US 4,117,033 AGrant
Polyoxymethylene/Copolyether-Ester Blends
Issue Date:1978-09-26
•19 Claims
Abstract
An oxymethylene polymer of improved melt processability is provided by the addition of about 0.1-5 percent by weight of a low molecular weight copolyether-ester resin. The copolyether-ester consists essentially of long-chain ester units derived from long-chain glycols and dicarboxylic acids and short-chain ester units derived from low molecular weight diols and dicarboxylic acids.
Metadata
Assignee
- E. I. Du Pont de Nemours and Company
Inventor
- David Mark Gale
Application Information
Application Number:US 7492200
Filing Date:1976-12-10
Priority Date:1976-12-10
Art Unit:143
Classifications
IPC:
C08L 5902
Field of Search:
260860;40 R;75 R
Patent Drawings
This patent does not have any drawings.
Description
Background of the Invention
1. Field of the Invention
This invention relates to thermoplastic molding compositions based on polyoxymethylene blends and more particularly to blends of polyoxymethylene polymers with small amounts of selected low molecular weight copolyether-ester resins to give polyoxymethylene polymer blends with improved molding properties.
2. Relation to the Prior Art
Thermoplastic molding resins based on polyoxymethylene blends are well-known in the art. For example, U.S. Pat. No. 3,795,715, describes mixtures of oxymethylene polymers with polyesters made from linear aliphatic dicarboxylic acids and .alpha., .omega.-diols; the addition of the polyester to the polyoxymethylene improves its toughness. Similarly, it is known that the properties of polyester molding compositions, based on linear saturated polyesters of aromatic dicarboxylic acids, can be improved by the addition of 0.1-25% of a polyacetal (U.S. Pat. No. 3,595,937). Polyoxymethylene polymers which contain up to 15% of a polyalkylene terephthalate have a more uniform spherulite size and improved color stability (U.S. Pat. No. 3,696,171), and polyoxymethylene/aliphatic polyester block polymers are known (U.S. Pat. No. 3,580,973). Oxymethylene polymer compositions with improved impact resistance are prepared by incorporating a rubbery polymeric material which contains pendant nitrile or carboxylic ester group (U.S. Pat. No. 3,476,832; Canadian Patent No. 829,368. Incorporation of up to 10% of selected polymeric materials with T.sub.g < 30.degree. C, including polyethylene oxide and polytetrahydrofuran, gives polyoxymethylene molding compositions of improved strength Canadian Patent No. 844,683; U.S. Pat. No. 3,795,715). Such polymers would be expected to exhibit improved molding properties, but polymer blending is difficult because of the low melting points and hygroscopic nature of the polyethers.
More recently, published German Patent No. 2,449,343, describes molding resins with improved impact resistance which are blends of an oxymethylene polymer with 0.1-50 weight % of a high molecular weight copolyester consisting of 75-35% of long chain ester units which contain ether linkages and 25-65% of short chain ester units. A plot of the reduced specific viscosity (RSV), measured as described in German Patent No. 2,449,343 vs. the inherent viscosity in m-cresol shows that polymers disclosed in the reference have inherent viscosities above 0.95, namely 1.0 and 1.7.
Summary of the Invention
According to the present invention there is provided a thermoplastic molding composition comprising a mixture of:
(A) about 99.9-95 percent by weight of an oxymethylene polymer consisting essentially of about 95-100 percent by weight of oxymethylene units and 0 to about 5 percent by weight of oxyalkylene units of 2-8 adjacent carbon atoms in the main chain, said polymer having a number average molecular weight of about 1000-500,000; and
(B) about 0.1-5 percent by weight of a copolyether-ester having an inherent viscosity of about 0.05-0.95, as measured in m-cresol in 0.1 g/dl concentration at 30.degree. C, said copolyether-ester consisting essentially of a multiplicity of recurring intralinear long-chain and short-chain ester units connected head-to-tail through ester linkages, said long-chain ester units having the formula: ##STR1## wherein G is a divalent radical remaining after removal of terminal hydroxyl groups from a poly(alkylene oxide) glycol having a carbon-to-oxygen mole ratio of about 2-4.3 and a molecular weight of about 400-6000; and
R is a divalent radical remaining after removal of carboxyl groups from a dicarboxylic acid having a molecular weight less than about 300;
and said short-chain ester units having the formula: ##STR2## wherein D is a divalent radical remaining after removal of hydroxyl groups from a low molecular weight diol having a molecular weight less than about 250; and
R is as defined above;
with the proviso that the short-chain ester units constitute about 15-75 percent by weight and the long-chain ester units constitute 85-25 percent by weight of the copolyether-ester.
