Flame Retardant Polycarbonate Composition

This invention is directed to a flame retardant polycarbonate composition and in particular an aromatic polycarbonate containing in admixture therewith a particular flame retardant additive which may be the metal salts of either mixtures of monomeric and polymeric aromatic sulfonesulfonates, or polymeric aromatic sulfonesulfonates.

With the increasing concern for safety, there is a positive move towards providing safe materials for public and household use. One particular area of need is that of providing flame resistant or flame retardant products for use by the ultimate consumer. As a result of this demand, many products are being required to meet certain flame retardant criteria both by local and federal government and the manufacturers of such products. One particular set of conditions employed as a measuring standard for flame retardancy is set forth in Underwriters' Laboratories, Inc. Bulletin 94. This Bulletin sets forth certain conditions by which materials are rated for self-extinguishing characteristics.

In the art, there are many known flame retardant additives which are employed by mixing with products to render such materials self-extinguishing or flame retardant. Such flame retardant additives have been known to be employed in amounts of 5 to 20 weight percent in order to be effective in extinguishing burning of those products which are combustible. It has also been found that such amounts can have a degrading effect upon the base product to be rendered flame retardant, resulting in the losses of valuable physical properties of the base product. This is particularly so when employing known flame retardant additives with the base product polycarbonate resins. Many of these known additives have a degrading effect upon the polymer.

It has now been surprisingly discovered that an aromatic polycarbonate can be made flame retardant by incorporating with the aromatic polycarbonate minor amounts of certain additives, which additives are inert and do not degrade the aromatic polycarbonate. The particular additive employed herein is unique in that even very minor amounts render the aromatic polycarbonate flame retardant. The amount of the additive employed herein can vary, preferably, from 0.01 to about 10 weight percent based on the weight of the aromatic polycarbonate.

More specifically, the particular additive of this invention is the metal salt of either mixtures of monomeric and polymeric aromatic sulfonesulfonates or polymeric aromatic sulfonesulfonates. The metal salt employed in the practice of this invention is either the alkali metal or alkali earth metal salt or mixtures of metal salts. The metals of these groups are sodium, lithium, potassium, rubidium, cesium, beryllium, magnesium, calcium, strontium and barium.

The aromatic sulfonesulfonates employed in the practice of this invention is a substituted or unsubstituted aromatic sulfonesulfonate wherein the substituent consists of an electron withdrawing radical. As employed herein and within the scope of this invention, any of the electron withdrawing radicals can be employed in the practice of this invention. However, preferably, the electron withdrawing radical or substituent employed in the practice of this invention is the halo-, nitro-, trihalomethyl and cyano electron withdrawing radicals or mixtures of these electron withdrawing radicals.

The electron withdrawing phenomenon, or as it is also referred to as electronegativity, is defined in Basic Principles of Organic Chemistry by Roberts and Caserio, 1964 (pages 185-186), and Physical Organic Chemistry by Jack Hine, McGraw-Hill Book Company, Inc. 1962 (pages 5, 32 and 85-93). Briefly, the electron withdrawing phenomenon is where the radical has a strong affinity for a negative charge, namely electrons, but still remains covalent and does not form an ion. This is an extremely brief description of this phenomenon and is merely set forth here to describe the electron withdrawing effect. Reference should be made to the texts set forth above.

In the practice of this invention, the types of aromatic sulfonesulfonates employed herein may be either mixtures of the monomeric form and the polymeric form or polymeric form. When first considering the monomeric form, the metal salt of the monomeric aromatic sulfonesulfonate can best be represented by the following formula:

wherein X is an electron withdrawing radical, M is a metal which may be selected from the periodic table of either an alkali metal or an alkali earth metal, and R' and R" may be either an aryl radical of 1-2 aromatic rings or an aliphatic radical of 1-6 carbon atoms and they may be the same or different. It is to be understood, however, that R' and R" together must contain at least one aromatic ring.

