US 4,012,478 AGrant
Method of Making Anti-Friction Members From Lubricant-Impregnated Polyamide Synthetic Resin Materials
Issue Date:1977-03-15
•11 Claims
•1 Drawing Sheets
Abstract
This invention relates to self-lubricating bearings or other anti-friction elements formed of a lubricant-containing polyamide. It can be manufactured in various shapes by molding a powdery mixture of the polyamide having a bulk factor of 2 - 5 with 2 - 12 wt % of a lubricant which is in a liquid state at a normal room temperature, are at a temperature between the room temperature and the polyamide melting temperature by the screw type injection or extrusion molding machine having controlled temperatures of the heating cylinders in the feed, the compressions, the metering, and the nozzle sections of the extruder.
Metadata
Inventors
- Masayuki Horikawa
- Yataro Takata
- Kikuo Sumiyoshi
Application Information
Application Number:US 3664260
Filing Date:1973-06-04
Priority Date:1967-12-29
Art Unit:147
Classifications
IPC:
B29B 110B29B 302B29F 302
Field of Search:
264260252176 R;329;21178 S;67 FP;18 N12
Patent Drawings (1 sheets)
Description
The foregoing and other objects, features and advantages of the present invention will become apparent from the following description when taken in conjunction with the accompanying drawing, in which:
FIG. 1 is a schematic vertical cross section of the heating cylinder of the molding machine designed for use in practicing the method of the present invention; and
FIG. 2 is a vertical cross section of the heating cylinder substantially taken along the line A--A of FIG. 1.
Referring to the drawings and particularly to FIG. 2, reference numeral 1 generally indicates the heating cylinder of the screw type molding machine; 2 indicates a hopper for feeding the molding materials; 4 a cooling device; 5 and 6 heaters; and 7 a nozzle. Obviously a driven propelling or feed screw, not shown, is received in the cylinder 1. Reference characters F, C, M and N indicate the feed, compression, metering and nozzle sections, respectively, of the heating cylinder.
The cooling device 4 includes an appropriate enclosed space 8 extending about the periphery of the feed section F of the heating cylinder and pump means (not shown) for circulation of cooling liquid or gas through the space 8. Arranged also about the periphery of the feed section F is heater means 5 which is outside of the cooling device 4 and particularly of space 8. The pump (not shown) and heater means 5 are selectively connected to a common electric power supply source through a changeover switch so that the heater means 5 remains disconnected as long as the pump means is held energized to keep the cooling device in action. Owing to such alternative heating and cooling arrangement, the feed section F of the heating cylinder can be controlled so as to maintain a predetermined relatively low temperature and the whole heating cylinder can be held at a predetermined temperature gradient rising toward the nozzle section N of the cylinder.
The temperatures of the compression, the metering and the nozzle sections of the heating cylinder except that of the feed section in the molding of the polyamide powder containing a lubricant are the same as those for polyamide powder not containing the lubricant.
Table 6 shows the relationship between the temperature of the feed section F of the heating cylinder and the time required to feed the molding material from the feed section to the head or nozzle section of a screw type injection molding machine of 3 ounces capacity, said molding material being prepared by mixing 5 wt % of SAE No. 120 cylinder oil with 95 wt % of 6-nylon having the bulk factor of 4.30.
Generally speaking, in the screw type injection molding machine of 3 ounces capacity, the heating cylinder of the feed section is 200.degree. C .+-. 5.degree. C and the time (seconds) required to feed the molding material from the feed section to the head section is preferable to be 10 - 35 seconds in the industrial scale production of the molded article of 6-nylon not containing any lubricant.
As shown in the Table 6, it is necessary to maintain the temperature of the feed section at 110.degree.- 160.degree. C to obtain the time required for feeding the molding material of 8 - 35 seconds to manufacture the bearings or antifriction elements of this invention.
If said temperature is more than 160.degree. C, the molding material of 6-nylon containing the lubricant will not be able to be molded on an industrial scale since a longer time; namely 35 - 250 seconds than that suitable for molding 6-nylon is consumed. While if said temperature is too low, namely less than 110.degree. C, it will be difficult to transfer the molding material from the feed section to the head section of the molding machine thereby consuming much time to transfer and also requiring about 30% excess of power than that necessary to molding the polyamide not containing any lubricant. The temperatures of the compression, metering and nozzle sections of the heating cylinder except that of the feed section in the molding of the polyamide powder containing 2 - 12 wt % of lubricant are the same or less than those of polyamide molding material not containing the lubricant.
