Process for the Production of Macrocyclic Esters and Lactones Utilizing Mixed Metal Catalysts

Lactones and cyclic esters are obtained by the thermal depolymerization of the corresponding linear polyesters accompanied by ring closure. For such processes, the polyester is heated at an elevated temperature in the presence of a catalyst. The reaction is carried out under reduced pressure and the macrocyclic compound and other volatile products formed during the course of the depolymerization are removed from the reaction zone as they are formed. Due to the poor heat transfer within the highly viscous reaction mass, until recently it was only possible to conduct the reaction as a batch-type operation--thus severely limiting the commercial utility of the process. With the discovery of the process of U.S. Pat. No. 4,165,321, however, the continuous and semi-continuous production of macrocyclic compounds by thermolysis of polyester is now possible.

Chlorides, nitrates, carbonates and oxides of magnesium, manganese, iron, cobalt and tin (all in the divalent state) are disclosed to be effective catalysts for the batch depolymerization of linear polyesters in U.S. Pat. No. 2,092,031. For the process of U.S. Pat. No. 4,165,321 Lewis metal salts such as the oxides, hydroxides, halides, or carboxylates, of Group IIIa, IVa, IVb, Va, VIIb and VIII metals are indicated to be useful catalyst. Yasakawa et al. reported the use of lead catalysts (oxide, hydroxide, carbonate, nitrate, borate or organic acid salts) for the preparation of large ring lactones via thermal depolymerization in Chemical Abstracts, Vol. 78 (1973), 158966q and 158968s. Cyclic esters are also obtained via thermal degradation of polyesters using SnCl.sub.2.2H.sub.2 O (Chemical Abstracts Vol. 86 (1977), 156163s) and in the U.S. Pat. Nos. 4,105,672, 4,136,098 and 4,157,330 a tin carboxylate or an organotin compound in conjunction with an O,O-dialkyl-(3,5-di-t-butyl-4-hydroxybenzyl)phosphonate are employed to catalyze the reaction. In somewhat related procedures, cyclic ester anhydrides of .alpha.-hydroxycarboxylic acids are formed in vacuo by depolymerizing the corresponding linear polymer at 200.degree.-240.degree. C. in the presence of lead (II) stearate (British Pat. No. 1,108,720).

While all of the aforementioned metal compounds catalyze the depolymerization and ring closure to varying extents, whether the process is conducted as a batch or continuous operation, they are not without certain disadvantages. In the first place, many of these catalysts are insoluble or have limited solubility in the reaction medium and give poor yields of the desired macrocyclic products. Even when acceptable yields are obtained the rates of reaction are often slower than desirable so that process equipment can be utilized at only a fraction of its capacity. Efforts to increase the reaction rate by raising the temperature of reaction are only partially successful since this often leads to destructive thermal decomposition and/or excessive foaming, particularly in batch-type operations.

Additionally, it is virtually impossible to completely eliminate the presence of some heavy metal contaminants in the macrocyclic product. The presence of even trace amounts of heavy metal residues can impart undesirable discoloration to the product and, if the product is stored, may promote degradation of the macrocyclic compound or other components formulated therewith. An even more serious problem exists when the catalyst is derived from a toxic metal, such as lead. Toxic metal contaminants cannot be tolerated in most applications where macrocyclic compounds are utilized and this either precludes the use of the products in these application areas or makes it necessary to subject the macrocyclic product to costly and time consuming post-treatment operation(s) capable of eliminating the metal residue.

Aluminum oxide has been used for depolymerizations carried out at atmospheric pressure using superheated steam (Czech Pat. No. 108,726) and the use of aluminum is reported in Japanese Patent Sho 36[1961]-1375 for the thermal depolymerization of polyesters to form cyclic esters and lactones. Aluminum alkoxides derived from simple alcohols are used for the preparation of large-ring lactones and large-ring ethylene dioates in Japan Pat. No. 72 25,071 and Japan Kokai Tokkyo Koho No. 79,115,390, respectively.

