US 4,074,012 AGrant
Fine-Metal-Particle-Based Magnetic Recording Medium of Improved Environmental Stability
Issue Date:1978-02-14
•10 Claims
Abstract
Magnetic recording media having a magnetizable layer that comprises fine metal particles based on iron, cobalt, or nickel dispersed in a nonmagnetizable binder material have improved environmental stability because of the presence in the magnetizable layer of an organic compound that bears sterically unhindered aliphatic amine functionality.
Metadata
Assignee
- Minnesota Mining and Manufacturing Company
Inventors
- Duane G. Heikkinen
- Thomas M. Kanten
Application Information
Application Number:US 608916&
Filing Date:1975-08-29
Priority Date:1973-01-02
Art Unit:164
Classifications
IPC:
H01F 1002
Field of Search:
428252360427538;539;900;425;413;418;328;323;461;463;447;411;520;212;330;32962.54134128;132;127
Patent Drawings
This patent does not have any drawings.
Description
The invention is further illustrated by the following examples.
EXAMPLE 1
The following ingredients were charged to a small ball mill (a 51/2 fluid-ounce "Quickie" mill supplied by Gardner Laboratories) having 1/8-inch-diameter grind media.
These ingredients were mixed for 45 minutes in the mill, after which 4 parts of tris(dimethylamino methyl) phenol was added to the mill, and the contents milled for 3 minutes. Then 16.8 parts by weight of a 30-weight-percent-solids solution of a high-molecular-weight polyester polyurethane polymer synthesized from neopentyl glycol, poly-epsilon-caprolactone diol, and diphenyl methane diisocyanate dissolved in dimethyl formamide were added to the mill and the contents milled for an additional 10 minutes. The coating dispersion was completed by adding 4.2 parts of triisocyanate derivative of toluene diisocyanate and 1-di(hydroxymethyl) butanol to the mill, and milling the contents an additional 30 seconds.
Another coating dispersion was prepared to serve as a control by omitting the addition of tris(dimethylamino methyl) phenol.
Both dispersions were knife-coated onto 1-mil-thick polyethylene terephthalate films in a wet-thickness of 2 mils. The coatings were dried in air, then heated to 150.degree. F for five minutes, and then allowed to cure at room temperature for one day. Both samples were then subjected to an environment of 150.degree. and 80% relative humidity for 18 hours. The control sample had a large amount of visible corrosion over the entire recording surface after this exposure, whereas the sample of this invention did not show any visible sign of corrosion.
EXAMPLES 2-17
It has been found that corrosion in tape form can be indicated by coating a thin layer of grind paste (having a thickness of about 2 mils when dry) onto a glass plate and exposing the layer to an environment of 150.degree. F and 80% relative humidity for 30 minutes. The layer is then observed for corrosion, and the amount of corrosion observed after 30 minutes is this test generally indicates the amount of corrosion that will appear after about 18 hours in a dry coating of the final dispersion with binder material on a tape backing.
In each of the following examples, the grind paste contained 100 parts of the fine metal particles described in Example 1, 7 parts of the surfactant described in Example 1, 87 parts toluene, and 3.5 to 4 parts (as indicated below) of the aliphatic-amine-bearing organic compound listed for each example. The ingredients were mixed for 45 minutes in a small ball mill having 1/8-inch-diameter grind media and then coated on the glass plate.
EXAMPLES 18 and 19
The procedure of Examples 2-17 was repeated for two examples of the invention and for four comparative examples (Examples A-D). For some coatings in the comparative examples the fine metal particles did not carry a chromium-based outer layer; and for other coatings, the reaction product of tris-(dimethylamino methyl) phenol and 2-ethyl hexoic acid ("triquaternary salt" in the table below) was used as an additive instead of an aliphatic-amine-bearing compound. The additive was used in an amount of 4 weight-parts per 100 parts of pigment. The results are summarized below.
COMPARATIVE EXAMPLE E
A magnetic recording tape like that of the control tape in Example 1 was prepared except that instead of the phosphate ester dispersing agent, a quaternary amine dispersing agent was used. When the resulting tape was subjected to an environment of 150.degree. and 80% relative humidity for 18 hours, there was a large amount of visible corrosion on the recording surface.
