Thermal Control Material

For a better understanding of the invention and to show how the same may be carried into effect, reference will now be made, by way of example, to the accompanying drawings in which:

FIGS. 1 and 2 are cross-sectional views of parts of respective thermal blankets for a spacecraft,

FIG. 3 is a cross-sectional view of a glass tile for use in a spacecraft, and

FIG. 4 is a diagram showing a method of enhancing the conductivity of glass .

The blanket shown in FIG. 1 comprises a thin outer layer of Kapton 1 and a thicker layer of Kapton 2 between which two layers there is a layer of electrically conductive material 3. "Kapton" is a registered trade mark and refers to a material sold under that name by the DuPont Company. The layer 3 could be formed by vacuum depositing a layer of conductive material onto the layer and then bonding the layer 2 to the layer 3 by way of a layer of adhesive material (not shown). It is believed better, however, to use for the layer 3 a conductive adhesive, e.g. an adhesive which has been loaded or filled with conductive material. This can be simply painted onto one of the layers 1 and 2 and the other of these two layers bonded to the first by means of the adhesive.

The electrically conductive material could be a metal such as aluminium or silver--this being in the form of dust if it is provided as the filling of a conductive adhesive. Preferably, however, the conductive material layer is made transparent for example by the use of indium-tin-oxide or a like transparent conductive material. Making the layer 3 transparent may increase the thermal emissivity of the thermal blanket which would be desirable for spacecraft. At the back or inner face of the layer 2 there is an optional further layer 4 of electrically conductive material of which the function is to prevent charge build-up due to any very high energy electrons which may be encountered and which penetrate the blanket to past the layer 3. The layer 4, like the layer 3, could be a thin vacuum deposited or painted-on metallic layer or it could be replaced by a relatively thick metal, e.g. aluminium, sheet (not shown) and be used also as an R.F. shield for the craft.

In order to connect the layers 3 and 4 to the spacecraft structure, the blanket has in it, along one or more edges for example, a series of holes 5 of which only one can be seen in the drawings. A bolt 6 is positioned in each hole with a Kapton reinforcing washer 7 beneath the head thereof and a nut 8 is tightened onto the bolt to make contact with one end of an aluminium earthing strap 9 of which the other end (not shown) is connected, e.g. by way of a further nut and bolt, to the spacecraft. Instead of a nut and bolt, each strap could be attached to the flexible blanket by some other means e.g. by soldering and the holes 5 filled up with conductive material, e.g. aluminium solder, to connect the layer 3 to the strap. As shown in FIG. 2, the outer Kapton layer 1 could end short of the edges of the blanket to leave exposed edge portions 3a of the conductive layer 3. Conductive paint 10 is applied over these exposed portions and around and under the blanket edges as shown and a strip of aluminium foil 1 is secured to the paint layer by bolts 12. The aluminium foil strip extends as an earthing strap (not shown) to the spacecraft body.

It is preferred that the overall thickness of the blanket is at least 0.002" in order to give it sufficient mechanical strength. Meanwhile, the thickness of the layer 1 can be optimised to give the most advantageous trade-off between the thermo-optical and electrostatic properties of the blanket. Such an optimum thickness can be determined for a particular application by experimentation. A thickness of 7.5.mu. has been found to be appropriate. The thickness of layer 3 should be kept to a minimum to save weight but should remain sufficient to be able to conduct well the envisaged current. 1000 Angstroms appears to be useful although a thinner layer might be adequate for some applications. The layer 4 could also have a thickness of 1000 Angstroms.

Instead of Kapton, the layer 1 and/or the layer 2 could comprise some other plastics material such as P.T.F.E. (Teflon) or it could comprise another dielectric material such as glass.

In space the electrons incident on the thermal blanket have energies in the range of 2-20 Kev. Their range in a plastic material is given by the equation:

where R is the range in Angstroms and T is the kinetic energy in Kev. This gives the range of electrons for 20 Kev energy to be about 7.15.mu..

In FIG. 3 there is shown a tile comprising a block 12 of borosillicate glass and backed by a layer of metallic silver 13 to make the tile into a second-surface mirror. The upper surface and the edges of the block 12 are coated with a layer 14 of transparent, electrically conductive material such as indium-tin-oxide. Finally, a relatively thin lamina of borosillicate glass 16 is attached to the top surface of the tile by means of transparent adhesive 17.

The borosillicate glass could be replaced by other kinds of glass, for example quartz. If the layer 14 is made of an electrically conductive adhesive material, then this could be used to attach the lamina 16 and the layer 17 may become unnecessary.

The tile shown in FIG. 3 may be attached, e.g. by means of adhesive, to an area which is to be thermally insulated on the outer surface of a spacecraft along with as many other like tiles as are needed to cover the area. Like the layer 3 in FIGS. 1 and 2, the function of the electrically conductive material layer 14 in FIG. 3 is to collect as many as possible of the penetrative electrons bombarding the spacecraft and to conduct them away so that charge does not build up to the point where disruptive discharges might occur. The thickness of the lamina 16 is thus again made such, having regard to the typical electron energy levels expected, that the majority of the bombarding electrons will come to rest in or close to the conductive layer. The conductive layer 14 extends down over the edges of the tile to the silver layer 13 and thence to the spacecraft, and provides an easy discharge path for charge associated with these electrons.

The tile of FIG. 3 could be made by taking a block of glass such as quartz or borosillicate glass for example, which is silvered on one side and forming an electrically conductive material layer a short way below the other side by the process known as ion bombardment. In this process, the block is irradiated by ions of an electrically conductive material having such energy that they penetrate and come to rest at the requisite distance below the surface of the block.

The process of ion bombardment can also be used to form the electrically conductive layer 3 in the blankets of FIGS. 1 and 2, i.e. by taking a single sheet of material such as Kapton and forming an electrically conductive layer by ion bombardment just below the surface of the sheet.

To further reduce undesirable build-up of electrical charge on and in each tile due to electron bombardment in space, the electrical conductivity of the glass, at least in the direction from the upper surface of the tile towards the spacecraft wall, may be enhanced for example by the method disclosed in our U.K. patent application No. 8018037, i.e. by preirradiating the tile with electrons in an electron accelerator and with sufficient electron energy to cause electrons to penetrate right through the tile. Alternatively, one or each of the glass layers 12 and 16 of the tile can be subjected to an electric field whilst molten, for example, when it is being moulded in a mould 10 as shown in FIG. 4. A strong D.C. field, preferably at around 4.times.10.sup.8 volts/meter, is applied to the tile by means of two electrodes 19 and 20 and a voltage source 21. The molten material is allowed to set while the field is still applied. The action of the field is to polarise otherwise random molecular alignments within the molten material and thus enhance the conductivity of the material in the direction from the cathode 19 to the anode 20 in the figure. The cathode side of the moulded glass layer is thus made the surface furthest from the spacecraft whilst for the layer 12, the silver reflective layer is applied, after the layer has solidified, to the anode side. The mould 18 should be made of a material, Teflon, for example, having a low dielectric constant so that it does not affect the electric field too much. Alternatively, the mould base could be made of conductive material, metal for example, and be arranged to act as the anode itself--then the separate anode 20 is unnecessary.

The aforementioned method of conductivity enhancement by irradiation with electrons of sufficient energy to pass right through the material may also be used in relation to materials such as Kapton as disclosed in U.K. patent application No. 8018037. Thus, the thermal blankets of FIGS. 1 and 2 may be improved by using this method to enhance the electrical conductivity of each Kapton layer.