US 4,559,385 AGrant
Method for Preparing Aqueous Emulsions
Issue Date:1985-12-17
•3 Claims
Abstract
Aqueous emulsions for impregnating organic fibers, comprising, in addition to water and dispersants, (1) a diorganopolysiloxane having a Si-bonded hydroxyl group in each terminal unit and whose organic radicals are free of basic nitrogen atoms; (2) an organopolysiloxane containing diorganosiloxane units in which the two organic radicals are monovalent hydrocarbon radicals and also contains at least two monovalent SiC-bonded organic radicals per molecule having a basic nitrogen atom in which the organopolysiloxane is present in the emulsion in an amount of from 5 to 50 weight percent based on the weight of the diorganopolysiloxane (1); (3) an organosilicon compound selected from an organosilane containing at least two SiOC-bonded monovalent organic radicals consisting of carbon, hydrogen and possibly oxygen and/or partial hydrolyzates thereof, in which the organosilicon compound is present in the emulsion in an amount of from 2 to 6 weight percent based on the total weight of the diorganopolysiloxane (1) and organopolysiloxane (2); and (4) a condensation catalyst, which is present in an amount of from 0.2 to 1 weight percent based on the total weight of the diorganopolysiloxane (1) and organopolysiloxane (2). These aqueous emulsions are prepared by mixing the organosilicon compound (3) with an emulsion of diorganopolysiloxane (1) and organopolysiloxane (2) and thereafter mixing the resultant mixture with the condensation catalyst (4).
Metadata
Assignee
- Wacker-Chemie GmbH
Inventors
- Karl Huhn
- Kurt Ullrich
Application Information
Application Number:US 6484166
Filing Date:1984-09-10
Priority Date:1983-12-01
Art Unit:151
Classifications
IPC:
C08L 8300
Field of Search:
524528838;864;58817;18;38
Patent Drawings
This patent does not have any drawings.
Description
The present invention relates to aqueous emulsions and more particularly to a method for preparing aqueous emulsions having better stability.
Background of the Invention
Aqueous emulsions of organopolysiloxanes have been applied to organic fibers to improve their resistance to shrinkage and to impart a durable soft handle. U.S. Pat. No. 3,876,459 to Burrill, for example, discloses treating wool with an aqueous emulsion containing (A) a diorganopolysiloxane having a Si-bonded hydroxyl group in each terminal unit and whose organic radicals are free of basic nitrogen; (B) an organosilane containing an organic radical which contains a basic nitrogen atom or a partial hydrolyzate of such organosilane or the reaction product of component (A) with such organosilane or partial hydrolyzate thereof; and possibly (C) a silane containing 3 or 4 SiOC-bonded alkyl or alkoxyalkylene radicals as well as; (D) a condensation catalyst. Koerner et al, however, disclose in U.S. Pat. No. 4,137,179 that such emulsions are unstable.
Therefore, it is an object of the present invention to provide stable aqueous emulsions. Another object of the present invention is to provide stable aqueous emulsions which may be applied to fibers. Still another object of the present invention is to provide stable aqueous emulsions which impart a pleasant hand and high resilience to fibers. A further object of the present invention is to provide treated fibers which will have a pleasant hand and high resilience after repeated cleanings in water or organic solvents. A still further object of the present invention is to provide a method for preparing stable aqueous emulsions which may be applied to fibers.
Summary of the Invention
The foregoing objects and others which will become apparent from the following description are accomplished in accordance with this invention, generally speaking, by providing a method for preparing aqueous emulsions for impregnating organic fibers which comprises mixing (1) a diorganopolysiloxane containing a Si-bonded hydroxyl group in each terminal unit and whose organic radicals are free of basic nitrogen atoms; and (2) an organopolysiloxane which contains diorganosiloxane units in which the organic radicals are monovalent hydrocarbon radicals and at least two monovalent SiC-bonded organic radicals per molecule which contain a basic nitrogen atom with water and dispersant to form an aqueous emulsion; mixing (3) an organosilicon compound selected from an organosilane containing at least two SiOC-bonded monovalent organic radicals consisting of carbon, hydrogen and possibly oxygen and/or a partial hydrolyzate of such a silane with the aqueous emulsion and then adding to the resultant emulsion, (4) a condensation catalyst, in which component (2) is present in the emulsion in an amount of from 5 to 50 weight percent based on the weight of component (1); component (3) is present in the emulsion in an amount of from 2 to 6 weight percent based on the total weight of components (1) and (2) and component (4) is present in the emulsion in an amount of from 0.2 to 1 weight percent based on the total weight of components (1) and (2).
