US 4,589,196 AGrant
Contacts for VLSI Devices Using Direct-Reacted Silicide
Issue Date:1986-05-20
•10 Claims
•1 Drawing Sheets
Abstract
Metal contacts and interconnections for semiconductor integrated circuits are formed by a process using direct-reacted silicide to increase step or sidewall coverage. First a thin layer of titanium or other refractory metal is deposited, extending into a contact hole, then polysilicon is deposited and a preferential etch removes all of the polysilicon except on the vertical sides of steps or apertures. A second thin layer of titanium is deposited, then a heat treatment forms silicide to create conductive sidewalls or a plug. Metal contacts then engage the direct-reacted silicide rather than relying upon step coverage.
Metadata
Assignee
- Texas Instruments Incorporated
Inventor
- Dirk N. Anderson
Application Information
Application Number:US 659610&
Filing Date:1984-10-11
Priority Date:1984-10-11
Art Unit:114
Classifications
IPC:
H01L 2124
Field of Search:
29148357589;590;591DIG. 19,DIG. 20;DIG 14767 S;71 S;68
Patent Drawings (1 sheets)
Description
Background of the Invention
This invention relates to semiconductor devices, and more particularly to metal contacts and interconnections for semiconductor integrated circuits.
In the manufacture of VLSI devices, a thin metal coating such as aluminum is deposited and patterned to create contacts and interconnections. Problems occur in thinning of the metal at near-vertical sidewalls of holes in thick insulator layers where the metallization pattern makes contact to silicon regions or to other layers such as polysilicon. Thinner metal at these sidewalls or other steps results in higher resistance and a propensity for electro-migration failures. Heretofore, the steepness of the sidewalls has been minimized by a "reflow" process, but this necessitates undesirable high temperature operations and larger geometries.
In particular, the shrinking dimensions of VLSI devices such as the 1-Megabit dynamic RAM, requiring one micron sized geometries, creates fundamental problems with forming good metalization to silicon contacts. The proximity to unrelated structures reaches the point where reflowing the insulating multilevel oxide, or sloping the contact edges in any other fashion, is becoming unacceptable. However, sputtered aluminum is unacceptably thin on the edge of a vertical contact. Various methods have been tried to resolve this problem, including using lower resistance materials beneath the insulating oxide which enables the use of a thinner oxide layer and hence a smaller step, and the use of other metals which may have better step coverage. Problems with approaches such as these include filaments or metal remaining after the metal etch and failure problems after long term operation resulting from the thinner metallization on the small dimensioned contact sidewalls, however improved by the use of other metals.
It is the principal object of this invention to provide an improved process for making metal contacts for semiconductor integrated circuits. Another object is to provide improved semiconductor devices with metallization patterns, avoiding the problems of thinning at steps and contact apertures. A further object is to provide improved step coverage and lower resistance for metallization of semiconductor devices. Another object is to provide a method of making contacts that allow smaller pitch for the metal pattern (closer spacing between metal lines) due to smaller contact areas being allowed; thus higher density VLSI devices are possible.
Summary of the Invention
In accordance with one embodiment of the invention, metal contacts and interconnections for semiconductor integrated circuits are formed by a process using direct-reacted silicide to increase step or sidewall coverage. First a thin layer of titanium or other refractory metal is deposited, extending into a contact hole, then polysilicon is deposited and a preferential etch removes all of the polysilicon except on the vertical sides of steps or apertures. A second thin layer of titanium is deposited, then a heat treatment forms silicide to create conductive sidewalls or a plug. Metal contacts then engage the direct-reacted silicide rather than relying upon step coverage.
Brief Description of the Drawings
The novel features believed characteristic of the invention are set forth in the appended claims. The invention itself, however, as well as other features and advantages thereof, will be best understood by reference to the detailed description which follows, read in conjunction with the accompanying drawings, wherein:
FIGS. 1-4 are greatly enlarged elevation views in section of a small part of a semiconductor chip having metal contacts made according to the invention.
FIG. 5 is an elevation view in section, corresponding to FIG. 4, for another embodiment of the invention.
Detailed Description of Specific Embodiment
Referring to FIGS. 1-4, a method of forming a metal-to-silicon contact according to the invention will be described. A silicon substrate 10 has a silicon oxide layer 11 deposited on it as seen in FIG. 1, by any of several methods. There may be depositions of and patterning of other layers of polysilicon, refractory metals, or the like included in the process prior to the steps to be described. In any event, a vertical-walled hole 12 is formed in the oxide layer 11 by an anisotropic etch technique such as RIE. Typically, the hole would be about one micron in width, in an oxide layer of about one micron thickness, or more likely slightly less than one micron.
