High Resolution Screen Printable Resists

1. Field of the Invention

This invention relates in general to a resinous protective coating capable of being applied to preselected portions of an insulating or metallic substrate. More particularly, the present invention relates to a resinous protective coating for use in producing patterns on circuit boards, the protective coating including a highly functional solid resin having a melting point between about 60.degree. C. and about 200.degree. C.

2. Description of the Prior Art

There are numerous methods employed in the manufacture of printed circuit boards. These methods typically contain at least one step in which a temporary or permanent protective coating is employed. Illustrative of these methods are the following:

In one method of producing circuit boards, a background pattern is printed with a permanent protective coating which leaves exposed a pattern on an adhesive coated laminate. The adhesive coated laminate contains catalytic material therewithin which allows the laminate to initiate electroless metal plating. The permanent protective coating or mask is hardened by curing, and the exposed pattern on the laminate is activated in an oxidizing solution, such as chromic-sulfuric acid solution to render the exposed pattern receptive to electroless copper plating with good adhesion of the copper to the activated surface. The permanent mask resists oxidation by the chromic-sulfuric acid solution. Copper is deposited on the exposed areas of the adhesive coated laminate to form an electrically conductive pattern via electroless deposition.

In another method of producing circuit boards, a laminate is coated with a non-catalytic adhesive. The entire laminate is then etched with an oxidizing solution, such as a chromic-sulfuric acid solution before being seeded and sensitized with a catalytic solution, such as palladium-tin-chloride. A background permanent mask or protective coating is then printed on the laminate before copper is electrolessly deposited on the exposed areas of the laminate in the form of the printed pattern.

In another method of producing printed circuit boards, a "print and etch" technique is employed. Copper foil is laminated to one or more sides of an insulating substrate, a positive pattern is printed (screen, photographically, etc.) with a temporary protective coating or resist, background copper is then etched away by subjecting the substrate to an etching solution, e.g, ferric chloride, ammonium persulfate and the like, the temporary resist is moved from the substrate using appropriate solvents, e.g. alkali soluble resists are removed with alkali solvents, holes are producted on the substrate by a laser beam, punching, drilling and the like, the substrate is sensitized and seeded by contacting it with, for example, aqueous acidic solutions of stannous tin ions and precious metal ions such as palladium ions, a registered solder mask which is a permanent protective coating is printed (screen, etc.) onto the substrate leaving lands and holes exposed, copper is electrolessly deposited onto the exposed lands and holes, but not the heat cured solder mask and the substrate is then dipped into solder to cause solder to adhere to the copper coated lands and holes.

In still another method of producing printed circuit boards, an "electroplating" technique is employed. Copper foil is laminated to one or more sides of an insulating substrate, holes are produced in the substrate where desired for a circuit pattern, the substrate is sensitized and seeded with well known seeding and sensitizing agents, copper is electrolessly deposited on the copper foil and into the holes, the copper foil surfaces are lightly sanded to remove electrolessly deposited copper, a temporary protective coating or background resist is printed (screen, etc.) on the substrate to form a pattern thereon, copper or another electroconductive metal is electroplated onto the pattern, the pattern is then solder plated, the temporary background resist is removed by use of a suitable solvent, and unwanted background copper is etched away. Contact areas such as edge connectors can be electroplated with noble metals such as gold, silver, etc.

In another method of producing printed circuit boards, a "fully additive" technique is employed. A suitable insulating substratum is prepared having a distance between hole centers of about 2.5 mm or less the substratum and walls of the holes are sensitized and seeded using known seeding and sensitizing agents such as stannous chloride, palladium chloride activation, a permanent protective coating or resist is screened to produce a permanent background resist leaving the desired circuit pattern exposed, the pattern having as low as about 0.35 mm between lines, the resist is heat cured, copper is electrolessly deposited on the exposed pattern and in the holes and the board is then dip soldered.

In another method of producing printed circuit boards, a "semi-additive" technique is employed. An insulating substrate is prepared having holes on 2.5 mm centers, the walls of the holes and the surface(s) of the substrate are sensitized and seeded in a conventional manner, copper is electrolessly deposited over the entire surface of the board and in the holes, a temporary protective coating or resist is employed to print a circuit pattern having 0.35 mm lines, the temporary resist is heat cured, the circuit pattern is built up by electroplating a metal onto the exposed areas of the substrate, the temporary resist is removed, the thin layer of electroless copper which had been covered by the mask is etched away, a permanent registered solder mask is printed and heat cured, and the substrate is then dip soldered.

In another method of producing circuit boards, a printed circuit is prepared on an insulating substratum by the print and etch technique, a permanent registered solder mask is printed thereover leaving lands and holes exposed, the permanent mask is cured, copper is electrolessly deposited on the walls of through-holes formed in the insulating substratum and the circuit is solder dipped to cause solder to adhere to the lands and holes. Another modification of this method involves using a fully additive or semi-additive process to prepare the printed circiuit board on the first step, the remaining steps being the same.

The temporary or permanent protective coatings used as resists, solder masks, etc. in the prior arts methods of producing circuit boards have had a number of deficiencies which are set forth subsequently herein. For high density circuits, it has been customary to use dry film photoresists which are extremely costly. Screen printed resists or masks, while economical, have not been able to achieve the high resolution necessary for high density circuit boards. For example, the problems associated with the use of prior art solder masks such as the PC-401 Series Solder Mask (commercially available from Kollmorgen Corporation, Glen Cove, N.Y.) are detailed hereinbelow as an illustration of the type of problem also associated with the use of other resinous protective coating compositions of the prior art as temporary or permanent resists or the like.

Virtually all printed circuit board assemblies, even in small quantity production are wave or dip soldered. Heretofore, in producing circuit boards which have a high circuit density per unit area, difficulty has been experienced due to the fact that the holes in such boards: (1) tend to have an extremely small diameter e.g. 0.35-1 mm; and (2) tend to be extremely closely spaced at least in some portions of the circuitry. High density boards may also have hole centers spaced a distance of less than 1 mm. When the holes are less than 2.5 mm apart with a conductor between the holes, it is practically impossible to print a registered permanent solder mask over the conductor without smearing solder mask around the lands adjacent the holes. In conventional practice, a plated through hole circuit board is produced with a circuit on one or more exposed surfaces. Before soldering, a registered solder mask is printed on the circuit pattern(s) to leave holes and lands or pads (i.e., small areas on the surface surrounding the holes) as well as fingers (i.e., terminal or contact areas of the circuit pattern) exposed. Subsequently, the components are fastened to the circuit as by dipping in a solder bath to apply solder to the component leads and on the exposed areas, i.e., on the exposed lands and in the metallized holes. The solder mask protects the major portion of the circuit from the solder and thus guards against short circuiting by confining solder to only those areas where it is desired.