This invention relates to an improved process whereby it is possible to obtain macrocyclic compounds, including esters, ether-esters, lactones and ether-lactones in good yield by the thermal depolymerization of polyesters using an aluminum alkoxide or carboxylate mixed metal catalyst. Furthermore, it has been observed that by the use of these catalysts rates of reaction are significantly increased and it is possible to conduct the reaction at higher temperatures than was heretofore possible. By the process of this invention it is also possible to conveniently and economically obtain macrocyclic compounds which are completely free of troublesome heavy metal residues.

For the present improved process a linear polyester is heated at a temperature in the range 200.degree. C. to 400.degree. C. under reduced pressure in the presence of a mixed metal catalyst comprised of an aluminum alkoxide or aluminum carboxylate and an alkoxide or carboxylate of lithium, sodium, potassium or magnesium. Typically the depolymerization is carried out at a pressure from about 10 mm Hg to 0.01 mm Hg and the catalyst is present in an amount from about 0.01 to 20 wt. %, based on the polyester. The resulting cyclic esters, cyclic ether-esters, lactones and ether-lactones will have from 8 to 20 carbon atoms.

Aluminum alkoxides useful as catalysts are derived from conventional monofunctional branched or straight-chain alcohols or alkoxyalcohols and have the formula Al--O--C.sub.m H.sub.2m)--R.sub.1 ].sub.3 where m is an integer from 1 to 22 and R.sub.1 is hydrogen or an alkoxy or polyalkoxy group having 1 to 16 carbons. The carboxylates of aluminum have the formula ##STR1## where R.sub.2 is a C.sub.2-22 alkyl (saturated or containing unsaturation), phenyl or substituted-phenyl having 7 to 20 carbon atoms.

Especially useful catalysts of this invention are mixed metal catalysts obtained when the aluminum alkoxide or aluminum carboxylate is combined with the alkali metal or magnesium alkoxide or carboxylate. The alkoxide and carboxylate moieties of the alkali metal or magnesium can be the same or different as that of the aluminum. Up to about 10 moles alkali metal or magnesium compound can be used per mole of the aluminum component, however, the molar ratio will more usually range from 0.05:1 to 8:1. Mixed metal catalysts obtained from alkoxides or carboxylates of lithium, sodium and potassium are particularly desirable. The components of the mixed metal catalyst may be added individually to the reactor or they may be combined prior to introduction into the reaction environment.

The present invention relates to an improvement in the process for the depolymerization of linear polyesters accompanied by ring closure to form macrocyclic esters and lactones having from 8 to 20 atoms in the ring, said improvement comprising the use of an aluminum alkoxide or aluminum carboxylate mixed metal catalyst.

Thermal depolymerization reactions are well known and in this regard reference may be had to the references previously referred to. Thermal depolymerization of polyesters is typically accomplished at temperatures in the range 200.degree. C. to 400.degree. C. and, more usually, in the range 250.degree. C. to 360.degree. C. Subatmospheric pressures are employed to facilitate removal of the macrocyclic products. The pressure will generally be less than about 50 mm Hg and, most preferably, will range from about 10 mm Hg to 0.01 mm Hg. The temperature and pressure employed for the reaction will vary depending on the particular polyester to be depolymerized, the manner of operation and design of the process equipment.

Polyesters useful in these depolymerization processes are obtained by conventional methods known to the art. If cyclic esters and ether-esters are to be produced the polyester will have the formula ##STR2## where R' represents a bivalent hydrocarbon radical of a dicarboxylic acid, R" represents a bivalent hydrocarbon radical of a diol, x is 1 in the case of cyclic esters and greater than 1 for cyclic ether-esters, and n represents the number of repeating units in the polyester, i.e. degree of polymerization. For the production of lactones and ether-lactones the polyesters will have the respective formulae ##STR3## where R", x and n are the same as above, R"' represents a bivalent hydrocarbon radical and A is an oxygen or sulfur atom. The above formulae indicate the recurring units present in the linear polyester without regard to terminal groups. It is advantageous to use polyesters which are terminated with monocarboxylic acid(s) and/or monofunctional alcohol(s) to control the molecular weight and viscosity of the polymer. Polyesters having acid values and hydroxyl values less than about 20 and, more usually, less than 10 are particularly useful. The degree of polymerization of the polyesters will generally be between about 5 and 150.

