Smoke Retardant Vinyl Chloride and Vinylidene Chloride Polymer Compositions

Vinyl chloride and vinylidene chloride polymers are known to be self-extinguishing and relatively more flame retardant than other polymers such as polyethylene, polypropylene, and the like. However, a substantial amount of smoke may be produced upon exposure of vinyl chloride and vinylidene chloride polymers to a flame. The fact that an additive is a flame retardant does not necessarily mean that it will have good smoke retardant properties, as is well known to those killed in the art.

U.S. Pat. Nos. 3,821,151, 3,845,001, 3,870,679 and 3,903,028 teach use of certain copper, iron and/or molybdenum compounds as smoke retardants in PVC. New smoke retardant vinyl chloride and vinylidene chloride polymer compositions are desired.

Smoke retardant vinyl chloride and vinylidene chloride polymer compositions are obtained by including therein a synergistic mixture of (A) at least one melamine molybdate or substituted melamine molybdate, the melamine or substituted melamine having the formula ##STR1## wherein X is hydrogen or an alkyl, alicyclic, aralkyl, alkaryl, aryl or heterocyclic group containing from 1 to 10 carbon atoms of C, O, S and/or N, and with two X's on each of one or more nitrogen atoms optionally being joined together to form a heterocyclic ring; and (B) at least one compound selected from the group consisting of nickel oxide, nickel (II) oxalate, nickel (II) acetylacetonate and hydrates thereof.

Smoke retardant vinyl chloride and vinylidene chloride polymer compositions are obtained by including therein a synergistic mixture of (A) at least one melamine molybdate or substituted melamine molybdate and (B) at least one compound selected from the group consisting of nickel oxide, nickel (II) oxalate, nickel (II) acetylacetonate and hydrates thereof.

The additive melamine molybdate and substituted melamine molybdates (hereinafter called amine molybdates), and the selected nickel compounds, used in this invention may be polycrystalline or amorphous fine powders, preferably with an average particle size from about 0.01 to about 800 microns, more preferably from about 0.1 to about 200 microns, and even more preferably from about 0.1 to about 50 microns. The additives are used in smoke retardant amounts, typically from about 0.1 to about 20 parts by weight, per 100 parts by weight of polymer. The amount of each additive may constitute from about 1% to about 99% by weight, more preferably from about 10% to about 90% by weight, of the additive compound mixture. Supporting media such as SiO.sub.2, Al.sub.2 O.sub.3 and the like may be used for the smoke retardant additives and in many cases are preferred, since additive surface area is increased greatly for smoke reduction purposes.

Amine molybdates may be produced by reacting a suitable amine with a molybdenum compound such as MoO.sub.3, molybdic acid or a molybdenum salt. Molybdenum salts include ammonium molybdate, ammonium dimolybdate, ammonium heptamolybdate (also called ammonium paramolybdate), ammonium octamolybdate, sodium molybdate, or the like. Ammonium molybdates are preferred and include ammonium molybdate [(NH.sub.4).sub.2 MoO.sub.4 ] itself, ammonium dimolybdate [(NH.sub.4).sub.2 Mo.sub.2 O 7], ammonium heptamolybdate [(NH.sub.4).sub.6 Mo.sub.7 O.sub.24.sup.. 4H.sub.2 O], and ammonium octamolybdate [(NH.sub.4).sub.4 Mo.sub.8 O.sub.26.sup.. 5H.sub.2 O]. Sodium molybdate also is preferred. Excellent results were obtained using ammonium dimolybdate, ammonium heptamolybdate, sodium molybdate, and the commercial so-called "molybdic acid", which consists primarily of ammonium molybdates.

The reaction preferably is conducted in the presence of an acid in order to maximize the amine molybdate yield. Suitable acids include organic acids containing one to 12 carbon atoms such as formic acid, acetic acid, propionic acid, benzoic acid, and the like; and inorganic acids such as hydrochloric acid, nitric acid, suluric acid, and the like. Mixtures of acids may also be used. Excellent results were obtained using formic acid, acetic acid, benzoic acid, hydrochloric acid, nitric acid and sulfuric acid. The amount of acid used may be varied widely from 0 to 10 equivalents and more of acid per equivalent of ammonium or other cation in a particular molybdenum salt. About a 1/1 equivalent ratio is preferred.