In such conventional circuits, the lands or pads are exposed while conductor lines making up the conductor pattern or patterns are protected by the solder mask. Accordingly, when the circuit density is high, it is extremely difficult to print a registered solder mask so as to provide exposed land or pad areas surrounding the holes without some solder mask accidentally lodging on the barrel of the hole.

Conventional registered, screen printed solder masks have other disadvantages. To maintain fine printing tolerances in such boards, extremely thin prints are used. Thus, even when great precautions are taken in printing the solder mask on high density circuit boards of the type described, there is a good possibility of the masks breaking down in part, thereby causing the solder to bridge from one land to another, or from one conductor line to another, which in turn results in short circuiting on the finished board. When thicker prints are used to avoid mask breakdown, the solder mask tends to block the holes, thereby preventing proper soldering.

In the prior art, various thermosetting resinous compositions have been used to provide protective coatings such as plating resists, temporary or permanent resists and solder masks. The thermosetting resins used in these compositions had low melting points and were liquid at room temperature. These resinous protective coatings were incapable of providing lines and spaces having a resolution lower than 0.6 mm without bleeding over into the exposed holes and lands surrounding the holes when a conductive pattern was being screened. These resins flowed at temperatures from about room temperature up to about 160.degree. C. during curing. Consequently after the prior art thermosetting resinous compositions had been screen printed onto an insulating substrate or onto a metallic pattern already on substrate, as the substrate was heated to evaporate the solvent in the resinous composition, the resinous composition would further liquify. The printed resinous composition pattern would become extremely liquid and "bleed" or spread to cause poorly, defined, fuzzy, pattern edges thereon. When such bleeding or spreading occurred, solder would not coat pattern edges which border lands and holes during the subsequent dip/wave solder operation.

Only after "bleeding" or spreading out of the printed pattern of the resinous composition would the resinous composition become polymerized and solidified (thermoset). This deficiency was attributable to the fact that in the curing step the resins would liquify before they hardened. During this liquification phase, the resinous composition further spread out the create a poorly defined pattern edge which borders areas where soldering is desired. Liquification of the resins during cure resulted in sloppy mask edges, i.e., the original print was sharp, but during cure the edges of the printed mask spread. Edges which are sharp and have not spread are quite important in high density boards, but not overly important in low density boards.

Prior art masking compositions were not very chemically resistant to adhesion promotion solutions such as chromic acid and highly alkaline, electroless copper baths used in the "fully additive" technique. Moreover, the prior art masking compositions were not smooth and produced rough coatings whose surfaces would be receptive to the production of adherent extraneous copper. With their use in making circuitry using the additive technique, unwanted spots of copper would appear on a background resist pattern for the reasons given hereinabove. Surface resistivity between conductors would be lowered unless the extraneous copper was removed by an extra step such as brushing.

1. Objects of the Invention

It is an object of the present invention to provide temporary and permanent protective coating compositions for use in the manufacture of printed circuit boards.

An object of the invention to provide high resolution screen printable resists.

Another object of the invention is to provide an improved method of improving the resolution of conductive patterns on circuit boards.

An object of this invention is to provide an improved resist for screen printing of patterns on circuit boards.

It is also an object of this invention to provide a solid resin based protective coating useful in producing printed circuit patterns on a circuit board the patterns including lines and spaces having a resolution of at least 0.25 mm and as low as 0.1 mm.

An object of this invention is to provide a thermoset resin based protective coating the solid resin having a melting point between about 60.degree. C. and about 200.degree. C.

Another object of this invention is to provide a protective coating comprised of a blend of resins and solvents such that, during heat cure, the coating passes directly into a gel stage rather than through a liquid stage.

Still another object of this invention is to provide a registered mask which, upon heat cure, retains its sharp edges and does not bleed over onto holes and lands surrounding the holes.

An object of this invention is to provide a thermoset resin based protective coating capable of adhering to adhesive coated base materials as well as metallic substrates and of withstanding the thermal shock associated with dip soldering.

An object of this invention is to provide a smooth, glossy protective coating which is not conducive to the formation of adherent extraneous copper in the additive method for producing circuit boards.

Another object of this invention is to provide an epoxy resin based electroplating resist.

Another object of this invention is to provide a temporary resist useful in the print and etch process of manufacturing circuit patterns on circuit boards.

Additional objects and advantages of the invention will be set forth in part in the description, or may be realized by practice of the invention, the objects and advantages being realized and attained by means of the methods, processes, instrumentalities and combinations particularly pointed out in the appended claims.

2. Brief Description of the Invention

The present invention provides improved high resolution, temporary and permanent, screen printable, protective coatings, improved methods of producing printed circuit boards employing the improved protective coatings, and the improved circuit boards formed thereby. As will be clear from the following description, there is used in the manufacture of circuit boards of this invention certain resinous protective coating compositions which do not bleed when cured.

The print and etch, semi-additive and electroplating techniques employed in the manufacture of printed circuit boards all involve the application of a temporary protective coating or resist to an insulating substrate which coating is subsequently removed in further processing. The additive technique and molten solder application steps employed in the manufacture of printed circuit boards each involve the application of a permanent protective coating or mask which is not subsequently removed. Various methods of producing printed circuit boards such as those described previously herein include the above-described steps and/or techniques and/or combinations thereof. The protective coating composition of the present invention, in one embodiment, provides improved temporary resists. In another embodiment, the protective coating composition of this invention provides improved permanent masks.

For illustrative purposes only and not intending the invention to be so limited, the application of the permanent protective coating composition of this invention is subsequently described herein in conjunction with a typical method (employing the additive technique) in the manufacture of printed circuit boards. The surface of an insulating substrate on which a printed circuit pattern is to be formed is coated with a permanent resinous protective coating or mask according to this invention. The mask has the characteristics of being able to resist attack by acids and alkali to which printed circuit boards will ordinarily be subjected in processing. The mask has a smooth, glossy surface. Holes defining cross-overs have been preformed or may then be formed in the insulating substrate by any method which does not damage the mask or substrate materials surrounding the holes, such as by drilling, piercing or punching methods. A catalytic insulating blank such as the one described in U.S. Pat. Nos. 3,600,330 and 3,672,986 may be used as the insulating substrate The board is contacted with a strong oxidizing solution such as chromic-sulfuric acid solution to adhesion promote the exposed or unmasked areas of the blank. Then the board is contacted with an electroless metal deposition solution to metallize the walls of the holes and the conductor pattern. In the next step, the insulating blank having circuit patterns electrolessly deposited thereon is printed with a permanent solder mask according to the present invention leaving the hole walls and if desired, lands surrounding the holes as well as finger areas, exposed. The permanent solder mask compositions of this invention are capable upon curing, of forming a smooth, glossy surface which not only is resistant to the thermal shock of soldering but also is resistant to flux removing solvents.

