Grafting Process for Preparing a Polyester Fabric Having Desirable Stain-Release, Antisoil-Redeposition, Antistatic and Hydrophilic Properties

This example illustrates the preparation of p-carboxycinnamic acid. ##STR2##

A mixture of 690 g. (6.6 moles) of malonic acid, 603 g. (3.68 moles) of methyl p-formyl benzoate, 7 ml. of piperidine and 890 ml. pyridine is stirred under a nitrogen atmosphere. The temperature is kept at 50.degree.-60.degree. C. during a period of 2 hours, and then at 70.degree.-75.degree. C. for 6 hours. The mixture is cooled and poured into a cold solution of 855 ml. of concentrated hydrochloric acid in 6700 ml. of water. The resulting while solid is removed by filtration, washed with water, and dried to give 735 g. (97%) of p-carbomethoxy cinnamic acid, melting point 241.degree.-244.degree. C.

This example illustrates the preparation of methyl p-carboxycinnamate. ##STR3##

A mixture of 40 g. of p-carbomethoxy cinnamic acid and 600 ml. of methanol is heated for 2 hours at 225.degree. C. in a stirred autoclave. The reaction mixture was filtered, and the resulting white solid was washed with methanol, sodium bicarbonate solution, and water and dried to give 27 g. (64%) of methyl p-carbomethoxy cinnamate, melting point 122.degree.-124.degree. C. Recrystallization from methanol gave material melting at 123.degree.-125.degree. C.

Anal. Calcd. for C.sub.12 H.sub.12 O.sub.4 : C, 65.45; H, 5.49. Found: C, 65.59; H, 5.60.

This example illustrates the preparation of textile fibers from a polyester prepared from P-carboxycinnamic acid.

Dimethyl terephthalate (77.6 g.; 0.4 mole), 20.6 g. (0.1 mole) of p-carbomethoxy cinnamic acid, 62.0 g. (1.0 mole) of ethylene glycol, 1.0 g. of an ethylene glycol solution containing soluble zinc acetate to give 65 ppm. Zn in the finished copolymer, 2.4 g. of an ethylene glycol solution containing soluble antimony acetate to give 230 ppm. Sb, and 0.1 ml. of titanium isopropoxide in butanol solution to give 15 ppm. Ti are placed in a reaction flask. The reaction mixture is heated under nitrogen atmosphere at 200.degree.-210.degree. C. for 2 hours. The theoretical volume of methanol is collected. The reaction temperature is then rapidly increased to 280.degree. C. The pressure is reduced to 0.2 mm. for a period of 1 hour. The reaction mixture is a viscous, clear melt. The copolymer is cooled to 25.degree. C. and the pressure released to a nitrogen atmosphere. The resulting polymer has a melting point of 200.degree.-205.degree. C. (by Fischer-John Hot Stage Melting Point apparatus) and an inherent viscosity of 0.74. Fibers can be drawn from the melt. These fibers are strong and can be drafted and further processed into textile fibers.

This example illustrates the preparation of textile fibers from a polyester prepared from p-carboxycinnamic acid.

The general conditions and quantities of Example 3 are followed except 90 g. (1.0 mole) of 1,4-butanediol is used as the dihydric alcohol, and 1.0 ml. of titanium isopropoxide in a butanol solution to give 150 ppm. titanium catalyst. The polycondensation step is carried out at 245.degree. C./0.2 mm for 1 hour. The resulting white copolymer has a T.sub.g of 42.degree. C. and an inherent viscosity of 1.07. Textile fibers are prepared from the polyester.

This example also illustrates the preparation of textile fibers from a polyester prepared from p-carboxycinnamic acid.

A mixture of 93 g. (0.48 mole) of dimethyl terephthalate, 4.4 g. (0.04 mole) of methyl-p-carbomethoxy cinnamate, 62 g. (1.0 mole) of ethylene glycol, 1.0 g. solution of an ethylene glycol containing soluble Sn(OAc).sub.2 to give 65 ppm. Sn, and 2.8 g. of an ethylene glycol solution containing soluble Sb(OAc).sub.3 to give 230 ppm. Sb is treated in the esterification step similarly to Example 3. The polycondensation step is carried out at 263.degree. C./0.2 mm. for 1 hour. A clear, viscous copolymer with an inherent viscosity of 0.55 results. Textile fibers are prepared from the polyester.

This example illustrates the process of the invention.

A fabric comprised of fibers prepared from a poly(ethylene terephthalate) modified with 4 mole percent p-carboxycinnamic acid is prepared. 1.0 g. of the fabric is heated for 15 minutes in 10 ml. of refluxing perchloroethylene containing 0.1 ml. of acrylic acid and 0.01 g. of lauroyl peroxide. The fabric was removed, scoured and dried.

This example illustrates the process of the invention.

1.0 g. of the fabric of Example 6 is padded with a solution of 1% lauroyl peroxide in perchloroethylene then suspended in perchloroethylene-acrylic acid vapor for 1 minute, removed, scoured and dried.

This example illustrates the properties of fabrics subjected to the process of the invention.

The fabric treated as in Example 6 is subjected to 20 cycles of the AATCC IVA wash test, then the AATCC Manhattan stain release test was applied. Stain-release ratings for the fabric are as follows: lipstick-5, liquid makeup-5, salad dressing-5, Wesson oil-5, gear lubricant-5. The highest possible rating is 5 on the scale of 1 to 5.

This example illustrates the properties of fabrics subjected to the process of the invention.

The fabric treated as in Example 6 is washed 10 times using the AATCC IVA wash test then subjected to a surface resistance test using a low-voltage, two electrode, D.C. technique under conditions of 23.degree.-25.degree. C. and 40% relative humidity. The fabric exhibits a surface resistance value of 3 .times. 10.sup.9 ohm./in..sup.2. A similar fabric not treated in accordance with the process of the invention exhibits a surface resistance value of 6 .times. 10.sup.12 ohm./in..sup.2.

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.