Adhesive Coating Material

(1) Field of the Invention:

The present invention relates to an adhesive coating material for a hard tissue, which comprises a specific polymer and a specific compound in combination. More particularly, the present invention relates to an adhesive coating material for a hard tissue, which comprises (1) a polymer having an acid value of 30 to 700 and including in recurring units a hydrophobic group and two carboxyl (--COOH) groups or one carboxylic anhydride ##STR2## group bonded to the polymer, said carboxyl groups or carboxylic anhydride group being bonded to adjacent carbon atoms, and (2) an organic titanate compound.

(2) Description of the Prior Art:

Various compounds are known as adhesives having particular applicability in specific fields. Among these adhesives, especially severe requirements are imposed on dental adhesives used for bonding to hard tissues under humid condition. Since a dental adhesive is used in the oral cavity, a high adhesion strength in the humid condition is required. Furthermore, this dental adhesive should have an adhesive force to both of hard tissue and a dental resinous restorative material comprising a polymerizable monomer and at least one member selected from inorganic, organic and inorganic/organic composite fillers.

As dental adhesives, an ionomer cement comprising an aqueous solution of polyacrylic acid and inorganic oxide, and a cold-setting adhesive comprising a polymerizable monomer are widely used.

The Ionomer cement has an adhesive force to the hard tissue, but no adhesive force to a dental resinous restorative material. And the Ionomer cement is readily separated from the bonded portion since its water resistance is low.

The cold-setting adhesive comprising a polymerizable monomer hardly adheres to the hard tissue without pretreatment. Accordingly, it is necessary that the hard tissue should be treated with a highly concentrated aqueous solution of phosphoric acid to prepare a mechanical retentive surface. This method, however, is defective in that even healthy hard tissue is damaged since phosphoric acid is used at a high concentration.

Special properties are required for adhesives according to application fields thereof, and a certain adhesive usable in a certain field can seldom be used industrially in other fields. Accordingly, special adhesives are used in respective application fields, and also in the field of the dental treatment, development of an adhesive satisfying the foregoing requirements is eagerly desired.

Under the above-mentioned background, we carried out research with a view to developing a satisfactory adhesive coating material for a hard tissue, and we have now completed the present invention.

It is therefore a primary object of the present invention to provide an adhesive for a hard tissue, which can be bonded to a hard tissue directly without a pretreatment with an aqueous solution of phosphoric acid.

Another object of the present invention is to provide an adhesive which can be bonded with a sufficient adhesive force to a tooth and a dental resinous restorative material even in the oral cavity in the humid condition and which has a high water resistance.

Other objects and advantages will become apparent from the description given hereinafter.

In accordance with a fundamental aspect of the present invention, there is provided an adhesive coating material for a hard tissue, which comprises (1) a polymer having an acid value of 30 to 700 and including a hydrophobic group and two carboxyl (--COOH) groups or one carboxylic anhydride ##STR3## group bonded to the polymer, said carboxyl groups or carboxylic anhydride group being bonded to adjacent carbon atoms, and (2) an organic titanate compound.

One main component of the adhesive coating material of the present invention is a polymer including a hydrophobic group and two carboxyl groups or one carboxylic anhydride group bonded to the polymer, said carboxyl groups or carboxylic anhydride group being bonded to adjacent carbon atoms. The reason why the hydrophobic group is introduced into the polymer used in the present invention is that a sufficient water resistance is given to the adhesive coating material, a good compatibility or affinity with a resin to be bonded, for example, a dental resinous restorative material, is imparted to the adhesive coating material and a sufficient adhesion strength is obtained even in the humid condition. Furthermore, in order to attain a sufficient adhesive strength to the hard tissue even in the humid condition, it is necessary that the two carboxyl groups or one carboxylic anhydride group should be bonded to adjacent carbon atoms in the polymer to be used in the present invention. Since the two carboxyl groups or one carboxylic anhydride group forms a bridge of a high strength with the organic titanate compound used as the other component of the present invention, an especially high water resistance is given to the adhesive coating material of the present invention. Accordingly, the adhesive coating material of the present invention acts effectively as an adhesive between a hard tissue and a dental resinous restorative material such as a composite resin, especially in the humid condition. In view of the foregoing description it is most preferred that the adhesive coating material of the present invention should comprise (1) a polymer including a hydrophobic group and two carboxyl groups or one carboxylic anhydride group bonded to adjacent carbon atoms, and (2) an organic titanate compound.