In order to illustrate another embodiment of the present invention, the application of the temporary protective coating composition of the invention is subsequently described herein in conjunction with a typical method (employing the electroplating technique) in the manufacture of printed circuit boards. Holes are drilled in a copper foil clad insulating substrate before the substrate is sensitized and seeded with known seeding and sensitizing agents. Copper is electrolessly deposited onto the copper foil and into the holes. The electrolessly deposited copper on the surface of the substrate may be removed by lightly sanding the surface. A temporary background resist according to the present invention is screen printed onto the substrate in a pattern before copper is electroplated onto the pattern. The pattern is then solder plated before the temporary background resist is removed with a solvent as subsequently described herein. Unwanted background copper may then be etched away.

A direct polyvinyl alcohol emulsion on a stainless steel wire screen is a common printing screen stencil employed for circuit printing because it is a tough and resistant stencil which meets the demands of relatively large production and is not difficult to prepare. Any practical screen emulsion, however, including transfer type screen process film, may be employed, depending upon the type of protective coating to be printed. By "transfer type films" are meant films which are first processed on a base and then transferred to the screen fabric on the printing screen. When a resinous protective coating is printed onto a substrate, any screen emulsion that will not be dissolved by the protective coating may be used. Examples of suitable screen fabrics include stainless steel wire screens, polyester fiber screens, and nickel coated polyester screens, preferably sized between about 110 and about 325 (U.S.A. Sieve Size) mesh.

According to the present invention, a thermosetting resin in the protective coating having a high melting point and high functionality permits the solvent in the protective coating to evaporate and the curing operation to occur without melting and liquifying the resin in the coating, thus avoiding spreading of the coating composition during the curing operation. It is believed that the viscosity of the protective coating composition increases as the thermosetting resin therein cures into a solid. The high functionality of the thermosetting resin also creates rapid cross-linking so that the printed mask pattern does not bleed or spread between lines or onto the lands and holes as maximum curing temperatures of the mask are reached. Consequently, the mask retains sharp edges.

It has been discovered that a thermosetting resin based screening mask capable of: (1) producing printed circuit patterns having a resolution of at least 0.25 mm lines and spaces on a substrate; (2) withstanding a copper plating bath; (3) adhering to adhesive coated base materials as well as metallic substrates; and (4) withstanding the thermal shock of soldering and subsequent flux removal, is provided by a protective coating composition which comprises a highly functional thermosetting resin dissolved in a solvent. The resin is a solid at room temperature and does not melt at temperatures up to its curing temperature, typically between about 60.degree. C. and about 200.degree. C.

A simple test was devised to determine whether a particular solid thermosetting resin meets the criteria of the present invention. A chunk or sample piece of the thermosetting resin approximately 5-10 grams in weight is placed in an oven and heated to a temperature between 100.degree. and 160.degree. C. The resin sample is then removed from the oven and visually examined for indication of its melting or spreading. If the sample thermosetting resin melts or spreads during such heating test, it is not suitable for the present invention. On the other hand, if the thermosetting resin becomes and remains tacky during such heating test, it is suitable for the present invention.

The thermosetting resin of this invention preferably comprises about 35-75% of the dry mask, the balance being curing agents and modifier(s). The highly functional thermosetting resin comprises more than about 10 weight %, preferably more than about 12 weight % of the protective coating composition of this invention. The highly functional thermosetting resin also comprises less than about 80 weight %, preferably less than about 60 weight % of the protective coating composition of this invention.

By highly functional thermosetting resins are meant those thermosetting resins having more than about 3 and less than about 10 functional groups, preferably between about 4 and about 7 functional groups. Suitable thermosetting resins include melamines and ureas (aminos), phenolic, polyamide-imide and polyimide, alkyd, polyurethane, and epoxy resins, and blends thereof having an average functionality between about 3 and about 6 and a melting point between about 60.degree. C. and about 200.degree. C.

Suitable amino resins as defined hereinabove include melamine formaldehydes and urea formaldehydes. A suitable urea formaldehyde is Uformite F-240M (a tradename of a commercial Rohm & Haas Co. resin) and a suitable melamine. formaldehyde is Uformite MM55 (a tradename of a commercial Rohm & Haas Co. resin). Other suitable melamine resins as defined hereinabove include RESIMENE 812 (a colorless resin powder commercially available from Monsanto Chemical Co., St. Louis, Mo.); MELMAC 1077 (a melamine resin with a cellulose filler), MELMAC 404 (a translucent melamine resin), and MELMAC 483 (a phenol modified melamine resin) (all commercially available from American Cyanamid Co., Wayne, N.J.).

Suitable phenolic resins as defined hereinabove include oil soluble heat reactive phenolic resins (prepolymers) such as CK-12-82 and CK-16-34 both commercially available from Union Carbide Corporation, 270 Park Avenue, New York, N.Y. 10017 and having respective Durran Softening points of 180.degree.-210.degree. F. and 190.degree.-220.degree. F.; prepolymers of phenol formaldehydes such as RESINOX P-90 and 3700 (both commercially available from Monsanto Chemical Co., St. Louis, Mo.) and SP 8014 and SP 6600 (both commercially available from Schenectady Chemical, Inc., Schenectady, N.Y. and having respective melting points of 160.degree. F. and 150.degree. F. and Sp8014 having a specific gravity of 1.25.

A suitable polyamide-imide resin is Kerimid 501 (commercially available from Rhodia, Inc., Monmouth Junction, N.J.) and a suitable polyimide resin is Kerimid 601 (also commercially available from Rhodia, Inc., Monmouth Junction, N.J.).

Suitable alkyd resins include ethylene glycol maleate polyesters such as Plaskon (commercially available from Allied Chemical Co., Morristown, N.J.) and Durez (commercially available from Hooker Chemical & Plastics Corp., Niagara Falls, N.Y.).

Suitable polyurethane resins include prepolymers combined with polyols such as Solithane 113 (Thiokol Chemical Co. Trenton, N.J.) and Polycin U56 (commercially available from Baker Caster Oil Co., Bayonne, N.J.).

Suitable epoxy resins include functional epoxy Novolac or bisphenol A type epoxy resins that exist normally as a solid at room temperature (having molecular weights between about 350 and 15,000) and have a melting point between about 60.degree. C. and 200.degree. C. For illustrative purposes, the subsequent discussion of the thermosetting resin based protective coatings of this invention will be directed to epoxy resin based protective coatings, but this is not intended to limit the scope of the invention thereto.

Preferred epoxy resins have an average epoxide functionality above 3 and include the following commercially available epoxy resins listed in Table 1 hereinbelow:

Other solid epoxy resins which are believed to be highly functional thermosetting resins within the scope of this invention include EPO GEN 1013 (commercially available from Apogee Chemical Co.); EPI-REZ 521 having an average epoxy equivalent weight of 200 and a Durran Softening Point between 70.degree. C. and 80.degree. C. (commercially available from Celanese Corp.); EPI-REZ 5291 having an average epoxy equivalent weight of 310 and a Durran Softening Point Between 90.degree. C. and 95.degree. C. (also commercially available from Celanese Corp); and EPOTUF 37-171 having an average epoxy equivalent weight of 150 and a Durran Softening Point between 172.degree. F. and 180.degree. F. (commercially available from Reichhold Chemical Co.O.

