Process for Forming Fishing Lure Component and Article Formed Thereby

1. Field of the Invention

This invention pertains to a method for making a fishing lure component and a resulting article.

2. Prior Art

Heretofore, fishing lures have included hair-like materials such as bucktail, bear hair, impala, squirrel tail, or thermoplastic fiber hair. These various hairs or fibers have typically been placed on the lure, and the practice has been to use thread to tie such materials to the lure. In use, it has been found that the thread used in tying a lure has been severed by teeth of fishes, and also that the thread has been abraded by rubbing action on rocks. Further, when one or more strands of hair or fiber have been pulled out of the tied lure, there is a gradual or rapid loss of remaining hair strands. Further, hand-tying techniques that have been used commercially have contributed materially to production costs because of the labor. Also, there have been various attempts to cement hair or hair sections onto or into a lure component, and such attempts have been faced with similar difficulties.

The present invention is directed to the use of heat-fusible material formed as hair-like fiber that is fused together by heat at a relatively closely controlled temperature, such fused-together hair comprising a hot flexible bond which is placed around an elongated member and jointly placed in a mold for reshaping the internal and external contour of the bond the same has cooled to the setting point. Such molding necessitates the use of a force or pressure of such magnitude as to effect not mere engagement of the ends of the bond, but as to effect actual joining of the ends of the bond together.

Accordingly, it is an object of the present invention to overcome the problems that are created by the formation of a film on the surface of the heated common bond.

A further object of the present invention is to provide a re-mold bond which will be structurally strong for keeping the hair fibers attached to the hook or for keeping the hair fibers strongly attached to the lure component.

Another object of the present invention is to provide a method by which certain fishing lure components can be inexpensively produced.

Yet another object of the present invention is to provide a fishing lure component made in accordance with the present invention.

Many other advantages, features and additional objects of the present invention will become manifest to those versed in the art upon making reference to the detailed description and the accompanying sheets of drawings in which a preferred structural embodiment incorporating the principles of the present invention is shown by way of illustrative example.

FIG. 1 is a diagram illustrating the formation of a hot bond;

FIG. 2 illustrates wrapping the hot bond around an elongated member;

FIG. 3 illustrates placing the hot bond and the elongated member jointly in a shaping and cooling mold;

FIG. 4 illustrates the resulting article;

FIG. 5 illustrates an alternate form of elongated member about which the hot bond can be wrapped; and

FIG. 6 illustrates a further fishing lure component that can be made using the elongated member of FIG. 5.

In accordance with the method, a quantity of heat-fusible material formed as hair-like fibers lying in a generally common direction is placed in a substantially flat planar manner as shown in FIG. 1, generally indicated by the numeral 10. The fibers comprise a short length of modacrylic fiber (such as sold under the trademarks Dynel, and Kaneckalon) arranged as a tow or part of a tow. Such fibers may have a previously made brittle bond 11. Such quantity of fibers can constitute a portion of a hair "bundle" broken from a bundle such as illustrated in FIG. 1 of U.S. Pat. No. 3,864,864 issued Feb. 11, 1975, and assigned to the assignee of the present application. Such initial bond may be made as described in U.S. Pat. No. 3,972,760 issued Aug. 3, 1976, a division of the first-mentioned patent.

The bundles normally have hair of a length that is proper for the manufacture of a particular lure component, or that is too long. The bundles normally have a width greater than necessary. As mentioned, a quantity can be broken from the brittle bundle which has enough hairs to make the desired component.

A pair of heated bars 12,13 are provided to reheat or soften the bond 11, such heating being at a temperature of about 375.degree. F. If the desired length "x" of the hair for the lure component is less than that of the bundle, then the hair can be placed between the bars as shown in FIG. 1 so that a new hot flexible narrow planar bond of the hair material is formed as shown at 14 and which extends transversely to the fibers and lies in the plane of the hair or material 10. If a heating bar is utilized as shown in the above-mentioned patents, then there will be automatic severance along the length of the bond 14. On the other hand, any other form of trimming away the excess material may be utilized while the bond 14 is still hot. The heated bars 12,13 perform their heating while the hair is compressed or clamped therebetween.