It also is important that the polymer that is used in the present invention should have an acid value of 30 to 700, especially 40 to 600. In the instant specification, the acid value is defined as the number of mg of KOH necessary for neutralizing 1 g of the polymer. This acid value indicates the concentration of the carboxyl group or carboxylic anhydride group in the polymer. If the acid value is smaller than 30, the adhesiveness to the hard tissue is reduced and the number of crosslinking points to the organic titanate compound is reduced, with the result that the toughness of the resulting coating is degraded. If the acid value is larger than 700, the coating formed from the polymer is excessively hydrophilic, and the water resistance is reduced. A polymer having an acid value within the above-mentioned range is especially suitable as a dental adhesive coating material.

The kind of the hydrophobic group bonded to the polymer is not particularly critical in the present invention, and any of known hydrophobic groups may be used. As preferred examples of the hydrophobic group, there can be mentioned (1) aryl groups such as phenyl and naphthyl groups, (2) alkyl groups such as methyl, ethyl, propyl and butyl groups, (3) alkoxy groups such as ethoxy, propoxy and butoxy groups, and (4) acyloxy groups such as an acetyloxy group. These hydrophobic groups (1) through (4) may be substituted with other substituents, such as halogen atoms, e.g., chlorine, bromine, iodine and fluorine, and alkyl, alkoxy and phenoxy groups.

In many cases, the hydrophobic group is ordinarily introduced into the polymer from a starting material used for the production of the polymer, as described hereinafter. The kind of the hydrophobic group-giving starting material is not particularly critical, and a known vinyl monomer is preferably used. More specifically, there are preferably used styrene, halogenostyrene, methylstyrene, halogenomethylstyrene and vinylnaphthalene as the monomer having the hydrophobic group (1), propylene and isobutene as the monomer having the hydrophobic group (2), ethylvinyl ether and n-butyl ether as the monomer having the hydrophobic group (3) and vinyl acetate as the monomer having the hydrophobic group (4).

A monomer for introduction of the hydrophobic group, which is especially preferred in the present invention, is represented by the following general formula: ##STR4## wherein R.sup.1 stands for a hydrogen atom or an alkyl group, and R.sup.2 stands for an aryl group, an alkyl group, an alkoxy group or an acyloxy group.

In the polymer used in the present invention, it is sufficient if the carboxyl groups or carboxylic anhydride group is finally bonded to adjacent carbon atoms, irrespectively of the preparation process. Ordinarily, a polymer having two carboxyl groups or one carboxylic anhydride group bonded thereto is preferably prepared by performing homopolymerization or copolymerization by using as the starting material a vinyl compound having two carboxyl groups or one carboxylic anhydride group bonded to adjacent carbon atoms, such as maleic acid, fumaric acid, itaconic acid, maleic anhydride or itaconic anhydride. Furthermore, there is preferably adopted a process in which a vinyl monomer having a carboxylic acid ester group or carboxylic anhydride group bonded to adjacent carbon atoms, such as maleic anhydride, maleic acid monoester, maleic acid diester, fumaric acid monoester or fumaric acid diester is used as one polymerizable component and copolymerized with other copolymerizable vinyl monomer, and the carboxylic anhydride group or carboxylic acid ester group of the formed copolymer is hydrolyzed to convert all or a part of the carboxylic anhydride group or carboxylic acid ester group to a carboxyl group.

The kind of the polymer that is used in the present invention is not particularly critical, so far as it includes a hydrophobic group as mentioned above and two carboxyl groups or one carboxylic anhydride group and the two hydroxyl groups or one carboxylic anhydride group is bonded to adjacent carbon atoms. In view of the availability and the handling easiness, it is industrially preferred that a polymer having an average molecular weight of 1,000 to 100,000, especially 2,000 to 50,000, be used. The process for the preparation of this polymer is not particularly critical. From the industrial viewpoint, however, there is preferably adopted a process in which a vinyl monomer having a hydrophobic group, such as mentioned above, is copolymerized with a vinyl monomer having a carboxyl group, a carboxylic acid ester group or a carboxylic anhydride group bonded to adjacent carbon atoms and, if necessary, the obtained polymer is then hydrolyzed.

A preferred polymer comprises (A) at least one kind of recurring units represented by the following formula: ##STR5## wherein R.sup.1 stands for a hydrogen atom or an alkyl group, and R.sup.2 stands for an aryl group, an alkyl group, an alkoxy group, an acyloxy group or an alkoxycarbonyl group, and (B) at least one kind of monomeric units represented by the following formula: ##STR6## wherein R.sup.3 stands for a hydrogen atom or a carboxymethyl group, n and m are numbers of zero or 1, with the proviso that when n is zero, m is 1 and R.sup.3 is a hydrogen atom and when n is 1, m is zero and R.sup.3 is a carboxymethyl group, and the two carboxyl groups may form a carboxylic acid anhydride group.

