US 4,092,268 AGrant
Catalytic Composition
Issue Date:1978-05-30
•6 Claims
Abstract
Polymers of conjugated dienes and copolymers of conjugated dienes with vinyl aromatic compounds or with other conjugated dienes having a high content of trans-1,4 linkages and a low content of 1,2 or 3,4 linkages and an elastomeric character are prepared by use of a catalytic composition which comprises (a ) an organo-lithium initiator and (b) a cocatalyst system comprising a compound of barium or strontium and an organometallic compound of a metal of Group IIB or IIIA of the Mendeleev periodic table of elements.
Metadata
Assignee
- Compagnie Generale des Etablissements Michelin, raison sociale Michelin & Cie
Inventor
- Yves de Zarauz
Application Information
Application Number:US 6606954
Filing Date:1976-02-23
Priority Date:1974-06-05
Art Unit:115
Classifications
IPC:
B01J 3112B01J 3102
Field of Search:
252428;431 R;431 C;431 N;431 L;430
Patent Drawings
This patent does not have any drawings.
Description
The present invention relates to polymers of conjugated dienes or copolymers of conjugated dienes either with each other or with vinyl aromatic compounds having a low content of 1,2 or 3,4 linkages and a high content of trans-1,4 linkages while retaining an elastomeric character, and a process of preparing these products with the use of a new catalytic composition.
A number of catalytic compositions are known which make it possible to prepare a solution in hydrocarbon media of diene polymers having a high degree of stereospecificity: high contents of cis-1,4 (for instance, polybutadiene, polyisoprene) or of trans-1,4 or else of 1,2 or 3,4. The polymers of high content of trans-1,4 (more than 95%) which are prepared in this manner have a very strong tendency to crystallize at ordinary temperature. They behave more like plastics than like elastomers and for this reason cannot be used as the main component of the mixture serving to manufacture elastic objects and in particular tires.
It is also well known that polymers of conjugated dienes and copolymers of conjugated dienes either with each other or with vinyl aromatic compounds prepared in hydrocarbon medium by means of lithium catalytic compositions do not have a high steric purity. As a matter of fact, with the lithium catalytic compositions the polymers and copolymers obtained have, for viscosities of the order of 2 or 3, a content of 1,2 or 3,4 linkages of the diene portion which is always greater than 6% and a content of trans-1,4 linkages which is always less than 60%. Thus the contents are as follows:
For polybutadienes and copolymers of butadiene
45% to 55% of trans-1,4
7% to 12% of 1,2
40% to 45% of cis-1,4
For polyisoprenes and copolymers of isoprene
10% to 25% of trans-1,4
6% to 10% of 3,4
70% to 85% of cis-1,4
For higher viscosities, equal to at least 6, one can note in particular in the case of isoprene and its copolymers a cis-1,4 content increase up to 95% to the detriment of the contents of trans-1,4 and of 1,2 or 3,4.
With lithium catalytic compositions the proportions of 1,2 or 3,4 linkages as compared to the 1,4 linkages can be increased within the above limits by recourse to certain artifices, for instance, by modifying the polarity of the reaction medium.
On the other hand, there are no methods for varying the content of trans-1,4 linkages within a wide range while retaining the content of 1,2 or 3,4 linkages at a very low level.
The object of the present invention is to remedy this state of the art by providing a means which makes it possible to obtain diene polymers or copolymers having a high content of trans-1,4 linkages in the diene portions of these compounds either over the entire length of the chain of the polymer or only over a portion of its length, as well as a very small content of 1,2 or 3,4 linkages.
Thus one object of the invention is to provide, on the one hand, a process for polymerizing or copolymerizing conjugated dienes with each other or with vinyl aromatic compounds leading to the obtaining of products having a high content of trans-1,4 linkages and at the same time a low content of 1,2 or 3,4 linkages and, on the other hand, these products themselves.
Another object of the invention is to provide a catalytic composition and its process of preparation which makes it possible to manufacture polymers of conjugated dienes and copolymers of conjugated dienes either with each other or with vinyl aromatic compounds which have a high content of trans-1,4 linkages and have only a low content of 1,2 or 3,4 linkages.
Accordingly, the present invention provides a catalytic composition for the polymerization of dienes or copolymerization of dienes with each other or with vinyl aromatic compounds which comprises:
a. an organo-lithium initiator and
b. a cocatalyst system comprising a compound of barium or strontium and an organometallic compound of a metal of Group IIB or IIIA of the Mendeleev periodic table of elements.
By "organo-lithium initiator" there is understood, first of all, any organometallic compound comprising one or more carbon-lithium bonds, and secondly any ionic-radical adduct of lithium and certain polynuclear aromatic hydrocarbons, and thirdly metallic lithium itself, as well as finally the oligomers produced by the addition of lithium to conjugated dienes or substituted styrenes.