Detailed Description of the Invention
Addition of about 0.1-5% by weight, preferably about 0.5-2%, of a low molecular weight copolyether-ester resin to an oxymethylene polymer gives a resin blend which exhibits improved melt processability compared with the oxymethylene polymer itself while essentially retaining the physical properties of the oxymethylene polymer. The improvement in molding cycle time correlates, in general, with the degree of increase of non-Newtonian melt flow. A measure of non-Newtonian flow is the Apparent Viscosity Ratio (AVR), the ratio of viscosities at low to moderately high shear stresses, e.g., the ratio at shears of 2 .times. 10.sup.5 to 2 .times. 10.sup.6 dynes/cm.sup.2. The larger the AVR of a polymer blend compared with an oxymethylene polymer itself, the greater is the flow during the molding cycle and the higher the production rate.
The polyoxymethylene component (A) of the polymer blend is a polymer having chains of recurring oxymethylene units (--CH.sub.2 O--) or chains containing a predominance of the aforementioned units with the chain normally terminated at each end by a hydroxyl group, an alkyl group, hydroxyalkyl, or an ester group. Polyoxymethylenes having alkyl or hydroxyalkyl groups (ether linkages) on the ends of the polymer chain are base stable. It is preferred to employ stabilized end-capped polymers which contain acetate end groups.
In general, the oxymethylene polymer consists essentially of about 95-100 percent by weight of oxymethylene units and 0 to about 5 percent by weight of oxyalkylene units of 2-8 adjacent carbon atoms in the main chain, preferably 2 adjacent carbon atoms. The polymers have a number average molecular weight of about 1,000-500,000, preferably having an inherent viscosity of about 0.5-2.8 measured in hexafluoroisopropyl alcohol (HFIP) in 0.5 percent by weight concentration at 30.degree. C, which corresponds to a number average molecular weight of about 5,000-100,000.
Homopolymers of formaldehyde or trioxane, or trioxane copolymers which preferably contain a linear structure are used as the oxymethylene component of the molding resin. Trioxane copolymers include copolymers of trioxane/cyclic ethers, cyclic acetals and/or linear polyacetals, which contain terminal primary alcohol groups. Suitable comonomers for trioxane are further described in U.S. Pat. No. 3,795,715. A preferred comonomer for copolymerization with trioxane is 1,3-dioxolane. Especially preferred as the polyoxymethylene component are homopolymers of formaldehyde.
The homopolymers of formaldehyde or trioxane used according to the invention may be produced by known methods by catalytic polymerization of the monomers, as described, for example, in U.S. Pat. Nos. 2,768,994; 2,982,758; and 2,989,505. Other patents which describe these polymers and processes for their production include U.S. Pat. Nos. 2,734,889; 2,768,994; 2,828,286; 2,844,561; 2,848,437; 2,841,570; and 2,994,687.
The copolymers used according to the invention are produced by known methods by copolymerization of the monomers, as described, for example, in U.S. Pat. Nos. 3,027,352 and 3,076,786.
Stabilization of oxymethylene homopolymers and copolymers is described in U.S. Pat. Nos. 3,183,211; 3,103,499 and 3,219,623.
The low molecular weight copolyether-ester resin has an inherent viscosity of about 0.05-0.95, preferably about 0.1-0.8 and most preferably about 0.1-0.5, measured in m-cresol in 0.1 g/dl concentration at 30.degree. C. The copolyether-ester consists essentially of a multiplicity of recurring intralinear long-chain and short-chain ester units connected head-to-tail through ester linkages, with the long-chain ester units having the formula: ##STR3## wherein G is a divalent radical remaining after removal of terminal hydroxyl groups from a poly(alkylene oxide) glycol having a carbon-to-oxygen mole ratio of about 2-4.3 and a molecular weight of about 400-6000 and
R is a divalent radical remaining after removal of carboxyl groups from a dicarboxylic acid having a molecular weight less than about 300, preferably ##STR4##
The term "long-chain ester units" as applied to units in the copolyether-ester polymer component B of the polymer blend refers to the reaction product of a long-chain glycol with a dicarboxylic acid. Such "long-chain ester units", which are a repeating unit in the copolyether-ester used in this invention, correspond to formula (a) above. The long-chain glycols are polymeric glycols having terminal (or as nearly terminal as possible) hydroxyl groups and a molecular weight from about 400-6000. The long-chain glycols used to prepare the copolyether-esters of this invention are poly(alkylene oxide) glycols having a carbon-to-oxygen ratio of about 2.0-4.3 and preferably having the alkylene moiety of 2-8 carbon atoms.
