Triazole Electroactive Polymers

This invention relates to electroactive organic polymeric materials. More specifically, this invention relates to associating electroactivating agents known in the art as dopants with an organic polymer.

Recently, research has been conducted into organic polymeric materials in order to modify their room temperature electrical conductivity by reacting them with electron donor or acceptor molecules. The electron donor or acceptor molecules, generally known in the art as n- and p-type dopants respectively, can transform the organic polymeric materials so that these modified organic polymeric materials exhibit semiconducting and metallic room temperature electrical conductivity. Polyacetylene is an example of an organic polymeric material whose room temperature electrical conductivity can be modified over several orders of magnitude above its insulator state, by the incorporation of dopant molecules, A. J. Heeger et al, U.S. Pat. No. 4,222,903, said patent incorporated herein by reference. Other examples of organic polymeric materials whose room temperature electrical conductivity can be enhanced by several orders of magnitude over their insulator state by means of incorporation of dopant molecules are poly-p-phenylene, polypyrrole, poly-1,6 heptadiyne, and polyphenylene vinylene. However, all of the above recited examples are of organic polymeric materials which are completely insoluble or infusable and hence are completely intractable.

Other examples of organic polymers whose room temperature electrical conductivity can be modified with the aid of dopants are polyphenylene sulfide and poly-m-phenylene. However, the above recited materials though being tractable in their original virgin state, undergo irreversible chemistry when reacted with dopants which modify their room temperature electrical conductivity. This irreversible chemistry imparts upon these dopant modified organic polymeric materials a state of intractability. Upon removal of the doping agents, these materials do not revert to the chemical structure which they originally exhibited prior to being modified by the dopants. The inorganic material polysulfur nitride is also considered a polymeric conductor. As with the previously recited polymeric materials, polysulfur nitride is also completely intractable.

The synthesis of poly(1,3,4-oxadiazole-2,5-diylvinylene) and poly(1,3,4-oxadiazole-2,5-diyl-ethynylene) is described by I. Schopov et al. in Makromolecular Chemie, vol. 179, No. 1, pp. 63-71 (1978). These undoped oxadiazole polymers are shown by Schopov to exhibit an electrical conductivity characteristic of insulators.

For use in a wide variety of electronic device applications, it is highly desirable to have available organic polymeric electrically conducting materials having a preselected room temperature conductivity which can be varied over a broad range. This range should preferably extend from the insulator state of the unmodified organic polymeric material through the semiconducting regime and extending into the highly conducting metallic state. It is also desirable that these organic polymeric electrically conducting materials should be tractable and hence processable so that useful articles of any desired shape and size can be fabricated. Tractable organic polymers are those which can be readily shaped, formed, molded, pressed, cast, etc., into desired articles from the liquid state, i.e. either from the melt, fluid glassy state, or from solution after the completion of the polymerization reaction of the organic polymeric material.

We have invented an electroactive polymeric material comprising a dopant modified organic polymer whose room temperature electrical conductivity is controlled in a highly selective and reversible manner. Electroactive polymer is defined as a polymer having a conductivity which has been modified with electron acceptor or donor dopants to be greater than the conductivity of the virgin state of the polymer. The electroactive organic polymeric material is fabricated from a virgin polymer, which in itself is completely tractable and processable and which exhibits excellent mechanical and thermal properties as well as being highly stable to oxidative degradation, by modifying the polymer with a conductivity modifier, i.e. electron donor dopants or electron acceptor dopants. The electroactive organic polymeric material is comprised of recurring units of an N-substituted 1,3,4-triazole ring system and a conductivity modifier. More specifically, the electroactive polymer is a charged polymer backbone incorporating a sufficient concentration of charge-compensating ionic dopants, i.e., ions of opposite charge to the charge of the polymer backbone. A sufficient concentration of ionic dopants is defined as that concentration which, when associated with the polymer, effects a significant increase in the polymer conductivity, i.e., on the order of about 10% or greater. The recurring units are diradicals. The diradicals are directly linked to one another, or may be connected to one another via connecting units. A "connecting unit" is defined as any atom or group of atoms which can link the hereinabove diradicals together into a polymer chain.

