US 3,974,131 AGrant
Aziridine Monomers and Copolymers
Issue Date:1976-08-10
•7 Claims
Abstract
A group of new monomers containing aziridinyl functionality as well as unsaturated carbon to carbon bonds are synthesized by addition of alkylenimine to propenic acid esters of polyhydroxy compounds in controlled quantities. The monomers readily form copolymers with other monomers and find use as adhesion promoters in vinyl formulations.
Metadata
Assignee
- Sybron Corporation
Inventors
- Joseph Emil Puskas
- William J. Shibe, Jr.
- William Wood
Application Information
Application Number:US 5501660
Filing Date:1975-02-14
Priority Date:1975-02-14
Art Unit:144
Classifications
IPC:
C08F22034C08F22602
Field of Search:
26045080.72;86.1 N725;723
Patent Drawings
This patent does not have any drawings.
Description
BACKGROUND OF THE INVENTION
This invention relates to a new group of monomer compounds containing aziridinyl group substituted esters; its derivatives and the method of their production.
OBJECTS OF THE INVENTION
It is the object of the invention to provide a novel aziridinyl monomer, as a building block for homopolymers and copolymers. It is another object of the invention to provide a method for preparing aziridinyl monomer, copolymers and homopolymers.
It is still another object of the invention to provide an adhesion promoter for vinyl formulations to enable them to bond to other substrates, without discoloring the vinyl compound under heat.
It is a further object of the invention to provide a reactive monomer having aziridinyl functionality.
It is still further object of the invention to provide an aziridinyl monomer which could be copolymerized with acrylic acid ester monomers, methacrylic acid ester monomers and other monomers.
BRIEF SUMMARY OF THE INVENTION
These objects are accomplished in accordance with the invention by the provision of unsaturated aziridinyl esters of the following general formula: ##STR1## R.sub.1 -- hydrogen or C.sub.1-5 alkyl group R.sub.2 -- hydrogen or C.sub.1-5 alkyl group
R.sub.3 -- hydrogen or C.sub.1-5 alkyl group
R.sub.4 -- hydrogen or C.sub.1-5 alkyl group
R.sub.5 -- hydrogen or C.sub.1-5 alkyl group
R.sub.6 -- hydrogen or C.sub.1-5 alkyl group
x = 1, 2, or 3
y = 1, 2, or 3
x + y = 2 to 4
Other objects and further scope of applicability of the present invention will become apparent from the detailed description given hereinafter; it should be understood however that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.
DESCRIPTION OF THE INVENTION
Bestian in U.S. Pat. No. 2,596,200 describes a compound containing aziridinyl group. The compound is made by the addition of .alpha..beta.-alkylenimines to .alpha..beta.-olefin carboxylic acid esters of polyhydric alcohols and is saturated. To ensure saturation and to cause a faster reaction excess of alkylenimine is added. An important feature of the present invention lies in adding alkylenimine to propenic acid esters of polyhydroxy compounds in such controlled quantity so as to maintain the end product unsaturated by not reacting all the vinyl groups in the ester. This resulting product is a monomer containing both an aziridinyl group as well as unsaturated carbon to carbon bonds.
The monomers of this invention are prepared by Michael's addition of alkylenimine to one or more of the vinyl groups available in various propenic acid esters of polyhydroxy compounds. The number of moles of alkylenimine added to the ester is always one or more less than the number of propenic acid groups present.
The propenic acid esters may be prepared from various glycols or polyhydroxy compounds of the following structure: A. R.sub.x C(CH.sub.2 OH).sub.4.sub.-x Where x = 0, 1, 2 R = lower alkyl where C is 1 through 5 B. HO (CH.sub.2 CHO) H Rx Where x = 1 - 10 R = H, lower alkyl C. HO (CH.sub.2 CH) OH Rx x = 1 to 6 R = lower alkyl, H
The propenic acid utilized may have the following structure: ##STR2## Where R is H or lower alkyl R.sub.1 is H or lower alkyl
The alkylenimine utilized in the preparation of novel monomers have the following general structure: ##STR3## R.sub.1 through R.sub.4 is hydrogen or lower alkyl radical.
The aziridinyl monomers of the general formula are used as building blocks. With other monomers they form comonomers which are polymerized and find use as adhesion promoters. Suitable material for use as monomers among others include: butyl acrylate, ethyl acrylate, isobutyl acrylate, ethyl methacrylate, butyl methacrylate, isobutyl methacrylate, isodecyl methacrylate, lauryl methacrylate and tridecyl methacrylate. However the invention is not limited to the use of acrylic acid esters and methacrylic acid esters only. Other comonomers which may effectively be utilized are vinyl acetate, acrylamide, methacrylamide, methacrylonitrile, acrylonitrile, vinyl toluene, .alpha.-methyl styrene, and styrene. Copolymers containing aziridinyl monomer in the range of about 5 to 60% by weight are found more suitable as adhesion promoters. Percentages of aziridinyl monomer less than about 5% do not possess adhesion promoting properties and precentages over about 60% are uneconomical.
