US 4,612,397 AGrant
Use of Supported Phosphate Catalysts for Preparation of Linear Polyethylenepolyamines
Issue Date:1986-09-16
•4 Claims
Abstract
This invention is directed to thermally activated pelletted catalyst compositions comprising titania having phosphorous derived from a diaminohydrogen phosphate deposited thereon and to their preparation and their use in the production of predominantly linear polyethylenepolyamines from ethylenediamine and monoethanolamine.
Metadata
Assignee
- Texaco, Inc.
Inventor
- Terry L. Renken
Application Information
Application Number:US 727307&
Filing Date:1985-04-25
Priority Date:1983-01-03
Art Unit:124
Classifications
IPC:
C07C 8506
Field of Search:
564260479;485;509;512687 R
Patent Drawings
This patent does not have any drawings.
Description
BACKGROUND OF THE INVENTION
1. Technical Field of the Invention
This invention relates to the preparation of predominately linear polyethylenepolyamines from the starting reagents of ethylenediamine and monoethanolamine in the presence of unique thermally activated catalyst compositions comprising titania having deposited thereon phosphorous derived from a diamminohydrogen phosphate.
2. Prior Art
Heretofore, polyethylenepolyamine compounds such as diethylenetriamine, triethylenetetramine and the higher homologs have been produced by the reaction of an alkyl halide such as ethylene dichloride with an amine such as ammonia or ethylenediamine at elevated temperatures and pressures. Normally, relatively high yields of predominately non-cyclic polyethylenepolyamine compounds are obtained from this process with varying yields of heterocyclic amines. The large amounts of energy required to produce the reactants as well as the difficult separation procedures required to recover the more valuable linear polyethylenepolyamines diminish the usefulness of the ethylene dichloride process. The hydrohalide salts of ammonia and the polyethylenepolyamine products must also undergo difficult and time consuming caustic neutralization to yield the free polyethylenepolyamines.
It has heretofore been known that phosphates can be used to catalyze reactions products to produce predominately heterocyclic rather than linear products. Thus, U.S. Pat. No. 3,297,701 teaches the use of aluminum phosphate to catalyse the reaction of ethanolamines and polyethylenepolyamines to yield cyclic compounds. U.S. Pat. No. 3,342,820 discloses the use of aluminum phosphate for the preparation of heterocyclic compounds such as triethylenediamine. As another example, U.S. Pat. No. 4,103,087 also discloses the use of aluminum phosphate catalysts for producing heterocyclic product compounds.
More recently, investigators have found that more linear products can also be obtained in a catalytic conversion. Thus, Ford et. al. U.S. Pat. No. 4,316,840 discloses the preparation of polyalkylenepolyamines from ethylene diamine utilizing a metal nitrate or sulfate as a catalyst. U.S. Pat. No. 4,314,083 discloses the reaction of ethylene diamine with monoethanolamine to prepare noncyclic polyalkylenepolyamines using, as a catalyst, a salt of a nitrogen or sulfur-containing compound.
In inventions originating in our laboratories, Brennan et. al. in U.S. Pat. No. 4,036,881 discloses the use of phosphorous-containing catalysts to catalyze the reaction of ethylenediamine with monoethanolamine. Excellent results were obtained when the reaction was conducted in an autoclave. However, when the phosphorous compound was supported on silica or diatomaceos earth, good results were obtained only at comparatively low conversions. Brennan et. al. U.S. Pat. No. 4,044,053 is also relevant in this regard. A recently filed Brennan copending application Ser. No. 283,713, filed July 16, 1981 (now abandoned) and entitled "Preparation of Linear Polyethylenepolyamines With an Aluminum Phosphate Catalyst" is directed to an aluminum phosphate catalyst. Excellent results were obtained using a catalyst of this nature in batch-type reactions. Brennan U.S. Pat. No. 4,103,087 discloses the use of pelleted aluminum phosphate to prepare di-(N,N-disubstituted amino)alkanes.
