Polymeric Carrier Bound Ligands

The present invention relates to a new process for bonding substances (ligands or effectors) of high or low molecular weight to polymeric carriers and to carrier/ligand reaction products.

It has already been disclosed that carriers containing hydroxyl groups can be activated with cyanogen bromide and subsequently coupled with suitable effectors or ligands via free amino groups in these effectors. (R. Axen, J. Porath and S. Ernback, Nature 1967, 214, 1302-1304). However, as Tesser et al. were able to show, this above mentioned process has the disadvantage that the isourea bond, which is present in this case, between the effector and the carrier is not stable to hydrolysis [G. I. Tesser et al. FEBS Letters (1972) 23, 56 and G. I. Tesser et al. Helv. Chim. Acta 57, 1718-1730 (1974)].

Another process, which goes back to E. Katchalski, Biochem. 1964, 3, 1905-1919, uses polymers containing anhydride groups. With this type of resin, the enzyme bond is due to the fact that the reaction of the amino groups of the enzyme with the anhydride groups of the resin takes place more rapidly than the competing reaction with the surrounding water.

Other processes use, for example, the reaction of epoxy groups on polymers with amino groups, thiol groups and hydroxyl groups (L. Sundberg and J. Porath, J. Chromatogr. 1974 90, 87-98), but in this case pH values of 8.5-11 and reaction times of 15 to 48 hours are required and these have a denaturing effect on numerous enzymes.

A summary of the numerous possibilities is given by, for example, C. Zaborsky in Immobilised Enzymes, CRC Press, Cleveland 1973.

Cyanuric chloride and other triazine derivatives were used by G. Kay and M. D. Lilly as early as 1967 for activating cellulose and for coupling with enzymes. (G. Kay and E. M. Crook, Nature 1967 216 514; and G. Kay, M. D. Lilly, A. K. Sharp and R. J. H. Wilson, Nature 1968 217, 641). The stability of the bond did not meet all of the requirements. Changing to the use of derivatives of trichlorotriazine (S. Kay and M. D. Lilly Biochim. Biophys. Acta (1970) 198, 276-285) resulted in better handling of the reaction but brought no improvement in the observed instability of the bonds.

It has now been found that an exceptionally stable bond between a ligand and a polymeric carrier can be obtained when:

(A) THE LIGAND CONTAINS AN OH, NH.sub.2, NHR.sup.5, CONH.sub.2, CONHR.sup.5 or SH group and is reacted, if necessary in the presence of a base, with an activated polymeric carrier that has at least one unit thereof of the formula: ##STR2## wherein T represents atoms of the polymeric carrier;

X is a divalent oxygen or sulfur atom, --NH--, --NHR.sup.5 --, --CONH-- or --CONR.sup.5 --, wherein R.sup.5 is lower alkyl;

R is independently hydrogen, hydroxyl, lower alkyl, lower alkoxy, loweralkylthio, loweracylamino, nitro, cyano, carboxamide, loweralkylsulphonyl, loweralkoxycarbonyl, phenyl, trifluoromethyl or chloromethyl, provided that at least one R is halogen; and

a is 1 or 2, b is 4-a, c is 0 or 1 and d is 2-c; or

(b) a ligand containing an OH, NH.sub.2, NHR.sup.5, CONH.sub.2, CONHR.sup.5 or SH group is activated by a condensation reaction with a pyrimidine derivative of the general formula: ##STR3## in which R.sup.1, R.sup.2, R.sup.3 and R.sup.4 are each independently hydrogen, hydroxyl, halogen, lower alkyl, lower alkoxy, lower-alkylthio, loweracylamino, nitro, cyano, carboxamido, loweralkylsulphonyl, loweralkoxycarbonyl, phenyl, trifluoromethyl or chloromethyl; provided that at least two of R.sup.1 to R.sup.4 are halogen,

and is then reacted with a polymeric carrier that contains OH, NH.sub.2, NHR.sup.5, CONH.sub.2, CONHR.sup.5 or SH, if necessary in the presence of a base and, if the activated ligand is a reactive dyestuff, the condensation product obtained from the carrier and the reactive azo dyestuff is optionally isolated, the condensation product is optionally reduced with a suitable reducing agent to give the free amino compound, the latter is diazotised with sodium nitrite and acid and the diazo compound is then reacted with a suitable coupling reagent.

As used herein, the terms "lower alkyl", "lower alkoxy", "loweralkylthio", "loweracylamino" and "loweralkylsulfonyl" denote radicals containing 1 to 6, preferably 1 to 4, carbon atoms, and the term "loweralkoxycarbonyl" denotes a radical containing 2 to 7, preferably 2 to 5, carbon atoms. The term "halogen" denotes fluoro, chloro, bromo and iodo.

The new reaction products according to the invention, which have been prepared according to process variant (a) or process variant (b), are suitable, for example, for carrying out separations by adsorption chromatography or, if the ligand represents, for example, an enzyme, also for carrying out enzymatic reactions.

Carrier-bonded enzymes are stabilized and can be directly employed for reactions and can be recovered after the reaction in a simple manner and re-used. R. A. Messing, "Immobilised Enzymes for Industrial Reactors" Acad. Press, N.J. 1975 and O. R. Zaborsky "Immobilised Enzymes" CRC Press, Cleveland 1973, are new summaries of the numerous literature sources.

Enzymes coated with soluble substances such as dextrans are stabilized to heat, despite their solubility, and can be used, for example, as additives for washing agents.

Because they have specific adsorbent properties, low-molecular weight effectors on carriers serve for the purification of proteins (Shaltiel, Methods Enzymol (1974) 34, 126).

Specific, carrier-bonded effectors, such as, for example, inhibitors, serve for the purification of proteins by affinity chromatography. A recent summary of the literature by J. Porath and T. Kristiansen is given in Neurath, edited by Hill, "The Proteins", volume 1, 3rd edition, Acad. Press 1975.

If, in a simplified method of preparation, a halogen atom of the pyrimidine derivative employed reacts with, in each case, a hydrophilic group of the ligand or of the carrier, the course of the process according to the invention can be illustrated by the following reaction equation:

(a) Activated carrier as the starting material ##STR4## (b) Activated ligand as the starting material ##STR5##

The method of preparation described above is greatly simplified; under certain circumstances two halogen atoms are exchanged, and crosslinking takes place, during the preparation of the activated carrier and, optionally, the ligands. Surprisingly, the new reaction products according to the invention, which have been prepared according to process variant (a) or process variant (b) are exceptionally stable to hydrolysis and are considerably more stable to hydrolysis than the carrier/ligand coupling products described in the literature.

As can be seen from the above description, the activated ligand can be represented by the general formula: ##STR6## where L is the residue of the ligand and X and R are as defined above, provided that at least one R is halogen.

The process according to the invention and the provision of the reaction products prepared by the process according to the invention represent a substantial advance in the art.