BRIEF DESCRIPTION OF PREFERRED EMBODIMENT:
The advantages of the improved adhesion properties of aziridinyl compounds will become apparent upon consideration of the following disclosure of the invention; especially when taken in conjunction with the accompanying examples wherein Example 1-8 show preparation of various monomers conforming to the general formula using different glycols. Examples 9-12 show preparation of copolymers with the aziridinyl monomers of this invention. Example 13 shows the use of this copolymer as adhesion promoter.
EXAMPLE 1
Preparation of Aziridinyl Monomer
Trimethylol propane bis-2-(1-aziridinyl) propionate mono acrylate is prepared by the addition of 2 mol ethylenimine to 1 mol of trimethylol propane triacrylate. ##STR4## x = 1 y = 2 x + y = 3 Glycol: Trimethylolpropane, imine = ethylenimine
0.5 mol (148 gms) trimethylol propane triacrylate and 90 gms. Dioxane is charged into a 500 ml 3-neck flask fitted with agitator, thermometer, addition funnel and condenser. The reaction is cooled to 20.degree.C. and 1 mol (43 gms) ethylenimine is added dropwise, keeping the temperature below about 30.degree.C with a cooling bath. The addition requires about 40 minutes after which the cooling bath is removed and the reaction allowed to exotherm to a max. of 35.degree.C., then heated to about 58.degree.-60.degree.C. over about 1 hour. The reaction is cooled to room temperature. The yield of product calculated from aziridine titration is 67%.
EXAMPLE 2
Preparation of trimethylol ethane (mono-2-aziridinyl 1-methyl propionate)dimethacrylate ##STR5## x = 2, y = 1, x+y = 3 glycol = trimethylolethane
imine: ethyleneimine
0.5 mole (162g) trimethylol ethane trimethacrylate and 90 g dioxane is charged into a 500 ml 3-neck flask described in example 1. The flask is cooled to 20.degree.C and 0.5 mole (21.5 g) ethylenimine is added dropwise over 40 minutes keeping the reaction temperature below 30.degree.C. After the ethylenimine addition is completed, the temperature is permitted to rise to 35.degree., and when the exotherm subsides, the temperature is raised over approximately one hour period to 60.degree.C. The batch is then cooled. The yield of product calculated from aziridine titration 99%.
EXAMPLE 3
Preparation of pentaerythritol (di-2-aziridinyl-2-methyl propionate)monocrotonate ##STR6## x = 1, y = 3, x+y = 4 glycol: pentaerythritol
imine: ethylenimine
0.25 mole (102 g) pentaerythritol tetracrotonate and 52 g dioxane is charged into equipment described in Example 1. The solution is neutralized with a few drops of triethylamine. One gram of sodium methylate is added and then 0.83 mole (35.5 g) ethylenimine (10% excess) added dropwise over 30 minutes. No temperature increase will be obtained. After the ethylenimine addition is completed, the reaction temperature is raised to 65.degree.C and maintained for 9 hours. The batch temperature is then lowered to 60.degree.C, and vacuum applied (100 mm Hg) for 15 minutes to remove excess ethylenimine. The yield of product calculated from aziridine titration, 81%.
EXAMPLE 4
Preparation of pentaerythritol diacrylate di-2-aziridinyl propionate ##STR7## x = 2, y = 2, x+y = 4 glycol = pentaerythritol
imine = ethylenimine
0.25 (88 g) pentaerythritol tetraacrylate and 50 g dioxane is charged into equipment described in Example 1. The solution is cooled to 25.degree.C. and 0.5 moles (21.5 g) ethylenimine is added dropwise over 30 minutes keeping the temperature at 40.degree.C. The reaction temperature is raised to 70.degree.C over 35 minutes and maintained for 3 hours. The batch is then cooled. The yield of product calculated from aziridine titration, 70%.
