Layered or Amorphous Cyclic Organometallic Inorganic Polymers

The present invention is directed to solid inorganic polymers having organo groups anchored to the surfaces of the polymers. The majority of the polymers formed are layered crystals which display intercalation activity.

The interface surfaces of solids, whether amorphous, crystalline, or semicrystalline, are responsive regions of chemical and physical action. In many practical chemical and physical phenomena, such as absorption, corrosion inhibition, heterogeneous catalysis, lubrication, ion exchange activity, adhesion and wetting and electrochemistry, activity occurs as a consequence of the presence of a definable solid surface.

Many inorganic solids crystallize with a layered structure and some could present sites for anchoring active groups. In this form, sheets or slabs with a thickness of from one to more than seven atomic diameters lie upon one another. With reference to FIG. 1, strong ionic or covalent bonds characterize the intrasheet structure, while relatively weak van der Waals or hydrogen bonding occurs between the interlamellar basal surfaces in the direction perpendicular to their planes. Some of the better known examples are prototypal graphite, most clay minerals, and many metal halides and sulfides. A useful characteristic of such materials is the tendency to incorporate "guest" species in between the lamella.

In this process, designated "intercalation," the incoming guest molecules, as illustrated in FIG. 2, cleave the layers apart and occupy the region between them. The layers are left virtually intact since the crystals simply swell in one dimension, i.e., perpendicular to the layers. If the tendency to intercalate is great, then the host-layered crystal can be thought of as possessing an internal "super surface" in addition to its apparent surface. In fact, this potential surface will be greater than the actual surface by a factor of the number of lamella composing the crystal. This value is typically on the order of 10.sup.2 to 10.sup.4. Although edge surface is practically insignificant compared to basal surface, it is critical in the rate of intercalation, since the inclusion process always occurs via the edges. This is because bonding within the sheets is strong and, therefore, basal penetration of the sheets is an unlikely route into the crystal.

In graphite, the function of the host is essentially passive. That is, on intercalation, the host serves as the matrix or surface with which the incoming guest molecules interact, but throughout the process and on deintercalation the guests undergo only minor perturbation.

In order for a more active process to occur during intercalation, such as selective complexation of catalytic conversion, specific groups must be present which effect such activity.

An approach in which catalytically active agents have been intercalated into graphite or clays for subsequent conversions has been described in "Advanced Materials in Catalysis," Boersma, Academic Press, N.Y. (1977), Burton et al, editors, and "Catalysis in Organic Chemistry," Pinnavia, Academic Press, N.Y. (1977), G. V. Smith, editor.

One of the few layered compounds which have potential available sites is zirconium phosphate, Zr(O.sub.3 POH).sub.2. It exists in both amorphous and crystalline forms which are known to be layered. In the layered structure, the site-site placement on the internal surfaces is about 5.3 A, which leads to an estimated 25 A area per site. This area can accommodate most of the functional groups desired to be attached to each site. The accepted structure, symbolized projection of a portion of a layer of this inorganic polymer and a representation of an edge view of two layers, are shown respectively in FIGS. 3, 4 and 5.

Besides the advantageous structural features of zirconium phosphate, the material is chemically and thermally stable, and nontoxic.

Quite a bit of work has been conducted on the zirconium phosphate, mainly because it has been found to be a promising inorganic cation exchanger for alkali, ammonium and actinide ions, Alberti, "Accounts of Chemistry Res." 11, 163, 1978. In addition, some limited work has been described on the reversible intercalation behavior of layered zirconium phosphate toward alcohols, acetone, dimethylformamide and amines, Yamaka and Koisuma, "Clay and Clay Minerals" 23, 477 (1975) and Michel and Weiss, "Z. Natur," 20, 1307 (1965). S. Yamaka described the reaction of this solid with ethylene oxide, which does not simply incorporate between the layers as do the other organics, but rather was found to irreversibly react with the acidic hydroxyls to form a covalent bonded product, Yamaka, "Inorg. Chem." 15, 2811, (1976). This product is composed of a bilayer of anchored ethanolic groups aimed into interlayers. The initial layer-layer repeat distance is expanded from about 7.5 A to 15 A, consistent with the double layer of organics present. The overall consequence of this reaction is to convert inorganic acid hydroxyls to bound organic alkanol groups.

A very recently reported effort in the field is Alberti, et al., "J. Inorg. Nucl. Chem.," 40, 1113 (1978). A method similar to that of this invention for the preparation of zirconium bis(benzenephosphonate), zirconium bis(hydroxymethanephosphonate) monohydrate, and zirconium bis(monoethylphosphate) is described, with descriptions of the properties for these products.

Following the Alberti publication, a paper by Maya appeared in "Inorg. Nucl. Chem. Letters," 15, 207 (1979), describing the preparation, properties and utility as solid phases in reversed phase liquid chromatography for the compounds Zr(O.sub.3 POC.sub.4 H.sub.9).sub.2.H.sub.2 O, Zr(O.sub.3 POC.sub.12 H.sub.25).sub.2 and Zr(O.sub.3 POC.sub.14 H.sub.21).sub.2.