The polyesters are derived from conventional dicarboxylic acids, diols and hydroxymonocarboxylic acids. Preferably these reactants are aliphatic and may be saturated or contain olefinic unsaturation and can be branched or straight-chain. Aromatic or alicyclic dicarboxylic acids will contain from 3 up to about 18 carbon atoms and more preferably these acids will have from about 8 to 14 carbon atoms. Useful dicarboxylic acids include, for example, malonic acid, maleic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, azelaic acid, sebacic acid, undecanedioic acid, dodecanedioic acid, brassylic acid, pentadecanedioic acid, and the like. Mixtures of two or more dicarboxylic acids may also be employed. Polyesters derived from alicyclic acids such as cyclohexane-1,4-dicarboxylic acid and 1,3-cyclohexadiene-1,4-dicarboxylic acid may also be used. C.sub.9-13 saturated aliphatic dicarboxylic acids are especially preferred since macrocyclic compounds derived therefrom exhibit especially desirable fragrance properties which make them useful in a wide variety of cosmetic applications.

Hydroxymonocarboxylic acids used for the preparation of polyesters include 15-hydroxypentadecanoic acid, 16-hydroxyhexadecanoic acid, 10-oxa-16-hydroxyhexadecanoic acid, 11-oxa-16-hydroxyhexadecanoic acid, 12-oxa-16-hydroxyhexadecanoic acid, 10-thia-16-hydroxyhexadecanoic acid, 11-thia-16-hydroxyhexadecanoic acid, 12-thia-16-hydroxyhexadecanoic acid, and the like.

Diols from which useful polyesters are typically derived by reaction with the aforementioned dicarboxylic acids are primarily aliphatic diols having from 2 to 12, and more preferably, 2 to 6 carbon atoms. The diols are preferably saturated and can be either straight-chain or branched. Useful diols include ethylene glycol, 1,2- or 1,3-propanediol, 1,2-, 1,3-, or 1,4-butanediol, 1,6-hexanediol, 3-methyl-1,5-pentanediol, 2,3-dimethyl-2,3-butanediol, 1,8-octanediol, 2-ethylhexanediol, 1,10-decanediol, 1,12-dodecanediol, diethylene glycol, triethylene glycol, tetraethylene glycol, and the like. Alicyclic diols such as 1,4-cyclohexadimethanol may also be employed. Polyesters derived from ethylene glycol and di-, tri- and tetraethylene glycol are especially advantageous for use in depolymerization processes of this type.

Employing polyesters of the above types in the process of this invention, it is possible to obtain cyclic esters, cyclic ether-esters, lactones and ether-lactones having from 8-20 carbon atoms in the ring. The cyclic esters and ether-esters will have the general formula ##STR4## where R' is a bivalent aliphatic hydrocarbon radical, which can be branched or straight chain, saturated or contain unsaturation, having from 1 to 16 carbon atoms, R" is a saturated bivalent aliphatic hydrocarbon radical having 2 to 12 carbon atoms and x is an integer from 1 to 4. Especially useful cyclic esters and ether-esters are those where the moiety R' is a saturated radical having from 6 to 12 carbon atoms, the radical R" has 2 to 6 carbon atoms, and x is 1 or 2. Lactones and ether-lactones obtained by the present improved process from polyesters of the above-identified types will have the formula ##STR5## wherein R"' represents a bivalent aliphatic hydrocarbon radical having from 6 to 18 carbon atoms, R" represents a saturated bivalent aliphatic hydrocarbon radical having 2 to 12 carbon atoms, A is oxygen or sulfur, and x is an integer from 1 to 4. Preferred lactones and ether-lactones are those wherein R"' is a saturated bivalent aliphatic hydrocarbon radical having from 10 to 14 carbon atoms, R" contains from 2 to 6 carbon atoms, A is oxygen, and x is 1 or 2.