The following pyrimidine derivatives: ##STR7## 2,4,6-trifluoro-5-chloropyrimidine ("FCP") ##STR8## tetrafluoropyrimidine ("TFP") ##STR9## tetrachloropyrimidine ("TCP") are particularly preferentially employed for the preparation of the starting materials for process variants (a) and (b), that is to say of the activated carriers and the activated ligands respectively; however, other pyrimidine derivatives of the general formula (III) can also additionally be employed.

The preparation of FCP has been described by H. J. Schroeder et al. in J. Org. Chem. 27, 2580-2584 (1962). Other methods of preparation are to be found in the British Patent Specification No. 1,157,948 and British Patent Specification No. 1,158,300.

Tetrachloropyrimidine (TCP) can be prepared easily by the method of S. J. Childress and R. L. McKee, J. Am. Chem. Soc. (1950) 72, 4271-72.

In addition to the preferred pyrimidines FCP and TCP, other pyrimidine derivatives of the general formula (III) can also be employed, such as 2-fluoro-4,5,6-trichloropyrimidine, 2,4-difluoropyrimidine, 2,4-difluoro-6-methylpyrimidine, 2,6-difluoro-4-methyl-5-chloropyrimidine, 2,4,6-trifluoropyrimidine, 2,4-difluoropyrimidine-5-ethylsulphone, 2,6-difluoro-4-chloropyrimidine, 2,4,5,6-tetrafluoropyrimidine, 2,4,6-trifluoro-5-chloropyrimidine, 2,6-difluoro-4-methyl-5-bromopyrimidine, 2,4-difluoro-5,6-chloro- or -dibromo-pyrimidine, 4,6-difluoro-2,5-dichloro- or -dibromo-pyrimidine, 2,6-difluoro-4-bromopyrimidine, 2,4,6-trifluoro-5-bromopyrimidine, 2,4,6-trifluoro-5-chloromethylpyrimidine, 2,4,6-trifluoro-5-nitropyrimidine, 2,4,6-trifluoro-5-cyanopyrimidine, 2,4,6-trifluoropyrimidine-5-carboxylic acid alkyl esters or -5-carboxylic acid amides, 2,6-difluoro-5-methyl-4-chloropyrimidine, 2,6-difluoro-5-chloropyrimidine, 2,4,6-trifluoro-5-methylpyrimidine, 2,4,5-trifluoro-6-methylpyrimidine, 2,4-difluoro-5-nitro-6-chloropyrimidine, 2,4-difluoro-5-cyanopyrimidine, 2,4-difluoro-5-methylpyrimidine, 6-trifluoromethyl-5-chloro-2,4-difluoropyrimidine, 6-phenyl-2,4-difluoropyrimidine, 6-trifluoromethyl-2,4-difluoropyrimidine, 5-trifluoromethyl-2,4,6-trifluoropyrimidine, 5-trifluoromethyl-2,4-difluoropyrimidine and others.

Polymeric carriers that can be used for the preparation of the activated carriers which serve as starting materials in the present invention include polymeric carrier substances, which contain hydroxyl, NH.sub.2, NHR.sup.5, CONH.sub.2, CONHR.sup.5, or SH as functional groups. Examples which may be mentioned from the large number of possibilities are those which follow: agarose, preferably bead-shaped agarose, supplied by Pharmacia Fine Chemicals under the tradename "Sepharose", types 2 B, 4 B and 6 B, crosslinked "Sepharose" gels, types Cl-2 B, Cl-4 B and Cl-6 B, and also dextrans and crosslinked dextrans (such as, for example, "Sephadex" supplied by Pharmacia Fine Chemicals, Uppsala, Sweden, for example in types G-75, G-100, G-150 and G-200, and, furthermore, cellulose (inter alia including cotton) and various cellulose derivatives, polyacrylamide resins, ion exchanger resins containing hydrophilic groups, such as, for example, aminomethylated polystyrene resins, polyvinyl alcohols and others. In this case it is entirely possible for yet further functional groups, such as carboxymethyl groups or diethylaminoacetyl groups, also to be present. Polymers based on styrene, acrylic acid and methacrylic acid, and their esters, can also be activated if they possess at least some of the above-mentioned functional groups in their structure. Thus, for example, weakly basic anion exchangers containing primary or secondary amines can be activated. It is also possible to activate polyvinyl alcohols and polyacrylamides. In the case of polymers that initially lack the above-mentioned functional groups, these functional groups can be introduced with the aid of secondary reactions and then the groups can be activated. Thus, for example, polymers containing anhydride groups (for example ethylene/maleic acid anhydride resins) can be reacted with polyalcohols or polyamines and these can then be activated with the halogenopyrimidines. Inorganic carriers, such as porous glasses ("glass beads"), can also be reacted with compounds containing functional groups or are already available commercially, such as, for example, "Glycophase"-G from Corning. Soluble polyhydroxy compounds, such as dextran, soluble starches, polyalcohols and polyamines can also be activated with the halogenated pyrimidines.

Literature relating to some of the cited carriers: "Sepharose" from agarose: Hjerten, Biochimica, Biophysica Acta 79, 393-398 (1968) and "Sephadex" as crosslinked dextran: thesis by Per Flodin, Uppsala 1962.

The NKZ 2 and NKZ 4 ion exchanger resins which, inter alia, are used in the examples are macroporous resins of polyvinylbenzylamine and crosslinked divinylbenzene, NKZ 2 containing about 8% of divinylbenzene and NKZ 4 containing approximately 6% of divinylbenzene. Examples of other ion exchangers which can be employed according to the invention are "Amberlite" IR 45 (containing a primary amino group) and "Lewatits", for example "Lewatit" MP 600.

When the new activated carriers of the formula (I) or (II) which are employed as starting materials in the process according to the invention, are prepared from hydrophilic carriers and pyrimidine derivatives of the formula (III), the procedure employed is such that the polymeric carrier, the halogenated pyrimidine and, if the carrier is not itself a base, also a further base for binding the hydrogen halide which is liberated, are brought together. This can be effected in an organic medium, for example dioxane, xylene or acetone or mixtures thereof, or also in organic-aqueous media. The reaction temperature is between about -10.degree. and about +30.degree. C. and preferably between about -2.degree. and about +6.degree. C.

The mixtures used by J. Warren, J. D. Reid and C. Hamalainen, Textile Res. Journal 1952, pages 584-590, for working with cyanuric chloride, and expecially the xylene/dioxane system, can advantageously be used.

When tetrahalogenated pyrimidines and carriers containing hydroxyl groups are used, 1 to 2 halogens, depending on the reaction conditions, react with the carrier. Crosslinking of the carrier can thus be achieved. The effect of this is extremely advantageous in, for example, the case of agarose ("Sepharose") since, as a result, this compound becomes stable to boiling.

