US 4,184,025 AGrant
High Solids Coating Composition Adapted for Use as Automotive Topcoat-#3
Issue Date:1980-01-15
•20 Claims
Abstract
A fast curing, high solids coating composition adapted for use as an automotive topcoat, which upon curing forms a hard, glossy, durable coating exhibiting excellent resistance to solvents and water. The coating composition contains greater than about 60 percent by weight of non-volatile solids and, exclusive of pigments, solvents and other nonreactive components, consists essentially of: The hydroxy functional organophosphate ester is included in the composition in an amount sufficient to provide between about 0.67 and about 1.4 equivalents of acid functionality for each equivalent of pendant epoxy functionality of copolymer (A), and the amino crosslinking agent is included in the composition in an amount sufficient to provide at least about 0.4 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in the composition. (A) a copolymer bearing pendant epoxy functionality, having a number average molecular weight (M.sub.n) of between about 1500 and about 10,000 and a glass transition temperature (Tg) of between about -25.degree. and about 70.degree. C.; (B) a reactive catalyst comprising at least one hydroxy functional organophosphate ester selected from certain mono- and diesters of phosphoric acid; (C) an amine-aldehyde crosslinking agent; and (D) optionally, a hydroxy functional additive.
Metadata
Assignee
- Ford Motor Company
Inventor
- Mohinder S. Chattha
Application Information
Application Number:US 9450289
Filing Date:1978-09-22
Priority Date:1977-12-27
Art Unit:142
Classifications
IPC:
C08L 6300C08L 6128C08L 3700
Field of Search:
260834
Patent Drawings
This patent does not have any drawings.
Description
Background of the Invention
This invention is related to a fast curing, high solids, thermosetting coating composition. More particularly, the invention relates to a polymeric, high solids, fast curing coating composition adapted to provide an automotive topcoat which demonstrates hardness, high gloss, outstanding durability and excellent resistance to solvents and water. Still more particularly, this invention relates to a fast curing, high solids, thermosetting ocating composition adapted to be used as an automotive topcoat wherein the topcoat includes metallic flake as a pigment.
Because of increasingly strict solvent emissions regulations in recent years, low solvent emission paints have become very desirable. A number of high solids paint compositions have been proposed to meet these low solvent emission requirements. However, many of these compositions are deficient because of difficulty in application, slow curing rates, lack of flexibility, poor durability and low solvent and water resistance. Many of the proposed compositions have been particularly deficient as automotive topcoats, particularly when the topcoat is to include metallic flake as a pigment.
The deficiency in compositions including metallic flake results from undesired reorientation of the metallic flake during application and cure of the coating. Flake reorientation results primarily because of the very low viscosity resins used in the paint compositions to accommodate high solids. The low viscosity is not sufficient to immobilize the flakes which tend to redistribute themselves to show "reverse flop" and nonuniform distribution.
The coating compositions of this invention combine the above discussed desired properties and low application viscosity with rapid cure so as to overcome deficiencies of previously proposed high solids materials and thereby achieve a high solids coating composition particularly adapted for automotive topcoats and still more particularly adapted for automotive topcoats including metallic flake as a pigment.
Summary of the Invention
The thermosetting coating composition of this invention contains greater than about 60 percent by weight of nonvolatile solids, preferably greater than about 70 percent by weight, and is capable of curing rapidly at a low temperature. The composition, exclusive of pigments, solvents and other nonreactive components, consists essentially of:
(A) a copolymer bearing pendant epoxy functionality, having a number average molecular weight (M.sub.n) of between about 1500 and about 10,000, preferably between about 2,000 and about 6,000, and a glass transition temperature (Tg) of between about -25.degree. C. and about 70.degree. C., preferably between about -10.degree. C. and about 50.degree. C., the copolymer consisting of between about 10 and about 30 weight percent of monoethylenically unsaturated monomers bearing glycidyl functionality and between about 90 and about 70 weight percent of other monoethylenically unsaturated monomers;
(B) a reactive catalyst comprising at least one hydroxy functional organophosphate ester having the formula: ##STR1## wherein n=1 to 2 and R is selected from the group consisting of mono- or dihydroxy alkyl, cycloalkyl, or aryl radicals;
(C) an amine-aldehyde crosslinking agent; and
(D) up to about 45 weight percent based on the total weight of (A), (B), (C) and (D) of a hydroxy functional additive having a number average molecular weight (M.sub.n) of between about 150 and about 6,000.
The organophosphate ester is included in the composition in an amount sufficient to provide between about 0.67 and about 1.4 equivalents, preferably between about 0.8 and about 1 equivalents, of acid functionality for each equivalent of pendant epoxy functionality of the copolymer. The amino resin crosslinking agent is included in the composition in an amount sufficient to provide at least about 0.4 equivalents, preferably between about 0.6 and about 2.1 equivalents, of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in the composition either as (i) an organic hydroxyl group on the organophosphate ester, (ii) a hydroxyl group on the optional hydroxy functional additive or (iii) as a result of esterification of the pendant epoxy functionality of the copolymer of (A) during cure of the coating composition. In addition, the high solids coating composition of the invention may include additives such as catalysts, antioxidants, U.V. absorbers, flow control or wetting agents, antistatic agents, pigments, plasticizers, solvents, etc.
Prior Art
U.S. Pat. Nos. 3,960,979 and 4,018,848 to Khanna teach high solids coating compositions adapted for use as a can coating material. The compositions consist essentially of (i) aromatic epoxide compositions having two or more epoxy groups on an epoxy resin which has a molecular weight not exceeding 2500; (ii) an amino crosslinking agent; (iii) an inorganic or organic monomeric or polymeric acid which acts as a reactive catalyst; and (iv) a flexiblizing polyol.
The compositions of Khanna have the advantage of quick reaction and low application viscosity, but lack durability, and, therefore, do not weather well. This is, in part, because of the presence of ether linkages in the aromatic epoxides. As such, the compositions of Khanna are not desirable for use as automotive topcoats. The Khanna patents describe the compositions as a low cure system. However, when considering the specific teachings of the patents one finds that the composition includes an excess of epoxide resin, apparently with the purpose of "killing off" excess catalyst after completion of the curing reaction. Excess epoxy resin in the composition remains uncured at the low temperature bake range of the baking temperatures disclosed, not giving a complete cure and desirable hardness, durability or solvent resistance. If heated to higher temperatures, as called for in the examples, the excess epoxy does react with excess hydroxy functionality to give still further ether linkages. These ether linkages so obtained have a further deleterious effect on durability and make the materials particularly unsuitable for use as an automotive topcoat. Also, the necessary high bake temperatures to achieve the utilization of this excess epoxy makes the composition undesirable from an energy point of view. Still further, because the epoxy/catalyst reaction occurs in earlfy stages of the cure, thus "killing off" the catalyst, the melamine-hydroxy curing reaction must proceed substantially without benefit of catalysis. The curing reaction thus proceeds slowly and requires the higher temperatures of the Khanna examples.