Among other factors, the present invention is based on our discovery that N-substituted 1,3,4-triazole polymers can be effectively doped with conductivity modifiers to provide electroactive polymers having an electrical conductivity several orders of magnitude greater than the conductivity of the undoped virgin polymers. In addition, the electroactive polymers of the invention are highly tractable and processable and therefore overcome the disadvantages of prior art materials.

An n-type electroactive organic polymer is obtained by reacting the virgin polymer with reducing or electron donor dopants. Electron donor dopants induce n-type conductivity in the polymer by donating an electron to the polymer and reducing same to a polyanion and the dopant is oxidized to a cation. Similarly, a p-type electroactive organic polymer is obtained by reacting the virgin polymer with oxidizing electron acceptor dopants. Electron acceptor dopants induce p-type conductivity in the polymer by oxidizing the polymer to a polycation and the dopant is reduced to an anion. The desired value of the room temperature electrical conductivity of the dopant modified electroactive organic polymer is preselected by controlling the level of incorporation of the dopants into the virgin polymer. Alternatively, the desired value of the room temperature electrical conductivity of the dopant modified electroactive organic polymer is preselected by controlling the length of the reaction time between the virgin polymer and dopants. Furthermore, the highly selective and reversible modification of the room temperature electrical conductivity of the virgin polymer can proceed by either chemical or electrochemical means. The highly selective and reversible modification of the electrical conductivity of the dopant containing organic polymeric material together with the tractability and processability of the virgin polymer is highly desirable in that the fabrication of useful articles and devices such as primary and secondary batteries, photovoltaic devices, Schottky type devices can be accomplished. Furthermore, the materials described in this invention can be utilized as active components in such devices and articles as electrochromic displays and photolithographic processes.

Electroactive organic polymers are tractable and processable virgin polymers consisting of recurring units of an N-substituted 1,3,4-triazole ring system modified by suitable conductivity modifiers. The polymers are composed of repeating diradical units derived from N-substituted 1,3,4-triazole ring systems wherein the triazole is substituted on the 1-nitrogen atom with lower alkyl of 1-6 carbon atoms or phenyl. A diradical is defined as a molecule that has two unsatisfied positions available for linking into the polymer chain. Optionally, the diradicals are separated in the polymer chain by connecting units.

Suitable examples of N-substituted 1,3,4-triazole recurring units are 1-phenyl-1,3,4-triazole, 1-methyl-1,3,4-triazole, 1-ethyl-1,3,4,-triazole, 1-propyl-1,3,4-triazole, 1-butyl-1,3,4-triazole, 1-pentyl-1,3,4-triazole, 1-hexyl-1,3,4-triazole, and mixtures thereof. The recurring units can be interspersed with one or more connecting units such as O, S, aryl, substituted aryl, alkenyl, thioalkenyl, thioaryl, and the like. Preferred connecting units are 1,4-phenylene, 4,4'-biphenylene, --CH.dbd.CH--, and --C.tbd.C--. A particularly preferred connecting unit is 1,4-phenylene. The connecting units can be the same or different between adjacent recurring units in the polymer chain.

The polymer can be a homopolymer of the triazole diradicals or a copolymer of the diradicals. A homopolymer is defined as a polymer comprising the same recurring diradical. A copolymer is defined as a polymer comprising different diradicals. In addition, the polymer is a copolymer if the same or different recurring diradicals are interspersed with connecting units.

