US 4,151,003 AGrant
Viscosity Modification of Bituminous Materials
Issue Date:1979-04-24
•11 Claims
•3 Drawing Sheets
Abstract
Methods of modifying the viscosity of bituminous materials in which a fluoro or chlorofluoro derivative of a lower alkane is mixed therewith, and processes involving and employing products so modified.
Metadata
Assignee
- Otisca Industries, Ltd.
Inventors
- Clay D. Smith
- Douglas V. Keller, Jr.
Application Information
Application Number:US 662619&
Filing Date:1976-03-01
Priority Date:1976-03-01
Art Unit:143
Classifications
IPC:
C08L 9500
Field of Search:
106278;280;281;284
Patent Drawings (3 sheets)
Description
Other important objects and features and further advantages of the invention will become apparent from the appended claims and as the ensuing detailed description and discussion of representative applications of the principles of our invention proceeds in conjunction with the accompanying drawing, in which:
FIG. 1 is a graph which shows how the viscosity of a North Slope crude oil can be so modified in accord with the principles of the present invention as to make the crude pumpable at arctic temperatures without the addition of heat and with the expenditure of only moderate amounts of energy;
FIG. 2 shows how varying amounts of one of our novel viscosity modifiers effect the viscosity of bitumen extracted from Athabaska tar sands; and
FIG. 3 shows the effect which a selected proportion of the modifier had on the bitumen at various temperatures.
Referring now to the drawing, FIG. 1 shows in graphic form the remarkable reduction in viscosity obtained by mixing viscosity modifiers of the character described above with crude oils.
The oil employed in the tests from which the graphically displayed data was obtained is a North Slope crude with a specific gravity of 0.882 obtained from Exxon Corporation. This crude is virtually a solid at the -60.degree. F. temperatures reached in Arctic regions in the wintertime.
Economics dictate that the viscosity of a crude be not greater than about 100 centipoises while it is pumped. As shown by curve 20 in FIG. 1, this means that the crude in question must be kept at above-freezing temperatures if heat alone is to be relied upon for viscosity reduction.
However, curve 22 shows that, by mixing 17 percent by volume trichlorofluoromethane with the same crude, it can be pumped at temperatures approaching 0.degree. F. By increasing the volume of CCl.sub.3 F to 30 percent the pumping temperature can be reduced to ca. -10.degree. F. (curve 24); and, by increasing the viscosity modifier volume to 50 percent, the viscosity of the crude remains below the economically pumpable 100 centipoise level at temperatures well below those typically encountered in Arctic regions (curve 26). At -60.degree. F., for example, the viscosity of the mixture is only ca. 45 centipoises.
Points 28 and 30 of FIG. 1 shows that mixtures of chlorofluoroalkyls are effective viscosity modifiers. These points represent data obtained from tests of mixtures which were, respectively, by volume: 88 percent crude, 10 percent CCl.sub.3 F, and 2 percent CHClF.sub.2 and 80 percent crude, 10 percent CCl.sub.3 F, and 10 percent CHClF.sub.2. The same North Slope crude was employed in these tests.
FIG. 1 shows that our novel viscosity modifiers are effective over a wide temperature. For example, though beyond the limits of the Figure, a mixture of 83 percent by volume of the North Slope crude and 17 percent CCl.sub.3 F is 50 percent less viscous at room temperature than the crude by itself. Even at relatively high temperatures, therefore, advantage can be taken of our novel viscosity modifiers to facilitate the handling and transport of hydrocarbonaceous materials.
Tests were also made to confirm that the viscosity modifier could be readily and economically stripped from the crude. The viscosity modifiers were removed as described in parent application Ser. No. 460,558. The tests showed that virtually all of the modifier could be recovered at temperatures below 100.degree. C. in the case of CCl.sub.3 F and below 50.degree. F. in the case of CHClF.sub.2.
To show that our novel technique for modifying the viscosity of hydrocarbonaceous materials so they can be economically pumped through pipelines is not limited to conventional crudes, tests similar to those described above were made substituting for the North Slope crude a bitumen recovered from Athabaska tar sands. This bitumen has a viscosity exceeding 20,000 centipoises at room temperature.
Curve 32 in FIG. 2 shows that the viscosity of the bitumen can be reduced by two orders of magnitude and more by mixing with it modest amounts of CCl.sub.3 F.
FIG. 3 shows, graphically, the effect on the viscosity of the bitumen which was obtained by mixing with the bitumen 40 percent by volume of chlorotrifluoromethane. As indicated by curve 34, at temperatures approaching 0.degree. F., the viscosity of the mixture was still 50 percent below the level necessary for economical pumping.
To demonstrate how the principles of the present invention can be employed to advantage in applications involving coatings and coverings, a mixture of 70 percent by volume CCl.sub.3 F and 30 percent asphalt was prepared by agitating the constituents in a beaker with a laboratory model Lightning mixer.
A piece of one-half inch thick CDX plywood was coated with the viscosity modified material. Tar (or roofing) paper was also coated with the mixture and placed on the plywood. The resulting bond between the roofing paper and the plywood was relatively uniform and of sufficient strength to hold the tar paper in place.
