US 2020/0067079 A1Application
METHOD OF PRODUCING ELECTROCHEMICALLY STABLE ELASTOMER-ENCAPSULATED PARTICLES OF CATHODE ACTIVE MATERIALS FOR LITHIUM BATTERIES
Publication Date:2020-02-27
•36 Claims
•7 Drawing Sheets
Abstract
A method of producing a powder mass for a lithium battery, comprising: (a) mixing an inorganic filler and an elastomer or its precursor in a liquid medium or solvent to form a suspension; (b) dispersing a plurality of particles of a cathode active material in the suspension to form a slurry; and (c) dispensing the slurry and removing the solvent and/or polymerizing or curing the precursor to form the powder mass, wherein at least a particulate comprises one or a plurality of cathode active material particles being encapsulated by a layer of inorganic filler-reinforced elastomer having a thickness from 1 nm to 10 μm, a fully recoverable tensile strain from 2% to 500%, and a lithium ion conductivity from 10−7 S/cm to 5×10−2 S/cm and the inorganic filler has a lithium intercalation potential from 1.1 V to 4.5 V versus Li/Li+.
Metadata
Assignee
- Nanotek Instruments, Inc.
Inventors
- Baofei Pan
- Hui He
- Bor Z. Jang
Application Information
Application Number:US 16/109,178
Filing Date:2018-08-22
Priority Date:2018-08-22
Classifications
IPC:
H01M4/36H01M4/62H01M10/0525
Patent Drawings (7 sheets)
Description
FIELD OF THE INVENTION
[0001] The present invention relates generally to the field of rechargeable lithium battery and, more particularly, to the cathode active materials in the form of particulates containing transition metal oxide-filled elastomer-encapsulated cathode active material particles and the method of producing same.
BACKGROUND OF THE INVENTION
[0002] A unit cell or building block of a lithium-ion battery is typically composed of an anode current collector, an anode or negative electrode layer (containing an anode active material responsible for storing lithium therein, a conductive additive, and a resin binder), an electrolyte and porous separator, a cathode or positive electrode layer (containing a cathode active material responsible for storing lithium therein, a conductive additive, and a resin binder), and a separate cathode current collector. The electrolyte is in ionic contact with both the anode active material and the cathode active material. A porous separator is not required if the electrolyte is a solid-state electrolyte.
[0003] The binder in the anode layer is used to bond the anode active material (e.g. graphite or Si particles) and a conductive filler (e.g. carbon black particles or carbon nanotube) together to form an anode layer of structural integrity, and to bond the anode layer to a separate anode current collector, which acts to collect electrons from the anode active material when the battery is discharged. In other words, in the negative electrode (anode) side of the battery, there are typically four different materials involved: an anode active material, a conductive additive, a resin binder (e.g. polyvinylidine fluoride, PVDF, or styrene-butadiene rubber, SBR), and an anode current collector (typically a sheet of Cu foil). Typically the former three materials form a separate, discrete anode active material layer (or, simply, anode layer) and the latter one forms another discrete layer (current collector layer). A binder resin (e.g. PVDF or PTFE) is also used in the cathode to bond cathode active materials and conductive additive particles together to form a cathode active layer of structural integrity. The same resin binder also acts to bond this cathode active layer to a cathode current collector (e.g. Al foil).
[0004] Historically, lithium-ion batteries actually evolved from rechargeable “lithium metal batteries” that use lithium (Li) metal as the anode and a Li intercalation compound (e.g. MoS2) as the cathode. Li metal is an ideal anode material due to its light weight (the lightest metal), high electronegativity (−3.04 V vs. the standard hydrogen electrode), and high theoretical capacity (3,860 mAh/g). Based on these outstanding properties, lithium metal batteries were proposed 40 years ago as an ideal system for high energy-density applications.
[0005] Due to some safety concerns (e.g. lithium dendrite formation and internal shorting) of pure lithium metal, graphite was implemented as an anode active material in place of the lithium metal to produce the current lithium-ion batteries. The past two decades have witnessed a continuous improvement in Li-ion batteries in terms of energy density, rate capability, and safety. However, the use of graphite-based anodes in Li-ion batteries has several significant drawbacks: low specific capacity (theoretical capacity of 372 mAh/g as opposed to 3,860 mAh/g for Li metal), long Li intercalation time (e.g. low solid-state diffusion coefficients of Li in and out of graphite and inorganic oxide particles) requiring long recharge times (e.g. 7 hours for electric vehicle batteries), inability to deliver high pulse power (power density <0.5 kW/kg), and necessity to use prelithiated cathodes (e.g. lithium cobalt oxide, as opposed to cobalt oxide), thereby limiting the choice of available cathode materials.
[0006] Further, these commonly used cathode active materials have a relatively low specific capacity (typically <220 mAh/g). These factors have contributed to the two major shortcomings of today's Li-ion batteries—a low energy density (typically 150-220 Wh/kgcell) and low power density (typically <0.5 kW/kg). In addition, even though the lithium metal anode has been replaced by an intercalation compound (e.g. graphite) and, hence, there is little or no lithium dendrite issue in the lithium-ion battery, the battery safety issue has not gone away. There have been no short of incidents involving lithium-ion batteries catching fire or exploding. To sum it up, battery scientists have been frustrated with the low energy density, inadequate cycle life, and flammability of lithium-ion cells for over three decades!
[0007] There have been tremendous efforts made in battery industry and research community to improve existing cathode materials and develop new cathode compositions. However, current and emerging cathode active materials for lithium secondary batteries still suffer from the following serious drawbacks:
-
- [0008] (1) The most commonly used cathode active materials (e.g. lithium transition metal oxides) contain a transition metal (e.g. Fe, Mn, Co, Ni, etc.) that is a powerful catalyst that can promote undesirable chemical reactions inside a battery (e.g. decomposition of electrolyte). These cathode active materials also contain a high oxygen content that could assist in the progression of thermal runaway and provide oxygen for electrolyte oxidation, increasing the danger of explosion or fire hazard. This is a serious problem that has hampered the widespread implementation of electric vehicles.
- [0009] (2) Most of promising organic or polymeric cathode active materials are either soluble in the commonly used electrolytes or are reactive with these electrolytes. Dissolution of active material in the electrolyte results in a continuing loss of the active material. Undesirable reactions between the active material and the electrolyte lead to graduate depletion of the electrolyte and the active material in the battery cell. All these phenomena lead to capacity loss of the battery and shortened cycle life.
- [0010] (3) The practical capacity achievable with current cathode materials (e.g. lithium iron phosphate and lithium transition metal oxides) has been limited to the range of 150-250 mAh/g and, in most cases, less than 200 mAh/g. Additionally, emerging high-capacity cathode active materials (e.g. FeF3) still cannot deliver a long battery cycle life.
- [0011] High-capacity cathode active materials, such as metal fluoride, metal chloride, and lithium transition metal silicide, can undergo large volume expansion and shrinkage during the discharge and charge of a lithium battery. These repeated volume changes lead to structural instability of the cathode, breakage of the normally weak bond between the binder resin and the active material, fragmentation of active material particles, delamination between the cathode active material layer and the current collector, and interruption of electron-conducting pathways. These high-capacity cathodes include CoF3, MnF3, FeF3, VF3, VOF3, TiF3, BiF3, NiF2, FeF2, CuF2, CuF, SnF2, AgF, CuCl2, FeCl3, MnCl2, etc. High-capacity cathode active materials also include a lithium transition metal silicate, Li2MSiO4 or Li2MaxMbySiO4, wherein M and Ma are selected from Fe, Mn, Co, Ni, V, or VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; andx+y≤1.
[0012] Hence, there is an urgent and continuing need for a new cathode active material and a cathode electrode (e.g. a cathode active material layer) that enable a lithium secondary battery to deliver a long cycle life and higher energy density. There is also a need for a method of readily and easily producing such a material in large quantities. Thus, it is a primary object of the present invention to meet these needs and address the issues associated the rapid capacity decay of a lithium battery.
SUMMARY OF THE INVENTION
[0013] Herein reported is a cathode active material layer or electrode (a cathode electrode or positive electrode) for a lithium battery that contains a very unique class of cathode active materials. The cathode active material is in a form of particulates, wherein at least a particulate contains one or a plurality of particles of a cathode active material being embraced or encapsulated by a thin layer of an inorganic filler-reinforced elastomer. This new class of material is capable of overcoming the cathode-induced rapid capacity decay problem commonly associated with a rechargeable lithium battery.
[0014] The cathode electrode comprises multiple particulates of a cathode active material, wherein at least a particulate is composed of one or a plurality of the cathode active material particles that are encapsulated by a thin layer of inorganic filler-reinforced elastomer having from 0.01% to 50% by weight of an inorganic filler dispersed in an elastomeric matrix material (based on the total weight of the inorganic filler-reinforced elastomer), wherein the encapsulating thin layer of inorganic filler-reinforced elastomer has a thickness from 1 nm to 10 μm, a fully recoverable tensile strain from 2% to 500%, and a lithium ion conductivity from 10−7 S/cm to 5×10−2 S/cm and wherein the inorganic filler has a lithium intercalation potential no less than 1.1 V versus Li/Li+ (preferably from 1.1 V to 4.5 V, more preferably from 1.1 to 3.5 V, and most preferably from 1.1 to 2.5 V).
[0015] The inorganic filler is preferably selected from an oxide, carbide, boride, nitride, sulfide, phosphide, or selenide of a transition metal, a lithiated version thereof, or a combination thereof. Preferably, the transition metal is selected from Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, Pd, Ag, Cd, La, Ta, W, Pt, Au, Hg, a combination thereof, or a combination thereof with Al, Ga, In, Sn, Pb, Sb, or Bi.
[0016] Preferably, particles of this inorganic filler are in a form of nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a dimension (diameter, thickness, or width, etc.) less than 100 nm, preferably less than 10 nm.
[0017] The encapsulating thin layer of inorganic filler-reinforced elastomer has a fully recoverable tensile strain from 2% to 500% (more typically from 5% to 300% and most typically from 10% to 150%), a thickness from 1 nm to 10 μm, and a lithium ion conductivity from 10−7 S/cm to 5×10−2 S/cm (more typically from 100.5 S/cm to 10−3 S/cm) when measured at room temperature on a cast thin film 20 μm thick. Preferably, this thin encapsulating layer also has an electrical conductivity from 10−7 S/cm to 100 S/cm (more typically from 10−3 S/cm to 10 S/cm when an electron-conducting additive is added into the elastomer matrix material).
[0018] Preferably, the elastomeric matrix material contains a sulfonated or non-sulfonated version of an elastomer selected from natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, metallocene-based poly(ethylene-co-octene) (POE) elastomer, poly(ethylene-co-butene) (PBE) elastomer, styrene-ethylene-butadiene-styrene (SIEBS) elastomer, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof. These sulfonated elastomers or rubbers, when present without graphene sheets, exhibit a high elasticity (having a fully recoverable tensile strain from 2% to 800%). In other words, they can be stretched up to 800% (8 times of the original length when under tension) and, upon release of the tensile stress, they can fully recover back to the original dimension. By adding from 0.01% to 50% by weight of graphene sheets dispersed in a sulfonated elastomeric matrix material, the fully recoverable tensile strains are typically reduced down to 2%-500% (more typically from 5% to 300% and most typically from 10% to 150%).
[0019] In certain preferred embodiments, the inorganic filler-reinforced elastomer further contains an electron-conducting filler dispersed in the elastomer matrix material wherein the electron-conducting filler is selected from a carbon nanotube, carbon nanofiber, nanocarbon particle, metal nanoparticle, metal nanowire, electron-conducting polymer, graphene, or a combination thereof. The graphene may be preferably selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, nitrogenated graphene, hydrogenated graphene, doped graphene, functionalized graphene, or a combination thereof and the graphene preferably comprises single-layer graphene or few-layer graphene, wherein the few-layer graphene is defined as a graphene platelet formed of less than 10 graphene planes. The electron-conducting polymer is preferably selected from (but not limited to) polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof.
[0020] Preferably, the graphene sheets have a lateral dimension (length or width) from 5 nm to 5 μm, more preferably from 10 nm to 1 μm, and most preferably from 10 nm to 300 nm. Shorter graphene sheets allow for easier encapsulation and enable faster lithium ion transport through the inorganic filler-reinforced elastomer-based encapsulating layer.
[0021] Preferably, the particulates are substantially or essentially spherical or ellipsoidal in shape. Also preferably, the particulate have a diameter or thickness smaller than 30 μm, more preferably smaller than 20 μm, and most preferably smaller than 10 μm.
[0022] The cathode active material particulate may contain a cathode active material selected from an inorganic material, an organic material, a polymeric material, or a combination thereof. The inorganic material may be selected from a metal oxide, metal phosphate, metal silicide, metal selenide, transition metal sulfide, or a combination thereof. The inorganic material may be selected from a lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, or a combination thereof.
[0023] In certain preferred embodiments, the inorganic material is selected from a metal fluoride or metal chloride including the group consisting of CoF3, MnF3, FeF3, VF3, VOF3, TiF3, BiF3, NiF2, FeF2, CuF2, CuF, SnF2, AgF, CuCl2, FeCl3, MnCl2, and combinations thereof. In certain preferred embodiments, the inorganic material is selected from a lithium transition metal silicate, denoted as Li2MSiO4 or Li2MaxMbySiO4, wherein M and Ma are selected from Fe, Mn, Co, Ni, V, or VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; and x+y≤1.
[0024] In certain preferred embodiments, the inorganic material is selected from a transition metal dichalcogenide, a transition metal trichalcogenide, or a combination thereof. The inorganic material is selected from TiS2, TaS2, MoS2, NbSe3, MnO2, CoO2, an iron oxide, a vanadium oxide, or a combination thereof.
[0025] The cathode active material layer may contain a metal oxide containing vanadium oxide selected from the group consisting of VO2, LixVO2, V2O5, LixV2O5, V3O8, LixV3O8, LixV3O7, V4O9, LixV4O9, V6O13, LixV6O13, their doped versions, their derivatives, and combinations thereof, wherein 0.1<x<5.
[0026] The cathode active material layer may contain a metal oxide or metal phosphate, selected from a layered compound LiMO2, spinel compound LiM2O4, olivine compound LiMPO4, silicate compound Li2MSiO4, tavorite compound LiMPO4F, borate compound LiMBO3, or a combination thereof, wherein M is a transition metal or a mixture of multiple transition metals.
[0027] In some embodiments, the inorganic material is selected from: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, manganese, iron, nickel, or a transition metal; (d) boron nitride, or (e) a combination thereof.