Illustrative macrocyclic esters and ether-esters which can be produced in accordance with the depolymerization process of this invention include: 3,6,9-tridecamethylene malonate, dodecamethylene malonate, decamethylene malonate, ethylene suberate, ethylene azelate, 3-oxa-pentamethylene azelate, 3-methylpentamethylene sebacate, ethylene undecanedioate, ethylene dodecanedioate, ethylene dodecanedioate, ethylene brassylate, ethylene-.alpha.-methylbrassylate, ethylene-.alpha.,.alpha.-dimethylbrassylate, ethylene-.alpha.-ethylbrassylate, and the like. In addition to the aforementioned products still other cyclic compounds such as tetradecamethylene carbonate, dodecamethylene oxalate and 7-oxa-tridecamethylene oxalate and bicyclic and polycyclic materials such as hexamethylene, tetra- (or hexa-) hydrophthalate can be obtained by the process of this invention. Exemplary lactones and ether-lactones corresponding to the above formulae include: pentadecanolide, 12-oxa-pentadecanolide, 12-thia-pentadecanolide, hexadecanolide, 10-oxa-hexadecanolide, 11-oxa-hexadecanolide, 11-thia-hexadecanolide and 12-oxa-hexadecanolide.

The improvement of this invention for the depolymerization of polyesters consists of the use of specific mixed metal catalysts wherein one of the catalyst components is an aluminum compound. Aluminum compounds used in the process are the alkoxides and carboxylates. While the aluminum compounds are effective catalysts by themselves for the thermal depolymerization and ring closure reaction, it has quite unexpectedly been discovered that improved results are obtained if an alkali metal or magnesium alkoxide or carboxylate is employed therewith. Catalytic systems obtained from aluminum alkoxides or aluminum carboxylates with alkoxides or carboxylates of lithium, sodium, potassium or magnesium, and which are referred to hereinafter as mixed metal or plural metal catalysts, have been found to be particularly effective.

Rapid reaction rates and high yields of the desired macrocyclic product are obtained by the process of this invention. In addition to these advantages, the use of troublesome heavy metals is avoided by the use of the mixed metal catalysts and the process can be carried out at higher temperatures than was heretofore considered possible with minimal thermal decomposition. The amount of catalyst employed for the depolymerization reaction will generally range from about 0.01 to about 20% by weight, based on the polyester. While even larger quantities of catalyst can be utilized, any advantage realized thereby is generally offset by the additional cost involved. Most usually the mixed metal catalyst will be present from about 0.1 to about 10 wt. %.

Aluminum alkoxides and carboxylates used to obtain the catalysts for the present process have the respective formulae ##STR6## where m is an integer from 1 to 22, R.sub.1 is hydrogen, an alkoxy or polyalkoxy radical having from 1 to 16 carbon atoms, and R.sub.2 is an alkyl group having from 2 to 22 carbon atoms and which can be saturated or contain unsaturation, phenyl or substituted phenyl having from 7 to 20 carbon atoms. Especially useful alkoxides and carboxylates are those wherein m is an integer from 2 to 12 and R.sub.1 is hydrogen, methoxy, ethoxy or di, tri-, or tetraethoxy, and wherein R.sub.2 is a C.sub.8-18 alkyl group, phenyl, or a substituted phenyl wherein the substituent is an alkyl, alkoxy or polyalkoxy group. The alkoxides and carboxylates of aluminum may be employed individually or a mixture of two or more of these compounds can be used. Furthermore, these compounds may be added to the reactor as such or generated in the reaction environment. For example, the aluminum may be introduced as an enolate, such as isopropoxy aluminum acetoacetonate, and the chelating group displaced by alkoxide and/or carboxylate groups to obtain the catalyst.

While the above-defined aluminum alkoxides and aluminum carboxylates are useful catalysts for the thermal depolymerization of polyesters to produce macrocyclic compounds, it has quite unexpectedly been discovered that the catalytic activity of these compounds is significantly enhanced if an amount ranging up to about 10 moles of an alkali metal or magnesium alkoxide or carboxylate is present per mole aluminum compound. Highly effective mixed metal catalysts capable of giving very rapid rates of reaction are obtained when from 0.05 to 8 moles alkali metal or magnesium compound is employed per mole aluminum compound. Especially useful catalysts are those wherein from about 0.1 to 3 moles of a carboxylate or alkoxide of lithium, sodium or potassium is present per mole aluminum alkoxide or carboxylate.

