US 4,011,361 AGrant
Fluoropolymer Coating Compositions Having Improved Adhesion
Issue Date:1977-03-08
•21 Claims
Abstract
Compositions containing fluoropolymer, colloidal silica, the salt of a polyamide acid, a coalescing agent and a liquid carrier are useful for priming metal, especially cookware, before topcoating it with a fluoropolymer enamel.
Metadata
Assignee
- E. I. Du Pont de Nemours and Company
Inventors
- Eustathios Vassiliou
- Thomas P. Concannon
Application Information
Application Number:US 588005&
Filing Date:1975-06-18
Priority Date:1975-06-18
Art Unit:164
Classifications
IPC:
B32B 2700C08G 5124C08J 148
Field of Search:
428260427422;327;407;435;458;33129.6 F;857 L;857 UN;29.2 N388;409
Patent Drawings
This patent does not have any drawings.
Description
BACKGROUND OF THE INVENTION
In recent years, the use of fluoropolymers as lubricious coatings has become widespread. Cookware coated with polytetrafluoroethylene (PTFE) has become especially popular because of its non-stick character.
The physical nature of fluoropolymers makes it difficult to bond them well enough to substrates to prevent coatings of such polymers from blistering and peeling away during use. This is especially true of PTFE.
SUMMARY OF THE INVENTION
It has now been found that the adhesion of a fluoropolymer coating to its substrate can be significantly improved if a composition of
A. fluoropolymer,
B. a binder comprising colloidal silica and the amine salt of a polyamide acid,
C. a coalescing agent, and
D. a liquid carrier
Is used to prime the substrate before the fluoropolymer topcoat is applied.
DETAILED DESCRIPTION OF THE INVENTION
The fluoropolymers used in the compositions of the invention are homopolymers and copolymers (meaning the polymer contains two or more different monomer units) of monoethylenically unsaturated hydrocarbon monomers completely substituted with fluorine atoms or completely substituted with a combination of fluorine atoms and chlorine atoms. Included in this group are perfluorolefin polymers such as polytetrafluoroethylene (PTFE) and copolymers of tetrafluoroethylene and hexafluoropropylene in all monomer unit weight ratios, fluorochlorocarbon polymers such as polymonochlorotrifluoroethylene, and the normally solid copolymers of tetrafluoroethylene and perfluoroalkyl vinyl ethers (wherein the alkyl group is of 1-5 carbon atoms). Mixtures of these can also be used. PTFE is preferred for its thermal stability.
The fluoropolymer used is particulate. The particles are preferably small enough to pass through the nozzle of a spray gun without clogging it and are also small enough to give the resulting film integrity.
The fluoropolymer should have a number average molecular weight of at least about 20,000, for a polymer with a molecular weight of less than this tends to be waxy and unsuited for use. The number average molecular weight is preferably at least 200,000. Number average molecular weight of PTFE is measured by the method described by Suwa, Takehisa and Machi in Journal of Applied Polymer Science, Volume 17, pp. 3253-3257 (1973). The number average molecular weight of a tetrafluoroethylene/hexafluoropropylene coplymer is measured by first determining its melt flow rate (MFR) according to ASTM D2116, using the MFR to determine melt viscosity (MV) according to the equation ##EQU1## AND THEN DETERMINING MOLECULAR WEIGHT (MW) according to the equation Number average molecular weight of a fluorochlorocarbon polymer is measured by ASTM D1430.
Although a powder of fluoropolymer can be used and a carrier provided separately, a polymer in the form of an aqueous dispersion is preferred for its stability and because it is most easily obtained in that form. Dispersions of fluoropolymers in organic liquids such as alcohols, ketones, aliphatic or aromatic hydrocarbons, or mixtures of these, can also be used. In either case, the liquid generally serves as the carrier for the composition.
The fluoropolymer is ordinarily present in the composition at a concentration of about 10-90% preferably about 60-80%, by weight of the total of fluoropolymer and binder (as will be defined later).
The binder in the compositions of the invention comprises a colloidal silica and the amine salt of a polyamide acid. This binder is ordinarily present in the composition at a concentration of about 10-90%, preferably about 20-40%, by weight of the total of fluoropolymer and binder.
The colloidal silica component of the binder can be any of those which air-dries to form a continuous film when laid down by itself. Such silicas are generally provided in the form of aqueous sols containing about 30-50% of colloidal silica.