[0028] The cathode active material layer may contain an organic material or polymeric material selected from poly(anthraquinonyl sulfide) (PAQS), a lithium oxocarbon, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA), poly(anthraquinonyl sulfide), pyrene-4,5,9,10-tetraone (PYT), polymer-bound PYT, quino(triazene), redox-active organic material, tetracyanoquinodimethane (TCNQ), tetracyanoethylene (TCNE), 2,3,6,7,10,11-hexamethoxytriphenylene (HMTP), poly(5-amino-1,4-dyhydroxy anthraquinone) (PADAQ), phosphazene disulfide polymer ([(NPS2)3]n), lithiated 1,4,5,8-naphthalenetetraol formaldehyde polymer, hexaazatrinaphtylene (HATN), hexaazatriphenylene hexacarbonitrile (HAT(CN)6), 5-benzylidene hydantoin, isatine lithium salt, pyromellitic diimide lithium salt, tetrahydroxy-p-benzoquinone derivatives (THQLi4), N,N′-diphenyl-2,3,5,6-tetraketopiperazine (PHP), N,N′-diallyl-2,3,5,6-tetraketopiperazine (AP), N,N′-dipropyl-2,3,5,6-tetraketopiperazine (PRP), a thioether polymer, a quinone compound, 1,4-benzoquinone, 5,7,12,14-pentacenetetrone (PT), 5-amino-2,3-dihydro-1,4-dyhydroxy anthraquinone (ADDAQ), 5-amino-1,4-dyhydroxy anthraquinone (ADAQ), calixquinone, Li4C6O6, Li2C6O6, Li6C6O6, or a combination thereof.
[0029] The thioether polymer is selected from poly[methanetetryl-tetra(thiomethylene)](PMTTM), poly(2,4-dithiopentanylene) (PDTP), a polymer containing poly(ethene-1,1,2,2-tetrathiol) (PETT) as a main-chain thioether polymers, a side-chain thioether polymer having a main-chain consisting of conjugating aromatic moieties, and having a thioether side chain as a pendant, poly(2-phenyl-1,3-dithiolane) (PPDT), poly(1,4-di(1,3-dithiolan-2-yl)benzene) (PDDTB), poly(tetrahydrobenzodithiophene) (PTHBDT), poly[1,2,4,5-tetrakis(propylthio)benzene] (PTKPTB, or poly[3,4(ethylenedithio)thiophene] (PEDTT).
[0030] In other embodiments, the cathode active material layer contains an organic material selected from a phthalocyanine compound, such as copper phthalocyanine, zinc phthalocyanine, tin phthalocyanine, iron phthalocyanine, lead phthalocyanine, nickel phthalocyanine, vanadyl phthalocyanine, fluorochromium phthalocyanine, magnesium phthalocyanine, manganous phthalocyanine, dilithium phthalocyanine, aluminum phthalocyanine chloride, cadmium phthalocyanine, chlorogallium phthalocyanine, cobalt phthalocyanine, silver phthalocyanine, a metal-free phthalocyanine, a chemical derivative thereof, or a combination thereof.
[0031] The cathode active material is preferably in a form of nanoparticle (spherical, ellipsoidal, and irregular shape), nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a thickness or diameter less than 100 nm. These shapes can be collectively referred to as “particles” unless otherwise specified or unless a specific type among the above species is desired. Further preferably, the cathode active material has a dimension less than 50 nm, even more preferably less than 20 nm, and most preferably less than 10 nm.
[0032] In some embodiments, one particle or a cluster of particles may be coated with or embraced by a layer of carbon disposed between the active material particle(s) and the protecting polymer layer (the encapsulating shell). Alternatively or additionally, a carbon layer may be deposited to embrace the encapsulated particle or the encapsulated cluster of multiple cathode active material particles.
[0033] The particulate may further contain a graphite or carbon material mixed with the active material particles, which are all encapsulated by the encapsulating shell (but not dispersed within this thin layer of inorganic filler-reinforced elastomer). The carbon or graphite material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, mesophase pitch, carbon black, coke, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, or a combination thereof.
[0034] The cathode active material particles may be coated with or embraced by a conductive protective coating (selected from a carbon material, electronically conductive polymer, conductive metal oxide, or conductive metal coating) prior to being encapsulated by the inorganic filler-reinforced elastomer shell.
[0035] Preferably and typically, the inorganic filler-reinforced elastomer has a lithium ion conductivity no less than 10−6 S/cm, more preferably no less than 5×10−5 S/cm. In certain embodiments, the inorganic filler-reinforced elastomer further contains from 0.1% to 40% by weight (preferably from 1% to 30% by weight) of a lithium ion-conducting additive dispersed in the elastomer matrix material.
[0036] In some embodiments, the elastomeric matrix material contains a material selected from a sulfonated or non-sulfonated version of natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), metallocene-based poly(ethylene-co-octene) (POE) elastomer, poly(ethylene-co-butene) (PBE) elastomer, styrene-ethylene-butadiene-styrene (SEBS) elastorner, epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof. Sulfonation imparts higher lithium ion conductivity to the elastomer.
[0037] In some preferred embodiments, the inorganic filler-reinforced elastomer further contains a lithium ion-conducting additive dispersed in an elastomer matrix material, wherein the lithium ion-conducting additive is selected from Li2CO3, Li2O, Li2C2O4, LiOH, LiX, ROCO2Li, HCOLi, ROLi, (ROCO2Li)2, (CH2OCO2Li)2, Li2S, LixSOy, or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1 and 1≤y≤4.
[0038] In some embodiments, the inorganic filler-reinforced elastomer further contains a lithium ion-conducting additive dispersed in a sulfonated elastomer matrix material, wherein the lithium ion-conducting additive contains a lithium salt selected from lithium perchlorate (LiClO4), lithium hexafluorophosphate (LiPF6), lithium borofluoride (LiBF4), lithium hexafluoroarsenide (LiAsF6), lithium trifluoro-methanesulfonate (LiCF3SO3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF3SO2)2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF2C2O4), lithium nitrate (LiNO3), Li-fluoroalkyl-phosphate (LiPF3(CF2CF3)3), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
[0039] The proportion of this lithium ion-conducing additive is preferably from 0.1% to 40% by weight, but more preferably from 1% to 25% by weight. The sum of this additive and graphene sheets preferably occupies from 1% to 40% by weight, more preferably from 3% to 35% by weight, and most preferably from 5% to 25% by weight of the resulting composite weight (the elastomer matrix, electron-conducting additive, and lithium ion-conducting additive combined).
[0040] In certain preferred embodiments, the elastomeric matrix material may contain a mixture or blend of a sulfonated elastomer and an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions of these electron-conducting polymers), or a combination thereof. The proportion of this electron-conducting polymer is preferably from 0.1% to 20% by weight.
[0041] In some embodiments, the elastomeric matrix material contains a mixture or blend of a sulfonated elastomer and a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a sulfonated derivative thereof, or a combination thereof. Sulfonation is herein found to impart improved lithium ion conductivity to a polymer. The proportion of this lithium ion-conducting polymer is preferably from 0.1% to 20% by weight. Mixing or dispersion of an additive or reinforcement species in an elastomer or rubber may be conducted using solution mixing or melt mixing.
[0042] The present invention also provides a powder mass of cathode active material for a lithium battery. The powder mass comprises multiple particulates of a cathode active material, wherein at least one particulate is composed of one or a plurality of the cathode active material particles that are encapsulated by a thin layer of inorganic filler-reinforced elastomer having from 0.01% to 50% by weight of an inorganic filler dispersed in an elastomeric matrix material (based on the total weight of the inorganic filler-reinforced elastomer), wherein the encapsulating thin layer of inorganic filler-reinforced elastomer has a thickness from 1 nm to 10 μm, a fully recoverable tensile strain from 2% to 500%, and a lithium ion conductivity from 10−7 S/cm to 5×10−2 S/cm and wherein the inorganic filler has a lithium intercalation potential from 1.1 V to 4.5 V. The inorganic filler is preferably selected from an oxide, carbide, boride, nitride, sulfide, phosphide, or selenide of a transition metal, a lithiated version thereof, or a combination thereof. Preferably, the transition metal is selected from Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, Pd, Ag, Cd, La, Ta, W, Pt, Au, Hg, a combination thereof, or a combination thereof with Al, Ga, In, Sn, Pb, Sb, or Bi. The particles of this inorganic filler are preferably in a form of nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a dimension (diameter, thickness, or width, etc.) less than 100 nm, preferably less than 10 nm.
[0043] In certain embodiments, the inorganic filler is selected from nanodiscs, nanoplatelets, or nanosheets of (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, nickel, manganese, or any transition metal; (d) boron nitride, or (e) a combination thereof, wherein the nanodiscs, nanoplatelets, or nanosheets have a thickness from 1 nm to 100 nm.
[0044] The present invention also provides a cathode electrode that contains the presently invented inorganic filler-reinforced elastomer-encapsulated cathode material particles, an optional conductive additive (e.g. expanded graphite flakes, carbon black, acetylene black, or carbon nanotube), and an optional resin binder (typically required).
[0045] The present invention also provides a lithium battery containing an optional cathode current collector (e.g. Al foil), the presently invented cathode electrode as described above, an anode active material layer or anode electrode, an optional anode current collector (e.g. Cu foil), an electrolyte in ionic contact with the anode active material layer and the cathode active material layer and an optional porous separator.
[0046] There is no limitation on the type of anode active material that can be used in the anode electrode to partner with the invented cathode. For instance, the anode active material may be selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide; (f) prelithiated versions thereof, (g) particles and foil of Li, Li alloy, or surface-stabilized Li particles having at least 60% by weight of lithium element therein; and (h) combinations thereof.
[0047] In some preferred embodiments, the anode active material contains a prelithiated Si, prelithiated Ge, prelithiated Sn, prelithiated SnOx, prelithiated SiOx, prelithiated iron oxide, prelithiated VO2, prelithiated Co3O4, prelithiated Ni3O4, or a combination thereof, wherein x=1 to 2. It may be noted that prelithiation of an anode active material means that this material has been pre-intercalated by or doped with lithium ions up to a weight fraction from 0.1% to 54.7% of Li in the lithiated product.
[0048] The lithium battery may be a lithium-ion battery, lithium metal battery (containing lithium metal or lithium alloy as the main anode active material and containing no intercalation-based anode active material), lithium-sulfur battery, lithium-selenium battery, or lithium-air battery.
[0049] The invention also provides a method of producing a powder mass of a cathode active material for a lithium battery, the method comprising: (a) mixing particles of an inorganic filler (optionally along with an electron-conducting filler and/or a lithium ion-conducting filler) and an elastomer or its precursor (e.g. monomer or oligomer) in a liquid medium or solvent to form a suspension; (b) dispersing a plurality of particles of a cathode active material in the suspension to form a slurry; and (c) dispensing the slurry and removing the solvent and/or polymerizing/curing the precursor to form the powder mass, wherein the powder mass comprises multiple particulates of the cathode active material, wherein at least one of the particulates is composed of one or a plurality of the cathode active material particles which are encapsulated by a thin layer of inorganic filler-reinforced elastomer having from 0.01% to 50% by weight of particles of an inorganic filler dispersed in an elastomeric matrix material and the encapsulating thin layer of inorganic filler-reinforced elastomer has a thickness from 1 nm to 10 μm (preferably from 1 nm to 100 nm), a fully recoverable tensile strain from 2% to 500%, and a lithium ion conductivity from 10−7 S/cm to 10−2 S/cm. Preferably, this encapsulating layer material also has an electrical conductivity from 10−7 S/cm to 100 S/cm when measured at room temperature.
[0050] Preferably, the step of mixing the inorganic filler particles and the elastomer (sulfonated or non-sulfonated) or its precursor (monomer and/or oligomer) preferably includes a procedure of chemically bonding the elastomer or its precursor to the inorganic filler particles. There can be several different sequences of operations.
[0051] For instance, one can disperse inorganic filler particles (with or without an electron-conducting filler or a lithium ion-conducting filler) in a monomer or oligomer (with or without a solvent; monomer itself being capable of serving as a liquid medium) to form a suspension. A chemical reaction may be optionally but preferably initiated between inorganic filler particles and the monomer/oligomer at this stage or later. Cathode active material particles are then dispersed in the suspension to form a slurry. A micro-encapsulation procedure (e.g. spray-drying) is then conducted to produce droplets (particulates), wherein a particulate can contain one or several cathode active material particles embraced/encapsulated by an elastomeric shell. The resulting particulate is then subjected to a polymerization/curing treatment (e.g. via heating and/or UV curing, etc.). If the starting monomer/oligomer already had sulfonate groups or were already sulfonated, the resulting reinforced elastomer shell would be a sulfonated elastomer composite. Otherwise, the resulting mass of particulates may be subsequently subjected to a sulfonating treatment, if so desired.
[0052] Alternatively, one may dissolve a linear or branched chain polymer (but uncured or un-crosslinked) in a solvent to form a polymer solution. Such a polymer can be a sulfonated polymer to begin with, or can be sulfonated during any subsequent stage (e.g. after the particulates are formed). Inorganic filler particles (optionally along with an electron-conducting additive and/or a lithium ion-conducting additive) are then added into the polymer solution to form a suspension; particles of the cathode active material can be added concurrently or sequentially. The suspension is then subjected to a micro-encapsulation treatment to form particulates. Curing or cross-linking of the elastomer/graphene composite is then allowed to proceed.
[0053] Thus, the step of providing the solution and suspension may include (a) sulfonating an elastomer to form a sulfonated elastomer and dissolving the sulfonated elastomer in a solvent to form a polymer solution, or (b) sulfonating the precursor (monomer or oligomer) to obtain a sulfonated precursor (sulfonated monomer or sulfonated oligomer), polymerizing the sulfonated precursor to form a sulfonated elastomer and dissolving the sulfonated elastomer in a solvent to form a solution. Inorganic filler particles (optionally along with an electron-conducting additive and/or a lithium ion-conducting additive) and cathode active material particles are concurrently or sequentially added into the solution to form a suspension.
[0054] In certain embodiments, the step of dispensing the slurry and removing the solvent and/or polymerizing/curing the precursor to form the powder mass includes operating a procedure (e.g. micro-encapsulation) selected from pan-coating, air-suspension coating, centrifugal extrusion, vibration-nozzle encapsulation, spray-drying, coacervation-phase separation, interfacial polycondensation and interfacial cross-linking, in-situ polymerization, matrix polymerization, or a combination thereof.
