Method of Making a Valve Metal Powder for Electrolytic Condensers and the Like

Our present invention relates to a method of making a valve metal powder for electrolytic condensers and, more particularly, for making such a powder from a metal of the vanadium group (Va) of the Periodic System of chemical elements.

Valve metals are metals on which anodic films can be formed and are referred to as such because of the rectifying characteristic of their anodic oxides. These metals include the vanadium group of elements, namely, the elements of Group Va of the Periodic System, i.e. vanadium, niobium and tantalum. Of these metals, tantalum has been found to be especially desirable in the production of electrolytic condensers and, for the production of such capacitors, it is known to produce tantalum powder by a chemical process.

In particular, it is known to produce tantalum powder by forming a reaction mixture of a double fluoride salt of the valve metal and metallic sodium and/or potassium and to react this mixture in the presence of a doping element to form a melt cake from which the reaction products which are water soluble can be leached to leave the valve metal in the form of a powder or in a form which can be readily broken up to produce the powder.

The product has been found to be especially suitable for use as electrodes for electrolytic condensers and the like.

To produce these electrodes, the powder is compacted to form a "green" body or compact which is thereafter sintered. Upon the sintered electrode a dielectric film is then formed.

For high electrical capacitance, it is important that the valve metal powder have an especially small particle size and hence large surface area. It is known to produce powders in the manner described from, for example, United Kingdom Pat. No. 2,068,924 in which the doping element is phosphorus.

While this process can produce a finely divided product with a large surface area, the method has many disadvantages and even with respect to the particle size and high surface area may not be fully satisfactory.

Accordingly, it is an object of the invention to provide a method of producing a valve metal powder with an especially fine grain structure and even greater surface area for improved electrical capacitance.

Another object of the invention is to provide an improved method of making a valve metal powder of a member of the vanadium group of metals which is free from disadvantages characterizing the earlier method.

We have discovered, most surprisingly, that by substituting sulfur as a doping element for the phosphorus used in the prior art, in a method as previously described, it is possible to improve the surface area and the fine division of the valve metal powder which is obtained.

This, it will be appreciated, is highly unexpected, at least in part because there was no way to predict that the choice of the doping element could have such a salutary effect.

The sulfur which can be used can be in the form of elemental sulfur, e.g. flower or sulfur, in the form of inorganic sulfur compounds such as sodium sulfate and sodium dithionite or in the form of organic sulfur compounds such as mercaptans. The sulfur can be supplied as mixtures of these sulfur-containing substances. The sulfur compounds or products which are used, of course, should be selected so that they are leachable from the melt cake during the leaching operation.

The amount of sulfur used for doping according to the invention must be an effective amount and the effective amount can be easily determined by experimentation. In general, we have found it to be advantageous to utilize elemental sulfur and/or one or more of the sulfur compounds mentioned in concentrations such that the reaction mixture contains 20 to 500 ppm with respect to the valve metal content of the reaction mixture.

According to the invention, the reaction mixture can be initially formed and the elemental sulfur and/or the sulfur compounds then added thereto. It is also possible, in accordance with the invention, to first form the double fluoride salt of the valve metal and to add the elemental sulfate and/or the sulfur compounds to the double fluoride salt before the reaction mixture is formed. The reaction mixture can then be produced by combining the double fluoride salt with the fluoride binding component, e.g. elemental sodium.

In a preferred embodiment of the invention, the elemental sulfur and/or the sulfur contents are added during the formation of the double fluoride salt of the valve metal so that they participate in forming or are trapped interstitially in the crystals of the double fluoride salt.

In addition to being free from various disadvantages resulting from the handling of phosphorus, the method of the invention provides a valve metal powder, especially tantalum powder, with an exceptionally high specific surface area and small particle size.

1,022 kg of K.sub.2 TaF.sub.7 is mixed iwth the stoichiometrically required quantity of metallic sodium necessary to remove the fluoride and with 0.3 kg of sodium chloride. The mixture is heated under a protective gas (nitrogen) to a temperature of 900.degree. C. and is held at this temperature for one hour. The result is a melt cake which is then leached to solubilize the sodium fluoride, potassium fluoride and sodium chloride from the tantalum metal powder which results.

Parallel tests were undertaken with mixtures as described and under the aforementioned conditions with the addition of (a) 100 ppm sulfur, (b) 200 ppm sulfur, (c) 500 ppm sulfur with reference to the tantalum and in the form of Na.sub.2 SO.sub.4 under identical conditions. The surface area of the powder was measured by the BET method and the mean grain size by FSSS method with the following results:

The reaction mixture was formed and processed as described in Example 1. 200 ppm sulfur relative to the tantalum was supplied in the form of flowers of sulfur.

The following results were obtained:

Surface area (BET) (m.sup.2 /g): 0.36

Mean grain size (FSSS) (.mu.): 1.5

The reaction mixture was formed as processed as described in Example 1. 200 ppm sulfur relative to the tantalum was added in the form of sodium dithionite.

The following results were obtained:

Surface area (BET) (m.sup.2 /g): 0.39

Mean grain size (FSSS) (.mu.): 1.4

110 kg K.sub.2 TaF.sub.7 is mixed with stoichiometrically required quantity of sodium (32.3 kg), 30 kg of sodium chloride and 44 g of Na.sub.2 SO.sub.4. The reaction mixture is heated under a protective gas (nitrogen) to 900.degree. C. and is maintained at this temperature for one hour to form a melt cake. The melt cake is then leached with water to yield a tantalum powder which was analyzed for surface area and mean particle size with the following results:

Surface area (BET) (m.sup.2 /g): 0.4

Mean grain size (FSSS) (.mu.): 1.4.