Detailed Description of the Invention
The high solids coating compositions of this invention overcome disadvantages of prior art high solids compositions, including those of Khanna, to provide a system which is particularly suitable for those applications requiring high gloss, hardness, durability, and high solvent and water resistance as well as a fast cure rate at low temperatures, e.g., between about 75.degree. C. and about 150.degree. C., preferably between about 110.degree. C. and about 130.degree. C. The desirable characteristics of the coating compositions of this invention result from the carefully controlled admixture of the particular components, including a hydroxy functional organophosphate ester, to achieve substantially complete utilization of reactant functionality and a resultant highly crosslinked coating in a fast and efficient manner.
Each of the components of the high solids coating compositions, the amounts of each of the components required to achieve the desired results of the invention and a method for applying the composition are described hereinafter in greater detail.
Epoxy Functional Copolymer
A principal material in the high solids coating compositions of this invention is an epoxy functional copolymer bearing pendant epoxy functionality, and which may be prepared by conventional free radical induced polymerization of suitable unsaturated monomers. The term "copolymer" as used herein means a copolymer of two or more different monomers.
The copolymers used in the high solids coating compositions of this invention have a number average molecular weight (M.sub.n) of between about 1500 and about 10,000, preferably between about 2,000 and about 6,000, and a glass transition temperature (Tg) of between about -25.degree. C. and about 70.degree. C., preferably between about -10.degree. C. and about 50.degree. C. The monomers used to prepare the copolymer include between about 10 and about 30 weight percent of one or more monoethylenically unsaturated monomers bearing glycidyl functionality. These monoethylenically unsaturated monomers may be glycidyl ethers or glycidyl esters. Preferably, however, the epoxy functional monomers are glycidyl esters of monoethylenically unsaturated carboxylic acids, e.g., glycidyl acrylate or glycidyl methacrylate. These monomers provide the copolymer with its pendant epoxy functionality.
The remainder of the monomers forming the epoxy functional copolymer, i.e., between about 90 and about 70 weight percent of the monomers of the copolymer, are other monoethylenically unsaturated monomers. These monoethylenically unsaturated monomers are preferably alpha-beta olefinically unsaturated monomers, i.e., monomers bearing olefinic unsaturation between the two carbon atoms in the alpha and beta positions with respect to the terminus of an aliphatic carbon-to-carbon chain.
Among the alpha-beta olefinically unsaturated monomers which may be employed are acrylates (meaning esters of either acrylic or methacrylic acids) as well as mixtures of acrylates and vinyl hydrocarbons. Preferably, in excess of 50 weight percent of the total of the copolymer monomers are esters of C.sub.1 -C.sub.12 monohydric alcohols and acrylic or methacrylic acids, e.g., methylmethacrylate, ethylacrylate, butylacrylate, butylmethacrylate, hexylacrylate, 2-ethylhexylacrylate, laurylmethacrylate, etc. Among the monovinyl hydrocarbons suitable for use in forming the copolymers are those containing 8 to 12 carbon atoms and including styrene, alpha-methylstyrene, vinyl toluene, t-butylstyrene and chlorostyrene. When such monovinyl hydrocarbons are employed, they should constitute less than 50 weight percent of the copolymer. Other monomers such as vinyl chloride, acrylonitrile, methacrylonitrile, and vinyl acetate may be included in the copolymer as modifying monomers. However, when employed, these modifying monomers should constitute only between about 0 and about 30 weight percent of the monomers in the copolymer.
In preparing the epoxy functional copolymer, the epoxy functional monomers and the remaining monoethylenically unsaturated monomers are mixed and reacted by conventional free radical initiated polymerization in such proportions as to obtain the copolymer desired. A large number of free radical initiators are known to the art and are suitable for the purpose. These include: benzoyl peroxide; lauryl peroxide; t-butylhydroxy peroxide; acetylcyclohexyl; sulfonyl peroxide; diisobutyryl peroxide; di-(2-ethylhexyl) peroxydicarbonate; diisopropylperoxydicarbonate; t-butylperoxypivalate; decanoyl peroxide, azobis(2-methylpropionitrile), etc. The polymerization is preferably carried out in solution using a solvent in which the epoxy functional copolymer is soluble. Included among the suitable solvents are toluene, xylene, dioxane, butanone, etc. If the epoxy functional copolymer is prepared in solution, the solid copolymer can be precipitated by pouring the solution at a slow rate into a nonsolvent for the copolymer such as hexane, octane, or water under suitable agitation conditions.
The pendant epoxy functional copolymer useful in the compositions of this invention can also be prepared by emulsion polymerization, suspension polymerization, bulk polymerization, or combinations thereof, or still other suitable methods. In these methods of preparing copolymers, chain transfer agents may be required to control the molecular weight of the copolymer to a desired range. When chain transfer agents are used, care must be taken so they do not descrease the shelf stability of the composition by causing premature chemical reactions.
Organophosphate Ester
A second essential component of the high solids coatings of this invention is a reactive catalyst which comprises a novel hydroxy functional organophosphate which is present in the composition as a mono- or diester or as a mixture of such mono- and diesters. The hydroxy functional organophosphate esters useful in the composition of the invention are those having the formula: ##STR2## wherein n=1 to 2 and R is selected from the group consisting of mono- or dihydroxy alkyl, cycloalkyl, or aryl radicals. Preferably, the hydroxy bearing alkyl, cycloalkyl, or aryl radicals contain 3 to 10 carbon atoms.
Among the numerous suitable mono- or dihydroxy functional radicals are: 2-ethyl-3-hydroxyhexyl; 4-methylol-cyclohexylmethyl; 2,2 diethyl-3-hydroxypropyl; 8-hydroxyoctyl; 6-hydroxyhexyl; 2,2-dimethyl-3-hydroxypropyl; 2-ethyl-2-methyl-3-hydroxypropyl; 7-hydroxyheptyl; 5-hydroxypentyl; 4-methylolbenzyl; 3-hydroxyphenyl; 2,3 dihydroxypropyl; 5,6 dihydroxyhexyl; 2-(3-hydroxycyclohexyl)-2-hydroxy ethyl; and 2-(3-hydroxypentyl)-2-hydroxyethyl.
