Method of Fabricating Fatigue Resistant Optical Fibers
Issue Date:1981-12-22
•30 Claims
•1 Drawing Sheets
Abstract
The fatigue resistant optical fiber is fabricated by producing an optical fiber having an electrically conducting surface, heating the produced optical fiber, and coating the heated optical fiber with a material impervious to water and water vapor.
Metadata
Assignee
- International Telephone and Telegraph Corporation
Inventor
- Mokhtar S. Maklad
Application Information
Application Number:US 140900&
Filing Date:1980-04-16
Priority Date:1980-04-16
Art Unit:173
Classifications
IPC:
C03B 3200C03B 37025C03B 37075C03C 2502
Field of Search:
654272643503 A;3 B;3.1;3.11;3.12;3.31;3.41;18.2163;45.1;52;126.2;166;1671.2;1.4;1.596.29;96.30;96.33;96.34
Patent Drawings (1 sheets)
Description
Background of the Invention
This invention relates to optical fibers and more particularly to a method of fabricating a fatigue resistant optical filter.
Summary of the Invention
An object of the present invention is to provide an improved method of fabricating a fatigue resistant optical fiber.
A feature of the present invention is the provision of a method of fabricating a fatigue resistant optical fiber comprising the steps of producing an optical fiber having an electrically conducting surface; heating the produced optical fiber; and coating the heated optical fiber with a material impervious to water and water vapor.
Brief Description of the Drawing
Above-mentioned and other features and objects of this invention will become more apparent by reference to the following description taken in conjunction with the accompanying drawing, in which:
FIG. 1 is a schematic diagram of a circuit employed to provide DC (direct current) heating of the optical fiber in the heating step in the method according to the principles of the present invention; and
FIG. 2 is a circuit diagram for RF (radio frequency) power heating of the optical fiber in the heating step of the method according to the principles of the present invention.
Description of the Preferred Embodiments
The method of fabricating a fatigue resistant optical fiber in accordance with the principles of the present invention comprises the steps of producing an optical fiber to have an electrically conducting surface, heating the produced optical fiber and coating the heated optical fiber with a material which is impervious to water and water vapor.
Basically the step of producing the optical fiber having an electrically conducting surface includes the steps of preparing an optical preform by a chemical vapor deposition technique, preparing an electrically conducting silica substrate tube containing carbon and placing the preform inside the tube. At this point in the producing step the optical fiber can be produced by two different embodiments. The first embodiment includes collapsing the tube onto the perform. The second embodiment includes the step of drawing the preform and the tube to provide the optical fiber.
The electrically conducting silica substrate tube containing carbon can be prepared as described in U.S. Pat. No. 2,556,616, issued on June 12, 1951 to R. B. Ellis.
The heating of the optical fiber having the electrically conducting surface can be accomplished by employing DC heating as illustrated in FIG. 1, wherein the optical fiber 1 having an electrically conducting surface, has a direct current voltage applied thereto from DC source 2 coupled to spaced mercury electrodes 3 and 4.
Alternately, the heating of the optical fiber having an electrically conducting surface can be provided by RF power heating as illustrated in FIG. 2 wherein the optical fiber 1 is heated by radio frequency power supplied from source 5 to RF coil 6.
There are two embodiments of the step of coating the heated optical fiber with a material impervious to water and water vapor. The first embodiment includes employing a chemical vapor deposition technique to coat the heated optical fiber with the impervious material and the second embodiment includes employing a thermal deposition technique to coat the heated optical fiber with the impervious material.
Below there are listed examples of materials and from where they are obtained to provide the impervious coating on the heated optical fiber.
(1) Si.sub.3 N.sub.4 which is obtained from SiH.sub.4 +NH.sub.3 or SiCl.sub.4 +NH.sub.3.
(2) Silicone oxynitride which is obtained from SiH.sub.4 +NH.sub.3 +H.sub.2 O, or SiCl.sub.4 +NH.sub.3 +H.sub.2 O.
(3) Carbon obtained by the thermal dissociation of a hydrocarbon.
(4) Nickel obtained from the thermal dissociation of nickel carbonyl.
While I have described above the principles of my invention in connection with specific apparatus it is to be clearly understood that this description is made only by way of example and not as a limitation to the scope of my invention as set forth in the objects thereof and in the accompanying claims.