The polymer is rendered electroactive by incorporating into the virgin polymer a conductivity modifier. More specifically, the polymer is rendered electroactive by adding electrons to (reducing) or removing electrons from (oxidizing) the virgin polymer backbone. This can be accomplished by incorporating into the virgin polymer a conductivity modifier which is either an electron donor dopant or an electron acceptor dopant. An electron donor dopant donates an electron to the polymer, the polymer becoming reduced to a polyanion and the dopant becoming oxidized to a cation. An electron acceptor dopant removes an electron from the polymer, the polymer becoming oxidized to a polycation and the dopant becoming reduced to an anion. Alternatively, the polymer can be rendered electroactive by electrochemical oxidation or reduction. In this case an electron is removed from or added to the polymer from an electrode, and charge-compensating anions or cations, respectively, are incorporated into the polymer from the supporting electrolyte solution.

In both cases the resulting electroactive polymer consists of a charged polymer backbone incorporating charge-compensating ionic dopants. A suitable positively charged compensating dopant can be a cation such as the alkali metal ions, alkali earth metal ions, Group III metal ions, strong Lewis acids, and organic cations such as ##STR1## where R.sup.xi is a straight- or branched-chain alkyl group of C.sub.1 -C.sub.6. Mixtures of these charge-compensating dopants can be employed. These ionic dopants produce n-type conductivity when associated with a reduced or negatively charged polymer polyanion.

A suitable negatively charged compensating dopant, i.e. anionic dopants, can be an anion such as the halogen ions, other ions such as AsF.sub.4.sup.-, and preferably ions such as AsF.sub.6.sup.-, ClO.sub.4.sup.-, PF.sub.6.sup.-, SO.sub.3 CF.sub.3.sup.-, BF.sub.4.sup.-, NO.sub.3.sup.-, POF.sub.4.sup.-, CN.sup.-, SiF.sub.5.sup.-, SbCl.sub.6.sup.-, SbF.sub.6.sup.-, HSO.sub.4.sup.-, organic anions ions such as CH.sub.3 CO.sub.2.sup.-, (acetate), C.sub.6 H.sub.5 CO.sub.2.sup.- (benzoate), CH.sub.3 C.sub.6 H.sub.4 SO.sub.3.sup.- (tosylate), strong Lewis bases, and the like. Mixtures of the charge-compensating dopants can be employed. These ionic dopants produce a p-type conductivity when associated with an oxidized or positively charged polymer polycation.

The dopant modified electroactive polymer has a charge opposite to the conductivity modifier, i.e. ionic dopant. The charges on the dopant modified electroactive polymer and the ionic dopant balance so that the dopant modified electroactive polymer is an electrically neutral system. The association of the virgin polymer with electron donor dopants produces an electroactive polymer which exhibits n-type conductivity. More specifically, reduction of the virgin polymer and the incorporation of cationic charge-compensating dopants produces a polymer which exhibits n-type conductivity. The association of the virgin polymer with electron acceptor dopants produces an electroactive polymer with p-type conductivity. More specifically, oxidation of the polymer and incorporation of anionic charge-compensating dopants produces a polymer with p-type conductivity.

The preferred electroactive polymers of the invention have the following formula: ##STR2## where a is either 0 or 1; b is either 0 or 1; c is either 0 or 1; n is an integer from 2 to 1,000; d is an integer from 1 to 2,000; s is an integer from 1 to 3; R and R' are each independently N-substituted 1,3,4-triazoles; X' and Y' are each independently connecting units comprising a single atom, or a group of atoms; and M is an atom or a group of atoms acting as a charge-compensating ionic dopant whose electrical charge is opposite to the charge exhibited by the recurring repeat units of the polymer backbone: ##STR3##

The repeat units from the polyanion or polycation of the electroactive polymer.

The R and R' groups are independently N-substituted 1,3,4-triazole rings, wherein the substituent on the 1-nitrogen atom is selected from the group consisting of lower alkyl of 1-6 carbon atoms and phenyl. More particularly, R and R' are N-substituted 1,3,4-triazole diradicals of the following formula: ##STR4## wherein R.sub.1 is lower alkyl of 1-6 carbon atoms or phenyl.