The above radicals are intended to be only exemplary and numerous other radicals falling within the defined scope of the novel organophosphate esters useful in the compositions of the invention will be apparent to those skilled in the art. Among the most preferred radicals are mono- or dihydroxy functional alkyl radicals containing 3 to 10 carbon atoms.
A preferred method for preparing the hydroxy functional organophosphate esters useful in the compositions of the invention is by an esterification reaction between an excess of an alkyl, cycloalkyl or aryl diol or triol and phosphorus pentoxide. When a triol is used as a reactant, preferably at least one of the hydroxyl groups should be secondary. The reaction between the diol or triol and the phosphorus pentoxide is generally carried out by adding phosphorus pentoxide portionwise to an excess of diol or triol in a liquid state or in solution in a suitable solvent.
Suitable solvents include, but are not limited to, butyl acetate, methyl ethyl ketone, methyl amyl ketone, toluene, xylene, etc.
A preferred temperature for carrying out the reaction is between about 50.degree. C. and about 60.degree. C. Due to the multiple hydroxy functionality of the diol or triol reactant, minor amounts of polymeric acid phosphate as well as certain cyclophosphates are also generated during the synthesis. These polymeric and cyclic materials also serve as a reactive catalyst and, therefore, need not be separated from the hydroxyphosphate esters described above. In fact, it has been found advantageous in preferred embodiments of the invention to employ all reaction products, i.e., the hydroxy functional organophosphate esters and the minor amount of polymeric acid phosphate cyclophosphates, as well as excess diol or triol in the coating compositions. The excess diol or triol serves in those compositions as the optional hydroxy functional additive. Reactive catalysts prepared by the above preferred method will generally include about a 1 to 1 ratio of the mono- and diester organophosphate.
Still another preferred method of preparing the hydroxy functional organophosphate esters useful in compositions of the invention is by an esterification reaction between phosphoric acid and an alkyl, cycloalkyl or arylmonoepoxide. This reaction is carried out by adding between about 1 and about 2 moles, preferably between about 1 and about 1.5 moles, of the monoepoxy material to 1 mole of phosphoric acid or its solution in a suitable solvent as above. During the esterification reaction which occurs, a hydroxyl group is formed. If a dihydroxy radical is desired in the organophosphate ester, a monoepoxide bearing hydroxy functionality may be used as a reactant. Preferred monoepoxide materials useful in this method are well known monoepoxides selected from monoepoxy ethers, monoepoxy esters and alkylene oxides. Exemplary of preferred monoepoxides for use in this esterification reaction are: propylene oxide, butylene oxide, cyclohexene oxide, styrene oxide, n-butylglycidyl ether, ethylglycidyl ether, n-butylepoxy stearate and glycidyl acetate. As will be understood by those skilled in the art, the proportion of monoester and diester formed by the reaction will vary with the selected molar ratio of the monoepoxide and the phosphoric acid. When 1 mole of monoepoxide is used per mole of phosphoric acid primarily monoester is formed while a molar ratio of 2 to 1 results in primarily diester. A molar ratio of 1.5 to 1 will result in an approximately 1 to 1 mixture of mono- and diesters. In all cases a minor amount of the triester will be formed. While this triester obviously will not serve as a reactive catalyst, it will crosslink with the amino crosslinking agent of the composition and, thus, may be safely included.
The hydroxy functional organophosphate ester component of the high solids coating composition of the invention is a reactive catalyst which allows the composition to cure rapidly at a low temperature. The acid functionality of the mono- or diester or mixture of such esters reacts with the pendant epoxy functionality of the epoxy functional copolymer to form an ester and a hydroxyl group. This hydroxyl group, as well as the organic hydroxyl groups on the hydroxy functional organophosphate ester and any optional hydroxy groups included in the composition in the form of hydroxy functional additive, including any diol or triol present from the synthesis of the hydroxy functional organophosphate ester, crosslinks with the amino resin crosslinking agent. It is critical to achieving the desired results of the high solids coating compositions of this invention, i.e., in making them suitable for use as automotive topcoats, that the amount of organophosphate ester be sufficient to convert substantially all of the epoxy functionality on the copolymer to the desired hydroxy functionality by esterification reaction. Therefore, the organophosphate ester is included in the composition in an amount sufficient to provide between about 0.67 and about 1.4 equivalents, preferably between about 0.8 and about 1 equivalents, of acid functionality for each equivalent of pendant epoxy functionality on the copolymer. As will be noted from the equivalent amounts of epoxy and organophosphate ester acid functionality stated above, the amount of acid functionality need not be in stoichiometric amounts to the epoxy functionality. This is because of the fact that during curing of the high solids coating composition, residual water present in the composition hydrolyzes some of the esterified product back to acid and this hydrolyzed product then, in turn, reacts with additional epoxy functionality.
Amino Crosslinking Agent
A third essential component of the high solids paint compositions of this invention is an amine-aldehyde crosslinking agent. Amine-aldehyde crosslinking agents suitable for crosslinking hydroxy functional bearing materials are well known in the art. Typically, these crosslinking materials are products of reactions of melamine, or urea with formaldehyde and various alcohols containing up to and including 4 carbon atoms. Preferably, the amine-aldehyde crosslinking agents useful in this invention are condensation products of formaldehyde with melamine, substituted melamine, urea, benzoguanamine or substituted benzoguanamine. Preferred members of this class are methylated melamine-formaldehyde resins such as hexamethoxymethylmelamine. These liquid crosslinking agents have substantially 100 percent nonvolatile content as measured by the foil method at 45.degree. C. for 45 minutes. For the purposes of the invention it should be recognized that it is important not to introduce extraneous diluents that would lower the final solids content of the coating.
Particularly preferred crosslinking agents are the amino crosslinking agents sold by American Cyanamid under the trademark "Cymel". In particular, Cymel 301, Cymel 303 and Cymel 1156, which are alkylated melamine-formaldehyde resins, are useful in the compositions of this invention.
The amine-aldehyde materials function as a cross-linking agent in the composition of the invention by reacting with hydroxy functionality present in the composition (i) as an organic hydroxyl group on the hydroxy functional organophosphate ester, (ii) as a hydroxyl group on the optional hydroxy functional additive including any excess diol or triol from the organophosphate synthesis, or (iii) as a result of esterification of the pendant epoxy functionality on the epoxy functional copolymer.
In order to achieve the outstanding properties which make these coating compositions particularly useful as automotive topcoat materials, it is essential that the amount of amino crosslinking agent be sufficient to substantially completely crosslink the hydroxy functionality in the coating composition. Therefore, the amino crosslinking agent should be included in the composition in an amount sufficient to provide at least about 0.4 equivalents, preferably between about 0.6 and about 2.1 equivalents, of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in the composition.