The choice of the halogen substituent is also decisive for the ease of reactivity. Thus, the reactivity increases from bromine via chlorine to fluorine. Moreover, the tetrahalogenated compounds are more reactive than the trihalogenated or dihalogenated compounds. Other substituents on the pyrimidine, such as, for example, lower alkoxy or loweralkylthio, may raise or lower the reactivity, such as, for example, the alkylsulphonyl group or the nitro group.

For the special case of trifluorochloropyrimidine (FCP), the following sequence has been found for the removal of the halogens by reaction: ##STR10## Under the conditions described below, the last halogen, that is the chlorine, does not take part in the reaction.

During activation of the carrier, the reaction can also be controlled by the amount of the alkali which is necessary for neutralization, since the reaction does not proceed at pH values below 5. The most reactive pyrimidines, such as, for example, tetrafluoropyrimidine, form a possible exception here. In the case of the other pyrimidines, it is possible, especially after removing one fluorine atom by reaction, to stop the reaction by adding acids, for example acetic acid or phosphoric acid, or a phosphate buffer of pH 5. The required alkali can be initially introduced with the carrier, for example "Sepharose", and the halogenopyrimidine can then be added and in this case, when trifluorochloropyrimidine (FCP) is used in excess alkali, two fluorine atoms first react, with the formation of crosslinking, the effect of which is, for example, that the "Sepharose" becomes stable at temperatures approaching the boiling point. If a carrier which is activated to the greatest possible degree without crosslinking is desired, either the carrier and the alkali are added together to an excess of the halogenopyrimidine or a measured amount of alkali is added to the mixture of the carrier and the halogenopyrimidine. There are no restrictions as to the choice of the base. In addition to the hydroxides of the alkali metals, it is also possible to use, for example, tertiary or quaternary ammonium compounds. The temperatures which are most advantageous for the activation depend on the reactivity of the halogenopyrimidine and on the nature of the functional group on the carrier. In the case of FCP, the reaction is advantageously carried out at temperatures of about 0.degree. C. and with tetrachloropyrimidine, which reacts more sluggishly, the temperature used is up to room temperature and, of course, the reaction time is then also shorter. The alkylation of the hydroxyl groups generally proceeds somewhat more slowly than that of primary amino groups.

It is preferred that the activated carriers are reacted with the ligand (effector) immediately after the carrier has been activated. In many cases, however, it is possible to stabilize the activated carrier so that it is still active, and can be used after days or even months.

In the case of carriers containing hydroxyl groups, thorough washing out at low pH values, say of 5-6, suffices to keep them active for months, even in a water-moist state, at temperatures of 0.degree.-5.degree. C. Thus, for example, a "Sepharose" activated with FCP can be reacted with enzymes after it has been stored for 3 months without any loss in its ability to couple. In the case of carriers containing amino groups, a more rapid decline in the bonding ability has been observed under the above conditions. In many cases, drying in vacuo and storage in the dried state is then to be preferred.

The reaction, according to the invention, of the activated carrier with the ligands according to process variant (a) can be carried out both in purely organic media and in aqueous buffered systems. Low-molecular ligands (effectors) and, in particular, compounds which are very sparingly soluble in water are preferably reacted in organic media, such as, for example, tetrahydrofurane, dioxane, toluene or xylene, and a base which can be used is, for example, triethylamine.

Highly hydrophilic effectors, such as, for example, proteins, on the other hand, are reacted in aqueous buffered systems. The astonishingly low sensitivity of the halogenopyrimidine substituted carriers to hydrolysis is very essential for this possibility. Thus, enzymes can be reacted with the activated carriers in phosphate-, borate- or acetate-buffers in the pH range of 5-8, at a temperature of between about 0.degree. and about 40.degree. C. Among the functional groups of the proteins, it is, above all, primary amino groups, such as the amino groups of lysine or the amino groups at the end of the chain, --SH groups and the imidazole group of histidine which react with the activated carriers (J. Shore, J. Soc. Dyers and Colourists 84, 408-412, 313-421, 545-555 (1968) and S. Reinert et al. Melliand Textilberichte 49, 1313-1321 (1968)). The guanidino groups of arginine and the OH group of tyrosine are generally coupled at pH 10-14.

The following materials are preferably used as the ligands (effectors) in the process of the invention, according to process variant (a) or (b): effectors for the adsorption chromatography of organic substances, such as the low-molecular effectors, e.g. hexamethylenediamine, p-aminobenzamidine, ethylmercaptan, aminocaproic acid and benzylamine; proteins, such as, for example, albumin or any desired other proteins and polypeptides containing OH, NH.sub.2, NHR, SH, CONH.sub.2 or CONHR groups, and preferably enzymes, such as, for example, trypsin, penicillinase, substilisin, glucoseoxydases, aparaginase and ribonuclease; hormones, such as, for example, insulin; or enzyme inhibitors, such as, for example, the kallikrein-trypsin inhibitor. Furthermore, dyestuffs and dyestuff derivatives or, optionally, coupling products of dyestuff derivatives are also suitable as ligands.

A large number of halogenopyrimidine-activated dyestuffs and their use have already been described (D. Hildebrand and G. Maier, Textilpraxis 1971, Number 8, page 499-504 and Number 9, page 557-562; and German Published Specification No. 1,644,171). These reactive dyestuffs can be bonded to the above-mentioned carriers and used as effectors for purifying proteins. Azo dyestuffs coupled with carriers can find a special application in this way if they are reduced, in a manner which is in itself known, with suitable reducing agents, such as sodium dithionite, to the aromatic amines and the amine which is still present on the carrier is then diazotized and, in turn, used for coupling with low-molecular agents (for example .beta.-naphthol) or specific proteins. Proteins which contain tyrosine or histidine can be bonded in this way. This process variant for the preparation of the concentration products of activated ligands and carriers is a necessary complement to the coupling process for special proteins (enzymes) according to process variant (a). The reaction equation can be illustrated as follows: ##STR11##

Reactive dyestuffs that are particularly suitable have the general formula: ##STR12## in which: B and E are substituted or unsubstituted aromatic, carbocyclic or heterocyclic radicals (preferably B is the carbocyclic residue of a diazo compound of the benzene or naphthalene series and E is an enolic or phenolic coupling radical, such as a 5-pyrazolone, 5-aminopyrazole, acetoacetic acid arylamide, hydroxynaphthalene or aminonaphthalene radical);

R.sub.1 is hydrogen or methyl, preferably hydrogen; and

R.sub.1 ' and R.sub.2 ' are independently hydrogen or halogen, for example Cl, Br or F.

Examples which may be mentioned of reactive azo dyestuffs which can be employed for the reaction are those which follow: ##STR13##

The above-mentioned compounds and further azo dyestuffs which can be employed, and also processes for their preparation, are to be found in British Patent Specification No. 1,169,254.

The present invention is illustrated by the following Examples.