Useful alkoxides and carboxylates of alkali metals or magnesium will be of the same type as described above for the aluminum compounds. In other words these compounds will have the formula ##STR7## where M is lithium, sodium, potassium or magnesium, y is 1 when M is lithium, sodium or potassium and 2 when M is magnesium and m, R.sub.1 and R.sub.2 are the same as defined above.

It is not necessary for the formation of the mixed metal catalysts that both metals contain the same alkoxide or carboxylate moieties. For example, if aluminum and alkali metal carboxylates are employed they can be derived from different carboxylic acids. It is also possible and sometimes advantageous to employ an alkali metal alkoxide with an aluminum carboxylate or, conversely, an aluminum alkoxide can be used with an alkali metal carboxylate.

Especially useful alkoxides to obtain the mixed metal catalysts of the present process are derived from conventional C.sub.1-8 aliphatic monofunctional branched or straight-chain alcohols or from a C.sub.3-12 alkoxyalcohol, such as monomethylethylene glycol, monoethylethylene glycol, ethoxydiethylene glycol, ethoxytriethylene glycol, methoxypolyethylene glycols, ethoxypolyethylene glycols and the like. Similarly, the carboxylates of the aluminum, alkali metal or magnesium are typically derived from the same or different branched or straight-chain aliphatic (fatty) acids which can contain olefinic unsaturation, benzoic acid or C.sub.1-8 alkyl substituted benzoic acid.

The mixed metal catalyst is obtained by combining the above-described aluminum compound(s) and lithium, sodium, potassium or magnesium compound(s) in the prescribed molar proportions. This can be accomplished by adding the aluminum compound and alkali metal or magnesium compound to the reactor as such or these compounds can be combined prior to addition to the depolymerization vessel. When the components of the mixed metal catalyst are combined prior to introduction into the reactor, the components may be physically admixed or, depending on the particular components employed and the conditions, partially or completely reacted. This is accomplished with agitation, preferably under a nitrogen atmosphere, and in the absence of moisture. Where the catalyst components are reacted prior to introduction to the reactor, the resulting mixed metal catalyst will vary depending on the nature and molar ratio of the components and the conditions employed. In some instances, such as where an alkoxide of aluminum is reacted with an alkali metal carboxylate, the resulting mixed metal catalyst may have entirely different physical and chemical characteristics than either of the components. For example, both metal components may be solids whereas the resulting mixed metal catalyst obtained upon heating will be a liquid. This feature can be advantageous in that it facilitates handling and introduction of the catalyst to the depolymerization reactor.

The manner in which the depolymerization reaction is carried out, i.e., whether the process is conducted as a batch, continuous or semi-continuous operation, will influence the amount and type of catalyst, the manner of catalyst preparation and reaction conditions used in the process. As has already been indicated the depolymerization can be carried out in conventional process equipment adaptable to removal of the macrocyclic products formed during the course of the reaction by vacuum distillation or in equipment such as that described in U.S. Pat. No. 4,165,321, capable of continuous or semi-continuous operation. If the process is conducted in accordance with the latter procedure the mixed metal catalyst is added continuously or incrementally throughout the course of the depolymerization.

The macrocyclic compounds obtained in accordance with the present improved process are primarily useful in cosmetic applications. They impart desirable fragrance properties and/or enhance the fragrance characteristics of other compounds combined therewith. For example, the cyclic esters and ether-esters, lactones and ether-lactones have utility in detergents (heavy duty and regular laundry), soaps (bar soaps, dish soaps and specialty beauty soaps), personal care products (bath oils, shampoos, hair rinses, deoderants, shaving creams and mouthwashes), and as fine fragrance components for perfumes, perfume oils, perfume fixatives, colognes, aftershave lotions and the like. Products obtained by the present improved process are particularly adaptable to applications where heavy metal residues cannot be tolerated.

The following examples illustrate the invention more fully but are not intended to limit the scope thereof. In these examples, all parts and percentages are on a weight basis unless otherwise indicated.