All of the compositions described herein can be useful in gas phase, liquid phase, gas liquid, reversed phase, and bulk and thin layer chromatography. The compounds can also be useful as hosts and carriers for organic molecules and especially biologically active organic molecules. They are also useful as catalysts or as supports for catalysts. For example, they can be used in an analogous fashion to the compositions which are discussed by Bailar, "Heterogenizing Homogeneous Catalysts," Catalysis Reviews--Sci. & Eng., 10(1) 17-35 (1974) and Hartley and Vezey, "Supported Transition Metal Complexes as Catalysts," Advances in Organo-metallic Chemistry, 15, 189-235 (1977).

The inorganic polymers of this invention have organo groups covalently bonded to pentavalent metal atoms, such as phosphorus, arsenic and antimony. The pentavalent metal atoms are, in turn, covalently bonded by an oxygen linkage to tetravalent metal atoms. When formed in a layered crystalline state, they provide the organo groups on all of the apparent and interlamellar surfaces.

For convenience herein, the description of the inorganic polymers will be described with regard to phosphorus and its selection as the pentavalent metal. However, it is to be understood that the other pentavalent metals can be used and the description with regard to phosphorus will generally also apply analogously to the other pentavalent metals, for example, such pentavalent metals can be phosphorus, arsenic antimony, vanadium, niobium and tantalum. The term "pentavalent metals" is used herein to describe the above pentavalent atoms which are metals or have metal-like properties; phosphorus, although not a true metal, is herein considered to be metal-like and included within the definition. With regard to selecting arsenic as the pentavalent metal, the general description herein of phosphorus is analogous because an arsine is analogous to a phosphine, an arsenate to a phosphate, an arsonate to a phosphonate, an arsinate to a phosphinate, an arsenic compound to a phosphorus compound, an arsenic compound to a phosphonic compound, an arsenic acid to phosphoric acid, and an arsenious acid to phosphorous acid.

The process of preparation comprises a liquid media reaction in which at least one organo-substituted pentavalent metal acid is reacted with at least one tetravalent metal ion. For example, an organophosphorus acid compound of the formula:

wherein n is 1 or 2 and R is an organo group covalently coupled to the phosphorus atom, and wherein when n is 2, R contains at least two carbon atoms and is directly or indirectly coupled to phosphorus atoms through different carbon atoms whereby the two phosphorus atoms are separated by at least two carbon atoms, is reacted with at least one tetravalent metal ion. The molar ratio of phosphorus to the tetravalent metal is 2 to 1. Reaction preferably occurs in the presence of an excess of the phosphorus acid compound and the metal ion is provided as a compound soluble in the liquid media.

Where only one specie of an organophosphorus acid compound is provided as the reactant with the tetravalent metal compound, the end product will have the empirical formula M(O.sub.3 PR).sub.2. Phosphoric and/or phosphorous acid can also be present as reactive diluents to form part of the solid inorganic polymeric structure which is the product of the reaction.

The products formed are layered crystalline to amorphous in nature. For all products, the R groups can be directly useful or serve as intermediates for the addition or substitution of other functional groups. When the product is crystalline and n is 2, cross-linking between the interlamellar layers occurs.

The normal liquid media is water. However, organic solvents, particularly ethanol, can be employed where water will interfere with the desired reaction. Preferably, the solvent is the solvent in which the organophosphorus acid compound is prepared. Where the organophosphorus acid compound has a sufficiently low melting point, it can serve as the liquid media.

The metathesis reaction occurs at temperatures up to the boiling point of the liquid media at the pressures involved, typically from ambient to about 150.degree. C. and more preferably from ambient to about 100.degree. C. While formation of the solid inorganic polymer is almost instantaneous, the degree of crystallinity of the product can be increased by refluxing the reaction products for times from about 5 to 15 hours. Crystallinity is also improved by employing a sequestering agent for the tetravalent metal ion.

FIG. 1 illustrates a layered microcrystal. Each lamellar slab is formed of strong covalent bonds and had a thickness of about 10 atoms.

FIG. 2 illustrates intercalation where the interlayer distance is shown as "d."

FIG. 3 illustrates the accepted structure for zirconium phosphate and spacing between layers. The dashed lines between zirconium (Zr) atoms is to establish the plane between them. In the drawing, P is phosphorus, O is oxygen and water of hydration is shown.

FIG. 4 illustrates a projection of a zirconium plane showing accepted spacing between Zr atoms and the available linkage area.

FIG. 5 is a symbolized depiction of spaced zirconium phosphate layers showing covalently bonded hydroxyl groups and water of hydration.

FIG. 6 illustrates an exchange reaction between anchored groups "A" and groups to be substituted for linking the terminal group "A" or "B" to the crystals or the organophosphorus acid compound reactant.