Description of the Invention
Diorganopolysiloxanes (1) containing a Si-bonded hydroxyl group in each terminal unit and whose organic radicals are free of basic nitrogen atoms which have been or could have been used heretofore in the preparation of aqueous emulsions for impregnating organic or inorganic fibers may be used in the method of this invention. The preferred diorganopolysiloxanes are those represented by the following general formula:
where R represents the same or different monovalent hydrocarbon radicals and n is an integer having a value such that the average viscosity of these diorganopolysiloxanes (1) is from 500 to 50,000 mPa.s at 25.degree. C. The hydrocarbon radicals represented by R preferably have from 1 to 20 carbon atoms per radical. Examples of hydrocarbon radicals which can be present in the diorganosiloxane units of diorganopolysiloxane (1) are alkyl radicals such as methyl, ethyl, n-propyl and isopropyl as well as butyl, octyl, tetradecyl and octadecyl radicals; aliphatic radicals which contain aliphatic multiple bonds such as vinyl, allyl and hexenyl radicals; cycloaliphatic hydrocarbon radicals such as cyclopentyl and cyclohexyl radicals; aromatic hydrocarbon radicals such as the phenyl and naphthyl radicals; alkaryl radicals such as the tolyl radical and aralkyl radicals such as the benzyl radical. It is preferred that at least 80 percent of the number of hydrocarbon radicals in the diorganopolysiloxane (1) be methyl radicals because of their availability.
Although only one type of diorganopolysiloxane (1) need be used, it is however possible to use a mixture of at least two different types of diorganopolysiloxanes (1).
The diorganopolysiloxane (1) can be prepared either by a polymerization which takes place at least essentially in the absence of water or it can be prepared by a polymerization in an aqueous emulsion.
The viscosity of diorganopolysiloxane (1) preferably ranges from about 2000 to 10,000 mPa.s at 25.degree. C.
Organopolysiloxane (2) contains at least two monovalent SiC-bonded organic radicals per molecule having a basic nitrogen atom and diorganosiloxane units, in which the two organic radicals are hydrocarbon radicals. The diorganosiloxane units, in which the two organic radicals are hydrocarbon radicals, may be represented by the general formula:
where R is the same as above. The examples of hydrocarbon radicals which may be present in diorganopolysiloxane (1) also applies equally to examples of hydrocarbon radicals which may be present in organopolysiloxane (2).
The siloxane units which contain SiC-bonded organic radicals having a basic nitrogen atom which are present in organopolysiloxane (2), preferably have the following general formula:
where R is the same as above; R.sup.1 represents a divalent hydrocarbon radical; R.sup.2 is hydrogen or the same or different alkyl or aminoalkyl radical; R.sup.3 is the same or different alkyl radical having from 1 to 4 carbon atoms; a is 0, 1 or 2; b is 0, 1 or 2 and the sum of a+b is at most 2.
Examples of divalent hydrocarbon radicals represented by R.sup.1 are methylene, ethylene, propylene, butylene, cyclohexylene, octadecylene, phenylene and butenylene. The n-butylene radical is preferred due to its availability.
The examples of the alkyl radicals represented by R also apply equally to the alkyl radicals represented by R.sup.2.
Examples of aminoalkyl radicals represented by R.sup.2 are those having the following formulas:
H.sub.2 N(CH.sub.2).sub.3 --
H.sub.2 N(CH.sub.2).sub.2 NH(CH.sub.2).sub.3 --
H.sub.2 N(CH.sub.2).sub.2 --
(H.sub.3 C).sub.2 N(CH.sub.2).sub.2 --
H.sub.2 N(CH.sub.2).sub.5 --
H(NHCH.sub.2 CH.sub.2).sub.3-- and
C.sub.4 H.sub.9 NHCH.sub.2 CH.sub.2 NHCH.sub.2 CH.sub.2--.