Winkler et al. in a 1966 publication [Deutsche Akad. Wiss., Berlin, Germany, Z. Anorg. Allgen. Chem. 346 (1-2), 92-112 (1966)] disclose compounds of the general formula HX.sup.v P.sub.2 O.sub.3 wherein X represents arsenic, antimony and mixtures thereof. Also disclosed are compounds of the general formula H.sub.2 X.sup.iv P.sub.2 O.sub.3, wherein X represents silicon, germanium, tin, lead, titanium and zirconium. It is shown that the group IV phosphates have cation exchange properties.
Daniel Br. Apcn. No. 2,092,467 pub. Aug. 18, 1982 modifies iron phosphate catalysts disclosed in Cavaterra U.S. Pat. No. 3,948,959 for making methacrylic acid from isobutyric acid. Daniel uses such catalysts in admixture with a support prepared by calcining the dried powder recovered from a slurry of silica with phosphoric acid. Daniel teaches that the support is inert and that titania or zirconia can also be used.
SUMMARY OF THE INVENTION
A method of preparing novel catalyst compositions is disclosed. The catalyst is extremely useful in the improved production of predominately linear polyethylenepolyamines from ethylenediamine and monoethanolamine reactants. The novel catalysts of the claimed invention can be prepared by treating titania with a diaminohydrogen phosphate such that, in a thermally activated condition, the phosphorous is chemically bound to the titania. These novel compositions can be used to catalyze the reaction of monoethanolamine with ethylenediamine to provide essentially linear polyethylenepolyamine reaction products.
DETAILED DESCRIPTION
In one aspect the invention is directed to improved catalyst compositions comprising titania to which phosphorous derived from a diaminohydrogen phosphate has been chemically bonded by thermal activation. In another aspect of the present invention, such catalysts are used in producing essentially linear polyethylenepolyamines such as diethylenetriamine, triethylenetetramine, tetraethylenepentamine and pentaethylenehexamine from the reaction of ethylenediamine and monoethanolamine. The inventor is unaware of the precise structural differences between the claimed catalysts and previous phosphate catalysts which have been tried in such reactions, but is cognizant of substantially higher rates of conversion to linear polyethylenepolyamines with the claimed catalysts.
The novel phosphate compounds catalyze the reaction of ethylenediamine and monoethanolamine at a temperature of from about 250.degree. C. to about 400.degree. C., preferably from about 300.degree. C. to about 350.degree. C. and a pressure of from about 500 to about 3000 psig. and more preferably from about 1000 to about 2000 psig. Higher temperatures and pressures can be used, but there is no particular advantage in going to higher temperatures and/or pressures. The ratio of ethylenediamine to monoethanolamine may range from about 1:2 to about 5:1.
The pelleted catalyst compositions of the present invention are normally employed as a fixed bed of catalyst in a continuous reaction system. In a continuous process of this nature, the time of contact of the reactants with the catalyst is one of the interrelated factors that those skilled in the art will adjust, along with temperature, pressure, bed geometry, pellet size, etc. in order to obtain a desired rate of reaction and, hence, a desired percentage of conversion of the reactants. Thus, in a continuous process, it is not necessary to drive the reaction to completion because unreacted feedstock components can be recycled to the reactor.
It is customary to use cylindrically-shaped catalyst pellets having a diameter essentially equal to the length thereof, such as diameters and lengths ranging from about 1/32" to about 3/8". It will be understood that the shape and dimensions of the pellets are not critical to the present invention and that pellets of any suitable shape and dimensions may be used as desired, by one wishing to practice the process of the present invention.
When cylindrical pellets of catalyst of the type described above are used, the weighted hourly space velocity may be varied within wide limits (e.g., 0.1 to 5 w/hr/w) in order to obtain a desired rate of conversion, as explained above. Normally, space velocities of about 0.5 to 2 w/hr/w will be employed.
Catalyst life is an important factor in conducting a continuous reaction. For example, if a catalyst is easily poisoned, or if catalyst pellets do not have good structural properties, the economics of the process will be seriously and adversely affected.