Representative long-chain glycols are described in U.S. Pat. No. 3,907,926, and include poly(ethylene oxide) glycol, poly(1,2- and 1,3-propylene oxide) glycol, poly(tetramethylene oxide) glycol, random or block copolymers of ethylene oxide and 1,2-propylene oxide, and random or block copolymers of tetrahydrofuran with minor amounts of a second monomer such as 3-methyltetrahydrofuran (used in proportions such that the carbon-to-oxygen mole ratio in the glycol does not exceed about 4.3).
The short-chain ester units in the low molecular weight copolyether-ester have the formula: ##STR5## wherein D is a divalent radical remaining after removal of hydroxyl groups from a low molecular weight diol having a molecular weight less than about 250, and
R is as defined above for (a).
The term "short-chain ester units" as applied to units in the polymer chain refers to low molecular weight compounds or polymer chain units having molecular weights less than about 550. They are made by reacting a low molecular weight diol (below about 250) with a dicarboxylic acid to form ester units represented by formula (b) above.
Included among the low molecular weight diols which react to form short-chain ester units are aliphatic, cycloaliphatic, and aromatic dihydroxy compounds. Preferred are diols with 2-15 carbon atoms such as ethylene, propylene, tetramethylene, pentamethylene, 2,2-dimethyltrimethylene, hexamethylene, and decamethylene glycols, dihydroxycyclohexane, cyclohexanedimethanol, resorcinol, hydroquinone, 1,5-dihydroxynaphthalene, etc. More preferred are aliphatic diols containing 2-8 carbon atoms, especially --CH.sub.2 --.sub.n where n is 2-4. Included among the bis-phenols which can be used are bis(p-hydroxy)diphenyl, bis(p-hydroxyphenyl)methane, and bis(p-hydroxyphenyl) propane. Equivalent ester-forming derivatives of diols are also useful (e.g., ethylene oxide or ethylene carbonate can be used in place of ethylene glycol). The term "low molecular weight diols" as used herein should be construed to include such equivalent ester-forming derivatives, provided, however, that the molecular weight requirement pertains to the diol only and not to its derivatives.
Dicarboxylic acids which are reacted with the foregoing long-chain glycols and low molecular weight diols to produce the copolyesters of this invention are also disclosed in U.S. Pat. No. 3,907,926, and include aliphatic, cycloaliphatic, or aromatic dicarboxylic acids of a low molecular weight, i.e., having a molecular weight of less than about 300. The term "dicarboxylic acids" as used herein, includes equivalents of dicarboxylic acids having two functional carboxyl groups which perform substantially like dicarboxylic acids in reaction with glycols and diols in forming copolyester polymers. These equivalents include esters and ester-forming derivatives, such as acid halides and anhydrides. The molecular weight requirement pertains to the acid and not to its equivalent ester or ester-forming derivative. Thus, an ester of a dicarboxylic acid having a molecular weight greater than 300 or an acid equivalent of a dicarboxylic acid having a molecular weight greater than 300 are included provided the acid has a molecular weight below about 300. The dicarboxylic acids can contain any substituent groups or combinations which do not substantially interfere with the copolyester polymer formation and use of the polymer blends of this invention.
Aliphatic dicarboxylic acids, as the term is used herein, refers to carboxylic acids having two carboxyl groups, each attached to a saturated carbon atom. If the carbon atom to which the carboxyl group is attached is saturated and is in a ring, the acid is cycloaliphatic. Aliphatic or cycloaliphatic acids having conjugated unsaturation often cannot be used because of homopolymerization. However, some unsaturated acids, such as maleic acid, can be used.
Aromatic dicarboxylic acids, as the term is used herein, are dicarboxylic acids having two carboxyl groups attached to a carbon atom in an isolated or fused benzene ring. It is not necessary that both functional carboxyl groups be attached to the same aromatic ring and where more than one ring is present, they can be joined by aliphatic or aromatic divalent radicals or divalent radicals such as --O-- or --SO.sub.2 --.