The above-mentioned copolymerization is not particularly critical. Ordinarily, however, there is preferably adopted a polymerization process in which a polymerization initiator described below is used. More specifically, there is preferably adopted a radical polymerization process using an organic peroxide such as benzoyl peroxide or lauroyl peroxide, an azo compound such as azobisisobutyronitrile, an organic metal compound such as tributyl boron or a redox type initiator.

In the above-mentioned polymer, it is preferred that the hydrophobic group be contained in an amount of 0.7 to 9.0 moles per mole of the two carboxylic groups or the one carboxylic anhydride group. If the content of the hydrophobic group is higher than 9.0 moles, no satisfactory adhesive force to a hard tissue can be obtained. The reason is not sufficiently elucidated, but it is presumed that since the hydrophobic characteristics of the copolymer are increased, the affinity with the hard tissue will be reduced. If the hydrophobic group is contained in the polymer in an amount smaller than 0.7 mole, there is not a suitable process for imparting a carboxyl group or carboxylic anhydride group to this copolymer, and therefore, the production of this copolymer is difficult and the water resistance of an adhesive comprising this polymer is not sufficient. As is apparent from the foregoing description, the content of the hydrophobic group in the polymer used in the present invention is very important.

The above-mentioned process in which the carboxylic acid ester group or carboxylic anhydride group is hydrolyzed is not particularly critical. Ordinarily, there is preferably adopted a process in which a copolymer comprising maleic anhydride, maleic acid diester, fumaric acid diester or itaconic acid diester is dissolved in an organic solvent, water and a small amount of an alkaline or acid component as a hydrolysis promotor are added to the solvent and the reaction is carried out at room temperature or under heating.

An organic titanate compound is used as still another component of the adhesive coating material of the present invention. The kind of the organic titanate compound is not particularly critical, and any of known organic titanate compounds can be used. For example, there can be mentioned tetra-isopropyl titanate, tetra-n-butyl titanate, tetrakis(2-ethylhexyl) titanate, tetrastearyl titanate, di-iso-propoxy-bis(acetylacetone) titanate, di-n-butoxybis(triethanolamine) titanate, dihydroxy-bis(lactic acid) titanate, tetraoctylene glycol titanate, tri-n-butoxymonostearyl titanate, isopropyltri-iso-stearoyl titanate, isopropyltridencybenzene-sulfonyl titanate, isopropyl-tris(dioctyl pyrophosphate) titanate, tetra-iso-propyl-bis(dioctyl phosphite) titanate, tetraoctyl-bis(ditridecyl phosphite) titanate, tetra-(2,2-diallyloxymethyl-1-butyl)-bis-(ditridecyl phosphite) titanate, bis(dioctyl pyrophosphate)oxyacetate titanate and bis(dioctyl pyrophosphate)ethylene titanate. These organic titanate compounds may be used singly or in the form of mixtures of two or more of them. Moreover, polymers of these titanates may be used.

In the present invention, an organic titanate represented by the following formula: ##STR7## wherein R.sup.4 stands for an alkyl group and p is a number of from 0 to 20, especially a tetraalkyl titanate, is preferably used as the organic titanate compound.

The adhesive coating material of the present invention comprises the above-mentioned polymer, and an organic titanate compound as the constituent components. The mixing ratio of these main components is not particularly critical, so far as the intended adhesive effect is attained. It is preferred that the organic titanate compound be used in an amount of 0.02 to 2 moles per mole of the unit having the bonded carboxyl group or carboxylic anhydride group in the polymer.