Other less functional epoxy resins may be optionally included in the coating composition to reduce the brittleness of the cured composition. Such epoxy resins include copolymers of epichlorohydrin (1-chloro-2,3-epoxy propane) with bisphenol A (2,2-hydroxy phenyl propane) which have melting points within the range of 70.degree. C. to 191.degree. C. and molecular weights of about 350 to 15,000. Although epichlorohydrin is the most important organic epoxide employed in the formation of the epoxy resins, other epoxides such as, for example, 1,2,3,4-diepoxy butane may be used. Moreover, while it is preferred to use epichlorohydrin in the preparation of the resinous polymeric epoxide of the prevent invention, other epihalohydrins such as epibromohydrin also may be used advantageously. Similarly, epoxy resins derived from phenols other than bisphenol A may be used including, for example, the reaction product of epichlorohydrin with resorcinol, with phenols derived from cashew nut oils, with hydroquinone, with 1,5-dihydroxy naphthalene or with 2,25,5-tetrabis-(4-hydroxy phenol) hexane. Phenolic intermediates of the resol type, hydrazines and sulfonamides, such as, for example, 2,4-toluene disulfonamide, may also be used for reaction with an organic epoxide to produce epoxy resins suitable for use. Aliphatic epoxy resins are suitable including, for example, the reaction product of epichlorohydrin with glycerol, with ethylene glycol or with pentaerythritol.

The less functional modifier epoxy resins comprise up to about 30 weight %, preferably up to about 15 weight % and when employed typically comprise more than about 10 weight % of the protective coating composition of this invention.

The highly functional epoxy resin is dissolved with a suitable solvent to prepare a solution between about 50% and 90% by weight highly functional epoxy resin, and preferably about 70% by weight highly functional resin. Suitable solvents include glycol ethers and esters such as diethylene glycol ethyl ether, ethylene glycol methyl esters, acetates of the glycol esters, secondary butyl acetate, normal butyl acetate, primary amyl acetate and the like.

Various modifiers are added to the epoxy resin-solvent solution to improve flow, screenability, to increase toughness and optionally to impart color, antioxidation and antisag properties.

Flow promoters (or flow control agents) prevent "fish eyes" from forming in a screening mask by lowering surface tension to provide a smooth, continuous surface. As indicated in N.I. Gaynes et al., Formulation of Organic Coatings (D. Van Vostrand Co. 1967) pp. 184-185, 294-295 and 300-301, resin films tend at times to cratter or pinhole. A flow promoter helps to provide a smooth, homogeneous film, without the unsightly craters and "orange peel" effect normally developed with the use of these resins. Examples of suitable flow promoters include alkyl acrylate polymers and silicones. Preferred commercial flow promoters are MODAFLOW (commercially available from Monsanto Chemical Co., St. Louis, Mo.); RAYBO 15 (commercially available from Raybo Chemical Co., W. Va.), and DC 840 (commercially available from Dow Corning Co., Midlands, Mich.). MODAFLOW is a high molecular weight polymer believed to be a blend of isobutylacrylate and ethyl acrylate polymers or a copolymer thereof which is commercially available from the Monsanto Chemical Co., St. Louis, Mo. MODAFLOW enhances the surface leveling properties of the composition such that the composition when applied to the insulating or conductive bases flows out to a smooth level without forming ripples or bubbles, so that on drying, it produces a smooth, glossy surface. The flow promoters comprise up to about 6 weight %, preferably up to about 4 weight % of the protective coating composition of this invention, and when included, typically comprise more than about 0.2 weight %.

Screening aids act as a lubricant, facilitating screen printing of the highly functional epoxy resin containing coating compositions of this invention to produce smooth coatings. Suitable screening aids include epoxy resins which are liquid at room temperature. Preferred commercially available epoxy resins include DER 330, DER 331 and DER 332 (all commercially available from Dow Chemical Co., Midlands, Mich.); EPON 820 (commercially available from Shell Oil Company, New York, N.Y.); EPOTUF 37-151, EPOTUF 37-134, EPOTUF 37-135, EPOTUF 37-250 (all commercially available from Reichhold Chemical Co., White Plains, N.Y.), EPI-REZ 508 and EPI-REZ 510 (commercially available from Celanese Corp., New York, N.Y.), and ARALDITE 6005 and ARALDITE 6010 (commercially available from CIBA-GEIGY CO., Ardsley, N.Y.). The screening aids comprise up to about 60 weight %, preferably up to about 40 weight %, and when used typically comprise more than about 1 weight %, preferably more than about 2 weight % of the protective coating composition of this invention.

Suitable tougheners include the liquid acrylonitrile butadiene copolymer rubbers and solid epoxy resins with high epoxy equivalent weights. The rubber tougheners precipitate out during curing as, for example, rubber-rich microglobules uniformly dispersed throughout the cured polymer. The microglobules stop crack propagation from occurring in the cured polymer. Preferred rubber tougheners include the following commercially available liquid, reactive rubbers: CTB, CTBN, CTBNX and ATBN (commercially available from B.F. Goodrich Chem. Co., Cleveland, Ohio). The solid epoxy resin tougheners toughen the protective coating composition by flexibilizing the cross-linked rigid structure. Preferred epoxy resin tougheners include the following epoxy resins listed in Table II which are solid at room temperature with epoxy equivalent weights greater than 350.

The tougheners comprise up to about 10 weight %, preferably up to about 7 weight % and when used, comprise more than about 1 weight % of the protective coating composition of this invention. The tougheners comprise more than about 1 weight %, less than about 10 weight %, preferably less than about 7 weight % of the protective coating composition of this invention.

Suitable color agents (pigments) include the following commercially available pigments: Cyan Green B-15-3100 (Blue Undertone), Cyan Green Y-15-3040 (Yellow Undertone), and Titanium dioxide (Rutile) OR-600 (all commercially available from American Cyanamid, Wayne, N.J. 07470); Irgazin Yellow 2GLT (commercially available from Ciba-Geigy Corp., Ardsley, N.Y. 10501); and Monastral Red RT-79D and Blue BT 417 (commercially available from E.I. duPont de Nemours, Wilmington, Del. 19899).

Antioxidants can optionally be included in the protective coating composition of this invention as a modifying agent when continuous use of the cured coating at temperatures above about 100.degree. C. is contemplated. The antioxidants prevent excessive air oxidation of the coating composition in such usage. Excessive air oxidation would otherwise cause the coating composition to become discolored. Brittleness and loss of adhesion to a substrate to which it is coated are also avoided.