Preparation of Polyester: Poly(ethylene brassylate) was prepared by charging to a top-agitated resin kettle fitted with a distillation head and condenser 109 parts dimethyl brassylate and 30.5 parts polymer grade ethylene glycol. About 2.3 percent, based on the dimethyl brassylate, methyl esters of a mixture of C.sub.16-22 fatty acids was included as the chain terminator. A supported titanium catalyst (0.08 part), prepared from tetraisopropyl titanate and a naturally acidic montmorillonite clay in accordance with the teachings of U.S. Pat. No. 4,032,550, was then added to the reaction mixture under a positive pressure of nitrogen and heating begun. When the temperature of the reaction mixture reached about 180.degree. C. methanol began distilling from the reaction mixture and was collected. After most of the methanol was removed and the temperature increased to about 195.degree. C.-205.degree. C., a vacuum of 2 in. Hg was applied and increased slowly to 30 in. Hg. Samples were periodically removed from the reactor for analysis and after about 11 hours the reaction mixture had an acid value of 0.1 and hydroxyl value of 15.3. Heating was terminated at this point, the reaction mixture cooled to about 180.degree. C. and the vacuum broken with nitrogen. The high molecular weight poly(ethylene brassylate), viscosity of 117 centistokes at 210.degree. C., was filtered to remove the supported titanium catalyst.

A mixed metal catalyst comprised of equimolar amounts of tri(ethoxyethoxyethyl) aluminate, Al[O(CH.sub.2).sub.2 O(CH.sub.2).sub.2 OC.sub.2 H.sub.5 ].sub.3, and potassium stearate was prepared. The catalyst was obtained by heating 75 parts aluminum isopropoxide, 115 parts potassium stearate and 160 parts diethylene glycol monoethylether at 185.degree. C. until essentially all of the isopropyl alcohol was distilled from the reaction mixture. The resulting mixed metal compound NaAl(OC.sub.2 H.sub.4 OC.sub.2 H.sub.4 OC.sub.2 H.sub.5).sub.3 (OOC.sub.17 H.sub.35) was a homogeneous waxy solid and melted at 80.degree. C.

Following the procedure of U.S. Pat. No. 4,165,321 poly(ethylene brassylate) was depolymerized using the above-prepared mixed metal compound as follows: 1.36 weight percent of the mixed metal catalyst was dissolved in the polyester and transferred to a stainless steel holding tank maintained at 150.degree. C. with agitation. From this tank the polyester was continuously metered into an electrically heated stainless steel inverted vertical cone reactor fitted with two conical, helicoidal blades whose axes coincide with the cone axes of the bowl and which intermesh as they rotate in opposite directions to provide top-to-bottom mixing throughout the total volume of the reaction mixture. The blades were positioned within the reactor so that the maximum blade-to-wall clearance (distance between the blades and the interior surface of the reactor) was about 0.25" and driven with a high torque motor at about 20 rpm. The reaction temperature was maintained between 330.degree. and 360.degree. C. at a vacuum of about 1-5 mm Hg. Ethylene brassylate was continuously distilled from the reactor and the rate of addition of the polyester containing the mixed metal catalyst adjusted as necessary to maintain the proper material balance. The yield of crude ethylene brassylate produced in this manner was 83.6%.

To demonstrate the versatility of the present process poly(ethylene brassylate) was depolymerized in accordance with the procedure described in U.S. Pat. No. 2,092,031. Seventy-five grams of the polyester and 2 grams of the mixed metal compound of Example I (2.66 wt. %) were charged to a glass reaction vessel equipped with a take-off condenser. The mixture was heated to 200.degree. C. with agitation until the mixed metal catalyst was thoroughly blended into the polymer. The reaction temperature was then increased and maintained at 320.degree. C. at a pressure of 0.1-0.5 mm Hg. After the vapor temperature and distillate take-off stabilized, the distillate rate was recorded. Crude ethylene brassylate was obtained at a rate of 40 mls/hour (measured during the first hour). After about 2 hours the reaction was essentially complete as evidenced by a sharp reduction in the distillation rate, however, heating was continued for two additional hours to insure completion of the distillation. The yield of ethylene brassylate (crude) was 89.7%.