[0055] In this method, the step of mixing the inorganic filler particles and elastomer or its precursor may include dissolving or dispersing from 0.1% to 40% by weight of a lithium ion-conducting additive in the liquid medium or solvent. The lithium ion-conducting additive may be selected from Li2CO3, Li2O, Li2C2O4, LiOH, LiX, ROCO2Li, HCOLi, ROLi, (ROCO2Li)2, (CH2OCO2Li)2, Li2S, LixSOy, or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1 and 1≤y≤4. Alternatively or additionally, the lithium ion-conducting additive contains a lithium salt selected from lithium perchlorate (LiClO4), lithium hexafluorophosphate (LiPF6), lithium borofluoride (LiBF4), lithium hexafluoroarsenide (LiAsF6), lithium trifluoro-methanesulfonate (LiCF3SO3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF3SO2)2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF2C2O4), lithium nitrate (LiNO3), Li-fluoroalkyl-phosphate (LiPF3(CF2CF3)3), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
[0056] In certain embodiments, the slurry further contains an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof. Alternatively or additionally, the slurry further contains a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a sulfonated derivative thereof, or a combination thereof.
[0057] The method may further comprise mixing multiple particulates of the aforementioned cathode active material, a binder resin, and an optional conductive additive to form a cathode electrode, which is optionally coated on a cathode current collector (e.g. Al foil). The method may further comprise combining an anode electrode, the presently invented cathode electrode (positive electrode), an electrolyte, and an optional porous separator into a lithium battery cell.
[0058] The presently invented inorganic filler-reinforced elastomer-encapsulated active material particles meet all of the criteria required of a lithium-ion battery cathode material:
-
- [0059] (a) The encapsulating material is of high strength and stiffness so that it can help to refrain the electrode active material particles, when lithiated, from expanding to an excessive extent.
- [0060] (b) The protective inorganic filler-reinforced elastomer shell, having both high elasticity and high strength, has a high fracture toughness and high resistance to crack formation to avoid disintegration during repeated cycling.
- [0061] (c) The inorganic filler-reinforced elastomer shell is relatively inert (inactive) with respect to the electrolyte. Further, since there is no direct contact between the cathode active material particles and liquid electrolyte, there is no opportunity for the transition metal in the cathode active material to catalyze the decomposition of electrolyte, which otherwise could generate undesirable chemical species (e.g. volatile molecules) inside the battery cell.
- [0062] (d) The inorganic filler-reinforced elastomer shell material can be both lithium ion-conducting and electron-conducting.
BRIEF DESCRIPTION OF THE DRAWINGS
[0063] FIG. 1(A) Schematic of a prior art lithium battery cell, wherein the anode layer is a thin Li foil and the cathode is composed of particles of a cathode active material, a conductive additive (not shown) and a resin binder (not shown).
[0064] FIG. 1(B) Schematic of a prior art lithium-ion battery; the anode layer being composed of particles of an anode active material, a conductive additive (not shown) and a resin binder (not shown).
[0065] FIG. 2(A) Schematic illustrating the notion that expansion/shrinkage of electrode active material particles, upon lithium insertion and de-insertion during discharge/charge of a prior art lithium-ion battery, can lead to detachment of resin binder from the particles, interruption of the conductive paths formed by the conductive additive, and loss of contact with the current collector;
[0066] FIG. 2(B) Several different types of particulates containing filled elastomer-encapsulated cathode active material particles.
[0067] FIG. 3 The specific intercalation capacity curves of four lithium cells: cathode containing un-encapsulated V2O5 particles, cathode containing un-encapsulated but graphene-embraced V2O5 particles, cathode containing filled elastomer-encapsulated V2O5 particles, and cathode containing filled elastomer-encapsulated graphene-embraced V2O5 particles.
[0068] FIG. 4 The specific capacity values of two lithium battery cells having a cathode active material featuring (1) filled elastomer-encapsulated carbon-coated LiFePO4 particles and (2) carbon-coated LiFePO4 particles without filled elastomer encapsulation, respectively.
[0069] FIG. 5 The discharge capacity curves of two coin cells having two different types of cathode active materials: (1) filled elastomer-encapsulated metal fluoride particles and (2) non-encapsulated metal fluorides.
[0070] FIG. 6 Specific capacities of two lithium-FePc (organic) cells, each having Li foil as an anode active material and FePc/RGO mixture particles as the cathode active material (one cell containing un-encapsulated particles and the other containing particles encapsulated by an elastomer composite).
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0071] This invention is directed at a cathode active material layer (positive electrode layer, not including the cathode current collector) for a lithium secondary battery. This positive electrode comprises a cathode active material that is in a form of an elastomer composite shell-protected particulate. The battery is preferably a secondary battery based on a non-aqueous electrolyte, a polymer gel electrolyte, an ionic liquid electrolyte, a quasi-solid electrolyte, or a solid-state electrolyte. The shape of a lithium secondary battery can be cylindrical, square, button-like, etc. The present invention is not limited to any battery shape or configuration or any type of electrolyte.
[0072] As illustrated in FIG. 1(B) , a lithium-ion battery cell is typically composed of an anode current collector (e.g. Cu foil), an anode or negative electrode active material layer (i.e. anode layer typically containing particles of an anode active material, conductive additive, and binder), a porous separator and/or an electrolyte component, a cathode or positive electrode active material layer (containing a cathode active material, conductive additive, and resin binder), and a cathode current collector (e.g. Al foil). More specifically, the cathode layer comprises particles of a cathode active material, a conductive additive (e.g. carbon black particles), and a resin binder (e.g. SBR or PVDF). This cathode layer is typically 50-300 m thick (more typically 100-200 μm) to give rise to a sufficient amount of current per unit electrode area.
[0073] In another cell configuration, as illustrated in FIG. 1(A) , the anode active material is a lithium metal foil or a layer of packed Li particles supported on an anode current collector, such as a sheet of copper foil. This can be a lithium meal secondary battery, lithium-sulfur battery, lithium-selenium battery, etc.
[0074] In order to obtain a higher energy density lithium-ion cell, the anode in FIG. 1(B) can be designed to contain higher-capacity anode active materials having a composition formula of LiaA (A is a metal or semiconductor element, such as Al and Si, and “a” satisfies 0<a≤5). These materials are of great interest due to their high theoretical capacity, e.g., Li4Si (3,829 mAh/g), Li4.4Si (4,200 mAh/g), Li4.4Ge (1,623 mAh/g), Li4.4Sn (993 mAh/g), Li3Cd (715 mAh/g), Li3Sb (660 mAh/g), Li4.4Pb (569 mAh/g), LiZn (410 mAh/g), and Li3Bi (385 mAh/g).
[0075] As schematically illustrated in FIG. 2(A) , one major problem in the current lithium battery is the notion that active material particles can get fragmented and the binder resin can detach from both the active material particles and conductive additive particles due to repeated volume expansion/shrinkage of the active material particles during the charge and discharge cycles. These binder detachment and particle fragmentation phenomena lead to loss of contacts between active material particles and conductive additives and loss of contacts between the active material and its current collector. These adverse effects result in a significantly shortened charge-discharge cycle life.
[0076] We have solved these challenging issues that have troubled battery designers and electrochemists alike for more than 30 years by developing a new class of cathode active materials. The cathode active material layer comprises multiple cathode active material particles that are fully embraced or encapsulated by an elastomer composite having a recoverable (elastic) tensile strain no less than 2% under uniaxial tension and a lithium ion conductivity no less than 10−5 S/cm at room temperature (preferably and more typically from 1×10−5 S/cm to 5×10−2 S/cm). The elastomer composite comprises an elastomer matrix which is reinforced with an inorganic filler.
[0077] As illustrated in FIG. 2(B) , the present invention provides four major types of particulates of elastomer composite-encapsulated cathode active material particles. The first one is a single-particle particulate containing a cathode active material core 10 encapsulated by a high-elasticity composite elastomer shell 12. The second is a multiple-particle particulate containing multiple cathode active material particles 14 (e.g. FeF3 particles), optionally along with other conductive materials (e.g. particles of graphite or hard carbon, not shown), which are encapsulated by an elastomer composite 16. The third is a single-particle particulate containing a cathode active material core 18 coated by a carbon or graphene layer 20 (or other conductive material) further encapsulated by an elastomer composite 22. The fourth is a multiple-particle particulate containing multiple cathode active material particles 24 (e.g. FeF3 particles) coated with a conductive protection layer 26 (carbon, graphene, etc.), optionally along with other active materials or conductive additive, which are encapsulated by an elastomer composite shell 28.
[0078] The elastomer refers to a polymer, typically a lightly cross-linked polymer, which exhibits an elastic deformation that is at least 5% when measured (without an additive or reinforcement in the polymer) under uniaxial tension. In the field of materials science and engineering, the “elastic deformation” is defined as a deformation of a material (when being mechanically stressed) that is essentially fully recoverable and the recovery is essentially instantaneous upon release of the load. The elastic deformation is preferably greater than 5%, more preferably greater than 10%, further more preferably greater than 50%, still more preferably greater than 100%, and most preferably greater than 200%. The preferred types of elastomer composites will be discussed later.
[0079] The application of the presently invented elastomer composite encapsulation approach is not limited to any particular class of cathode active materials. The cathode active material layer may contain a cathode active material selected from an inorganic material, an organic material, a polymeric material, or a combination thereof. The inorganic material may be selected from a metal oxide, metal phosphate, metal silicide, metal selenide, transition metal sulfide, or a combination thereof.
[0080] The inorganic material, as a cathode active material, may be selected from a lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, or a combination thereof.
[0081] In certain embodiments, the inorganic filler for reinforcing the elastomer may be selected from an oxide, carbide, boride, nitride, sulfide, phosphide, or selenide of a transition metal, a lithiated version thereof, or a combination thereof. Preferably, the transition metal is selected from Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, Pd, Ag, Cd, La, Ta, W, Pt, Au, Hg, a combination thereof, or a combination thereof with Al, Ga, In, Sn, Pb, Sb, or Bi.
[0082] These inorganic fillers for reinforcing the elastomer shell are preferably selected to have an intercalation potential (the electrochemical potential at which lithium intercalates into these materials) higher than the intercalation potential of the active material encapsulated in the particulate. For instance, lithium intercalates into Si at approximately 0.4-0.5 V (vs. Li/Li+) and the intercalation potential of lithium titanate (Li4Ti5O12) is 1.1-1.5 V. The lithium titanate may be considered as a lithiated version of titanium oxide (TiO2), which has a lithium intercalation potential >2.5 V. The inorganic filler must have a lithium intercalation potential higher than 1.1 V versus Li/Li+, preferably higher than 1.2 V, more preferably higher than 1.4 V, and most preferably higher than 1.5 V. These electrochemical potential conditions are found to be surprisingly capable of avoiding the formation of SEI on/in the encapsulating shell and preventing repeated formation and breakage of SEI on active material particles, which otherwise would result in continued and rapid decay of battery capacity.
[0083] Other examples of metal oxide are NbO2 and its lithiated version and titanium-niobium composite oxide (e.g. represented by a general formula TiNb2O7) and its lithiated versions. They typically have a lithium intercalation potential higher than 1.1 V versus Li/Li+.
[0084] The niobium-containing composite metal oxide for use as an inorganic filler in the encapsulating elastomer shell may be selected from the group consisting of TiNb2O7, LixTiNb2O7(0≤x≤5), LixM(1-y)NbyNb2O(7+δ) (wherein 0≤x≤6, 0≤y≤1, −1≤δ≤1, and M=Ti or Zr), TixNbyO7(0.5≤y/x≤2.0), TiNbxO(2+5x/2) (1.9≤x≤2.0), MxTi(1-2x)Nb(2+x)O(7+δ) (wherein 0≤x≤0.2, −0.3≤δ≤0.3, and M=a trivalent metal selected from Fe, Ga, Mo, Ta, V, Al, B, and a mixture thereof), MxTi(2−2x)Nb(10+x)O(29+δ) (wherein 0≤x≤0.4, −0.3≤δ≤0.3, and M=a trivalent metal selected from Fe, Ga, Mo, Al, B, and a mixture thereof), MxTiNb2O7(x<0.5, and M=B, Na, Mg, Al, Si, S, P, K, Ca, Mo, W, Cr, Mn, Co, Ni, and Fe), TiNb2−zTaxOy (0≤x<2, 7≤y≤10), Ti2Nb10−vTavOw (0≤v<2, 27≤y≤29), LixTi(1−y)M1yNb(2−z)M2zO(7+δ) (wherein 0≤x≤5, 0≤y≤1, 0≤z≤2, −0.3≤δ≤0.3, M1=Zr, Si, and Sn, and M2=V, Ta, and Bi), P-doped versions thereof, B-doped versions thereof, carbon-coated versions thereof, and combinations thereof. In such a niobium-containing composite metal oxide, niobium oxide typically forms the main framework or backbone of the crystal structure, along with at least a transition metal oxide.
[0085] Transition metal oxide is but one of the many suitable inorganic filler materials for reinforcing the elastomer matrix. The inorganic filler may be selected from an oxide, carbide, boride, nitride, sulfide, phosphide, or selenide of a transition metal, a lithiated version thereof, or a combination thereof. Preferably, these and other inorganic fillers are in a form of nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a dimension (diameter, thickness, or width, etc.) less than 100 nm, preferably less than 10 nm. These inorganic filler materials typically have a lithium intercalation potential from 1.1 V to 4.5 V versus Li/Li+, and more typically and preferably from 1.1 V to 3.5 V, and most preferably from 1.1 V to 1.5 V. The lithium intercalation potential of a filler dispersed in the elastomeric matrix material may be higher than the lithium intercalation potential of the active material encapsulated by the filled elastomer.
[0086] The inorganic filler material for reinforcing an elastomer matrix material may also be selected from nanodiscs, nanoplatelets, or nanosheets (having a thickness from 1 nm to 100 nm) of: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, nickel, manganese, or any transition metal; (d) boron nitride, or (e) a combination thereof. These nanodiscs, nanoplatelets, or nanosheets preferably have a thickness less than 20 nm, more preferably from 1 nm to 10 nm.
