Oil Soluble Comb Polymers

[0001] The present application relates to oil-soluble comb polymers, to processes for their preparation and to their use.

[0002] Polyalkyl(meth)acrylates (PAMAs)—generally synthesized by simple free-radical copolymerization of a mixture of different alkyl methacrylates (AMAs)—bring about, as oil additives, depending on the molecular weight and composition, a rise in the viscosity index (VI) paired with, in comparison to other viscosity index improvers (VIIs), outstanding low-temperature properties (cf. R. M. Mortier, S. T. Orszulik (eds.), Chemistry and Technology of Lubricants, Blackie Academic & Professional, 1st ed., London 1993, 124-159 & 165-167). A fundamental prerequisite for usability as oil additives is, trivially, the oil solubility of the polymer which, in the case of the PAMAs, depends on the presence of a sufficiently large number of alkyl side chains having typically 6-24 carbon atoms. The VI of PAMA can frequently be raised by copolymerizing short-chain alkyl(meth)acrylates, for example methyl methacrylate or butyl methacrylate (cf. EP 0 637 332, EP 0 937 769 or EP 0 979 834). However, the short-chain component lowers the solubility at low temperatures, so that the proportion of methyl methacrylate, for example, remains restricted to about 25% by weight. The VIs of these comb-like polymers thus achievable are, depending on concentration, permanent shear stability index (PSSI) and base oil type, in the range between 150 and 250.

[0003] A further class of VIIs is given by styrene-alkyl maleate copolymers which are obtained by polymer-analogous esterification of styrene-maleic anhydride copolymers with typically C6-C24 alcohols. The esterification is driven up to a conversion of about 95% with addition of butanol. Complete conversion of the acid functionalities is possible by adding an amine to form amidic or imidic groups (U.S. Pat. No. 3,702,300, EP 0 969 077).

[0004] The viscosities of polymer solutions in mineral oils or synthetic oils are dependent upon the molecular weight to a high degree. This also has the consequence that the temperature dependence of the viscosity decreases or the VI increases with rising molecular weight (J. Bartz, Additive für Schmierstoffe [Additives for Lubricants], Expert-Verlag, Renningen-Malmsheim 1994, 197-252). In connection with the temperature increase, reference is also made to disentanglement of collapsed knots to give the extended worm-like molecule.

[0005] In parallel to the molecular weight, the shear stability, however, decreases as a result of chain breakage under high shear. As a result of this contrary effect, shear-stable VIIs, as required for manual transmission oils, automatic transmission oils, hydraulic oils or motor oils, based on conventional polymer types such as the PAMAs are realizable only with high addition amounts. VIIs with a low contribution to viscosity at low temperatures, normal thickening in the VI range from 40 to 100° C., high contribution to viscosity above 100° C. and simultaneously ensured good oil solubility within the entire temperature range are therefore of particular interest.

[0006] In addition to linear comb-like polymers such as the PAMAs, VIIs based on true comb polymers are also already known in the patent literature. EP 0 744 457 describes comb polymers of relatively high order based purely on PAMA, in which the side arms themselves consist of oligomeric PAMA. In addition, the patent literature is aware of two further patents regarding comb polymers in which the side chains consist of saturated or hydrogenated polyolefins and the backbone of short-chain monomers such as AMAs or alkylstyrenes. For instance, EP 0 621 293 describes comb polymers in which the side chains are preferably formed from hydrogenated polybutadiene. Similarly, EP 0 699 694 relates to comb polymers with side arms preferably based on saturated olefin monomers, for example polyisobutylene or atactic polypropylene.

[0007] In the widest sense, A-B-A triblock copolymers can also be considered to be comb polymers with only two side arms. For instance, triblock copolymers have already been described as VIIs based purely on PAMA (P. Callais, S. Schmidt, N. Macy, SAE Technical Paper Series, No. 2004-01-3047) and also based on a polybutyl methacrylate core and hydrogenated polybutadiene or polyisoprene arms (U.S. Pat. No. 5,002,676). Anionically prepared A-B-A block copolymers with a polystyrene core and, for example, hydrogenated polyisoprene arms even find commercial use as VIIs (U.S. Pat. No. 4,788,361). Such VIIs are also assigned to the class of the hydrogenated styrene-diene copolymers.

[0008] In addition to the above-described application as VIIs, comb polymers with hydrogenated or saturated side arms are also known in entirely different applications. For instance, DE 196 31 170 describes comb polymers for impact-resistant molding materials, the polymers being a sequence of polyisobutylene-containing macromonomers without additional short-chain backbone monomers. Also described in the patent literature is a way of attaching a functionalized polypropylene to a styrene-maleic anhydride backbone in a polymer-analogous reaction to form a soft highly insulating comb polymer gel (EP 0 955, 320); the molecular weights of the polypropylene used are exceptionally high, being up to 300 000 g/mol. In one example from the chemistry of adhesives, comb polymers with hydrogenated polybutadiene or isoprene arms are described, the backbone also comprising acrylic acid as well as AMAs (U.S. Pat. No. 5,625,005).