FIG. 7 is infrared spectra for a mixed component product Zr(O.sub.3 P(H).sub.1/3, .phi..sub.2/3).sub.2 as compared to the pure phases Zr(O.sub.3 P.phi.).sub.2 and Zr(O.sub.3 PH).sub.2 where .phi. is the radical --C.sub.6 H.sub.5.

FIG. 8 shows the basic structural unit of the inorganic polymer wherein n is 1 and wherein P is phosphorus, O is oxygen, M is tetravalent metal and R is the organo group.

FIG. 9 shows the basic structural unit of the inorganic polymer wherein n is 2 and wherein P is a phosphorus atom, O is an oxygen atom, M is a tetravalent metal and R is the organo group.

FIG. 10 shows the basic structural unit of an inorganic polymer wherein n is 1 and wherein As is arsenic (the pentavalent metal), O is oxygen, M is a tetravalent metal and R is the organo group.

FIG. 11 shows the basic structural unit of an inorganic polymer wherein n is 2 and wherein As is arsenic, O is an oxygen atom, M is a tetravalent metal and R is the organo group.

According to the present invention there is provided inorganic polymers in layered crystalline to amorphous state formed by the liquid phase metathesis reaction of a tetravalent metal ion with an organo-substituted pentavalent metal acid, for example, at least one organophosphorus acid compound having the formula:

wherein n is 1 or 2 and R is an organo group covalently coupled to the phosphorus atom to form a solid inorganic polymer precipitate in which the pentavalent metal (e.g., phosphorus) is linked to the tetravalent metal by oxygen and the organo group is covalently bonded to the pentavalent (e.g., phosphorus) atom. Illustrative with phosphorus in the organophosphorus compound wherein n is 2, the end product occurs in the bis configuration. In this configuration, R must contain two or more carbon atoms, preferably from two to about twenty carbon atoms, such that at least two carbon atoms separate the phosphorus atoms. In this bis configuration, no single carbon atom is bound directly or indirectly to more than one (PO(OH).sub.2) group. When n is 1, and as depicted in FIGS. 14 and 16, the organo groups are pendant from phosphorus or arsenic atoms respectively. When n is 2, and as depicted in FIGS. 15 and 16, cross-linking occurs between interlamellar surfaces of the crystalline end product. Typically, the tetravalent metal ion is provided as a soluble salt MX.sub.4 and X is the anion(s) of the salt. Typical anions include halides, HSO.sub.4.sup.-1, SO.sub.4.sup.-2, O.sub.2 C-CH.sub.3.sup.-1, NO.sub.3.sup.-1, O.sup.-2 and the like.

Tetravalent metal ions useful herein are analogous to Zr.sup.+4 in the process to make zirconium phosphate and phosphonate analogs and are metals with approximately the same ionic radius as Zr.sup.+4 (0.8 A); for example, the following:

The majority of the polymeric reaction products formed from the above metals are found to be layered crystalline or semicrystalline in nature and, as such, provide layered structures similar to zirconium phosphates. The remainder are amorphous polymers possessing a large quantity of available pendant groups similar to silica gel.

By the term "organophosphorus acid compound," as used herein, there is meant a compound of the formula:

wherein n is 1 or 2, R is any group which will replace a hydroxyl of phosphoric acid and/or the hydrogen of phosphorous acid and couple to the acid by a covalent bond. Coupling to the acid may be through carbon, oxygen, silicon, sulfur, nitrogen and the like. Coupling through carbon or an oxygen-carbon group is presently preferred.

When, in the organophosphorus compound, n is 2, the end product occurs in the bis configuration. In this configuration, R must contain two or more carbon atoms, preferably from two to about 20 carbon atoms, such that at least two carbon atoms separate the phosphorus atoms. In such a configuration R can be considered to have a phosphate or phosphonate termination. In this bis configuration, no single carbon atom is bound directly or indirectly to more than one (PO(OH).sub.2) group. Thus, the groups which link to the metal have the basic structural formula: ##STR1## wherein R" is a bis group containing at least two carbon atoms bonded directly or indirectly to phosphorus and such that no phosphorus atoms are bonded directly or indirectly to the same carbon atom. The basic structures of the inorganic polymer forms are shown in FIGS. 14-16.

When coupling is through carbon, the organophosphorus acid compound is an organophosphonic acid and the product a phosphonate. When coupling is through oxygen-carbon, the organophosphorus acid compound is an organophosphoric monoester acid and the product a phosphate.

The general reaction for phosphonic acids alone is shown in equation (1) below and for monoesters of phosphoric acid alone by equation (2).

wherein R' is the remainder of the organo group.

The product contains phosphorus to metal in a molar ratio of about 2 to 1, and the empirical formula for the product would show all groups bound to phosphorus.

As used herein, R is an acyclic group, heteroacyclic group, alicyclic group, aromatic group or heterocyclic group.

The term "acyclic group," as used herein, means a substituted or unsubstituted acyclic group. The term "acyclic" includes saturated and unsaturated aliphatics which can be straight chain or branched chain. The "aliphatics" include alkyl, alkenyl and alkynyl.