As representative examples of the organo-lithium initiator the following compounds may be mentioned:
The alkyl organo-lithiums such as ethyl-lithium, n-butyl-lithium, isobutyl-lithium, sec.-butyl-lithium, ter.-butyl-lithium, isopropyl-lithium, n-amyl-lithium, isoamyllithium; the alkenyl organo-lithiums such as allyl-lithium, propenyl-lithium, isobutenyl-lithium; the "live" lithium polymers such as polybutadienyl-lithium, polyisoprenyllithium, and polystyryl-lithium; the dilithium polymethylenes such as 1,4-dilithium butane, 1,5-dilithium pentane, 1,20-dilithium eicosane; the aryl organo-lithiums such as benzyllithium, phenyl-lithium, 1,1-diphenyl-methyl-lithium; the polylithiums resulting from the reaction of metallic lithium with aryl-substituted ethylene compounds such as 1,1-diphenylethylene, trans-stilbene, tetra-phenylethylene; the radical ions such as lithium-naphthalene, lithium-anthracene, lithium-chrysene, lithium-diphenyl as well as the derivatives substituted by one or more alkyls.
With respect to the components of the cocatalyst system there is understood by "compound of barium or strontium": the hydrides H.sub.2 Ba and H.sub.2 Sr; the mono or polyfunctional organic acid salts of the formulas (R -- COO).sub.2 Ba or Sr, R.sub.1 -- (COO).sub.2 Ba or Sr in which R and R.sub.1 are organic radicals, the first monovalent and the second divalent, not having other functions capable of inactivating the organo-lithium initiator, and the corresponding thio acids, as well as the mono or polyfunctional alcoholates and the corresponding thiolates; the mono or polyfunctional phenates and the corresponding thiophenates; the alcohol acid and phenol acid salts of barium or strontium and the corresponding thio products; barium or strontium .beta.-diketonates such as the reaction products of barium or strontium with acetylacetone, dibenzoylmethane, thenoyltrifluoro-acetone, benzoyltrifluoroacetone, benzoyl-acetone; the organic derivatives of barium or strontium such as those of 1,1-diphenylethylene, 1,2-acenaphthylene, tetraphenylbutane, .alpha.-methyl-styrene or else those such as diphenyl barium or strontium, bis-cyclopentadienyl barium or strontium, the barium or strontium trialkylsilyls, barium or strontium triphenylsilyl; the mixed organic derivatives such as phenyl-barium iodide, methyl-strontium iodide, barium or strontium salts of secondary amines; ketone metals such as barium or strontium benzophenone, barium or strontium cinnamone, and the corresponding alkyl products as well as the sulfided homologues; the radical ions of barium and of strontium such as those of naphthalene, anthracene, chrysene, diphenyl, etc.
As representative examples of the organometallic compound of a metal of Group IIB or IIIA of the Mendeleev periodic table of elements there may be mentioned: Dialkyl zinc or cadmium compounds such as diethyl zinc, diethyl cadmium; halogenated or nonhalogenated organoaluminum compounds such as triethyl aluminum, tri-isobutyl aluminum, diethyl aluminum chloride, ethyl aluminum dichloride, ethyl aluminum sesquichloride, methyl aluminum sesquichloride; dialkyl aluminum hydrides such as diethyl aluminum hydride, diisobutyl aluminum hydride; and organoboron compounds.
The cocatalytic system may be formed in accordance with the following two preferred variants:
In accordance with the first variant, the different components of the cocatalytic system are dissolved separately in a separate hydrocarbon solvent, preferably identical to the one which will be used subsequently upon the polymerization or copolymerization reaction so as to be able to be introduced separately into the reaction medium.
In accordance with the second variant, the cocatalyst system is "preformed" by mixing the barium or strontium compound and the organometallic compound of a metal of Group IIB or IIIA within a hydrocarbon solvent. These preformed cocatalyst systems are characterized by the fact that they are more soluble in the hydrocarbon solvents and by the fact that they retain their high activity for long periods of time. This mixing between the two components of the cocatalyst system is accompanied, as a matter of fact, by a total or partial solubilizing of the barium or strontium compound and in particular of those which are normally insoluble in hydrocarbon media such as the hydrides, the acetylacetonates and most of the alcoholates. The result is thus that the use of the preformed cocatalytic system is particularly easy.
In accordance with the first variant, the components of the cocatalytic system dissolved in the hydrocarbon solvent are introduced separately into the reaction medium, either at the start of the reaction at the same time as the organolithium initiator in order to form the catalytic composition "in situ", or during the course of the polymerization jointly in small quantities or at a single time, or else one after the other in any order. This manner of procedure is justified primarily for barium or strontium compounds which are soluble in the solvents in question.