More specifically, R and R' are the triazole diradicals previously recited or mixtures of the diradicals which are linked to one another either directly or via the connecting units X' and Y' by forming bridges.

The connecting units X' and Y' can be selected from the group comprising: ##STR5## wherein R.sub.1 is lower alkyl C.sub.1 -C.sub.6, aryl, cycloalkyl and alkoxy; R.sup.v, R.sup.vi and R.sup.vii are H or methyl, methoxy, halogen and mixtures thereof; and R.sup.x is C.sub.1 -C.sub.4 alkyl. 4,4'-Biphenylene, vinylene; 1,4-phenylene, and acetylene connecting groups are preferred connecting units. Especially preferred connecting units are 1,4-phenylene and 4,4'-N-alkylaminodiphenylene.

The molecular weight determines the physical properties of the electroactive polymer. The magnitude of n is a function of the molecular weight. Preferably, n is from 5 to 500. More preferably, n is from 10 to 300. Molecular weights of the polymer should be between about 250 and 250,000. A preferred molecular weight is above about 10,000. Tractable films are formed with electroactive polymers wherein n is adjusted so that the molecular weight exceeds 10,000.

The enhancement in conductivity of the electroactive polymer above the conductivity of polymer in the virgin state is determined by d. The value for d is not greater than 2 n. The conductivity is increased and adjusted by increasing d. Conductivities in the semiconductor region can generally be achieved with d values of about 5 percent the n value, e.g., d equals 5 when n equals 100.

Preferred electroactive polymers are doped polymers that have conductivities greater than about 1.times.10.sup.-10 ohm.sup.-1 cm.sup.-1, most preferably greater than 1.times.10.sup.-4 ohm.sup.-1 cm.sup.-1. Greater concentrations of the charge-compensating ionic dopant M increase the conductivity to the metallic conductivity regime. The charge-compensating cationic or anionic dopant M is selected from the previously recited dopants and the like. M remains the same for all the following preferred polymers.

The R and R' groups may be the same or different. When a is 1, b and c are zero, R' and Y' drop out and the polymer has the following formula: ##STR6## A preferred polymer of this formula is poly 1,4-phenylene-2,5-(1-phenyl-1,3,4-triazole) doped with a conductivity modifier.

When a and c are 1 and b is zero, Y' drops out and the polymer has the formula: ##STR7## A preferred polymer of this formula is poly-5,5'-(1,4-phenylene-bis-2,2'-(1-phenyl-1,3,4-triazole)) doped with a conductivity modifier.

When a is zero and b and c are 1, X' drops out and the polymer has the formula: ##STR8##

When a, b, and c are zero, R', X', Y' drop out and the polymer has the formula: ##STR9## A preferred polymer of this formula is poly-2,5-(1-phenyl-1,3,4-triazole) doped with a conductivity modifier.

Although the polymers of the invention can be made up solely of 1,3,4-triazoles, the preferred materials are copolymers wherein the triazole rings are connected through another group, designated a connecting unit. In general, the connecting units should preserve the conjugation of the heterodiazole rings. The connecting units themselves must either be conjugated or maintain pi orbital overlap with the heterocyclic ring systems.

Connecting units may be selected from heteroatoms, such as the Group VB and VIB elements of the Periodic Table, including oxygen, sulfur, selenium, tellurium, monosubstituted nitrogen, phosphorus, arsenic or antimony. Preferably, the connecting uints are conjugated carbon systems, such as olefins or aryl ring systems.

Olefinic connecting units are those obtained by removing a hydrogen atom from each end of the olefinic double bond or from each end of a conjugated double bond system. Typical olefinic connecting units include those obtained from ethylene, butadiene, cyclopentadiene, divinylether, and the like.