To demonstrate the improved yields and increased reaction rates obtained utilizing the mixed metal catalysts of this invention, batch polymerizations were identically conducted using (a) a mixed metal catalyst comprised of aluminum stearate and sodium stearate (1:1 molar ratio), (b) aluminum stearate catalyst, and (c) lead stearate catalyst. These reactions were conducted in accordance with the procedure employed in Example II utilizing 74 grams poly(ethylene brassylate) and 0.5 mole percent of the catalyst. Reactions were carried out at 310.degree.-320.degree. C. and 0.1-0.5 mm Hg. for four hours. The amount of distillate (crude ethylene brassylate) recovered was recorded after the first hour of reaction. With the mixed metal catalyst, 45 mls. ethylene brassylate was obtained after 1 hour and the overall yield was 95.9%. With the aluminum stearate, 36 mls. crude ethylene brassylate was obtained in the first hour and the overall yield was only 78%. Using lead stearate only 25 mls distillate was obtained after 1 hour and the yield of crude ethylene brassylate was 69.1%.

A mixed metal catalyst comprised of aluminum stearate and lithium stearate (molar ratio 1:1) was used for the depolymerization. For the reaction aluminum stearate (1.09 g) and lithium stearate (0.36 g) were blended in 70 g poly(ethylene brassylate) at 200.degree. C. The temperature was then raised to 314.degree. C. while maintaining a vacuum of 0.05-0.1 mm Hg. Ethylene brassylate was obtained (40 mls during the first hour) in an 88.9% yield. Of the ethylene brassylate recovered, 90% of the product was obtained after 2 hours.

A mixed metal catalyst comprised of 0.40 g potassium stearate and 1.09 g aluminum stearate (molar ratio 1:1) was employed at a 2.1 weight percent level to depolymerize poly(ethylene brassylate) at a temperature of 316.degree. C. and pressure of 0.10-0.15 mm Hg. 88.7 Percent yield crude ethylene brassylate containing less than 3 ppm aluminum and only 1.2 ppm potassium was obtained. In a similar manner, ethylene brassylate was produced using the same level of a mixed metal catalyst comprised of 0.74 g magnesium stearate and 1.09 g aluminum stearate.

Mixed metal catalysts comprised of potassium stearate and aluminum stearate were utilized to depolymerize poly(ethylene brassylate). The molar ratios of catalyst components were varied from 3:1 to 1:10 (potassium stearate:aluminum stearate). Reaction conditions and percent yield ethylene brassylate are provided below for each of the ctalysts.

Excellent rates of reaction based on distillation data obtained during the first hour of reaction were observed for all of the above reactions.

Aluminum tripelargonate, obtained by reacting 0.5 mole aluminum isopropoxide and 1.5 mole pelargonic acid at 120.degree. C., was combined with an equimolar amount, based on aluminum, of potassium stearate and the resulting mixed metal catalyst (1.7 weight percent) charged to a reactor with 76 g poly(ethylene brassylate). The depolymerization was conducted in the usual manner. Ethylene brassylate was obtained at a rate of 42 mls/hr. and yield of 89.3%.

A mixed metal catalyst comprised of potassium brassylate and aluminum stearate (1:1 molar ratio of K:Al) was employed for the depolymerization of poly(ethylene brassylate) at a 1.8 wt. percent level. An 81.6 percent yield of ethylene brassylate was obtained. Comparable yields are obtained when this mixed metal catalyst is used for the depolymerization of poly(ethylene sebacate) and poly(3-oxa-pentamethylene azelate).

Sodium brassylate (0.33 g) and aluminum stearate (1.09 g) were added to 70 g poly(ethylene brassylate) and the mixture heated at 200.degree. C. until a homogeneous viscous mass was obtained. The molar ratio of sodium to aluminum was 2:1. The temperature was then increased to 312.degree. C. and the pressure reduced to 0.3-0.5 mm Hg. The depolymerization reaction was complete in about 3 hours and 88.1% yield ethylene brassylate was obtained.

An effective mixed metal catalyst was prepared by heating 0.05 mole powdered aluminum isopropylate, 0.05 mole potassium stearate and 0.14 mole ethyl cellusolve (HOC.sub.2 H.sub.4 OC.sub.2 H.sub.5) at 140.degree. C. and the theoretical amount of isopropanol removed. The resulting solid mixed metal catalyst (0.5 mole %) was used for the depolymerization of a monocarboxylic acid-terminated poly(ethylene brassylate) (AV<10; OHV<10) at 320.degree. C. and 0.1-0.5 mm Hg. Forty-two mls crude ethylene brassylate was distilled from the reaction vessel during the first hour and the overall yield of crude ethylene brassylate was 82.4%.

