US 4,427,445 AGrant
Tungsten Alloys Containing A15 Structure and Method for Making Same
Issue Date:1984-01-24
•8 Claims
Abstract
A hard fine-grained internally stressed material of tungsten and carbon or tungsten, carbon and oxygen is described which is produced by thermochemical deposition. The material consists primarily of a two phase mixture of pure tungsten and an A15 structure, is free of columnar grain distribution, and has a hardness of greater than 1,200 VHN. The average grain size is less than 0.1 micron.
Metadata
Assignee
- Dart Industries, Inc.
Inventors
- Robert A. Holzl
- Robert E. Benander
- Robert D. Davis
Application Information
Application Number:US 3992012
Filing Date:1982-07-21
Priority Date:1979-10-15
Art Unit:223
Classifications
IPC:
B22F 704
Field of Search:
75234;236;248
Patent Drawings
This patent does not have any drawings.
Description
Example I
Graphite bars 2.5 mm by 5 mm by 76 mm were mounted in an inductively heated graphite furnace inside a gas-tight quartz envelope. The bars were heated to a temperature of about 450.degree. C. and a gaseous mixture of 200 milliliters per minute of tungsten hexafluoride, 1000 milliliters per minute of hydrogen, 4 milliliters per minute of methanol, and 3300 milliliters per minute of N.sub.2 were passed into the furnace over the bars. The gas preheat temperature was 300.degree. C. The total pressure within the system was maintained at 250 Torr and the effluent gases were exhausted from the furnace by a vacuum pump. The deposition was conducted for one hour and thereafter the flow of the reactive gases was stopped and the bars were cooled.
A bright, smooth, adherent, coherent coating was observed to have been deposited on the rods. The composition of the coating was determined by x-ray diffraction to be comprised primarily of a mixture of tungsten phase and A15 phase, 33% volume tungsten and 67% volume A15 structure. The hardness was 1820 VHN (kilograms per square millimeter) measured using a 500 gram load. The A15 structure lattice spacing was about 5.03A indicating an internal hydrostatic compressive stress of 3200 MPa. Because the graphite substrate was selected to have nearly exactly the same expansion coefficient as the coating, the indicated prestress is intrinsic to the coating.
Example II
The method of the invention was carried out on steel cylinders of 76 mm internal dia. by 2000 mm in length, coating the inside surface, preplated with approximately 5.mu. of nickel, as follows:
WF.sub.6 --200 ml/min.
H.sub.2 --1200 ml/min.
CH.sub.3 OCH.sub.3 (dimethyl ether)--15 ml/min.
N.sub.2 --1500 ml/min.
Temperature--425.degree. C.
Gas preheat--200.degree. C.
Deposition was carried out for about two hours and a coating thickness of 15-18.mu. was obtained.
A bright, smooth, adherent, coherent coating was observed with a Vickers hardness of 2200 VHN (kilograms per square millimeter) using a 500 gram load. X-ray diffraction analysis was similar to Example I.
Example III
A wear test was carried out on the deposit of Example II using a miniature sand blast unit. Silica sand at 90 psi was directed at the samples at an angle of 22.5.degree. for 20 minutes cumulative time. Weight loss was measured and converted to volume loss and compared to a hard chrome plated steel sample of 800.mu. coating which was similarly tested. The coating of the invention had a wear rate of 3.times.10.sup.-4 cu. cm/hr. whereas the chrome plated steel had a wear rate of 313.times.10.sup.-4 cu. cm/hr.
Tests on 26% chrome stainless steel exhibited similar results versus the coatings of the invention.
ExampIe IV
Coatings have been produced under conditions similar to those of Example I except using the following flow rates:
WF.sub.6 --100 ml/min.
H.sub.2 --500 ml/min.
N.sub.2 --500 ml/min.
Ethanol--5 ml/min.
Pressure--200 torr.
Substrate Temp.--450.degree. C.
Gas Preheat--200.degree. C.