[0087] In certain preferred embodiments, the inorganic filler-reinforced elastomer further contains an electron-conducting filler dispersed in the elastomer matrix material wherein the electron-conducting filler is selected from a carbon nanotube, carbon nanofiber, nanocarbon particle, metal nanoparticle, metal nanowire, electron-conducting polymer, graphene, or a combination thereof. The graphene may be preferably selected from pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, nitrogenated graphene, hydrogenated graphene, doped graphene, functionalized graphene, or a combination thereof and the graphene preferably comprises single-layer graphene or few-layer graphene, wherein the few-layer graphene is defined as a graphene platelet formed of 2-10 graphene planes. More preferably, the graphene sheets contain 1-5 graphene planes, most preferably 1-3 graphene planes (i.e. single-layer, double-layer, or triple-layer graphene). The electron-conducting polymer is preferably selected from (but not limited to) polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof. Preferably and typically, the inorganic filler reinforced elastomer has a lithium ion conductivity from 10−7 S/cm to 5×10−2 S/cm, more preferably and typically greater than 10−5 S/cm, further more preferably and typically greater than 100.4 S/cm, and most preferably no less than 10−3 S/cm. In some embodiments, the composite further contains from 0.1% to 40% (preferably 1% to 35%) by weight of a lithium ion-conducting additive dispersed in an elastomer matrix material.
[0088] The inorganic filler-reinforced elastomer must have a high elasticity (high elastic deformation value). By definition, an elastic deformation is a deformation that is fully recoverable upon release of the mechanical stress and the recovery process is essentially instantaneous (no significant time delay). An elastomer, such as a vulcanized natural rubber, can exhibit a tensile elastic deformation from 2% up to 1,000% (10 times of its original length). Sulfonation of the rubber reduces the elasticity to 800%. With the addition of 0.01%-50% of inorganic filler particles and/or conductive filler (e.g. CNT and graphene sheets), the tensile elastic deformation of a sulfonated elastomer/rubber is reduced to typically from 2% to 500%. It may be noted that although a metal typically has a high ductility (i.e. can be extended to a large extent without breakage), the majority of the deformation is plastic deformation (non-recoverable) and elastic deformation occurs to only a small extent (typically <1% and more typically <0.2%).
[0089] A broad array of inorganic filler reinforced elastomers can be used to encapsulate a cathode active material particle or multiple particles. Encapsulation means substantially fully embracing the particle(s) without allowing the particle to be in direct contact with electrolyte in the battery. The elastomeric matrix material may be selected from a sulfonated or non-sulfonated version of natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), metallocene-based poly(ethylene-co-octene) (POE) elastomer, poly(ethylene-co-butene) (PBE) elastomer, styrene-ethylene-butadiene-styrene (SEBS) elastomer, epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.
[0090] The urethane-urea copolymer film usually consists of two types of domains, soft domains and hard domains. Entangled linear backbone chains consisting of poly(tetramethylene ether) glycol (PTMEG) units constitute the soft domains, while repeated methylene diphenyl diisocyanate (MDI) and ethylene diamine (EDA) units constitute the hard domains. The lithium ion-conducting additive can be incorporated in the soft domains or other more amorphous zones.
[0091] The electron-conducting filler may be selected from a carbon nanotube (CNT), carbon nanofiber, graphene, nanocarbon particles, metal nanowires, etc. A graphene sheet or nanographene platelet (NGP) composed of one basal plane (graphene plane) or multiple basal planes stacked together in the thickness direction. In a graphene plane, carbon atoms occupy a 2-D hexagonal lattice in which carbon atoms are bonded together through strong in-plane covalent bonds. In the c-axis or thickness direction, these graphene planes may be weakly bonded together through van der Waals forces. An NGP can have a platelet thickness from less than 0.34 nm (single layer) to 100 nm (multi-layer). For the present electrode use, the preferred thickness is <10 nm, more preferably <3 nm (or <10 layers), and most preferably single-layer graphene. Thus, the presently invented sulfonated elastomer/graphene composite shell preferably contains mostly single-layer graphene, but could make use of some few-layer graphene (less than 10 layers or 10 graphene planes). The graphene sheet may contain a small amount (typically <25% by weight) of non-carbon elements, such as hydrogen, nitrogen, fluorine, and oxygen, which are attached to an edge or surface of the graphene plane.
[0092] Graphene sheets may be oxidized to various extents during their preparation, resulting in graphite oxide (GO) or graphene oxide. Hence, in the present context, graphene preferably or primarily refers to those graphene sheets containing no or low oxygen content; but, they can include GO of various oxygen contents. Further, graphene may be fluorinated to a controlled extent to obtain graphite fluoride, or can be doped using various dopants, such as boron and nitrogen.
[0093] Graphite oxide may be prepared by dispersing or immersing a laminar graphite material (e.g., powder of natural flake graphite or synthetic graphite) in an oxidizing agent, typically a mixture of an intercalant (e.g., concentrated sulfuric acid) and an oxidant (e.g., nitric acid, hydrogen peroxide, sodium perchlorate, potassium permanganate) at a desired temperature (typically 0-70° C.) for a sufficient length of time (typically 30 minutes to 5 days). In order to reduce the time required to produce a precursor solution or suspension, one may choose to oxidize the graphite to some extent for a shorter period of time (e.g., 30 minutes) to obtain graphite intercalation compound (GIC). The GIC particles are then exposed to a thermal shock, preferably in a temperature range of 600-1,100° C. for typically 15 to 60 seconds to obtain exfoliated graphite or graphite worms, which are optionally (but preferably) subjected to mechanical shearing (e.g. using a mechanical shearing machine or an ultrasonicator) to break up the graphite flakes that constitute a graphite worm. The un-broken graphite worms or individual graphite flakes are then re-dispersed in water, acid, or organic solvent and ultrasonicated to obtain a graphene polymer solution or suspension.
[0094] The pristine graphene material is preferably produced by one of the following three processes: (A) Intercalating the graphitic material with a non-oxidizing agent, followed by a thermal or chemical exfoliation treatment in a non-oxidizing environment; (B) Subjecting the graphitic material to a supercritical fluid environment for inter-graphene layer penetration and exfoliation; or (C) Dispersing the graphitic material in a powder form to an aqueous solution containing a surfactant or dispersing agent to obtain a suspension and subjecting the suspension to direct ultrasonication.
[0095] In Procedure (A), a particularly preferred step comprises (i) intercalating the graphitic material with a non-oxidizing agent, selected from an alkali metal (e.g., potassium, sodium, lithium, or cesium), alkaline earth metal, or an alloy, mixture, or eutectic of an alkali or alkaline metal; and (ii) a chemical exfoliation treatment (e.g., by immersing potassium-intercalated graphite in ethanol solution).
[0096] In Procedure (B), a preferred step comprises immersing the graphitic material to a supercritical fluid, such as carbon dioxide (e.g., at temperature T>31° C. and pressure P>7.4 MPa) and water (e.g., at T>374° C. and P>22.1 MPa), for a period of time sufficient for inter-graphene layer penetration (tentative intercalation). This step is then followed by a sudden de-pressurization to exfoliate individual graphene layers. Other suitable supercritical fluids include methane, ethane, ethylene, hydrogen peroxide, ozone, water oxidation (water containing a high concentration of dissolved oxygen), or a mixture thereof.
[0097] In Procedure (C), a preferred step comprises (a) dispersing particles of a graphitic material in a liquid medium containing therein a surfactant or dispersing agent to obtain a suspension or slurry; and (b) exposing the suspension or slurry to ultrasonic waves (a process commonly referred to as ultrasonication) at an energy level for a sufficient length of time to produce the separated nanoscaled platelets, which are pristine, non-oxidized NGPs.
[0098] Reduced graphene oxide can be produced with an oxygen content no greater than 25% by weight, preferably below 20% by weight, further preferably below 5%. Typically, the oxygen content is between 5% and 20% by weight. The oxygen content can be determined using chemical elemental analysis and/or X-ray photoelectron spectroscopy (XPS).
[0099] The laminar graphite materials used in the prior art processes for the production of the GIC, graphite oxide, and subsequently made exfoliated graphite, flexible graphite sheets, and graphene platelets are, in most cases, natural graphite. However, the present invention is not limited to natural graphite. The starting material may be selected from the group consisting of natural graphite, artificial graphite (e.g., highly oriented pyrolytic graphite, HOPG), graphite oxide, graphite fluoride, graphite fiber, carbon fiber, carbon nanofiber, carbon nanotube, mesophase carbon microbead (MCMB) or carbonaceous micro-sphere (CMS), soft carbon, hard carbon, and combinations thereof. All of these materials contain graphite crystallites that are composed of layers of graphene planes stacked or bonded together via van der Waals forces. In natural graphite, multiple stacks of graphene planes, with the graphene plane orientation varying from stack to stack, are clustered together. In carbon fibers, the graphene planes are usually oriented along a preferred direction. Generally speaking, soft carbons are carbonaceous materials obtained from carbonization of liquid-state, aromatic molecules. Their aromatic ring or graphene structures are more or less parallel to one another, enabling further graphitization. Hard carbons are carbonaceous materials obtained from aromatic solid materials (e.g., polymers, such as phenolic resin and polyfurfuryl alcohol). Their graphene structures are relatively randomly oriented and, hence, further graphitization is difficult to achieve even at a temperature higher than 2,500° C. But, graphene sheets do exist in these carbons.
[0100] Graphene sheets may be oxidized to various extents during their preparation, resulting in graphite oxide or graphene oxide (GO). Hence, in the present context, graphene preferably or primarily refers to those graphene sheets containing no or low oxygen content; but, they can include GO of various oxygen contents. Further, graphene may be fluorinated to a controlled extent to obtain graphene fluoride.
[0101] Pristine graphene may be produced by direct ultrasonication (also known as liquid phase production) or supercritical fluid exfoliation of graphite particles. These processes are well-known in the art. Multiple pristine graphene sheets may be dispersed in water or other liquid medium with the assistance of a surfactant to form a suspension.
[0102] Fluorinated graphene or graphene fluoride is herein used as an example of the halogenated graphene material group. There are two different approaches that have been followed to produce fluorinated graphene: (1) fluorination of pre-synthesized graphene: This approach entails treating graphene prepared by mechanical exfoliation or by CVD growth with fluorinating agent such as XeF2, or F-based plasmas; (2) Exfoliation of multilayered graphite fluorides: Both mechanical exfoliation and liquid phase exfoliation of graphite fluoride can be readily accomplished [F. Karlicky, et al. “Halogenated Graphenes: Rapidly Growing Family of Graphene Derivatives” ACS Nano, 2013, 7 (8), pp 6434-6464].
[0103] Interaction of F2 with graphite at high temperature leads to covalent graphite fluorides (CF)n or (C2F)n, while at low temperatures graphite intercalation compounds (GIC) CxF (2≤x≤24) form. In (CF), carbon atoms are sp3-hybridized and thus the fluorocarbon layers are corrugated consisting of trans-linked cyclohexane chairs. In (C2F)n only half of the C atoms are fluorinated and every pair of the adjacent carbon sheets are linked together by covalent C—C bonds. Systematic studies on the fluorination reaction showed that the resulting F/C ratio is largely dependent on the fluorination temperature, the partial pressure of the fluorine in the fluorinating gas, and physical characteristics of the graphite precursor, including the degree of graphitization, particle size, and specific surface area. In addition to fluorine (F2), other fluorinating agents may be used, although most of the available literature involves fluorination with F2 gas, sometimes in presence of fluorides.
[0104] For exfoliating a layered precursor material to the state of individual layers or few-layers of graphene planes (hexagonal carbon atom planes), it is necessary to overcome the attractive forces between adjacent layers and to further stabilize the layers. This may be achieved by either covalent modification of the graphene surface by functional groups or by non-covalent modification using specific solvents, surfactants, polymers, or donor-acceptor aromatic molecules. The process of liquid phase exfoliation includes ultra-sonic treatment of a graphite fluoride in a liquid medium.
[0105] The nitrogenation of graphene can be conducted by exposing a graphene material, such as graphene oxide, to ammonia at high temperatures (200-400° C.). Nitrogenated graphene could also be formed at lower temperatures by a hydrothermal method; e.g. by sealing GO and ammonia in an autoclave and then increased the temperature to 150-250° C. Other methods to synthesize nitrogen doped graphene include nitrogen plasma treatment on graphene, arc-discharge between graphite electrodes in the presence of ammonia, ammonolysis of graphene oxide under CVD conditions, and hydrothermal treatment of graphene oxide and urea at different temperatures.
[0106] In some embodiments, the inorganic filler-reinforced elastomer further contains a lithium ion-conducting additive dispersed in an elastomer matrix material. The lithium ion-conducting additive may be selected from Li2CO3, Li2O, Li2C2O4, LiOH, LiX, ROCO2Li, HCOLi, ROLi, (ROCO2Li)2, (CH2OCO2Li)2, Li2S, LixSOy, or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1 and 1≤y≤4.
[0107] Alternatively, the lithium ion-conducting additive may contain a lithium salt selected from lithium perchlorate (LiClO4), lithium hexafluorophosphate (LiPF6), lithium borofluoride (LiBF4), lithium hexafluoroarsenide (LiAsF6), lithium trifluoro-methanesulfonate (LiCF3SO3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF3SO2)2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF2C2O4), lithium nitrate (LiNO3), Li-fluoroalkyl-phosphate (LiPF3(CF2CF3)3), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
[0108] In some embodiments, the lithium ion-conducting additive or filler is a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a derivative thereof (e.g. sulfonated versions), or a combination thereof.
[0109] The elastomeric matrix material may contain an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof.
[0110] Some elastomers are originally in an unsaturated chemical state (unsaturated rubbers) that can be cured by sulfur vulcanization to form a cross-linked polymer that is highly elastic (hence, an elastomer). Prior to vulcanization, these polymers or oligomers are soluble in an organic solvent to form a polymer solution. Graphene sheets can be chemically functionalized to contain functional groups (e.g. —OH, —COOH, NH2, etc.) that can react with the polymer or its oligomer. The graphene-bonded oligomer or polymer may then be dispersed in a liquid medium (e.g. a solvent) to form a solution or suspension. Particles of a cathode active material (e.g. LiCoO2 nanoparticles) can be dispersed in this polymer solution or suspension to form a slurry of an active material particle-polymer mixture. This suspension can then be subjected to a solvent removal treatment while individual particles remain substantially separated from one another. The graphene-bonded polymer precipitates out to deposit on surfaces of these active material particles. This can be accomplished, for instance, via spray drying.