It will be understood that only as from the moment when the entire cocatalytic system which has been introduced into the reaction medium has reacted with the organo-lithium initiator will one benefit from the effect desired, namely the increase in the content of trans-1,4 linkages and the decrease in the content of 1,2 or 3,4 linkages. The result is that when the entire cocatalytic system is present from the very start of the reaction, one obtains products having a very high content of trans-1,4 linkages and a very low content of 1,2 or 3,4 linkages over the entire length of the polymer or copolymer.
On the other hand, when the components of the cocatalytic system are introduced during the reaction, either jointly in small quantities or one after the other, one can prepare products having several sequences and having different steric configurations, the addition of the cocatalytic system resulting in the formation of sequences high in trans-1,4 linkages and low in 1,2 or 3,4 linkages.
In accordance with the second variant, when the cocatalytic system is used in "preformed" form, one can add it to the organo-lithium initiator either at the start of the reaction in order to obtain a product having a content of trans-1,4 linkages which is constant from one end to the other of the macromolecular chains or during the reaction in one or more additions, depending on whether it is desired to have a modification of steric configuration only as from said addition or whether it is desired to have the modification of configuration progressively.
The catalytic composition in accordance with the invention has an activity which is spread over a wide range of concentrations of the catalyst and ratios of the components of the catalytic composition.
Depending on the conditions under which the reaction takes place (nature of solvent, the monomer or monomers present, temperature, etc.) the molar ratios between each of the components of the cocatalytic system and between one of the latter with either the organo-lithium initiator or the "live" lithium polymer or copolymer can be different in order to obtain given contents of trans-1,4 and 1,2. It will therefore be necessary to adjust these different molar ratios in accordance with the conditions under which one is operating and the steric configurations desired. In this way, for instance, the contents can be regulated continuously from 45 to 95% of trans-1,4 and from 12 to 3% of 1,2 in the case of polybutadiene or copolymers having a base of butadiene and from 25 to 45% of trans-1,4 and 10 to 5% of 3,4 in the case of polyisoprene or of copolymers having a base of isoprene.
The result is that the optimum concentration for one component of the catalyst composition depends on the concentration of the other components of the catalyst composition. However, one can assign certain limits to the different molar ratios within which one will obtain optimum contents of trans-1,4 linkages and minimum contents of 1,2 or 3,4 linkages.
The said limits are: ##EQU1## with R.sup.3 Me IIIA representing an organometallic compound of a metal of Group IIIA and R.sup.2 Me IIB representing an organometallic compound of a metal of Group IIB.
By gram atom of lithium there is understood the quantity of active organo-lithium compound used which represents the difference between the total amount actually introduced and the minimum necessary to obtain a commencement of the polymerization (quantity serving, inter alia, to neutralize the residual impurities of the reaction media).
The present invention provides, in addition to a catalytic composition and its method of preparation, products having a very high content of trans-1,4 linkages and a low content of 1,2 or 3,4 linkages, retaining however an elastomeric character, and a process by which the monomers are polymerized and copolymerized, leading to these products.
In accordance with a first variant, a product having a high content of trans-1,4 linkages and a low content of 1,2 or 3,4 linkages over the entire length of the polymer or copolymer is obtained by introducing the catalytic composition at the start of the reaction.
In accordance with another variant, the process leads to polymers and copolymers having different or else progressive sequences and steric configurations depending on whether the components of the catalytic composition are added to the reaction medium one or more times, jointly or separately.
The process in accordance with the invention is particularly suitable for the polymerization of dienes and the copolymerization of dienes and vinyl aromatic compounds.
As representative examples of dienes, mention may be made of conjugated dienes such as 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 2-methyl-1,3-pentadiene, and 2,4-hexadiene.
As representative examples of vinyl aromatic compounds mention may be made of styrene, ortho-, meta-, and paramethyl styrene or the commercial mixture "vinyl-toluene", the di- and polymethyl styrenes, p-tertiobutyl-styrene, the vinylnaphthalenes, the methoxy styrenes, the halostyrenes, vinylmesitylene, vinyldurol, and divinylbenzene.
Products having a high content of trans-1,4 linkages prepared in accordance with this new process on basis of the new catalytic composition have the characteristic of being elastomers and therefore of lending themselves to being placed in the form of a mixture in order to produce rubbers, contrary to the other polymers of very high trans-1,4 purity prepared up to now by means of different catalytic compositions, which are plastic and brittle at ordinary temperature because crystalline.
The mixtures in nonvulcanized state produced with the products obtained by the carrying out of the process due to their high content of trans-1,4 have characteristics such as improved green strength, very high breaking force and elongation at rupture and better dimensional stability.
These mixtures of improved properties are then capable of leading to better rubbers which can be used in particular for the manufacture of tires.
The following nonlimitative examples are given solely in order to illustrate the invention.