Aryl ring connecting units are obtained from the corresponding aromatic compounds by removing two hydrogen atoms from carbon atoms in the aromatic ring system. Typical aromatic connecting units include those obtained from benzene, naphthalene, diphenyl, diphenyl ether, diphenyl sulfide, diphenylalkylamine, anthracene, and the like. Other aryl connecting units are obtained from alkyl or aklenyl aromatics, by removing two hydrogen atoms, either from the ring, from the alkenyl group, or one hydrogen each from the ring and from the alkenyl group. Typical connecting units of this type include those obtained from styrene, divinylbenzene, stilbene, and the like.

The starting material for preparing the electroactive polymers of this invention are polymers and copolymers comprising recurring units of N-substituted 1,3,4-triazoles, wherein the substituent on the 1-nitrogen atom is lower alkyl of 1-6 carbon atoms or phenyl. These polymers and copolymers are well known materials having been synthesized in a variety of ways.

The triazole-containing polymers useful for making electroactive polymers by appropriate doping techniques are prepared by two alternate routes.

In one process, the corresponding oxadiazole-containing polymer is reacted with an appropriate primary amine. The reaction is carried out in an acid solvent such as polyphosphoric acid, sulfuric acid and the like, at temperatures in the range of 200.degree. C. to 350.degree. C., preferably 250.degree. C. to 300.degree. C. The reaction is carried out in a closed vessel at autogenous pressure. The polymer product is isolated by filtration followed by washing to remove the acidic medium. For this process, the oxadiazole polymer feedstock is made by the reaction of a dibasic acid with hydrazine. This reaction is carried out in one of the above named solvents at temperatures in the range of 100.degree. C. to 250.degree. C., preferably 140.degree. C. to 180.degree. C. (Ref. J. Polymer Sci., 3, 45 (1965)). Dibasic acids are readily obtainable; hydrazine is a commercial material. For this reaction, hydrazine salts such as the sulfate, halide, phosphate, etc. are preferred.

The alternate method for preparing the triazole polymers of this invention is by the reaction of an appropriate primary amine with a polyhydrazide. The reaction is carried out in a high boiling acidic solvent at temperatures in the range of 100.degree. C. to 300.degree. C., preferably 150.degree. C. to 200.degree. C. The polyhydrazide feedstock is made by the reaciton of essentially equal moles of an appropriate dibasic acid chloride with one mole of hydrazine. This reaction is carried out in an organic tertiary amine solvent which also functions as a hydrogen chloride scavenger. Amines useful in this reaction include pyridine, diethylamine, triethyl amine, and the like.

Subsequent to polymerization, articles such as fibers, ribbons, or free-standing films are cast from solution. The solution is formed by dissolving the desired polymer in a solvent which consists of sulfuric acid, formic acid, methane sulfonic or polyphosphoric acid. The solution temperature is generally from about 20.degree. C. to about 100.degree. C. The polymers are coagulated into solid shapes such as fibers, ribbons, or free-standing films in a basic coagulation bath. For free-standing films, the polymers are fabricated from solutions containing about 2 to 25% polymer dissolved in the solvent. At concentrations which exceed 10%, the cast films take on an anisotropic morphology. The anisotropic property enhances the conductivity in the anisotropic direction. An amine, for example triethylamine, dissolved in a protonic solvent such as H.sub.2 O and preferably ethyl alcohol comprises the coagulation bath. The bath is maintained at a lower temperature than the dissolution temperature of the polymer in the solvent. Usually room temperature is selected as the operating temperature of the coagulation bath. The fabricated articles are dried. Elevated temperatures, usually 60.degree. C., and reduced pressure accelerated the drying process. Drying is continued until no further weight loss is observed.

Alternatively, films are cast into water, comprising the coagulation bath, followed by neutralization in aqueous bicarbonate. Neutralized films are washed in water and dried at elevated temperatures, 60.degree.-100.degree. C., under reduced pressure.

