US 4,272,585 AGrant
Process for Treating Polyvinylidene Fluoride and Resulting Products
Issue Date:1981-06-09
•9 Claims
Abstract
The present invention relates to a process for treating polyvinylidene fluoride surfaces to enhance adhesion of other polymers thereto comprising applying to at least one surface thereof a solution consisting essentially of a coating polymer selected from a polyurethane or an alkyl polymethacrylate and at least one aprotic polar solvent in which said polymer is soluble, and exposing said surface to a temperature of from about 100.degree. to 300.degree. C. for a time sufficient to evaporate said solvent.
Metadata
Assignee
- Produits Chimiques Ugine Kuhlmann
Inventor
- Albert Strassel
Application Information
Application Number:US 1003763
Filing Date:1979-12-05
Priority Date:1976-04-06
Art Unit:162
Classifications
IPC:
B32B 2738B32B 2740
Field of Search:
427428156138421;428;429;412.4;386;387;208.4;208.8;385.5;393.5;412.4;430.1413;421;424;424.6327;331146;177;DIG. 3;DIG. 7;137;141;145;140
Patent Drawings
This patent does not have any drawings.
Description
BACKGROUND OF THE INVENTION
The adhesion of polyvinylidene fluoride (hereinafter PVF.sub.2) to other polymers is generally minimal or nonexistent. This enables PVF.sub.2 to be used as an unmolding surface (stripping surface) for certain resins even at very high temperatures.
To effect adhesion of other polymers to PVF.sub.2 it is necessary to use expensive and extensive treatments of the PVF.sub.2 surface which treatments are, therefore, not commercially satisfactory.
SUMMARY OF THE INVENTION
According to the present invention, it has been found that polymers can be made to adhere satisfactorily to PVF.sub.2 by a simple and inexpensive treatment of PVF.sub.2 surfaces.
Briefly stated, the present invention comprises a process for treatment polyvinylidene fluoride surfaces to enhance adhesion of other polymers thereto comprising applying to at least one surface thereof a solution consisting essentially of a coating polymer selected from a polyurethane or an alkyl polymethacrylate and at least one aprotic polar solvent in which said polymer is soluble, and exposing said surface to a temperature of from about 100.degree. to 300.degree. C. for a time sufficient to evaporate said solvent. The invention also comprises the further step of adhering to said treated surfaces other polymers and the resultant products.
DETAILED DESCRIPTION
Although polyurethanes and alkyl polymethacrylates generally do not adhere to PVF.sub.2, it was found that after application to the PVF.sub.2 of a polyurethane or alkyl polymethacrylate solution in an aprotic polar solvent and evaporation of the solvent, these polymers adhere to PVF.sub.2.
The category of aprotic polar solvents is known. It is described and illustrated by A. J. Parker in Quarterly Reviews (1962) 16, pages 163-187. The following can be cited as examples of aprotic polar solvents: dimethylformamide, dimethylacetamide, tetrahydrofurane, dimethylsulfoxide, cyclohexanone, hexamethylphosphoramide, tetramethylurea or solvents of the same family. These solvents are known as hot solvents of PVF.sub.2.
Any type of polyurethane may be deposited on the PVF.sub.2 surface as long as it is soluble in aprotic polar solvents or mixtures thereof. However, it is an advantage to select linear polyurethanes or slightly reticulated polyurethanes such as those derived from the well-known reaction of a polyether polyol and/or polyester on a polyisocyanate, generally in the presence of a catalyst, or even polyurethanes comprising urea groups in the chain derived from the equally known reaction of a polyether polyol and/or polyester on a polyisocyanate in excess in the presence of a polyamine, an amino alcohol and/or water.
It is also possible to use polyurethanes or polyurethane polyureas obtained either from mixtures of polyether polyols and/or polyesters or their copolymers or even polyols comprising grafts such as acrylonitrile, .alpha.-acrylonitrile styrene, methyl styrene, vinyl chloride, vinylidene chloride, methyl methacrylate.
Linear polyurethanes or polyurethane polyureas derived from difunctional compounds, such as diols, diisocyanates and diamines and/or amino alcohols and/or water and polyurethanes or polyurethane polyureas obtained by reacting an excess of hydroxyl functions relative to isocyanate functions so as to produce free associations favorable to adhesion irrespective of whether the polyurethanes are of the polyether or polyester type or both at the same time are preferably used.
The alkyl polymethacrylates are preferably C.sub.1 or C.sub.2 alkyl methacrylates with poly(methyl methacrylate) or a copolymer containing at least 85% by weight poly(methyl methacrylate) preferably used as the alkyl polymethacrylate.