EXAMPLE 1
Butadiene/Styrene Copolymerization by Means of the Catalytic Composition n-Butyl Lithium/Cinnamone-Barium/Triethyl Aluminum
Preparation of the Cocatalyst System
Since the cinnamone-barium complex is soluble in toluene, it was possible to study the specific influence of each of the components of the cocatalyst system, the ratio Ba/Al not being fixed for reasons of solubility in the reaction medium.
The cinnamone-barium complex is prepared in a 250 cc. Steinie bottle in an atmosphere of rectified nitrogen, by dissolving 0.1 mole of cinnamone (1,5-diphenyl-1,4-pentadiene-3-one) in 50 cc. of tetrahydrofurane in which 1.5 g. of finely divided metallic barium are present in suspension. After this mixture has been agitated for about 20 hours at room temperature, a red solution is obtained, which is filtered. This solution is evaporated under vacuum. The brownish-red deposit obtained, after being washed twice with heptane, is dissolved in toluene, still under an atmosphere of rectified nitrogen, so as to obtain an 0.025 M solution of barium.
Copolymerization
Two series of copolymerization experiments are carried out by introducing into 250 cc. Steinie bottles, as catalytic composition:
variable amounts of from 0 to 200 .times. 10.sup.-6 moles of triethyl aluminum.
50 .times. 10.sup.-6 moles of active n-butyl-lithium, as defined above.
In the first series, no barium compound is used. 50 .times. 10.sup.-6 moles of cinnamone-barium are introduced into each of the bottles of the second series.
The copolymerization is carried out in the presence of cyclohexane (123 g. per 250 cc. Steinie bottle) with 9.225 g. of butadiene and 3.075 g. of styrene per bottle.
The reaction flasks are placed in a thermostatically controlled tank maintained at 70.degree. C. where they are agitated for a variable period of time so as to obtain samples corresponding to increasing percentages of conversion.
The results obtained at 50% conversion are set forth in Tables IA and IB below:
First Series ( [Ba] =O)
When examining these results one notes the influence of each of the compounds introduced on the steric configuration of the polymers obtained (% of trans-1,4 and % of 1,2) and subsidiarily on the reaction kinetics, the inherent viscosity reached and the method of incorporating the styrene.
With respect to the influence on the steric configuration and in particular on the contents of trans-1,4 and of 1,2, it is noted that the expected effect is obtained only when the three components of the catalytic composition are present together in the reaction medium; if one or the other is absent, a steric configuration is obtained which is rather close to the one obtained with n-butyl-lithium used by itself.
EXAMPLE 2
Polymerization of Butadiene by Means of n-Butyl Lithium and a "Preformed" Cocatalytic System: Barium Acetylacetonate/Trialkyl Aluminum
Preparation of Cocatalyst System
The barium acetylacetonate is prepared directly by reaction of acetylacetone and barium hydroxide in anhydrous methanol medium.
The product prepared is insoluble in hydrocarbons. A soluble cocatalytic system is obtained by mixing the barium acetylacetonate and the trialkyl aluminum in the presence of a hydrocarbon solvent under a rectified-nitrogen atmosphere for 15 minutes at room temperature.
Three cocatalytic systems are prepared:
System A: 5.32 millimoles of barium acetylacetonate having been placed in suspension in 170 g. of normal heptane, 23.4 millimoles of commercial triethyl aluminum of a concentration of 0.92 M are added. After agitation, a clear solution of 2.9 .times. 10.sup.-2 M barium and 11.3 .times. 10.sup.-2 M aluminum is obtained.
System B: To 5.85 millimoles of barium acetylacetonate suspended in 170 g. of toluene there are added 26.3 millimoles of commercial triethyl aluminum of a concentration of 0.92 M. After agitation there is obtained a clear solution of a concentration of 3.2 .times. 10.sup.-2 M barium and 11.6 .times. 10.sup.-2 M aluminum.
System C: To 5.58 millimoles of barium acetylacetonate suspended in 170 g. of heptane there are added 25.1 millimoles of commercial tri-isobutyl aluminum of a concentration of 0.79 M. Upon agitation there is obtained a clear solution of a concentration of 2.4 .times. 10.sup.-2 M barium and 11.8 .times. 10.sup.-2 M aluminum.
Polymerization
These three cocatalytic systems are used in combination with n-butyl-lithium to polymerize butadiene dissolved in heptane (first series of experiments) or in toluene (second series of experiments).
These series of experiments are carried out in 250 cc. Steinie bottles closed by a rubber stopper through which the different ingredients necessary for the polymerization are introduced. Into these bottles, under the pressure of rectified nitrogen (about 1 bar) there are introduced 123 g. of solvent (heptane or toluene) and then 12.3 g. of butadiene followed by one of the preceding cocatalytic systems and finally the n-butyl-lithium. The bottles are then placed in a tank which is maintained constant by thermostat at 60.degree. C. and are agitated therein for three hours.
