US 4,085,083 AGrant
Plasticized Polymers of Vinyl Acetate
Issue Date:1978-04-18
•7 Claims
Abstract
Polyesters derived from the reaction of a dibasic acid, a polyethylene glycol and an aliphatic alcohol are used as plasticizers for vinyl acetate polymers.
Metadata
Assignee
- Ciba-Geigy AG
Inventors
- Frank Lamb
- Malcolm Combey
- Hugh Melvin Cooper
Application Information
Application Number:US 602887&
Filing Date:1975-08-07
Priority Date:1970-10-27
Art Unit:142
Classifications
IPC:
C08K 511
Field of Search:
26031.6;475 P
Patent Drawings
This patent does not have any drawings.
Description
According to the present invention is provided a composition comprising a vinyl acetate polymer or copolymer and from 10% to 100% by weight based on the weight of the polymer of a polyester derived from the reaction of an acid or anhydride selected from succinic, glutaric or adipic or any mixture thereof, a polyethylene glycol having a molecular weight up to 500, and an aliphatic alcohol containing from 2 to 11 carbon atoms. The amount of polyester is preferably from 40% to 80% by weight based on the weight of the polymer. The polyester may be obtained by reacting the acid or acid anhydride with a glycol and an alcohol. A deficiency or excess of either or both of the glycol and alcohol may be used: where there is a deficiency of glycol this may be from 0 to 10 mole% below the theoretical amount and where there is a deficiency of alcohol, this may be from 0 to 50 mole% below the theoretical amount: where there is an excess of either or both glycol and alcohol this may be up to 20 mole% in excess of the theoretical amount.
The polyester may also be obtained by ester interchange as, for example, by heating a di-alkyl ester of a di-carboxylic acid with a glycol in the presence of a catalyst.
The molecular weight of the polyester may conveniently be from 250 to 3000 but it is preferably from 350 to 1500.
A mixture of succinic, glutaric and adipic acids which is particularly preferred, is a commercially available mixture having the approximate composition by weight of 21% succinic acid, 45% glutaric acid and 34% adipic acid.
The polyethylene glycol preferably has an average molecular weight of from 175 to 225.
The alcohol is preferably one containing from 3 to 6 carbon atoms per molecule, for example, n-butyl alcohol or isobutyl alcohol.
Examples of plasticisers which may be used are those derived from:
(a) 4 moles of a mixture of adipic, glutaric and succinic acids (with the approximate composition by weight 21% succinic, 45% glutaric and 34% adipic acids), 3.59 moles of polyethylene glycol having a molecular weight of 200, and 1.28 moles of isobutanol.
(b) 4 moles of a mixture of adipic, glutaric and succinic acids (with the approximate composition by weight 21% succinic, 45% glutaric and 34% adipic acids), 3.76 moles of polyethylene glycol having a molecular weight of 200 and 1.24 moles of isobutanol.
The vinyl acetate polymer may be derived from the polymerisation of 100% vinyl acetate monomer or it may be a copolymer derived from the polymerisation of a mixture comprising between 55% and 100% of vinyl acetate, the remainder being one or more ethylenically unsaturated, non-halogenated co-monomers, for example a maleate, an acrylate, a methacrylate or ethylene. The maleates, acrylates and methacrylates may be the alkyl esters for instance the methyl esters. An example of the vinyl acetate polymer is the one sold under the Trade Mark "Vinamul 9800".
The present invention also provides a method for producing a plasticised vinyl acetate polymer or copolymer by adding the plasticiser to an emulsion of the polymer while stirring.
The plasticiser is conveniently added to the emulsion of the polymer and the mixture stirred vigorously using a Silverson homogeniser to obtain a free flowing dispersion.
Vinyl acetate polymers plasticised with the polyesters hereinbefore described may be used in surface coatings, fusible interlinings, adhesives, binders for fibres and non-woven fabrics, sizes for glass fibres, barrier coatings for bitumen-containing floor coverings, linoleum and leather finishes.
Vinyl acetate polymers plasticised in accordance with the present invention are superior to those plasticised with di-n-butyl phthalate which is the commonest plasticiser for polyvinyl acetate. For instance, the volatile loss is significantly less and there is an improvement in the solvent extraction resistance.
We have found, surprisingly, that the light transmission of compositions of vinyl acetate polymers or copolymers containing alcohol end-stopped polyesters hereinbefore described, is superior to that of vinyl acetate polymers or copolymers containing similar polyesters but which are not end-stopped with an aliphatic alcohol.
The following Examples further illustrate the present invention. Parts by weight shown therein bear the same relation to parts by volume as do kilograms to liters. Parts and percentages are expressed by weight.
EXAMPLE 1
(a) A polyester having a molecular weight of 1100 was prepared from 4 moles of a mixture of adipic, glutaric and succinic acid (with the approximate composition 21% succinic, 45% glutaric and 34% adipic acids), 3.59 moles of polyethylene glycol having a molecular weight of 200, and 1.28 moles of isobutanol. The acid value was 8.4 mg potassium hydroxide per gram and the hydroxyl value was 20 mg potassium hydroxide per gram. The viscosity was 1,740 centistokes at 25.degree. C.