25g of moist agarose in bead form ("Sepharose" 4 B, Pharmacia) were suspended in water and the suspension was poured into a G 3 glass suction filter, at the outlet of which an approximately 80 cm long tube, which hangs down, effects gentle suction of the water. A mark made on the filter enables a volume of 24 ml of the "Sepharose" to be filled into the filter. The "Sepharose" was rinsed with 250 ml of distilled water. 50 ml of 3 M sodium hydroxide solution were added to the measured moist "Sepharose" and the mixture was shaken in a flask for 15 minutes at room temperature. The suspension was filtered in the same filter as above and the residue was suspended in 40 ml of a xylene/dioxane mixture (1:1, weight/weight) at 0.degree. C. in a silicone-coated round-bottomed flask with a stirrer or vibro-mixer. A solution of 2.5 ml of trifluorochloropyrimidine (FCP, density: 1.675.) in 4 ml of the xylene/dioxane mixture is allowed to run dropwise into this suspension so slowly that the temperature does not rise above +0.5.degree. C. One hour was required for this. After all of the FCP had been added, the reaction was stopped by adding 4.2 ml of concentrated acetic acid. The reaction mixture was poured into a suction filter and washed four times in this filter with 50 ml of the xylene/dioxane mixture and with 4 times 50 ml of dioxane and then with 1 l of distilled water. This washed, activated "Sepharose" can be stored for at least 3 months at 4.degree. C. (see Example 13).

In contrast to untreated "Sepharose", the FCP activated "Sepharose" does not dissolve on boiling.

In order to check the activation, samples from different batches were examined by elementary analysis.

The following composition (-galactose-anhydrogalactose-) (DFP).sub.2 would give the analysis: 4.61% N, 5.84% Cl and 6.28% F. DFP = difluorochloropyrimidine radical. The reduced content of F can be explained by the formation of crosslinkages and by partial hydrolysis of the fluorine (54%). The residual 40% remains as reactive fluorine.

23g of "Sepharose", which was prepared and treated with alkali according to Example 1, are added in portions to a solution, which has been cooled to 0.degree.-3.degree. C., of 4g of FCP in 40 ml of a xylene/dioxane mixture (1:1 weight/weight). Forty-five minutes were required for this. The reaction was then stopped by adding 4.2 ml of concentrated acetic acid and the reaction mixture was further worked up as described in Example 1.

The elementary analysis was: 5.69% N; 5.05% F; 6.42% Cl. The following composition (-galactose-anhydrogalactose).sub.4 (DFP).sub.3 would give the analysis: 5.03% N; 6.83% F; 6.38% Cl. The somewhat reduced content of fluorine can be explained by the formation of crosslinkages and by partial hydrolysis of the fluorine (24%). The residual 76% remain as reactive fluorine.

2g of moist "Sepharose" activated with FCP and prepared according to Example 1 were washed with water on a glass frit and introduced into a solution of 400 mg of hexamethylenediamine (HMDA) in 20 ml of water and the suspension was mixed well. The suspension was stirred for 12 hours at room temperature. The "Sepharose" was then washed with 200 ml of water, 100 ml of 0.1 N sodium hydroxide solution, 250 ml of water and 100 ml of methanol on the glass frit and filtered and the residue was dried in vacuo to constant weight.

Analysis: 5.91, 6.95 and 7.59% N.

This corresponds to the following composition: (-galactose-anhydrogalactose-).sub.3 (CP).sub.2 (HMDA).about..sub.2 .multidot.CP = monochloropyrimidine radical.

2g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 were washed on a glass frit with water and introduced into a solution of 50 mg of aniline in a 1:1 mixture of dioxane and McIlvain buffer of pH 7. The coupling reaction and further working up are carried out as indicated in Example 2. Analysis gave the following nitrogen content: 5.72%, 5.98% and 5.42% and this gives the following composition: (-galactose-anhydrogalactose-).sub.3 (CP).sub.2 (aniline).about..sub.2.

A solution of 102 mg of p-aminobenzamidine HCl in 3 ml of a 0.1 M borate buffer of pH 7.0 and 0.5 ml of 1 N sodium hydroxide solution was added to 2.15g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1. The suspension was stirred in a round-bottomed flask at room temperature for 20 hours. The coupling product was filtered off and washed with 200 ml of 0.1 M borate buffer of pH 7. From the determination, by spectrophotometry, of the p-aminobenzamidine in the filtrates and wash solutions and from the amount employed, it was possible to calculate a degree of substitution of 86 .mu.mols of benzamidine per gram of moist "Sepharose".

0.1 M borate buffer of pH 9.2 and 7 ml of ethanol and 1 ml of ethylmercaptan were added to 2g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1. The suspension was stirred for one night at room temperature. The coupling product was washed in a column with 200 ml of ethanol, 500 ml of water and 230 ml of ethanol/water (1:1, volume/volume). Elementary analysis gave a sulphur content of 2.77%. For comparison, a "Sepharose" 4 B which had not been activated but had otherwise been treated in an identical manner gave a sulphur content of less than 0.2%.

3g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 were washed briefly with 0.1 M borate buffer of pH 9.2 and stirred in a round-bottomed flask with a solution of 400 mg of cattle serum albumin in 4 ml of a 0.1 M borate buffer of pH 9.2 for 22 hours at room temperature. The resin was filtered off, washed with the above buffer, then suspended in a 1 M ethanolamine solution of pH 9.1 and after 3 hours filtered off again and washed with buffer. All of the filtrates and wash solutions were combined and the protein content of this combined solution was determined. 280 mg were found. Accordingly, 120 mg of albumin had been bonded to the "Sepharose".

800 mg of cattle serum albumin were bonded with 3g of moist, FCP-activated "Sepharose" 4 B by the method of Example 6. The protein content of the filtrates and wash solutions was 669 mg. Accordingly, 131 mg of albumin had been bonded to the "Sepharose".

3g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 were washed briefly with 0.1 M borate buffer of pH 9.2 and a solution of 8P mg of insulin (cattle) in 4.5 ml of 0.1 M borate buffer of pH 9.2 was added to the washed "Sepharose" in a round-bottomed flask and the mixture was stirred at room temperature for 22 hours. The coupling product was washed with the above borate buffer and in order to complete the removal of the active halogen byproduct, allowed to rotate for 17 hours at room temperature in 1 M ethanolamine of pH 9.2. After the product had again been washed with water and filtered, a degree of substitution of 8.54 mg of insulin per gram of moist "Sepharose" was obtained from the aminoacid analysis. In the lipocyte test, the formulation displayed an antilipolysis action of 85% of the theoretical activity.

The loss of bonded insulin, determined by radioimmunoassay, after 2.5 hours in Krebs solution, Ringer solution and albumin solution of pH 7.4 at 37.degree. C. was 0.3.degree./00.