Preferably at least one R.sup.2 is hydrogen.
Examples of alkyl radicals represented by R.sup.3 are in particular methyl, ethyl and ispropyl radicals.
The organopolysiloxanes (2) used in the method of this invention preferably have a viscosity of from 20 to 20,000 mPa.s at 25.degree. C.
One type of organopolysiloxane (2) can be used; however, it is also possible to use a mixture of at least two different types of organopolysiloxanes (2).
Organosilicon compounds (3) which contain at least two SiOC-bonded monovalent organic radicals consisting of carbon, hydrogen and possible oxygen preferably have the following general formula:
where R.sup.4 represents an alkyl radical substituted by at least one amino or imino group, such as the examples described above for aminoalkyl radicals R.sup.2 or R.sup.4 is the same as R; R.sup.5 is hydrogen or an alkyl radical having from 1 to 4 carbon atoms; X is hydrogen or an alkyl radical having from 1 to 4 carbon atcms or an acyl radical having from 1 to 5 carbon atoms, preferably three carbon atoms or less; a is 0, 1 or 2 and m is 0 or an integer having a value of 1 to 30, provided that m is at least 1 when X is hydrogen or an acyl radical.
Examples of organosilicon compounds are organosilanes or partial hydrolyzates thereof, such as methyltrimethoxysilane, methyltriethoxysilane, the ethoxypolysiloxane, often referred to as "ethylsilicate 40" and which contains 40 weight percent SiO.sub.2 and silanes having the following formulas:
H.sub.2 N(CH.sub.2).sub.2 HN(CH.sub.2).sub.3 Si(OCH.sub.3).sub.3
CH.sub.3 Si(OCH.sub.2 CH.sub.2 OCH.sub.3).sub.3
CH.sub.3 O(CH.sub.2 CH.sub.2 O).sub.6 (CH.sub.2).sub.3 Si(OCH.sub.3).sub.3
H.sub.2 N(CH.sub.2).sub.2 NH(CH.sub.2).sub.3 Si(OCH.sub.3).sub.2.
One type of organosilicon compound (3) can be used; however, it is also possible to use a mixture of at least two different types of such a silanes or partial hydrolyzates thereof.
Any catalyst which has has been or could have been used heretofore in the condensation of Si-bonded condensable groups can be used as the condensation catalyst (4) in this invention. Examples of such catalysts are in particular the tin or zinc salts of carboxylic acids in which the hydrocarbon radicals can be bonded directly to the tin atom. Specific examples of such tin compounds are di-n-butyltin dilaurate, tin octoates, di-2-ethylhexyltin dilaurate, di-n-butyltin di-2-ethylhexoate, di-2-ethylhexyltin di-2-ethylhexoate and zinc octoates. Other examples of condensation catalysts (4) are alkoxy titanates such as butyl titanates and triethanolamine titanates and zirconium compounds.
One type of catalyst (4) can be used or a mixture of at least two different types of condensation catalysts (4), may be employed in this invention. An example of a mixture of condensation catalysts which may be employed are di-n-butyltin dilaurate and triethanolamine titanate.
The relative proportions of the components employed in the aqueous emulsions are critical in order to obtain a stable emulsion. The organopolysiloxane (2) having a basic nitrogen atom per molecule should be present in the emulsion in an amount of from 5 to 50 weight percent based on the weight of the diorganopolysiloxane (1) and the amount of organosilicon compound (3) ranges from 2 to 6 weight percent based on the total weight of diorganopolysiloxane (1) and organopolysiloxane (2). The condensation catalyst (4) is present in the emulsion in an amount of from 0.2 to 1 percent based on the total weight of diorganopolysiloxane (1) and organopolysiloxane (2).