Table 7 shows the preferably temperature distribution at various parts of the heating cylinder of said injection or extrusion molding machine.
It is preferable to use as short a time, for example, 10 - 35 sec., as possible to feed the molding material from the feed section to the head secion of the molding machine, while the molding material of the polyamide containing the lubricant is not able to be molded at a temperature of the feed section of more than 200.degree. C, as shown in Table 6.
Therefore, it is an essential matter to maintain the temperature of the feed section of the heating cylinder to a low temperature and is preferable to have a short feed time, for example, of 8 - 35 sec. as shown in table 6, so as to feed the molding material to the head section smoothly.
It was observed that the time of more than several ten seconds (for example 35 - 250 sec. as shown in Table 6) required to feed the molding material from the feed section to the head section of the molding molding brings not only a lowering of the work efficiency but also a heat deterioration of the material in the heating cylinder. Also the temperature of the heating cylinder in the feed section suitable for a polyamide not containing any lubricant, makes the feed of the molding of the invention impossible.
It is preferable to select the temperature of the heating cylinder in the feed section to that of lower than 75%, especially about 50% of the melting point of the polyamide used and to control the temperature of the heating cylinder in the section except the feed section to about the same temperature or less than the molding temperature of the polyamide not containing the lubricant.
Thus is has been found that the lubricant-contained molded articles suitable for the bearings or other antifriction elements in which the lubricant is uniformly dispersed as finely divided particles separated from each other can be manufactured.
It is to be noted that lubricant-contained molded articles made according to the present invention do not lose their lubricant content even when heated and that during molding, further oil impregnation may be effected in a sintered bearing article but any further oil impregnation can not be effected if tried in the molded articles of the invention since said oil dsperses into the polyamide powder as independent and unlinked oil particles.
Some examples of practicing the present invention will be described.
Example
92 weight % of a polyamide (6-nylon) powder having the bulk factor of 4.3 was mixed with 8 weight % of SAE No. 120 cylinder oil forming a dry loose mixture. From this mixture, tubular oil-contained molded articles were produced by use of a screw type injection molding machine having its heating cylinder temperature controlled to 120.degree. .+-. 3.degree. C in the feed section, 210.degree. .+-. 3.degree. C in the compression section, and 230.degree. .+-. 3.degree. C in the metering and nozzle sections of the cylinder.
The bearing performances of the molded articles are shown in Table 5, Specimen No. 5.
It will be understood that a suitable mold can be connected to the nozzle section of the extrusion machine or that the nozzle 7 can be changed to form a product such as a tube. Such extruded tube can be cut into articles to provide the molded bearing or equivalent production.
While several complete embodiments of the invention have been disclosed herein, it will be appreciated that modification of these particular eembodiments of the invention may be resorted to without departing from the scope of the invention.
Claims
What is claimed is:
1. A method of making bearings or other antifriction elements by plasticating a lubricant-contained polyamide comprising polyamide and about 2 - 12 wt. % of a mineral oil lubricant in relation to the total weight of the material uniformly dispersed therein which lubricant is in a liquid state at a normal room temperature, comprising the steps of uniformly mixing at room temperature a polyamide powder having a bulk factor of 2 - 5 so that an increased amount of lubricant may be added, said polyamide selected from the class consisting of nylon-6 having a melting point of from 215.degree. to 220.degree. C and an average molecular weight of about 45,000, nylon 6-6 having a melting point of about 255.degree. C and an average molecular weight of about 45,000, nylon -11 having a melting point of from 184.degree. to 185.degree. C and an average molecular weight of about 40,000 and nylon -12 having a melting point of 175.degree. to 177.degree. C at an average molecular weight of about 45,000, molding the resultant molding composition to article form under heat and pressure by use of a screw type injection or extrusion molding machine, controlling the temperature of the feed section of the machine to that of about 50 - 75 % of the crystalline melting point of the polyamide, the temperature of said feed section of said machine ranges from 80.degree. to 150.degree. plus or minus 3.degree. C, said machine having a compression section, the temperature in said compression section ranging from 175 to 225 plus or minus 3.degree. C, said machine having a metering section, the temperature in said metering section ranging from 192.degree. to 265.degree. plus or minus 3.degree. C, said machine having a nozzle section, the temperature in said nozzle section ranging from 190.degree. to 230.degree. plus or minus 3.degree. C so that an article is provided in which the lubricant oil is uniformly dispersed.