[0111] Unsaturated rubbers that can be vulcanized to become elastomer include natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR),
[0112] Some elastomers are saturated rubbers that cannot be cured by sulfur vulcanization; they are made into a rubbery or elastomeric material via different means: e.g. by having a copolymer domain that holds other linear chains together. Graphene sheets can be solution- or melt-dispersed into the elastomer to form a graphene/elastomer composite. Each of these graphene/elastomer composites can be used to encapsulate particles of an active material by one of several means: melt mixing (followed by pelletizing and ball-milling, for instance), solution mixing (dissolving the active material particles in an uncured polymer, monomer, or oligomer, with or without an organic solvent) followed by drying (e.g. spray drying), interfacial polymerization, or in situ polymerization of elastomer in the presence of active material particles.
[0113] Saturated rubbers and related elastomers in this category include EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, and protein elastin. Polyurethane and its copolymers (e.g. urea-urethane copolymer) are particularly useful elastomeric shell materials for encapsulating active material particles.
[0114] Several micro-encapsulation processes require the elastomer materials to be dissolvable in a solvent. Fortunately, all the elastomers used herein are soluble in some common solvents. Even for those rubbers that are not very soluble after vulcanization, the un-cured polymer (prior to vulcanization or curing) can be readily dissolved in a common organic solvent to form a solution. This solution can then be used to encapsulate solid particles via several of the micro-encapsulation methods to be discussed in what follows. Upon encapsulation, the elastomer shell is then vulcanized or cured. Some examples of rubbers and their solvents are polybutadiene (2-methyl pentane+n-hexane or 2,3-dimethylbutane), styrene-butadiene rubber (toluene, benzene, etc.), butyl rubber (n-hexane, toluene, cyclohexane), etc. The SBR can be vulcanized with different amounts of sulfur and accelerator at 433° K in order to obtain different network structures and crosslink densities. Butyl rubber (IIR) is a copolymer of isobutylene and a small amount of isoprene (e.g. about 98% polyisobutylene with 2% isoprene distributed randomly in the polymer chain). Elemental sulfur and organic accelerators (such as thiuram or thiocarbamates) can be used to cross-link butyl rubber to different extents as desired. Thermoplastic elastomers are also readily soluble in solvents.
[0115] There are three broad categories of micro-encapsulation methods that can be implemented to produce elastomer-encapsulated particles of a cathode active material: physical methods, physico-chemical methods, and chemical methods. The physical methods include pan-coating, air-suspension coating, centrifugal extrusion, vibration nozzle, and spray-drying methods. The physico-chemical methods include ionotropic gelation and coacervation-phase separation methods. The chemical methods include interfacial polycondensation, interfacial cross-linking, in-situ polymerization, and matrix polymerization.
[0116] Pan-Coating Method:
[0117] The pan coating process involves tumbling the active material particles in a pan or a similar device while the encapsulating material (e.g. elastomer monomer/oligomer, elastomer melt, elastomer/solvent solution) is applied slowly until a desired encapsulating shell thickness is attained.
[0118] Air-Suspension Coating Method:
[0119] In the air suspension coating process, the solid particles (core material) are dispersed into the supporting air stream in an encapsulating chamber. A controlled stream of a polymer-solvent solution (elastomer or its monomer or oligomer dissolved in a solvent; or its monomer or oligomer alone in a liquid state) is concurrently introduced into this chamber, allowing the solution to hit and coat the suspended particles. These suspended particles are encapsulated (fully coated) with polymers while the volatile solvent is removed, leaving a very thin layer of polymer (elastomer or its precursor, which is cured/hardened subsequently) on surfaces of these particles. This process may be repeated several times until the required parameters, such as full-coating thickness (i.e. encapsulating shell or wall thickness), are achieved. The air stream which supports the particles also helps to dry them, and the rate of drying is directly proportional to the temperature of the air stream, which can be adjusted for optimized shell thickness.
[0120] In a preferred mode, the particles in the encapsulating zone portion may be subjected to re-circulation for repeated coating. Preferably, the encapsulating chamber is arranged such that the particles pass upwards through the encapsulating zone, then are dispersed into slower moving air and sink back to the base of the encapsulating chamber, enabling repeated passes of the particles through the encapsulating zone until the desired encapsulating shell thickness is achieved.
[0121] Centrifugal Extrusion:
[0122] Active material particles may be encapsulated using a rotating extrusion head containing concentric nozzles. In this process, a stream of core fluid (slurry containing particles of an active material dispersed in a solvent) is surrounded by a sheath of shell solution or melt. As the device rotates and the stream moves through the air it breaks, due to Rayleigh instability, into droplets of core, each coated with the shell solution. While the droplets are in flight, the molten shell may be hardened or the solvent may be evaporated from the shell solution. If needed, the capsules can be hardened after formation by catching them in a hardening bath. Since the drops are formed by the breakup of a liquid stream, the process is only suitable for liquid or slurry. A high production rate can be achieved. Up to 22.5 kg of microcapsules can be produced per nozzle per hour and extrusion heads containing 16 nozzles are readily available.
[0123] Vibrational Nozzle Encapsulation Method:
[0124] Core-shell encapsulation or matrix-encapsulation of an active material can be conducted using a laminar flow through a nozzle and vibration of the nozzle or the liquid. The vibration has to be done in resonance with the Rayleigh instability, leading to very uniform droplets. The liquid can consist of any liquids with limited viscosities (1-50,000 mPa·s): emulsions, suspensions or slurry containing the active material. The solidification can be done according to the used gelation system with an internal gelation (e.g. sol-gel processing, melt) or an external (additional binder system, e.g. in a slurry).
[0125] Spray-Drying:
[0126] Spray drying may be used to encapsulate particles of an active material when the active material is dissolved or suspended in a melt or polymer solution. In spray drying, the liquid feed (solution or suspension) is atomized to form droplets which, upon contacts with hot gas, allow solvent to get vaporized and thin polymer shell to fully embrace the solid particles of the active material.
[0127] Coacervation-Phase Separation:
[0128] This process consists of three steps carried out under continuous agitation:
- [0129] (a) Formation of three immiscible chemical phases: liquid manufacturing vehicle phase, core material phase and encapsulation material phase. The core material is dispersed in a solution of the encapsulating polymer (elastomer or its monomer or oligomer). The encapsulating material phase, which is an immiscible polymer in liquid state, is formed by (i) changing temperature in polymer solution, (ii) addition of salt, (iii) addition of non-solvent, or (iv) addition of an incompatible polymer in the polymer solution.
- [0130] (b) Deposition of encapsulation shell material: core material being dispersed in the encapsulating polymer solution, encapsulating polymer material coated around core particles, and deposition of liquid polymer embracing around core particles by polymer adsorbed at the interface formed between core material and vehicle phase; and
- [0131] (c) Hardening of encapsulating shell material: shell material being immiscible in vehicle phase and made rigid via thermal, cross-linking, or dissolution techniques.
[0132] Interfacial Polycondensation and Interfacial Cross-Linking:
[0133] Interfacial polycondensation entails introducing the two reactants to meet at the interface where they react with each other. This is based on the concept of the Schotten-Baumann reaction between an acid chloride and a compound containing an active hydrogen atom (such as an amine or alcohol), polyester, polyurea, polyurethane, or urea-urethane condensation. Under proper conditions, thin flexible encapsulating shell (wall) forms rapidly at the interface. A solution of the active material and a diacid chloride are emulsified in water and an aqueous solution containing an amine and a polyfunctional isocyanate is added. A base may be added to neutralize the acid formed during the reaction. Condensed polymer shells form instantaneously at the interface of the emulsion droplets. Interfacial cross-linking is derived from interfacial polycondensation, wherein cross-linking occurs between growing polymer chains and a multi-functional chemical groups to form an elastomer shell material.
[0134] In-Situ Polymerization:
[0135] In some micro-encapsulation processes, active materials particles are fully coated with a monomer or oligomer first. Then, direct polymerization of the monomer or oligomer is carried out on the surfaces of these material particles.
[0136] Matrix Polymerization:
[0137] This method involves dispersing and embedding a core material in a polymeric matrix during formation of the particles. This can be accomplished via spray-drying, in which the particles are formed by evaporation of the solvent from the matrix material. Another possible route is the notion that the solidification of the matrix is caused by a chemical change.
[0138] A variety of synthetic methods may be used to sulfonate an elastomer or rubber: (i) exposure to sulfur trioxide in vapor phase or in solution, possibly in presence of Lewis bases such as triethyl phosphate, tetrahydrofuran, dioxane, or amines; (ii) chlorosulfonic acid in diethyl ether; (iii) concentrated sulfuric acid or mixtures of sulfuric acid with alkyl hypochlorite; (iv) bisulfites combined to dioxygen, hydrogen peroxide, metallic catalysts, or peroxo derivates; and (v) acetyl sulfate.
[0139] Sulfonation of an elastomer or rubber may be conducted before, during, or after curing of the elastomer or rubber. Further, sulfonation of the elastomer or rubber may be conducted before or after the particles of an electrode active material are embraced or encapsulated by the elastomer/rubber or its precursor (monomer or oligomer). Sulfonation of an elastomer or rubber may be accomplished by exposing the elastomer/rubber to a sulfonation agent in a solution state or melt state, in a batch manner or in a continuous process. The sulfonating agent may be selected from sulfuric acid, sulfonic acid, sulfur trioxide, chlorosulfonic acid, a bisulfate, a sulfate (e.g. zinc sulfate, acetyl sulfate, etc.), a mixture thereof, or a mixture thereof with another chemical species (e.g. acetic anhydride, thiolacetic acid, or other types of acids, etc.). In addition to zinc sulfate, there are a wide variety of metal sulfates that may be used as a sulfonating agent; e.g. those sulfates containing Mg, Ca, Co, Li, Ba, Na, Pb, Ni, Fe, Mn, K, Hg, Cr, and other transition metals, etc.
[0140] For instance, a triblock copolymer, poly(styrene-isobutylene-styrene) or SIBS, may be sulfonated to several different levels ranging from 0.36 to 2.04 mequiv./g (13 to 82 mol % of styrene; styrene being 19 mol % of the unsulfonated block copolymer). Sulfonation of SIBS may be performed in solution with acetyl sulfate as the sulfonating agent. First, acetic anhydride reacts with sulfuric acid to form acetyl sulfate (a sulfonating agent) and acetic acid (a by-product). Then, excess water is removed since anhydrous conditions are required for sulfonation of SIBS. The SIBS is then mixed with the mixture of acetyl sulfate and acetic acid. Such a sulfonation reaction produces sulfonic acid substituted to the para-position of the aromatic ring in the styrene block of the polymer. Elastomers having an aromatic ring may be sulfonated in a similar manner.
[0141] A sulfonated elastomer also may be synthesized by copolymerization of a low level of functionalized (i.e. sulfonated) monomer with an unsaturated monomer (e.g. olefinic monomer, isoprene monomer or oligomer, butadiene monomer or oligomer, etc.).
Example 1: Sol-Gel Process for Producing LixTiNb2O7(TNO) as a Reinforcement or Filler for the Elastomer Shell
[0142] The synthesis method involves precipitating the precursor to niobium-based composite metal oxide nanoparticles from a solution reactant mixture of Nb(OH)5 (dissolved in citric acid) and water-ethanol solution containing Ti(OC3H7)4. Specifically, Nb2O5 was dissolved in hydrofluoric acid to form a transparent solution. In order to remove the F− ions from the solution, ammonia was added to obtain a white Nb(OH)5 precipitate. After the precipitate was washed and dried, the Nb(OH)5 was dissolved in citric acid to form a Nb(V)-citrate solution. A water-ethanol solution containing Ti(OC3H7)4 was added to this solution while the pH value of the solution was adjusted using ammonia. This final mixture containing Nb(V) and Ti(IV) ions was then stirred at 90° C. to form a citric gel. This gel was then heated to 140° C. to obtain a precursor, which was annealed at 900° C. and at 1350° C. to obtain the LixTiNb2O7(TNO) powder.
[0143] The powder was ball-milled in a high-intensity ball mill to obtain nanoparticles of TNO, which were then dispersed in monomers/oligomers of several different elastomers (e.g. polyurethane, polybutadine, etc.) to form reacting suspensions. The monomers/oligomers were then polymerized to a controlled extent without allowing for any significant cross-linking of chains. This procedure often enables chemical bonding between the composite metal oxide particles and other inorganic filler species (particles of transition metal carbide, sulfide, selenide, phosphide, nitride, boride, etc.). These non-cured or non-crosslinked polymers were then each separately dissolved in an organic solvent to form a suspension (polymer-solvent solution plus bonded metal oxide particles). Particles of cathode active materials were then dispersed into this suspension to form a slurry. The slurry was then spray-dried to form particulates containing cathode active material particles being embraced by an encapsulating shell of metal oxide-reinforced elastomer.
Example 2: Preparation of TiNb2O7, TiMoNbO7, and TiFe0.3Nb1.7O7 as a Reinforcement or Filler for the Elastomer Shell
[0144] A niobium-titanium composite oxide represented by the general formula TiNb2O7 was synthesized, by following the following procedure: Commercially available niobium oxide (Nb2O5) and a titanate proton compound were used as starting materials. The titanate proton compound was prepared by immersing potassium titanate in hydrochloric acid at 25° C. for 72 hours. In the process, 1M hydrochloric acid was replaced with a 1M of fresh acid every 24 hours. As a result, potassium ions were exchanged for protons to obtain the titanate proton compound.
[0145] The niobium oxide (Nb2O5) and the titanate proton compound were weighed such that the molar ratio of niobium to titanium in the synthesized compound was 3. The mixture was dispersed in 100 ml of pure water, followed by vigorous mixing. The obtained mixture was placed in a heat resistant container and was subjected to hydrothermal synthesis under conditions of 180° C. for a total of 24 hours. The obtained sample was washed in pure water three times, and then dried. The sample was then subjected to a heat treatment at 1,100° C. for 24 hours to obtain TiNb2O7.
[0146] Additionally, a niobium-molybdenum-titanium composite oxide was synthesized in the same manner as above except that niobium oxide (Nb2O5), molybdenum oxide (Mo2O5), and a titanate proton compound were weighed such that the molar ratio of niobium to titanium and that of molybdenum to titanium in the synthesized compound was 1.5 and 1.5, respectively. As a result, a niobium-molybdenum-titanium composite oxide (TiMoNbO7) was obtained.
[0147] In addition, a niobium-iron-titanium composite oxide was synthesized in the same manner as above except that niobium oxide (Nb2O5), a titanate proton compound, and iron oxide (Fe2O3) were weighed such that the molar ratio of niobium to titanium and of iron to titanium in the synthesized compound was 3 and 0.3, respectively. As a result, a niobium-titanium composite oxide (TiFe0.3Nb1.7O7) was obtained.