Illustrative of the colloidal silica sols which can be used are those sold by E. I. duPont de Nemours and Company as
The preferred colloidal silica sol is "Ludox AM". This product is a sodium stabilized colloidal silica having a pH of about 9 at 25.degree. C., and a silica content (calculated as SiO.sub.2) of 30%, whose particles are surface-modified with aluminum and have a particle diameter of 13-14 millimicrons and a specific surface area of 210-230 square meters per gram.
Mixtures of colloidal silicas can also be used.
The colloidal silica is ordinarily present in the binder at a concentration of about 5-95%, preferably about 20-80%, by weight of the binder.
The polyamide acid salt component of the binder can be any of those described in copending application Ser. No. 546,998, filed on Feb. 4, 1975, by Thomas P. Concannon. The portions of that application which describe these polyamide acid salts and how they are made are incorporated into this application by reference.
Generally speaking, the polyamide acid salts used in the compositions of the invention are those of polyamide acids with tertiary amines.
The polyamide acids can be represented by the structure ##STR1## where G is hydrogen or a carboxyl group; .fwdarw. denotes isomerism;
R is a tetravalent organic radical containing at least two carbon atoms, no more than two carbonyl groups of each polyamide acid unit being attached to any one carbon atom of said tetravalent radical;
R.sub.1 is a divalent radical containing at least two carbon atoms, the amide groups of adjacent polyamide acid units each being attached to separate atoms of said divalent radical; and
n is a number large enough to give the polyamide acid an inherent viscosity of at least 0.1, measured as a 0.5% solution in N,N-dimethyl acetamide at 30.degree. C.
These polyamide acids are neutralized with stoichiometric amounts of tertiary amines to give the amine salts.
The amine salts of polyamide acids preferred for use in the binder component are those prepared from at least one amine represented by the structure
H.sub.2 N - R.sub.1 - NH.sub.2
and at least one acid anhydride represented by the structure ##STR2## where, in both structures, R and R.sub.1 are as previously defined, neutralized with a stoichiometric amount of a tertiary amine.
The amine salts of polyamide acids especially preferred for use in the binder component are those prepared from
1. meta- or para-phenylenediamines, bis(4-aminophenyl)ether, benzidine, 2,2-bis(4'-aminophenyl) propane, bis(4-aminophenyl)methane, bis(4-aminophenyl)sulfone, bis(4-aminophenyl) sulfide or 1,6-hexamethylenediamine;
and
2. pyromellitic dianhydride, trimellitic anhydride 2,2-bis(3',4'-dicarboxyphenyl)propane dianhydride, or bis(3,4-dicarboxyphenyl)ether dianhydride, neutralized with a stoichiometric amount of trimethylamine, triethylamine, dimethylethanolamine, diethyl 2-hydroxyethylamine, tributylamine, tris(2-hydroxyethyl)amine, ethyl bis(2-hydroxyethyl) amine, N,N-dimethylaniline, morpholine, pyridine, N-methylpyrrole, or mixtures of these.
The polyamide acid salt most preferred for use in the binder component is one prepared from (bis(4-aminophenyl) methane and trimellitic anhydride, neutralized with a stoichiometric amount of a 2/1 weight ratio mixture of triethylamine and diethyl 2-hydroxyethylamine.
The amine salt is ordinarily present in the binder at a concentration of about 5-95%, preferably about 20-80%, by weight of the binder.
The coalescing agent used in the composition of the invention is, generally speaking, an organic liquid which can dissolve the polyamide acid amine salt used. Organic liquids of this type are highly polar and have boiling points above 100.degree. C. Illustrative are
N-methylpyrrolidone
dimethylformamide
dimethylacetamide
dimethylsulfoxide
cresylic acid
sulfolane
and
formamide.
The coalescing agent preferred for use because of its availability and low toxicity is N-methylpyrrolidone.
The coalescing agent is ordinarily present in the compositions of the invention at a concentration of about 10-90% by weight of the polyamide acid amine salt used, preferably about 30-50%.
The compositions of the invention will have more workable viscosities at higher solids content if they contain about 15-200%, preferably about 80-150%, by weight of the polyamide acid amine salt used, of a viscosity reducing agent which is an organic liquid whose solubility parameter, .delta..sub.T, falls within the range of 10-21.6 and which is miscible with water. A definition of solubility parameter appears in Kirk-Othmer, "Encyclopedia of Chemical Technology", second edition (1963), pages 889-896. Total solubility parameter, T, has the following component parameters:
where the equation
describes the relationship of the components to the total solubility parameter.