The deposit hardness was 2000-2500 VHN using a 500 gram load.
Example V
Using similar conditions to those of Example IV, except for a flow of 2.5 ml/min. methanol and 2.5 ml/min. dimethyl ether, the deposits had a hardness of 1500 VHN.
It may be seen therefore, that the method of the invention is capable of producing deposits of superior hardness and wear resistance at relatively low substrate temperatures. Successful results are achievable with substrates having coefficients of thermal expansion as high as about 13 micrometers per meter per .degree.C., and thus includes ferritic and martensitic steels and cast irons, as well as precipitation hardening steels. In certain special instances where the substrate geometry is simple or when the substrate has substantial compliance because of low Young's modulus or low yield strength, substrates of higher expansion coefficients can be used.
Because of a lower deposition rate, inherently achievable in the method of the invention, better throwing power and more uniform deposits result. Lower substrate temperatures also means there is more flexibility as to methods of heating the part being coated. The extremely small and symmetrical grain size in the deposits results in an intrinsically stronger and more corrosion-resistant material. Moreover, conical grain growth structures, sometimes present in deposits made at higher temperatures, do not occur with the method of the invention. Such structures may introduce regions of weakness in a deposit.
Various modifications of the invention, in addition to those shown and described herein, will become apparent to those skilled in the art having the benefit of the present description. Such modifications are intended to fall within the scope of the appended claims.
Claims
We claim:
1. A thermochemically deposited product consisting primarily of a two phase mixture of tungsten and carbon or tungsten, carbon and oxygen, one phase being pure tungsten and the other phase being an A15 structure, said tungsten phase being present in between about twenty percent and ninety percent, said product having a carbon content in said A15 structure phase by weight greater than about 0.1 percent and less than about 1 percent, said carbon content being substantially less than the carbon content corresponding to an A15 structure consisting of W.sub.3 C, said product being free of columnar distribution of grains, having a hardness of greater than 1200 VHN, and having an average grain size of less than 0.1 microns.
2. A thermochemically deposited product in accordance with claim 1 wherein, upon heat treating at between about 600.degree. C. and 700.degree. C., said A15 structure is transformed and said hardness is maintained to at least half of its pre-heat treated hardness.
3. A thermochemically deposited product in accordance with claim 1 wherein the A15 phase is internally prestressed in compression.
4. A thermochemically deposited product in accordance with claim 3 wherein the prestress is in excess of 1000 MPa.
5. A thermochemically deposited product in accordance with claim 1 wherein the lattice spacing of the A15 phase is substantially less than 5.04A as determined by x-ray diffraction analysis.
6. A coated substrate product comprising a metal substrate having a coating thereon consisting primarily of a two phase mixture of tungsten and carbon or tungsten can carbon and oxygen, one phase being pure tungsten and the other phase being an A15 structure, said tungsten phase being present in between about twenty percent and ninety percent, said coating having a carbon content in said A15 structure phase by weight greater than about 0.1 percent and less than about 1 percent, said carbon content being substantially less than the carbon content corresponding to an A15 structure consisting of W.sub.3 C, said product being free of columnar distribution of grains, having a hardness of greater than 1200 VHN, and having an average grain size of less than 0.1 microns.
7. A coated substrate product in accordance with claim 4 wherein the substrate comprises a ferrous body having a coefficient of thermal expansion of less than 13 micrometers per meter per degree C.
8. A coated substrate product in accordance with claim 4 wherein the substrate comprises a cemented tungsten carbide.
Patent Citations (8)
Non-Patent Literature (2)
- N. J. Archer and K. K. Yee, "Chemical Vapour Deposited Tungsten Carbide Wear-Resistant Coatings Formed at Low Temperatures", Wear, vol. 48, pp. 237-250 (1978).
- N. J. Archer, "Tungsten Carbide Coatings on Steel" Proceedings of the Conference on Chemical Vapour Deposition, Fifth Int'l. Conference 1975, The Electrochemical Society, Inc., Princeton, N.J.