At the end of these 3 hours, the polymerizations are stopped by introducing into said tank 0.25 cc. of a solution of methanol in toluene of 60 g./liter. A phenolic antioxidant is also introduced (Agerite Geltrol manufactured by Vanderbilt) (2 cc. of a 246 g./liter solution).
The polymers are then recovered by coagulation by means of a methanol-acetone mixture and dried under vacuum in an oven (80.degree. C. -- 0.2 bar -- 15 hours).
The percentages of conversion of butadiene into polybutadiene which have been obtained, the inherent viscosities established at 25.degree. C. in 1 g./liter solution in toluene and the steric configurations are determined on the samples thus obtained.
The results obtained are summarized in Tables IIA and IIB below:
First Series (solvent: heptane)
EXAMPLE 3
Polymerization of Butadiene by Means of n-Butyl Lithium and a "Preformed" Cocatalytic System: Dibenzoylmethane Barium/Triethyl Aluminum
Preparation of Cocatalyst System
The dibenzoylmethane barium chelate is prepared directly from dibenzoylmethane and barium hydroxide, in anhydrous methanol medium.
The product prepared is insoluble in hydrocarbons. The cocatalytic system is prepared by mixing 5.2 millimoles of dibenzoylmethane barium and 26 millimoles of commercial triethyl aluminum of a concentration of 0.84 M in an atmosphere of rectified nitrogen suspended in 123 g. of heptane. This mixture is brought to 60.degree. C. for one half hour while agitating so that the chelate dissolves. There is then obtained a yellow solution which remains clear after it has returned to room temperature. It has a concentration of about 3 .times. 10.sup.-2 M barium and 15 .times. 10.sup.-2 M aluminum.
Polymerization
This cocatalytic system is used in combination with n-butyl lithium to polymerize butadiene in solution in heptane.
The polymerization conditions are the same as those described previously (Steinie bottles of 250 cc., 123 g. of heptane and 12.3 g. of butadiene, 3 hours at 60.degree. C.).
Results Obtained
EXAMPLE 4
Copolymerization of Butadiene and Styrene by Means of n-Butyl Lithium and the "Preformed" Cocatalytic System of Example 3
The same dibenzoylmethane barium triethyl aluminum cocatalytic system is used.
The copolymerization is carried out in 250 cc. Steinie bottles as previously, under the same experimental conditions.
Into each of the reaction flasks there are introduced:
123 g. of heptane
12.3 g. of monomer: 9.225 g. of butadiene and 3.075 g. of styrene (namely 25% of the charge)
65 .times. 10.sup.-6 moles of active n-BuLi
60 .times. 10.sup.-6 moles of cocatalytic complex, calculated as barium (and therefore accompanied by 300 .times. 10.sup.-6 moles of Al)
At 80.degree. C., the results obtained, as a function of the time of the reaction, are as follows:
The final copolymer obtained after the end of 18 hours had an inherent viscosity of 1.1.
EXAMPLE 5
Butadiene-Styrene Copolymerization by Means of the Catalytic Composition n-Butyl Lithium/Barium Nonylphenate/Triethyl Aluminum or Diethyl Zinc
Preparation of the Cocatalyst System
The barium nonylphenate is prepared by contacting nonylphenol (0.02 mole) and barium hydroxide (0.01 mole of Ba(OH).sub.2) in the presence of 100 cc. of toluene. The mixture is agitated in the hot (60.degree.-80.degree. C.) until the barium hydroxide has entirely disappeared. About half the solvent is evaporated in vacuum so as to carry over all of the water formed and the concentrated solution is then made up to 100 cc. by means of fresh toluene. In this way there is obtained a solution of anhydrous barium nonylphenate in toluene of a concentration of about 1/10 M.
Copolymerization
Butadiene and styrene are copolymerized in 250 cc. Steinie bottles, into which there are introduced:
In order to complete the catalytic composition there are added:
either 100 .times. 10.sup.-6 moles of triethyl aluminum or
100 .times. 10.sup.-6 moles of diethyl zinc.
In the case of the control test, neither of these two compounds is added.
The copolymerization is carried out at 70.degree. C. for variable periods of time set forth in Table V in which the results obtained are entered.
EXAMPLE 6
Copolymerization of Butadiene-Styrene and Copolymers having Two Different Sequences with Steric Configuration of Their Own
This copolymer is obtained by adding, during the polymerization, one of the three components of the catalytic composition, triethyl aluminum in the present case, the n-butyl-lithium and the barium compound being added together upon the start of the reaction.
Into a 250 cc. Steinie bottle there are added, in all cases under an atmosphere of rectified nitrogen, 123 g. of heptane, 9.225 g. of butadiene, 3.075 g. of styrene, 50 .times. 10.sup.-6 moles of active n-butyl lithium, 50 .times. 10.sup.-6 moles of barium nonylphenate prepared as in the preceding example.