After fabrication of the desired articles from the heterocyclic polymers by means of the procedure described above, the articles are rendered electroactive by, for example, chemical or electrochemical procedures. The articles can be rendered electroactive in an atmosphere which is inert with respect to the polymer and dopant, by contacting them with suitable conductivity modifiers, i.e. dopants. An inert atmosphere is defined as an atmosphere which does not react with the polymer, the dopant, or the electroactive polymer. For example, the atmosphere can be argon, helium, and nitrogen and the like. The doping can also be carried out in an inert liquid medium such as tetrahydrofuran, acetonitrile and the like. The inert liquid medium should be able to wet and swell the polymer but not react with it. The dopants can be oxidizing or electron accepting molecules, or reducing or electron donating molecules. Both types of dopants may be in the form of gases or vapors, pure liquids or liquid solutions. Preferably, oxygen and water moisture are excluded during and after the doping process because the conductive polymers tend to degrade, i.e. lose conductivity, when exposed thereto.

For example, the polymer can be contacted with conductivity modifiers such as alkali naphthalides, or alkali anthracenides such as sodium naphthalide, potassium naphthalide, or sodium anthracenide, in a tetrahydrofuran solution. The conductivity modifier concentration can be from about 0.001 to about 1 molar and preferably from about 0.01 to about 0.5 molar in the THF or other suitable solvent. Alternative doping methods are taught in U.S. Pat. No. 4,204,216 and incorporated herein by reference.

The incorporation of the dopants into the polymer can be observed by a color change in the polymer as well as an enhanced conductivity. For example, a virgin polymer film having a yellow, orange or brown color, changes to a green, blue or black color with a metallic luster upon doping and the measured conductivity increases by many orders of magnitude.

Alternatively, the polymers can be oxidized or reduced to their conductive forms using electrochemical techniques. In this method, herein referred to as electrochemical doping, the polymer is immersed in a suitable electrolyte solution and used as one electrode of an electrochemical cell. Upon passing an electric current through such a cell the polymer becomes reduced (or oxidized, depending upon the direction of current flow) and charge-compensating cations (or anions) from the supporting electrolyte become incorporated into the polymer. This doping also proceeds with the characteristic color change described above. Thus, the polymer can be electrochemically doped with whatever appropriately charged ion is present in the electrolyte solution. Electrolyte solutions are comprised of a salt dissolved in a solvent. Suitable solvents are acetonitrile, tetrahydrofuran, 2-methyl-tetrahydrofuran, propylene carbonate, dimethylformamide, dimethylsulfoxide and the like. Alternative electrolytes are specified in U.S. application Ser. No. 334,509, filed Dec. 28, 1981, entitled "Batteries Fabricated With Electroactive Polymers", and completely incorporated herein by reference. Suitable cations are Li.sup.+, Na.sup.+, K.sup.+, (CH.sub.3).sub.4 N.sup.+, (C.sub.2 H.sub.5).sub.4 N.sup.+ and (C.sub.4 H.sub.9).sub.4 N.sup.+. Suitable anions are Cl.sup. -, Br.sup.-, ClO.sub.4.sup.-, BF.sub.4.sup.-, and PF.sub.6.sup.-. The extent of doping can be easily controlled by adjusting the amount of charge electrochemically injected into the polymer, either by controlling the magnitude of the current used (galvanostatic charging) or by controlling the potential of the polymer electrode with respect to a reference electrode (potentiostatic charging).

The above-described electrochemical doping process is completely reversible. The polymer can be "undoped" and returned to its original, neutral, non-conducting state simply by applying a current opposite in sign to that used for the doping process. Upon complete undoping the color of the polymer reverts back to its original color. Thus, for example, a reduced, conducting poly-N-substituted triazole polymer can be reoxidized completely to its neutral, non-conducting form, and the charge-compensating cations incorporated during the electrochemical reduction process are expelled from the article during electrochemical re-oxidation.

Having described the methods of fabrication and the basic heterocyclic systems, the following examples are intended to be illustrative of the invention and not meant to limit the scope thereof. Modification which would be obvious to one of ordinary skill in the art are contemplated to be within the scope of the invention.