In the case where the organic titanate compound is used as one component of the adhesive coating material of the present invention, in order to use the adhesive coating material in a more stable state, it is preferred that a stabilizer for the organic titanate compound be used. Especially in the case where a solvent is used when the adhesive coating material of the present invention is actually applied, it is often preferred that water contained in the solvent be not removed and a stabilizer for the organic titanate compound be used. An appropriate stabilizer is selected and used according to the application mode of the adhesive coating material of the present invention. For example, when an o-alkoxybenzoic acid such as o-methoxybenzoic acid, o-ethoxybenzoic acid or o-propoxybenzoic acid, or a .beta.-hydroxycarboxylic acid such as hydroacrylic acid, .beta.-hydroxybutyric acid or .beta.-hydroxyisovaleric acid, is used as the stabilizer, a one-pack type product comprising a solvent solution of the above-mentioned polymer and organic titanate compound in one packing vessel can be provided. When an .beta.-hydroxycarboxylic acid such as lactic acid, .alpha.-hydroxy-n-butyric acid or mandelic acid, a .beta.-hydroxyalkyl acrylate or methacrylate such as .beta.-hydroxyethyl methacrylate, .beta.-hydroxypropyl acrylate or glycerin dimethacrylate, a catechol derivative such as catechol, guaiacol or eugenol, a proline derivative such as proline, 4-methylene-proline or 4-methylproline, or a cyclic ester such as .beta.-butyrolactone, .gamma.-butyrolactone or .beta.-caprolactone, is used as the stabilizer for the organic titanate compound, the adhesive coating material of the present invention is applied in the form of a two-pack type product in which a solvent solution of the above-mentioned polymer and a solvent solution of the organic titanate compound and the stabilizer are contained in different vessels and both the solutions are mixed together at the time of application. The kind of the solvent to be used for the one-pack type or two-pack type product is not particularly critical, and an appropriate solvent is selected among known solvents. Ordinarily, there are preferably used alcohols such as ethyl alcohol and isopropyl alcohol, esters such as ethyl acetate, and dioxane and tetrahydrofuran. The amount added of the stabilizer for the organic titanate compound differs according to the kind of the stabilizer and it is not sweepingly determined. However, it is ordinarily preferred that the stabilizer be used in an amount of 0.1 to 4 moles, especially 0.5 to 2 moles, per mole of the organic titanate compound. The stabilizer may be mixed with the organic titanate compound in advance or it may be added to the organic titanate compound together with other ingredients.

As is apparent from the foregoing description, the adhesive coating material of the present invention has a very high adhesiveness to a hard tissue and a synthetic resin, and this adhesiveness is excellent even in the humid condition. Accordingly, the adhesive coating material of the present invention can be used especially advantageously as a dental restorative material. By the term "dental restorative material" is meant a material which is used for remedy and restoration of a tooth and is coated on the surface of the tooth or the surface of the cavity formed on the tooth, and this is the most important use for the adhesive coating material of the present invention. As the dental restorative material, there can be mentioned, for example, a tooth adhesive, a protective lining material for the dental pulp and a border sealer for a tooth and a restorative material.

An embodiment where the adhesive coating material of the present invention is used as a dental restorative material will now be described.

In the conventional method of remedy and restoration of teeth, when a filler such as a composite restorative resin is filled in a cavity of a tooth, an adhesive is used for bonding the restorative material to the hard tissue. However, since a conventional adhesive has no substantial adhesiveness to the hard tissue, it is necessary to treat the hard tissue in advance with an aqueous solution of phosphoric acid to prepare a mechanical retentive surface. This method, however, is defective in that since an aqueous solution of phosphoric acid having a high concentration is used, even the healthy dentin is damaged. Especially when the dentin is etched, attainment of any substantial adhesive force cannot be expected and it is anticipated that even the pulp will be influenced by the aqueous solution of phosphoric acid introduced through ductules of the dentin. Furthermore, in the method described before, since a residual monomer is inevitably left, there is a risk of damage of the pulp by this monomer.

In contrast, when the adhesive coating material of the present invention is used, since the pretreatment with an aqueous solution of phosphoric acid is not necessary and the adhesive coating material can directly be bonded to the dentin, there is no risk of damage of the pulp by a residual monomer.

A lining material of the calcium hydroxide type or a cement has heretofore been used as the protecting lining material for the pulp. This lining material is used for protecting the dentin from the phosphoric acid etching conducted at the step of filling a material such as a restorative composite resin. However, if the conventional lining material is used, increase of the thickness of the coating cannot be avoided, and the conventional lining material has no adhesive force to a filler. Accordingly, the conventional lining material can hardly be used for filling of a shallow cavity in a tooth. In contrast, when the adhesive coating material of the present invention is dissolved in an organic solvent and is used as the lining material, the dentin can be protected from the phosphoric acid etching even though the formed coating layer is very thin, and furthermore, the material exerts an excellent function of being bonded to a restorative material.

A zinc phosphate cement which is often used for bonding a metal to the hard tissue involves a risk of damage of the pulp because it contains a large amount of phosphoric acid. Therefore, the treatment with this cement inherently includes use of a lining material for protection of the dentin. However, in case of the conventional lining material providing a thick coating layer, the compressive strength of the coating material is insufficient and the conventional lining material cannot be used for this purpose. When the adhesive coating material is used as a lining material of the above-mentioned type, since the coating layer is very thin, a high compressive strength is not necessary for the coating layer, and moreover, this thin coating layer does not allow permeation of phosphoric acid. Accordingly, the adhesive coating material exerts ideal effects.

As the third function of the adhesive coating material, there can be mentioned the improvement of a border sealing property.