The polyurethane or alkyl polymethacrylate is placed in solution in the aprotic polar solvent or solvents in a concentration of 1-50% by weight. Non-polar aprotic solvents such as ketones, esters, aromatic or aliphatic solvents can also be added in minor amounts to ultimately reduce the viscosity of the solution.
The solution is prepared by dissolving polyurethane or alkyl polymethacrylate in an aprotic polar solvent or a mixture of solvents containing at least one aprotic polar solvent. The polyurethane solution can also be prepared by producing polyurethane in situ by causing its constituents to react under known conditions in an aprotic polar solvent or a mixtures of solvents containing at least one aprotic polar solvent.
The polyurethane or alkyl polymethacrylate solution is applied to the PVF.sub.2 under ambient conditions and by conventional means; for example, by means of a roller, scraper, brush, by spraying, soaking, and the like. The PVF.sub.2 is then heated at a temperature of 100.degree. to 300.degree. C. for sufficient time to evaporate the solvent. This time period, which depends on the thickness of the polyurethane solution coating layer is generally in the order of a few minutes and, in most cases, a period of 1 to 10 minutes is sufficient. In the painting and varnishing trade the time required to evaporate the solvent is determined by the touch test; when a finger is applied, no mark should be left on the treated surface, and this test can be used as a standard to determine the necessary drying time for the instant process.
A polyurethane or alkyl polymethacrylate, which subsequently serves as an intermediary for making an exterior polymer adhere to the PVF.sub.2, is attached to the PVF.sub.2 surface after it has been treated in the above manner. Accordingly, the polymers which can be made to adhere to the PVF.sub.2 are preferably those which adhere to the polyurethane or alkyl polymethacrylate without any intermediary. Of these polymers it is possible to cite the following as examples: polyesters, epoxides, silicons, polysulfides, phenolics, chlorinated rubbers, polyvinyls, polyurethanes, polyacrylics and copolymers thereof such as acrylonitrilebutadiene-styrene or acrylonitrile-butadiene resins.
These exterior polymers can be made to adhere to the PVF.sub.2 by different known means, as, for example, by applying on the treated surface either components which produce the polymer by reaction in situ or polymerizable resins or even by thermal gluing or bonding of the polymer to the treated surface.
PVF.sub.2 surfaces which have been treated by the process according to the invention can also be subjected to all the different treatments which are generally carried out on a polyurethane surface such as painting, metalizing, and the like.
The process according to the invention is applicable to any type of PVF.sub.2 material such as sheets, panels, webs, tubes, any compression or injection molded article or even heat molded articles thereof.
The invention will be further described in the examples that follow which are set forth for purposes of illustration only.
EXAMPLE 1
A 4 mm. thick PVF.sub.2 sheet produced by extrusion through calender rolls is coated at 20.degree. C. by means of a brush with a dimethylformamide solution containing 20% by weight dry extract of a linear polyurethane polymer derived from the reaction of polyethylenglycol adipate (molecular weight 2,000), diphenylmethane diisocyanate, and water.
The reaction takes place under nitrogen for 5 hours at 90.degree. C. in the total quantity of dimethylformamide until the free isocyanate functions have disappeared; the relation ##EQU1##
The sheet which has been coated in this manner is placed in an oven at 140.degree. C. for 3 minutes.
A polyester-glass stratification process is carried out on the cooled treated surface; the polyester consisting of an orthophthalic unsaturated polyester resin containing methyl methacrylate (UKAPON T 215 MRL, Produits Chimiques Ugine Kuhlmann).
Upon hardening of the polyester, excellent adhesion of the stratified layer to the PVF.sub.2 was noted.
EXAMPLE 2
A solution containing 15% by weight solid polyesterpolyurethane (DESMOCOLLE 500, Farbenfabriken Bayer) in dimethylacetamide is prepared at room temperature.
This solution is pulverized on a PVF.sub.2 web having a thickness of 400.mu.. This web is allowed to stand for 5 minutes at 150.degree. C. in a ventilated oven.
One week later the epoxide components necessary to form an epoxy resin (Araldite AV 138 and its adjuvants, Ciba) are poured onto the treated surface of the web. Perfect adhesion between the different polymers is noted after polymerization of the epoxide.
EXAMPLE 3
A solution containing 20% by weight of the same linear polyurethane as used in Example 1 in dimethylacetamide is applied by brush to a PVF.sub.2 web having a thickness of 200.mu.. After evaporating the solvent at 170.degree. C. for 2 minutes, the treated PVF.sub.2 is stored.
Three days later this web is heat bonded by high frequency to a 5/10 mm. thermoplastic polyurethane sheet. Excellent adhesion is obtained between the different polymers.
By comparison, it was found that there was no adhesion between the same untreated PVF.sub.2 web and the 5/10 mm. thermoplastic polyurethane sheet when heat bonded by high frequency.
