Heterojunction Semiconductor Device

The invention relates to a heterojunction semiconductor device. The term heterojunction semiconductor device is understood to mean a device having a substrate on which have been formed layers of different compositions, usually by epitaxy. Such devices are well known in the art and the substrates are generally formed from the alloy GaAs (gallium arsenide) or InP (indium phosphide), whilst the active layers, i.e. those which directly contribute to the operation of the device are generally formed by ternary or quaternary mixtures comprising incorporated elements (doping agents).

This is the case in particular with electroluminescent diodes, photodetecting diodes and field effect transistors of the MESFET type (metal semiconductor field effect transistor of the Schottky type) comprising active zones which are the seat of light emission and the absorption of photons and where the conductive channel is formed in the case of MESFET.

In the case of electroluminescent diodes, for example of the laser type the active zone must be surrounded by two layers having a forbidden band width greater than that of the active zone.

Generally liquid phase epitaxy is used for producing such structures. However, liquid phase epitaxy is performed at temperatures of 500.degree. to 1000.degree. C. Consequently although the adaptation of the crystalline meshes conveniently takes place at the epitaxial temperature, this is not always the case at the operating temperature, because the thermal expansion coefficients are not always the same in different materials, which leads to disadvantages, particularly in the case of thermal shocks.

The invention aims at obviating these disadvantages.

The invention therefore relates to a heterojunction semiconductor device comprising a substrate constituted by a first semiconductor material having a first expansion coefficient and, deposited by epitaxy on the substrate, at least a first and a second layer of a second semiconductor material of a ternary or quaternary type having a crystalline mesh of approximately the same size as the crystalline mesh of the substrate material and having an expansion coefficient which varies with the composition of the second material, wherein the compositions of the first and second layers are selected in such a way that the expansion coefficient of the first layer is intermediate between the expansion coefficients of the substrate and the second layer.

Another feature of the invention relates to a heterojunction semiconductor device comprising a substrate constituted by a first semiconductor material and, deposited by successive epitaxial processes on the substrate, a buffer layer and at least one active layer constituted by a second semiconductor material with a ternary or quaternary composition, wherein the buffer layer is constituted by the same material as the active layer and from which it only differs by its doping.

The invention is described in greater detail hereinafter relative to non-limitative embodiments and the attached drawings, wherein show:

FIG. 1, an explanatory graph.

FIG. 2, a longitudinal sectional view of an embodiment of the invention.

FIG. 1 shows the thermal expansion coefficient .alpha. of an alloy of formula:

as a function of x, with x varying between 0 and 0.47, the relationship y/x being constant and substantially equal to 2.2. On the ordinate is plotted the coefficient .alpha., giving:

a being the size of a crystal mesh. It should be noted that the gradient of the curve is high when x is between 0 and 0.25 approximately and low when x is between 0.35 and 0.47.

It is known that by liquid phase epitaxy a quaternary mixture of type Ga.sub.x In.sub.1-x As.sub.y P.sub.1-y can be grown on an indium phosphide substrate, this operation being performed at a temperature of about 600.degree. C. As a result if there is a good mesh matching 600.degree. C. this will disappear at ambient temperature which is generally the temperature at which the semiconductor is used. Thus, for InP the expansion coefficient is 4,5. 10.sup.-6 and for x=0.25 that of the quaternary material exceeds 5.10.sup.-6. However, the latter varies slightly for 0.30<x<0.47. Thus, there are constraints at ambient temperature between a layer having a parameter x close to 0.45 and an indium phosphide layer, which reduces the reliability of the device.

A first embodiment is shown in FIG. 2 which is a cross-section of a photoluminescent diode of the laser type along the longitudinal axis of its cavity resonator.

It comprises an indium phosphide substrate 1 on the lower face of which is placed an ohmic contact 2. This substrate of the n.sup.+ conductivity-type with a doping of the order of 10.sup.19 at/cm.sup.3 has a thickness of 10 to 100 .mu.m. A first layer 3 of formula Ga.sub.x3 In.sub.1-x3 As.sub.y3 P.sub.1-y3 of thickness 1 to 10 .mu.m is deposited on this substrate. On layer 3 is deposited active layer 4 having a thickness of only 0.1 to 1 .mu.m of the same quaternary alloy of type Ga.sub.x4 In.sub.1-x4 As.sub.y4 P.sub.1-y4.

Finally layer 4 is surmounted by a layer 5, which is identical to layer 3 and by an ohmic contact 6. Layers 3 and 5 have opposite conductivity types (n and p), whilst the conductivity type of the active zone can be n or p.

The parameters x.sub.3 and x.sub.4, y.sub.3 and y.sub.4 are selected in the following manner. Two conditions must be fulfilled at the same time:

(a) The compositions of the semiconductor materials must be such that the forbidden band width of the intermediate layer 4 is smaller than the forbidden band width of layers 3 and 5 which surround it, this being necessary for laser diode operation.

(b) Assuming a position on the graph of FIG. 1 at two points A and B of abscissas x.sub.3 and x.sub.4 such that the expansion coefficient relative to point A is between the expansion coefficient of InP, i.e. the ordinate at the origin of the curve and the expansion coefficient of the material of layer 4, i.e. the ordinate of B.

A first compromise consists of choosing:

on the one hand for layers 3 and 5:

0.05.ltoreq.x.sub.3 .ltoreq.0.15 with 2x.sub.3 .ltoreq.y.sub.3 .ltoreq.2.4x.sub.3

i.e. approx. 0.1.ltoreq.y.sub.3 .ltoreq.1.6

on the other hand for layer 4:

0.20.ltoreq.x.sub.4 .ltoreq.0.35 with 2x.sub.4 .ltoreq.y.sub.4 .ltoreq.2.4x.sub.4

i.e. approx. 0.4.ltoreq.y.sub.4 .ltoreq.0.8.

A tighter compromise consists of choosing:

x.sub.3 =0.1 with y.sub.3 =0.22

x.sub.4 =0.27 with y.sub.4 =0.59

In the latter case a laser diode is obtained which emits over a wavelength close to 1.3 micron (infrared).

The invention is not limited to the embodiments described and represented hereinbefore and various modifications can be made thereto without passing beyond the scope of the invention.