The catalysts of the present invention are not particularly susceptible to poisoning so this normally does not present a problem. However, under the reaction conditions employed, amines of the type used and formed herein have the potential capability of leaching or otherwise adversely affecting the structural integrity of the pellets. In an extreme instance, catalyst pellets having good initial crush strength and surface hardness will be reduced to fines very rapidly when used under reaction conditions such as those employed herein.
It is a feature of the present invention that the pelleted catalyst compositions have improved resistance to physical degradation when used to catalyse the reaction of monoethanolamine with ethylenediamine.
The catalyst compositions of the present invention are prepared by heating titania pellets in the presence of a diamminohydrogen phosphate to provide phosphorous-containing titania-supported catalyst pellets. The titania pellets may be prepared by extrusion or by compaction in conventional pelleting apparatus using a pelleting aid such as graphite. It is also within the scope of the present invention to deposit the phosphorus compound on a powdered titania followed by pelleting and, if desired, calcination.
The source of the phosphorous, in accordance with the present invention, is a diamminohydrogen phosphate such as diammonium hydrogen phosphate, (NH.sub.4).sub.2 HPO.sub.4, dimethylaminohydrogen phosphate, (CH.sub.3).sub.2 NH.PO.sub.4, diethylaminohydrogen phosphate (CH.sub.3 CH.sub.2).sub.2 NH.PO.sub.4, etc. In general, the pelleted composition should contain at least about 0.5 weight percent of phosphorus.
When the catalyst composition is to be prepared by impregnating a preformed pellet, a suitable procedure to be used is to heat a liquid containing the liquid or liquifiable phosphorus compound at a temperature of about 100.degree. to about 150.degree. C. and to then add pellets in an amount about equal to the volume of the heated liquid. This treatment should be continued from about 0.5 to about 5 hours. At the end of that time, the resulting slurry may be cooled, decanted to remove excess liquid followed by washing with an amount of water adequate to substantially completely remove un-adsorbed liquid. Temperatures above 150.degree. C. can be used, if desired, but there is no particular advantage in doing so.
It will be understood that the phosphorous that is present on a thus-treated pellet is not present as elemental phosphorous, but rather as phosphorous that is chemically bound, probably as an oxide, to the support. This is demonstrated by the fact that repeated washing will not remove all of the phosphorous. However, the exact nature of the bonding is not completely understood.
The amount of phosphorous that is bonded or otherwise adheres to the support is a function of heating and other conditions used in the treating step and is also a function of the chemical identity of the phosphorous compound that is used as a source of phosphorous. Under the treating conditions exemplified above, at least about 2.5 wt % of phosphorous is caused to bond or otherwise permanently adhere to the pellets. There is an upper limit to the amount of phosphorous that bonds or otherwise permanently adheres to the support. This upper limit is, as indicated, a function of both the treating conditions and the chemical used as a source of the phosphorous. Normally, the maximum amount of phosphorous that can be caused to bond or otherwise permanently adhere to the pellets is within the range of about 5 to 10 wt %.
As a matter of convenience, the normal practice is to use only one chemical as a phosphorous source (e.g., diammonium hydrogen phosphate). However, mixtures of two or more such reagents may be used, if desired.
When the pellets are impregnated with the phosphorous compound at a temperature of at least about 100.degree. C., there is no absolute need to calcine the catalyst composition before use. However, the pellets can be calcined, if desired, as a precautionary measure and/or in order to still further improve the physical properties of the pellets. The pellets are suitably calcined at a temperature of about 200.degree. C. to about 800.degree. C. for a period of time within the range of 2 to 24 hours; more preferably at a temperature of about 500.degree. C. to about 700.degree. C. for about 4 to 16 hours.
Other procedures can be used in adding phosphorous to the support. For example, the pellets can be treated with the phosphorous compound at ambient temperatures or at more modest elevated temperatures of less than about 100.degree. C. In this situation, however, it is necessary to thermally activate the treated pellets by calcining under the conditions recited above.