When the organopolysiloxane (2), organosilicon compound (3) and condensation catalyst (4) are employed in the emulsions in amounts below the limits prescribed above, fibers impregnated with these emulsions do not have as pleasant a hand or as high a resilience as fibers impregnated with emulsions containing organopolysiloxane (2), organosilicon compound (3) and condensation catalyst (4) within the prescribed limits; even though these properties are retained by the fibers after repeated cleaning with water or organic solvent. When organosilicon compound (3) and condensation catalyst (4) are employed in the emulsions in an amount which exceeds the limits described above, the resultant emulsions are unstable. In addition, the use of more than 50 weight percent of organopolysiloxane (2), based on the weight of diorganopolysiloxane (1) is uneconomical since no additional advantages are obtained over those obtained using lower amounts.
Any dispersant which has been used or could have been used heretofore to produce aqueous emulsions of organopolysiloxanes for impregnating organic fibers may be used as dispersants in this invention.
Preferred dispersants are nonionic emulsifiers such as the polyglycol ethers of alkanols or phenol or alkylphenols such as nonylphenol polyglycol ethers, tert-butylphenol polyglycol ethers, polyoxyethylene sorbitan hexastearate, polyoxyethylene isotridecyl ethers and trimethylnonylethers of polyethylene glycol which contain 6 to 14 ethylene oxide units per molecule; polyoxyethylene sorbitan oleate having a saponification number of 102 to 108 and a hydroxyl number of 25 to 35 and dimethylpolysiloxane-ethylene oxide block copolymers.
Other examples of dispersants which can be used in the method of this invention are anionic emulsifiers such as alkylbenzenesulfonates and sodium alkylarylpolyethyleneglycol sulfonates.
Other examples of dispersants which can be used in the method of this invention are cationic emulsifiers such as tetraalkylammonium chlorides.
The dispersants are preferably used in an amount of from 3 to 20 weight percent and more preferably from 5 to 10 weight percent, based on the total weight of diorganopolysiloxanes (1), organopolysiloxane (2), organosilicon compound (3) and condensation catalyst (4).
The emulsions prepared in accordance with this invention preferably contain from 35 to 80 weight percent and more preferably from 45 to 60 weight percent of water, based on the total weight of the emulsion. When the emulsion contains a lower content of the substances other than water, the resultant emulsion may be unstable. A higher content of substances other than water, generally produces emulsions which can be handled only with difficulty because of their higher viscosity.
When the emulsions prepared in accordance with this invention are applied to organic fibers, they are preferably diluted to a content of from about 95 to 99.5 weight percent of water, based on the total weight of the emulsion.
These emulsions may be prepared in any high-speed stirring apparatus which has been used or could have been used heretofore in preparing aqueous emulsions.
In preparing the aqueous emulsions, organosilicon compound (3) is first mixed with an aqueous emulsion of diorganopolysiloxane (1) and organopolysiloxane (2), followed by the addition of the condensation catalyst (4). Diorganopolysiloxane (1) and organopolysiloxane (2) can be emulsified separately or together in water. Preferably, organosilicon compound (3) is dissolved or emulsified in water before it is mixed with an aqueous emulsion of diorganopolysiloxane (1) and organopolysiloxane (2). Likewise, the condensation catalyst (4) is preferably dissolved or dispersed in water before it is mixed with an aqueous mixture consisting of diorganopolysiloxane (1), organopolysiloxane (2) and organosilicon compound (3).
Other substances, such as textile finishing agents may also be included in the emulsions of this invention. Examples of such substances are so-called "crease-resistant finishes" such as dimethyloldihydroxyethyleneurea (DMDHEU) mixed with zinc nitrate, particularly when the fibers to be impregnated are made of cellulose or cotton or are fiber mixtures which contain cellulose or cotton fiber. Because of emulsion stability reasons, blending of the emulsions of this invention with other substances should be done only immediately before impregnating fibers with these blends.
Emulsions prepared in accordance with this invention are stable at room temperature for at least 6 months. They crosslink to form an elastcmeric film upon removal of water. The film produced from a freshly prepared emulsion does not essentially differ from the film produced from an emulsion stored at room temperature for 6 months.