Suitable reaction media include water, alcohols such as ethanol or the like, and water/alcohol mixtures. Reaction components may be mixed in any order. A preferred reaction method comprises adding an aqueous solution of an ammonium molybdate or other molybdenum salt to an amine solution in dilute hydrochloric acid, followed by refluxing the reaction mixture for 0.25 to 16 hours, more preferably for 0.25 to 4 hours. Another preferred reaction method comprises charging all reaction components essentially simultaneously to a reaction vessel, followed by refluxing as just described.

The reaction mixture is stirred continuously as a slurry. When the desired reaction time has passed, the mixture is cooled to about room temperature (25.degree. C.). The amine molybdate may be separated by filtration, centrifugation or the like and optionally washed with water, ethanol or a mixture thereof. The amine molybdate may be air dried at about 100.degree.-200.degree. C., or it may be vacuum dried at temperatures up to 150.degree. C. and higher. The amine molybdate is identifiable by means of infrared and x-ray diffraction spectroscopy.

Melamine and substituted melamines suitable for preparing melamine molybdate and substituted melamine molybdates have the formula ##STR2## wherein X is hydrogen or an alkyl, alicyclic, aralkyl, alkaryl, aryl or heterocyclic group containing from 1 to 10 atoms of C, O, S and/or N. Two X's on each of one or more nitrogen atoms may also be joined together to form a heterocyclic ring such as a morpholino group, for example as in 2,4,6-tri(morpholino)-1,3,5-triazine. Other examples of suitable substituted melamines include N,N',N"-hexaethylmelamine; 2-anilino-4-(2',4'-dimethylanilino)-6-piperidino-1,3,5-triazine; and 2,4,6-tri(N-methylanilino)-1,3,5-triazine. Melamine is preferred since melamine molybdate is both white and highly effective as a smoke retardant. Melamine molybdate also processes easily without discoloring the polymers.

Vinyl chloride and vinylidene chloride polymers used in this invention include homopolymers, copolymers and blends of homopolymers and/or copolymers. The vinyl chloride and vinylidene chloride polymers may contain from 0 to about 50% by weight of at least one other olefinically unsaturated monomer, more preferably from 0 to about 50% by weight of at least one other vinylidene monomer (i.e., a monomer containing at least one terminal CH.sub.2 =C< group per molecule) copolymerized therewith, even more preferably from 0 to about 20% by weight of such vinylidene monomer. Suitable monomers include 1-olefins containing from 2 to 12 carbon atoms, more preferably from 2 to 8 carbon atoms, such as ethylene, propylene, 1-butene, isobutylene, 1-hexene, 4-methyl-1-pentene, and the like; dienes containing from 4 to 10 carbon atoms including conjugated dienes as butadiene, isoprene, piperylene, and the like; ethylidene norbornene and dicyclopentadiene; vinyl esters and allyl esters such as vinyl acetate, vinyl chloroacetate, vinyl propionate, vinyl laurate, allyl acetate, and the like; vinyl aromatics such as styrene, .alpha.-methyl styrene, chlorostyrene, vinyl toluene, vinyl naphthalene, and the like; vinyl and allyl ethers and ketones such as vinyl methyl ether, allyl methyl ether, vinyl isobutyl ether, vinyl n-butyl ether, vinyl chloroethyl ether, methyl vinyl ketone, and the like; vinyl nitriles such as acrylonitrile, methacrylonitrile, and the like; cyanoalkyl acrylates such as .alpha.-cyanomethyl acrylate, the .alpha.,.beta.- and .gamma.-cyanopropyl acrylates, and the like; olefinically unsaturated carboxylic acids and esters thereof, including .alpha.,.beta.-olefinically unsaturated acids and esters thereof such as methyl acrylate, ethyl acrylate, chloropropyl acrylate, butyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, dodecyl acrylate, octadecyl acrylate, cyclohexyl acrylate, phenyl acrylate, glycidyl acrylate, methoxyethyl acrylate, ethoxyethyl acrylate, hexylthioethyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, glycidyl methacrylate, and the like, and including esters of maleic and fumaric acid, and the like; amides of the .alpha.,.beta.-olefinically unsaturated carboxylic acids such as acrylamide, and the like; divinyls, diacrylates and other polyfunctional monomers such as divinyl benzene, divinyl ether, diethylene glycol diacrylate, ethylene glycol dimethacrylate, methylene-bis-acrylamide, allyl pentaerylthritol, and the like; and bis(.beta.-haloalkyl)alkenyl phosphonates such as bis(.beta.-chloroethyl)vinyl phosphonate, and the like.