Representative aliphatic and cycloaliphatic acids which can be used for this invention are sebacic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, adipic acid, glutaric acid, succinic acid, carbonic acid, oxalic acid, azelaic acid, diethylmalonic acid, allylmalonic acid, 4-cyclohexene-1,2-dicarboxylic acid, 2-ethylsuberic acid, 2,2,3,3-tetramethylsuccinic acid, cyclopentanedicarboxylic acid, decahydro-1,5-naphthalenedicarboxylic acid, 4,4'-bicyclohexyldicarboxylic acid, decahydro-2,6-naphthalenedicarboxylic acid, 4,4'-methylenebis(cyclohexanecarboxylic acid), 3,4-furandicarboxylic acid, and 1,1-cyclobutanedicarboxylic acid. Preferred aliphatic acids are cyclohexanedicarboxylic acids and adipic acid.
Representative aromatic dicarboxylic acids which can be used include terephthalic, phthalic and isophthalic acids, bi-benzoic acid, substituted dicarboxy compounds with two benzene nuclei such as bis(p-carboxyphenyl)methane, p-oxy(p-carboxyphenyl)benzoic acid, ethylene-bis(p-oxybenzoic acid), 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, phenanthrenedicarboxylic acid, anthracenedicarboxylic acid, 4,4'-sulfonyldibenzoic acid, and C.sub.1 -C.sub.12 alkyl and ring substitution derivatives thereof, such as halo, alkoxy and aryl derivatives. Hydroxyl acids such as p(.beta.-hydroxyethoxy)benzoic acid can also be used providing an aromatic dicarboxylic acid is also present.
Aromatic dicarboxylic acids are an especially preferred class for preparing the copolyether-ester polymers of this invention. Among the aromatic acids, those with 8-16 carbon atoms are preferred, particularly the phenylenedicarboxylic acids, i.e., phthalic, terephthalic and isophthalic acids and their dimethyl derivatives.
It is preferred that at least about 50% of the short segments are identical, and that the identical segments form a homopolymer in the fiber-forming molecular weight range (molecular weight > 5000) having a melting point of at least 150.degree. C and preferably greater than 200.degree. C. Polymer melting points are conveniently determined by differential scanning calorimetry.
The short-chain ester units will constitute about 15-75 weight percent of the copolyether-ester. The remainder of the copolyether-ester will be the long segments, ergo the long segment will comprise about 25-85 weight percent of the copolyether-ester. Copolyether-esters in which the short-chain units comprise 20-60 weight percent with 40-80 weight percent long-chain units are preferred.
With regard to the manufacture of the copolyether-esters, they may be made by a conventional ester interchange reaction followed by conversion of the low molecular weight prepolymer to a higher molecular weight copolyether-ester by a "polycondensation" process at reduced pressure. The manufacturing process is described in detail in U.S. Pat. No. 3,907,926, Columns 4-6, and this patent is hereby incorporated by reference. Preparative procedures (A-D) employed for preparation of the copolyether-ester resins employed in the specific embodiments are described below.
Preferred copolyethers-esters which are blended by the process of this invention are those prepared from dimethyl terephthalate, 1,4-butanediol and poly(tetramethylene oxide)glycol having a molecular weight of about 600-2000, poly(ethylene oxide) glycol having a molecular weight of about 600-1500, or poly(propylene oxide) glycol having a molecular weight of about 1,000-2,500. Optionally, a portion, preferably up to about 30 mole percent, of the dimethyl terephthalate in these polymers can be replaced by dimethyl phthalate or dimethyl isophthalate. The polymers based on poly(tetramethylene oxide) glycol are especially preferred because they are easily prepared, have overall superior physical properties, and are especially resistant to water. Most preferred are copolyether-esters containing 45-55% by weight of short-chain ester units derived from terephthalate and 1,4-butanediol.
The most preferred copolyether-ester compositions also contain 0.5 to 5 weight percent of an antioxidant, preferably 4,4'-bis(.alpha.,.alpha.-dimethylbenzyl)diphenylamine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hexahydro-s-triazine or 1,6-bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionamido]hexane. Optionally they also may contain a stabilizer, e.g., 0.5 to 3.0 weight percent of amide linkages, preferably provided by a copolymer of polycaprolactam and polyhexamethylene adipamide, or terpolymer of polycarprolactam, polyhexamethylene adipamide, and polyhexamethylene sebacamide.