EXAMPLE 4
The viscosity of a solution of linear polyurethane as used in Example 1, but obtained from polyoxypropyleneglycol having a molecular weight of 2,000 instead of polyethylenglycol adipate, is lowered by adding 15% by weight methylethyl ketone.
This solution is sprayed on a PVF.sub.2 web having a thickness of 25.mu. and the solvents are evaporated at 140.degree. C. in a ventilated oven over a period of 3 minutes.
After cooling, the web is rolled and stored at room temperature.
Three weeks later the web is unrolled and a chlorinated polyester diol resin (UKADIOL 74,300, Produits Chimiques Ugine Kuhlmann) is poured onto the treated surface. Polyester-glass stratification is carried out by conventional methods. Polyester panels coated with a PVF.sub.2 protective adhesive layer are thereby produced.
EXAMPLES 5 and 6
Dimethylformamide solutions containing 10 and 40% by weight dry extract of polyurethane polyurea are prepared by reacting a mixture containing the constituents listed hereafter in dimethylformamide at 75.degree. C. for 3 hours:
1,000 g. of a 1/1 by weight mixture of polyoxypropylene glycol, molecular weight 2,000; polyethylenglycol adipate molecular weight 2,000; 20 g. butanediol; 4 g. water; and toluene diisocyanate such that the relation reagent NCO/OH=0.95.
The cooled solutions are thereafter used as in Example 1.
EXAMPLE 7
After treating a PVF.sub.2 sheet having a thickness of 1 mm. as described with a liquid polyurethane as set forth in Example 4, it is placed at the bottom of a mold for molding rigid polyurethane foams. Components A and B, below, are mixed at room temperature and poured into the mold. Panels consisting of rigid polyurethane foams coated with adhering, weather-resistant PVF.sub.2 are thereby obtained.
EXAMPLE 8
A solution containing 20% by weight dry extract of a linear polyurethane polymer derived from the reaction of polyethylenglycol adipate, molecular weight 2,000, diphenylmethanediisocyanate and water in dimethylformamide is applied by brush at room temperature to a PVF.sub.2 web having a thickness of 100 microns and extruded by the blowing process.
The reaction is carried out under nitrogen for 5 hours at 90.degree. C. in the total quantity of dimethylformamide until the free isocyanate functions have disappeared; the relation ##EQU2##
The web coated in the solution is placed in an oven at 100.degree. C. for 4 minutes. The web is then rolled with a paper comprising a silicone coated face which acts as the antiadhering intermediary. After a storage period of three months, the web is unrolled and is passed between calender rollers heated to 130.degree. C. A 2 mm. thick sheet of acrylonitrilebutadiene-styrene copolymer is simultaneously calendered between these rollers; the treated face of the PVF.sub.2 being disposed in contact with the copolymer sheet. After cooling, a copolymer sheet coated with a PVF.sub.2 web having excellent adhesive properties is obtained.
EXAMPLE 9
The viscosity of a linear polyurethane solution as described in Example 8, but produced from polyoxypropylene glycol, molecular weight 2,000, instead of polyethyleneglycol adipate is reduced by adding 15% by weight methylethylketone.
This solution is applied by brush to a PVF.sub.2 panel having a thickness of 4 mm. The solvent is then evaporated at 100.degree. C. for 1 hour. A chlorinated polyester diol resin (UKADIOL 74,300, Produits Chimiques Ugine Kuhlmann) is poured onto the treated face of the cooled panel. The polyester-glass stratification process is carried out by conventional methods.
Stratified polyester panels coated with adhering, protective PVF.sub.2 are thereby produced.
EXAMPLE 10
A solution containing 15% by weight solid polyurethane polyester (DESMOCOLLE 420, Farbenfabriken Bayer) in dimethylacetamide is prepared at room temperature. Three grams of a solution containing 20% triphenylmethanediisocyanate in methylene chloride (DESMODUR R, Farbenfabriken Bayer) are added to 100 grams of this solution.
This preparation is immediately applied by brush to a 3 mm. thick PVF.sub.2 panel. The PVF.sub.2 panel is then placed in an oven at 100.degree. C. for 15 minutes.
A polyester-glass stratification process is then carried out as described in Example 9. Upon reticulation, a stratified polyester panel covered with adhering, protective PVF.sub.2 is obtained.
EXAMPLE 11
15 g. of a polymethymethagrylate having a molecular weight of approximately 120,000 are dissolved in 85 g. dimethylformamide. This solution is applied to a 4 mm. thick PVF.sub.2 panel by means of a brush. The solvent is evaporated by allowing the PVF.sub.2 panel to remain in a ventilated oven at 150.degree. C. for 5 minutes.