Optional Hydroxy Functional Additive
Additional hydroxy functionality other than that achieved by esterification of pendant epoxy functionality of the epoxy functional copolymer or by the hydroxy functional organophosphate ester may be achieved by adding a hydroxy functional additive in amounts up to about 45 weight percent based on the total of the three above discussed components and the hydroxy functional additive itself. Such a material serves to provide additional hydroxy functionality so as to provide a more intimate crosslinked structure in the final cured product. The hydroxy functional additives useful in the composition are preferably selected from various polyols having a number average molecular weight (M.sub.n) of between about 150 and about 6,000, preferably between about 400 and about 2500. As used herein the term polyol means a compound having two or more hydroxyl groups.
The polyols useful for the invention preferably are selected from the group consisting of: (i) hydroxy functional polyesters; (ii) hydroxy functional polyethers; (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers produced by free radical polymerization of monoethylenically unsaturated monomers, one of which bears hydroxy functionality and which is included in the copolymer in an amount ranging from about 2.5 to about 30 weight percent of the copolymer and (vi) mixtures of (i)-(v).
The hydroxy functional polyesters useful in the invention are preferably fully saturated products prepared from aliphatic dibasic acids containing 2-20 carbon atoms, such as succinic acid, glutaric acid, adipic acid, azelaic acid, etc., and short chain glycols of up to and including 21 carbon atoms, such as ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,2-butylene glycol, 1,3-butylene glycol, 1,4-butylene glycol, neopentyl glycol 1,4-cyclohexane dimethylol, 1,6-hexamethylene glycol and 2-ethyl-2-methyl-1,3-propane diol. The molecular weight of these materials ranges from about 200 to about 2500 and the hydroxyl number ranges from about 30 to about 230. The hydroxyl number is defined as the number of milligrams of potassium hydroxide needed for each gram of sample to neutralize the acetic acid generated during the reaction between the polyol and excess acetic anhydride. The polyester polyols utilized in the invention are low melting, soft waxy solids which are easily maintained in the molten state.
Among preferred polyesters are products derived from the esterification of ethylene glycol and 1,4 butane diol with adipic acid, ethylene glycol and 1,2 propylene glycol with adipic acid, azelaic acid and sebacic acid copolyester diols, and mixtures thereof.
Among useful polyether diols are polytetramethylene ether glycol, polyethylene glycol, polypropylene glycol and the like.
The hydroxy functional oligoesters useful as hydroxy functional additives in the compositions of the invention are oligoesters preferably having a molecular weight of between about 150 and about 3000. Such oligoesters may be selected from the group consisting of: (i) oligoesters prepared by reacting a dicarboxylic acid with a monoepoxide such as an alkylene oxide; (ii) oligoesters prepared by reacting a polyepoxide with a monocarboxylic acid; and (iii) oligoesters prepared by reacting a hydroxy functional monocarboxylic acid with either a mono- or polyepoxide.
The oligoester prepared by reacting a dicarboxylic acid with an alkylene oxide is a low molecular weight adduct which has a narrow molecular weight distribution when compared to similar compositions made by normal polyester manufacturing techniques. The adduct is prepared by reacting a dibasic carboxylic acid with alkylene oxides, preferably ethylene oxide or propylene oxide, in the presence of a catalyst. Preferred dicarboxylic acids are C.sub.6 -C.sub.12 aliphatic acids such as adipic acid,, azelaic acid sebacic acid or dodecane dicarboxylic acid. Mixtures of these acids or mixtures of the aliphatic dicarboxylic acids with aromatic dicarboxylic acids also yield suitable hydroxy functional oligoesters.
The preparation of oligoesters from monocarboxylic acids and polyepoxides is well known and is described, for example, in U.S. Pat. Nos. 2,456,408 and 2,653,141. Numerous hydroxy functional oligoesters within this general category will be apparent to those skilled in the art.
The third type of hydroxy functional oligoester, i.e., those prepared by reaction of a hydroxy functional monocarboxylic acid with an epoxide is described in U.S. Pat. No. 3,404,018. While the epoxides employed in accordance with the teachings of that patent are polyepoxides, oligoesters may be prepared in a similar manner to that described therein by employing a monoepoxide, such as an alkylene oxide, and a hydroxy functional monocarboxylic acid as described therein. Numerous monoepoxide materials suitable for this purpose will be apparent to those skilled in the art.
Among the numerous monomeric polyols which may be employed as the hydroxy functional additive are the various short chain glycols of up to and including 21 carbon atoms which are useful in preparing the hydroxy functional polyesters discussed above. Other conventional polyhydric alcohols such as glycerols and sugar alcohols are also among the numerous monomeric polyols which will be apparent to those skilled in the art.
The hydroxy bearing copolymer useful as the hydroxy functional additive may be formed from monoethylenically unsaturated monomers, with between about 10 and about 30 weight percent bearing hydroxyl functionality.
The long list of hydroxy functional monomers which may be employed in these hydroxy functional copolymers includes, but is not limited to, the following esters of acrylic or methacrylic acid and aliphatic alcohols: 2-hydroxyethyl acrylate; 3-chloro-2-hydroxypropyl acrylate; 2-hydroxy-1-methylethyl acrylate; 2-hydroxypropyl acrylate; 3-hydroxy-propyl acrylate; 2,3 dihydroxypropyl acrylate; 2-hydroxy-butyl acrylate; 4-hydroxybutyl acrylate; diethyleneglycol acrylate; 5-hydroxypentyl acrylate; 6-hydroxyhexyl acrylate; triethyleneglycol acrylate; 7-hydroxyheptyl acrylate; 2-hydroxymethyl methacrylate; 3-chloro-2-hydroxypropyl methacrylate; 2-hydroxy-1-methylethyl methacrylate; 2-hydroxypropyl methacrylate; 3-hydroxypropyl methacrylate; 2,3 dihydroxypropyl methacrylate; 2-hydroxybutyl methacrylate; 4-hydroxybutyl methacrylate; 3,4 dihydroxybutyl methacrylate; 5-hydroxypentyl methacrylate; 6-hydroxyhexyl methacrylate; 1,3-dimethyl-3-hydroxybutyl methacrylate; 5,6 dihydroxyhexyl methacrylate; and 7-hydroxyheptyl methacrylate.
Although one of ordinary skill in the art will recognize the many different hydroxy bearing monomers including those listed above could be employed, the preferred hydroxy functional monomers for use in the hydroxy functional resin of the invention are C.sub.5 -C.sub.7 hydroxy alkyl acrylates and/or C.sub.5 -C.sub.7 hydroxy alkyl methacrylates, i.e., esters of C.sub.2 -C.sub.3 dihydric alcohols and acrylic or methacrylic acids.