Alternatively, the support can be treated with the phosphorous-containing compound in powdered form and the powder can thereafter be pelleted. If the treatment is conducted at a temperature of about 100.degree. C. or more, thermal activation will normally have been obtained and it will not be absolutely necessary to perform a calcining operation. If lower treating temperatures are used, calcining is a desired operation. The calcining operation can be conducted prior to or subsequent to the pelleting step. Any appropriate pelleting procedure of the type known to those skilled in the art may be used. For example, the treated powdered support can be mixed with graphite and/or other binders and compacted or extruded under conventional conditions.
There are many compounds which can be formed from the reaction of ethylenediamine and monoethanolamine besides the preferred linear polyethylenepolyamines such as diethylenetriamine, triethylenetetramine, tetraethylenepentamine and pentaethylenehexamine. Less desirable cyclics and other compounds, such as piperazine, N-(2-aminoethyl)ethanolamine and N-(2-aminoethyl)piperazine, are also formed. The more desired linear polyethylenepolyamines can be easily recovered from the reaction product mixture by conventional methods such as distillation. Such distillation recovery methods are well known in the art. An advantage of the claimed invention is that the lower molecular weight polyethylenepolyamines recovered from the reaction mixture can be further reacted with monoethanolamine to produce a larger percentage of the higher molecular weight linear polyethylenepolyamines.
The following example will further illustrate the preparation of predominantly linear polyethylenepolyamines from ethylenediamine and monoethanolamine by the use of the catalyst compositions of the present invention. It is given by way of illustration and not as a limitation on the scope of the invention. Thus, it will be understood that reactants, proportions of reactants, and time, temperature and pressure of the reaction steps may be varied with much the same results achieved.
For purposes of convenience and brevity, the reactant compounds employed and the products obtained have been abbreviated in the following examples and tables. The abbreviations employed for these various compounds are:
EDA--ethylenediamine
MEA--monoethanolamine
PIP--piperazine
DETA--diethylenetriamine
TETA--triethylenetetramine
TEPA--tetraethylenepentamine
AEEA--N-(2-aminoethyl)ethanolamine
AEP--N-(2-aminoethyl)piperazine.
EXAMPLE I
Titania Catalyst Preparation
A series of pelleted catalysts were prepared by depositing phosphorus on a titania support.
A flask containing 65.0 g of (NH.sub.4).sub.2 HPO.sub.4, 150 cc. of titania pellets and 50 cc of water was spun on a roto evaporator under aspirator pressure at room temperature for 2 hours. The contents of the flask were then poured onto a sieve and washed with a small amount of water. The wet pellets were then charged to a tubular furnace and dry nitrogen was passed through at ca. 50 cc/hr. The pellets were dried by heating the furance to 60.degree. C. for 3 hours, then to 80.degree. C. for 1 hour and then to 90.degree. C. overnight. The temperature of the furnace was then increased by 10.degree. C. every 30-60 minutes until a temperature of 250.degree. C. was reached. This temperature was maintained for 16 hours. Analysis of the resulting catalyst by atomic absorption indicated a phosphorus content of 4.3 wt %.
The catalyst was then placed in a 25 cc tubular continuous reactor system. A 2:1 (wt/wt) EDA/MEA feed was charged to the reactor at a space velocity of 1.0 g/cc-hr.
Data are presented below which compare the activity and product selectivity of this catalyst to a commercially available 40 wt % phosphate-on-alumina catalyst of the type disclosed in Brennan U.S. Pat. No. 4,103,087 at column 8, lines 50-54.
There are times when it is desirable to obtain greater yields of the higher polyethylenepolyamines such as triethylene tetramine on tetraethylpentamine than those reported herein. In such instances, the diethylenetriamine can be recycled by substituting diethylene triamine for all or a part of the ethylenediamine feedstock.
This specification includes data related to the invention disclosed and claimed herein and also, for comparative purposes, data is disclosed in this specification that is also disclosed and claimed in copending Vanderpool U.S. patent application Ser. No. 06/455,160, filed. Jan. 3, 1983, of an even date herewith and entitled "Catalysts and Preparation of Linear Polyethylenepolyamines Therewith".
The foregoing examples of the present invention have been given by way of illustration only and are not intended as limitations on the scope of the invention which is defined by the following claims.