As seen in FIG. 2, a first layer 13 of titanium is deposited over the face of the silicon slice using a deposition method such as sputtering so that the titanium coats the sidewall, as well as the bottom of the hole 12. The thickness of the titanium is about 1000 .ANG. on the top of the slice, although thinner in the hole. Next, a layer of polycrystalline silicon is deposited over the face of the slice, again by an isotropic deposition method such as low temperature, plasma-enhanced CVD, to leave a uniform coating of about 1500 to 3000 .ANG. thickness over the sidewalls as well as the bottom of the hole. An anisotropic etch of the polysilicon leaves sidewall portions 14. Due to the thin titanium coating 13 in the bottom of the hole 12, the polysilicon etch may remove the titanium and some of the silicon face, as seen in the Figure. This is not necessary, but not harmful; if the etch is more selective it would not occur.
Turning now to FIG. 3, a second layer 15 of titanium is deposited by an isotropic method such as sputtering (to a thickness of about 1500 .ANG. on top) so that it coats the sidewalls of the hole as well as the bottom. The slice is then heated to about 675.degree. C. for one-half to one hour to form silicide wherever titanium is in contact with silicon (single crystal or poly). After the siliciding operation, the unwanted residue of titanium is removed by an etchant such as piranha which removes other reacted titanium compounds (titanium nitride and oxide) from the silicon oxide 11 but not titanium silicide in the hole. The silicide formation will actually perform some physical redistribution of the forming layers, so this method does not require such good step coverage of the deposit films.
As seen in FIG. 4, a deposited and patterned metal layer 16 (such as aluminum) makes contact to the top area 17 of the titanium-silicide/polysilicon structure built up on the sidewalls of the hole 12. The thickness over the flat surface is much greater than in the hole. It does not matter that the step coverage is inadequate; if the metal 16 is thinned at the steps and does not make a low resistance connection to the bottom of the hole it is of no consequence because of the conductive walls.
The polysilicon layer may be deposited in such a way that the hole 12 is almost filled with a plug of polysilicon instead of merely the sidewalls 14. The layer 15 would not then come into contact with the silicon substrate 10. The silicided plug would function as before, however. This embodiment is illustrated in FIG. 5.
While this invention has been described with reference to an illustrative embodiment, this description is not intended to be construed in a limiting sense. Various modifications to the illustrative embodiment, as well as other embodiments of the invention, will be apparent to persons skilled in the art upon reference to this description. It is therefore contemplated that the appended claims will cover any such modifications or embodiments as fall within the true scope of the invention.
Claims
What is claimed:
1. A method of making contact to a face of a semiconductor body through an aperature in an insulating layer on said face, comprising the steps of: (a) depositing a thin layer of conductive material on said face to cover the semiconductor body within said aperture and also to cover the insulating layer and the sidewalls of the aperture, (b) depositing a layer of semiconductor material over said conductive material and etching said layer of semiconductor material from said face but leaving the layer in place on the sidewalls, (c) depositing another thin layer of conductive material on said face to extend continuously over the insulator and over the layer of semiconductor material and down the sidewall into the aperature, (d) reacting the thin layer of conductive material with the semiconductor material to form a silicide/semiconductor material structure, (e) removing unwanted residue of said thin and said another thin layers of conductive material from said insulating layer, (f) depositing a metal layer over said insulator to make contact to the reacted conductive material and semiconductor material at said aperture.
2. A method according to claim 1 wherein said conductive material is a refractory metal and said semiconductor material is silicon.
3. A method according to claim 2 wherein said layer of semiconductor material is polycrystalline silicon, and said insulating layer is silicon oxide.
4. A method according to claim 4 wherein said refractory metal is titanium.
5. A method according to claim 4 wherein said another thin layer extends into said aperture to make direct contact to the semiconductor material at said face.
6. A method of making a metal connection at a face of a semiconductor body, said connection extending over a step in an insulating layer on said face, comprising the steps of: (a) depositing a first layer of conductive material on said face to cover the semiconductor body and to cover the insulating layer and the sidewall of the step, (b) depositing a layer of semiconductor material of said first layer of conductive material and selectively removing the layer of semiconductor material over said insulating layer but leaving the layer on said sidewall, (c) depositing a second layer of said conductive material on said face to extend continuously across the step over the layer of semiconductor material, (d) reacting the conductive material with the semiconductive material to form a silicide/semiconductor material structure, (e) removing unwanted residue of said first and second layers of conductive material over the insulating layer, (f) depositing a conductor on said face to engage the reacted conductive material and semiconductor material at said step.
7. A method according to claim 6 wherein said conductive material is a refractory metal and said semiconductor material is silicon.
8. A method according to claim 7 wherein said layer of semiconductor material is polycrystalline silicon, and said insulating layer is silicon oxide.
9. A method according to claim 8 wherein said refractory metal is titanium.
10. A method according to claim 6 wherein said another thin layer extends into said aperture to make direct contact to the semiconductor material at said face.
Patent Citations (5)
Non-Patent Literature (2)
- Ku, "Ohmic Contacts for Small, Shallow Structure Device", IBM Tech. Discl. Bull., vol. 22, No. 4, 9/79.
- Gates et al, "Encapsulation for Semiconductor Device", IBM Tech. Discl. Bull., vol. 8, No. 11, 4/66.