EXAMPLE 20
A magnetic recording tape was prepared in the same manner described in Example 1 except that the tris(dimethyl-amino methyl) phenol was added to the phosphate ester surfactant in an amount equal to 4 weight-parts per 100 parts of the fine metal particles before the surfactant was added to the ball mill. After exposure of the tape for 18 hours at 150.degree. F and an 80% relative humidity, no corrosion of the tape was observed.
EXAMPLE 21
The procedure of Example 1 was repeated except that the amount of tris(dimethylamino methyl) phenol was varied from 1 to 7 weight-parts per 100 parts of the fine metal particles, and the samples were surface-treated in a conventional manner using a temperature of 185.degree. F and a pressure of 70 pounds per square inch. After 18 hours of exposure at 150.degree. F and 80% relative humidity, there was no corrosion for any of the samples.
EXAMPLES 22 and 23
The procedure of Example 1 was repeated except that different binder materials were added to the grind paste instead of the polyurethane-forming materials. In Example 22, 15.8 parts of a vinyl chloride-vinyl acetate copolymer (87 percent vinyl chloride and 13 percent vinyl acetate) and 5.2 parts of dioctylphthalate were used, and in Example 23, 13.6 parts of a diglycidyl ether of bisphenol A having an epoxide equivalent weight of about 190, 4.6 parts of an acrylonitrile-butadiene copolymer (15 weight-percent acrylonitrile), and 2.8 parts of methylene dianiline were used. In both examples no corrosion of the tape sample was observed after 18 hours of exposure at 150.degree. F and 80% relative humidity.
Claims
What is claim is:
1. Magnetic recording medium comprising a magnetizable layer carried on a nonmagnetizable support, the magnetizable layer comprising (a) a nonmagnetizable organic polymeric binder material; (b) fine magnetizable particles that comprise at least 75 weight-percent metal, at least a majority of which is iron, cobalt, or nickel, uniformly and thoroughly dispersed in the binder material; and (c) an organic compound having a molecular weight of less than 500 and providing, per gram of particles, at least 0.0001 gram-equivalent of sterically unhinered aliphatic tertiay amine which is located in terminal groups on the organic compound, is not reacted with said binder material and has a pK.sub.a of at least 8 when measured in an aqueous solution at 25.degree. C, whereby the recording medium exhibits improved resistance to corrosion of said magnetizable particles.
2. Magnetic recording medium of claim 1 in which the binder material comprises a polyurethane.
3. Magnetic recording medium of claim 1 in which the magnetizable layer further includes an acidic organic surfactant for assisting to disperse the particles.
4. Magnetic recording medium of claim 1 in which the particles carry a chromium-based outer layer formed prior to dispersion of the particles in the binder material.
5. Magnetic recording medium of claim 1 in which the aliphatic-amine-bearing oganic compound comprises tris-2,4,6-(dimethyl-amino methyl) phenol.
6. Magnetic recording medium of claim 1 which the particles constitute at least 70 weight-percent of the magnetizable layer.
7. Magnetic recording medium of claim 1 in which the aliphatic-amine-bearing organic compound is included in an amount providing, per gram of particles, at least 0.0003 gram-equivalent of sterically unhindered aliphatic amine having a pK.sub.a of at least 8 in an aqueous soluton at 25.degree. C.
8. Magnetic recording medium of claim 1 in which said organic compound is included in an amount of less than 0.07 gram/gram of particles included in the medium.
9. Magnetic recording medium of claim 1 in which at least 75 weight-percent of the metal in said particles is iron.
10. Magnetic recording medium of claim 8 in which said particles carry a chromium-based outer layer.
Patent Citations (10)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3148082 | 1964-09-01 | Ricco et al. | |
| US3474073 | 1969-10-01 | Higashi | |
| US3476596 | 1969-11-01 | Carroll | |
| US3546675 | 1976-12-01 | Che Chung Chou et al. | |
| US3554798 | 1971-01-01 | Nacci | |
| US3562011 | 1971-02-01 | Hirst et al. | |
| US3573979 | 1971-04-01 | Honjo | |
| US3837912 | 1974-09-01 | Roden | |
| UK1161068 | 1969-08-01 | ||
| UK1167527 | 1969-10-01 |