As the known substance expected to exert this function, there can be mentioned, for example, a solution of a resin such as Copalite (tradename) in an organic solvent which is used for filling of amalgam. Indeed, this material provides a thin coating layer, but the material has no adhesive force to the dentin or amalgam, and no substantial border sealing effect can be attained. In contrast, if the adhesive coating material of the present invention is used as a border sealer, a high border sealing effect can be attained. In view of the fact that the adhesive coating material of the present invention can be bonded to the dentin but cannot be bonded to amalgam, it is considered that the above function is due to properties other than the adhesiveness, for example, the close adhesion and hydrophobic property.

When the adhesive coating material of the present invention is used for the filling operations other than the amalgam filling, for example, the restorative composite resin filling, the cement filling and the rubber capping, the border sealing effect can be improved.

The adhesive coating material of the present invention can be applied to uses other than the above-mentioned uses. For example, when it is intended to remove the material filled in the cavity of a tooth or to restore a wedge-shaped defect on the neck of the tooth, if the adhesive coating material is coated, it can effectively act as an insulating material to external stimulant.

The functions of the adhesive coating material of the present invention as the dental adhesive, the protective lining material for the pulp and the border sealer have independently been described. Since the adhesive coating material of the present invention has these functions in combination, if the coating material of the present invention is applied to the treatment of one case, all of these functions can be exerted at one time. According to the conventional technique, a plurality of materials should be used in combination for the treatment of one case, and hence, the operation becomes complicated, and the functions of the respective materials are degraded of the combined application of the materials. If this fact is taken into consideration, it will readily be understood that the adhesive coating material of the present invention is very valuable as a dental restorative material.

When the adhesive coating material of the present invention is used as a dental restorative material, it is important that the polymer used as one component should have a carboxyl group or carboxylic anhydride group in addition to the hydrophobic group, and because of the presence of the carboxyl group or carboxylic acid anhydride group, the function as the dental restorative material is further improved. Namely, the water resistance is improved so that the above function can sufficiently be exerted even under the severe condition in the oral cavity, that is, 100% relative humidity. When the adhesive coating material is used as an adhesive for bonding a composite restorative resin to the dentin, since the carboxyl group or carboxylic anhydride group has an affinity with the dentin and the hydrophobic group has an affinity with the composite restorative resin, the adhesive force is highly improved over adhesive forces attainable by conventional adhesives.

The present invention will now be described in detail with reference to the following Examples that by no means limit the scope of the invention.

A 500 ml-capacity glass separable flask was charged with 200 ml of cyclohexane, and 5.2 g of styrene, 4.9 g of maleic anhydride and 0.05 g of benzoyl peroxide (hereinafter referred to as "BPO") were added and the mixture was sufficiently stirred.

Then, the pressure in the vessel was reduced and the atmosphere was replaced with nitrogen, and the mixture was heated at 80.degree. C. with stirring for 4 hours to effect polymerization. The reaction mixture was cooled to room temperature and the formed precipitate was recovered by filtration. The obtained solid was sufficiently washed with 300 ml of benzene and dried to obtain 8.7 g of a white polymer. When the composition of the formed copolymer was determined by the elementary analysis, it was found that the copolymer comprised 48.4 mole % of styrene and 51.6 mole % of maleic anhydride.

Then, the product was dissolved in 80 ml of dioxane, and the solution was charged into a 500 ml-capacity flask and 100 ml of an aqueous solution of potassium hydroxide having a concentration of 5% by weight was added to the solution with sufficient stirring. Reaction was carried out at room temperature for 10 hours. Then, concentrated hydrochloric acid was added to the reaction mixture to effect neutralization, and an excessive amount of hydrochloric acid was further added to obtain a white solid precipitate. The solid was recovered by filtration and it was washed with water repeatedly until the solid became neutral, and the solid was dried to obtain 8.0 g of a copolymer. When the product was subjected to the infrared absorption spectrum analysis, it was found that characteristic absorptions attributed to the carbonyl group of maleic anhydride at 1850 cm.sup.-1 and 1775 cm.sup.-1 completely disappeared and a characteristic absorption attributed to the carbonyl group of maleic acid newly appeared at 1720 cm.sup.-1. Thus, it was confirmed that the hydrolysis reaction was advanced substantially quantitatively. Namely, it was confirmed that the obtained white solid was a copolymer comprising 48.4 mole % of styrene and 51.6 mole % of maleic acid. Incidentally, the acid value of the polymer was 370.