All organic fibers in the form of thread, yarn, non-wovens, mats, weaves or knit textiles which heretofore could be impregnated with organosilicon compounds from an aqueous emulsion can be impregnated with the emulsions prepared in accordance with this invention. The fibers can be natural or synthetic in origin. Examples of fibers which can be impregnated with the emulsions prepared in accordance with this invention are fibers made of keratin, particularly wool, cotton, rayon, hemp, natural silk, polypropylene, polyethylene, polyester, polyurethane, polyamide, cellulose acetate and mixtures of at least two such fibers. The textiles can be present in the form of fabric webs or articles of clothing or parts of articles of clothing.
With keratin and particularly wool, shrinkage by felting can be prevented by impregnating keratin with the emulsion prepared in accordance with this invention, especially when the keratin has been pretreated with clorine, rinsed and neutralized.
An emulsion prepared in accordance with this invention can be applied to fibers in any manner which is known for impregnating organic fibers with liquid substances, for example, by immersion, coating, pouring, spraying, rolling on, pressing, knife or doctor coating or padding.
The crosslinkable organopolysiloxane is crosslinked on the fibers after the evaporation of the water. This evaporation is preferably carried out at a temperature of from 50.degree. to 180.degree. C.
The weight gain of fibers impregnated with the emulsions prepared in accordance with this invention after evaporation of the water is preferably from 0.1 to 20 weight percent and more preferably from 0.5 to 3 weight percent, based on the weight of the individual fibers prior to impregnation.
In the following examples, all parts and percentages are by weight unless otherwise specified.
A high-speed stirrer was used in the apparatus to prepare the emulsions in each of the following examples.
Example 1
(a) About 35 parts of a dimethylpolysiloxane which has a Si-bonded hydroxyl group in each terminal unit and a viscosity of 6000 mPa.s at 25.degree. C. are first mixed with 4 parts of a nonylphenol polyglycol ether which is obtained by reacting nonylphenol (1 mol) with ethylene oxide (15 mol) and then with 4 parts water.
An emulsion is prepared from the mixture thus obtained by the addition of 57 parts water.
(b) The procedure described in (a) above is repeated except that 35 parts of the product obtained from the reaction of a dimethylpolysiloxane having a Si-bonded hydroxyl group in each terminal unit and a viscosity of 100 mPa.s at 25.degree. C. and a silane having the following formula:
is substituted for the 35 parts of the dimethylpolysiloxane with a Si-bonded hydroxyl group in each terminal unit. This reaction product has an amine number (number of ml of 1N HCl required to neutralize 1 g) of 1.2 and a viscosity of 65 mPa.s at 25.degree. C.
(c) About 25 parts di-2-ethylhexyltin dilaurate are first mixed with 3 parts tert-butylphenol polyglycol ether which is obtained by reacting tert-butylphenol (1 mol) with ethylene oxide (13 mol) and 3 parts water. An emulsion is prepared from the mixture thus obtained by adding 69 parts water.
(d) About 90 parts of the emulsion whose preparation is described in (a) above are mixed with 4.5 parts of the emulsion whose preparation is described in (b) above. About 5 parts of a solution which is obtained by adding 40 parts of a silane having the following formula
to 60 parts water is added to the aqueous emulsion consisting of the emulsions (a) and (b) above. About 0.5 parts of the emulsion whose preparation is described in (c) above are mixed into the mixture thus obtained.
The emulsion thus obtained is stable even after storage for 6 months in a closed container at 40.degree. C.
A polyester knit is immersed in an aqueous emulsion prepared by mixing 30 parts of the emulsion prepared in (d) above with 970 parts by volume of water. The polyester is squeezed out to a 100 percent liquid uptake and then heated at 150.degree. C. for 10 minutes. The polyester thus obtained has a soft, pleasant and elastic hand which is still present even after 5 washings at 30.degree. C. in a household washing machine or after treating five times for 20 minutes with perchloroethylene.
Example 2
(a) About 30 parts of an 80 percent solution of zirconium octoate in white spirit (zirconium content: 18 percent) are first mixed with 3 parts of the tert-butylphenol polyglycol ether described in Example 1(c) above and 3 parts of water. An emulsion is prepared from the mixture thus obtained by the addition of 64 parts of water.