The antioxidant and the amide may be added at any time during the preparation of the copolyether-ester or following its preparation. Preferably an antioxidant should be present during the polycondensation aspect of the reaction in an amount of at least about 0.2 percent by weight based on the estimated yield of copolyether-ester product, preferably in an amount of 0.5 to 2.0 percent by weight. It is preferred that a suitable antioxidant be present at any point in the process where the poly(alkylene oxide) glycol is exposed to elevated temperatures, e.g., above about 100.degree. C. The antioxidant, depending on its melting point, may be added as a solid, a molten liquid, or as a solution or dispersion in one or more of the reactants. In batch operations, it is conveniently added as a solid or as a solution or dispersion in the diol or the poly(alkylene oxide)glycol at the time of charging the reactor. In continuous operation, the antioxidant is most conveniently added as a solution or dispersion in the diol and/or glycol entering the process. The antioxidant may, of course, be introduced at later stages in the process and even after preparation of the copolyether-ester is complete. It is usually convenient to add the total amount of antioxidant desired in the finished copolyether-ester during its preparation; however, additional amounts of antioxidant can be added to the finished copolyether-ester by melt blending.
The resulting copolyether-ester may be blended by any of several techniques with the oxymethylene polymer. For best results in preparing the blends of this invention, the components must be thoroughly and uniformly blended, otherwise localized areas will differ in properties. The blend is produced by mixing the components and subsequently homogenizing. The mixing usually takes place at ambient temperatures, i.e., 20.degree.-35.degree. C, and the homogenizing takes place in any easily heated mixing apparatus, e.g., rollers, calenders, kneaders or extruders, at a temperature above the crystalline melting point of the oxymethylene polymer, i.e., at a temperature of 150.degree.-260.degree. C, preferably 170.degree.-230.degree. C. Necessarily, depending on the amount of short-chain segments present in the copolyether-ester, there will be a good deal of variation in the broad range; operating most efficiently within such temperature range will present no difficulty for one skilled in the art.
The pressure utilized during blending may vary broadly, but in most instances ambient pressure is satisfactory. On occasion, higher pressures may be inherent due to the nature of the equipment in which blending is performed.
Solution blending may also be employed by use of a solvent common to the polymeric ingredients, e.g., chlorinated aromatics such as o-dichlorobenzene. Polymer recovery is achieved by solvent evaporation or by precipitation with a non-solvent.
The mixing or blending of the oxymethylene polymer and the copolyether-ester is preferably accomplished by means of extrusion blending. Suitable devices for the blending include single screw extruders, twin screw extruders, internal mixers such as the Banbury Mixer, heated rubber mills (electric or oil heat) or a Farrell continuous mixer. Injection molding equipment can be used to accomplish blending just prior to molding, but care must be taken to provide sufficient time and agitation to insure uniform blending prior to molding.
Provided that the final compositions are within the stated limits, one, or more than one, oxymethylene polymer may be blended with one, or more than one, copolyether-ester resin.
The molding resin blends may also contain additives, especially stabilizers and/or fillers as well as nucleating agents, antistatic agents, flame retardants, lubricants, plasticizers, pigments, dyes, optical brightening agents or mold-release agents, known in the art.
Antioxidants and stabilizers especially suited for the copolyether-ester component of the blend are described above. Conventional stabilizers for oxymethylene polymers, e.g., nylon oligomers, copolymers and terpolymers; and phenolic and aromatic amine-containing antioxidants may also be employed. The amounts of stabilizers employed are preferably less than 2 weight percent of each ingredient resin.
Suitable fillers include, for example, asbestos fibers, glass fibers, glass powder, graphite, carbon black, graphite metal powder, boron fibers, metal oxides, silicates, silica, carbonate, clay, alumina, etc. Polymeric additives which may be added include those that are melt-blended, e.g., ethylene/methacrylic acid copolymers, neutralized or unneutralized; ethylene/acrylic acid copolymers, neutralized or unneutralized; non-meltable polymeric fibrous additives such as aramid fibers, etc. The total amount of fillers and other additives is preferably less than 70 weight percent of the molding resin composition.
In computing the useful compositions of the molding resins, the oxymethylene polymers and copolyether-ester resins are considered to be free of fillers and other additives except for the oxidation and thermal stabilizers normally included in commercially available samples of the components.
The molding resin blends can be broken up mechanically, e.g., by chopping or grinding, to form a granulate, shavings, flakes or powder. Since they are thermoplastic, they can be worked by injection molding, extrusion, melt spinning or deep-drawing. They are also suitable as a commercial raw material for the production of semi-finished materials and finished products such as molded articles, e.g., strips, rods, plates, films, pipes, and hoses, as well as machine parts, e.g., housings, gear wheels, bearing components and control elements. These and other utilities are well known applications of conventional polyoxymethylene resins.