When the polymeric form of the aromatic sulfonesulfonate is employed in the practice of this invention, the polymer consists of at least 2 repeating units in the following formula:

in the above formula, B is an aromatic sulfone having the following formula: ##STR1## and A and C are dioxy radicals having 1-2 aromatic rings and may be independently selected from ##STR2## In the above formulae, M is a metal which may be either an alkali metal or an alkali earth metal, R is an alkylene or alkylidene radical of 1-10 carbon atoms and y is an integer of from 0-4 providing that the sum of y when employed in Formula II is at least 1. In the above formulae, X is a halo electron withdrawing radical. As shown, the polymeric form of the additive may or may not have an electron withdrawing radical and if it is employed, the electron withdrawing radical is only a halo radical. Also, in Formula II, m is 1 and n is an integer of from 0-20 and p is an integer from 2-200.

Also, in the practice of this invention, the above units of [AB] and [CB] can be randomly selected while the polymer structure can be either a copolymer, a random copolymer, a block copolymer or a random-block copolymer, or mixtures of these polymeric forms. In addition, the ratio of sulfonated aromatic rings to unsulfonated aromatic rings can vary from greater than 1 to 1 to as low as that which is necessary to render the polycarbonate flame retardant and this may be 1:100.

In the practice of this invention, there are many polymers that meet the requirements of Formula II above and which offer excellent flame retardant characteristics to an aromatic polycarbonate. The preferred polymeric additive employed in the practice of this invention has the following formula: ##STR3##

Another preferred polymeric additive employed in the practice of this invention is one containing an electron withdrawing radical and has the following formula: ##STR4##

Also mixtures of the above-described monomeric form and polymeric form are employed in the practice of the instant invention.

The compositions of the instant invention may contain fillers, pigments, dyes, antioxidants, stabilizers, ultraviolet light absorbers, mold release agents, etc.

In order to more fully and clearly illustrate the present invention, the following specific examples are presented. It is intended that the examples be considered as illustrative rather than limiting the invention disclosed and claimed herein. In the examples, all parts and percentages are on a weight basis unless otherwise specified.

Ninety-nine (99) parts of an aromatic polycarbonate, prepared by reacting 2,2-bis(4-hydroxyphenyl)propane and phosgene in the presence of an acid acceptor and a molecular weight regulator and having an intrinsic viscosity of 0.57 is mixed with 1 part of a finely ground dehydrated additive listed in Table 1 by tumbling the ingredients together in a laboratory tumbler. The resulting mixture is then fed to an extruder, which extruder is operated at about 265.degree. C., and the extrudate is comminuted into pellets.

The pellets are then injection molded at about 315.degree. C. into test bars of about 5 in. by 1/2 in. by about 1/16-1/8 in. thick. The test bars (5 for each additive listed in the Table) are subject to the test procedure set forth in Underwriters' Laboratories, Inc. Bulletin UL-94, Burning Test for Classifying Materials. In accordance with this test procedure, materials so investigated are rated either SE-O, SE-I or SE-II based on the results of 5 specimens. The criteria for each SE rating per UL-94 is briefly as follows:

"SE-0": Average flaming and/or glowing after removal of the igniting flame shall not exceed 5 seconds and none of the specimens shall drip flaming particles which ignite absorbent cotton.

"SE-I": Average flaming and/or glowing after removal of the igniting flame shall not exceed 25 seconds and the glowing does not travel vertically for more than 1/8 inch of the specimen after flaming ceases and glowing is incapable of igniting absorbent cotton.

"SE-II": Average flaming and/or glowing after removal of the igniting flame shall not exceed 25 seconds and the specimens drip flaming particles which ignite absorbent cotton.

