US 3,970,466 AGrant
Chemically Stable Optical Glass
Issue Date:1976-07-20
•6 Claims
Abstract
Optical glass, nd = 1.650 .+-. 2 .times. 10.sup..sup.-3 and vd = 55.5 .+-. 1.0, having a high chemical stability and a sufficiently low tendency toward crystallization that it can be manufactured in a continuous tank melting process into gobs, pressed components, and other formed articles as a mass-produced glass, said glass consisting essentially of, in percent by weight:
Metadata
Assignee
- Jenaer Glaswerk Schott & Gen.
Inventor
- Marga Faulstich
Application Information
Application Number:US 597092&
Filing Date:1975-07-18
Priority Date:1974-07-24
Art Unit:115
Classifications
IPC:
C03C 310C03C 308C03C 304
Field of Search:
10647 Q;47 R;54
Patent Drawings
This patent does not have any drawings.
Description
Background of the Invention
This invention relates to an optical glass of the optical position nd (refraction index) = 1.650 .+-. 2 .times. 10.sup..sup.-3 and vd (Abbe number) = 55.5 .+-. 1.0.
Glasses of this optical position are conventional; however heretofore, all of these glasses had a very low chemical stability. Consequently, there were restrictions on their manufacture and application.
Summary of the Invention
An object of this invention is to provide an optical glass of the optical position nd = 1.650 .+-. 2 .times. 10.sup.-.sup.3, vd = 55.5 .+-. 1.0 having a high chemical stability and a sufficiently low tendency toward crystallization that it can be manufactured by a continuous tank melting method into gobs, pressed articles, and block glass of any desired form as a mass-produced glass.
Other objects are to provide starting glass composition intermediates in the production of and/or process to produce said optical glasses.
Upon further study of the specification and appended claims, further objects and advantages of this invention will become apparent to those skilled in the
To attain these objects, it has been discovered that the desired optical glasses can be produced on the basis of a glass having the following composition (in percent by weight): SiO.sub.2 33.0 .+-. 0.5 B.sub.2 O.sub.3 11.6 .+-. 0.5 BaO 36.6 .+-. 1.0 La.sub.2 O.sub.3 14.0 .+-. 2.5 ZrO.sub.2 4.0 .+-. 2.5 As.sub.2 O.sub.3 0 - 0.5 as refining agent or Sb.sub.2 O.sub.3 preferably nd = 1.650 .+-. 1 .times. 10.sup..sup.-3 preferably vd = 55.0 .+-. 0.5
The glass of the present invention has the following properties:
THE COEFFICIENT OF EXPANSION .alpha. .times. 10.sup.7 /.degree. C. between 20.degree. and 300.degree. C. is 74 .+-. 2;
THE TRANSFORMATION TEMPERATURE IS 683 .+-. 5.degree. C.;
the softening temperature at 10.sup.7.65 poises is 810 .+-. 10.degree. C;
the specific gravity is 3.78 .+-. 0.10.
The chemical resistance is 2-3 classes better than that of the glasses on the market which have this optical position, i.e., La K22 nd = 1.6511 vd = 55.89. The chemical resistance test was conducted in accordance with the acid resistance and spotting tendency tests customary with Schott, as described in the Schott pocket catalogue No. 3050 of 1972.
The crystallization test shows, after a tempering of 60 minutes in a gradient furnace, no devitrification in the glass and only on the surface in isolated instances a crystallization growth rate of <0.3 .mu./min. The test was conducted according to O. H. Grauer and E. H. Hamilton: "Improved Apparatus for Determination of Liquidus Temperatures and Rates of Crystal Growth in Glasses," J. Research Natl. Bur. Standards, 44 (5) 495-502 (1950); RP 2096.
The following table shows examples of glasses according to the invention in percentages by weight:
Example 3 with an Abbe-number vdof 55,9 at a refraction index nd of 1,651 represents a particularly preferred embodiment of the invention.
Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize the present invention to its fullest extent. The following preferred specific embodiment is, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever. In the following example, all temperatures are set forth uncorrected in degrees Celsius; unless otherwise indicated, all parts and percentages are by weight.
For a glass according to Example 3 a blended batch of 300 kg. is formulated as follows:
The preceding example can be repeated with similar success by substituting the generically or specifically described invention for those used in the preceding example.
From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.
Claims
What is claimed is:
1. Optical glass, nd = 1.650 .+-. 2 .times. 10.sup..sup.-3 and vd = 55.5 .+-. 1.0, having a high chemical stability and a sufficiently low tendency toward crystallization that it can be manufactured in a continuous tank melting process into gobs, pressed components, and other formed articles as a mass-produced glass, said glass consisting essentially of, in percent by weight: B.sub.2 O.sub.3 11.6 .+-. 0.5 BaO 36.6 .+-. 1.0 La.sub.2 O.sub.3 14.0 .+-. 2.5 ZrO.sub.2 4.0 .+-. 2.5 As.sub.2 O.sub.3 0 - 0.5. or Sb.sub.2 O.sub.3
2. An optical glass according to claim 1, wherein nd = 1.650 .+-. 1 .times. 10.sup..sup.-3.
3. An optical glass according to claim 1, wherein vd = 55.0 .+-. 0.5.
4. An optical glass according to claim 2, wherein vd = 55.0 .+-. 0.5.
5. A glass composition consisting essentially of, in percent by weight: B.sub.2 O.sub.3 11.6 .+-. 0.5 BaO 36.6 .+-. 1.0 La.sub.2 O.sub.3 14.0 .+-. 2.5 ZrO.sub.2 4.0 .+-. 2.5 As.sub.2 O.sub.3 0 - 0.5 or Sb.sub.2 O.sub.3
6. A glass composition according to claim 4, having the following properties: the coefficient of expansion .alpha. .times. 10.sup.-.sup.7 /.degree. C. between 20.degree. and 300.degree. C. is 74 .+-. 2; the transformation temperature is 683 .+-. 5.degree. C; the softening temperature at 10.sup.7.65 poises is 810 .+-. 10.degree. C.; the specific gravity is 3.78 .+-. 0.05.
Patent Citations (1)
| Patent | Date | Inventor | Cited By |
|---|---|---|---|
| US3740242 | 1973-06-01 | Faulstich et al. |