Embodiments of the Invention
The following are illustrative examples of the invention in which all parts and percentages are by weight and all degrees are Celsius unless otherwise stated.
The following ASTM methods were employed in determining the properties of the polymer compositions prepared in the examples which follow:
AVR was obtained by calculation of the ratio of the apparent viscosity (poise) at 2 .times. 10.sup.5 dynes/cm.sup.2 to the apparent viscosity at 2 .times. 10.sup.6 dynes/cm.sup.2. A procedure for rheology determination described in ASTM Bulletin No. 232, pp. 63-67, September, 1958, was employed using a temperature of 200.degree. and a L/D ratio of 16.
Inherent viscosities of the copolyether-ester resins were measured at 30.degree. at a concentration of 0.1 g/dl in m-cresol.
The following catalyst was used in preparing copolyether-ester resins A-H and AA of the examples:
Catalyst
To 425 parts of anhydrous 1,4-butanediol was added 23.32 parts of tetrabutyl titanate. The mixture was agitated at 50.degree. for 2-3 hours until the small amounts of solids originally present disappeared.
Procedure A
Copolyether-ester resins A-G were prepared using the following charge in an agitated flask fitted for distillation:
A stainless steel stirrer with a paddle cut to conform with the internal radius of the flask was positioned about one-eight inch from the bottom of the flask and agitation was started. The flask was placed in an oil bath at 160.degree., agitated for 5 minutes, and then the catalyst was added. Methanol distilled from the reaction mixture as the temperature was slowly raised to 250.degree. over a period of 1 hour. When the temperature reached 250.degree., the pressure was gradually reduced to 0.3 mm within 20 minutes. The polymerization mass was agitated at 250.degree./0.3 mm for 1-35 minutes. The resulting viscous molten product was scraped from the flask in a nitrogen (water and oxygen free) atmosphere and allowed to cool. The inherent viscosity of the product at a concentration of 0.1 g/dl in m-cresol at 30.degree. was measured. The inherent viscosities of the resins were varied by varying the polycondensation times as described.
Procedure B
Copolyether-ester resin H was prepared by the same procedure as described for resins A-G using the following ingredients charge:
Procedure C
Copolyether-ester resin AA was prepared by the same procedure as described for resins A-G using the following ingredients charge:
Procedure D
Copolyether-ester resins O, P, U, V, W, X and Y were prepared using the appropriate amounts of starting materials by the following procedure:
The dimethyl terephthalate (211 parts), dimethyl isophthalate (60 parts), 4,4'-bis(.alpha.,.alpha.-dimethylbenzyl) diphenylamine (2.5 parts), and the appropriate long-chain glycol and low molecular weight diol were charged into a 500 ml resin kettle, and the reaction mixture was heated to 180.degree.. The catalysts, sodium formate (1.0 part) and tetrabutyl titanate (1.0 part), were charged, and the reaction mixture was heated to 260.degree. under nitrogen for 4 hours to remove methanol by distillation. When the temperature reached 260.degree., a vacuum was applied at a constant rate so that after 0.5 hour the pressure had been reduced to > 1 mm. Distillation was continued at 260.degree. for a time sufficient to obtain polymer of the desired molecular weight, i.e., for periods up to several hours. The resulting viscous mass was removed from the flask in a nitrogen atmosphere and allowed to cool.
The resulting copolyether-ester resins are shown in Table I.
Example 1
A 95/5 mixture of dry-blended pellets of acetate-capped polyoxymethylene polymer (MW 25,000-30,000) and copolyether-ester resin A was fed through a water-cooled hopper into a 28-mm twin screw extruder (Werner and Pfleiderer Corp.) to effect melt-blending of the mix. Typical extrusion conditions were as follows: screw speed, 150 revolutions/min; vacuum, 30 inches of Hg; hopper temperature, 105.degree.; barrel temperatures, 162.degree. (rear) to 187.degree. (front of center); die temperature, 181.degree.. The blended pellets were dried at 60.degree. under vacuum, and they were injection molded to provide samples suitable for physical testing.
Physical properties of this blend are tabulated in Table II. For comparison, the AVR ratios of unblended polyoxymethylene polymer, and a 95/5 polyoxymethylene polymer/high molecular weight copolyether-ester resin (B) are listed. The data show the increase in AVR ratio when a low molecular weight copolyether-ester resin is blended with a polyoxymethylene polymer.