Suitable antioxidants include thioesters such as dialkyl thiodipropionate, dilauryl thiodipropionate, distearyl thiodipropionate, and dimyristyl thiodipropionate; phosphites such as tris (nonylphenol) phosphite and alkaryl phosphite; and phenolics such as fatty acid modified substituted phenolics, hindered phenolics and high molecular weight hindered phenolics (e.g. butylated hydroxy toluene), and mixtures thereof. Preferred antioxidants include a combination of a thioester with a hindered phenolic in a ratio by weight of 9 to 1 hindered phenolic to thioester. The antioxidants comprise up to about 1.0 weight %, preferably up to about 0.8 weight %, and when used, comprise more than about 0.1 weight %, preferably more than about 0.3 weight % of the protective coating composition of this invention.

Gelling agents may be added without impairing properties of the coating composition to improve antisag properties and screen printing techniques. When racking, storing and/or curing of the protective coating on the substrate in a substantially vertical orientation is contemplated, without the addition of the thickening or gelling agent, sagging of the printed image would occur. The thickening or gelling agent prevents sagging of the printed image during storage (particularly vertical storage) and/or heat curing. The addition of the thickening or gelling agent to the protective coating composition of this invention operates to improve the screen printing capabilities of the protective coating composition by thickening it to a soft "gel-like" state.

This soft "gel-like" state can be described as a non-Newtonian fluid which, when free-standing, does not flow. When a force is applied such as by a screenprinting squeegee, the flow occurs, and when such applied force is removed, the composition returns to its non-flowing, non-sagging state.

Suitable thickening or gelling agents include a fumed silica having particles of submicroscopic size with a total surface area of 200 to 400 square meters per gram such as Cab-O-Sil (commercially available from Cabot Corporation, Boston, Mass.); organic modified montmorillonite clays such as a trialkylaryl smectite (Bentone 27) and a tetraalkyl ammonium smectite (Bentone 38), an amine treated bentonite (commercially available from NL Industries, 1230 Sixth Avenue, New York, N.Y.); a colloidal silica made according to the disclosures of U.S. Pat. Nos. 2,574,902 and 2,577,485 such as Ludox (commercially available from E. I. duPont de Nemours & Co., Wilmington, Del.); a silica aerogel having particles of small microscopic size with a total surface area of 280 m.sup.2 /g such as Santocel Z (commercially available from Monsanto Chemical Company, St. Louis, Mo.).

The thickening or gelling agent comprises up to about 5 weight % and when employed, comprises more than about 1 weight % of the epoxy resin solids content of the protective coating composition of this invention. Upon curing of the protective coating composition containing the thickening or gelling agent, the "gel-like" composition remains in its soft "gel-like" state until it is fully cured and solidified in situ without bleed, flow or sag occurring.

The apparent viscosity of the epoxy resin screen printable mask is between about 10,000 centipoise and about 200,000 centipoise, preferably between about 15,000 and about 100,000 centipoise. For purposes of control, the apparent viscosity of the coating composition of this invention are measured with the Brookfield Viscometer at 10 RPM with a No. 7 spindle.

Suitable coreactants for the highly functional epoxy resin in the protective coating composition may be another resin, such as, for example, a phenolic type resin; a polyamide resin; or a melamine-formaldehyde resin; or it may be, for example, a dibasic acid. The coreactants function to harden the coating composition. Suitable curing agents for the highly functional thermosetting resin are an amine such as, for example, methylene dianiline, diethylene triamine or metaphenylene diamine; or an amide, such as, for example, dicyandiamide. A particularly preferred curing agent is the ethylhexoic acid salt of a tertiary amine or 50% by weight of the above-described salts in combination with another amine. Such preferred curing agent provides sufficient latency, about 8 hours, but provides fast cure.

In preparing a permanent protective coating according to the present invention, an amount of curing agent is employed which is sufficient to completely cure the highly functional epoxy resin in the protective coating. This may be calculated according to the amine equivalent weight (A.E.W.) of the curing agent and the epoxy equivalent weight (E.E.W.) of the epoxy resin according to the formula:

Where the curing agent does not have a readily known amine equivalent weight such as when a catalytic curing agent like dicyandiamide is used, the amount of curing agent to effect substantially complete cure is determined empirically by trial and error.

When a temporary protective coating according to the present invention is desired, the amount of curing agent which is employed should be sufficient to only partially cure the protective coating. It has been found that when less than the amount of curing agent required to effect substantially complete cure of the highly functional epoxy resin in the protective coating is used, the protective coating is only temporary. The amount of curing agent to effect partial cure of the highly functional epoxy resin in the coating is more than about 10 weight percent, should be more than about 20 weight percent, typically is more than about 30 weight percent, and suitably is more than 40 weight percent of the amount of curing agent required to effect substantially complete cure of the highly functional epoxy resin in the protective coating. Moreover, the amount of curing agent to effect partial cure of the highly functional epoxy resin in the coating is less than about 80 weight percent, typically is less than about 70 weight percent, should be less than about 60 weight percent and preferably is less than 50 weight percent of the amount of curing agent required to effect substantially complete cure of the highly functional epoxy resin in the protective coating. Consequently, the protective coating so formed when cured is temporary and may be subsequently removed with hot alkaline cleaners or solvents.

Use of the amount of curing agent delineated hereinabove, which amounts are all less than the amount of curing agent used in forming the permanent protective coating of this invention allows a temporary coating to be formed. In the curing of electroplating resists, the temperatures which are typically used are lower than the melting point of the highly functional epoxy resins used in the protective coating compositions of this invention. Even in the absence of a curing agent, there would be some cure of the protective coatings of this invention. Such partial cure would produce a removable coating having the attributes of the permanent coating of this invention, i.e. high-resolution without bleeding allowing closer spacing of lines on a printed circuit board.

As will be clear from the following description, use of the temporary and permanent protective coatings of the present invention eliminates bleeding upon cure of the coatings and therefore eliminates the problems concomitant with the use of resinous masking compositions which bleed when cured. Also important is the fact that the use of these temporary and permanent protective coatings leads to the achievement of high resolution at the edges of the coatings, a result not possible with conventional masking compositions. Consequently, improved high density printed circuit boards may be produced by various methods of producing circuit boards which involve the use of the improved temporary and permanent protective coatings of this invention.

Other objects and advantages of the invention will be set forth in part herein and in part will be obvious herefrom or may be learned by practice with the invention, the same being realized and attained by means of the instrumentalities and combinations pointed out in the appended claims.

The invention is more fully described hereinafter with reference to the accompanying drawings which illustrate certain embodiments of the invention and together with the specification serve to explain the principles of the invention.

FIGS. 1-10 illustrate procedures which can be used to produce printed circuit boards from insulating substrates and for alternative embodiments of printed circuit boards produced in accordance with the teachings herein; and

FIGS. 11-13 are flow sheets illustrating typical procedures for making printed circuits following the teachings of this invention.

In the drawings, similar reference numerals are used to represent similar parts.