A 300 ml 3-neck flask, equipped with a stirrer, thermometer, condenser and an addition funnel, was charged with 150 g of polyphosphoric acid. After heating to 140.degree. C., 6.6 g (0.25 mol) of hydrazine sulfate was added, followed by 6.93 g (0.0417 mol) of terephthalic acid. Stirring and heating was continued at 140.degree. C. for 5 hours and then at 175.degree. C. for 2 hours. After standing at room temperature for 16 hours, 50 g of polyphosphoric acid was added. Next the reaction mixture was heated at 140.degree. C. and 27.9 g (0.3 mol) of aniline was added. Heating was continued for 2 hours and finally at 195.degree. C. for about 6 hours.

At the end of this time, the crude reaction mixture was poured into water. The resulting slurry was filtered. The precipitate was washed with water, neutralized with triethylamine, and extracted (Soxhlet) with ethanol for 4 days. After drying, 14.5 grams of poly 1,4-phenylene-2,5-(1-phenyl-1,3,4-triazole) was obtained.

A 200 ml 3-neck flask, equipped with a stirrer, thermometer and condenser with a calcium chloride drying tube, was charged with 100 ml of hexamethylphosphoramide, 1.5 g of powdered lithium chloride, and 3.88 g (0.02 mol) of terephthaloyl hydrazide, and the mixture was stirred at 50.degree. C. until a complete solution was obtained. The solution was cooled to 0.degree. to 5.degree. C., and 4.06 g (0.02 mol) of terephthaloyl chloride was added in 4 essentially equal portions at this temperature over 30 minutes, and then stirred for one additional hour. The temperature was raised to room temperature, and stirring was continued for two more hours. The reaction mixture was poured into ice water with stirring, and filtered. The filter cake was washed with water until the filtrate became neutral to pH paper, and dried in air. After drying, 6.71 g of poly-terephthaloylhydrazide was obtained.

A 300 ml 3-neck flask, equipped with a stirrer, thermometer, condenser and an addition funnel, was charged with 110 g of polyphosphoric acid. After heating to 150.degree. C., 27.5 g (0.296 mol) of aniline was added while the temperature was held below 190.degree. C. The temperature was adjusted to 175.degree. C., and 3.6 g of poly-terephthaloylhydrazide was added. Stirring and heating were continued at 175.degree. C. for 21 hours, then at 200.degree. C. for 8 hours, and then at 220.degree. C. for 92 hours. At the end of this time, the crude reaction mixture was poured into water, and the resulting slurry was filtered. The precipitate was washed with water, neutralized with aqueous triethylamine, and extracted (Soxhlet) with ethanol overnight. After drying, 4.2 g of tan-colored crude polymer was obtained, which was purified by dissolving in concentrated sulfuric acid (2 weight percent solution), filtering, and reprecipitating the polymer by pouring into ethanol. After drying, 0.78 g of poly 1,4-phenylene-2,5-(1-phenyl-1,3,4-triazole) was obtained.

The product of the example was dissolved in concentrated sulfuric acid to give about a 2 weight percent solution. A platinum wire, 0.5 mm in diameter, was dipped into this solution. After removing it from the solution, excess liquid was gently wiped off and then the wire was placed in a water bath for 30 minutes at ambient temperature. Next it was soaked in a 5% sodium bicarbonate solution for 16 hours. At the end of this time the wire was rinsed with water, rinsed with acetone, and then dried under vacuum.

The resulting polymer-coated wire was submitted to a cyclic voltammetric analysis. For this analysis, the electrolyte was an 0.1 molar solution of tetraethylammonium tetrafluoroborate in acetonitrile. Measurements were made with reference to a silver/silver nitrate reference electrode and subsequently converted into voltages with the standard calomel electrode (SCE). A reversible reduction potential of -2.2 V vs. SCE was obtained.