At approximately one-half hour intervals, two additional plies of the roofing paper were cemented to the first ply with the viscosity modified asphalt. A coating of the material was applied to the third ply.
In none of these applications was the viscosity modified asphalt heated.
The resulting three-ply, simulated roof had a good appearance. After drying for 24 hours at ambient temperature a strong bond developed between the roofing paper plies and between the latter and the plywood substrate.
In another test, a conventional concrete building block was coated with viscosity modified asphalt as discussed above, again at ambient temperature. The material readily penetrated approximately one-sixteenth inch into the block. All of the pores opening onto the exterior of the block appeared to be sealed. To ensure that they were, a second coat of the viscosity modified asphalt was applied.
Standing water would not penetrate the dried coating. The bond between it and the concrete block was rated excellent.
In a companion test, unprimed sheet metal was coated with the viscosity modified asphalt at ambient temperature. After the material had dried for 24 hours, the specimen was bent to a three inch radius. The asphalt cracked, but did not flake off. This is an indication that a good bond had formed between the coating material and the sheet material substrate.
As discussed above, viscosity modified hydrocarbonaceous materials in accord with the principles of the present invention can also be employed to advantage in road patching and similar compositions. To demonstrate this aspect of the invention, equal volumes of asphalt and trichlorofluoromethane were blended as discussed above. This composition was mixed with clay which had been oven dried for three hours at 350.degree. F. in the proportion of 20 percent by weight clay and 80 percent viscosity modified asphalt. The CCl.sub.3 F-asphalt-clay composition was blended with crushed, size IA limestone to form a cold patch material.
This was applied to a concrete surface which had been primed with the 50 percent asphalt, 50 percent CCl.sub.3 F mixture. The patch was approximately six inches wide by twelve inches long and two inches deep. After it had dried for twelve hours, the patch would support the weight of a man without any appearance of plastic deformation.
The CCl.sub.3 F-asphalt-clay mixture was also applied as a coating to a concrete block. It was found that the extent to which blistering was present in the coating was significantly lower than is typically the case when conventional asphaltic coatings are employed.
The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. For example, other fillers and adjuvants can be employed to tailor the composition to the requirements of a particular application or to alter the characteristics of a particular hydrocarbonaceous material as required by the circumstances at hand. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description; and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
Claims
What is claimed and desired to be secured by Letters Patent is:
1. A stable plastic or flowable composition consisting essentially of a viscous bituminous material in stable solution in a non-azetropic, non-flammable, non-toxic viscosity modifier which is a liquid at a temperature of 75.degree. F. and ambient pressure, said viscosity modifier being essentially free of aqueous fluids, emulsifiers, and propellant gases and consisting of trichlorofluoromethane alone or in admixture with at least one of the group consisting of dichlorodifluoromethane, monochlorotrifluoromethane, tetrafluoromethane, monochlorodifluoromethane, trichlorotrifluoroethane, dichlorotetrafluoroethane, and tetrachlorodifluoroethane in an amount effective to produce a reduction in the viscosity of the bituminous material at ambient pressures and temperatures.
2. A composition according to claim 1, in which the viscosity modifier constitutes from 10 to 70 percent by volume based on the total volume of the solution.
3. A composition according to claim 1, containing a filler in admixture with said bituminous material and said viscosity modifier.
4. A composition according to claim 1, in which the bituminous material is a crude oil or the organic fraction of a tar sand or oil shale.
5. A composition according to claim 1, in which the bituminous material is an asphalt or tar.
6. A composition according to claim 1, which has a viscosity not exceeding about 100 centipoises under ambient conditions.
7. A method of reducing the viscosity of a bituminous material which comprises the step of dissolving said material in a non-azeotropic, non-flammable, non-toxic viscosity modifier which is essentially free of aqueous fluids and propellant gases and is a liquid at a temperature of 75.degree. F. and ambient pressure to produce a stable solution of bituminous material in the viscosity modifier, said viscosity modifier consisting of trichlorofluoromethane alone or in admixture with at least one of the group consisting of dichlorodifluoromethane, monochlorotrifluoromethane, tetrafluoromethane, monochlorodifluoromethane, trichlorotrifluoroethane, dichlorotetrafluoroethane and tetrachlorodifluoroethane in an amount effective to produce a reduction in the viscosity of the bituminous material at ambient pressures and temperatures.
8. A method according to claim 7, in which the bituminous material is dissolved in from 10 to 70 percent by volume of viscosity modifier based on the total volume of the solution.
9. A method according to claim 7, together with the step of mixing a filler with said bituminous material and viscosity modifier.
10. A method according to claim 7, in which the bituminous material is a crude oil on the organic fraction of a tar sand or oil shale.
11. A method according to claim 7, in which the bituminous material is an asphalt or tar.
Patent Citations (4)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2524590 | 1950-10-01 | Boe | |
| US3313636 | 1967-04-01 | Blair et al. | |
| US3314907 | 1967-04-01 | Fronczak | |
| US3536509 | 1970-10-01 | Tay |
Non-Patent Literature (1)
- Rose et al., The Condensed Chemical Dictionary, Seventh Edition, Pub'd by Van Nostrand Reinhold Co., N.Y., p. 963, "Trichlorofluoromethane", 1966.