More preferred monomers include 1-olefins containing from 2 to 12 carbon atoms, more preferably from 2 to 8 carbon atoms, such as ethylene, propylene, 1-butene, isobutylene, 1-hexene, 4-methyl-1-pentene, and the like; vinyl esters and allyl esters such as vinyl acetate, vinyl chloroacetate, vinyl propionate, vinyl laurate, allyl acetate, and the like; olefinically unsaturated carboxylic acids and esters thereof, including .alpha.,.beta.-olefinically unsaturated acids and esters thereof such as methyl acrylate, ethyl acrylate, chloropropyl acrylate, butyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, dodecyl acrylate, octadecyl acrylate, cyclohexyl acrylate, phenyl acrylate, glycidyl acrylate, methoxyethyl acrylate, ethoxyethyl acrylate, hexylthioacrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, glycidyl methacrylate, and the like, and including esters of maleic and fumaric acid, and the like; and amides of .alpha.,.beta.-olefinically unsaturated carboxylic acids such as acrylamide, and the like.

The vinyl chloride and vinylidene chloride polymers may be prepared by any method known to the art such as by emulsion, suspension, bulk or solution polymerization. The additive compounds may be mixed with the polymer emulsion, suspension, solution or bulk mass before monomer recovery and/or drying. More preferably, the compounds may be mixed with dry granular or powdered polymers. The polymers and compounds may be mixed thoroughly in granular or powder form in apparatus such as a Henschel mixer, or the like. Alternatively, this step may be eliminated and the mixing done while the polymer mass is fluxed, fused and masticated to homogeneity under fairly intensive shear in or on a mixer apparatus having its metal surface in contact with the material. The fusion temperature and time will vary according to the polymer composition and level of additive compounds but will generally be in the range of about 300.degree. to 400.degree. F. and 2 to 10 minutes.

Smoke retardancy may be measured using an NBS Smoke Chamber according to procedures described by Gross et al, "Method for Measuring Smoke from Burning Materials", Symposium on Fire Test Methods -- Restraint & Smoke 1966, ASTM STP 422, pp. 166-204. Maximum smoke density (D.sub.m) is a dimensionless number and has the advantage of representing smoke density independent of chamber volume, specimen size or photometer path length, provided a consistent dimensional system is used. Percent smoke reduction is calculated using this equation: ##EQU1##

The term "D.sub.m /g" means maximum smoke density per gram of sample. D.sub.m and other aspects of the physical optics of light transmission through smoke are discussed fully in the above ASTM publication.

Smoke retardance may be measured quickly using the Goodrich Smoke-Char Test. Test samples may be prepared by dry blending polymer resin and smoke retardant additives. The blend is ground in a liquid N.sub.2 -cooled grinder to assure uniform dispersion of the smoke retardant additives in the resin. Small (about 0.3g) samples of the polymer blend are pressed into pellets about 1/4 inch in diameter for testing. Alternatively, test samples may be prepared by blending resin, smoke retardant additives and lubricant(s) or processing aid(s) in a blender such as an Osterizer blender. The blend is milled, pressed into sheets, and cut into small (about 0.3 gram) samples for testing. The test samples are placed on a screen and burned for 60 seconds with a propane gas flame rising vertically from beneath the samples. Sample geometry at a constant weight has been found not to be significant for the small samples used in this test. A Bernz-O-Matic pencil flame burner head is used with gas pressure maintained at about 40 psig. Each sample is immersed totally and continuously in the flame. Smoke from the burning sample rises in a vertical chimney and passes through the light beam of a Model 407 Precision Wideband Photometer (Grace Electronics, Inc., Cleveland, Ohio) coupled with a photometer integrator. Smoke generation is measured as integrated area per gram of sample.

The vinyl chloride and vinylidene chloride polymer compositions of this invention may contain the usual compounding ingredients known to the art such as fillers, stabilizers, lubricants, processing aids, impact modifying resins, plasticizers, antioxidants, and the like.

The following examples illustrate the present invention more fully.

Melamine molybdate having a 1/1 molybdenum/melamine molar ratio was prepared in a non-acid reaction medium as follows. 100 grams of melamine was dissolved in 2.5 liters of distilled water by heating to reflux in a 3-liter round-bottomed flask equipped with a watercooled condenser. 275.30 grams of ammonium heptamolybdate was dissolved in 1-liter of hot distilled water and then added to the first solution. A white precipitate formed immediately.

