forwarded to a recovery furnance to recover sodium hydroxide which is then utilized in step (a).
3. A process suitable for pulping hardwood material comprising the steps of: (a) Subjecting the lignocellulosic material to a digestion stage in the presence of NaOH as active alkali compound charged at between 15 to 17% and anthraquinone charged at between 0.05 to 0.4% at a temperature of between 160.degree. C. to 170.degree. C. for a time period of between 20 to 100 minutes to have a final K number of 10 to 20; (b) subjecting the said pulp from step (a) to a screening and washing, and sending black liquor removed by the washing to the evaporator; (c) pressing the said pulp from step (b); (d) further bleaching said pulp from step (b) in the presence of ozone at between 0.2 to 1% at a pulp consistency of between 1 to 40% for a time of between 5 to 300 minutes at a temperature of between 15.degree. to 60.degree. C. at a pH of between 2 to 7 and subsequently washing the pulp; (e) subjecting the said washed pulp from step (c) to an oxygen bleaching with oxygen charged at between 0.2 to 3% with a pulp consistency of between 3 to 30% at a temperature of between 80.degree. to 120.degree. C. at a pH of between 9 to 12 for a time period of 10 to 60 minutes with a magnesium ion present at between 0.1 to 0.3% and NaOH present at between 3-7% and subsequently washing said pulp; (f) further bleaching said pulp from step (d) in the presence of hydrogen peroxide charged at between 0.2 to 2% at a pulp consistency of between 10 to 25% for a time period of between 10 to 300 minutes at a temperature of between 20.degree. to 90.degree. C. with a pH of between 7 to 11 and subsequently washing the pulp; (g) the efflucent from the washing of the said pulp in the above said steps (f), (e) and (d) is counter-currently recycled to the said screening and washing step in (b) and subsequently sent to the evaporator; all the percentages being based on oven-dried pulp, the process being characterized in that the process is free of chlorine and sulphur compounds and the black liquor from the washing in step (b) is forwarded to a recovery furnace to recover sodium hydroxide which is then utilized in step (a).
Patent Citations (3)
Non-Patent Literature (3)
- Andrews et al., "Oxygen Delignification and Bleaching of Soda-Anthraquinone Pulps", TAPPI, vol. 62, No. 6, Jun. 1979, p. 29.
- Fujii et al., Oxygen Pulping of Hardwoods, TAPPI, vol. 61, No. 8, Aug. 1978, p. 37.
- Soteland, "Bleaching of Chemical Pulps with Oxygen and Ozone", Pulp and Paper Magazine Canada, vol. 75, No. 4; Apr. 1974, p. 91.