2-Acrylamido-2-Methylpropane Sulfonic Acid Vinyl Aminimide/Copolymer

The monomer 2-acrylamido-2-methylpropane sulfonic acid is known to the art and is commercially available.

A class of monomers characterized as vinyl aminimides are also known to the art. Such aminimide monomers are disclosed, for example, in U.S. Pat. Nos. 3,527,892 and 3,641,145. Reference should also be made to copending application Ser. No. 753,521, filed Dec. 22, 1976 in the names of Avinash C. Mehta, Donald O. Rickter and Lloyd D. Taylor, commonly assigned which discloses monomers of the formula: ##STR1## wherein R is hydrogen or a lower alkyl.

The aminimide group may be represented by the formula: ##STR2##

A novel class of copolymers of 2-acylamido-2-methylpropane sulfonic acid and a vinyl aminimide has now been found.

The novel compositions of the present invention comprise copolymers of 2-acrylamido-2-methylpropane sulfonic acid and vinyl aminimides and possess surfactant and suspending properties and relatively high electrical conductivity. The property of conductivity makes the novel copolymers of the present invention particularly suitable for use in the products and processes disclosed and claimed in copending application Ser. No. 672,647, filed Apr. 1, 1976 in the names of Arthur M. Gerber and Vivian Walworth, now U.S. Pat. No. 4,060,419, issued Nov. 29, 1977, and commonly assigned.

The novel copolymers of the present invention are prepared by conventional vinyl polymerization techniques such as free radical polymerization techniques. Although the monomers may be combined in substantially any ratio, if relatively high conductivity is desired it is preferred to employ at least 50% by weight of 2-acrylamido-2-methylpropane sulfonic acid. In a particularly preferred embodiment, at least 80% by weight is employed.

The following non-limiting examples illustrate the preparation of the novel copolymers of the present invention.

The following materials were placed in a glass vessel:

The mixture was heated under a blanket of nitrogen at 65.degree. C. for 30 hours. An aqueous viscous solution of the copolymer was obtained.

The following materials were placed in a glass vessel:

The mixture was heated under a blanket of nitrogen for 3 days at 65.degree. C. An aqueous solution of the copolymer was obtained having a viscosity of about 5000 cps (Brookfield No. 4 spindle, 60 rpm at 25.degree. C.).

The novel copolymers of the present invention possess unusual salt stability while retaining their viscosity. This property makes the copolymers particularly suitable for use in the procedures set forth in the above-mentioned application Ser. No. 672,647.