2.5g of moist "Sepharose" activated with FCP and prepared according to Example 1 were suspended in 30 ml of a 0.1 M phosphate buffer of pH 7.0 and 25 mg (91 U) of kallikrein-trypsin inhibitor obtained from the lungs of cattle were added. The batch was stirred at room temperature for 20 hours. The "Sepharose"-bonded inhibitor was filtered off under a slightly reduced pressure and washed with the above phosphate buffer with and without the addition of 0.5 M sodium chloride. 2.48g of moist "Sepharose" containing inhibitor were obtained.

The inhibitory capacity determined by the inhibition of trypsin with benzoylarginine-p-nitroanilide (BAPNA) at 25.degree. C. of the filtrate and wash water was 27 U, and of the inhibitor on "Sepharose" was 13 U, which is 14% of the inhibitory capacity of the inhibitor employed.

2g of "Sepharose" activated with FCP and prepared according to Example 1 were suspended at 4.degree. C. in 30 ml of a 0.05 M phosphate buffer of pH 7.0 and 20 mg (18.6 U) of trypsin; 0.93 U/mg (as determined by BAPNA test) of trypsin were added. The mixture was stirred for 20 hours at 4.degree. C. and then washed with 100 ml of the above phosphate buffer, which also contained 0.5 M sodium chloride, and again with 100 ml of phosphate buffer without sodium chloride. The resin was filtered off on a G 2 glass frit using a very slight vacuum. 1.59g of moist trypsin-"Sepharose" were obtained.

The enzymatic activity (BAPNA; 25.degree. C.) in the filtrate and in the wash buffers was less than 0.5 U, and in the enzyme resin was 6.19 U (3.9 U/g of moist weight), which is 33% of the activity employed.

2g of the "Sepharose" activated with FCP and prepared according to Example 1 were suspended at room temperature in 30 ml of a 0.05 M phosphate buffer of pH 7.0 and a solution of 2.5 mg of penicillinase obtained from B. cereus and having an activity of 250 U (benzylpenicillin as the substrate) was added. The batch was stirred at room temperature for 20 hours. The enzyme-resin was filtered off on a G 2 glass frit under a slight vacuum and then washed with 100 ml of the above phosphate buffer, which also contained 0.5 M sodium chloride. After a further wash with 100 ml of phosphate buffer, but without sodium chloride, the resin was filtered off again.

Yield of enzyme-resin 1.50g

Enzymatic activity (benzylpenicillin; 25.degree. C.)

Filtrate and wash water 28 U

Enzyme-resin 218 U (145 U/g of moist weight).

The enzymatic activity was 87% of the activity employed or 98% of the activity of the bonded enzyme.

In order to test the stability of the bond of the enzyme to the carrier and also the enzyme activity, a 0.1 M phosphate buffer of pH 7.0 which contained 50 mg of Thimerosal per liter was allowed to flow, at a rate of 17 ml/hour, at room temperature through the enzyme-resin in a column. Samples were taken after 68 and 116 hours and their enzymatic activity was tested. After 68 hours 79% of the initial activity were found and after 116 hours 66% of the initial activity were still found. No activity could be detected in the eluates.

3g of moist, FCP-active "Sepharose" prepared according to Example 1, 4 ml of Palitzsch borate buffer of pH 8.4 and 18.7 mg of penicillinase with an activity of 1,650 U were stirred at room temperature for 18 hours. The enzyme-resin was filtered under gentle suction and rinsed three times with 10 ml of the above buffer. In order to inactivate any FCP-activated "Sepharose" which may still be present, the resin was stirred with 10 ml of 1 M ethanolamine solution, the pH of which had been adjusted to 8.4, at room temperature for 5 hours. The resin was then transferred into a small column and rinsed with 260 ml of 1 M sodium chloride solution and with 370 ml of a 0.05% strength sodium azide solution. After removing excess wash solution under gentle suction, 4.25g of enzyme-resin were obtained.

The enzymatic activity (benzylpenicillin, 25.degree. C.) was 907 U (213 U/g of moist weight), which is 55% of the activity employed.

After washing thoroughly, moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 was stored for 3 months at 4.degree. C. After this time, a 1g sample was taken and, as described in Example 11, was reacted with 110 U of penicillinase in a buffer at pH 7 and washed. 1.71g of moist enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash water was 1.8 U, and of the enzyme-resin was 101 U (59 U/g of moist weight), which is 92% of the activity employed.

1g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 was suspended in 20 ml of a phosphate buffer of pH 8.0, 10 mg of substilisin (1,980 U) were added and the mixture was stirred at room temperature for 18 hours. Further working up was carried out as described for penicillinase in Example 11, and the yield was 0.91g of the enzyme-resin. The enzymatic activity (acetyltyrosine ethyl ester, 25.degree. C.) of the filtrate and wash water was 1,611 U and of the enzyme-resin was 272 U (299 U/g of moist weight), which is 14.1% of the enzyme activity employed or 74% of the activity of the bonded enzyme.

1g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 was suspended in 20 ml of a 0.1 M phosphate buffer of pH 7.0, 10 mg (1,730 U) of glucose-oxydase were added and the mixture was shaken for 18 hours at room temperature. The enzyme-resin was filtered off and washed with the above phosphate buffer, with and without the addition of 0.5 M sodium chloride, in the customary manner. Yield: 0.89g of enzyme resin. The enzymatic activity (test with glucose and peroxydase, at 25.degree. C.) of the filtrate and wash water was 1,290 U and of the enzyme-resin was 36 U (32 U/g of moist weight), which is 2.1% of the enzyme activity employed or 8.2% of the bonded enzyme.

3g of moist "Sepharose" 4 B activated with FCP and prepared according to Example 1 were added to a solution of 98.5 mg (19,400 U) of asparaginase in Palitzsch borate buffer of pH 8.4 in a round-bottomed flask and the mixture was rotated for 17 hours at room temperature. After coupling, the "Sepharose" was filtered off in a G 2 glass frit and washed 3 times with the above borate buffer. The enzyme-resin was then left to stand in 1 M ethanolamine-HCl of pH 8.4 for 5 hours at room temperature and washed in a column with 260 ml of 1 M sodium chloride solution and 370 ml of a 0.05% strength sodium chloride solution. After filtering, 5.21g of moist enzyme-resin were obtained.

The enzymatic activity (L-asparagine, 37.degree. C.) of the enzyme-resin was 850 U (163 U/g of moist weight), which is 4.4% of the enzyme activity employed.

24g of moist "Sepharose" 4 B prepared as in Example 1 was suspended in 20 ml of xylene and 20 ml of dioxane and during this process was cooled to 0.degree. C. 10.9 ml (32.6 mmols) of 3 N sodium hydroxide solution were added and a solution of 2.99 ml (5.0g) (29.7 mmols) of FCP was then added in the course of 1 hour. The mixture was stirred for a further 1 hour and then worked up as described in Example 1.

