Solder Composition for Thin Coatings

The electrical contact leads of integrated circuits are often coated with a thin layer of solder, by plating or other techniques, so as to improve their connection and solderability characteristics. This classically has been done after the chip has been assembled and using hot dip processes which result in relatively thick solder coatings. A newer, more efficient process has been recently adopted, called pre-plating, in which the solder is deposited before assembly so as to increase productivity. However, the pre-plated solder layer is necessarily quite thin because of the stringent dimensional requirements and productivity requirements that the leads must meet. The lead base materials are usually copper or nickel alloys.

A severe problem arises with these new thin coatings, however, because industry practice requires severe quality control tests for integrated circuits which include subjecting the parts to high temperatures of 155-175 degrees centigrade for extended periods of many hours to test the integrity of the part. Also, the assembly process involves the application of heat to cure the molded DIPS. This additional heat sometimes affected the solderability of prior art pre-plated leads which did not become apparent until the part actually reached the end user who had difficulty in properly soldering the part into a circuit board. After an extensive investigatory program, it was discovered that a close control of the lead to tin ratio in the solder will eliminate later burnin induced solderability problems for thin layers of solder on copper, nickel, or other base materials that can form intermetallics with tin.

The type of solder layer used on pre-plated integrated circuit leads ranges from 50 to 500 micro inches in thickness. Layers this thin, when subjected to temperatures of 175 degrees centigrade for up to 24 hours, followed by 155 degrees for 160 hours, can form intermetallic compositions with the base metal, especially if the base metal is copper or nickel containing material. These intermetallic compositions may extend all the way through the thin layer in some cases and seriously degrade the solderability characteristics of the leads. We have found that this degradation can be avoided, while still retaining other necessary solder characteristics if the solder is constrained to a range of 10 to 40 percent tin with the balance comprising lead. The preferred range is from 25 to 35 percent tin. This contrasts with the industry wide common practice of using about 60% tin and 40% lead compositions for lead frame solder coatings.

The drawing shows a composite graph, developed from extensive empirical testing, that correlates the percentage solderability failures as a function of the percentage tin in the solder.

The graph was developed from tests of thin solder coatings in the range of 100 to 300 microinches on copper bases. Solderability problems caused failures at high rates for compositions having less than 10% or more than 40% tin. Too much tin allowed the excessive formation of intermetallics with the base material. Too little tin produced other unacceptable solder characteristics. It was determined that the preferred range of composition would be from 25 to 35 percent tin with the balance lead.