A method for making printed circuits using an insulating substrate 10 is illustrated in FIG. 1. As shown in FIG. 1A, the insulating substrate 10 has bonded thereto metal layers 12 and 14 on both sides of substrate 10. The metal layers 12 and 14 typically are copper. In FIG. 1B, hole 15 is drilled through the copper clad substrate 10. The substrate 10 is then immensed in a palladium-tin chloride solution to apply a thin film of catalyst 18 in hole 16 as shown in FIG. 1C. Copper is then electrolessly deposited, by methods well known in the art, through the hole 16 to form a copper conductive film 20 about 1 micron thick on the walls of the hole 16, as shown in FIG. 1D. In FIG. 1E, there is shown a temporary mask 22 according to the present invention which has been screen printed in a negative pattern. Copper 24 is electroplated and then solder 26 is plated onto the exposed hole 16 and conductor 21 (FIG. 1F). The temporary mask 22 is then stripped with a hot alkaline solvent and the copper layers 12 and 14 are etched with ammonium persulfate or ammoniacal copper chloride solution (FIG. 1G). A permanent solder mask 30 according to the present invention may be then applied over the circuit lines, leaving hole 16 exposed (FIG. 1H).

Alternatively, to remove the solder from underneath the solder mask, the solder can be stripped from the board with hydrogen peroxide and hydrochloric acid solution before applying the solder mask.

In order to preserve adhesion of the mask of this invention to copper, diamines, aromatic diamines such as p-phenylene diamine, aryl amines, hindered phenols such as butylated hydroxy toluene, and thioesters such as dialkyl thio-dipropionates may be employed.

A method for making printed circuits using a catalytic insulating substrate is illustrated in FIG. 2. As shown in FIG. 2A, a catalytic insulating substrate 100 has bonded thereto metal layers 102 and 104. In its simplest form, the substrate 100 has distributed therein an agent (not shown) which is catalytic to the reception of electroless metal from an electroless metal deposition solution. Hereinafter, whenever the term "catalytic" is employed it will refer to a material which has this property, i.e., the ability to receive a metal deposit when exposed to an electroless metal deposition solution, or to catalyze the deposition of metal from such a solution. The catalytic agent may be dissolved in or dispersed throughout the substrate 100. Alternatively, the insulating base metal, e.g., the insulating base material may be formed in whole or in part of an insulating organo-metallic compound which is catalytic to the reception of electroless metal. Superimposed on the substrate 100 and adhered thereto are thin unitary and integral metal layers 102 and 104 which preferably cover and are substantially conterminous with, i.e., each have the same boundaries as, the surface of substrate 100. The thickness of the metal layers 102 and 104 will depend primarily upon the manner in which they are fabricated and bonded to the substrate 100, and will also depend upon the ultimate use to which the substrate is to be put. Typically, the metal layers 102 and 104 will have a thickness of between about 0.05 micron and 105 microns. In a preferred embodiment, the metal layers 102 and 104 are copper. The thickness of the metal layers 102 and 104 when made of copper will preferably be such that their weight will vary between about 0.03 and 2 ounces per square foot.

When the metal layers 102 and 104 are superimposed on the substrate 100 by means of conventional metal cladding techniques, i.e., by preforming a thin foil of metal, e.g., by electrolytic deposition, and laminating it to the base, the foils 102 and 104 will each have a thickness of at least about 8 microns. On the other hand, if the metal layers are produced by vapor deposition or by the electroless chemical metal deposition technique described herein, they can be as thin as 0.05 micron.

Using a print and etch technique of the type described hereinbelow, circuit 106 is imposed on the catalytic substrate 100. In FIG. 2B, a positive pattern of the desired circuit is made on the surface of the substrate 100 by printing a positive pattern of the desired circuit on each surface by means of a screen stencil step and repeat negative 116 with an acid resistent material 115, the temporary protective coating of this invention. In FIG. 2C, the metal on both surfaces in the area not covered by the mask is ready to be etched to remove the metal foil 102, 104 and form a conductor pattern 106 shown in FIG. 2D. Following etching, the resist 115 is removed to leave conductor pattern 106 adhered to substrate 100 as shown in FIG. 2E. The printed pattern may be formed on the metal clad substrate 100 in a variety of ways.

In screen printing, the step and repeat negative is used to produce a stencil on the silk polyester fiber or wire mesh of the screen frame. The stencil is made photographically from a negative and reproduces it exactly.

It will be understood that either a positive or a negative image of the desired conducting patterns may be imposed on the substrate, with suitable modifications to insure that the final conductive pattern desired is ultimately obtained.

When screen stencil printing is employed, the ink used in printing must be acid resistant, so that the portions of the metal foil covered thereby are not affected by the etching solution when the plate is contacted therewith. The temporary protective coating composition of this invention provides such an acid resistant ink. The temporary protective coating is acid resistant but can be readily removed when desired by readily available solvents or otherwise.

One etching solution commonly used with copper clad stock is ferric chloride. The etching operation is carried out by either blasting the surface of the panel with a fine spray of ferric chloride or immersing the printed sheets, which are held in a rack or on a conveyor, in an agitated tank of ferric chloride. The etching operation is controlled by the concentration of the etching solution and time of contact, and these variables must be carefully controlled empirically for good results. After etching, a water rinsing process is employed to remove all etching chemicals, thereby preventing contramination of the surface or edges of the panel.

Frequently, a bare copper foil circuit is not adequate. If, for example, the circuit pattern is to be used as a switch, slip ring, or commutator, it may be necessary to plate the circuit pattern with silver, nickel, rhodium, gold and similar highly wear resistant metals. Where it is necessary to solder lugs or other hardware to the pattern, it may be advisable to have the conductor pattern solder plated. In FIG. 2F the circuit 106 is coated with a permanent solder mask 108 according to this invention to leave exposed lands 107 defining interconnecting points between the circuits. In FIG. 2G, holes 112 are provided in the lands 107. The circuit board as it looks in FIG. 2G is then exposed to an electroless metal deposition solution of the type described herein to deposit electroless metal 116 on the walls surrounding the holes and to deposit additional electroless metal 114 on the lands surrounding the holes as shown in FIG. 2H. In an alternative embodiment, the solder mask shown in FIG. 2G, could cover the entire circuit pattern with the exception of the holes per se. When the resulting base is exposed to electroless metal, the walls of the holes would be plated but there would be no lands exposed. The embodiment of FIG. 2, including the alternative suggested, represents a preferred commercial process for practicing the invention described herein. FIG. 2 described supra illustrates an important embodiment of the invention which can be used to good advantage in the production of high density printed circuit boards.

When the circuit density is high, it is extremely difficult to print a registered solder mask so as to leave the lands surrounding holes exposed, for the simple reason that little free space not covered by conductor lines or not taken up by holes is available on the surface of the board. For this reason, holes constitute a serious limiting factor on the density of printed circuit boards made conventionally. Even when great precautions are taken in printing the solder mask on high density circuit boards of the type described, there is a good possibility of the masks breaking down in part, thereby causing the solder to bridge from one land to another, which in turn results in short circuiting of the finished board, or the solder mask may block the holes, thereby preventing proper soldering.