A solution of 10 g of a commercially available styrene-maleic anhydride copolymer having a molecular weight of 50,000 (supplied by Monsanto Co.) in 200 ml of dioxane was charged in a 500 ml-capacity flask, and 10 g of distilled water was added to the solution with sufficient stirring and the mixture was heated at 100.degree. C. for 4 hours with stirring. The solution was cooled to room temperature and thown into 2 liters of distilled water to precipitate a white cotton-like polymer. When the polymer was washed with water and dried, 9.8 g of a white solid was obtained. From the results of the elementary analysis and infrared absorption spectrum analysis, it was confirmed that a styrene-maleic acid copolymer was obtained. Incidentally, the acid value of the polymer was 367.

In the same manner as described in Production Example 1, two commercially available styrene-maleic anhydride copolymers (supplied by Arco Chemical Co.) differing in their composition as shown in Table 1 were hydrolyzed. From the results of the elementary analysis of the starting copolymers and the results of the infrared absorption spectrum analysis of the hydrolyzed copolymers, it was confirmed that styrene-maleic acid copolymers having compositions shown in Table 1 were obtained. The molecular weights of the copolymers were 1,700 and 1,900, and the acid values of the copolymers were 251 and 184.

A pressure glass vessel having an inner capacity of 300 ml was charged with 50 ml of benzene containing 35 g of maleic anhydride and 90 mg of azobisisobutyronitrile (hereinafter referred to as "AIBN"), and the inner atmosphere was replaced by nitrogen under reduced pressure while cooling in a dry ice-methanol bath. Then, 12 g of propylene was introduced into the reaction vessel by distillation through a liquefaction meter, and the mixture was stirred at 60.degree. C. for 36 hours to effect copolymerization. After the termination of the polymerization, the content was thrown into a large amount of anhydrous ether to precipitate the formed copolymer. The polymer was sufficiently washed by decantation and promptly dried in a reduced pressure dryer. The yield was 60%. From the results of the elementary analysis, it was found that the copolymer comprised 55.6 mole % of maleic anhydride and 44.4 mole % of propylene.

Then, the product was hydrolyzed in the same manner as described in Production Example 1 to obtain 24.2 g of a propylene-maleic acid copolymer. From the results of the infrared absorption spectrum analysis, it was confirmed that the maleic anhydride group in the starting copolymer was converted to maleic acid substantially quantitatively. Incidentally, the acid value of the polymer was 508.

A pressure glass vessel having an inner capacity of 300 ml was charged with 50 ml of benzene containing 35.7 g of maleic anhydride and 90 mg of AIBN, and 12.5 g of isobutene was introduced into the reaction vessel by distillation through a liquefaction meter and copolymerization was carried out at 60.degree. C. for 15 minutes. After the termination of the polymerization, the content was thrown into a large amount of anhydrous ether to precipitate the formed copolymer, and the supernatant was discarded by decantation and the residue was sufficiently washed with anhydrous ether and then dried under reduced pressure. The yield was 43.3%. From the results of the elementary analysis, it was found that the product was a copolymer comprising 47.1 mole % of isobutene and 52.9 mole % of maleic anhydride.

In the same manner as described in Production Example 1, the product was hydrolyzed to obtain 20.5 g of an isobutene-maleic acid copolymer. From the results of the infrared absorption spectrum analysis of this copolymer, it was confirmed that the maleic anhydride group in the starting copolymer was converted to maleic acid substantially quantitatively. Incidentally, the acid value of this copolymer was 470.

A 500 ml-capacity glass separable flask was charged with 200 ml of benzene, and 5.3 g of n-butylvinyl ether, 4.9 g of maleic anhydride and 0.05 g of AIBN were added and the mixture was sufficiently stirred.

Then, the pressure in the vessel was reduced and the inner atmosphere was replaced by nitrogen, and heat polymerization was carried out at 60.degree. C. for 6 hours and the formed precipitate was recovered by filtration. From the results of the elementary analysis, it was found that the formed copolymer comprised 49.8 mole % of n-butylvinyl ether and 50.2 mole % of maleic anhydride. Then, the product was dissolved in 200 ml of dioxane and the solution was charged in a 500 ml-capacity flask, and 10 g of distilled water was added under sufficient stirring and the mixture was heated and stirred at 60.degree. C. for 2 hours. The obtained polymer solution was solidified by dry ice-methanol and then freeze-dried to obtain 10.1 g of a white solid. From the results of the infrared absorption spectrum analysis of the product, it was confirmed that the majority of the maleic anhydride group in the starting copolymer was converted to a maleic acid group. Incidentally, the acid value of the polymer was 375.

A commercially available n-octadecylvinyl ethermaleic anhydride copolymer (supplied by Polysciences, Inc.) was hydrolyzed in the same manner as described in Production Example 2. From the results of the elementary nalysis of the starting copolymer and the results of the infrared absorption spectrum analysis of the hydrolyzed copolymer, it was confirmed that the product was an n-octadecylvinyl ether-maleic acid copolymer having an acid value of 196.