Claims
I claim:
1. A method of fabricating a fatigue resistant optical fiber, comprising the steps of: producing a completely formed, unsupported optical fiber having an electrically conducting surface; heating said produced optical fiber; and coating said heated optical fiber with a material impervious to water and water vapor; said step of producing including the steps of preparing an optical preform by a chemical vapor deposition technique, preparing an electrically conducting silica substrate tube containing carbon, placing said preform inside said tube, and collapsing said tube onto said preform to provide said produced optical fiber.
2. A method according to claim 1, wherein said step of heating includes direct current heating of said produced optical fiber.
3. A method according to claim 2, wherein said step of coating includes the step of employing a chemical vapor deposition technique to coat said heated optical fiber with said material.
4. A method according to claim 3, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
5. A method according to claim 2, wherein said step of coating includes the step of employing a thermal dissociation technique to coat said heated optical fiber with said material.
6. A method according to claim 5, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
7. A method according to claim 1, wherein said step of heating includes radio frequency power heating of said produced optical fiber.
8. A method according to claim 7, wherein said step of coating includes the step of employing a chemical vapor deposition technique to coat said heated optical fiber with said material.
9. A method according to claim 8, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
10. A method according to claim 7, wherein said step of coating includes the step of employing a thermal dissociation technique to coat said heated optical fiber with said material.
11. A method according to claim 10, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
12. A method according to claim 1, wherein said step of coating includes the step of employing a chemical vapor deposition technique to coat said heated optical fiber with said material.
13. A method according to claim 12, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
14. A method according to claim 1, wherein said step of coating includes the step of employing a thermal dissociation technique to coat said heated optical fiber with said material.
15. A method according to claim 14, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
16. A method of fabricating a fatigue resistant optical fiber, comprising the steps of: producing a completely formed, unsupported optical fiber having an electrically conducting surface; heating said produced optical fiber; and coating said heated optical fiber with a material impervious to water and water vapor; said step of producing including the steps of preparing an optical preform by a chemical vapor deposition technique, preparing an electrically conducting silica substrate tube containing carbon, placing said preform inside said tube, and drawing said preform and said tube to provide said produced optical fiber.
17. A method according to claim 16, wherein said step of heating includes direct current heating of said produced optical fiber.
18. A method according to claim 17, wherein said step of coating includes the step of employing a chemical vapor deposition technique to coat said heated optical fiber with said material.
19. A method according to claim 18, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride carbon and nickel.
20. A method according to claim 17, wherein said step of coating includes the step of employing a thermal dissociation technique to coat said heated optical fiber with said material.
21. A method according to claim 20, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
22. A method according to claim 16, wherein said step of heating includes radio frequency power heating of said produced optical fiber.
23. A method according to claim 22, wherein said step of coating includes the step of employing a chemical vapor deposition technique to coat said heated optical fiber with said material.
24. A method according to claim 23, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
25. A method according to claim 22, wherein said step of coating includes the step of employing a thermal dissociation technique to coat said heated optical fiber with said material.
26. A method according to claim 25, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
27. A method according to claim 1, wherein said step of coating includes the step of employing a chemical vapor deposition technique to coat said heated optical fiber with said material.
28. A method according to claim 27, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
29. A method according to claim 1, wherein said step of coating includes the step of employing a thermal dissociation technique to coat said heated optical fiber with said material.
30. A method according to claim 29, wherein said material is selected from a group of materials consisting of Si.sub.3 N.sub.4, silicone oxynitride, carbon and nickel.
Patent Citations (13)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US1771055 | 1930-07-01 | Pender | |
| US2556616 | 1951-06-01 | Ellis | |
| US3850689 | 1974-11-01 | Basche et al. | |
| US3877912 | 1975-08-01 | Shiraishi et al. | |
| US4118211 | 1978-10-01 | Au Coin et al. | |
| US4173393 | 1979-11-01 | Maurer | |
| US4183621 | 1980-01-01 | Kao et al. | |
| US4227907 | 1980-10-01 | Merritt | |
| DEX2415052 | 1975-10-01 | ||
| DEX2818036 | 1978-11-01 | ||
| JPX51-50745 | 1976-05-01 | ||
| GBX1185260 | 1970-03-01 | ||
| GBX1559768 | 1980-01-01 |