In addition, a test bar which continues to burn for more than 25 seconds after removal of the igniting flame is classified, not by UL-94, but by the standards of the instant invention, as "burns". Further, UL-94 requires that all test bars in each test group must meet the SE type rating to achieve the particular classification. Otherwise, the 5 bars receive the rating of the worst single bar. For example, if one bar is classified as SE-II and the other four (4) are classified as SE-O, then the rating for all 5 bars is SE-II.

The results of the different additives within the scope of the instant invention are as follows with a control being the aromatic polycarbonate as prepared above without the additive of the type set forth herein. Seconds (Avg.) Per Test Bar Rating Remarks Polysodium salt of 3.6 0 SE-0 ##STR5## Polysodium salt of 4.8 0 SE-0 ##STR6## Polysodium salt of 3.3 0 SE-O ##STR7##

This Example is set forth to demonstrate the effect of the flame retardant additives of this invention at the lower limits of 0.01 weight percent based on the weight of the polymer composition.

In preparing the test bars for this Example, 99.99 parts of the polycarbonate of Example I is mixed with 0.01 weight percent of the additives listed in Table 2 employing the same procedure. Test bars are then molded using the same procedure employed in Example I. The test bars are subjected to the same test procedure of Example I with the following results: Seconds (Avg.) Per Test Bar Rating Remarks CONTROL 31.6 4+ Burns Polysodium salt of 7.2 4.0 SE-II ##STR8## Polysodium salt of 7.0 3.0 SE-II ##STR9##

This Example is set forth to demonstrate the effect of a mixture of flame retardant additives of this invention.

In preparing the test bars for this Example, 99.80 and 99.70 parts of the polycarbonate of Example I is mixed with 0.10 weight percent each of the monomeric and polymeric additive and 0.10 weight percent of the monomeric additive and 0.20 weight percent of the polymeric additive listed in Table 3, respectively, employing the same procedure. Test bars are then molded using the same procedure employed in Example I. The test bars are subjected to the same test procedure of Example I with the following results: Bar Rating Remarks CONTROL 31.6 4+ Burns Mixture of 0.10 weight percent of potassium salt of diphenyl-sulfone- 3-sulfonic acid and 0.1 weight percent of polypotassium salt of 5.8 0 SE-I ##STR10## Mixture of 0.20 weight percent of dipostassium salt of diphenyl- sulfone-3,3'-disulfonic acid and 0.1 weight percent of polypotassium salt of 4.9 0 SE-0 ##STR11##

This Example is set forth to show the effect of a known commercially available flame retardant additive.

Example I is repeated except that in place of the additives employed therein, only 1 part 1,2,5,6,9,10-hexabromocyclododecane is used herein. The results obtained upon evaluating five (5) test bars are the same as obtained for the Control shown in Table 1 above.

Part A. above is repeated but using 5 weight percent of the above additive, namely 1,2,5,6,9,10-hexabromocyclododecane. The results obtained are the same as obtained in Part A. above.

Part A. above is repeated but using 10 weight percent of the above additive, namely 1,2,5,6,9,10-hexabromocyclododecane. At this level of additive, test bars are rated SE-II. However, the polycarbonate is badly degraded as evidenced by severe dark streaking of the molded test bars, which degradation does not occur with the additives of the instant invention.

Example IV is repeated except that hexabromobiphenyl is employed herein. The results obtained are essentially the same as those of Example V.

Example IV is repeated except that the additive employed herein is a combination of antimony oxide and a material which is a mixture of polychlorinated biphenyl (Aroclor by Monsanto Company). The proportion of the ingredients of the additive employed in this example is based on 3 parts of chlorine per 1 part of antimony. The results obtained at 1 weight percent and 5 weight percent amounts are the same as in Example IV.

However, at the higher amount, namely 10 weight percent, a flame retardancy effect is noted, but with, again, severe degradation of the polycarbonate, as evidenced by the substantial reduction in the intrinsic viscosity of the molded test bars. As molded, the intrinsic viscosity os the test bars with 1 weight percent of the above additive is about 0.50. The intrinsic viscosity of the molded test bars containing 10 weight percent of the flame retardant additive of this Example is 0.253. This shows the severe degradation of the polycarbonate when employing this type of well known flame retardant.