(b) 33 parts of the polyester prepared in Example 1(a) was added slowly to a mixture of 33 parts water and 100 parts of an emulsion of polyvinyl acetate containing 50 parts of polyvinylacetate. The emulsion was stirred vigorously in a Silverson homogeniser until a free flowing dispersion was obtained, which was cast at a wet film thickness of 0.020 inches onto a clean glass plate. After standing for 24 hours the cast film was assessed visually for clarity and was found to be very good.
Compositions with similarly good clarity were also obtained when the procedure of Example 1(b) is repeated except that instead of polyvinyl acetate the following copolymers are employed. The percentages are by weight:
(a) 90% vinyl acetate-10% ethylene
(b) 80% vinyl acetate-20% ethylene
(c) 60% vinyl acetate-40% dimethylmaleate
(d) 55% vinyl acetate-45% methyl acrylate
(e) 75% vinyl acetate-25% methylmethacrylate
EXAMPLE 2
A polyester was prepared from 2.00 moles of adipic acid, 1.71 moles of polyethylene glycol having a molecular weight of 200 and 0.64 moles of isooctyl alcohol. The molecular weight of this polyester was 1225, the acid value 6.9 mg potassium hydroxide per gram, the hydroxyl value 12 mg potassium hydroxide per gram, and the viscosity was 1,172 centistokes at 25.degree. C. This was added to polyvinyl acetate as in Example 1(b) and the clarity was found to be very good.
Examples 3 to 11
Each of the polyesters shown in Table I were prepared from 4 moles of a mixture of adipic, glutaric and succinic acid (with the approximate composition 21% succinic, 45% glutaric and 34% adipic acids) together with the molar quantities of glycol and alcohol reactants denoted in the second column of the Table.
Each polyester was added to polyvinyl acetate as in Example 1(b), and the clarity was found to be very good.
Comparative Example
The film clarity/compatibility of polyvinyl acetate containing the polyester of Example 2 was compared with that of polyvinyl acetate containing a commercially available plasticiser based on adipic acid and polyethylene glycol having a molecular weight of 200, but not end-stopped with an aliphatic alcohol (Polyester A). Both emulsions and films were prepared as in Example 1(b) and the clarity of the films measured as a percentage of light transmission was as follows:
Polyester A produced a film of poorer clarity indicating less compatibility with polyvinyl acetate than the polyester of Example 2 of the present invention.
Claims
We claim:
1. A composition comprising a vinyl acetate homopolymer or copolymer, made up of at least 55% of a vinyl acetate monomer and the remainder being one or more ethylenically unsaturated non-halogenated comonomers, and from 10 to 100% by weight based on the weight of the polymer of a polyester having a molecular weight from 350 to 1500 derived from the reaction of an acid or anhydride selected from succinic, glutaric or adipic acid or anhydride, or any mixture thereof, a polyethylene glycol having a molecular weight of from 175 to 225 and an aliphatic alcohol containing from 3 to 6 carbon atoms, said glycol and alcohol being reacted with the acid or anhydride in the theoretical amounts necessary to effect the reaction with the proviso that the glycol may be reacted with the acid or anhydride in amounts ranging from 0-10 mol % below the theoretical amount necessary to effect the reaction to up to 20% in excess of the theoretical amount and the alcohol may be reacted with the acid or anhydride in amounts ranging from 0 to 50 mol % below the theoretical amount to up to 20 mol % in excess of the theoretical amount needed to produce the final product.
2. A composition according to claim 1 in which the acid from which the polyester is derived is a mixture of succinic, glutaric and adipic acids with the approximate composition by weight of 21% succinic, 45% glutaric and 34% adipic acid.
3. A composition according to claim 1 in which the alcohol from which the polyester is derived is n-butyl alcohol or iso-butyl alcohol.
4. A composition according to claim 1 in which the polyester is derived from 4 moles of a mixture of adipic, glutaric and succinic acids having the approximate composition by weight of 21% succinic, 45% glutaric and 34% adipic acids, 3.59 moles of polyethylene glycol having a molecular weight of 200 and 1.28 moles of isobutanol.
5. A composition according to claim 1 in which the amount of polyester is from 40 to 80% by weight based on the weight of vinyl acetate polymer.
6. A composition according to claim 1 wherein the vinyl acetate component is a homopolymer.
7. A composition according to claim 1, in which the polyester is derived from a mixture of succinic, glutaric and adipic acids with the approximate composition by weight of 21% succinic, 45% glutaric and 34% adipic acid and the alcohol is n-butyl or iso-butyl alcohol.
Patent Citations (6)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2611756 | 1952-09-01 | Pockel | |
| US3149087 | 1964-09-01 | Anagnostopoulos | |
| US3250738 | 1966-05-01 | Isaacs | |
| BE522,931 | 1953-10-01 | ||
| CA560,036 | 1958-07-01 | ||
| UK734,115 | 1955-07-01 |
Non-Patent Literature (2)
- Koroly et al, Industrial and Engineering Chemistry, vol. 45, No. 5, May 1953, pp. 1060-1063.
- Bjorksten, "Polyesters and Their Applications," Reinhold Pub. Corp., New York, 1956, p. 162.