Examples 2-18
Polymer blends (95/5) of the acetate-capped polyoxymethylene polymer of Example 1 and various copolyether-ester resins were prepared as described in Example 1, and physical properties of these blends are tabulated in Table III. The data show the increase in AVR ratio by addition of a low molecular weight copolyether-ester resin to the polyoxymethylene.
Examples 19-22
Polymer blends of the acetate-capped polyoxymethylene polymer of Example 1 and various copolyether-ester resins were prepared as described in Example 1 except that a single-screw extruder was employed. The physical properties of these blends are tabulated in Table IV. The data show the increase in AVR ratio by addition of a low molecular weight copolyether-ester resin to the polyoxymethylene.
Examples 23-30
95/5 polymer blends of the acetate-capped polyoxymethylene polymer of Example 1 and various copolyether-ester resins were prepared as described in Example 1. The physical properties of these blends are tabulated in Table V. The data show the increase in AVR ratio by addition of a low molecular weight copolyether-ester resin to the polyoxymethylene.
Examples 31-41
Polymer blends (95/5) of an acetate-capped polyoxymethylene polymer (MW .about. 60,000) and various copolyether-ester resins were prepared as described in Example 1, and physical properties of these blends are tabulated in Table VI. The data show the increase in AVR ratio obtained by addition of a low molecular weight copolyether-ester resin to the polyoxymethylene.
Examples 42-44
Polymer blends (95/5) of an oxymethylene copolymer (Celcon.RTM. M-25-01) and various copolyether-ester resins were prepared as described in Example 1, and physical properties of these blends are tabulated in Table VII. The data show the increase in AVR ratio obtained by addition of a low molecular weight copolyether-ester resin to the oxymethylene copolymer.
Claims
What is claimed is:
1. A thermoplastic molding composition comprising a mixture of: (A) about 99.9-95 percent by weight of an oxymethylene polymer consisting essentially of about 95-100 percent by weight of oxymethylene units and 0 to about 5 percent by weight of oxyalkylene units of 2-8 adjacent carbon atoms in the main chain, said polymer having a number average molecular weight of about 1,000-500,000; (B) about 0.1-5 percent by weight of a copolyether-ester having an inherent viscosity of about 0.05-0.8, as measured in m-cresol in 0.1 g/dl concentration at 30.degree. C, said copolyether-ester consisting essentially of a multiplicity of recurring intralinear long-chain and short-chain ester units connected head-to-tail through ester linkages, said long-chain ester units having the formula: ##STR6## wherein G is a divalent radical remaining after removal of terminal hydroxyl groups from a poly(alkylene oxide) glycol having a carbon-to-oxygen mole ratio of about 2-4.3 and a molecular weight of about 400-6000; and R is a divalent radical remaining after removal of carboxyl groups from a dicarboxylic acid having a molecular weight less than about 300; and said short-chain ester units having the formula: ##STR7## wherein D is a divalent radical remaining after removal of hydroxyl groups from a low molecular weight diol having a molecular weight less than about 250; and R is as defined above; with the proviso that the short-chain ester units constitute about 15-75 percent by weight and the long-chain ester units constitute about 85-25 percent by weight of the copolyether-ester.
2. The composition of claim 1 wherein (1) the alkylene in poly(alkylene oxide) glycol is from 2-8 carbon atoms; (2) the diol is an aliphatic, cycloaliphatic or aromatic diol of 2-15 carbon atoms and (3) the dicarboxylic acid is an aliphatic, cycloaliphatic or aromatic dicarboxylic acid or an ester, acid halide or anhydride thereof.
3. The composition of claim 2 wherein the copolyether-ester inherent viscosity is about 0.1-0.5.
4. The composition of claim 3 wherein the short-chain ester units constitute about 20-60 percent by weight and the long-chain ester units constitute about 80-40 percent by weight of the copolyether-ester.
5. The composition of claim 4 wherein the copolyether-ester comprises about 0.5-2 percent by weight of the mixture.
6. The composition of claim 5 wherein the glycol is selected from the group consisting of poly(tetramethylene oxide) glycol, poly(ethylene oxide) glycol and poly(propylene oxide) glycol; the diol is selected from the group consisting of ethylene glycol and 1,4-butanediol and the dicarboxylic acid is selected from the group consisting of phthalic acid, terephthalic acid and isophthalic acid and their dimethyl derivatives.