[0148] The above niobium-containing composite metal oxide powders (TiNb2O7, TiMoNbO7, and TiFe0.3Nb1.7O7) were separately added into a monomer of synthetic polyisoprene and a mixture of monomers for urethane-urea copolymer, respectively. Polymerization of the respective reacting mass was initiated and proceeded to obtain linear chains without crosslinking. This step was found to create some bonding between the composite metal oxide particles. Subsequently, these substantially linear chains were dissolved in a solvent (e.g. benzene and DMAc) to form a solution and particles of selected cathode active materials (V2O5, lithium iron phosphate, LiCoO2, etc.) were dispersed in the solution to form a slurry. The slurry was then made into particulates using the vibration nozzle method.
Example 3: Preparation of Ga0.1Ti0.8Nb2.1O7 as a Reinforcement or Filler for the Elastomer Shell
[0149] In an experiment, 0.125 g of GaCl3 and 4.025 g of NbCl5 were dissolved in 10 mL of anhydrous ethanol under an inert atmosphere (argon) and magnetic stirring. The solution was transferred under air. Then, added to this solution was 6.052 g solution of titanium oxysulfate (TiOSO4) at 15% by mass in sulfuric acid, followed by 10 mL of ethanol to dissolve the precursors under a magnetic stirring. The pH of the solution was adjusted to 10 by slow addition of ammonia NH3 at 28% by mass into water.
[0150] The paste was transferred into a Teflon container having a 90-mL capacity, which was then placed in an autoclave. The paste was then heated up to 220° C. for 5 hours with a heating and cooling ramp of 2 and 5 degrees C./min, respectively. The paste was then washed with distilled water by centrifugation until a pH between 6 and 7 was obtained. The resulting compound was heated at 60° C. for 12 hours and then ball-milled for 30 min at 500 rpm (revolutions per minute) in hexane. After evaporation of the solvent, the powder was calcinated at 950° C. for 1 hour with a heating/cooling ramp of 3 degrees C./min to produce crystals of Ga0.1Ti0.8Nb2.1O7. These particles were used as an inorganic filler to reinforce an elastomer matrix.
Example 4: Preparation of Fe0.1Ti0.8Nb2.1O7 Powder as a Reinforcement for Elastomer
[0151] In a representative procedure, 0.116 g of FeCl3 and 4.025 g of NbCl5 were dissolved in 10 mL of anhydrous ethanol under an inert atmosphere (argon) and magnetic stirring. The resulting solution was transferred under air. Then, added to this solution was 6.052 g of titanium oxysulfate (TiOSO4) at 15% by mass in sulfuric acid and 10 mL of ethanol to dissolve the precursors under a magnetic stirring. The pH of the solution was adjusted to 10 by slow addition of ammonia NH3 at 28% by mass into water.
[0152] The paste was transferred into a Teflon container having a 90-mL capacity, which was then placed in an autoclave. The paste was then heated up to 220° C. for 5 hours with a heating and cooling ramp of 2 and 5 degrees C./min, respectively. The paste was then washed with distilled water by centrifugation until a pH between 6 and 7 was obtained. The compound was heated at 60° C. for 12 hours and then ball-milled for 30 min at 500 rpm in hexane. After evaporation of hexane, the powder was calcinated at 950° C. for 1 hour with a heating/cooling ramp of 3 degrees C./min to obtain Fe0.1Ti0.8Nb2.1O7 crystals.
Example 5: Production of Molybdenum Diselenide Nanoplatelets Using Direct Ultrasonication
[0153] A sequence of steps can be utilized to form nanoplatelets from many different types of layered compounds: (a) dispersion of a layered compound in a low surface tension solvent or a mixture of water and surfactant, (b) ultrasonication, and (c) an optional mechanical shear treatment. For instance, dichalcogenides (MoSe2) consisting of Se—Mo—Se layers held together by weak van der Waals forces can be exfoliated via the direct ultrasonication process invented by our research group. Intercalation can be achieved by dispersing MoSe2 powder in a silicon oil beaker, with the resulting suspension subjected to ultrasonication at 120 W for two hours. The resulting MoSe2 platelets were found to have a thickness in the range from approximately 1.4 nm to 13.5 nm with most of the platelets being mono-layers or double layers.
[0154] Other single-layer platelets of the form MX2 (transition metal dichalcogenide), including MoS2, TaS2, ZrS2, and WS2, were similarly exfoliated and separated. Again, most of the platelets were mono-layers or double layers when a high sonic wave intensity was utilized for a sufficiently long ultrasonication time.
Example 6: Production of ZrS2 Nanodiscs as a Nanofiller for the Elastomer Shell
[0155] In a representative procedure, zirconium chloride (ZrCl4) precursor (1.5 mmol) and oleylamine (5.0 g, 18.7 mmol) were added to a 25-mL three-neck round-bottom flask under a protective argon atmosphere. The reaction mixture was first heated to 300° C. at a heating rate of 5° C./min under argon flow and subsequently CS2 (0.3 mL, 5.0 mmol) was injected. After 1 h, the reaction was stopped and cooled down to room temperature. After addition of excess butanol and hexane mixtures (1:1 by volume), 18 nm ZrS2 nanodiscs (˜100 mg) were obtained by centrifugation. Larger sized nanodiscs ZrS2 of 32 nm and 55 nm were obtained by changing reaction time to 3 h and 6 h, respectively otherwise under identical conditions.
Example 7: Preparation of Boron Nitride Nanosheets as a Nanofiller for the Elastomer Shell
[0156] Five grams of boron nitride (BN) powder, ground to approximately 20 μm or less in sizes, were dispersed in a strong polar solvent (dimethyl formamide) to obtain a suspension. An ultrasonic energy level of 85 W (Branson S450 Ultrasonicator) was used for exfoliation, separation, and size reduction for a period of 1-3 hours. This is followed by centrifugation to isolate the BN nanosheets. The BN nanosheets obtained were from 1 nm thick (<3 atomic layers) up to 7 nm thick.
Example 8: Sulfonation of Triblock Copolymer Poly(Styrene-Isobutylene-Styrene) or SIBS
[0157] An example of the sulfonation procedure used in this study is summarized as follows: a 10% (w/v) solution of SIBS (50 g) and a desired amount of graphene oxide sheets (0.15 TO 405 by wt.) in methylene chloride (500 ml) was prepared. The solution was stirred and refluxed at approximately 40 8 C, while a specified amount of acetyl sulfate in methylene chloride was slowly added to begin the sulfonation reaction. Acetyl sulfate in methylene chloride was prepared prior to this reaction by cooling 150 ml of methylene chloride in an ice bath for approximately 10 min. A specified amount of acetic anhydride and sulfuric acid was then added to the chilled methylene chloride under stirring conditions. Sulfuric acid was added approximately 10 min after the addition of acetic anhydride with acetic anhydride in excess of a 1:1 mole ratio. This solution was then allowed to return to room temperature before addition to the reaction vessel.
[0158] After approximately 5 h, the reaction was terminated by slowly adding 100 ml of methanol. The reacted polymer solution was then precipitated with deionized water. The precipitate was washed several times with water and methanol, separately, and then dried in a vacuum oven at 50 8 C for 24 h. This washing and drying procedure was repeated until the pH of the wash water was neutral. After this process, the final polymer yield was approximately 98% on average. This sulfonation procedure was repeated with different amounts of acetyl sulfate to produce several sulfonated polymers with various levels of sulfonation or ion-exchange capacities (IECs). The mol % sulfonation is defined as: mol %=(moles of sulfonic acid/moles of styrene)×100%, and the IEC is defined as the mille-equivalents of sulfonic acid per gram of polymer (mequiv./g).
[0159] After sulfonation and washing of each polymer, the S-SIBS samples were dissolved in a mixed solvent of toluene/hexanol (85/15, w/w) to form solutions having polymer concentrations ranging from 5 to 2.5% (w/v). Desired amounts of transition metal oxides prepared in Examples 1-4 were added into these solutions and the resulting slurries were ultrasonicated for 0.5-1.5 hours. Particles of a desired cathode active material, along with a desired amount of conducting additive (e.g. graphene sheets or CNTs) were then added into the slurry samples. The slurry samples were separately spray-dried to form transition metal oxide-reinforced sulfonated elastomer-embraced particles.
[0160] Alternatively, sulfonation may be conducted on the reinforced elastomer layer after this encapsulating layer is form. (e.g. after the active material particle(s) is/are encapsulated.
Example 9: Synthesis of Sulfonated Polybutadiene (PB) by Free Radical Addition of Thiolacetic Acid (TAA) Followed by In Situ Oxidation with Performic Acid
[0161] A representative procedure is given as follows. PB (8.0 g) was dissolved in toluene (800 mL) under vigorous stirring for 72 h at room temperature in a 1 L round-bottom flask. Benzophenone (BZP) (0.225 g; 1.23 mmol; BZP/olefin molar ratio=1:120) and TAA (11.9 mL; 0.163 mol, TAA/olefin molar ratio=1.1) and a desired amount of inorganic filler particles (0.1%-40% by wt.) were introduced into the reactor, and the polymer solution was irradiated for 1 h at room temperature with UV light of 365 nm and power of 100 W.
[0162] The resulting inorganic material-reinforced thioacetylated polybutadiene (PB-TA) was isolated by pouring 200 mL of the toluene solution in a plenty of methanol and the polymer recovered by filtration, washed with fresh methanol, and dried in vacuum at room temperature (Yield=3.54 g). Formic acid (117 mL; 3.06 mol; HCOOH/olefin molar ratio=25), along with a desired amount of cathode active material particles, from 10 to 100 grams) were added to the toluene solution of PB-TA at 50° C. followed by slow addition of 52.6 mL of hydrogen peroxide (35 wt %; 0.61 mol; H2O2/olefin molar ratio=5) in 20 min. We would like to caution that the reaction is autocatalytic and strongly exothermic. The resulting slurry was spray-dried to obtain reinforced sulfonated polybutadiene (PB-SA-encapsulated cathode active material particles.
[0163] It may be noted that inorganic filler material particles may be added at different stages of the procedure: before, during or after BZP is added or before/during/after the cathode active material particles are added.
Example 10: Synthesis of Sulfonated SBS
[0164] Sulfonated styrene-butadiene-styrene triblock copolymer (SBS) based elastomer was directly synthesized. First, SBS (optionally along with graphene sheets) is first epoxidized by performic acid formed in situ, followed by ring-opening reaction with an aqueous solution of NaHSO3. In a typical procedure, epoxidation of SBS was carried out via reaction of SBS in cyclohexane solution (SBS concentration=11 g/100 mL) with performic acid formed in situ from HCOOH and 30% aqueous H2O2 solution at 70° C. for 4 h, using 1 wt % poly(ethylene glycol)/SBS as a phase transfer catalyst. The molar ratio of H2O2/HCOOH was 1. The product (ESBS) was precipitated and washed several times with ethanol, followed by drying in a vacuum dryer at 60° C.
[0165] Subsequently, ESBS was first dissolved in toluene to form a solution with a concentration of 10 g/100 mL, into which was added 5 wt % TEAB/ESBS as a phase transfer catalyst and 5 wt % DMA/ESBS as a ring-opening catalyst. Herein, TEAB=tetraethyl ammonium bromide and DMA=N,N-dimethyl aniline. An aqueous solution of NaHSO3 and Na2SO3 (optionally along with graphene sheets, if not added earlier) was then added with vigorous stirring at 60° C. for 7 h at a molar ratio of NaHSO3/epoxy group at 1.8 and a weight ratio of Na2SO3/NaHSO3 at 36%. This reaction allows for opening of the epoxide ring and attaching of the sulfonate group according to the following reaction:
[0166] The reaction was terminated by adding a small amount of acetone solution containing antioxidant. The mixture was washed with distilled water three times, then precipitated by ethanol, followed by drying in a vacuum dryer at 50° C. It may be noted that particles of an inorganic filler and an electrode active material may be added during various stages of the aforementioned procedure (e.g. right from the beginning, or prior to the ring opening reaction). Preferably, the inorganic filler (along with the optional electron-conducting additive or lithium ion-conducting additive) is added before or during the ring opening reaction and the cathode active material is added afterwards.
Example 11: Synthesis of Sulfonated SBS by Free Radical Addition of Thiolacetic Acid (TAA) Followed by In Situ Oxidation with Performic Acid
[0167] A representative procedure is given as follows. SBS (8.000 g) in toluene (800 mL) was left under vigorous stirring for 72 hours at room temperature and heated later on for 1 h at 65° C. in a 1 L round-bottom flask until the complete dissolution of the polymer. Thus, benzophenone (BZP, 0.173 g; 0.950 mmol; BZP/olefin molar ratio=1:132) and TAA (8.02 mL; 0.114 mol, TAA/olefin molar ratio=1.1) were added, and the polymer solution was irradiated for 4 h at room temperature with UV light of 365 nm and power of 100 W. To isolate a fraction of the thioacetylated sample, 20 mL of the polymer solution was treated with plenty of methanol, and the polymer was recovered by filtration, washed with fresh methanol, and dried in vacuum at room temperature. The toluene solution containing the thioacetylated polymer was equilibrated at 50° C., and 107.4 mL of formic acid (2.84 mol; HCOOH/olefin molar ratio=27.5) and 48.9 mL of hydrogen peroxide (35 wt %; 0.57 mol; H2O2/olefin molar ratio=5.5) were added in about 15 min. It may be cautioned that the reaction is autocatalytic and strongly exothermic!Particles of the desired cathode active materials were added before or after this reaction. The resulting slurry was stirred for 1 h, and then most of the solvent was distilled off in vacuum at 35° C. Finally, the slurry containing the sulfonated elastomer was coagulated in a plenty of acetonitrile, isolated by filtration, washed with fresh acetonitrile, and dried in vacuum at 35° C. to obtain sulfonated elastomers.
[0168] Other elastomers (e.g. polyisoprene, EPDM, EPR, polyurethane, etc.) were sulfonated in a similar manner. Alternatively, all the rubbers or elastomers can be directly immersed in a solution of sulfuric acid, a mixture of sulfuric acid and acetyl sulfate, or other sulfonating agent discussed above to produce sulfonated elastomers/rubbers. Again, both the inorganic filler material and cathode active material particles may be added at various stages of the procedure. However, the inorganic filler material is preferably added before or immediately after addition of TAA and the cathode active material particles are added at a later stage.