In 200 g of dioxane were dissolved 30 g of itaconic acid and 20 g of styrene, and BPO was added to the solution in an amount of 0.1% based on the monomers and polymerization was carried out at 10.degree. C. for 5 hours. The reaction mixture was thrown in 1 lter of hexane, and the precipitate was recovered by filtration, dried and washed with distilled water to remove unreacted itaconic acid. The yield was 4.2%. From the results of the elementary analysis, it was found that the product was a copolymer comprising 49.0 mole % of itaconic acid and 51.0 mole % of styrene. The acid value of the polymer was 340.

Styrene was copolymerized with diethyl fumarate at 60.degree. C. for 20 hours by using AIBN as the initiator. From the results of the elementary analysis of the formed polymer, it was found that the formed polymer was a copolymer comprising 56.5 mole % of styrene and 43.5 mole % of diethyl fumarate. Then, 0.5 g of the polymer was charged in an Erlenmeyer flask having an inner capacity of 100 ml, and 30 ml of concentrated sulfuric acid was added and the mixture was allowed to stand still. In 2 days, the polymer was completely dissolved and a yellow solution was obtained. When the solution was poured into a large amount of ice water, a styrene-fumaric acid copolymer was precipitated. The precipitate was recovered by filtration, washed sufficiently with water repeatedly and dried to obtain 0.45 g of a solid. The acid value of the polymer was 93.

A commercially available vinyl acetate-maleic anhydride copolymer (supplied by Polysciences, Inc.) was hydrolyzed in the same manner as described in Production Example 7. From the results of the elementary analysis of the starting copolymer and the results of the infrared absorption spectrum analysis of the hydrolyzed copolymer, it was found that the product was a vinyl acetate-maleic acid copolymer. The acid value of the polymer was 399.

p-Chlorostyrene was copolymerized with maleic anhydride by using BPO as the initiator under the same conditions as adopted in Production Example 1. From the results of the elementary analysis of the obtained copolymer, it was found that the obtained copolymer comprised 47.9 mole % of p-chlorostyrene and 52.1 mole % of maleic anhydride. The product was hydrolyzed in the same manner as described in Production Example 7. From the results of the elementary analysis of the formed polymer and the results of the infrared absorption spectrum analysis of the hydrolyzed polymer, it was confirmed that the product was a vinyl acetate-maleic acid copolymer. The acid value of this polymer was 318.

p-Chloromethylstyrene was copolymerized with maleic anhydride by using BPO as the initiator under the same conditions as adopted in Production Example 1. From the results of the elementary analysis of the obtained copolymer, it was found that the formed copolymer comprised 48.9 mole % of p-chloromethylstyrene and 51.1 mole % of maleic anhydride. The product was hydrolyzed in the same manner as described in Production Example 7. From the results of the elementary analysis of the formed copolymer and the results of the infrared absorption spectrum analysis of the hydrolyzed copolymer, it was confirmed that the product was a p-chloromethylstyrenemaleic acid copolymer. The acid value of this polymer was 301.

(i) Liquids (I) and (II) shown in Table 2 were prepared by using the copolymer obtained in Production Example 1 and an organic titanate shown in Table 2. In Table 2, the amount used of the copolymer (parts by weight per 90 parts by weight of ethanol) and the amount used of the organic titanate (parts by weight per 100 parts by weight of ethanol) are shown. The adhesive strength of an adhesive coating material formed from these liquids (I) and (II) was determined according to the following procedures.

Pastes (A) and (B) were prepared according to the following recipes.

The lip side surface of a freshly extracted bovine tooth was polished by emery paper (#320) to expose a smooth dentin, and nitrogen gas was blown to dry the surface. Then, a plate-like wax having a through hole having a diameter of 4 mm was attached to the dried surface by using a double-coated tape. Then, the adhesive liquids (I) and (II) were mixed at a ratio of 1:1 and the mixture was coated on the dentin surface surrounded by the plate-like wax, and nitrogen gas was blown to sweep off the excessive adhesive. Then, the pastes (A) and (B) were mixed at a ratio of 1:1 and the mixture was filled onto the adhesive coating. After standing for 1 hour, the plate-like wax was removed, and the treated tooth was dipped in water maintained at 37.degree. C. for 24 hours and the tensile strength was measured at a pulling speed of 10 mm/min by using Tensilon supplied by Toyo-Baldwin. The obtained results are shown in Table 2.

(ii) In order to confirm that the coating layer of the adhesive coating material of the present invention has an insulating effect to an aqueous solution of phosphoric acid, the following test was carried out.