EXAMPLE 5
Preparation of diethylene glycol monoacrylate mono-2-aziridinyl propionate ##STR8## x = 1, y = 1, x+y = 2 glycol = diethylene glycol
imine = ethylenimine
0.5 moles (107 g) diethylene glycol diacrylate and 50 g benzene is charged into equipment described in Example 1. The solution is cooled to 20.degree.C. and 0.5 moles (21.5 g) ethylenimine is added dropwise over 30 minutes. The reaction temperature is maintained between 25.degree.-30.degree.C. After all the ethylenimine had been added, the reaction temperature is maintained at 30.degree.C for 1 hour. The temperature is then raised to reflux (80.degree.C) and held for 2 hours. The benzene is removed by distillation at 80.degree.C under 100 mm mercury. The product is cooled and clarified from a small amount of white precipitate by filtration. The yield of product calculated from aziridine titration, 91.5%.
EXAMPLE 6
Preparation of tripropylene glycol monomethacrylate mono-2-aziridinyl 1-methyl propionate ##STR9## x = 1, y = 1, x+y = 2 glycol = tripropylene glycol
imine = propylenimine
0.5 mol (164 g) of tripropylene glycol dimethacrylate 0.5 mol (28.5g) propylenimine and 2 gms of sodium methoxide are utilized and the abovementioned compound prepared by the same process as in the Example 5. The yield of product calculated from aziridine titration, 80%.
EXAMPLE 7
Preparation of hexylene glycol monoacrylate mono-2-aziridinyl propionate ##STR10## x = 1, y = 1, x+y = 2 glycol = hexylene glycol
imine = propylenimine
0.5 moles (113.5 g) of hexylene glycol diacrylate and 0.5 moles (28.5) of propylenimine are utilized and the abovementioned compound prepared by the same process as in example 5. The yield of product calculated from aziridine titration, 90%.
EXAMPLE 8
Preparation of dipropylene glycol monomethacrylate mono-2-aziridinyl-1-methyl propionate ##STR11## x = 1, y = 1, x+y = 2 Glycol = propylene glycol
imine = ethylenimine
0.5 moles (106 g) of propylene glycol dimethacrylate 0.5 moles (21.5 g) ethylenimine and 2 gms of sodium methoxide are utilized and the abovementioned compound prepared by the same process as in example 5. The yield of product calculated from aziridine titration, 82%.
EXAMPLE 9
Preparation of Copolymers
The copolymer is prepared in a 2000 cc resin kettle equipped wit heating mantle, condenser, thermometer, nitrogen purge inlet, and Teflon (Trademark for polytetrafluoroethylene made by duPont) bladed stirrer.
The nitrogen purging is started, agitator speed set at 160 rpm, and the batch temperature raised to 90.degree.C. The following mixture of monomers is then added over a two hour period.:
The reaction temperature is maintained at 90.degree.C., and when the addition of the delayed monomers is completed, the following are added:
An hour later 1 gram of AIBN is added. Another hour later, the temperature is lowered to 85.degree.C., and approximately 28 inches vacuum applied till all volatile matter at this temperature is removed.
EXAMPLE 10
Preparation of copolymer using cellosolve acetate as solvent in place of DIDP.
The equipment used is the same as in example 9.
The CO.sub.2 purging is started, agitator speed set at 160 rpm, and the batch temperature raised to 90.degree.C. The following mixture of monomers is then added over a two hour period:
The reaction temperature is maintained between 90.degree.-95.degree.C. and when the addition of the delayed monomers is completed, the following are added:
Half an hour later one gram AIBN is added followed by 1.5 g. AIBN another half hour later.
EXAMPLE 11
Preparation of copolymer using xylene as solvent in place of DIDP.
A 500 ml reactor is used equipped in the same manner as the one in example 10.
Polymerization is carried out in the same manner as in Example 2 except the following monomer mix is used:
When the addition of delayed monomers is completed, eight grams of, aziridinyl product of example 1 and 0.5g. AIBN are added. An hour later, the batch is cooled.
EXAMPLE 12
Preparation of copolymer using high ratio of aziridinyl monomer to acrylates
The procedure is exactly the same as for example 10 except the delay charge and chaser monomer are modified as follows:
Thus, Example 9 shows that aziridinyl monomers can be copolymerized with other vinyl monomers. Examples 10 and 11 illustrate the use of different solvents, and the example 12 shows that higher aziridinyl ratio can be used.
Alternate solvents which may be utilized in the copolymerization include esters, ethers, ketones, aliphatic, and aromatic solvents. Specific examples for each group are cellosolve acetate, dioxane, cyclohexanone, xylene, hexane, and toluene. These solvents are unreactive organic solvents having boiling point of at least 90.degree.C or higher.
In the preferred embodiment the aziridinyl monomer trimethylol propane bis-2-(1-aziridinyl) propionate monoacrylate (preparation shown in example 1) is copolymerized with other acrylate monomers as shown in Example 13.
EXAMPLE 13
A polymer is prepared as 27% solids solution in diisodecylphthalate (DIDP) as it is used as an adhesion promoter in this form.
The product is prepared in a 500 cc resin kettle equipped with heating mantle, condenser, thermometer, nitrogen purge inlet, and Teflon bladed stirrer.
The nitrogen purging is started, agitation set at 180 rpm, and batch temperature raised to 90.degree.C. When the batch temperature reaches 90.degree.C, the following monomers are added over 2.5 hours:
The reaction temperature is maintained at 90.degree.C and held there 1.25 hours after the delay is added. 5g of aziridinyl monomer of example 1 is then added and 90.degree.C maintained for an hour. The batch is cooled to 80.degree.C, approximately 28 inches vaccum applied for one hour during which time a small amount of N.sub.2 is leaked through the system, and then cooled. A clear solution with very slight haze is obtained.
From experience it is found that in order to obtain proper distribution of the functional monomer, the monomers had to be delayed. It is also learned that the residual monomers may be reduced by adding a small portion of the functional monomer after the delayed portion of the monomers are added to the reactor. The final product is vacuum stripped to remove the dioxane which is in the aziridinyl monomer. The final product contained 0.6% total residual monomers.
The adhesion promoting properties of a copolymer containing aziridinyl monomer are tested by incorporating such copolymer in a polyvinylchloride (PVC) powder coating formula such as follows:
A dryblend powder mix of the above formula is made in a blender and cooled. The vinyl coating mix freshly prepared as well as one aged 6 weeks at room temperature are applied to Bonderite 37 treated steel panels for adhesion testing and color development on heating. The coatings are cured at 450.degree.F for 5 minutes. Adhesion is measured on the Dillon Universal Testing Machine by the 180.degree. peel test (ASTM D903-49). Heat stability is measured by the degree of color development in coatings observed at 10-minute time intervals at 350.degree.F. Variations of the dryblend vinyl coating formula containing different amounts of copolymer, from 0 to 9 gms keeping amounts of other ingredients constant are tested. It is concluded that addition of aziridinyl based copolymers improves adhesion of PVC powder to steel and that adhesion increases with increasing amount of copolymer in the formula and the vinyl compound is not discolored. Tests are conducted with vinyl plastisols which confirm the same results.
All these aziridine monomers and copolymers have utility as adhesion promoters.
Thus, it should be appreciated that the present invention accomplishes its intended objects in providing a unique aziridinyl monomer which by itself and on copolymerizing with other monomers acts as an adhesion promoter. Although specific components proportions and procedures have been stated in the above description of the preferred embodiments of the novel adhesion promoting compound, other suitable materials and procedures such as those described above may be employed to synergize, enhance or otherwise modify the novel method. Other modifications and ramifications of the present invention would appear to those skilled in the art upon a reading of this disclosure. These are intended to be included within the scope of this invention.
Claims
We claim:
1. A copolymer composition comprised of free radical polymerized aziridinyl monomer of the following structure: ##EQU1## R.sub.1 -- hydrogen or C.sub.1-5 alkyl group R.sub.2 -- hydrogen or C.sub.1-5 alkyl group R.sub.3 -- hydrogen or C.sub.1-5 alkyl group R.sub.4 -- hydrogen or C.sub.1-5 alkyl group R.sub.5 -- hydrogen or C.sub.1-5 alkyl group R.sub.6 -- hydrogen or C.sub.1-5 alkyl group x = 1, 2, or 3 y = 1, 2, or 3 x + y = 2 to 4 with ethenically unsaturated monomers.
3. The copolymer composition of claim 2 wherein the acrylic acid ester monomer is butyl acrylate and the methacrylic acid ester monomer is methyl methacrylate.
4. The copolymer composition of claim 2 wherein the aziridinyl monomer is trimethylol propane bis-2-(1-aziridinyl) propionate monoacrylate.
5. The copolymer composition of claim 2 wherein the acrylic acid ester monomer is 2-ethylhexyl acrylate and the methacrylic acid ester monomer is methyl methacrylate.
6. The composition of claim 2 wherein the aziridinyl monomer is approximately 5-60% by weight of the copolymer.
7. A copolymer composition which comprises methyl methacrylate 2-ethylhexyl acrylate, and trimethylol propane bis-2-(1-aziridinyl) propionate monoacrylate.
Patent Citations (4)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3413272 | 1968-11-01 | Rees | |
| US3448094 | 1969-06-01 | Zief et al. | |
| US3480601 | 1969-11-01 | Ashby et al. | |
| US3719646 | 1973-03-01 | Stecklen et al. |