2. A method of making bearings or other antifriction elements as claimed in claim 1 characterized by the step of uniformly mixing a small quantity up to 3 wt % of a soap as an additive, and a small quantity up to 5 wt % of an additive from the group consisting of graphite, and MoS.sub.2 and 80 - 98 wt % of the said polyamide powder having a bulk factor of 2 - 5 and containing about 2-12 wt % of lubricant, and molding the resultant composition into an antifriction element.
3. A method as in claim 1 and including the step of selecting the polyamide from the group consisting of polymerization-condensation products of di-carborylic acid and diamine, and a polymerization product of a lactam of amino-carboxylic acid.
4. A method as claimed in claim 1 and including forming the article without any bleeding of the oil from the oil-polyamide mixture.
5. A method as in claim 1 and including the step of using 2 to 5 parts of oil with a polyamide having a bulk factor of 2-3; up to 8 parts of oil with a bulk factor polyamide of 3 - 4; and up to 12 parts of oil with a polyamide having a bulk factor of 4 - 5.
6. A method of making bearings or by plasticating according to claim 1 wherein the mixing time of the material in the feed section is from 8 to 35 seconds.
7. A method of making bearings by plasticating according to claim 1, wherein said polyamide is nylon -6, said feed section temperature is 120.degree. plus or minus 3.degree. C, said compression section temperature is 210.degree. plus or minus 3.degree. C, said metering section temperature is 230.degree. plus or minus 3.degree. C and said nozzle section temperature is 230.degree. plus or minus 3.degree. C.
8. A method of making bearings by plasticating according to claim 1, wherein said polyamide is nylon 6-6, said feed section temperature is 150.degree. plus or minus 3.degree. C, said compression section temperature is 225.degree. plus or minus 3.degree. C, said metering section temperature is 265.degree. plus or minus 3.degree. C and said nozzle temperature is 265.degree. plus or minus 3.degree. C.
9. A method of making bearings by plasticating according to claim 1, wherein said polyamide is nylon -11, said feed section temperature is 90.degree. plus or minus 3.degree. C, said compression section temperature is 184.degree. plus or minus 3.degree. C, said metering section temperature is 200.degree. plus or minus 3.degree. C and said nozzle temperature is 200.degree. plus or minus 3.degree. C.
10. A method of making bearings by plasticating according to claim 1, wherein said polyamide is nylon -12, said feed section temperature is 70.degree. plus or minus 3.degree. C, said compression section temperature is 175.degree. plus or minus 3.degree. C, said metering section temperature is 190.degree. plus or minus 3.degree. C and said nozzle temperature is 190.degree. plus or minus 3.degree. C.
11. A method of making bearings by plasticating according to claim 1, wherein said mineral oil is selected from the class consisting of cylinder oil and synthetic lubricant oil.
Patent Citations (16)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2246086 | 1941-06-01 | Austin | |
| US2374069 | 1945-04-01 | Balthis | |
| US2698966 | 1955-01-01 | Stott et al. | |
| US2855377 | 1958-10-01 | Stott | |
| US3079338 | 1963-02-01 | Caubet | |
| US3146287 | 1964-08-01 | Kleine-Albers | |
| US3164563 | 1965-01-01 | Maxwell et al. | |
| US3297808 | 1967-01-01 | Pflueger | |
| US3484399 | 1969-12-01 | Kakos | |
| US3679788 | 1972-07-01 | Kiyono et al. | |
| US3755221 | 1973-08-01 | Hitch | |
| BE683,232 | 1966-12-01 | ||
| BE683,233 | 1966-12-01 | ||
| UK889,403 | 1962-02-01 | ||
| UK1,102,851 | 1968-02-01 | ||
| UK1,102,852 | 1968-02-01 |
Non-Patent Literature (2)
- "Buyers Guide to Engineering Thermoplastics," In Plastics Technology, vol. 12, No. 10, Oct. 1966, pp. 32, 45-54.
- Bernhardt; Ernest C., Edt. "Processing of Thermoplastic Materials," New York, Reinhold, c 1959, pp. 154-165.