The mixture is allowed to copolymerize for 11/2 hours at 70.degree. C.
The percentage conversion reached is 54%. The copolymer contains 16% styrene and shows the following steric configuration: 53% trans-1,4 and 10% 1,2 (in its polybutadiene portion).
Whereupon 100 .times. 10.sup.-6 moles of triethyl aluminum are added per Steinie bottle whereupon the polymerization is allowed to proceed at 70.degree. C. for an hour and a half. The final copolymer contains 14% styrene. Moreover, on the average 61% of the butadiene links are in trans-1,4 form and 8% in 1,2. The overall percentage of conversion is 76%.
This means that the resultant copolymer has two sequences, namely:
the first, representing 71% of the total copolymer, contains on the one hand 16% styrene and 53% trans-1,4% and on the other hand 10% 1,2 for the steric configuration of the polybutadiene portion,
the second, representing 29% of the total copolymer, contains on the one hand 9% styrene and on the other hand 79% trans-1,4 and 4% of 1,2, for the polybutadiene portion.
EXAMPLE 7
Polymerization of Butadiene by Means of n-Butyl Lithium and a "Preformed" Cocatalytic System: Barium Alcoholate/Organo-Aluminum, Chlorinated or Nonchlorinated
Preparation of the Cocatalytic System
Various barium alcoholates and various organo-aluminum compounds are used to preform different cocatalytic systems under the following general conditions:
About 2 g. of barium alcoholate are introduced into 250 cc. Steinie flasks under an atmosphere of rectified nitrogen. 100 cc. of heptane are added and then an amount of alkyl or chloro-alkyl aluminum as indicated in the following table. The flasks are then placed in a tank which is maintained by thermostat at 60.degree. C. in which they are agitated for 6 hours. The barium alcoholate which may still not have dissolved is then filtered off under an atmosphere of rectified nitrogen and the amount of barium in solution is determined.
In Table VIIA below there are given for each of the alcoholates and organo-aluminums used the quantities of product introduced (for 100 cc. of heptane.), the concentration of barium (in moles/liter) obtained after dissolving and filtration, as well as the yield of dissolved barium with reference to the quantity of barium alcoholate introduced, and the reference to the cocatalytic system thus prepared:
Polymerizations
With these cocatalytic systems butadiene is polymerized under the following conditions:
Into a 250 cc. Steinie bottle there are introduced:
The polymerization reaction is carried out with agitation for 14 hours at 70.degree. C.
The results obtained with the different cocatalytic systems are set forth in Table VIIB:
EXAMPLE 8
Polymerization of Butadiene by Means of n-Butyl Lithium and a "Preformed" Cocatalytic System: Strontium Alcoholate/Organo-Aluminum Compound, Chlorinated or Not
Preparation of the Cocatalytic Systems
Conditions indentical to those of the preceding examples (except agitation for 7 hours at 70.degree. C. instead of 6 hours at 60.degree. C.).
The quantities indicated also correspond to 100 cc. of heptane.
Polymerization
The same conditions as in the preceding example except
-- polymerization for 6 hours at 70.degree. C. with 50 .times. 10.sup.-6 moles of strontium alcoholate per reaction flask.
EXAMPLE 9
Polymerization of Butadiene by Means of n-Butyl Lithium and a "Preformed" Cocatalytic System: Barium Hydride/Organo-Aluminum Compound, Chlorinated or Not
Preparation of the Cocatalytic Systems
The conditions of preparation are identical to those of Example 7 (6 hours at 60.degree. C.), the two grams of barium alcoholate being replaced by three grams of barium hydride.
Two series of cocatalytic systems were prepared, one in heptane (100 cc. per Steinie flask) and the other in toluene (20 cc. per flask).
In Tables IXA and IXB below, there are given for each of the two series the quantities of products used per Steinie bottle, the final concentration of barium in the solution obtained after filtration as well as the yield of barium as previously and the reference to the preparation.
Polymerization
Same conditions as in Example 7:
-- polymerization at 70.degree. C. for 24 hours in heptane medium
-- quantity of BaH.sub.2 per 250 cc. reaction flask: 50 .times. 10.sup.-6 moles.
The results obtained, as a function of the quantities of n-butyl-lithium used, are set forth in Table IXC:
EXAMPLE 10
Polymerization of Butadiene by Means of the Catalyst Composition n-Butyl-Lithium/Barium Naphthenate/Diethyl Zinc
Preparation of the Barium Catalyst
The barium naphthenate, prepared from commercial naphthenic acid by neutralization with caustic soda in aqueous medium and precipitation by barium chloride is a salt soluble in toluene medium. There is therefore used an 0.113 mole/liter solution in barium of barium naphthenate in toluene.