The remainder of the monomers forming the hydroxy functional copolymer, i.e., between about 90 and about 70 weight percent, are other monoethylenically unsaturated monomers. These monoethylenically unsaturated monomers, as was the case with respect to the epoxy functional copolymer discussed above, are preferably alpha-beta olefinically unsaturated monomers. As was also the case with respect to the epoxy functional copolymer, the preferred alpha-beta olefinically unsaturated monomers are acrylates and preferably are employed in excess of 50 weight percent of the total copolymer. Preferred acrylate monomers are esters of C.sub.1 -C.sub.12 monohydric alcohols and acrylic or methacrylic acids. Monovinyl hydrocarbons and other modifying monomers may also be employed in the same proportion as they are employed in the epoxy functional copolymer discussed above.
Other Materials
In addition to the above discussed components, other materials may be included in the high solids coating compositions of the invention. These include materials such as catalysts, antioxidants, U.V. absorbers, solvents, surface modifiers and wetting agents as well as pigments. The solvents used in the coating compositions of the invention are those which are commonly used. Typical solvents useful in the coating compositions facilitate spray application at high solids content and include toluene, xylene, methyethyl ketone, acetone, 2-ethoxy-1-ethanol, 2-butoxy-1-ethanol, diacetone alcohol. tetrahydrofuran, ethylacetate, dimethylsuccinate, dimethylglutarate, dimethyladipate or mixtures thereof. The solvent in which the epoxy functional copolymer of the coating composition is prepared, may be employed as the solvent for the coating composition thus eliminating the need for drying the epoxy functional copolymer after preparation if such is desired. As mentioned above, the nonvolatile solids content of the high solids coating composition is at least 60 percent and preferably 70 percent or more, thus limiting the amount of solvent included in the composition.
Surface modifiers or wetting agents are common additives for liquid paint compositions. The exact mode of operation of these surface modifiers is not known, but it is thought that their presence contributes to better adhesion of the coating composition to the surface being coated and helps formation of thin coating on surfaces, particularly metal surfaces. These surface modifiers are exemplified by acrylic polymers containing 0.1-10 percent by weight of a copolymerized monoethylenically unsaturated carboxylic acids such as methacrylic acid, acrylic acid or itaconic acid, cellulose acetate butyrate, silicon oils or mixtures thereof. Of course, the choice of surface modifier or wetting agent is dependent upon the type of surface to be coated and selection of the same is clearly within the skill of the artisan.
The high solids coating composition of the invention also may include pigments. As noted above, the high solids compositions of this invention are particularly useful when the coating composition includes metallic flake as a pigment. The rapid set and curing of the composition eliminates problems associated with redistribution of the metallic flake in the composition. The amount of pigment in the high solids coating composition may vary, but preferably is between about 3 and about 45 weight percent based on the total weight of the paint composition. If the pigment is metallic flake, the amount ranges from about 1 to about 7 weight percent.
Application Techniques
The high solids coating composition can be applied by conventional methods known to those in the art. These methods include roller coating, spray coating, dipping or brushing and, of course, the particular application technique chosen will depend on the particular substrate to be coated and the environment in which the coating operation is to take place.
A particularly preferred technique for applying the high solids coating compositions, particularly when applying the same to automobiles as topcoats, is spray coating through the nozzle of a spray gun.
The invention will be further understood by referring to the following detailed examples. It should be understood that the specific examples are presented by way of illustration and not by way of limitation. Unless otherwise specified, all references to "parts" is intended to mean parts by weight.
Example 1
(a) Five Hundred (500) grams of dry (dried over molecular sieves) 2-ethyl-1,3 hexane diol are placed in a three-necked round bottom flask equipped with a stirrer, dropping funnel and a thermometer. Solid phosphorus pentoxide is added portionwise with continuous stirring and an exothermic reaction occurs. The addition of phosphorus pentoxide is regulated to maintain the temperature at 50.degree. C. and test portions of the reaction mixture are withdrawn at short intervals of time and titrated with potassium hydroxide solution. The addition of P.sub.2 O.sub.5 is continued until the acid equivalent weight equals 500. The reaction mixture is stirred at 50.degree. C. for one more hour and is filtered. The acid equivalent weight, by titration with KOH solution, is found to be 485.
(b) In a round-bottom four-necked flask, equipped with a stirrer, a dropping funnel, a thermometer and a condenser, 500 ml of methyl amyl ketone is brought to reflux under nitrogen. The following mixture of monomers is employed for polymer synthesis:
Thirty-seven (37) grams of tert-butyl perbenzoate is added to the above monomers and the resulting solution added dropwise to refluxing methyl amyl ketone over a period of one hour and ten minutes. The heating and stirring is continued for half an hour after the addition is complete and then two more grams t-butyl perbenzoate are added portionwise. The reaction mixture is refluxed for two more hours and then allowed to cool to room temperature. The molecular weight of the copolymer is determined by Gel Permeation Chromatography and found to be M.sub.n =3250 and Mw/M.sub.n =2.2. The calculated Tg of the polymer is 9.degree. C. and the solution viscosity (#4 Ford cup) is 41 seconds.
Eighty (80) parts of the copolymer solution prepared in (b) and 40 parts of Cymel 301 are dissolved in 20 parts of butyl acetate and 44.5 parts of the hydroxy phosphate prepared in (a) are added to this solution. The resulting formulation is spray applied to steel test panels and the panels are baked at 130.degree. C. for 20 minutes to obtain a glossy (81/20.degree.) coating with excellent hardness, adhesion and solvent (xylene and methyl amyl ketone) resistance. The coating does not show any loss of gloss or adhesion after 14 days exposure in the Cleveland Humidity Chamber.
Example 2
Five (5) parts of aluminum flakes (65% in naphtha) are mixed well with 80 parts of the copolymer solution from Example 1(b). Thirty-nine (39) parts Cymel 301 and 30 parts of butyl acetate are added to the above mixture and the resulting material is filtered through a coarse filtering cloth. Forty-five (45) parts of hydroxy phosphate from Example 1(a) are added to the filtrate and the resulting formulation spray applied to primed steel test panels in a three coat application. The intermediate flash time is one minute and the final flash is five minutes. The panels are baked at 115.degree. C. for 20 minutes to obtain a silver metallic coating with excellent hardness, adhesion and solvent (xylene and methyl amyl ketone) resistance.
Example 3
(a) The hydroxyphosphate preparation described in Example 1(a) is repeated with an increased amount of phosphorus pentoxide to obtain an acid equivalent weight of 271.
