Water-Soluble Terpolymers of 2-Acrylamido-2-Methylpropane-Sulfonic Acid, Sodium Salt (AMPS), N-Vinylpyrrolidone and Acrylonitrile

A serious problem is encountered when clay-based oil well drilling fluids are subjected to conditions of high temperature and high pressure in conjunction with utilization of high calcium-containing brines which are used to prepare these drilling fluids. When these conditions exist, conventional drilling fluid polymeric additives such as acrylamide polymers, when used as stabilizers for these fluids, tend to be rendered ineffective.

Recently a partial solution to the problem has been provided by the utilization as a fluid loss additive and rheology stabilizer a terpolymer composed of:

This terpolymer, while proving to be effective as a high temperature fluid loss additive for oil well drilling fluids, has the disadvantage of using in its composition 16.0 mole % of N-methyl-N-vinyl acetamide. This renders the material expensive to use.

If it were possible to use a polymeric high temperature fluid loss additive and rheology stabilizer that was resistant to high calcium-containing brines, an improvement in the art would be afforded.

The invention comprises the utilization of terpolymers with the following composition:

As will be shown hereafter, these terpolymers provide excellent high temperature fluid loss protection to a clay-based brine prepared drilling fluid.

These terpolymers may be prepared in accordance with the following preparative technique, illustrating the preparation of the preferred terpolymer listed above:

A polymerization vessel was fitted with a stirrer, thermometer, condenser and addition port. The vessel was charged with 325 g of water, 53 g of AMPS, 21 g of a 50% solution of sodium hydroxide, 21 g of a 50% solution of sodium hydroxide, 4 g of N-vinylpyrrolidone and 7.6 g of acrylonitrile. The pH was adjusted to 8.3 and the polymerization was initiated by the sequential addition of 10 ml. of a 0.5% solution of sodium bisulfite and 10 ml. of a 0.5% solution of ammonium persulfate. After two hours reaction time, the temperature was raised to 75.degree. C. and 10 ml of a 2% solution of sodium bisulfite and 10 ml of a 2% solution of ammonium persulfate were added. The reaction was heated for one hour before cooling to room temperature. The polymer solution had a Brookfield viscosity of 2940 cps.

The amount of polymer used to stabilize clay-based drilling fluids under conditions of high temperature and pressure may vary between about 10% up to 60% by weight based on the clay present in the fluid.

The polymers may be further characterized as having a molecular weight below 1,000,000. Preferably, they have a molecular weight within the range of 10,000-500,000.

To illustrate the invention, the preferred composition shown above was tested in a high temperature, high pressure fluid loss additive test which is described in detail in the American Petroleum Institute publication, RP13B.

The particular drilling fluid tested contained 15 pounds/barrel of a pre-hydrated Bentonite drilling fluid clay and a 50% dilution of a brine known as a Williston Basin brine. This brine contained a substantial amount of calcium.

The blank test produced a filtrate of 42 ml/7.5 min.

The preferred composition of the invention was added to provide 6 pounds/barrel of active polymer. This provided an approximate dosage of 40% by weight active polymer based on active clay. At the end of 30 minutes, the fluid loss in the above described test was 22 ml.

Using the same preparative technique and test method for determining fluid loss additive effectiveness, the following additional polymers were prepared and tested: