US 4,006,097 AGrant
Yb Activated Hafnium Oxide Phosphor and Methods of Making
Issue Date:1977-02-01
•2 Claims
Abstract
A phosphor composition having the general formula HfO.sub.2 :Yb with ytterbium being present in an amount of from 0.005 to 0.10 moles per mole of hafnium is disclosed. The phosphor can be prepared from the mixed oxides or from the oxalates, carbonates, or hydroxides by precipitating the latter from an aqueous solution. Firing takes place under a reducing atmosphere, preferably nitrogen, to reduce the ytterbium to the plus 2 ion. The phosphor is a bright green emitter under ultraviolet, x-radiation and cathode ray excitation.
Metadata
Assignee
- GTE Sylvania Incorporated
Inventor
- Paul V. Kelsey, Jr.
Application Information
Application Number:US 5742757
Filing Date:1975-05-05
Priority Date:1974-09-24
Art Unit:113
Classifications
IPC:
C09K 1146
Field of Search:
252301.4 R;301.4 F
Patent Drawings
This patent does not have any drawings.
Description
Background of the Invention
This invention relates to synthetic inorganic phosphors. More particularly, the invention relates to compounds of ytterbium activated hafnium oxide which emit light in the green region of the spectrum under excitation with suitable radiation. This radiation includes both long and short wavelength ultraviolet x-radiation and cathode rays.
Phosphors are known products of commerce. Generally, the term is employed in the art to describe luminescent or fluorescent solids which comprise two essential ingredients: a host matrix; and an activator. Such phosphors are employed in color cathode ray tubes, fluorescent lamps, x-ray tubes and both high pressure and low pressure mercury vapor lamps.
It would be an advance in the art to discover new materials which would be useful in the above applications.
Objects and Summary of the Invention
Accordingly, it is an object of this invention to provide such a phosphor.
It is a further object of the invention to provide methods for making such phosphors.
These objects are accomplished in one aspect of the invention by the provision of compounds of ytterbium activated hafnium oxide.
Description of the Preferred Embodiments
For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims.
Referring now to the invention with greater particularity, therein is herein provided a new, bright green-emitting phosphor having the general formula HfO.sub.2 :Yb with ytterbium being present in an amount of from 0.005 to 0.10 moles per mole of hafnium. In the preferred embodiment the ytterbium is approximately 0.025 mole per mole of hafnium.
The following non-limiting examples are illustrative of the methods of preparation.
Example I
The phosphor can be prepared by forming mixtures of hafnium oxide and ytterbium oxide in proportions to yield 0.005 to 0.10 moles of ytterbium oxide for each mole of hafnium oxide. As noted above, the preferred embodiment employs 0.025 moles Yb/mole Hf. The well mixed oxides are fired in a controlled atmosphere furnace with a nitrogen atmosphere for 6 hours at 1000.degree. C, remortared and fired at 1250.degree. C for 6 hours, also in nitrogen. A controlled atmosphere furnace is one which is closed to the outside air so that the firing atmosphere can be more closely controlled. The resulting phosphor has a green emission under both 2537A and 3650A ultraviolet radiation, x-radiation and under cathode ray bombardment.
During the processing it is believed that the Yb.sup.+.sup.3 is reduced to Yb.sup.+.sup.2 ; however, it is not known for certain whether this reduction takes place. Also, it is not known what position the Yb occupies in the HfO.sub.2 matrix.
Example Ii
20 g HfOCl.sub.2 . 8H.sub.2 O
0.25 g Yb.sub.2 O.sub.3
1 ml 70% HNO.sub.3
200 ml H.sub.2 O
7.0 g oxalic acid (H.sub.2 C.sub.2 O.sub.4 . 2H.sub.2 O)
An aqueous solution of 20 g HfOCl.sub.2 . 8H.sub.2 O and 0.25 Yb.sub.2 O.sub.3 with 1 ml HNO.sub.3 added is heated and stirred constantly at a temperature of 70.degree. C until a clear solution is obtained. The HNO.sub.3 is added to solubilize the Yb.sub.2 O.sub.3 ; the HfOCl.sub.2 being soluble in H.sub.2 O. Add a precipitating agent such as the aqueous solution of oxalic acid (7 g) which causes a white precipitate to form. Filter the precipitate and dry in an electric oven at about 110.degree. C. To aid in filtering, it is advisable to add approximately 3 g of sodium acetate to the solution before filtering. The dried oxalate is then first fired in a controlled atmosphere furnace with a nitrogen atmosphere at 980.degree. to 1000.degree. C for 2 hours and second fired at 1200.degree. to 1250.degree. C for 2 hours.
Example Iii
The procedure as in Example II except (NH.sub.4).sub.2 CO.sub.3 is employed in place of the oxalic acid. The firing time remains the same.
Example Iv
The procedure as in Example II except NH.sub.4 OH is used in place of the oxalic acid. The firing time remains the same.
It will be seen from the above that there is herein provided a new and useful phosphor as well as novel methods of preparing the same.
While there have been shown and described what are at present considered the preferred embodiments of the invention, it will be apparent to those skilled in the art that various changes and modifications may be made herein without departing from the scope of the invention as defined by the appended claims.
Claims
What is claimed is:
1. A method of making a phosphor composition having the general formula HfO.sub.2 :Yb with Yb being present in an amount of from 0.005 to 0.10 moles per mole of hafnium which comprises the steps of: forming a substantially homogeneous mixture of appropriate amounts of the oxides of hafnium and ytterbium to yield the desired formulation; firing said mixture in a controlled atmosphere furnace under a nitrogen atmosphere for about 6 hours at about 1000.degree. C; and mortaring said fired mixture and refiring in a nitrogen atmosphere at about 1250.degree. C for about 6 hours.
2. A method of making a phosphor composition having the general formula HfO.sub.2 :Yb with Yb being present in an amount of from 0.005 to 0.10 moles per mole of hafnium which comprises the steps of: forming an aqueous solution of appropriate amounts of HfOCl.sub.2.8H.sub.2 O and Yb.sub.2 O.sub.3 ; adding a sufficient amount of HNO.sub.3 to said solution to solubilize said Yb.sub.2 O.sub.3 and heating and stirring constantly at a temperature of about 70.degree. C until a clear solution is obtained; adding a precipitating agent selected from the group consisting of oxalic acid, ammonium carbonate, and ammonium hydroxide to form a precipitate; filtering and drying said precipitate; and first firing said precipitate in a controlled atmosphere furnace with a nitrogen atmosphere at about 980.degree. C to 1000.degree. C for about 2 hours and second firing said precipitate in said furnace at about 1200.degree. C for 2 hours.
Patent Citations (4)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3322682 | 1967-05-01 | Thompson | |
| US3338841 | 1967-08-01 | Brixner | |
| US3449259 | 1969-06-01 | Ropp | |
| UK1,208,565 | 1970-10-01 |
Non-Patent Literature (4)
- Iwase et al. "Chem. Abstracts" vol. 61, 1964, p. 6545e.
- Calgerova et al. "Chem. Abstracts" vol. 79, 1973, p. 59486x.
- Kroger "Some Aspects of the Luminescence of Solids", Elseveviar Pub. Co., 1948, p. 298.
- Kroger et al. "Chem. Abstracts", 1954, p. 3150b.