(b) Fifty (50) parts of the polymer solution from Example 1(b) is mixed with 24 parts of hexamethoxymethyl melamine, 5 parts of polypropylene glycol (Pluracol P710, BASF Wyndotte Co.) and 15 parts of butyl acetate. 14.9 parts of hydroxyphosphate from (a) is added to the above solution and the resulting formulation is spray applied to steel test panels. The panels are baked at 130.degree. C. for 20 minutes to obtain glossy (85/20.degree.) coatings with excellent hardness, adhesion and solvent (xylene and methtyl ethyl ketone) resistance. The coating does not show any loss of gloss or adhesion after 14 days exposure in a Cleveland Humidity Chamber.
Example 4
Six (6) parts of aluminum flakes (65% in naphtha) are mixed well with 70 parts of the polymer solution from Example 1(b). Thirty-nine (39) parts Cymel 301 and 30 parts of butyl acetate are added to the above mixture and the resulting material is filtered through a coarse filtering cloth. Twenty-five (25) parts of hydroxy phosphate from Example 3(a) are added to the filtrate and the resulting formulation spray applied to primed steel test panels in a three coat application; the intermediate flash time in one minute and the final flash five minutes. The panels are baked at 115.degree. C. for 20 minutes to obtain silver metallic coatings with excellent hardness, adhesion and solvent (xylene and methyl ethyl ketone) resistance.
Example 5
The following monomers are utilized in the synthesis of a glycidyl methacrylate polymer.
The polymerization is carried out as outlined in Example 1 by employing 500 grams of methyl amyl ketone and 30 grams of tert-butyl perbenzoate. The addition of initiator and the monomer mixture is complete in two hours and the reaction mixture refluxed for one additional hour. Two grams of initiator are then added and the reaction mixture refluxed for two hours. The molecular weight determined by Gel Permeation Chromatography is found to be M.sub.n =3168 and Mw/M.sub.n =2.15. The Tg of this polymer is calculated to be 20.degree. C.
Thirty-two (32) parts of the above polymer solution, fourteen (14) parts of hexamethoxymethyl melamine (Cymel 301) and two parts of 1,4-Cyclohexanedimethanol are dissolved in ten parts of butyl acetate. 9.9 parts of hydroxyphosphate from Example 3(a) are added to the above solution and the resulting formulation spray applied to primed steel panels; the panels are baked at 120.degree. C. for 20 minutes to obtain a coating with excellent physical properties.
Example 6
Twenty-seven (27) parts of the polymer described in Example 5, 16 parts of Cymel 301 and 5 parts of Acryloid OL-42 (Rohm and Haas Chem. Co.) are dissolved in 10 parts of butyl acetate. 8.4 parts of hydroxyphosphate from Example 3(a) is added to the above solution and the resulting formulation drawn on a steel test panel and baked at 130.degree. C. for ten minutes to obtain a glossy coating with excellent hardness, adhesion and solvent resistance.
Example 7
(a) One hundred (100) grams of 1,4-cyclohexanemethanol are dissolved in 80 grams of butyl acetate at 50.degree. C. and the procedure outlined in Example 1(a) is followed to obtain a hydroxyphosphate with an acid equivalent weight of 645.
(b) Eighty (80) parts of the polymer solution prepared in Example (b), 10 parts of bis-(hydroxypropyl) azelate (product of propylene oxide and azelaic acid) and 45 parts of ethoxy methoxymethylbenzoguanamine (Cymel 1123, American Cyanamid) are dissolved in 25 parts of butyl acetate and 58.2 parts of hydroxyphosphate from (a) are added to this solution. The resulting formulation is spray applied to primed steel panels and baked at 130.degree. C. for 20 minutes to obtain hard, glossy coatings with excellent adhesion and solvent resistance.
Example 8
Thirty-five (35) parts of the polymer solution prepared in Example 5, 17 parts of hexamethoxymethyl melamine (Cymel 301, American Cyanamid) and 5 parts of caprolactone based hydroxyester PCPO300 (Union Carbide) are dissolved in 10 parts of butyl acetate. 10.7 parts of hydroxyphosphate from Example 3(a) are added to the above solution and the resulting formulation spray applied to primed steel test panels. The panels are baked at 130.degree. C. for 20 minutes to obtain coatings with excellent hardness, adhesion, gloss and solvent resistance (xylene and methyl ethyl ketone).
Example 9
The following mixture of monomers is used in the polymer synthesis:
The polymerization is carried out as outlined in Example 1 to obtain a 50% solution of the polymer.
Seventy (70) parts of the above polymer solution, 15 parts of bis-(hydroxypropyl) azelate (reaction product of propylene oxide and azelaic acid) and 35 parts of hexamethoxymethyl melamine (Cymel 301) are dissolved in 10 parts of butyl acetate. 22.3 parts of hydroxyphosphate from Example 3(a), are added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 130.degree. C. for 15 minutes to obtain glossy (88.degree./20.degree.) coatings with excellent adhesion, hardness and solvent (xylene and methyl ethyl ketone) resistance.
Example 10
(A) A hydroxy acrylic copolymer is prepared from the following monomers:
One hundred (100) grams tert-butyl perbenzoate is added to the above monomer mixture and the resulting solution added dropwise over a period of two hours to 1400 grams of refluxing methyl amyl ketone under nitrogen. The heating and stirring is continued for half an hour after the addition is complete and then five grams of tert-butyl perbenzoate are added portionwise to the reaction mixture. The reaction mixture is refluxed for an additional ninety (90) minutes and then allowed to cool to room temperature. The molecular weight is determined by Gel Permeation Chromatography M.sub.n -2540 and Ms/M.sub.n =1.94
(B) A solution of 1250 grams of 2-ethyl-1,3 hexane diol in 1250 grams of butyl acetate is placed under nitrogen in a three-necked round bottom flask equipped with a mechanical stirrer. Phosphorus pentoxide (442 grams) is added portionwise with continuous stirring, an exotherimic reaction occurs and the addition of P.sub.2 O.sub.5 is regulated to maintain the temperature between about 50.degree. and about 60.degree. C. After completing the addition (about 4 hours), the reaction mixture is stirred for three more hours. The acid equivalent weight, by titration with KoH solution, is found to be 315.
Forty (40) parts of the polymer from (A), 45 parts by weight of the glycidyl methacrylate polymer from Example 1(b) and 34 parts of hexamethoxymethyl melamine (Cymel 301) are dissolved in 20 parts of butyl acetate. 16.3 parts of hydroxyphosphate from (b) is added to the above solution and the resulting formulation spray applied to primed steel test panels. The panels are baked at 130.degree. C. for 20 minutes to obtain glossy coatings with excellent hardness, adhesion and solvent (xylene and methyl ethyl ketone) resistance.