Claims
I claim:
1. In a method wherein monoethanolamine is reacted with ethylenediamine in the presence of a phosphorus containing catalyst to provide an essentially noncyclic product comprising polyethylenepolyamines, the improvement for conducting said process on a continuous basis which comprises: a. using, as a catalyst, a pelleted composition consisting essentially of titania having thermally chemically bonded thereto from about 0.5 to about 10 wt. % of phosphorous derived from a diamminohydrogen phosphate, b. continuously contacting a mixture of ethylenediamine and monoethanolamine in a molar ratio of about 1 to 5 moles of ethylenediamine per mole of monoethanolamine with said pelleted catalyst at a temperature of about 250.degree. to about 400.degree. C. and a pressure of about 500 to about 3000 psig. to obtain an essentially noncyclic reaction product.
2. A method as in claim 1, wherein the diamminohydrogen phosphate is diammonium hydrogen phosphate and wherein the titania pellets, after having been treated with the diammonium hydrogen phosphate are calcined at a temperature of from about 200.degree. to about 800.degree. C.
3. In a method wherein monoethanolamine is reacted with ethylene diamine in the presence of a phosphorous containing catalyst to provide an essentially noncyclic product comprising polyethylenepolyamines, the improvement for conducting said process on a continuous basis which comprises: a. using, as a catalyst, a composition prepared by a method which consists of impregnating titania pellets with a diamminohydrogen phosphate and heating the impregnated pellets at a temperature of about 100.degree. to about 250.degree. C. for a period of time sufficient to thermally chemically bond from about 0.5 to about 10 wt. % of phosphorous to said titania pellets, water washing the thus treated pellets to remove chemically uncombined phosphorous and thereafter recovering and drying the thus treated pellets, to thereby provide a catalyst composition consisting essentially of titania having from 0.5 to about 10 wt. % of phosphorous thermally chemically bonded thereto, b. continuously contacting a mixture of ethylene diamine and monoethanolamine in a molar ratio of about 1 to 5 moles of ethylene diamine per mole of monoethanolamine with said pelleted catalyst at a temperature of about 250.degree. to about 400.degree. C. and a pressure of about 500 to about 3000 psig. to obtain an essentially noncyclic reaction product.
4. A method as in claim 3, wherein: a. the diamino hydrogen phosphate is diammonium hydrogen phosphate and wherein the catalyst pellets are calcined at a temperature within the range of about 200.degree. to about 800.degree. C. prior to use; and b. wherein the mixture of ethylene diamine and monoethanolamine are contacted with said pellets at a temperature within the range of about 300.degree. to about 350.degree. C. and a pressure within the range of about 1000 to about 2000 psig.
Patent Citations (13)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2824073 | 1958-02-01 | Rylander, Jr. et al. | |
| US2854498 | 1958-09-01 | Zimmerschied et al. | |
| US3297701 | 1967-01-01 | Brader et al. | |
| US3342820 | 1967-09-01 | Brader | |
| US3448164 | 1969-06-01 | Holm et al. | |
| US4036881 | 1977-07-01 | Brennan et al. | |
| US4044053 | 1977-08-01 | Brennan et al. | |
| US4103087 | 1978-07-01 | Brennan | |
| US4314083 | 1982-02-01 | Ford et al. | |
| US4316840 | 1982-02-01 | Ford et al. | |
| US4409418 | 1983-10-01 | Johnson et al. | |
| US4430207 | 1984-02-01 | Kukes | |
| GBX2092467 | 1982-01-01 |
Non-Patent Literature (3)
- A. Winkler & E. Thilo (Deutsche Akad. Wiss. Berlin, Germany) Z. Anurg Chem 346 (1-2) 65 C.A. 14807c, 1966.
- Brennan U.S. application Ser. No. 453,841 filed 12/27/82, "Preparation of Linear Polyethylenepolyamines with Aluminum Phosphate Catalyst".
- "Refractories", F. H. Norton, McGraw-Hill Book Co., 3rd Ed., 1949.