The term "heteroacyclic group," as used herein, means an acyclic group containing one or more heteroatoms in the chain selected from oxygen, nitrogen and sulfur. The heteroatoms can be the same or different in each chain and usually the number of heteroatoms is one, two or three.

The term "alicyclic group," as used herein, means a substituted or unsubstituted alicyclic group. The term "alicyclic" includes saturated and unsaturated cyclic aliphatics.

The term "aromatic groups" as used herein, means a substituted or unsubstituted aromatic group. The term "aromatic" includes phenyl, naphthyl, biphenyl, anthracyl and phenanthryl.

The term "heterocyclic group," as, used herein, means a substituted or unsubstituted heterocyclic group. The term "heterocyclic" means an alicyclic or aromatic group containing one or more heteroatoms in the ring selected from oxygen, nitrogen and sulfur. The heteroatom can be the same or different in each ring and usually the number of heteroatoms is one, two or three.

The terms "substituted acyclic," "substituted heteroacyclic," "substituted alicyclic," "substituted aromatic" and "substituted heterocyclic," as used herein, mean an acyclic, heteroacyclic, alicyclic, aromatic or heterocyclic group substituted with one or more of the groups selected from alkyl, alkenyl, alkynyl, alkoxy, alkenyloxy, alkynyloxy, alkylthio, alkenylthio, alkynylthio, halo, oxo, hydroxy, carbonyl, carboxy, alkylcarbonylloxy, alkylcarbonyl, carboxyalkyl, thio, mercapto, sulfinyl, sulfonyl, imino, amino, cyano, nitro, hydroxyamine, nitroso, cycloalkyl, cycloalkalkyl, aryl, aralkyl, alkaryl, aryloxy, arylalkoxy, alkaryloxy, arylthio, aralkylthio, alkarylthio, arylamino, aralkylamine and alkarylamino.

In general, with phosphorus as the pentavalent, metal, the organo group should occupy no more than about 24 A.sup.2 for proper spacing. This limitation is imposed by the basic crystal structure of zirconium phosphate. Referring to FIG. 4, a spacing of 5.3 A is shown between zirconium atoms in the zirconium plane of a crystal a total area of about 24 A.sup.2 is shown for the space bounded by zirconium atoms. It follows that any group anchored on each available site cannot have an area much larger than the site area and maintain the layered structure.

This limitation can be avoided through the use of a combination of larger and smaller groups, i.e., mixed components. If some of the sites are occupied by groups which have an area much less than about 24 A.sup.2, adjacent groups can be somewhat larger than 24 A.sup.2 and still maintain the layered structure of the compound.

The cross-sectional area which will be occupied by a given organo group can be estimated in advance of actual compound preparation by use of CPK space filling molecular models (Ealing Company) as follows: A model of the alkyl or aryl chain and terminal group is constructed, and it is situated on a scaled pattern of a hexagonal array with 5.3 A site distances. The area of the group is the projection area on this plane. Some areas which have been determined by this procedure are listed in Table I.

The process for the formation of the novel inorganic polymers is a metathesis reaction conducted in the presence of a liquid medium receptive to the tetravalent metal ion at a temperature up to the boiling point of the liquid medium, preferably from ambient to about 150.degree. C. and, more preferably, to about 100.degree. C. at the pressure employed.

While water is the preferred liquid medium with phosphorus, as most of the organophosphorus acid compounds are hygroscopic, an organic solvent, such as ethanol can be employed, where water interferes with the reaction. There need only be provided a solvent for the organo-substituted pentavalent metal acid compound since the tetravalent ion can be dispersed as a solid in the solvent for slow release of the metal ion for reaction with the acid, e.g., the organophosphorus acid compound. If it has a sufficiently low melting point, the organo-substituted pentavalent metal acid compound can serve as a solvent. Typically, the liquid medium is the liquid medium in which the organo-substituted pentavalent metal acid is formed.

To illustrate with phosphorus acids, for complete consumption of the tetravalent compound, the amount of acid employed should be sufficient to provide two moles of phosphorus per mole of tetravalent metal. An excess is preferred. Phosphorous acid and/or phosphoric acid, if present, enters into the reaction and provides an inorganic polymer diluted in respect of the organo group in proportion to the amount of phosphorous or phosphoric acid employed.

Reaction is virtually instantaneous at all temperatures leading to precipitation of layered crystalline, semicrystalline or amorphous solid inorganic polymer.

The amorphous phase appears as a gel similar to silica gel. The gel can be crystallized by extended reflux in the reaction medium, usually from about 5 to about 15 hours. The semicrystalline product is characterized by a rather broad X-ray powder pattern.

The presence of sequestering agents for the metal ion slows down the reaction and also leads to more highly crystalline products. For instance, a semicrystalline solid was prepared by the aqueous phase reaction of zirconium chloride and excess 2-carboxyethyl phosphonic acid, followed by 15 hours of reflux. A highly crystalline modification was prepared under identical conditions except that hydrogen fluoride was added to the reaction mixture. A slow purge of N.sub.2 over the surface of the reaction solution slowly removed the fluoride from the system. Fluoride is a very strong complexing agent for zirconium ions. The slow removal of fluoride results in slow release of the metal ion for reaction with the phosphonic acid, resulting in an increase in crystallinity.