Example 11
Twenty-five (25) parts of polymer from Example 5, 25 parts of the hydroxypolymer from Example 10 and 27 parts of hexabutoxymethyl melamine (Cymel 1156) are dissolved in 15 parts of butyl acetate. 9.1 parts of hydroxyphosphate from 10(b) is added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 130.degree. C. for 20 minutes to obtain glossy coatings with excellent hardness, adhesion and solvent resistance.
Example 12
(a) Fifty (50) grams of 1,4-benzenedimethanol are dissolved in 150 grams of 2-ethyl-1,3-hexanediol and 40 ml of butyl acetate. Phosphorus pentoxide is added portionwise to the above solution as described in Example 1(a) to obtain a hydroxyphosphate with an acid equivalent weight weight of 364.
(a) Thirty (30) parts of glycidyl methacrylate polymer from Example 5. 5 parts of bis-(hydroxypropyl) azelate and 18 parts of ethoxymethoxymethyl benzoguanamine (Cymel 1123, American Cyanamid) are dissolved in 10 parts of butyl acetate. 13.2 parts of the hydroxyphosphate are added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 180.degree. C. for 20 minutes to obtain hard, glossy coatings with excellent adhesion and solvent (xylene and methyl ethyl ketone) resistance.
Example 13
(a) Example 1(a) is repeated to obtain a hydroxy phosphate with acid equivalent weight of 212.
(b) Twenty-five (25) parts of glycidyl methacrylate polymer from Example 1, 20 parts of hydroxy polymer from Example 10, 5 parts of bis(hydroxypropyl) azelate and 19 parts of butoxymethyl glycoluril (Cymel 1170, American Cyanamid) are dissolved in 15 parts of butyl acetate. 5.8 parts of the hydroxyphosphate are added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 130.degree. C. for 20 minutes to obtain hard, glossy coatings with excellent adhesion and solvent (xylene and methyl ethyl ketone) resistance.
Example 14
Thirty (30) parts of glycidyl methacrylate polymer from Example 5, 7 parts of Acryloid OL42 (Rohm and Haas Chem. Co.) and 27 parts of butoxymethyl urea resin (Beetle 80, American Cyanamid) are dissolved in 20 parts of butyl acetate. 7.3 parts of hydroxyphosphate from Example 13(a) are added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 130.degree. C. for 20 minutes to obtain a hard and glossy coating.
Example 15
The following mixture of monomers is employed in the synthesis of a polymer:
The polymerization is carried out as outlined in Example 1 to obtain a 52% solution of the polymer in methyl amyl ketone.
Thirty-one (31) parts of the above polymer, 20 parts of the hydroxy polymer from Example 8, 17 parts of hexamethoxymethyl melamine (Cymel 301, American Cyanamid) are dissolved in 10 parts butyl acetate. 8.9 parts of hydroxyphosphate from Example 13(a) are added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 130.degree. C. for 20 minutes to obtain hard, glossy coatings with excellent adhesion and solvent (xylene and methyl ethyl ketone) resistance.
Example 16
The following monomers are employed in the synthesis of this polymer.
The polymerization is carried out in methyl amyl ketone by employing 1.8% (by wt. of the monomers) of the initiator. The molecular weight from Gel Permeation Chromatography is found to be M.sub.n =5750, Mw/M.sub.n =24. The solids content is found to be 54% by weight.
Sixty (60) parts of this polymer solution, 70 parts of the polymer from Example 5 and 50 parts of hexamethoxymethyl melamine (Cymel 301) are dissolved in 30 parts of butyl acetate. 15.4 parts of hydroxyphosphate from Example 3(a) is added to the above solution and the resulting formulation spray applied to primed steel panels. The panels are baked at 130.degree. C. for 20 minutes to obtain coatings with excellent hardness and adhesion and solvent (xylene and methyl ethyl ketone) resistance.
Example 17
Three hundred Fifty (350) grams of titanium dioxide are mixed with 350 parts of Acryloid OL-42 (Rohm and Haas Chem. Co.) and 25 parts of butyl acetate. The above mixture is taken up in a porcelain bottle containing porcelain beeds and is put on a roller mill for 16 hours. Forty (40 parts of the above millbase are mixed with 28 parts of polymer from Example 1, 5 parts of hycroxy ester Desmophen KL5-2330 (Rohm and Haas Chem. Co.), 13 parts of hexamethoxymethyl melamine (Cymel 301) and 20 parts of butyl acetate. 6.7 parts of hydroxyphosphate from Example 13 are added to the above mixture and the resulting formulation spray applied to primed steel panels. The panels are baked at 120.degree. C. for 20 minutes to obtain coatings with excellent physical properties.
Example 18
Five hundred (500) parts of titanium dioxide and 250 parts of Ferrite yellow are mixed with 500 parts of Acryloid OL-42 (Rohm and Haas Chem. Co.), 7.8 parts of dispersing agent BYK P104S (Mellinckrodt) and 200 parts of butyl acetate. The millbase is prepared as described in Example 17.
Thirty-five parts of this millbase are mixed with 50 parts of polymer from Example 5, 25 parts of hexamethoxymethyl melamine, 3 parts of 1,4-cyclohexanedimethanol and 22 parts of butyl acetate. 17.9 parts of hydroxyphosphate from Example 10(b) are added to the above mixture and the resulting formulation spray applied to primed steel panels. The panels are baked at 115.degree. C. for 20 minutes to obtain coatings with excellent physical properties.
Example 19
Fifty (50) parts of blue pigment Phthalo Blue are mixed with 500 parts of Acryloid OL-42 (Rohm and Haas Chem. C9.) and 44 parts of butyl acetate, the millbase was ground as described in Example 17.
Twenty-five (25) parts of the above millbase are mixed with 6 parts of aluminum flakes (65% in naphtha), 41 parts of bis-(hydroxypropyl)azelate, 29 parts of hexamethoxymethyl melamine (Cymel 301) and 20 parts butyl acetate. 9.8 parts of the hydroxyphosphate from Example 13 is added to the above mixture and the resulting formulation spray applied to primed steel panels in four coats with one minute flash time between coats. After five minutes final flash the panels are baked at 130.degree. C. for 20 minutes to obtain a blue metallic coating with excellent hardness, adhesion and solvent resistance.
Example 20
Ninety-eight (98) grams of phosphoric acid and 50 ml of butyl acetate are placed in a round-bottom flask fitted with a condenser and a dropping funnel and cooled with an ice water mixture. Propylene oxide, 136 grams, is added dropwise with continuous stirring; the addition is complete in two hours.
Example 1 is repeated by substituting 21 parts of the above hydroxyphosphate for the hydroxyphosphate used therein. The coatings have excellent physical properties.