In the practice of this invention, aromatic carbonate polymers are rendered flame retardant by the addition of certain particular additives which are the metal salts of substituted and unsubstituted mixtures of monomeric and polymeric aromatic sulfonesulfonates and polymeric aromatic sulfonesulfonates. The amount of the additives employed in the practice of this invention may vary from 0.01 to up to that amount which after further increasing of such an amount does not materially increase the flame retardant properties of the carbonate polymer. This is generally up to about 10 weight percent based on the weight of the aromatic carbonate polymer but may be higher. The amount of the additive to be employed can also be a function of the degree of flame retardancy desired.

It is not exactly understood how the additive of this invention functions or how such minor amounts can act as an effective flame retardant for the aromatic carbonate polymer. Analysis of the composition of this invention after being subjected to a fire temperature of about 600.degree. C. showed an unusually high percentage of remaining char. This leads one to hypothesize that the additive may act as a cross-linking agent when the aromatic carbonate polymer is subjected to fire temperatures. However, it is emphasized that this is only theory and should not be construed as actually occurring.

As indicated previously, the additive of the instant invention comprises the alkali or alkali earth metal salts of mixtures of monomeric and polymeric aromatic sulfonesulfonates and polymeric aromatic sulfonesulfonates. While a great number of such salts are set forth in the tables of the Examples of the instant invention, these are only a representative sample of the additives of this invention. The sodium, calcium, magnesium, potassium, strontium, lithium, barium, rubidium and cesium salts of other aromatic sulfonesulfonic acids can be employed in place of those of the Examples with the same effective flame retardancy being achieved.

In the practice of this invention, the additive is generally prepared by well known methods in the art. For example, one such well known method involves taking an aromatic sulfone such as diphenylsulfone and subjecting it to sulfonation using either sulfuric acid, chlorosulfonic acid, fuming sulfonic acid or sulfuric trioxide. These reactions can be carried out at room temperature or at elevated temperatures such as about 50.degree. C. The salt is then prepared by adding the proper alkaline reagent in sufficient amount to make the neutral salt. The salt is then recovered by precipitation or by distillation of the solvent.

In the case of a halo-electron withdrawing substituent, such as trifluoromethyl electron withdrawing substituent, it is best to start with the prepared trifluoromethyl aromatic sulfone and then sulfonate as above, as well as preparing the salt thereof.

In the practice of this invention, any of the aromatic polycarbonates can be employed herein. These are homopolymers and copolymers and mixtures thereof that are prepared by reacting a dihydric phenol with a carbonate precursor. Typical of some of the dihydric phenols that may be employed in the practice of this invention are bisphenol-A, (2,2-bis(4-hydroxyphenyl)propane), bis(4-hydroxyphenyl) methane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 4,4-bis(4-hydroxyphenyl)heptane, 2,2-(3,5,3',5'-tetrachloro-4,4'-dihydroxydiphenyl) propane, 2,2-(3,5,3',5'-tetrabromo-4,4'-dihydroxydiphenyl)propane, (3,3'-dichloro-4,4'-dihydroxyphenyl)methane. Other dihydric phenols of the bisphenol type are also available and are disclosed in U.S. Pat. Nos. 2,999,835, 3,028,365 and 3,334,154.

It is, of course, possible to employ two or more different dihydric phenols or a copolymer of a dihydric phenol with a glycol or with hydroxy or acid terminated polyester, or with a dibasic acid in the event a carbonate copolymer or interpolymer rather than a homopolymer is desired for use in the preparation of the aromatic carbonate polymers of this invention. Also employed in the practice of this invention may be blends of any of the above materials to provide the aromatic carbonate polymer.