A similar enhancement of crystallinity was obtained in the reaction of thorium nitrate with 2-carboxyethyl phosphonic acid. Nitrate ion is a sequestering agent for thorium and the rate of formation of this product is slow and the product polymer quite crystalline.

As compared to zirconium phosphate forming crystals of 1-5 microns, crystals of 100 to greater than 1000 microns in size have been prepared in accordance with the invention.

A critical property for many of the likely uses of the products is their thermal stability. This is because deficiencies in activity can be compensated for by reasonable increases in operating temperature. A standard method for thermal characterization is thermal gravimetric/differential thermal analysis (TGA/DTA). These techniques indicate changes in weight and heat flow of substances as a function of temperature. Thus, decomposition and phase changes can be monitored as temperature increases.

Zirconium phosphate itself is quite a stable material. Interlayer water is lost at about 100.degree. C., and a second dehydration involving the phosphates occurs above 400.degree. C. The practical ion-exchanging abilities are lost in this step.

The inorganic phosphorus-containing polymers of this invention are also stabilized toward thermal decomposition as compared to pure inorganic analogs as a result of the fixation and separating effect of the inorganic support.

For zirconium chloromethyl phosphonate, for instance, weight loss did not commence until well above 400.degree. C. The organic fragment was half lost at about 525.degree. C., indicating remarkable stability. Decomposition of zirconium 2-carboxyethylphosphonate begins between 300.degree. and 400.degree. C. The decomposition process inflection point, approximate midpoint, falls at about 400.degree. C.

While not bound by theory, phosphates probably decompose like carboxylic esters to yield acid and unsaturates, whereas phosphonates likely form radicals by homolytic cleavage. Both nitrophenyl and cyanoethyl phosphates of zirconium decompose at about 300.degree. C. The phenylphosphonate decomposes at about 425.degree. C.

Besides proving the suitability of such compounds in elevated temperature applications, the TGA analysis affirmed covalent bonding to phosphorus. This is because normal intercalative interactions are reversed within 10.degree. to 100.degree. C. above the boiling point of the guest.

The process of this invention permits a wide variety of inorganic polymers to be formed having the characteristic of the organo group protected by the inorganic polymer structure and with subsequent exchange or substitution reactions, the formation of other inorganic polymers. Polymers formed may be block, random and the like.

For instance, a mixture of phenyl phosphonic acid and phosphorous acid was simultaneously reacted with zirconium ion to yield a single solid phase. The interlamellar distance was the same as zirconium phenyl phosphonate, or about 15.7 A. There was no reflection at 5.6 A, the normal spacing for zirconium phosphite. This established that the largest group should determine interlamellar distance and indicated that a discreet zirconium phosphate phase was not present. Evidence of a change in chemical environment of P-H band was established by infrared analysis. In infrared analysis of zirconium phosphite, P-H stretching is observed as a sharp band at 2470 cm.sup.-1 (moderate intensity). In the mixed compound solid, this band was shifted to 2440 cm.sup.-1 and broadened.

Another route is to exchange one pendant group for another. The exchange reaction is described in Example 131. While not bound by theory, the present expected points of exchange are at the periphery of the crystal and are schematically illustrated in FIG. 6. Such bifunctional materials exhibit the quality of providing terminal groups for attracting species for intercalation and then interaction with the internal groups.

The reaction of bis acids with tetravalent metal ions permits interlamellar cross-linking by a reaction such as ##STR2## whereas in FIG. 6, represents the interlamellar layers to which the alkyl group is anchored. As with all organo groups, for the bis configuration at least two carbon atoms are present, preferably from two to twenty atoms, and the phosphorus atoms are linked directly or indirectly to different carbon atoms. Since size of the linking group will control and fix interlamellar spacing, there is provided effective laminar sieves of fixed spacing for application analogous to that of molecular sieves.

Ion exchange activity was established with pendant carboxylic acid groups. Prepared zirconium 2-carboxyethyl phosphonate was established to have an interlayer distance of 12.8 A. When intercalated to form its n-hexylammonium salt, the interlayer distance increased to 27.2 A. When sodium was taken up, layer spacing increased to 14.2 A. X-ray and infrared data indicated the highly crystalline inorganic polymer to behave as expected for a carboxylic acid, with behavior analogous to ion exchange resins, except that both external and internal surfaces were functional, establishing them as super surface ion exchange resins. Moreover, since the inorganic polymers can be prepared as microcrystalline powders, diffusion distances are short.

As summarized in Table II, nitrile and mercapto anchored groups show the ability to take up silver and copper ions at room temperature for catalytic activity.

The alternate to catalytic utility is to attach the metals to the organophosphorus acid prior to reaction with the soluble tetravalent metal compound.