Elementary analysis: 2.8% N.

1.17g of moist "Sepharose" 4 B activated with FCP according to Example 17 was suspended in 30 ml of a 0.05 M phosphate buffer of pH 7.0 and a solution of 2.5 mg of penicillinase (from B. cereus, 250 U) in 1 ml of the above phosphate buffer was added to this suspension. The batch was stirred at room temperature for 20 hours and worked up as described in Example 3. 1.63g of moist enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash solutions was 118 U and of the enzyme-resin was 130 U, 80 U/g of moist weight, which is 52% of the activity employed or 98% of the bonded enzyme.

Agarose in bead form ("Sepharose" 4 B from Pharmacia) were prepared analogously to Example 1 and treated with 3 M sodium hydroxide solution. The alkaline "Sepharose", which had been subjected to suction until the original volume of 24 ml was reached, was introduced into a solution, which had been cooled to -3.degree. to 0.degree. C., of 5.13g of TFP (tetrafluoropyrimidine) in 40 ml of xylene/dioxane (1:1, weight/weight) in the course of about 12 minutes using an injection syringe. The batch was stirred for a total of 30 minutes and the reaction was then stopped by adding 4.5 ml of concentrated acetic acid. The activated "Sepharose" was washed, and filtered off, as described in Example 1.

Like the FCP-activated "Sepharose", the TFP-activated "Sepharose" is so strongly crosslinked that, in contrast to the starting material, it does not dissolve on boiling.

Elementary analysis: 7.29% N. 13.19% F.

2g of moist "Sepharose" activated with TFP according to Example 19 were stirred with 5 ml of 0.7 M hexamethylenediamine in a round-bottomed flask for 20 hours at room temperature. The product was filtered off, washed with 250 ml of water, 100 ml of 0.1 N sodium hydroxide solution and 100 ml of water and eluted in a column with a further 500 ml of water. The product was filtered off.

A deep coloration is obtained with nitrin.

For elementary analysis, the product was washed with methanol and dried in vacuo.

Analysis: 6.24% F. 11.65% N.

2g of moist "Sepharose" activated with TFP according to Example 19, were washed with tetrahydrofurane and added to 3 ml of tetrahydrofurane, 1 ml of triethylamine and 1 ml of ethylmercaptan. The batch was rotated in a round-bottomed flask for 17 hours at room temperature. The resin was filtered off, washed with 100 ml of ethanol and 100 ml of ethanol/water (1:1) and finally eluted in a column with 300 ml of ethanol. The product was filtered off and dried in vacuo.

Lassaigne test strongly positive.

Elementary analysis: 6.51% S. 8.74% F.

1g of moist "Sepharose" 4 B activated with TFP (tetrafluoropyrimidine) according to Example 19, was suspended in 20 ml of a 0.05 M phosphate buffer of pH 7.0 and a solution of 0.5 ml (110 U) of penicillinase was added. The suspension was shaken at room temperature for 18 hours and then filtered and the product was washed with the above phosphate buffer, with and without addition of 0.5 M sodium chloride. After filtering under suction, 1.47g of moist enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash solutions was 15 U and of the enzyme-resin was 79 U (54 U/g of moist weight), which is 72% of the enzyme activity employed or 85% of the activity of the bonded enzyme.

Agarose in bead form ("Sepharose" 4 B from Pharmacia) was prepared analogously to Example 1 and treated with 3 M sodium hydroxide solution. The alkaline "Sepharose", which had been subjected to suction until the original volume of 24 ml was reached, was introduced in portions in the course of 12 minutes at room temperature into a mixture of 4.90g of tetrachloropyrimidine (TCP) in 40 ml of xylene/dioxane (1:1, weight/weight). During the addition, the temperature rose up to 32.degree. C. The flask was cooled by a stream of air. The batch was stirred for a further 15 minutes. The reaction was stopped by adding 4.2 ml of concentrated acetic acid. The activated "Sepharose" was filtered off and washed with 4 times 50 ml of the dioxane/xylene mixture, with 4 times 50 ml of dioxane and with 1 liter of water and was stored in the moist form. A sample was washed with acetone and dried in vacuo. It gave the following analysis: 5.71% Cl. 2.23% N.

10 ml of an aqueous solution of 0.35 M hexamethylenediamine were added to 1.3g of moist "Sepharose" activated with TCP and prepared according to Example 20, in a round-bottomed flask and the mixture was stirred for 60 hours at room temperature. The product was filtered off and washed in a column with with 250 ml of water, 100 ml of 1 M sodium hydroxide solution and 250 ml of water. The substituted "Sepharose" was filtered off, washed with methanol and dried in vacuo.

Analysis: 4.67% Cl. 3.27% N.

Ninhydrin test positive.

1.3g of moist "Sepharose" activated with TCP and prepared according to Example 20 were washed with tetrahydrofurane, filtered off and introduced into 3 ml of tetrahydrofurane, 0.5 ml of triethylamine and 0.5 ml of ethylmercaptan. The batch was stirred in a round-bottomed flask for 60 hours at room temperature. The resin was filtered off, washed in a column with ethanol, filtered off and dried in vacuo.

Lassaigne test positive.

Analysis: 4.82% Cl. 1.04% S.

1g of moist "Sepharose" 4 B activated with TCP (tetrachloropyrimidine) and prepared according to Example 20 was suspended in 20 ml of a 0.05 M phosphate buffer of pH 7.0 and a solution of 1 ml (110 U) of penicillinase was added. The suspension was stirred at room temperature for 18 hours and further worked up as described in Example 19c. 1.36g of moist enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash water was 9 U and of the enzyme-resin was 84 U (61 U/g of moist weight) which is 76% of the enzyme activity employed or 83% of the activity of the bonded enzyme.

Crosslinked dextran in bead form ("Sephadex" G 50 from Pharmacia) was activated with FCP as described in Example 1 for "Sepharose" and worked up. Elementary analysis gave a content of 0.38% of N, 0.20% of F and 0.50% of Cl.

2g of moist "Sephadex" activated with FCP and prepared according to Example 24 were reacted with 200 mg of hexamethylenediamine, and worked up, analogously to Example 2.

Elementary analysis: N 0.71%. F 0.10%. Cl 0.59%.

2g of moist "Sephadex" activated with FCP and prepared according to Example 24 were reacted with a solution of 7 ml of ethanol and 1 ml ethylmercaptan, and worked up, analogously to Example 5. Elementary analysis gave a sulphur content of 0.29.