Polymerization
Butadiene is polymerized under the same conditions as previously in 250 cc. Steinie bottles, 12.3 g. of butadiene for 123 g. of heptane with 50 .times. 10.sup.-6 of barium naphthenate and 50 .times. 10.sup.-6 moles of active n-butyl-lithium per flask, for 6 hours at 70.degree. C.
The results, based on the quantities of diethyl zinc introduced, are set forth in Table X.
EXAMPLE 11
Polymerization of Isoprene by Means of the Catalyst Composition n-Butyl-Lithium/Barium Nonylphenate/Triethyl Aluminum or Diethyl Zinc
The solution of barium nonylphenate in toluene is prepared in the same manner as in Example 5.
The isoprene (12.3 g.) is polymerized in 250 cc. Steinie bottles in heptane medium (123 g.) for 6 hours at 70.degree. C. with, per reaction flask:
50 .times. 10.sup.-6 moles of active n-BuLi
0 or 50 .times. 10.sup.-6 moles of barium nonylphenate
0, 100, or 200 .times. 10.sup.-6 moles of triethyl aluminum or diethyl zinc.
In Table XI the influence of the combination of these different additives is compared.
EXAMPLE 12
Isoprene/Styrene Copolymerization by Means of the Same Catalyst Composition as in Example 11
One operates under the same polymerization conditions in 250 cc. Steinie bottles, in heptane medium (123 g.) with 9.24 g. of isoprene and 3.08 g. of styrene (25% referred to the isoprene). Copolymerization is effected for 2 hours at 70.degree. C. in the presence of 50 .times. 10.sup.-6 moles of active n-BuLi.
EXAMPLE 13
Butadiene/Vinyl Toluene Copolymerization by Means of the Catalyst Composition n-Butyl-Lithium/Barium Nonylphenate/Triethyl Aluminum
In 250 cc. flasks there are copolymerized:
9.24 g. of butadiene
3.08 g. of vinyl toluene (commercial mixture of 2/3 metamethyl styrene and 1/3 paramethyl styrene)
123 g. of heptane
50 .times. 10.sup.-6 moles of active n-BuLi
50 .times. 10.sup.-6 moles of barium nonylphenate
200 .times. 10.sup.-6 moles of triethyl aluminum for 3 hours at 70.degree. C.
the results obtained are as follows:
conversion rate obtained: 64%
.eta. = 0.97
9% vinyl toluene present in the copolymer
82% trans-1,4 linkages and 3% 1,2 linkages in the polybutadiene phase.
EXAMPLE 14
Butadiene/Tertiobutylstyrene Copolymerization by Means of the Same Catalyst Composition as in Example 13
Per 250 cc. Steinie flask there are introduced:
9.24 g. of butadiene
3.08 g. of tertiobutylstyrene (95% para, 5% ortho)
123 g. of heptane
50 .times. 10.sup.-6 moles of active n-BuLi
50 .times. 10.sup.-6 moles of barium nonylphenate
200 .times. 10.sup.-6 moles of triethyl aluminum, copolymerization is effected for 51/2 hours at 70.degree. C.
the results obtained are as follows:
.eta. = 1.12
7% tertiobutylstyrene present in the copolymer
85% trans-1,4 linkages and 3%, 1,2 linkages
EXAMPLE 15
Mechanical Properties of a Mixture for Rubber Having a Base of Butadiene/Styrene Copolymer with a High Content of Trans-1,4 and Low Content of 1,2
1. Preparation of the Copolymer
The catalytic composition of Example 3 or 4 is used:
n-butyl-lithium
preformed cocatalytic system: dibenzoylmethane barium/triethyl aluminum.
The polymerization is carried out in a 10 liter reactor in an atmosphere of rectified nitrogen with:
Solvent: heptane: 5040 g.
Monomers:
butadiene: 378 g.
styrene: 126 g.
Initiator: active n-butyl-lithium: 1.64 .times. 10.sup.-3 moles
Cocatalytic system: barium:
1.64 .times. 10.sup.-3 moles
aluminum 8.2 .times. 10.sup.-3 moles
for 2 hours at 80.degree. C.
The percentage conversion obtained is 75% and the viscosity reached is 1.4.
A tri-chain grafting is then effected by introducing into the medium which is still active 1.64 .times. 10.sup.-3 moles of diphenyl carbonate in accordance with Michelin French Pat. No. 2,053,786. Reaction is allowed to continue for 20 minutes at a temperature of 80.degree. C. Methanol is then introduced to stop the reaction as well as an antioxidant (0.5% by weight referred to the rubber) and the elastomer (about 380 g.) is recovered by steam distillation of the solvent and drying under vacuum.
The final viscosity after grafting has become 1.9. The Mooney viscosity (1 + 3 at 100.degree. C.) is then 45.
The resultant copolymer has the following steric configuration:
The content of incorporated styrene is 8%.