The high surface area of the crystalline products also makes them useful for sorption of impurities from aqueous and nonaqueous media.

Another utility is as an additive to polymeric compositions. Similar to the high aspect ratio provided by solids such as mica which improve the stress strain properties of the polymers, the powdered inorganic polymer products of the invention can serve the same function and add features. By the presence of reactive end groups on the bonded organo groups, chemical grafting to the polymer network can be achieved to increase composite crystallinity and elevating heat distortion temperature. In addition, the presence of phosphorus induces flame retardant properties, as would bound halogen.

Still other utilities include solid lubricants which behave like mica, graphite and molybdenum disulfide; solid slow release agents where intercalated materials can be slowly leached or released from the internal layers of the crystals; substance displaying electrical, optical phase or field changes with or without doping, and the like.

While nowise limiting, the following examples are illustrative of the preparation of solid inorganic polymers of this invention and some of their utilities.

In the examples conducted in the atmosphere, no extraordinary precautions were taken concerning oxygen or moisture. Reagents were usually used as received from suppliers. The products formed are insoluble in normal solvents and do not sublime. However, the combined weight of yield data, spectroscopy, elemental analyses, TGA and powder diffraction results confirm the compositions reported with good reliability.

X-ray powder patterns were run on a Phillips diffractometer using CuK radiation.

Thermal analyses were conducted on a Mettler instrument. Infrared spectra were obtained with a Beckman Acculab spectrophotometer.

Surface areas were determined using both dynamic flow method, on a Quantasorb instrument, and also with a vacuum static system on a Micromeritic device. Both employ a standard BET interpretation of nitrogen coverage.

Titrations were carried out in aqueous or alcoholic medium. A standard combiation electrode and an Orion Ionalyzer pH meter wre used for pH determination. The titration of the solid interlamellar anchored materials is analogous to the titration of an ion exchange resin.

A solution of 2.990 g of ZrOCl.sub.2.8H.sub.2 O dissolved in 20 ml of deionized water was placed in a round bottom flask fitted with a reflux condenser, stirrer and heating mantle. To this was added 30 ml of an aqueous solution containing 6.040 g of phenylphosphonic acid, with stirring. A white precipitate formed very rapidly. The mixture was heated to about 90.degree. C. and maintained at this level for two days.

After cooling to room temperature, the solid was isolated by filtration, washed with water, washed with acetone, and dried at 55.degree. C. for one hour. The yield was 4.782 g.

The infrared absorption spectrum of this solid indicates the presence of an aromatic substituent in the compound. An X-ray diffraction pattern confirmed the expected interlayer spacing of 14.9 A. Analysis of the solid gave the following results:

These data confirm the empirical formula for the product of Zr(O.sub.3 PC.sub.6 H.sub.5).sub.2.

Using the procedure of Example 1, 1.959 g of ZrOCl.sub.2.8H.sub.2 O in 150 ml of deionized water was reacted with 1.999 g of phenylphosphonic acid and 1 ml of 38% by weight hydrochloric acid. A white precipitate formed very rapidly. The temperature was raised to afford a gentle reflux, which was maintained for 18 hours, followed by cooling to room temperature.

The solid was isolated by filtration, washed with water and dried at 75.degree. C. for one hour, giving a product weight of 2.56 g of Zr(O.sub.3 PC.sub.6 H.sub.5).sub.2, which is approximately 100% of the theoretical yield.

The X-ray diffraction pattern indicates that this product is crystalline, with an interlayer spacing of 15.2 A.

Samples of the product were analyzed by two laboratories for surface area, using a standard BET interpretation of nitrogen coverage obtained both with a dynamic flow method (Quantachrome) and a vacuum static system (Micromeritics). The results were as follows:

These values correspond approximately 50% coverage of the total external and internal (interlamellar) surfaces; the theoretical surface area is about 360 m.sup.2 /g.

Using the method detailed in Example 1 or Example 2, the following compounds were prepared from the reagents listed. The inorganic polymer compounds produced, reagents used, elemental analysis of product, interlayer spacing and polymer structure are listed in the following Table III. In the examples set forth in Table III the M.sup.+4 salt used was ZrOCl.sub.2.8H.sub.2 O. In the last column on the right designated "Str.," the letters C, S and A are used to refer to structures of the compounds that are crystalline, semicrystalline and amorphous respectively. The interlayer spacings for the compounds were determined using X-ray powder diffraction techniques. In the column designated "Other" the elements analyzed are listed immediately following the weight percentage determined.

Using the method outlined in Example 1 or Example 2, the inorganic polymers listed in the following Table IV were prepared. In Table IV the compound produced, phosphorus-containing reagent, M.sup.+4 salt, elemental analysis of product, interlayer spacing and product structure are listed. The weights are listed in grams. When the M.sup.+4 salt is listed as Th(NO.sub.3).sub.4 it is meant Th(NO.sub.3).sub.4.4H.sub.2 O was used in the example. In the column designated "Other" the element analyzed is listed following its determined weight percentage. The interlayer spacings for the compounds were determined using X-ray powder diffraction techniques. In the column designated structure the letters C, S and A are used to designate crystalline, semicrystalline and amorphous configurations respectively.