Example 12: Graphene Oxide from Sulfuric Acid Intercalation and Exfoliation of MCMBs
[0169] MCMB (mesocarbon microbeads) were supplied by China Steel Chemical Co. This material has a density of about 2.24 g/cm3 with a median particle size of about 16 μm. MCMBs (10 grams) were intercalated with an acid solution (sulfuric acid, nitric acid, and potassium permanganate at a ratio of 4:1:0.05) for 48 hours. Upon completion of the reaction, the mixture was poured into deionized water and filtered. The intercalated MCMBs were repeatedly washed in a 5% solution of HCl to remove most of the sulfate ions. The sample was then washed repeatedly with deionized water until the pH of the filtrate was neutral. The slurry was dried and stored in a vacuum oven at 60° C. for 24 hours. The dried powder sample was placed in a quartz tube and inserted into a horizontal tube furnace pre-set at a desired temperature, 800° C.-1,100° C. for 30-90 seconds to obtain graphene samples. A small quantity of graphene was mixed with water and ultrasonicated at 60-W power for 10 minutes to obtain a suspension. A small amount was sampled out, dried, and investigated with TEM, which indicated that most of the NGPs were between 1 and 10 layers. The oxygen content of the graphene powders (GO or RGO) produced was from 0.1% to approximately 25%, depending upon the exfoliation temperature and time.
Example 13: Oxidation and Exfoliation of Natural Graphite
[0170] Graphite oxide was prepared by oxidation of graphite flakes with sulfuric acid, sodium nitrate, and potassium permanganate at a ratio of 4:1:0.05 at 30° C. for 48 hours, according to the method of Hummers [U.S. Pat. No. 2,798,878, Jul. 9, 1957]. Upon completion of the reaction, the mixture was poured into deionized water and filtered. The sample was then washed with 5% HCl solution to remove most of the sulfate ions and residual salt and then repeatedly rinsed with deionized water until the pH of the filtrate was approximately 4. The intent was to remove all sulfuric and nitric acid residue out of graphite interstices. The slurry was dried and stored in a vacuum oven at 60° C. for 24 hours.
[0171] The dried, intercalated (oxidized) compound was exfoliated by placing the sample in a quartz tube that was inserted into a horizontal tube furnace pre-set at 1,050° C. to obtain highly exfoliated graphite. The exfoliated graphite was dispersed in water along with a 1% surfactant at 45° C. in a flat-bottomed flask and the resulting graphene oxide (GO) suspension was subjected to ultrasonication for a period of 15 minutes to obtain a homogeneous graphene-water suspension.
Example 14: Preparation of Pristine Graphene Sheets
[0172] Pristine graphene sheets were produced by using the direct ultrasonication or liquid-phase exfoliation process. In a typical procedure, five grams of graphite flakes, ground to approximately 20 μm in sizes, were dispersed in 1,000 mL of deionized water (containing 0.1% by weight of a dispersing agent, Zonyl® FSO from DuPont) to obtain a suspension. An ultrasonic energy level of 85 W (Branson S450 Ultrasonicator) was used for exfoliation, separation, and size reduction of graphene sheets for a period of 15 minutes to 2 hours. The resulting graphene sheets were pristine graphene that had never been oxidized and were oxygen-free and relatively defect-free. There are substantially no other non-carbon elements.
Example 15: Preparation of Graphene Fluoride (GF) Sheets
[0173] Several processes have been used by us to produce GF, but only one process is herein described as an example. In a typical procedure, highly exfoliated graphite (HEG) was prepared from intercalated compound C2F.xClF3. HEG was further fluorinated by vapors of chlorine trifluoride to yield fluorinated highly exfoliated graphite (FHEG). A pre-cooled Teflon reactor was filled with 20-30 mL of liquid pre-cooled ClF3, and then the reactor was closed and cooled to liquid nitrogen temperature. Subsequently, no more than 1 g of HEG was put in a container with holes for ClF3 gas to access the reactor. After 7-10 days, a gray-beige product with approximate formula C2F was formed. GF sheets were then dispersed in halogenated solvents to form suspensions.
Example 16: Preparation of Nitrogenated Graphene Sheets
[0174] Graphene oxide (GO), synthesized in Example 12, was finely ground with different proportions of urea and the pelletized mixture heated in a microwave reactor (900 W) for 30 s. The product was washed several times with deionized water and vacuum dried. In this method graphene oxide gets simultaneously reduced and doped with nitrogen. The products obtained with graphene/urea mass ratios of 1/0.5, 1/1 and 1/2 are designated as N-1, N-2 and N-3 respectively and the nitrogen contents of these samples were 14.7, 18.2 and 17.5 wt. % respectively as determined by elemental analysis. These nitrogenated graphene sheets remain dispersible in water.
Example 17: Cathode Particulates Containing V2O5 Particles Encapsulated by a Shell of Elastomer Composite
[0175] Cathode active material layers were prepared from V2O5 particles and graphene-embraced V2O5 particles, respectively. V2O5 particles were commercially available. Graphene-embraced V2O5 particles were prepared in-house. In a typical experiment, vanadium pentoxide gels were obtained by mixing V2O5 in a LiCl aqueous solution. The Li+-exchanged gels obtained by interaction with LiCl solution (the Li:V molar ratio was kept as 1:1) was mixed with a GO suspension and then placed in a Teflon-lined stainless steel 35 ml autoclave, sealed, and heated up to 180° C. for 12 h. After such a hydrothermal treatment, the green solids were collected, thoroughly washed, ultrasonicated for 2 minutes, and dried at 70° C. for 12 h followed by mixing with another 0.1% GO in water, ultrasonicating to break down nanobelt sizes, and then spray-drying at 200° C. to obtain graphene-embraced V2O5 composite particulates.
[0176] For electrochemical testing, the working electrodes were prepared by mixing 85 wt. % active material (elastomer composite encapsulated or non-encapsulated particulates of V2O5, separately), 7 wt. % acetylene black (Super-P), and 8 wt. % polyvinylidene fluoride (PVDF) binder dissolved in N-methyl-2-pyrrolidinoe (NMP) to form a slurry of 5 wt. % total solid content. After coating the slurries on Al foil, the electrodes were dried at 120° C. in vacuum for 2 h to remove the solvent before pressing. Then, the electrodes were cut into a disk (ϕ=12 mm) and dried at 100° C. for 24 h in vacuum. Electrochemical measurements were carried out using CR2032 (3V) coin-type cells with lithium metal as the counter/reference electrode, Celgard 2400 membrane as separator, and 1 M LiPF6 electrolyte solution dissolved in a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) (EC-DEC, 1:1 v/v). The cell assembly was performed in an argon-filled glove-box. The CV measurements were carried out using a CH-6 electrochemical workstation at a scanning rate of 1 mV/s.
[0177] The electrochemical performance of the particulates of nano Li4Ti5O12-reinforced sulfonated elastomer-encapsulated V2O5 particles and that of non-protected V2O5 were evaluated by galvanostatic charge/discharge cycling at a current density of 50 mA/g, using a LAND electrochemical workstation.
[0178] Summarized in FIG. 3 are the specific intercalation capacity curves of four lithium cells: cathode containing un-encapsulated V2O5 particles, cathode containing un-encapsulated but graphene-embraced V2O5 particles, cathode containing elastomer composite-encapsulated V2O5 particles, and cathode containing elastomer composite-encapsulated graphene-embraced V2O5 particles. As the number of cycles increases, the specific capacity of the un-encapsulated V2O5 electrode drops at the fastest rate. In contrast, the presently invented filled elastomer composite encapsulation provides the battery cell with a significantly more stable and higher specific capacity for a large number of cycles. These data have clearly demonstrated the surprising and superior performance of the presently invented filled elastomer composite encapsulation approach.
[0179] The protecting elastomer composite encapsulation shell appears to be capable of reversibly deforming to a great extent without breakage when the active material particles expand and shrink. The elastomer also remains chemically bonded to the binder resin when the encapsulated particles expand or shrink. In contrast, the PVDF binder is broken or detached from some of the non-encapsulated active material particles. These were observed by using SEM to examine the surfaces of the electrodes recovered from the battery cells after some numbers of charge-discharge cycles.
Example 18: Inorganic Filler Reinforced Elastomer-Encapsulated Lithium Iron Phosphate (LFP) Particles
[0180] Commercially available lithium iron phosphate (LFP) particles were used in the present study. The battery cells from the TiNb2O7 reinforced elastomer-encapsulated LFP particles and non-coated LFP particles were prepared using a procedure described in Example 1. FIG. 4 shows that the cathode prepared according to the presently invented inorganic filler reinforced elastomer-encapsulated particulate approach offers a significantly more stable and higher reversible capacity compared to the un-coated LFP particle-based. The high-elasticity elastomer is more capable of holding the active material particles and conductive additive together, significantly improving the structural integrity of the active material electrode. The high-elasticity elastomer also acts to isolate the electrolyte from the active material yet still allowing for easy diffusion of lithium ions.
Example 19: Metal Fluoride and Metal Chloride Particles Encapsulated by a MoSe2-Reinforced Sulfonated Styrene-Butadiene Rubber (SBR)/Graphene Composite
[0181] Commercially available powders of CoF3, MnF3, FeF3, VF3, VOF3, TiF3, and BiF3 were subjected to high-intensity ball-milling to reduce the particle size down to approximately 0.5-2.3 μm. Each type of these metal fluoride particles, along with graphene sheets (as a conductive additive), were encapsulated with a thin layer of MoSe2 nanoplatelet-filled SBR shell via the spray-drying method, followed by curing of the butadiene segment of the SBR chains to impart high elasticity to the SBR. For comparison, some amount of FeF3 nanoparticles was encapsulated by a carbon shell. Carbon encapsulation is well-known in the art. Un-protected FeF3 nanoparticles from the same batch were also investigated to determine and compare the cycling behaviors of the lithium-ion batteries containing these particles as the cathode active material.
[0182] Shown in FIG. 5 are the discharge capacity curves of two coin cells having two different types of cathode active materials: (1) elastomer composite-encapsulated metal fluoride particles and (2) non-encapsulated metal fluorides. These results have clearly demonstrated that the high-elasticity filled elastomer encapsulation strategy provides excellent protection against capacity decay of a lithium metal battery featuring a high-capacity cathode active material.
[0183] The high-elasticity elastomer composite appears to be capable of reversibly deforming without breakage when the cathode active material particles expand and shrink. The elastomer also remains chemically bonded to the binder resin when the active particles expand or shrink. In contrast, both SBR and PVDF, the two conventional binder resins, are broken or detached from some of the non-encapsulated active material particles. The high-elasticity elastomer has contributed to the structural stability of the electrode layer. These were observed by using SEM to examine the surfaces of the electrodes recovered from the battery cells after some numbers of charge-discharge cycles.
Example 20: Metal Naphthalocyanine-Reduced Graphene Oxide (FePc/RGO) Hybrid Particulates Encapsulated by a High-Elasticity ZrS2-Filled Elastomer
[0184] Particles of combined FePc/graphene sheets were obtained by ball-milling a mixture of FePc and RGO in a milling chamber for 30 minutes. The resulting FePc/RGO mixture particles were potato-like in shape. Some of these mixture particles were encapsulated by a high-elasticity elastomer using the pan-coating procedure. Two lithium cells were prepared, each containing a Li foil anode, a porous separator, and a cathode layer of FePc/RGO particles (encapsulated or un-encapsulated).
[0185] The cycling behaviors of these 2 lithium cells are shown in FIG. 6 , which indicates that the lithium-organic cell having a filled elastomer-encapsulated particulates in the cathode layer exhibits a significantly more stable cycling response. This encapsulation elastomer reduces or eliminates direct contact between the catalytic transition metal element (Fe) and the electrolyte, yet still being permeable to lithium ions. This elastomer shell also completely eliminates the dissolution of naphthalocyanine compounds in the liquid electrolyte. This approach has significantly increased the cycle life of all lithium-organic batteries.
Example 21: Effect of Lithium Ion-Conducting Additive in an Elastomer Shell
[0186] A wide variety of lithium ion-conducting additives were added to several different sulfonated elastomer composites to prepare encapsulation shell materials for protecting core particles of active material. We have discovered that these filled elastomer materials are suitable encapsulation shell materials provided that their lithium ion conductivity at room temperature is no less than 10−7 S/cm. With these materials, lithium ions appear to be capable of readily diffusing in and out of the encapsulation shell having a thickness no greater than 1 μm. For thicker shells (e.g. 10 μm), a lithium ion conductivity at room temperature no less than 10−4 S/cm would be required.
| TABLE 1 | |||
|---|---|---|---|
| Lithium ion conductivity of various sulfonated elastomer composite compositions as a | |||
| shell material for protecting active material particles. | |||
| Li4Ti5O12-elastomer (1-2 μm | |||
| thick); 5-10% | |||
| Sample | Lithium-conducting | Li4Ti5O12 unless | |
| No. | additive | otherwise noted | Li-ion conductivity (S/cm) |
| E-1s | Li2CO3 + (CH2OCO2Li)2 | 70-99% polyurethane, | 5.2 × 10−6 to 4.8 × 10−3 S/cm |
| 2% RGO | |||
| E-2s | Li2CO3 + (CH2OCO2Li)2 | 65-99% polyisoprene, | 1.8 × 10−5 to 7.5 × 10−4 S/cm |
| 8% pristine graphene | |||
| E-3s | Li2CO3 + (CH2OCO2Li)2 | 65-80% SBR, 15% RGO | 8.9 × 10−6 to 8.7 × 10−4 S/cm |
| D-4s | Li2CO3 + (CH2OCO2Li)2 | 70-99% urethane-urea, | 1.6 × 10−6 to 6.6 × 10−4 S/cm |
| 12% nitrogenated | |||
| graphene | |||
| D-5s | Li2CO3 + (CH2OCO2Li)2 | 75-99% polybutadiene | 2.2 × 10−5 to 7.9 × 10−3 S/cm |
| B1s | LiF + LiOH + Li2C2O4 | 80-99% chloroprene | 1.7 × 10−6 to 6.8 × 10−4 S/cm |
| rubber | |||
| B2s | LiF + HCOLi | 80-99% EPDM | 5.6 × 10−6 to 4.4 × 10−3 S/cm |
| B3s | LiOH | 70-99% polyurethane | 3.9 × 10−5 to 4.5 × 10−3 S/cm |
| B4s | Li2CO3 | 70-99% polyurethane | 5.4 × 10−5 to 5.3 × 10−3 S/cm |
| B5s | Li2C2O4 | 70-99% polyurethane | 2.4 × 10−5 to 3.2 × 10−3 S/cm |
| B6s | Li2CO3 + LiOH | 70-99% polyurethane | 2.6 × 10−5 to 4.1 × 10−3 S/cm |
| C1s | LiClO4 | 70-99% urethane-urea | 5.7 × 10−5 to 4.8 × 10−3 S/cm |
| C2s | LiPF6 | 70-99% urethane-urea | 4.7 × 10−5 to 1.7 × 10−3 S/cm |
| C3s | LiBF4 | 70-99% urethane-urea | 3.2 × 10−5 to 4.4 × 10−4 S/cm |
| C4s | LiBOB + LiNO3 | 70-99% urethane-urea | 8.7 × 10−6 to 3.5 × 10−4 S/cm |
| S1s | Sulfonated polyaniline | 85-99% SBR | 8.2 × 10−6 to 9.3 × 10−4 S/cm |
| S2s | Sulfonated SBR | 85-99% SBR | 7.8 × 10−6 to 5.8 × 10−4 S/cm |
| S3s | Sulfonated PVDF | 80-99% chlorosulfonated | 5.4 × 10−6 to 5.7 × 10−4 S/cm |
| polyethylene (CS-PE) | |||
| S4s | Polyethylene oxide | 80-99% CS-PE | 6.6 × 10−6 to 4.7 × 10−4 S/cm |
[0187] Some advantages of the present invention may be summarized in the following:
-
- [0188] (1) The inorganic filler reinforced elastomer encapsulation strategy is surprisingly effective in alleviating the cathode expansion/shrinkage-induced capacity decay problems.