By utilizing the registered mask of this invention shown in FIG. 2, high density printed circuit boards are facilitated. As shown in FIG. 2, A-F, there is first produced a printed circuit pattern 106 on a suitable insulating substrate 100. As described with respect to FIG. 2G, the circuit pattern may be then covered completely with a solder mask 108 with the exception of holes defining cross-over points which extend through the mask and the board. As shown in FIG. 2H, the hole is next metallized by a suitable technique such as described in U.S. Pat. No. 3,269,861 or U.S. Pat. No. 3,259,559 to provide a metal coated wall. The completed circuit board within this embodiment takes the form shown in FIG. 2H. When the circuit board of FIG. 2H is subjected to a solder bath, solder deposits only on the electroless metal deposit 116 on the walls surrounding holes 112. The mask 108 insures that no solder deposits on the surface of the circuit board itself. The solder mask of this invention substantially eliminates any possibility of solder bridging or mask blocking the holes, regardless of how close the holes or how high the circuit density.

As will be appreciated, this technique permits the holes and lines to be placed close together, thereby enabling a high density circuit pattern to be produced, and also minimizes or eliminates the possibility of solder bridging.

A wide variety of additional circuit boards may be produced using the permanent mask of this invention.

In its simplest form, this technique can be used to provide a one-sided plated through hole circuit board following the technique illustrated, for example, in FIG. 3. In FIG. 3A is shown a blank which comprises a catalytic substrate 1000 having bonded thereto a thin film of metal 1400. In FIG. 3B, a circuit pattern 1402 has been produced on base 1000 by following the print and etch principles described hereinabove. In FIG. 3C the lines of the circuit pattern 1402 have been covered with a permanent solder mask 1600 according to the present invention leaving the pads 1402 exposed. In FIG. 3D holes 1500 are then provided in the board. The holes can be put in the board before or after forming the pattern 1402 or before or after application of the mask 1600. In FIG. 3E, the board has been subjected to an electroless metal solution to deposit a coating of electroless metal 1502 on the walls surrounding the holes 1500. When subjected to a solder bath, the board of FIG. 3E will not receive solder on the portion of the mask edge 1601 surrounding the holes which is adjacent the surface of the mask. Note however that the lower surface 1507 of catalytic substrate may accept on occasion unwanted electroless metal deposits.

To avoid the formation of such deposits on the bottom surface, a permanent resin mask 1600 according to the present invention could be superimposed on both surfaces of the board to enhance the insulating characteristics of the board. Such one-sided circuit boards would have the appearance shown in FIG. 4. Here again, the smooth, glossy, protective coating of the mask will prevent unwanted deposits on the lower surfaces surrounding the holes.

The technique for producing two-sided plated through hole boards utilizing this permanent resin mask concept has already been illustrated in FIG. 2.

It will be appreciated that in the FIG. 2 embodiment, the original circuit pattern 106 shown in FIG. 2C could, if desired, be produced by the additive technique described hereinabove, rather than the print and etch technique. Similarly, in FIGS. 3 and 4, the original circuit pattern 1402 could be produced by the additive technique as distinguished from the print and etch technique.

In FIG. 5 is shown a way in which multi-layer plated through hole boards could be used utilizing the permanent resin mask concept described hereinabove. In FIG. 5A is shown a blank comprising a catalytic substrate 1000 having superimposed thereon a thin metal film 1200.

In FIG. 5B, a printed circuit pattern 1202 has been formed on the catalytic substrate 1000 utilizing a print and etch technique.

In FIG. 5C, there has been superimposed upon the circuit pattern 1202 a catalytic blank 1100 comprising a catalytic substrate 1002 and a thin metal film 1400. A similar catalytic blank 1102 has been superimposed on the bottom layer of the catalytic substrate 1000 as is also shown in FIG. 5C. In FIG. 5D, additional circuit patterns 1404 have been formed on the top and bottom catalytic substrate layers 1002 using a print and etch technique. As shown in FIG. 5E, the circuit pattern top and bottom is next coated with a permanent solder mask 1600 according to the present invention. Next, holes 1500 are provided in the circuit board as shown in FIG. 5F. Finally, the board is subjected to an electroless metal deposition solution to deposit electroless metal 1502 on the walls surrounding holes 1500, as shown in FIG. 5G.

The finished circuit board could then be solder plated, for example, by immersing in a solder bath to coat the walls of holes 1500 with solder, if desired.

In a further refinement of the embodiment shown in FIG. 5, suitable indicia at 1201 could be superimposed or provided on the substrate 1000, preferably prior to lamination of the metal clad blanks shown broadly at 1100 and 1102. These indicia could then be used as bull's eyes for pattern registration during printing of the circuit patterns on metal layers 1400. The bull's eyes 1201 may take a variety of forms. Thus, for example, they could be holes boarded or otherwise provided in the substrate 1000 which could serve as a ground plane or a support for an actual circuit pattern, or both. Alternatively, bull's eyes 1201 could take the form of a metal spot or dot produced either by the print and etch or additive technique described herein.

It should also be brought out that the initial circuit pattern 1202 need not be formed on the ground plane or substrate 1000 by print and etch techniques. Similarly, the metal clad blanks 1100 and 1102 in FIG. 5 could if desired be replaced simply by a catalytic base, following which the circuit patterns 1404 could be made by the additive technique rather than the print and etch.

In FIG. 6 is shown still a further embodiment for producing multi-layer boards utilizing the registered printed solder mask concept.

In FIG. 6A is shown a blank comprising a catalytic substrate 1000 having superimposed on both surfaces thin metal films 1200.

Using a print and etch technique, a circuit or ground pattern 1202 is formed on the substrate 1000. Here again, if desired, bull's eyes or registration marks 1201 may be formed on the substrate 1000 simultaneously with production of the first printed circuit or ground pattern 1202. In FIG. 6C a catalytic blank 1100 comprising a catalytic substrate 1000 and a thin metal film 1400 has been superimposed on circuit pattern 1202 and laminated to the catalytic substrate 1000.

Using print and etch techniques, a circuit pattern 1404 is formed on the surface of substrate 1002 and on the lower surface of ground substrate 1000 as shown in FIG. 6D. In FIG. 6E, a permanent registered mask 1600 according to the present invention is superimposed on circuit pattern 1404 so that the resulting three-layered board appears as shown in FIG. 6E.

In FIG. 6F holes 1500 are provided in the board, following which the board is subjected to an electroless metal deposition solution to deposit metal on the walls surrounding the holes. The finished three-layer circuit board is shown in FIG. 6G, wherein 1501 refers to the metal surrounding the walls of the holes.