Using the method outlined in Examples 1, the following compounds are prepared:

An aqueous solution of organic compounds for use in sorption experiments was prepared by shaking 25 ml of chloroform, 25 ml of toluene and 25 ml of hexane in a separatory funnel with 100 ml of deionized water for ten minutes. After settling for five minutes, the aqueous layer was separated and stored in a stoppered flask.

A gas chromatographic analysis of the aqueous solution yielded peaks for ethanol (a stabilizer present in the chloroform reagent used), chloroform and water. The ratio of chloroform peak area to ethanol peak area was determined for two samples at 15 minute intervals prior to beginning the sorption experiment.

A 3.060 g portion of the product, Zr(O.sub.3 PC.sub.6 H.sub.5).sub.2, from Example 1 was added to the aqueous solution, the stopper replaced, and the mixture agitated briefly. After 15 minutes, a sample was withdrawn for gas chromatographic analysis. The mixture was agitated, then allowed to settle for about five minutes prior to obtaining each of the remaining samples in the experiment.

Ethanol was not extracted from the solution in a significant amount. However, more than 50 percent of the chloroform was extracted by the Zr(O.sub.3 PC.sub.6 H.sub.5).sub.2 compound. This indicates the utility as a selective sorbent which removes specific contaminants from solutions, while leaving other dissolved materials in solution.

An aqueous solution of organic compounds for use in absorption experiments was prepared by shaking 25 ml of chloroform, 25 ml of benzene and 25 ml of n-hexanol in a separatory funnel with 100 ml of deionized water. After settling, the aqueous layer was separated and placed into a 125 ml Erlenmeyer flask containing a stirring bar and the flask was sealed. This solution was stirred continuously during sampling and experimentation. First, some samples were taken about every 15 minutes to establish a baseline concentration of each organic in the water.

A 2.442 g sample of ground ##STR10## was added quickly to the solution. This mixture was shaken for a minute to prevent the solid from floating on the water. Aqueous samples were taken after allowing the solid to partially settle in order to obtain a clear solution for gas chromatographic analysis.

On gas chromatograph testing, a slow but continuous drop of organics and then a sudden drop in concentration of all three (n-hexanol, benzene and chloroform) was shown when the ##STR11## was added to the system. A leveling off occurred after the initial rapid extraction and at time infinity.

A plot of the area of an ethanol peak from gas chromatography data shows a fairly constant concentration of the ethanol throughout the whole experiment indicating it is a reliable internal reference peak. Ethanol seemed more soluble in water over the solid. The ethanol came from the chloroform used in the experiment. The chloroform contained about one percent ethanol stabilizer. The ##STR12## had an affinity to absorb the organic compounds. The weight distribution coefficient (K.sub.wt) and the molar distribution coefficient (K.sub.m) for the n-hexanol, chloroform and benzene were determined to be as follows for the

These results indicate the utility of the compound as a selective sorbent which can remove specific contaminants from solutions while leaving other dissolved materials in the solution.

A 25 ml sample of water was saturated by contact with 5 ml of a solution of equal parts of benzene, chloroform, and 1-hexanol. Twenty ml of the saturated aqueous solution was removed and transferred to a stoppered 50 ml flask. To the solution was added 0.1 ml of ethanol as an internal standard for gas chromatographic analysis. The area ratio of each component to the standard was determined. Then 0.5 g of zirconium chlorophenyl arsonate was added with agitation. Within 30 minutes, equilibrium was established. The area ratio of each component to the standard was again determined. As is evident in the table below, the concentration of all components decreased substantially.

Titanium phenylphosphonate having a surface area of about 151-167 m.sup.2 /g was evaluated as sorption solid. A sample of water was contaminated with 1-hexanol (1700 ppm), chloroform (1100 ppm) and benzene (300 ppm). One hundred ml of this solution was treated with 2.4 g of the titanium phenylphosphonate. Analysis established that the solid absorbed the organics. The distribution coefficients were 750 (benzene), 430 (1-hexanol) and 250 (CHCl.sub.3). Absorption of benzene was preferred.

Extraction of palladium +2 ion from aqueous solution by ion exchange with Zr(O.sub.3 PO).sub.8/5 (O.sub.3 PCH.sub.2 CH.sub.2 CO.sub.2 H).sub.2/5.

A solution of palladium (II) chloride was prepared by dissolving about 1.0 g of commercially available palladium (II) chloride in about 100 ml of water under a nitrogen purge. A small amount of undissolved material was removed by filtration. The pH of this solution was 2.90. To this solution was added 3.0 g of Zr(O.sub.3 PO).sub.8/5 (O.sub.3 PCH.sub.2 CH.sub.2 CO.sub.2 H).sub.2/5. The pH decreased to 2.35. Using an auto-titrator in a pH stat mode, the pH was raised in small steps to 3.5 by addition of 0.10 N aqueous sodium hydroxide. The pale yellow solid product was isolated by filtration and washed successively with water, acetone and ethyl ether. After oven drying, elemental analysis indicated 3.72% Pd content of the solid phase.