Illustrative of such viscosity reducing agents are furfuryl alcohol, 1-butanol, 2-propanol, ethylene glycol monoethyl ether, triethylene glycol, formic acid, and mixtures of these. Furfuryl alcohol is preferred for its effectiveness.
The compositions of the invention can also contain such conventional additives as pigments, flow control agents, surfactants and plasticizers as are necessary or seem desirable. These additives are added for the usual reasons, in the usual ways and in the usual amounts.
The amount of total solids in the coating compositions will be governed by the substrate to which the compositions are to be applied, the method of application, the curing procedures, and like factors. In the usual case, the composition will contain about 10-80%, by weight, of solids.
The compositions can be made by simply mixing together appropriate amounts of the proper components. Pigments can be added, if this is desired, by first conventionally preparing a suitable pigment dispersion and then adding this dispersion to the composition.
The resulting compositions can be applied by spraying, brushing, roller-coating, dipping, or by electrodeposition. If the substrate is metal, this is preferably pretreated by grit blasting, by the flame spraying of metals or metal oxides, or by frit-coating, although the compositions can also be applied to phosphated and chromated metals. If the substrate is glass, it is preferably first grit-blasted or frit-coated.
A composition of the invention is ordinarily applied to a thickness of about 2-15 microns (dry) and is then air-dried. This primer coat is then topcoated with a conventional clear or pigmented fluoropolymer enamel, and baked in the usual way to give an adherent fluoropolymer coating.
Although the best coating is obtained with the twocoat system just described, a strongly adherent fluoropolymer coating can be obtained with a one-coat operation. To do this, a coat of a composition of the invention is applied to a thickness of 5-50 microns (dry). This coat is then air-dried and baked at a temperature high enough to fuse the fluoropolymer used.
The compositions of the invention are most useful for priming metal cookware, especially frypans, before coating them with PTFE, but the compositions can also be used to prime other articles requiring tightly bonded fluoropolymer coatings. These other articles can be made of glass or any other material capable of withstanding the baking temperatures used. For example, the compositions can be used to prime or coat bearings, valves, wire, metal foil, boilers, pipes, ship bottoms, oven liners, iron soleplates, waffle irons, ice cube trays, snow shovels and plows, chutes, conveyors, dies, tools such as saws, files and drills, hoppers and other industrial containers and molds.
The following examples illustrate the invention. In these examples, all parts and percentages are by weight unless indicated otherwise.
EXAMPLE 1
The following were added to a vessel in the order stated and mixed:
The resulting composition was sprayed on a gritblasted aluminum pan to a thickness of 5 microns (dry) and then air-dried. The pan was then topcoated by spraying it with "Teflon" enamel-Classic White 455.102 (sold by E. I. duPont de Nemours and Company) to a thickness of about 100 microns (dry), baking it for 15 minutes at 95.degree. C., raising the baking temperature to 425.degree. C., and then removing the pan from the oven.
The resulting coating is strongly adherent to the pan.
EXAMPLE 2
The following were added to a vessel in the order stated and mixed:
The resulting composition was applied to a fritcoated aluminum pan, topcoated and then cured as in Example 1, with substantially the same results.
Claims
We claim:
1. A coating composition comprising a. about 10%-90%, by weight of the total of (a) and (b) solids, of a particulate polymer of monoethylenically unsaturated hydrocarbon monomers completely substituted with fluorine atoms or a cominbation of fluorine atoms and chlorine atoms, the polymer having a number average molecular weight of at least 20,000; b. about 10%-90%, by weight of the total of (a) and (b) solids, of a binder which comprises 1. about 5-95%, by weight of the total of (1) and (2) solids, of a colloidal silica which air-dries to form a continuous film when laid down by itself, and 2. about 5-95%, by weight of the total of (1) and (2) solids, of a salt of a polyamide acid represented by the structure ##STR3## where G is hydrogen or a carboxyl group; .fwdarw. denotes isomerism; R is a tetravalent organic radical containing at least two carbon atoms, no more than two carbonyl groups of each polyamide acid unit being attached to any one carbon atom of each tetravalent radical; R.sub.1 is a divalent radical containing at least two carbon atoms, the amide groups of adjacent polyamide acid units each being attached to separate atoms of said divalent radical; and n is a number large enough to give the polyamide acid an inherent viscosity of at least 0.1, measured as a 0.5% solution in N,N-dimethylacetamide at 30.degree. C.; neutralized with a stoichiometric amount of a tertiary amine; c. about 10-90%, by weight of the polyamide acid amide salt, of N-methyl pyrrolidone, dimethyl formamide, dimethylacetamide, dimethysulfoxide, cresylic acid, sulfolane or formamide; and d. a liquid carrier.