The reaction mixture was refluxed for 4 hours and thereafter filtered hot through Whatman No. 42 filter paper that was backed by a Macherey, Negel and Company (Duren, Germany) MN-85 filter paper supported on a Buchner funnel. A white solid was separated and washed with three 50 ml water portions and three 50 ml ethanol portions. The solid was dried for about 16 hours at 57.degree. C. and found to weigh 235.01 grams.

A white crystalline solid precipated from the filtrate after it stood overnight at room temperature. The precipitate was recovered and washed as just described. It was vacuum dried for 1 hour at 70.degree. C. and found to weight 10.70 grams. Infrared and x-ray diffraction spectroscopic analyses demonstrated that both solids were identical, i.e., both were melamine molybdate. Total product yield was 245.71 grams.

Examples 2-18 summarized in Table I illustrate the production of melamine molybdate having a 1/1 molybdenum/melamine molar ratio using the general reaction and recovery procedures of Example 1 in an aqueous medium.

Examples 19-39 summarized in Table II illustrate the production of melamine molybdate using the general reaction and recovery procedures of Example 1 in an aqueous HCl medium. The malamine molybdate produced in Examples 19-24 had a 1/1 molybdenum/melamine molar ratio. In Examples 26-39 the melamine molybdate produced had a 2/1 molybdenum/melamine molar ratio. The product in Example 25 was a mixture of the 1/1 and 2/1 molybdenum/melamine molar ratio melamine molybdates.

Melamine molybdate was prepared in the presence of formic acid as follows. 10 grams of melamine, 7.30 grams of formic acid, and 250 ml water were dissolved together by refluxing in a 500 ml. round-bottomed flask equipped with a stirrer and water-cooled condenser. 26.95 grams of ammonium dimolybdate was dissolved in 50 ml hot water and then added to the first solution. A white precipitate formed immediately.

The reaction mixture was refluxed for one hour and filtered hot as in Example 1. A white solid was recovered and washed three times with water. The solid weighed 29.25 grams after being vacuum dried for 3.25 hours at 120.degree. C.

Melamine molybdate was prepared in the presence of acetic acid as follows. 10 grams of melamine, 9.52 grams of acetic acid, and 250 ml water were dissolved together by refluxing in a 500 ml round-bottomed flask equipped with a stirrer and water-cooled condenser. 26.95 grams of ammonium dimolybdate was dissolved in 50 ml. hot water and then added to the first solution. A white precipitate formed immediately.

The reaction mixture was refluxed for 1 hour, cooled to room temperature (about 25.degree. C.), and filtered through Whatman No. 42 filter paper that was backed by a Macherey, Negel and Company (Duren, Germany) MN-85 filter paper supported on a Buchner funnel. A white solid was recovered and washed three times with water. The solid weighed 28.38 grams after being vacuum dried for 3 hours at 120.degree. C.

Melamine molybdate was prepared in the presence of benzoic acid as follows. 5 grams of melamine, 9.68 grams of benzoic acid, and 250 ml water were dissolved together by refluxing in a 500 ml round-bottomed flask equipped with a stirrer and water-cooled condenser. 13.47 grams of ammonium dimolybdate was dissolved in 25 ml hot water and then added to the first solution. A white precipitate formed immediately.

The reaction mixture was refluxed for one hour and filtered hot as in Example 1. A white solid was recovered and washed three times with water. The solid weighed 13.04 grams after being vacuum dried for 3 hours at 120.degree. C.

N,N',N"-hexaethylmelamine molybdate having a 2/1 molybdenum/N,N',N"-hexaethylmelamine molar ratio was prepared in the presence of HCl as follows. 10 grams N,N',N"-hexaethylmelamine, 6.69 grams of a 37 wt.% aqueous HCl solution, and 250 ml water were mixed together and heated to reflux in a 500 ml round-bottomed flask equipped with a stirrer and water-cooled condenser. 11.54 grams of ammonium dimolybdate was dissolved in 25 ml hot water and then added to the refluxing mixture. A bright yellow precipitate formed immediately.

The reaction mixture was refluxed for 20 minutes, cooled to room temperature, and filtered as in Example 41. A bright yellow solid was recovered and washed three times with water. The solid weighed 19.32 grams after being vacuum dried for 2.25 hours at 120.degree. C.

2-Anilino-4-(2',4'-dimethylanilino)-6-piperidino)-1,3,5-triazine is a substituted melamine having the formula ##STR3## 2-Anilino-4-(2',4'-dimethylanilino)-6-piperidino-1,3,5-triazine molybdate having a 2/1 molar ratio of molybdenum to substituted melamine was prepared in the presence of HCl as follows. 5 grams of the substituted melamine, 2.63 grams of a 37% aqueous HCl solution, 125 ml water and 160 ml ethanol were dissolved together by refluxing in a 500 ml round-bottomed flask equipped with a stirrer and water-cooled condenser. 4.54 grams of ammonium dimolybdate was dissolved in 10 ml hot water and then added to the first solution. An off-white precipitate formed immediately.

The reaction mixture was refluxed for 20 minutes, cooled to room temperature and filtered as in Example 41. An off-white solid was recovered and washed twice with a 50/50 by volume ethanol/water solution and twice with water. The solid weighed 8.22 grams after being vacuum dried for 2.5 hours at 120.degree. C.

2,4,6-Tri(N-methylanilino)-1,3,5-triazine is a substituted melamine having the formula ##STR4## 2,4,6-Tri(N-methylanilino)-1,3,5-triazine molybdate having a 2/1 molar ratio of molybdenum to substituted melamine was prepared in the presence of HCl as follows. 7 grams of substituted melamine, 3.48 grams of a 37 wt.% aqueous HCl solution, 75 ml water and 100 ml ethanol were dissolved together by refluxing in a 500 ml round-bottomed flask equipped with a stirrer and water-cooled condenser. 6 grams of ammonium dimolybdate was dissolved in 12 ml hot water and then added to the first solution. A yellow precipitate formed immediately.

The reaction mixture was refluxed for 1.25 hours, cooled to room temperature and filtered as in Example 41. A yellow solid was recovered and washed twice with water. The solid weighed 11.90 grams after being vacuum dried for 4.25 hours at 120.degree. C.

2,4,6-Tri(morpholino)-1,3,5-triazine is a substituted melamine having the formula ##STR5## 2,4,6-Tri(morpholino)-1,3,5-triazine molybdate having a 2/1 molar ratio of molybdenum to substituted melamine was prepared in the presence of HCl as follows. 3.50 grams of substituted melamine, 2.05 grams of a 37 wt.% aqueous HCl solution, 88 ml water and 88 ml ethanol were dissolved together by refluxing in a 500 ml round-bottomed flask equipped with a stirrer and water-cooled condenser. 3.50 grams of ammonium dimolybdate was dissolved in 8 ml hot water and then added to the first solution. A bright yellow precipitate formed immediately.

The reaction mixture was refluxed for 1 hour, cooled to room temperature and filtered as in Example 41. A yellow solid was recovered and washed twice with a 50/50 by volume ethanol/water solution and twice with water. The solid weighed 6.20 grams after being vacuum dried for 2.5 hours at 120.degree. C.

The following recipe was used:

Each experimental sample was prepared by milling the recipe materials on a two-roll mill for about 5 minutes at a roll surface temperature of about 320.degree. F. The milled samples were pressed into 6 .times. 6 .times. 0.025 inch sheets. Pressing was done at about 320.degree.-330.degree. F. using 40,000 lbs. of force applied to a 4-in. ram. The samples were given a 2 - 5 minute preheat prior to pressing for 8 minutes under full load.

The molded samples were cut into 27/8 .times. 27/8 .times. 0.025 inch sections. Testing was performed using the flaming mode of the NBS Smoke Chamber test (ASTM STP 422, pp. 166-204) described heretofore. Test results are given in Table III.

The test data in Table III demonstrates that the additive mixtures are synergistic and substantially retard smoke formation during burning of rigid polyvinyl chloride in the NBS Smoke Chamber (ASTM STP 442, pp. 166-204). The results also demonstrate the smoke retardant effects of individual additives in the same test.

The improved smoke retardant vinyl chloride and vinylidene chloride polymer compositions of this invention are useful wherever smoke resistance is desirable, such as in carpets, house siding, plastic components for airplane interiors, and the like. Of course, overall suitability for a particular use will depend upon other factors as well, such as comonomer type and level, compounding ingredient type and level, polymer particle size and the like.