This example demonstrates the extraction of a precious metal, more broadly a Group VIII metal, from solution. The palladium-containing product incorporates a catalytically active species and represents a novel example of a heterogenized or anchored catalyst which can be used for the reactions shown in the J. C. Bailar and Hartley & Vezey publications incorporated herein.

The usefulness of a tetravalent metal carboxyorgano phosphonate was shown in an experiment which tested the ability of the compound to extract copper ions from aqueous solutions.

In the experiment, 1.00 g of the compound was mixed with 40 ml of 0.103 M copper solution having a pH of 4.01 and, after about 30 minutes, a 10 ml aliquot of the solution phase was removed, its pH being 2.19. The remaining slurry was treated with 4 ml of 2.5 percent of sodium hydroxide solution and, after about 10 minutes, the liquid, with a pH of 3.93, was removed. A second 1.11 g portion of the compound was mixed with 40 ml of the 0.103 M copper solution, and 2.0 ml of 2.5 percent sodium hydroxide solution was added. After about 15 minutes, a 10 ml aliquot of the supernatant liquid, which had a pH of 3.39, was removed. The remaining slurry was treated with 5.0 ml of 2.5 percent sodium hydroxide solution.

The ion exchange capability of a tetravalent metal sulfo-organo phosphonate was demonstrated for both the sulfonic acid and sodium sulfonate forms of that compound.

A 0.50 g portion of the acid form was slurried with 10 ml of 0.215 N copper sulfate solution. The pH of the solution was initially 3.80 but immediately dropped to 0.92, the initially white solid became a pale blue color, and the blue solution color decreased markedly in intensity. Atomic absorption analysis of the solution after exchange indicated a copper concentration of 0.093 N, for copper loading in the solid of 2.46 meq/g, or 77 percent of the theoretical capacity.

The exchange experiment was repeated with the sodium sulfonate form of the compound. After exchange, the solution had a pH of 2.88 and a copper content of 0.135 N. Loading of the solid was calculated as 1.62 meq/g, or 51 percent of the theoretical capacity.

A tetravalent metal sulfo-organo phosphonate was used as a catalyst in an esterification reaction. A 0.503 g portion was added to a distillation flask containing 2.85 ml of acetic acid and 2.85 ml of denatured ethanol. The mixture was heated and a distillate product collected. This product was identified by gas chromatography and infrared spectrophotometry as ethyl acetate.

The solid phase of the reaction mixture was recovered and weighed 0.51 g. Its X-ray diffraction pattern matched that of the initial material added.

A slurry of 0.100 g of a tetravalent metal sulfo-organo phosphonate and 1.0 g cyclohexanol was heated to 125.degree. C. in a micro distillation apparatus. An essentially quantitive yield of cyclohexene was recovered in the distillate receiver, indicating utility of the compound as a catalyst for dehydrating alcohols.

In an experiment to determine the ability of a tetravalent metal mercapto-organo phosphonate to extract silver ions from solution, 0.076 g of the compound was shaken in a vial with 5 ml of 0.10 M silver nitrate. The mixture was allowed to stand for several days, after which a sample of the supernatant liquid was decanted for analysis.

The original silver solution was found to contain 4.96 g/l silver, indicating that 5.85 g/l silver was extracted by the compound.

An experiment was performed to determine the ability of a layered cyano end terminated polymer to extract copper ions from aqueous solution. A 0.09 g portion of a tetravalent metal cyano-organo phosphate compound was mixed with 5 ml of a solution containing 0.1 MCuSO.sub.4, 0.5 MCH.sub.3 COONa and 0.5 MCH.sub.3 COOH. The mixture was permitted to stand for a day and a portion of the supernatant liquid was decanted and analyzed for copper.

The initial copper solution contained 6.45 g/l Cu and the extracted solution contained 5.94 g/l Cu, indicating an extraction of 0.51 g/l copper.

To 100 ml three-necked flask was charged 5.0 g of a tetravalent metal carboxyorgano phosphonate, 40 g n-butanol and 10 g H.sub.2 O. To this was added 3 ml of HCl as catalyst. The slurry was refluxed and water removed azeotropically. After about one day, 40 ml of fresh butanol was added and azeotropic distillation continued for about a week. The product was isolated by filtration and washed with acetone and ethyl ether. The dry product weighed 5.44 g. The infrared spectrum clearly shows the conversion from the carboxylic acid to the ester. This material can be used as a host or carrier for biologically active organic molecules (e.g., methoprene).

The above procedures of Examples 28-39 are illustrative of simple utility screening tests which can be used to show ways of using the solid compounds of the invention whether crystalline, semicrystalline, or amorphous. Of course, the tests are preferably modified by the skilled chemist to suit the fundamental character of the compound being tested and the desired end use. Other well-known test procedures can also be used.