The carbonate precursor may be either a carbonyl halide, a carbonate ester or a haloformate. The carbonyl halides which can be employed herein are carbonyl bromide, carbonyl chloride and mixtures thereof. Typical of the carbonate esters which may be employed herein are diphenyl carbonate, di-(halophenyl) carbonates such as di-(chlorophenyl) carbonate, di-(bromophenyl) carbonate, di-(trichlorophenyl) carbonate, di-(tribromophenyl) carbonates, etc., di-(alkylphenyl) carbonates such as di(tolyl) carbonate, etc., di-(naphthyl) carbonate, di-(chloronaphthyl) carbonate, phenyl tolyl carbonate, chlorophenyl chloronaphthyl carbonate, etc., or mixtures thereof. The haloformates suitable for use herein include bis-haloformates of dihydric phenols (bischloroformates of hydroquinone, etc.) or glycols (bishaloformates of ethylene glycol, neopentyl glycol, polyethylene glycol, etc.). While other carbonate precursors will occur to those skilled in the art, carbonyl chloride, also known as phosgene, is preferred.

Also included are the polymeric derivatives of a dihydric phenol, a dicarboxylic acid and carbonic acid. These are disclosed in U.S. Pat. No. 3,169,121 which is incorporated herein by reference.

The aromatic carbonate polymers of this invention may be prepared by employing a molecular weight regulator, an acid acceptor and a catalyst. The molecular weight regulators which can be employed in carrying out the process of this invention include monohydric phenols such as phenol, chroman-I, paratertiary-butylphenol, parabromophenol, primary and secondary amines, etc. Preferably, phenol is employed as the molecular weight regulator.

A suitable acid acceptor may be either an organic or an inorganic acid acceptor. A suitable organic acid acceptor is a tertiary amine and includes such materials as pyridine, triethylamine, dimethylaniline, tributylamine, etc. The inorganic acid acceptor may be one which can be either a hydroxide, a carbonate, a bicarbonate, or a phosphate of an alkali or alkaline earth metal.

The catalysts which are employed herein can be any of the suitable catalysts that aid the polymerization of bisphenol-A with phosgene. Suitable catalysts include tertiary amines such as for example, triethylamine, tripropylamine, N,N-dimethylaniline, quaternary ammonium compounds such as, for example, tetraethylammonium bromide, cetyl triethyl ammonium bromide, tetra-n-heptylammonium iodide, tetra-n-propyl ammonium bromide, tetramethylammonium chloride, tetramethyl ammonium hydroxide, tetra-n-butylammonium iodide, benzyltrimethylammonium chloride and quaternary phosphonium compounds such as, for example, n-butyltriphenyl phosphonium bromide and methyltriphenyl phosphonium bromide.

Also, included herein are branched polycarbonates wherein a polyfunctional aromatic compound is reacted with the dihydric phenol and carbonate precursor to provide a thermoplastic randomly branched polycarbonate.

These polyfunctional aromatic compounds contain at least three functional groups which are carboxyl, carboxylic anhydride, haloformyl or mixtures thereof. Examples of these polyfunctional aromatic compounds which may be employed in the practice of this invention include: trimellitic anhydride, trimellitic acid, trimellityl trichloride, 4-chloroformyl phthalic anhydride, pyromellitic acid, pyromellitic dianhydride, mellitic acid, mellitic anhydride, trimesic acid, benzophenonetetracarboxylic acid, benzophenonetetracarboxylic anhydride and the like. The preferred polyfunctional aromatic compounds are trimellitic anhydride or trimellitic acid, or their haloformyl derivatives.

Also included herein are blends of a linear polycarbonate and a branched polycarbonate.

It will thus be seen that the objects set forth above among those made apparent from the preceding description are efficiently attained and since certain changes may be made in carrying out the above process and in the composition set forth without departing from the scope of this invention, it is intended that all matters contained in the above description shall be interpreted as illustrative and not in a limiting sense.