Method of Making a Metal Catalyst Support

U.S. Pat. No. 4,162,993 describes a catalyst support formed by winding a single strip of metal upon itself, wherein the spacing between layers of the spiral is uniform and equal to the height of the indentations in the strip. The indentations are spaced along the strip in a pattern that varies, and is not repeated in any layer of the spiral. By varying the pattern in this way, the indentations in successive layers are prevented from nesting together. If the indentations are formed by passing the strip between a pair of die wheels, and if the circumference of the die wheels is at least as great as the diameter of the finished spiral, and if the pattern of spacing is not repeated around the circumference of the die wheels, then the indentations in successive layers cannot nest together. This is the essence of U.S. Pat. No. 4,162,993. It is an economical way to construct spirals of small diameter, say for automobile mufflers and for small catalytic combustors. But for spirals having a diameter of more than about 20 cm., the cost of the die wheel is excessive. An object of the present invention is to enable us to wind spirals of any diameter, using die wheels having a diameter that is both smaller than, and independent of, the diameter of the spiral.

FIG. 1 shows a spiral being wound onto a mandrel. There is a pointer 10 that rotates with the mandrel. Whenever the pointer passes through some fixed point, say 12 o'clock, it trips a mechanism that changes the pattern being wound onto the spiral. Whether the mechanism be mechanical or electric is immaterial. What is important is that the pattern being wound onto the spiral is changed automatically at the beginning of each new layer. Also shown in FIG. 1 are a first and second set of die wheels, 11 and 12. How they cooperate is explained later on.

FIG. 2 is a perspective view of a fragmentary portion of a single strip showing first and second rows of indentations of uniform height.

All that is necessary to prevent successive layers from nesting together is that the pattern formed by the indentations be different in successive layers. This can be accomplished with just two different patterns that repeat in alternate layers. More than two patterns can be used, but two are sufficient. FIG. 1 indicates some methods for winding a spiral having just two patterns that repeat in alternate layers.

These methods are:

1. The first pair of die wheels 11 is in mesh continuously.

The second pair 12 is in mesh only while alternate layers are being wound onto the spiral. Pair 12 prints one or more rows of indentations between the rows already printed by pair 11.

2. There is only one set of die wheels, be it the first or second set in FIG. 1. The pattern being printed is not centered on the center line of the strip, so that there is a wider border along one side of the strip, and a narrower border along the other side. Upon signal from the pointer 10, the strip stops, the die wheels are parted and moved across the strip, so that the positions of the wide and narrow borders are reversed. Then printing is resumed.

3. This is the same as Method 2, except that the strip is not stopped upon signal, but instead the strip is urged to the opposite side of the die wheels, to reverse gradually the positions of the borders.

4. There is only one pair of die wheels. Instead of printing the indentations in FIG. 2, the wheels corrugate the strip. The resulting spiral resembles those in U.S. Pat. Nos. 3,770,389 and 3,891,575, except that it is wound from a single strip instead of from one flat and one corrugated strip.

5. Now let us wind a spiral having more than two patterns. One method would be to have a pair of die wheels for each pattern. Upon signal from the pointer, the strip stops, and the single pair of die wheels is changed.

FIG. 2 shows the preferred shape for the indentations. This shape is cylindrical, which means that the surface is generated by a straight line that remains parallel to its original position as it generates the surface. The ends of the indentations are open. The indentations are aligned perpendicular to the length of the strip, and therefore parallel to the axis of the spiral. The indentations present only the edge of the indented metal to the gas flowing through the spiral.

As is seen in FIG. 1 (and also as is claimed in U.S. Pat. No. 4,162,993, cited above), the indentations are of uniform height, so that the spacing between layers of the spiral is equal to this height. When Method Nos. 1, 2, 3, or 5, described above, are used, different patterns are wound onto successive layers of the catalyst support, so that the indentations in successive layers cannot coincide and nest together.

The metal catalyst support is coated with a catalyst by processes known in the art.