In FIG. 6, circuit pattern 1202 need not be formed by the print and etch technique. Rather, it could be formed by the additive process described herein. Similarly, blank 1100 need not be a metal clad blank but could simply consist of a catalytic substrate. In such an embodiment, circuit patterns 1404 could also be produced by the additive technique.

In FIG. 7 is shown a particular important embodiment of the invention wherein a four-layer plated throughhole circuit board containing a registered permanent solder mask is produced. In FIG. 7A is shown a blank comprising a substrate 1000 having superimposed thereon thin metal films 1200. In FIG. 7B print and etch circuit patterns 1202 are formed on the top and bottom layer of the ground plane 1000. At 7C, blanks 1100 and 1102 are laminated top and bottom to the substrate 1000 and cover the circuit patterns 1202. Blank 1100 and 1102 comprise a catalytic substrate 1002 and a thin metal film 1400.

In FIG. 7D, additional circuit patterns 1402 are formed top and bottom by print and etch techniques. Here again, bull's eyes or registry marks 1201 may be used if desired for registration purposes in forming the circuit patterns 1402. In FIG. 7E a permanent registered solder mask 1600 according to the present invention is coated over both the top and bottom surfaces on the board.

Next, holes 1500 defining cross-over points are provided in the board shown in FIG. 7F. Then the board is subjected to electroless metal deposition to deposit metal in the walls surrounding the holes is shown in FIG. 7G. Here again, in the FIG. 7 embodiment, it is not necessary to form the circuit patterns 1402 and 1202 by print and etch techniques. Rather, each of these circuit patterns could be produced using the additive technique described herein. In such embodiments, the metal cladding 1200 and 1400 would be eliminated.

In FIG. 8, 210 is a catalytic substrate and 218 is a catalytic adhesive superimposed on the substrate 210. Numeral 217 represents the printed circuit pattern and 216 represents the permanent solder mask according to the present invention. In FIG. 8, the wall of hole 215 has a deposit of metal 221 to make a through connection. Note that the plating on the hole wall extends over the edge of the board at the lower surface to form a small exposed eyelet 221(a).

To avoid the formation of eyelets 225(a) on the lower surface, that surface could be coated with a permanent or nonpermanent mask as shown in FIG. 9.

In FIG. 9, is shown a plated through hole formed utilizing the registered permanent resin mask concept. In FIG. 9, the board comprises a catalytic base 210, the lower surface of which comprises an insulating resinous layer 211. On the upper surface, the base 210 is coated with a layer 218 of catalytic adhesive material on which as been formed the printed circuit pattern 217. A permanent resin mask 216 according to the present invention covers the circuits pattern completely. Hole 215 has its walls covered with metal 221, which terminates short of the outer surfaces of masks 216 and 211.

In FIG. 10 is shown a plated through hole board. The board of FIG. 10 comprises a catalytic base 210 having superimposed thereon layers of catalytic adhesive 218. Printed circuit pattern 217 is formed on the upper surface of adhesive 218. Permanent solder mask 216 according to the present invention covers the entire circuit pattern. Hole 215 has a plated wall 221. Here the plated wall extends to the lower surface of the board. In FIG. 10, the electroless metal layer 221 will grow over the lower surface of catalytic ink 218 to form eyelets as shown at 221(a) in FIG. 8 unless this surface is coated with a temporary mask. Accordingly, to produce the board shown in FIG. 10, a temporary mask according to the present invention will have to be superimposed over the lower surface of catalytic adhesive 218 before electroless metal deposits and then stripped after deposition. Alternatively, the mask on the lower surface could be permanent.

In FIGS. 8 through 10, additional circuit patterns could be imposed on the lower surface as well as the upper surface of the base following the techniques described herein.

To place the embodiments of FIGS. 1-10 in proper prospective, it should be pointed out that whenever distance between hole centers in plated through hole printed circuit boards is 2.5 mm or less, silk screen printing techniques break down due to ink bleed, so that when high density circuit patterns are desired having hole center spacing of 2.5 mm or less, photoprinting techniques will ordinarily be used. It is exactly on such high density boards that conductors between the holes cause the difficulties descried above. The permanent non-bleeding solder mask concepts for protecting conductors between plated through holes described in connection with the identified drawings is therefore particularly applicable to manufacture of printed circuit boards having plated through holes whose centers are spaced apart 2.5 mm or less, i.e., between about 1.2 to 2.5 mm; and particularly between 0.8 and 1.2 mm.

It should again be emphasized that the permanent registered insulating mask concept described herein, although suitable for the manufacture of a wide variety of printed circuit boards, has exceptional advantages when used in combination with the catalytic bases described herein to produce high density plated through hole printed circuit boards. Such a technique using the identified materials represents a practical way for achieving even plating on the walls of small, high aspect ratio (small diameter with respect to the thickness of the part) holes. Heretofore, using conventional techniques and materials, the plating on the hole walls has tended to be uneven.

The non-bleeding permanent solder mask concept avoids the problems heretofore described of printing a permanent insulating mask. As has been brought out above, it is very difficult using modern printing concepts to print a registered permanent solder mask on boards on which the hole centers are spaced a distance less than 125 mils. The consensus in the art is that when the holes are less than 100 mils apart, it is practically impossible to print a registered permanent solder mask.

FIGS. 11-13 are flow sheets of procedures for manufacturing a variety of printed circuit products which contain copper as the primary conductive metal using the materials, compositions and techniques described herein. These flow sheets are self explanatory when read in the light of the foregoing specification. Of course, the procedures of FIGS. 11-15 are equally applicable to products which use metals other than copper, e.g., nickel, as the primary conductive metal.

The following examples illustrate at least one of the best modes of the protective coating compositions and methods of the present invention as presently understood.

7 typical mask compositions are given hereinbelow:

Electroless nickel baths which may be used are described in Brenner, Metal Finishing, November, 1954, pages 68 to 76. They comprise aqueous solutions of a nickel salt, such as nickel chloride, an active chemical reducing agent for the nickel salt, such as the hypophosphite ion; and a complexing agent, such as carboxylic acids and salts thereof.

Electroless gold plating baths which may be used are disclosed in U.S. Pat. No. 3,589,916. They contain a water soluble gold salt, such as gold chloride, a reducing agent for the gold salt, such as the dimethylamine borane, a chelating or complexing agent, such as sodium potassium tartrate and a stabilizer such as sodium cyanide. The purpose of the complexing agent is to maintain the gold in solution as a water soluble gold complex. The pH of the bath will be about 13 or between about 10 and 14.

A specific example of an electroless copper depositing bath suitable for use is a bath having the following composition:

This bath is preferably operated at a temperature of about 52.degree. C. and will deposit a coating of ductile electroless copper about 35 microns thick in about 18 hours.

Utilizing the electroless metal baths of the type described, very thin conducting metal films may be laid down. Ordinarily, the metal films superimposed by electroless metal deposition will range from 2.5 to 100 microns in thickness, with metal films having a thickness of even less than 2.5 microns a distinct possibility.