- [0189] (2) The encapsulation of high-capacity cathode active material particles by carbon or other non-elastomeric protective materials does not provide much benefit in terms of improving cycling stability of a lithium-ion battery
- [0190] (3) Sulfonation further improves the lithium ion conductivity of an elastomer and, hence, power density of the resulting battery.
- [0191] (4) This encapsulation elastomer strategy reduces or eliminates direct contact between the catalytic transition metal element (e.g. Fe, Mn, Ni, Co, etc.) commonly used in a cathode active material and the electrolyte, thereby reducing/eliminating catalytic decomposition of the electrolyte.
Claims
We claim:
1. A method of producing a powder mass of a cathode active material for a lithium battery, the method comprising: (a) mixing an inorganic filler material and an elastomer or its precursor in a liquid medium or solvent to form a suspension; (b) dispersing a plurality of particles of said cathode active material in the suspension to form a slurry; and (c) dispensing the slurry and removing the solvent and/or polymerizing or curing the precursor to form the powder mass, wherein the powder mass comprises multiple particulates of the cathode active material and at least a particulate comprises one or a plurality of particles of said cathode active material being encapsulated by a thin layer of inorganic filler-reinforced elastomer having from 0.01% to 50% by weight of an inorganic filler dispersed in an elastomeric matrix material, wherein said encapsulating thin layer of inorganic filler-reinforced elastomer has a thickness from 1 nm to 10 μm, a fully recoverable tensile strain from 2% to 500%, and a lithium ion conductivity from 10−7 S/cm to 5×10−2 S/cm and said inorganic filler has a lithium intercalation potential from 1.1 V to 4.5 V versus Li/Li+.
2. The method of claim 1, wherein said inorganic filler is selected from an oxide, carbide, boride, nitride, sulfide, phosphide, or selenide of a transition metal, a lithiated version thereof, or a combination thereof.
3. The method of claim 2, wherein said transition metal is selected from Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, Pd, Ag, Cd, La, Ta, W, Pt, Au, Hg, a combination thereof, or a combination thereof with Al, Ga, In, Sn, Pb, Sb, or Bi.
4. The method of claim 1, wherein said inorganic filler is selected from the group consisting of nanodiscs, nanoplatelets, or nanosheets of (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, nickel, manganese, or any transition metal; (d) boron nitride, and (e) combinations thereof, wherein said nanodiscs, nanoplatelets, or nanosheets have a thickness from 1 nm to 100 nm.
5. The method of claim 1, wherein said elastomeric matrix material comprises a material selected from the group consisting of sulfonated or un-sulfonated versions of natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, metallocene-based poly(ethylene-co-octene) elastomer, poly(ethylene-co-butene) elastomer, styrene-ethylene-butadiene-styrene elastomer, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, thermoplastic elastomer, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.
6. The method of claim 1, wherein said inorganic filler-reinforced elastomer further comprises an electron-conducting filler dispersed in said elastomer matrix material wherein said electron-conducting filler is selected from the group consisting of carbon nanotube, carbon nanofiber, nano carbon particle, metal nanoparticle, metal nanowire, electron-conducting polymer, graphene, and combinations thereof, wherein said graphene is selected from sheets of pristine graphene, graphene oxide, reduced graphene oxide, graphene fluoride, graphene chloride, nitrogenated graphene, hydrogenated graphene, doped graphene, functionalized graphene, or a combination thereof and said graphene comprise single-layer graphene or few-layer graphene.
7. The method of claim 6, wherein said electron-conducting polymer is selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof.
8. The method of claim 6, wherein said graphene sheets have a length or width from 5 nm to 5 μm.
9. The method of claim 1, wherein said cathode active material is selected from an inorganic material, an organic material, a polymeric material, or a combination thereof.
10. The method of claim 9, wherein said inorganic material is selected from a metal oxide, metal phosphate, metal silicide, metal selenide, transition metal sulfide, or a combination thereof.
11. The method of claim 9, wherein said inorganic material is selected from the group consisting of lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, and combinations thereof.
12. The method of claim 9, wherein said inorganic material is selected from a metal fluoride or metal chloride including the group consisting of CoF3, MnF3, FeF3, VF3, VOF3, TiF3, BiF3, NiF2, FeF2, CuF2, CuF, SnF2, AgF, CuCl2, FeCl3, MnCl2, and combinations thereof.
13. The method of claim 9, wherein said inorganic material is selected from a lithium transition metal silicate, denoted as Li2MSiO4 or Li2MaxMbySiO4, wherein M and Ma are selected from Fe, Mn, Co, Ni, V, or VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; and x+y≤1.
14. The method of claim 9, wherein said inorganic material is selected from a transition metal dichalcogenide, a transition metal trichalcogenide, or a combination thereof.
15. The method of claim 9, wherein said inorganic material is selected from the group consisting of TiS2, TaS2, MoS2, NbSe3, MnO2, CoO2, an iron oxide, a vanadium oxide, and combinations thereof.
16. The method of claim 10, wherein said metal oxide comprises a vanadium oxide selected from the group consisting of VO2, LixVO2, V2O5, LixV2O5, V3O8, LixV3O8, LixV3O7, V4O9, LixV4O9, V6O13, LixV6O13, their doped versions, their derivatives, and combinations thereof, wherein 0.1<x<5.
17. The method of claim 10, wherein said metal oxide or metal phosphate is selected from a layered compound LiMO2, spinel compound LiM2O4, olivine compound LiMPO4, silicate compound Li2MSiO4, tavorite compound LiMPO4F, borate compound LiMBO3, or a combination thereof, wherein M is a transition metal or a mixture of multiple transition metals.
18. The method of claim 9, wherein said inorganic material is selected from the group consisting of: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, manganese, iron, nickel, or a transition metal; (d) boron nitride, and (e) combinations thereof.
19. The method of claim 9, wherein said organic material or polymeric material is selected from the group consisting of poly(anthraquinonyl sulfide) (PAQS), a lithium oxocarbon, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA), poly(anthraquinonyl sulfide), pyrene-4,5,9,10-tetraone (PYT), polymer-bound PYT, quino(triazene), redox-active organic material, tetracyanoquinodimethane (TCNQ), tetracyanoethylene (TCNE), 2,3,6,7,10,11-hexamethoxytriphenylene (HMTP), poly(5-amino-1,4-dyhydroxy anthraquinone) (PADAQ), phosphazene disulfide polymer ([(NPS2)3]n), lithiated 1,4,5,8-naphthalenetetraol formaldehyde polymer, hexaazatrinaphtylene (HATN), hexaazatriphenylene hexacarbonitrile (HAT(CN)6), 5-benzylidene hydantoin, isatine lithium salt, pyromellitic diimide lithium salt, tetrahydroxy-p-benzoquinone derivatives (THQLi4), N,N′-diphenyl-2,3,5,6-tetraketopiperazine (PHP), N,N′-diallyl-2,3,5,6-tetraketopiperazine (AP), N,N′-dipropyl-2,3,5,6-tetraketopiperazine (PRP), a thioether polymer, a quinone compound, 1,4-benzoquinone, 5,7,12,14-pentacenetetrone (PT), 5-amino-2,3-dihydro-1,4-dyhydroxy anthraquinone (ADDAQ), 5-amino-1,4-dyhydroxy anthraquinone (ADAQ), calixquinone, Li4C6O6, Li2C6O6, Li6C6O6, and combinations thereof.
20. The method of claim 19, wherein said thioether polymer is selected from the group consisting of poly[methanetetryl-tetra(thiomethylene)] (PMTTM), poly(2,4-dithiopentanylene) (PDTP), a polymer containing poly(ethene-1,1,2,2-tetrathiol) (PETT) as a main-chain thioether polymers, a side-chain thioether polymer having a main-chain consisting of conjugating aromatic moieties, and having a thioether side chain as a pendant, poly(2-phenyl-1,3-dithiolane) (PPDT), poly(1,4-di(1,3-dithiolan-2-yl)benzene) (PDDTB), poly(tetrahydrobenzodithiophene) (PTHBDT), poly[1,2,4,5-tetrakis(propylthio)benzene](PTKPTB, and poly[3,4(ethylenedithio)thiophene] (PEDTT).
21. The method of claim 9, wherein said organic material contains a phthalocyanine compound selected from the group consisting of copper phthalocyanine, zinc phthalocyanine, tin phthalocyanine, iron phthalocyanine, lead phthalocyanine, nickel phthalocyanine, vanadyl phthalocyanine, fluorochromium phthalocyanine, magnesium phthalocyanine, manganous phthalocyanine, dilithium phthalocyanine, aluminum phthalocyanine chloride, cadmium phthalocyanine, chlorogallium phthalocyanine, cobalt phthalocyanine, silver phthalocyanine, a metal-free phthalocyanine, chemical derivatives thereof, and combinations thereof.
22. The method of claim 1, wherein said step of mixing the inorganic filler material and the elastomer or its precursor includes a procedure of chemically bonding the elastomer or its precursor to particles of said inorganic filler material.
23. The method of claim 1, wherein said step of forming the solution comprises (a) sulfonating an elastomer to form a sulfonated elastomer and dissolving the sulfonated elastomer in a solvent to form a polymer solution, or (b) sulfonating the precursor to obtain a sulfonated precursor, polymerizing the sulfonated precursor to form a sulfonated elastomer and dissolving the sulfonated elastomer in a solvent to form said solution.
24. The method of claim 1, wherein step (b) includes concurrently or sequentially adding said inorganic filler material and said cathode active material particles into said solution to form said suspension.
25. The method of claim 1, wherein step (c) includes operating a micro-encapsulation procedure selected from pan-coating, air-suspension coating, centrifugal extrusion, vibration-nozzle encapsulation, spray-drying, coacervation-phase separation, interfacial polycondensation and interfacial cross-linking, in-situ polymerization, matrix polymerization, or a combination thereof.
26. The method of claim 1, wherein said cathode active material is in a form of nanoparticle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a thickness or diameter from 0.5 nm to 100 nm.
27. The method of claim 1, further including coating said one or a plurality of particles with a layer of carbon disposed between said one or said a plurality of particles and said inorganic filler-reinforced elastomer layer.
28. The method of claim 1, further includes dispersing particles of a graphite or carbon material in said slurry in such a manner that said particulate further contains particles of said graphite or carbon material encapsulated therein.
29. The method of claim 28, wherein said graphite or carbon material is selected from polymeric carbon, amorphous carbon, chemical vapor deposition carbon, coal tar pitch, petroleum pitch, meso-phase pitch, carbon black, coke, acetylene black, activated carbon, fine expanded graphite particle with a dimension smaller than 100 nm, artificial graphite particle, natural graphite particle, or a combination thereof.
30. The method of claim 1, further comprising a step of dissolving or dispersing 0.1% to 40% by weight of a lithium ion-conducting additive in said slurry in such a manner that said inorganic filler material-reinforced elastomer further contains said lithium ion-conducting additive dispersed in said elastomeric matrix material.
31. The method of claim 30, wherein said lithium ion-conducting additive is selected from Li2CO3, Li2O, Li2C2O4, LiOH, LiX, ROCO2Li, HCOLi, ROLi, (ROCO2Li)2, (CH2OCO2Li)2, Li2S, LixSOy, or a combination thereof, wherein X═F, Cl, I, or Br, R=a hydrocarbon group, 0<x≤1 and 1≤y≤4.
The method of claim 30, wherein said lithium ion-conducting additive contains a lithium salt selected from the group consisting of lithium perchlorate (LiClO4), lithium hexafluorophosphate (LiPF6), lithium borofluoride (LiBF4), lithium hexafluoroarsenide (LiAsF6), lithium trifluoro-methanesulfonate (LiCF3SO3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF3SO2)2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF2C2O4), lithium nitrate (LiNO3), Li-fluoroalkyl-phosphate (LiPF3(CF2CF3)3), lithium bisperfluoro-ethylsulfonylimide (LiBETI), lithium bis(trifluoromethanesulfonyl)imide, lithium bis(fluorosulfonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), an ionic liquid-based lithium salt, or a combination thereof.
32. The method of claim 1, further comprising a step of dissolving or dispersing an electron-conducting polymer in said slurry wherein said electron-conducting polymer is selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, a sulfonated derivative thereof, or a combination thereof.
33. The method of claim 1, further comprising a step of dissolving or dispersing a lithium ion-conducting polymer in said slurry wherein said lithium ion-conducting polymer is selected from poly(ethylene oxide) (PEO), polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVDF), poly bis-methoxy ethoxyethoxide-phosphazene, polyvinyl chloride, polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a sulfonated derivative thereof, or a combination thereof.
34. The method of claim 1, further comprising a step of mixing multiple particulates of said cathode active material, a binder resin, and an optional conductive additive to form a cathode active material layer, which is optionally coated on a cathode current collector.
35. The method of claim 35, further comprising combining said cathode active material layer, an anode layer, an electrolyte, and an optional porous separator into a lithium battery cell.
36. The method of claim 36, wherein said lithium battery cell is a lithium-ion battery, lithium metal battery, lithium-sulfur battery, or lithium-selenium battery.