US 4,451,306 AGrant

Manufacture of Coextruded Oriented Products

Issue Date:1984-05-29

•4 Claims

•1 Drawing Sheets

Abstract

A wire or other core is enclosed by two concentric extruded layers, at least one of which is of crystallizable polymeric material, by extruding the layers in succession around but spaced from the core. The first and second layers are brought into thermal and mechanical engagement with each other before the first contacts the core, and the relative thermal capacities of the parts and the temperatures of the layers as they are brought into engagement are such that as the second layer cools and increases in strength and the first layer is heated by thermal transfer from the second layer and decreases in strength, a region of least overall yield strength is formed at a position where the temperature of at least one of the parts (being made of a crystallizable polymeric material) is at a temperature between its glass transition temperature and its crystalline melting point. A braking force is applied to the first layer by a gripping device engaging it after it has cooled below its glass transition temperature and before the second layer is extruded around it and an advancing force is applied to the inner and outer layers at a place beyond the region of least overall yield strength to stretch both layers longitudinally by at least 50% in the region of least overall yield strength and so orient at least one of them and at the same time contract them until the inner layer engages the core.

Metadata

Assignee

BICC Public Limited Company

Inventor

Stefan Verne

Application Information

Application Number:US 3617785

Filing Date:1982-03-25

Priority Date:1978-08-02

Art Unit:161

Classifications

IPC:

H01B 1314

Field of Search:

15617426442742851;52;56;229;165;244.11;244.12;244.13110 R;110 SR;120 SR;DIG. 8171;173;174;210.1;210.5;DIG. 54118;120409;212;910

Patent Drawings (1 sheets)

Description

A bare wire 1 is taken from any suitable source (not shown) and a first cross-head extruder 2 forms around it an oversize tube 3 of crystallisable polymeric material; the wire is centred in the tube sufficiently to avoid adhesion of the tube to the wire. The tube 3, with the wire inside it, passes through a cooling zone 4, which may comprise a water trough or a spray or other force cooling means, and in which it is cooled to a temperature, below its glass transition temperature, at which it can be gripped, whereupon it is gripped by a caterpillar device which controls its advance at an appropriate speed V.sub.1.

The assembly now passes through an extruder station consisting of a second cross-head extruder 6 which forms a second tube 7 of crystallisable polymer around and in intimate contact with the tube 3. The assembly now passes through a second cooling zone 8 to a take-up caterpillar 9 which advances the assembly at a speed V.sub.2 which is at least 1.5 times V.sub.1 and may be up to around ten times V.sub.1, and thence to reeling equipment.

On emerging from the second extruder 6 into the cooling zone 8 the temperature of the outer tube 7 is well above the crystalline melting point of its material and it contributes little or nothing to the yield strength of the composite tube; nevertheless no substantial elongation takes place at this point because the cool inner tube 3 gives the assembly substantial strength. As the assembly travels through the cooling zone 8, the outer tube cools until at a point 10 its temperature falls below its crystalline melting point and it begins to contribute some appreciable strength; at the same time it heats the inner tube 3 until at a point 11 (arranged to be downstream of 10 by choosing the temperature at which the tube 7 is extruded and that of the tube 3 when it reaches the extruder 6 to suit the relative cross-sections of the tubes) its temperature exceeds the glass transition temperature of its material; the consequent loss of yield strength of the inner tube exceeds the concurrent increase in yield strength of the outer layer, and the tubes now elongate together to the extent required by the speeds V.sub.1 and V.sub.2, thereby orienting the material of both the tubes.

The use of two concentric layers greatly reduces the risk of electrical failure due to "pinhole" faults either initially from manufacturing imperfections or after a period of service due to environmental stress-cracking propagated from a surface of the insulation.

Claims

What I claim as my invention is:

1. A method of making a product comprising a core enclosed by two radially successive concentric extruded layers, at least one of which is of crystallisable polymeric material in which (a) a core is enclosed by two concentric extruded layers, at least one of which is of crystallisable polymeric material, by extruding the said layers in succession around but spaced from the core; (b) the first and second layers are brought into thermal and mechanical engagement with each other before the first contacts the core; (c) the relative thermal capacities of the parts and the temperatures of the layers as they are brought into enagagement are such that as the second layer cools and increases in strength and the first layer is heated by thermal transfer from the second layer and decreases in strength, a region of least overall yield strength is formed at a position where the temperature of at least one of said parts (being made of a crystallisable polymeric material) is at a temperature between its glass transition temperature and its crystalline melting point; and (d) a braking force is applied to the first layer by a gripping device engaging it after it has cooled below its glass transition temperature and before the second layer is extruded around it and an advancing force is applied to the inner and outer layers at a place beyond the region of least overall yield strength to stretch both layers longitudinally by at least 50% in the said region of least overall yield strength and so orient at least one of them and at the same time contract them until the inner layer engages the core.

2. A method as claimed in claim 1 in which the core is a wire.

3. A method as claimed in claim 1 in which both layers are of crystallisable polymeric material and each of them is at a temperature between its glass transition temperature and its crystalline melting point in the region of least overall strength, whereby both are oriented.

4. A method as claimed in claim 3 in which both layers are of the same material.

Patent Citations (17)

Patent	Date	Inventor
US2471752	1949-05-01	Ingmanson
US3486196	1969-12-01	Klenk et al.
US3600487	1971-08-01	Zavasnik
US3876462	1975-04-01	Carini et al.
US3949042	1976-04-01	Utz
US3965226	1976-06-01	Werwitzke et al.
US4051298	1977-09-01	Misiura et al.
US4077098	1978-03-01	Ayusawa et al.
US4110385	1978-08-01	Akutin et al.
US4150082	1979-04-01	Brick et al.
FRX2197713	1974-03-01
FRX2347805	1977-11-01
JPX38-6381	1963-05-01
JPX53-24465	1978-07-01
GBX773542	1957-04-01
GBX1440651	1976-06-01
GBX1599106	1981-09-01