2. The composition of claim 1 additionally containing about 15-200% of an organic liquid, miscible with water, having a solubility parameter of about 10-21.6, the parameter having a dispersion component of about 7-10, a polar component of about 2-11 and a hydrogen bonding component of about 7-14, where the equation .delta.T.sup.2 =.delta.D.sup.2 .delta.P.sup.2 .delta.H.sup.2 describes the relationship of the components to the total solubility parameter.
3. The composition of claim 2 wherein the organic liquid is furfuryl alcohol, 1-butanol, 2-propanol, ethylene glycol monomethyl ether, triethylene glycol, formic acid, or a mixture of these.
4. The composition of claim 1 wherein the colloidal silica is a sodium stabilized colloidal silica.
5. The composition of claim 1 wherein the salt of the polyamide acid is one prepared from at least one amine represented by the structure and at least one acid anhydride represented by the structure ##STR4## where, in both structures, R and R.sub.1 are as defined in claim 1, neutralized with a stoichiometric amount of tertiary amine.
6. The composition of claim 5 wherein the salt of a polyamide acid is one prepared from a. meta- or para-phenylene diamine, bis(4-aminophenyl) ether, benzidine, 2,2-bis(4'-aminophenyl)propane, bis(4-aminophenyl)methane, bis(4-aminophenyl) sulfone, bis(4-aminophenyl)sulfide or 1,6-hexamethylenediamine, and b. pyromellitic dianhydride, trimellitic anhydride 2,2-bis(3',4'-dicarboxyphenyl)propane dianhydride or bis(3,4-dicarboxyphenyl) ether dianhydride, neutralized with a stoichiometric amount of a tertiary amine.
7. The composition of claim 1 wherein the fluorocarbon polymer is PTFE.
8. The composition of claim 1 wherein the carrier is water.
9. The composition of claim 1 wherein a. the fluorocarbon polymer is PTFE; b. the colloidal silica is a sodium stabilized colloidal silica; c. the salt of a polyamide acid is one prepared from trimellitic anhydride and bis(4-aminophenyl) methane, neutralized with a 2/1 weight ratio combination of triethylamine and diethyl 2-hydroxy ethylamine; and d. the liquid carrier is water.
10. The composition of claim 8 additionally containing about 15-200%, of furfuryl alcohol.
11. An article bearing a primer coat of the composition of claim 1, topcoated with a fused fluoropolymer enamel.
12. An article bearing a primer coat of the composition of claim 2, topcoated with a fused fluoropolymer enamel.
13. An article bearing a primer coat of the composition of claim 3, topcoated with a fused fluoropolymer enamel.
14. An article bearing a primer coat of the composition of claim 4, topcoated with a fused fluoropolymer enamel.
15. An article bearing a primer coat of the composition of claim 5, topcoated with a fused fluoropolymer enamel.
16. An article bearing a primer coat of the composition of claim 6, topcoated with a fused fluoropolymer enamel.
17. An article bearing a primer coat of the composition of claim 7, topcoated with a fused fluoropolymer enamel.
18. An article bearing a primer coat of the composition of claim 8, topcoated with a fused fluoropolymer enamel.
19. An article bearing a primer coat of the composition of claim 9, topcoated with a fused fluoropolymer enamel.
20. An article bearing a primer coat of the composition of claim 10, topcoated with a fused fluoropolymer enamel.
21. In a method for improving the adhesion of a fluoropolymer coating to its substrate, the improvement comprising priming the substrate, before the fluoropolymer coating is applied, with a composition according to claim 1.
Patent Citations (7)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US2961341 | 1960-11-01 | Long | |
| US2979418 | 1961-04-01 | Dipner | |
| US3655604 | 1972-04-01 | Strolle | |
| US3661831 | 1972-05-01 | Fang | |
| US3663728 | 1972-05-01 | Hoback | |
| US3694392 | 1972-09-01 | Werner | |
| US3787338 | 1974-01-01 | Skelly |