US 4,174,490 AGrant
Cathode-Ray Tube
Issue Date:1979-11-13
•2 Claims
Abstract
Disclosed is a cathode-ray tube having a face plate of soft glass which up to an accelerating voltage of 40 KV gives an X-ray emission of at most 0.5 mr/h measured at a distance of 5 cm. The glass has a strain point between 450.degree. and 480.degree. C. and a softening temperature between 660.degree. and 770.degree. C. and comprises, inter alia, 3-14% by weight of BaO and 5-10% by weight of PbO.
Metadata
Assignee
- U.S. Philips Corporation
Inventors
- Klaus C. Van Erk
- Marinus Ploeger
- Peter H. Von Reth
Application Information
Application Number:US 9075534
Filing Date:1978-05-19
Priority Date:1977-05-25
Art Unit:113
Classifications
IPC:
H01J 3120C03C 310C03C 330
Field of Search:
10631325253480478
Patent Drawings
This patent does not have any drawings.
Description
The invention relates to a cathode-ray tube for displaying television pictures in colour comprising an evacuated glass envelope with one or several electron guns positioned therein and a face plate with a fluorescent layer comprising a pattern of phosphor regions disposed opposite the electron guns.
The invention, in particular, relates to a face plate for such a tube and to a glass composition for the face-plate.
The envelope of such display tubes is composed of three glass parts, namely the neck, the cone and the face plate, which may consist of different types of glass which, however, are physically matched to each other.
British Patent application 76/13,864 discloses one type of glass suitable for the face-plate and the cone of such a cathode-ray tube for displaying black-and-white pictures which is also suitable for the face-plate of a colour cathode-ray tube. The glass which contains no lithium oxide is characterized by a composition in % by weight between the following limits:
These glasses have the following physical properties: an annealing point (.eta.=10.sup.14.6 poises) of approximately 430.degree.-450.degree. C.; a strain point (.eta.=10.sup.13.5 poises) of approximately 450.degree.-480.degree. C.; a softening temperature (.eta.=10.sup.7.6 poises) of 660.degree.-700.degree. C. and a working temperature (.eta.=10.sup.4 poises) of 990.degree.-1040.degree. C. The values for the strain point and the annealing point are 20.degree. to 40.degree. C. lower than it was heretofore believed necessary to make a colour cathode-ray tube and to evacuate the envelope without unacceptable deformation. A consequence of this is that the softer glass can be polished much more rapidly, since the shear mark is less deep.
In addition, there are a few requirements which have to be fulfilled, namely the difference between the softening temperature and the high strain point must be at least 190.degree. C. and the difference between the working temperature and the softening temperature, the so-called "warm length" should be at least 300.degree. C.
Then there is also a requirement with respect to the permeability of X-rays, namely a screen glass having a thickness of at least 11 mm and an accelerating voltage of 27.5 kV on the electron gun and an anode current of 3.times.100 .mu.A may have an X-ray transmission which, measured at a distance of 5 cm from the face-plate, is at most 0.5 millirontgen per hour.
For circuits of a certain type in some devices with colour cathode-ray tubes a larger margin is necessary for the accelerating voltage in order to fulfil the above mentioned criterion under all circumstances, namely 40 kV. However, the above-defined class of glasses no longer satisfies this requirement. It is the object of the invention to provide a class of glasses which does fulfil this requirement and also has the above-mentioned ranges of strain point, softening temperature and working temperature.
A cathode-ray tube according to the invention comprises a glass envelope with a face-plate made from a glass having a strain point between 450.degree. and 480.degree. C., a softening temperature between 660.degree. and 700.degree. C. and a working temperature between 990.degree. and 1040.degree. C. The glass of the face plate has a composition in % by weight characterized by the following limits:
, with the complementary conditions that
Al.sub.2 O.sub.3 +ZrO.sub.2 >2
BaO+2SrO+2ZrO.sub.2 +3PbO>28 and
3CaO+2MgO+SrO+4ZrO.sub.2 <12
Glass compositions which satisfy these limits have an X-ray absorption coefficient .mu. at 0.6 A>26.sup.-1 and at 0.31 A>5 cm.sup.-1, so that they satisfy the above-mentioned criterion.
It is to be noted that a lead oxide-containing glass for envelopes of cathode-ray tubes is known from U.S. Pat. No. 3,663,246 which has a somewhat related composition. However, it comprises more potassium oxide, more calcium oxide, less sodium oxide and is thus considerably harder.
The invention will be described in detail with reference to the following examples.
The glass compositions defined in the following Table were melted in a glass furnace which was heated by natural gas in a weakly oxidizing atmosphere. The starting mixture consisted of sand, potassium telspar, potassium carbonate, sodium carbonate, barium carbonate, minium, antimony oxide and optionally dolomite, magnesium oxide, calcium carbonate and zirconium silicate. The SrO occurring in the glass is to be ascribed to a contamination in the BaCO.sub.3.
The physical properties of the resulting glasses are recorded, namely the viscous properties as defined above, the t.sub.K =100, which is the temperature at which the specific resistance of the glass is 100 M Ohm.cm. the T.epsilon., which is the temperature at which the specific resistance of the glass is 10.sup.6.5 Ohm.cm, the value of log.epsilon.(.epsilon. in Ohm.cm) at the temperatures 250.degree. and 350.degree. C. and the X-ray absorption coefficient .mu. at 0.6 A.
Face plates of these glass compositions were pressed and were provided on the inner surface with a pattern of red, green and blue phosphor dots.
The face plates were secured, by means of a devitrifiable vitreous enamel, to a glass cone having the following composition in % by weight
and to a neck portion, in which the electron guns are sealed in, of the following composition in % by weight
After sealing together, the tube was heated to a temperature of approximately 450.degree. C. and evacuated.
Claims
What is claimed is:
1. In a colour television cathode ray tube included an evacuated glass envelope having a glass face plate, a fluorescent layer having a pattern of phosphor regions on the inner surface thereof, and at least one electron gun disposed in said envelope opposite said face plate, the improvement wherein said glass of said face plate consists essentially of, in percent by weight: SiO.sub.2 60-68 SrO 0-1 Al.sub.2 O.sub.3 0-6 PbO 5-10 Na.sub.2 O 5-12 combined ZrO.sub.2 0-3 K.sub.2 O 3-11 >13 CeO.sub.2 0-0.6 CaO 0-1 Sb.sub.2 O.sub.3 + As.sub.2 O.sub.3 0.3-0.7 MgO 0-2 F 0-1.5 BaO 3-14 TiO.sub.2 0-0.3 ______________________________________ with the complementary conditions that Al.sub.2 O.sub.3 +ZrO.sub.2 >2 BaO+2SrO+2ZrO.sub.2 +3PbO>28 and 3CaO+2MgO+SrO+4ZrO.sub.2 <12
2. A glass composition for a face plate of a cathode ray tube consisting essentially of, in percent by weight: SiO.sub.2 60-68 SrO 0-1 Al.sub.2 O.sub.3 0-6 PbO 5-10 Na.sub.2 O 5-12 combined ZrO.sub.2 0-3 K.sub.2 O 3-11 >13 CeO.sub.2 0-0.6 CaO 0-1 Sb.sub.2 O.sub.3 + As.sub.2 O.sub.3 0.3-0.7 MgO 0-2 F 0-1.5 BaO 3-14 TiO.sub.2 0-0.3 ______________________________________ with the complementary conditions that Al.sub.2 O.sub.3 +ZrO.sub.2 >2 BaO+2SrO+2ZrO.sub.2 +3PbO>28 and 3CaO+2MgO+SrO+4ZrO.sub.2 <12