2. Rubber-Making Mixture
The elastomer described above is used to make a mixture having the following formula:
The same mix is prepared with a commercial butadienestyrene copolymer (SBR 1500) as control. Stress strain measurements are carried out on test pieces of these nonvulcanized mixes (measurement of the green strength).
The results obtained are as follows:
The mixture prepared with the elastomer in accordance with the invention has a better mechanical strength than the control mixture.
The two mixtures are then vulcanized for 60 minutes at 144.degree. C. The mechanical properties obtained are set forth in Table XVB.
It is noted that the elastomer in accordance with the invention, that is to say the SBR, with a high content of trans-1,4 and a low content of 1,2, actually has the properties of a rubber and even of a good rubber if one considers the level of hysteresis losses reached.
Claims
What is claimed is:
1. A catalytic composition for the polymerization and copolymerization of olefins consisting of a. a lithium initiator selected from the group consisting of metallic lithium, ethyl-lithium, n-butyl lithium, isobutyl-lithium, sec.-butyl-lithium, ter.-butyl-lithium, isopropyl-lithium, n-amyl-lithium, isoamyl-lithium, allyl-lithium, propenyl-lithium, isobutenyl-lithium, polybutadienyl-lithium, polyisoprenyl-lithium, polystyryl-lithium, 1, 4-dilithium butane, 1-5-dilithium pentane, 1, 20-dilithium eicosane, benzyl-lithium, phenyl-lithium, 1, 1-diphenylmethyl-lithium, the polylithium reaction product of metallic lithium with 1, 1-diphenylethylene, the polylithium reaction product of metallic lithium with trans-stilbene, the polylithium reaction product of metallic lithium with tetraphenylethylene, lithium-naphthalene, lithiumanthracene, lithium-chrysene and lithiumdiphenyl; and b. a cocatalyst system consisting of (b.sub.1) a compound of barium or strontium selected from the group consisting of barium hydride, strontium hydride, barium naphthenate, barium methanolate, strontium methanolate, barium ethanolate, strontium ethanolate, barium tertio-butanolate, barium nonylphenate, barium acetylacetonate, strontium acetylacetonate, barium dibenzoylmethane, strontium dibenzoylmethane, barium thenoyltrifluoroacetonate, strontium thenoyltrifluoro-acetonate, barium benzoyltrifluoro-acetonate, strontium benzolytrifluoro-acetonate, barium benzoyl-acetonate, strontium benzoyl-acetonate, barium 1, 1-diphenylethylene, strontium 1, 1-diphenylethylene, barium 1, 2-acenaphthylene, strontium 1, 2-acenaphthylene, barium tetraphenyl-butane, strontium tetraphenylbutane, barium alpha-methyl-styrene, strontium alpha-methyl-styrene, diphenyl-barium, diphenylstrontium, bis-cyclopentadienyl-barium, bis-cyclopentadienyl-strontium, barium triphenylsilyl, strontium triphenylsilyl, phenyl-barium iodide, methyl-strontium iodide, barium-benzophenone, strontium-benzophenone, barium-cinnamone, strontium-cinnamone, barium-naphthalene, strontium-naphthalene, barium-anthracene, strontium-anthracene, barium-chrysene and strontium-chrysene; and (b.sub.2) an organometallic compound of aluminum or zinc selected from the group consisting of diethyl zinc, triethyl aluminum, tri-isobutyl aluminum, diethyl aluminum chloride, ethyl aluminum dichloride, ethyl aluminum sesquichloride, methyl aluminum sesquichloride, diethyl aluminum hydride and diisobutyl aluminum hydride; said components being present in such quantities that the ratios are within the following limits: ##EQU2##
2. The catalytic composition according to claim 1 wherein said components are present in such quantities that the ratios are within the following limits: ##EQU3##
3. The catalytic composition according to claim 1 consisting of n-butyl lithium, barium nonylphenate and triethyl aluminum.
4. The catalytic composition according to claim 1 consisting of n-butyl lithium, dibenzoylmethane barium and triethyl aluminum.
5. A process of preparing the catalytic composition defined by claim 1 which comprises preforming the cocatalyst system by mixing together the components thereof which have been previously placed in solution or suspension in a hydrocarbon solvent.
6. The process according to claim 5 wherein the hydrocarbon solvent is heptane or toluene.
Patent Citations (9)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3294768 | 1966-12-01 | Wofford | |
| US3542751 | 1970-11-01 | Throckmorton | |
| US3624000 | 1971-11-01 | Throckmorton | |
| US3629213 | 1971-12-01 | Onishi et al. | |
| US3664989 | 1972-05-01 | Petrov et al. | |
| US3665062 | 1972-05-01 | Onishi et al. | |
| US3725301 | 1973-04-01 | Mueller et al. | |
| US3734900 | 1973-05-01 | Throckmorton | |
| US3769270 | 1973-10-01 | Saltman et al. |