A polyester-glass stratification process is carried out by conventional methods on the surface of the treated cooled PVF.sub.2 panel. The polyester is an orthophthalic unsaturated polyester resin containing methylmethacrylate (UKAPON T 215 MRL, Produits Chimiques Ugine Kuhlmann).
Upon hardening of the polyester, excellent adhesion of the stratified layer to the PVF.sub.2 is noted.
EXAMPLE 12
50 g. ethyl acetate are added to 100 g. of the solution according to Example 11. This new solution is applied by means of a coating machine equipped with scraper to a 50.mu. thick PVF.sub.2 web. The web is allowed to remain for 3 minutes in an oven at a temperature of 165.degree. C.
A 2 mm. thick panel of acrylonitrile-butadiene-styrene copolymer is made to adhere to the treated surface of the PVF.sub.2 web by a thermal bonding operation. The thermal bonding operation consists in applying the treated face of the PVF.sub.2 on the copolymer panel and passing the two together between the cylinders of a calender heated to 130.degree. C. Perfect adhesion of the PVF.sub.2 to the copolymer is obtained.
EXAMPLE 13
The tests of this example demonstrate the relationship existing between the evaporation temperature of the solvent and the influence of the aprotic polar solvent used in the solution. The polyurethane used in these tests consisted of a polymer prepared by the reaction in toto of a mixture of 100 parts by weight butanediol polyadipate (molecular weight 2,000) and 3 parts by weight butanediol which had been dehydrated in advance at 70.degree. C. with fused diphenylmethane diisocyanate at 50.degree. C. in an NCO/OH ratio of 1. After stirring the reagents for 5 minutes, the liquid mixture is poured into a mold and baked at 140.degree. C. for 14 hours.
(a) A polyurethane solution containing 20% by weight dry extract in dimethylformamide coated on a PVF.sub.2 sheet leaves on its surface after 5 days at 20.degree. C. a polyurethane layer which does not adhere to PVF.sub.2.
(b) The same polyurethane in solution in acetone containing 20% by weight dry extract does not adhere to PVF.sub.2 after the solvent is evaporated at a temperature in excess of 120.degree. C.
(c) The preceding tests are repeated with the polyurethane in solution in the dimethylformamide and the solvent is removed at 140.degree. C. Excellent adhesion between the polyurethane and the PVF.sub.2 is obtained.
While the invention has been described in connection with the preferred embodiments, it is not intended to limit the invention to the particular forms set forth, but, on the contrary, it is intended to cover such alternatives, modifications, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims.
Claims
What is claimed is:
1. A process for treating solid polyvinylidene fluoride surfaces to enhance adhesion of other polymers thereto comprising applying to at least one surface thereof a solution consisting essentially of a coating polymer selected from a polyurethane or an alkyl polymethacrylate and at least one aprotic polar solvent in which said polymer is soluble, and exposing said surface to a temperature of from about 100.degree. to 300.degree. C. for a time sufficient to evaporate said solvent.
2. The process of claim 1 wherein the solution contains from 1 to 50% by weight of said polymer.
3. The process of claim 1 wherein said alkyl polymethacrylate is poly(methyl methacrylate) or poly (ethyl methacrylate).
4. The process of claim 1 wherein the aprotic polar solvent is selected from dimethyl formamide, dimethylacetamide, tetrahydrofurane, dimethylsulfoxide, cyclohexanone, hexamethylphosphoramide, tetramethylurea, or mixtures thereof.
5. The process of claim 1 including adhering to said surface, after evaporation of said solvent, an exterior polymer which will adhere to said coating polymer without need for an intermediate coating.
6. The process of claim 5 wherein said exterior polymer is selected from polyesters, epoxides, silicons, polysulfides, chlorinated rubbers, phenolics, polyvinyls, polyurethanes, polyacrylics, or copolymers thereof.
7. The process of adhering other polymers to a polyvinylidene fluoride surface comprising coating said surface with a solution consisting essentially of an aprotic polar solvent selected from dimethylformamide, dimethylacetamide, tetrahydrofurane, dimethylsulfoxide, cyclohexanone, hexamethylphosphoramide, tetramethylurea, or mixtures thereof, and a coating polymer selected from a polyurethane or alkyl polymethacrylate soluble in said solvent and being in said solution in an amount from 1 to 50% by weight, heating said surface at a temperature of from 100.degree. to 300.degree. C. for a time sufficient to evaporate said solvent, and adhering to said surface an exterior polymer selected from polyesters, epoxides, silicons, polysulfides, phenolics, chlorinated rubbers, polyvinyls, polyurethanes, polyacrylics, or copolymers thereof.
8. The product of the process of claim 1.
9. The product of the process of claim 7.
Patent Citations (7)
Non-Patent Literature (1)
- Rubber Chemistry and Technology, vol. 34, 1962, pp. 1522-1524.