Example 21
The blue metallic formulation described in Example 19 is repeated by employing 10.2 parts of the hydroxyphosphate described in Example 20. The formulation is spray applied to primed steel panels in three coats with one minute final flash the panels are baked at 100.degree. C. for 20 minutes to obtain blue metallic coatings with excellent hardness, adhesion and solvent resistance.
In view of this disclosure, many modifications of this invention will be apparent to those skilled in the art. It is intended that all such modifications which fall within the true scope of this invention be included within the terms of the appended claims.
Claims
I claim:
1. A thermosetting coating composition adapted for low temperature bake applications which contains greater than about 60% by weight of nonvolatile solids, and which, exclusive of pigments, solvents and other nonreactive components, consists essentially of: (A) a copolymer bearing pendant epoxy functionality, having a number average molecular weight (M.sub.n) of between about 1500 and about 10,000 and a glass transition temperature (Tg) of between about -25.degree. C. and about 70.degree. C., said copolymer consisting of between about 10 and about 30 weight percent of monoethylenically unsaturated monomers bearing glycidyl functionality and between about 90 and about 70 weight percent of other monoethylenically unsaturated monomers; (B) a reactive catalyst comprising at least one hydroxy functional organophosphate ester having the formula: ##STR3## wherein n=1 to 2 and R is selected from the group consisting of mono- or dihydroxy alkyl, cycloalkyl, or aryl radicals; (C) an amine-aldehyde crosslinking agent; and (D) up to 45 weight percent based on the total weight of (A), (B), (C), and (D) of a hydroxy functional additive having a number average molecular weight (M.sub.n) of between 150 and about 6000, said hydroxy functional organophosphate ester being included in said composition in an amount sufficient to provide between about 0.67 and about 1.4 equivalents of acid functionality for each equivalent of pendant epoxy functionality on said copolymer, and said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.4 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in said composition either as (i) an organic hydroxyl group on said organophosphate ester, (ii) a hydroxyl group on said hydroxy functional additive, or (iii) as a result of esterification of said pendant epoxy functionality of said copolymer during cure of said coating composition.
2. A composition in accordance with claim 1, wherein said monoethylenically unsaturated monomers bearing glycidyl functionality are selected from glycidyl esters and glycidyl ethers.
3. A composition in accordance with claim 2, wherein said monoethylenically unsaturated monomers bearing glycidyl functionality are selected from glycidyl esters of monoethylenically unsaturated carboxylic acids.
4. A composition in accordance with claim 1, wherein said other monoethylenically unsaturated monomers in said copolymer are selected from the group consisting of acrylates and other monoethylenically unsaturated vinyl monomers.
5. A composition in accordance with claim 4, wherein said acrylate monomers comprise at least about 50 weight percent of the total monomers in said copolymer and are selected from esters of C.sub.1 -C.sub.12 monohydric alcohols and acrylic or methacrylic acids.
6. A composition in accordance with claim 1, wherein said hydroxy functional organophosphate esters are esters wherein R is a mono- or dihydroxy alkyl, cycloalkyl or aryl radical containing 3 to 10 carbon atoms.
7. A composition in accordance with claim 1, wherein at least a portion of said organophosphate esters are esters wherein R is a mono- or dihydroxy alkyl radical containing 3 to 10 carbon atoms.
8. A composition in accordance with claim 1, wherein said organophosphate ester is a monoester.
9. A composition in accordance with claim 1, wherein said organophosphate ester is a diester.
10. A composition in accordance with claim 1, wherein said organophosphate ester is a mixture of mono- and diesters.
11. A composition in accordance with claim 10, wherein said hydroxy functional organophosphate esters are esters wherein R is a mono- or dihydroxy alkyl, cycloalkyl or aryl radical containing 3 to 10 carbon atoms.
12. A composition in accordance with claim 10, wherein at least a portion of said organophosphate esters are esters wherein R is a mono- or dihydroxy alkyl radical containing 3 to 10 carbon atoms.
13. A composition in accordance with claim 1 wherein said reactive catalyst including said hydroxy functional organophosphate ester is the reaction product of an excess of an alkyl, cycloalkyl or aryl diol or triol and phosphorus pentoxide.
14. A composition in accordance with claim 1 wherein said reactive catalyst including said hydroxy functional organophosphate ester is the reaction product of an excess of an alkyl, cycloalkyl or aryl triol in which at least one of the hydroxyl groups is secondary, and phosphorus pentoxide.
15. A composition in accordance with claim 1 wherein said reactive catalyst including said hydroxy functional organophosphate ester is the reaction product of an alkyl, cycloalkyl or aryl monoepoxide and phosphoric acid in a molar ratio of between about 1:1 and about 2:1.
16. A composition in accordance with claim 15 wherein said monoepoxide also bears hydroxy functionality.
17. A composition in accordance with claim 15 wherein said monoepoxide is selected from monoepoxy esters, monoepoxy ethers and alkylene oxides.
18. A composition in accordance with claim 1, wherein said amino resin crosslinking agent is amine-aldehyde selected from the group consisting of condensation products of formaldehyde with melamine, substituted melamine, urea, benzoguanamine and substituted benzoguanamine, and mixtures of said condensation products and is included in an amount sufficient to provide between about 0.6 and about 2.1 equivalents of nitrogen crosslinking functionality per equivalent of hydroxy functionality.
19. A composition in accordance with claim 1, wherein said hydroxy functional additive is a polyol selected from the group consisting of (i) hydroxy functional polyesters, (ii) hydroxy functional polyethers, (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers formed from monoethylenically unsaturated monomers, one or more of which bears hydroxy functionality and which is included in said copolymer in amounts ranging from about 10 to about 30 weight percent of said copolymer, and (vi) mixtures of (i)-(v).
20. A composition in accordance with claim 1, wherein said organophosphate ester is included in said composition in an amount sufficient to provide between about 1.2 equivalents of acid functionality for each equivalent of pendant epoxy functionality on said copolymer.
Patent Citations (11)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2528359 | 1950-10-01 | Greenlee | |
| US2528360 | 1950-10-01 | Greenlee | |
| US2541027 | 1951-02-01 | Bradley | |
| US2732367 | 1956-01-01 | Shokal | |
| US2849418 | 1958-08-01 | Fang | |
| US3133838 | 1964-05-01 | Higgins | |
| US3198850 | 1965-08-01 | Levantin | |
| US3651169 | 1972-05-01 | Davis | |
| US3960979 | 1976-06-01 | Khanna | |
| US4027066 | 1977-05-01 | Victorius | |
| US4055607 | 1977-10-01 | Sullivan |