A membrane filter having a pore size of 3 microns was dipped in distilled water for 1 hour, and the membrane filter was taken out and was dried by blowing nitrogen gas to the surface of the membrane filter. Then, the dried surface of the membrane filter was coated with a commercially available insulating material (lining material) (Copalite or Dycal, each being a tradename) or the adhesive coating material used in Example 1. Then, nitrogen gas was blown to the surface again to remove the solvent. One drop of a 37% aqueous solution of orthophosphoric acid was applied to the surface of the insulating coating, and the coated membrane filter was allowed to stand still.

In order to detect phosphoric acid permeating through the insulating layer, a pH test paper was placed below the membrane filter and the insulating property was evaluated based on the permeation time, namely the time at which the color of the pH test paper was changed.

When the insulating material was not used, the permeation time was 15 seconds. When Copalite (tradename) was used, the permeation time was 1 minute and 10 seconds, and when Dycal (tradename) was used, the permeation time was more than 10 minutes. In contrast, when adhesive coating materials of the present invention (Runs Nos. 1 through 5 in Table 2) were used, the permeation time of the aqueous solution of phosphoric acid was more than 10 minutes in each case.

The procedures of Example 1 (Run No. 1 in Table 2) were repeated in the same manner except that a stabilizer shown in Table 6 was added to the organic titanate used in Example 1 (Run No. 1 in Table 2). The obtained results are shown in Table 6. The storage stability of the liquid (II) was evaluated by checking the transparency and the change of the viscosity in the solution. Incidentally, it was found that when both the liquids (I) and (II) were mixed, gelation or precipitation was caused within several days in each run.

The liquids (I) and (II) were prepared in the same manner as in Example 1 (Run No. 2 in Table 2) except that the organic titanate used in Example 1 (Run No. 2 in Table 2) and a stabilizer shown in Table 4 were used. Then, the liquids (I) and (II) were mixed. Each of the resulting solutions having a composition shown in Table 4 was kept transparent and no change of the viscosity was caused for more than 1 , week. After passage of 1 week from the time of mixing the liquids (I) and (II), the bonding test was carried out in the same manner as in Example 2. The storage stability in the one-pack state was subsequently observed. The obtained results are shown in Table 4.

The following test was carried out so as to examine the border sealing property of each composition.

A cavity having a diameter of 3 mm and a depth of 2 mm was formed on the lip side surface of an extracted human tooth. Adhesive coating materials of Example 3 (Runs Nos. 1 to 6 in Table 4) and Copalite as the conventional material were used as the sample. The sample was thinly coated on the cavity, and then, a cement or amalgam was filled in the cavity. After passage of 1 hour, the tooth was stored in water maintained at 37.degree. C., and after passage of 1 day, the tooth was dipped in an aqueous solution of Fuchsine maintained at 4.degree. C. for 1 minute and then in an aqueous solution of Fuchsine maintained at 60.degree. C. for 1 minute and this operation was repeated 60 times, whereby the percolation test was carried out. The border sealing effect was evaluated by cutting the tooth at the center and checking whether the dye (Fuchsine) had intruded between the cavity and the filler. In each run, five specimens were used so as to confirm the reproducibility. When the amalgam or cement was directly filled without using any material, or when Copalite was coated and the amalgam or cement was then filled, intrusion of the dye was observed in each specimen. In contrast, in case of each of the adhesive coating materials of Example 3 (Runs Nos. 1 through 6 in Table 4), intrusion of the dye was not observed and good results were obtained.

The procedures of Example 3 (Run No. 2 in Table 4) were repeated in the same manner except that a polymer shown in Table 5 was used instead of the polymer used in Example 3 (Run No. 2 in Table 4). The obtained results are shown in Table 5.

By using liquids (I) and (II) for the first treatment, shown in Table 6, an untreated dentin of a bovine tooth was subjected to the coating treatment in the same manner as described in Example 1. Then, the coated surface was further coated with a liquid mixture of liquids (I') and (II') for the second treatment, shown in Table 6. Namely, liquid (I') comprising 10 parts by weight of a commercially available styrene/maleic anhydride copolymer (SMA 1000), 90 parts by weight of 2-hydroxyethyl methacrylate and 1 part by weight of BPO was mixed with liquid (II') comprising 1.5 parts by weight of DEPT, 3.0 parts by weight of sodium p-toluene-sulfinate and 100 parts by weight of ethanol at a ratio of 1:1, and the resulting liquid mixture was coated on the coated surface of the tooth. The adhesive test was carried out in the same manner as described in Example 1. The obtained results are shown in Table 6.