7. The composition of claim 1 wherein the oxymethylene polymer is a homopolymer of formaldehyde end terminated with hydroxyl, alkyl, hydroxyalkyl or ester groups.
8. The composition of claim 7 wherein the oxymethylene polymer has a number average molecular weight of about 5,000-100,000.
9. The composition of claim 8 wherein (1) the alkylene in poly(alkylene oxide) glycol is from 2-8 carbon atoms; (2) the diol is an aliphatic, cycloaliphatic or aromatic diol of 2-15 carbon atoms and (3) the dicarboxylic acid is an aliphatic, cycloaliphatic or aromatic dicarboxylic acid or an ester, acid halide or anhydride thereof.
10. The composition of claim 9 wherein the copolyether-ester inherent viscosity is about 0.1-0.5 and the short-chain ester units constitute about 20-60 percent by weight and the long-chain ester units constitute about 80-40 percent by weight of the copolyether-ester.
11. A thermoplastic molding composition comprising a mixture of: (A) about 99.9-95 percent by weight of an oxymethylene homopolymer of formaldehyde end-capped with acetate groups and having a number average molecular weight of about 5,000-100,000; and (B) about 0.1-5 percent by weight of a copolyether-ester having an inherent viscosity of about 0.1-0.8, as measured in m-cresol in 0.1 g/dl concentration at 30.degree. C, said copolyether-ester consisting essentially of a multiplicity of recurring intralinear long-chain and short-chain ester units connected head-to-tail through ester linkages, said long-chain ester units having the formula: ##STR8## wherein G is a divalent radical remaining after removal of terminal hydroxyl groups from a glycol selected from poly(tetramethylene oxide) glycol having a molecular weight of about 600-2000, poly(ethylene oxide) glycol having a molecular weight of about 600-1500 and poly(propylene oxide) glycol having a molecular weight of about 1000-2500; and said short-chain ester units having the formula: ##STR9## wherein n is 2-4, and with the proviso that the short-chain ester units constitute about 20-60 percent by weight and the long-chain ester units constitute about 80-40 percent by weight of the copolyether-ester.
12. The composition of claim 11 wherein ##STR10## is at least one of terephthalate and isophthalate.
13. The composition of claim 12 wherein the glycol is poly(tetramethylene oxide) glycol and n is 4.
14. The composition of claim 13 wherein the short-chain ester units constitute about 45-55 percent by weight and the long-chain ester units constitute about 55-45 percent by weight of the copolyether-ester.
15. The composition of claim 14 wherein the copolyether-ester comprises about 0.5-2 percent by weight of the mixture and has an inherent viscosity of about 0.1-0.5.
16. The composition of claim 13 wherein the composition additionally contains about 0.5-5 percent by weight of an antioxidant selected from the group consisting of 4,4'-bis(.alpha.,.alpha.-dimethylbenzyl)diphenylamine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hexahydro-s-triazine, and 1,6-bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionamido]hexane and 0.5-3 percent by weight of a stabilizer selected from the group consisting of copolymers of polycaprolactam and polyhexamethylene adipamide, and terpolymers of polycaprolactam, polyhexamethylene adipamide and polyhexamethylene sebacamide.
17. The composition of claim 1 wherein the composition additionally contains about 0.5-5 percent by weight of an antioxidant selected from the group consisting of 4,4'-bis(.alpha.,.alpha.-dimethylbenzyl)diphenylamine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hexahydro-s-triazine, an 1,6-bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionamido]-hexane and 0.5-3 percent by weight of a stabilizer selected from the group consisting of copolymers of polycaprolactam and polyhexamethylene adipamide, and terpolymers of polycaprolactam, polyhexamethylene adipamide and polyhexamethylene sebacamide.
18. The composition of claim 17 containing up to 70 percent by weight of fillers selected from the group consisting of inorganic fillers, melt-blendable polymers and non-meltable polymeric fibers based on the combined weight of molding composition and fillers.
19. The composition of claim 16 containing up to 70 percent by weight of fillers selected from the group consisting of inorganic fillers, melt-blendable polymers and non-meltable polymeric fibers based on the combined weight of molding composition and fillers.
Patent Citations (3)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3595937 | 1971-07-01 | Weissermel et al. | |
| US3924103 | 1975-12-01 | Furuishi et al. | |
| DEX2,449,343 | 1976-04-01 |