0.20g of dried "Sephadex" G 50 activated with FCP and prepared according to Example 24 was swollen with 2 ml of water for 1 hour at 4.degree. C. The swollen "Sephadex" was suspended in 30 ml of a 0.05 M phosphate buffer of pH 7.0 and 1 ml of a solution of penicillinase with an activity of 220 U was added. The suspension was stirred at room temperature for 20 hours. After the resin had been filtered off, it was washed with the above phosphate buffer, with and without the addition of 0.5 M sodium chloride. 1.57g of (moist) enzyme resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash water was 0.1 U and of the enzyme-resin was 79 U (62 U/g of moist weight), which is 44% of the activity employed.

50 ml of 3 M sodium hydroxide solution were added to 4g of cellulose (Whatman CF 11) in a round-bottomed flask and the mixture was stirred for 18 hours at room temperature. The cellulose was filtered off on a G 3 glass frit. The total amount was slowly added to a mixture of xylene and dioxane (1:1, weight/weight) which contained 7.19g of FCP, is cooled to 0.degree. to +5.degree. C. and is stirred with a vibro mixer. The mixture is allowed to react for a total of 20 minutes and the reaction is then stopped by adding 5 ml of concentrated acetic acid. The activated cellulose was filtered off and washed with 4 times 50 ml of xylene/dioxane (1:1), 4 times 50 ml of dioxane and 500 ml of water and acetone. After drying in vacuo, the following elementary analysis was obtained:

N: 2.43%, F: 2.43%, Cl: 2.42%.

5 ml of 0.35 M hexamethylenediamine in water were added to 1g of moist cellulose activated with FCP and prepared according to Example 28. The round-bottomed flask was stirred at room temperature for 22 hours. The product was filtered off and washed with 250 ml of water, 100 ml of 1 N sodium hydroxide solution, 250 ml of water and 100 ml of acetone. The cellulose was dried in vacuo. Elementary analysis gave 3.99% of N, 0.36% of F and 2.51% of Cl.

0.5g of moist cellulose activated with FCP according to Example 28 was stirred with 1 ml of tetrahydrofurane, 0.5 ml of ethylmercaptan and 3 drops of triethylamine for 21 hours at room temperature. The product was filtered off, washed with 250 ml of ethanol, 50 ml of water and 50 ml of acetone and dried in vacuo.

Elementary analysis: 0.90% F. 2.35% S.

150g of moist cellulose (Whatman CF-11) activated with FCP and prepared according to Example 28 were suspended, at 4.degree. C., in a solution of 50 mg (54.5 U) of trypsin in 0.01 M benzamidine-HCl phosphate buffer, according to Sorensen, of pH 6.0 and the suspension was mixed thoroughly for 24 hours at 4.degree. C. in a rotating flask. After the coupling reaction, the cellulose was filtered off and washed with 50 ml of the above phosphate/benzamidine solution of pH 6. After filtering off again, the enzyme-cellulose was rotated in 5 ml of 1 M ethanolamine-HCl/0.01 M benzamidine-HCl of pH 6 for 36 hours. Filtering again and washing with 0.005 M benzamidine-HCl of pH 5.5. 1.90g of moist trypsin-cellulose were obtained. The enzymatic activity (BAPNA, 25.degree. C.) of the filtrate and wash solution was 26.4 U and of the trypsin-cellulose was 2.9 U (1.53 U/g of moist weight), which is 5.3% of the enzyme activity employed.

0.40g of dried cellulose activated with FCP and prepared according to Example 28 was left to stand with 200 ml of water for 1 hour at 4.degree. C. The swollen cellulose was suspended in 30 ml of a 0.05 M phosphate buffer of pH 7.0 and 1 ml of a solution of penicillinase with an activity of 220 U was added. The suspension was stirred for 20 hours at room temperature. After filtering off, the cellulose was washed with the above phosphate buffer, with and without the addition of 0.5 M sodium chloride. 0.76g moist weight of cellulose-bonded enzyme were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the cellulose bonded enzyme was 95 U (125 U/g of moist weight), which is 43% of the activity employed.

1g of polyacrylamide in bead form (Bio-Gel P-300, 100-200 mesh wet from Bio Rad) was swollen in water for 5.5 hours and filtered off and, in a round-bottomed flask, 80 ml of 1 N sodium hydroxide solution were added and the mixture was rotated for 15 minutes at room temperature. The resin was filtered off and added in portions to a solution of 4.72g of FCP in 40 ml of a mixture of xylene and dioxane (1:1, weight/weight). The suspension was stirred by a vibro mixer and cooled externally by a stream of air. The gel was introduced in the course of 10 minutes. During the addition, the temperature rose from 23.5.degree. to 29.degree. C. After a further 15 minutes the reaction was stopped by adding 3 ml of concentrated acetic acid. The resin was washed four times with 50 ml of the xylene/dioxane mixture and then with 250 ml of dioxane/water (1:1). A thick suspension of the resin in dioxane/water was poured into tetrahydrofurane, while stirring well, and the product was filtered off and washed with tetrahydrofurane. The product can be dried in vacuo.

3 ml of tetrahydrofurane, 1 ml of ethylmercaptan and 1 ml of triethylamine were added to 2.5g of the tetrahydrofuranemoist polyacrylamide activated with FCP according to Example 33 and the mixture was stirred at room temperature for 14 hours. The resin was filtered off, washed with ethanol and further extracted, in a column, with 250 ml of ethanol. The washed product was filtered and dried in vacuo. Lassaigne test positive.

Elementary analysis: 0.44% of sulphur.

100 mg of dry polyacrylamide activated with FCP according to Example 33 were suspended in 20 ml of a 0.05 M phosphate buffer of pH 7.0 and 0.5 ml of a solution of penicillinase (110 U) was added. The suspension was shaken overnight at room temperature. The enzyme resin was filtered off and washed with the above phosphate buffer, with and without the addition of 0.5 M sodium chloride. 2.59g of moist enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash solutions was 85 U and of the enzyme-resin was 22.4 U (8.6 U/g of moist weight), which is 20% of the enzyme activity employed or 90% of the bonded enzyme.

20g of a weakly basic, macroporous ion exchanger based on polystyrene and containing primary amino groups (NKZ-4), which have been washed with methanol and water, were suspended in 150 ml of a 0.05 M phosphate buffer of pH 6 and the pH was adjusted to 6 with a little 1 N hydrochloric acid. A solution of 2 ml of FCP in 20 ml of dioxane is allowed to run in dropwise in the course of 1 hour, while stirring, at room temperature. During the addition, the pH value was kept constant at pH 6 by adding 0.1 N sodium hydroxide solution. Subsequently, the resin was stirred for a further 30 minutes, then filtered off and washed with a solution of 0.1 M acetic acid, 0.5 M sodium chloride and water. Yield: 2.2g of resin. It is best to use the FCP-activated resin immediately thereafter for the coupling reaction. On storage in the moist state at 4.degree. C., the ability for enzyme coupling decreases by about 10% per day.