A mixed metal catalyst prepared similarly to that of Example X, except that sodium stearate was substituted for the potassium stearate and ethyl cellusolve replaced with diethylene glycol monoethyl ether, was employed for the continuous depolymerization of poly(ethylene brassylate) in accordance with the procedure and conditions of Example I. Ethylene brassylate was continuously produced and distilled from the reactor at a rapid rate and the overall yield was 73.2%. Comparable results are obtained with a catalyst comprised of sodium benzoate and aluminum tricellusolve (Al(OCH.sub.2 CH.sub.2 OC.sub.2 H.sub.5).sub.3).

A mixed metal catalyst of the formula NaAl(OCH.sub.2 CH.sub.2 OCH.sub.3).sub.2 (O(CH.sub.2).sub.6 CH.sub.3).sub.2 and identical to that obtained by combining sodium heptoxide with heptyl di(methoxyethyl) aluminate, was prepared by adding 0.25 mole sodium bis-2-methoxyethoxy aluminum hydride (70% sodium in benzene) to 0.5 mole heptanal with cooling over a two hour period. Evaporation of the solvent gave a viscous liquid. 0.46 Grams of the mixed sodium-aluminum alkoxide catalyst was employed to depolymerize 70 g poly(ethylene brassylate at 310.degree.-314.degree. C. and 0.15-0.3 mm Hg. About 85% yield was obtained in 2 hours. Useful mixed metal alkoxide catalysts are also prepared in accordance with the procedure described in U.S. Pat. No. 3,852,309.

A mixed metal catalyst comprised of aluminum isopropoxide and sodium methoxide (1:1 molar ratio) was utilized to depolymerize poly(ethylene brassylate). The mixed metal catalyst was employed at a 0.48 weight percent level. Ethylene brassylate was obtained at a rate of 44.5 mls per hour (based on the amount collected during the first hour of the reaction) and the overall yield at the end of the 4 hours was 80 percent.

The ability to depolymerize different polyester compositions to obtain a variety of useful macrocyclic compounds is demonstrated by this example wherein a mixed metal catalyst was employed for the preparation of ethylene dodecanedioate. For this reaction a mixed metal catalyst obtained by heating equimolar amounts of aluminum tricarbitol (Al(OCH.sub.2 CH.sub.2 OCH.sub.2 CH.sub.2 OC.sub.2 H.sub.5).sub.3) and potassium stearate was added at a 1.3 wt. % level to 70 grams poly(ethylene dodecanedioate). The mixture was heated to 325.degree. C. under reduced pressure (1 mm Hg). About 75% conversion of the polyester to cyclic product was achieved in 1 hour. Eighty-six percent yield ethylene dodecanedioate was achieved. Comparable results are obtained using a polyester derived from diethylene glycol.

To 50 g of the polyester of 15-hydroxypentadecanoic acid was added 2.0 g of the mixed metal catalyst of Example XIV and the mixture heated to 320.degree. C. at 0.8-1.0 mm Hg. Heating was terminated after 4 hours during which time 43.85 g pentadecanolide (87.7% yield) was obtained. An ether-lactone is produced when a polyester prepared from 12-oxa-15-hydroxypentadecanoic acid is depolymerized in a similar manner.

An alcohol terminated polyester of low acid and hydroxyl value was obtained by reacting dimethyl brassylate, ethylene glycol and cetyl alcohol (0.04 mole per mole dimethyl brassylate). Seventy grams of the resulting polyester was then combined with the mixed metal catalyst of Example XIV (1.36 wt. %) and the mixture heated under reduced pressure to effect depolymerization and formation of the cyclic diester product. The depolymerization reaction proceeded at a rapid rate with no difficulty and 52.9 g ethylene brassylate was recovered. In an identical manner, a polyester terminated with an aromatic monocarboxylic acid (p-decyloxybenzoic acid) was depolymerized and 53.7 g ethylene brassylate obtained.