US 4,129,470 AGrant

Method of Preparing a Porous Implantable Material From Polytetrafluoroethylene and Carbon Fibers

Issue Date:1978-12-12

•10 Claims

Abstract

A composition of material suitable for in vivo implantation to provide an environment in which normal tissue growth is fostered which composition is a porous fibrous structure in which the critical surface tension of the fibers is 35 dynes per centimeter or higher. This composition in the preferred form is a porous structure of carbon or graphite fibers bonded together by sintered polytetrafluoroethylene in a manner to expose a maximum amount of fiber surface. Another composition of material suitable for implantation for wear surfaces includes carbon fibers and polytetrafluoroethylene resin and is processed to align the carbon fibers with the wear surfaces. The method of preparing both material includes the step of mixing, filtering, compressing, rolling, sintering and drying. The method of stabilizing appliances or implants includes bonding the ingrowth material to the appliance or implant. Also the combination of the ingrowth material with appliances, tendon replacement elements and wear material are included.

Metadata

Inventor

Charles A. Homsy

Application Information

Application Number:US 6940560

Filing Date:1976-06-07

Priority Date:1971-05-20

Art Unit:147

Classifications

IPC:

B29D 2700B32B 3100

Field of Search:

26415626049;45.3;DIG. 17;DIG. 19155;309;3332.5 M

Patent Drawings

This patent does not have any drawings.

Claims

What is claimed is:

1. A method of preparing an implantable composition of material which comprises mixing together in an organic liquid media, carbon fibers, polytetrafluoroethylene fibers, polytetrafluoroethylene resin, and from 60 to 80 percent of a material soluble in solvents other than the media used to form a uniform slurry, filtering the slurry to form a filter cake having a reduced amount of organic liquid media, compressing the filter cake at elevated temperatures at a pressure of up to about 3,000 pounds per square inch (lbs/in.sup.2), rolling the compressed filter cake between rolls heated between about 100.degree. up to about 280.degree. F., drying the rolled cake at a temperature of up to about 350.degree. F., sintering the dry cake at temperatures between 600.degree. and 680.degree. F., at a pressure of up to about 5,000 lbs/in.sup.2, for a period in excess of three minutes; leaching said sintered cake to remove said soluble material and subsequently drying same, to produce a material having spheroidal and dendritic spaces therein and which is bio-compatible.

2. The method according to claim 1 wherein the drying step is carried out at temperatures between 150.degree. and 350.degree. F. for several hours prior to sintering said dry cake.

3. The method according to claim 1 wherein said compressing step is carried out at a temperature between 100.degree. and 250.degree. F. and at a pressure between 100 to 3,000 pounds per square inch.

4. The method according to claim 1 wherein said soluble material is sodium chloride and said leaching is done with distilled water as the solvent for said sodium chloride.

5. The method according to claim 1 wherein the implantable composition is bonded on at least one side thereof to a bonding material including the steps of leaching from the surface of the sintered cake, that is to be bonded, the soluble material, drying the leached material, and bonding a bonding material to the surface of the material from which the soluble material has been leached.

6. The method according to claim 5 including the step of bonding said composition to a metal prosthesis.

7. The method according to claim 5 including the step of bonding a wear material to the surface to which said bonding material is bonded.

8. The method according to claim 5 including the steps of forming said composition to fit the surface of a metal prosthesis, and bonding said composition to the surface of said prosthesis.

9. The method according to claim 7 including the step of forming the composition including said wear material into a desired shape in a mold by subjecting it to both heat and pressure.

10. The method according to claim 1, including the step of stacking a plurality of dry rolled cake before said sintering step to provide material of the desired thickness.

Patent Citations (5)

Patent	Date	Inventor
US3890417	1975-06-01	Vallance
US3930886	1976-01-01	Mesiti et al.
US3930979	1976-01-01	Vallance
US3980613	1976-09-01	Bachot et al.
US4003818	1976-01-01	Juillard et al.

Abstract

Claims