2g of moist polystyrene resin (NKZ 4-FCP) activated with FCP and prepared according to Example 36 were suspended in 40 ml of a 0.05 M phosphate buffer of pH 7.0, and a solution of 5 mg (440 U) of penicillinase was added. The reaction mixture was stirred at room temperature for 28 hours. The resin was filtered off and worked up as described in Example 35. 2.33g of enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the enzyme resin was 180 U (77 U/g of moist weight), which is 41% of the enzyme activity employed.

Aminomethylated polystyrene resin (NKZ-2) was dried for 2 days at 40.degree. C. and then for 2 days under a high vacuum at room temperature. 10g of dry resin were added, at 0.5.degree. C., to a solution of 10g of FCP in 50 ml of toluene. The resin was suspended using a vibro mixer and 5.5 ml of triethylamine were added dropwise. After a total of 1 hour, the reaction was stopped by adding 3 ml of concentrated acetic acid. The resin was filtered off, washed five times with 50 ml of toluene and five times with 50 ml of diethyl ether, filtered off and dried in vacuo. The dry resin is stored in a refrigerator.

3 ml of tetrahydrofurane, 1.5 ml of ethylmercaptan and 1.6 ml of triethylamine were added to 2g of dry, aminomethylated polystyrene resin (NKZ-2) activated with FCP according to Example 38 and the mixture was rotated for 28 hours at room temperature. The resin was filtered off and washed with ethanol and diethyl ether and dried in vacuo.

Elementary analysis: 0.44% of sulphur.

3g of dried polystyrene resin (NKZ-2-FCP) activated with FCP and prepared according to Example 38 were suspended in 25 ml of Sorensen phosphate buffer of pH 7.0 and a solution of 10 mg (880 U) of penicillinase was added. The reaction mixture was shaken at room temperature for 28 hours. The resin was filtered off, washed with the above buffer and, in order to remove the reactive halogen, shaken in 25 ml of a 1 N ethanolamine solution of pH 8.0 for a further 1 hour at room temperature. The resin was filtered off and washed in the customary manner with phosphate buffer, with and without the addition of 0.5 M sodium chloride. 6.4g of enzyme-resin were obtained. The enzymatic activity (benzylpenicillin, 25.degree. C.) of the filtrate and wash solutions was 13 U and of the enzyme-resin was 163 U (25.5 U/g of moist weight), which is 18.5% of the enzyme activity employed.

1g (4.8 mmols) of p-aminobenzamidine.2 HCl was dissolved in 12.5 ml of water and 9 ml of dioxane. The pH was adjusted to 7.0 in a receiver, cooled to 0.5.degree. C., on a pH-stat by adding 1 N sodium hydroxide solution. 0.81g (4.81 mmols) of FCP in 1 ml of dioxane was added dropwise to this solution and the pH value was kept constant by adding sodium hydroxide solution. After a total of 2 equivalents of sodium hydroxide solution (9.62 ml of 1 N NaOH) had been consumed, the mixture was poured into a saturated solution of sodium chloride. A precipitate formed and this was centrifuged off and further processed.

20g of moist agarose in bead form ("Sepharose" 4 B) were suspended in 30 ml of water and 0.75g of moist p-amino benzamidine activated with FCP according to Example 41 was added to the suspension. The pH of the stirred batch was adjusted to 10 at room temperature with the pH-stat by adding 0.1 N sodium hydroxide solution and the batch was kept at this pH value for 13 hours. The suspension was filled into a column and washed with 0.1 M tris-buffer of pH 8.

This resin was used for affinity chromatography of trypsin. Trypsin dissolved in this buffer is absorbed by the resin but cytochrome, for example, is not. The absorbed trypsin can be washed and eluted again in a very pure form using 0.1 M glycine/hydrochloric acid buffer of pH 2.

For elementary analysis, the resin was washed thoroughly with water and alcohol and dried in vacuo. The following values were found: 5.69% of N, 0.89% of F and 4.12% of Cl.

25g of moist agarose in bead form ("Sepharose" 4 B) were suspended in a solution of 0.1g of an azo dyestuff in 11 ml of water. The dyestuff has the following structure: ##STR14##

The suspension was stirred for 10 minutes at room temperature and a solution of 5g of sodium chloride in 15 ml of water was then added. The pH value was brought to 11.0 using the pH-stat by adding 1 M sodium hydroxide solution and the mixture was kept at this pH value for 24 hours. The "Sepharose" was filtered off and washed thoroughly with water and "Levapon" --TH solution. The deeply colored "Sepharose" was stored at 4.degree. C. in 0.05% sodium azide solution. The degree of substitution determined by spectrophotometry was 12%.

In order to test the stability of the staining, 2g portions of the moist resin were filled into small columns, washed with buffers of different pH values and stored under these buffers for 66 hours at room temperature. 3 ml eluates were then collected and measured by spectrophotometry. The following table shows the result:

Within the stability range for "Sepharose", the coupling proved to be completely stable. Gel chromatography of the eluates at pH 2.5 showed high-molecular colored agarose fragments in addition to the dyestuff.

1g of moist "Sepharose" stained according to Example 43 was suspended in 20 ml of water and solid sodium dithionite was added, while stirring, until the color had changed to a light yellowish brown. The reduced "Sepharose" was filtered off and washed with water.

For diazotization, the reduced "Sepharose" was suspended in 3 ml of 0.15 N hydrochloric acid and, after cooling the suspension to 0.degree. C., 5 drops of a 1 M sodium nitrite solution were added. The suspension was stirred for 30 minutes and then filtered and the product was washed with cold water.

A sample of this "diazo-Sepharose" was subjected to a coupling reaction with .beta.-naphthol and gave a deep red product.

The bulk of the "diazo-Sepharose" was suspended in 20 ml of a 0.05 M phosphate buffer of pH 7 and 0.5 ml of a solution of penicillinase (110 U) was added. The suspension was stirred at room temperature for 18 hours. The resin was filtered off, washed with the above phosphate buffer, with and without 0.5 M sodium chloride, and filtered off. 0.82g of enzyme-resin was obtained.

Enzymatic activity (benzylpenicillin, 25.degree. C.)

Filtrate and wash solutions 12 U

Enzyme-resin 97 U (118 U/g of moist weight)

which is 88% of the enzyme activity employed or 99% of the activity of the bonded enzyme.

As can be seen from the above description and Examples, the present invention provides a carrier bound ligand of the formula:

wherein T represents the residue of a polymeric carrier;

X is independently a divalent oxygen or sulfur atom, --NH--, --NHR.sup.5 --, --CONH-- or --CONR.sup.5 --, wherein R.sup.5 is lower alkyl;

L is the residue of a ligand; and

P is ##STR15## wherein each R.sup.6 is hydrogen, hydroxyl, lower alkyl, lower alkoxy, loweralkylthio, loweracylamino, nitro, cyano, carboxamide, loweralkylsulphonyl, loweralkoxycarbonyl, phenyl, trifluoromethyl, chloromethyl or T--X--.