(b) About 85 parts of an emulsion prepared in accordance with Example 1(a) above are mixed with 10 parts of an emulsion prepared in accordance with Example 1(b) above. About 4 parts of a solution prepared by adding 40 parts of a silane having the following formula
to 60 parts water are added to the aqueous emulsion.
About 1 part of the emulsion prepared in (a) above is mixed into the resultant mixture.
The emulsion thus obtained is stable even after storage for 6 months in a closed container at 40.degree. C.
Example 3
(a) The procedure described in Example 1(a) is repeated except that 35 parts of the product obtained from the reaction of a dimethylpolysiloxane having a Si-bonded hydroxyl group in each terminal unit and a viscosity of 100 mPa.s at 25.degree. C. with a silane having the following formula
are substituted for the 35 parts of dimethylpolysiloxane having a Si-bonded hydroxyl group in each terminal unit. This reaction product has an amine number of 0.1 and a viscosity of 5000 mPa.s at 25.degree. C.
(b) About 50 parts of the emulsion prepared in accordance with Example 1(a) above are mixed with 10 parts of the emulsion prepared in (a) above. About 4 parts of a solution prepared by adding 40 parts of a silane having the following formula
to 60 parts water is added to the resultant aqueous emulsion.
About 1 part of the emulsion prepared in Example 2(a) above is mixed into the resultant mixture.
The emulsion thus obtained is stable even after storage for 6 months in a closed container at 40.degree. C.
A 100 percent cotton fabric is immersed in an aqueous emulsion which is prepared by mixing 40 parts of an emulsion prepared in accordance with (b) above with 100 parts of a 45 percent aqueous solution of dimethyloldihydroxyethyleneurea, 20 parts of zinc nitrate and 860 parts of water. The fabric is then squeezed out to a 100 percent liquid uptake and finally heated at 150.degree. C. for 10 minutes. The fabric treated in this manner has a soft, pleasant and elastic hand which is still present even after 5 washings at 30.degree. C. in a household washing machine or after treating with perchloroethylene five times for 20 minutes as in chemical cleaning.
Claims
What is claimed is:
1. An aqueous emulsion for impregnating organic fibers comprising in addition to water and a dispersant: (1) a diorganopolysiloxane having a Si-bonded hydroxyl group in each terminal unit, in which the organic radicals of the diorganopolysiloxane are free of basic nitrogen atoms; (2) an organopolysiloxane containing diorganosiloxane units in which the organic radicals of the diorganosiloxane are monovalent hydrocarbon radicals, and at least two monovalent SiC-bonded organic radicals per molecule having a basic nitrogen atom, in which the organopolysiloxane (2) is present in the emulsion in an amount of from 5 to 50 weight percent based on the weight of diorganopolysiloxane (1); (3) an organosilicon compound selected from the group consisting of an organosilane containing at least two SiOC-bonded monovalent organic radicals containing carbon and hydrogen or carbon, hydrogen and oxygen, partial hydrolyzates of such organosilane and mixtures thereof, in which the organosilicon compound (3) is present in the emulsion in an amount of from 2 to 6 weight percent based on the total weight of the diorganopolysiloxane (1) and organopolysiloxane (2); and (4) a condensation catalyst, which is present in the emulsion in an amount of from 0.2 to 1 weight percent based on the toatal weight of the diorganopolysiloxane (1) and organosiloxane (2), in which the emulsion is prepared by mixing the organosilicon compound (3) with an aqueous emulsion containing diorganopolysiloxane (1) and organopolysiloxane (2) and thereafter mixing the resultant emulsion with the condensation catalyst.
2. The emulsion prepared by the method of claim 1, wherein the organosilicon compound (3) is mixed with water before it is mixed with an aqueous emulsion of diorganopolysiloxane (1) and organopolysiloxane (2).
3. The emulsion prepared by the method of claim 1, wherein the condensation catalyst (4) is mixed with water before it is mixed with an aqueous emulsion containing diorganopolysiloxane (1), organopolysiloxane (2) and organosilicon compound (3).
Patent Citations (2)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3836371 | 1974-09-01 | Kokoszka | |
| US3876459 | 1975-04-01 | Burrill |