After any necessary trimming has been completed, the hot flexible bond 14 is wrapped around an elongated member, such elongated member here constituting the shank of a treble hook 15. As there are two or three wires in the shank 15, the portion of the hook that is surrounded by the hot band 14 is noncircular in cross-section, taken as a whole.

With the hot bond 14 in place around the shank 15, the bond with its hair and the shank are jointly immediately placed into a mold shown in FIG. 3, there typically being a lower portion 16 which is fixedly supported and a movable portion 17. If desired, the mold portions 16,17 may be provided with cutting edges 18,19 to trim away any excess thermoplastic material. The mold halves 16,17 are then brought together, preferably with an impact and with a substantial pressure, the pressure being typically in excess of 1000 psi. The mold halves 16,17 are not of themselves heated, and they provide a shaping function to the outside of the bond, and because of reaction by the elongated member 15, the interior of the re-molded bond is also determined. The mold 16,17 is held closed until it has chilled the bond so that it is no longer flexible. Because of the configuration of the cross-section of the elongated member, the molded bond is securely affixed to such elongated member or lure component.

In working with this method, I have found that the bond 11 and the bond 14, as a consequence of the heating described, acquire a film thereon which is waxy to the touch, and the material of this film also adheres to certain tooling that has been used. It is therefore believed that such film is a decomposition product of the material of which the synthetic thermoplastic hair is made. This film forms a barrier that tends to prevent the joining together of the ends of the bond 14 that are shown adjacent to each other in FIG. 2. However, when there is sufficient temperature, pressure, and movement within the die, part of which comes as a consequence of impact on closing the die, such film appears to be adequately broken so that the material beneath the film at the opposite ends of the bond can in fact join together and be as strong as other parts of the original bond.

Where the elongated member is to comprise a single element 20 of circular cross-section, it then becomes desirable to provide some form of roughness 21 on the surface. For example, such roughness could be provided as an adhesive. On the other hand, when the roughness 21 is omitted, the elongated element 20 can constitute a highly polished mandrel to which the molded bond will not stick, and because of the waxy surface of the interior of the resulting tubular bond 22, FIG. 6, the molded component will readily slip off the mandrel 20 to provide an alternate form of fishing lure component. The film inherently has a low coefficient of friction which not only facilitates the removal of the component of FIG. 6 from the mandrel of FIG. 5, but which has a utility in use. The article of FIG. 6 is slipped over a fishing line and it is permitted to slide therealong until it reaches some other component near the end of the line that blocks further movement. If the hook-end of the line extends from the end where the hair is joined, the hair will tend to flow backward in use over whatever element is there in abutting relation, for example a swivel (not shown). If the lure component of FIG. 6 is put on in the other direction, then the hair tends to form a cone that fans out and forms a larger diameter effect in the water.

If desired, the molded portion of the article of FIG. 4 or the molded portion of the article of FIG. 6 may be covered with an epoxy-base paint. If painting is desired, it should be kept in mind that the film on the molded bond will prevent the adherence of most paints, but a paint having the adherence-property of an epoxy-base paint should therefore be used.

Although the invention can be practiced optionally beginning with an amount of loose hair fiber cut to proper length, it is more convenient to manufacture the lures beginning with the article of U.S. Pat. No. 3,864,864 as a starting material. A typical area that would be heated in the step of FIG. 1 would be three-eighths inch along the length of the hair and three-fourths inch along the length of the heater bars. If so, by trimming, the 3/8 inch dimension can be reduced to 3/16 inch. The dimension "x" typically is on the order of two inches.

The nature of the apparent break-down of the modacrylic fiber is not fully understood, but the effect thereof and the manner of overcomming such effect is adequately set forth herein. The scrubbing action of the heated bond within the mold is one of the factors that disrupts such film to enable formation of the bond-to-bond joint. Thus the result is a uniform forgewelded, integral common material head. The avoidance of weakness at such joint is essential to provide the necessary structural strength.

The resulting articles have molded bonds that cannot be adversely effected by the teeth of fish or by the rubbing action on rocks, and any loss of a few strands of hair or fibers has no effect whatever on the integrity or strength of the molded bond.

Although various minor modifications might be suggested by those versed in the art, it should be understood that I wish to embody within the scope of the patent warranted hereon, all such embodiments as reasonably and properly come within the scope of my contribution to the art.