[0009] The polymers detailed above are used commercially in many ways. Accordingly, most of these polymers exhibit a satisfactory property profile. However, there is a permanent effort to remove the relationship of thickening action, viscosity index and shear stability in order to achieve a desired viscosity with minimum use of additive in lubricant oils over a wide temperature range without impairing this property through premature degradation of the polymers.

[0010] Furthermore, the polymers should be producible in a simple and inexpensive manner, and especially commercially available components should be used. In this context, they should be producible on the industrial scale without new plants or plants of complicated construction being required for this purpose.

[0011] These objects and also further objects which are not stated explicitly but are immediately derivable or discernible from the connections discussed herein by way of introduction are achieved by comb polymers having all features of claim 1. Appropriate modifications to the inventive comb polymers are protected in the subclaims referring back to claim 1. With regard to the process for preparing comb polymers, claim 18 provides a solution to the underlying problem, while claim 26 protects a lubricant oil composition comprising the comb polymers of the present invention.

[0012] By virtue of the molar degree of branching being in the range from 0.1 to 10 mol % and the comb polymer comprising a total of at least 80% by weight, based on the weight of the repeat units, of repeat units which are derived from polyolefin-based macromonomers, and repeat units which are derived from low molecular weight monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers, it is possible in a not immediately foreseeable manner to provide a comb polymer comprising, in the main chain, repeat units which are derived from polyolefin-based macromonomers, and repeat units which are derived from low molecular weight monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers, which have a low shear sensitivity with a high thickening action.

[0013] At the same time, the inventive comb polymers allow a series of further advantages to be achieved. These include:

• • [0014] The inventive comb polymers have a particularly high viscosity index-improving action in lubricant oils.
  • [0015] The comb polymers of the present invention can be prepared in a particularly easy and simple manner. It is possible to use customary industrial scale plants.

[0016] The term “comb polymer” used herein is known per se, relatively long side chains being bonded to a polymeric main chain, frequently also known as the backbone. In the present case, the inventive polymers have at least one repeat unit which is derived from polyolefin-based macromonomers. The exact proportion is evident via the molar degree of branching. The term “main chain” does not necessarily mean that the chain length of the main chain is greater than that of the side chains. Instead, this term relates to the composition of this chain. While the side chain has very high proportions of olefinic repeat units, especially units which are derived from alkenes or alkadienes, for example ethylene, propylene, n-butene, isobutene, butadiene, isoprene, the main chain comprises relatively large proportions of polar unsaturated monomers which have been detailed above.

[0017] The term “repeat unit” is widely known in the technical field. The present comb polymers can preferably be obtained by means of free-radical polymerization of macromonomers and low molecular weight monomers. In this reaction, double bonds are opened up to form covalent bonds. Accordingly, the repeat unit arises from the monomers used. However, the present comb polymers can also be obtained by polymer-analogous reactions and/or graft copolymerization. In this case, the converted repeat unit of the main chain is counted as a repeat unit which is derived from a polyolefin-based macromonomer. The same applies in the case of preparation of the inventive comb polymers by graft copolymerization.

[0018] The present invention describes comb polymers which preferably have a high oil solubility. The term “oil-soluble” means that a mixture of a base oil and an inventive comb polymer which has at least 0.1% by weight, preferably at least 0.5% by weight of the inventive comb polymers is preparable without macroscopic phase formation. The comb polymer can be present in dispersed and/or dissolved form in this mixture. The oil solubility depends in particular on the proportion of lipophilic side chains and on the base oil. This property is known to those skilled in the art and can be adjusted for the particular base oil easily via a proportion of lipophilic monomers.

[0019] The inventive comb polymers comprise repeat units which are derived from polyolefin-based macromonomers. Polyolefin-based macromonomers are known in the technical field. These repeat units comprise at least one group which is derived from polyolefins. Polyolefins are known in the technical field, and can be obtained by polymerizing alkenes and/or alkadienes which consist of the elements carbon and hydrogen, for example C2-C10-alkenes such as ethylene, propylene, n-butene, isobutene, norbornene, and/or C4-C10-alkadienes such as butadiene, isoprene, norbornadiene. The repeat units derived from polyolefin-based macromonomers comprise preferably at least 70% by weight and more preferably at least 80% by weight and most preferably at least 90% by weight of groups which are derived from alkenes and/or alkadienes, based on the weight of the repeat units derived from polyolefin-based macromonomers. The polyolefinic groups may in particular also be present in hydrogenated form. In addition to the groups which are derived from alkenes and/or alkadienes, the repeat units derived from polyolefin-based macromonomers may comprise further groups. These include small proportions of copolymerizable monomers. These monomers are known per se and include, among other monomers, alkyl(meth)acrylates, styrene monomers, fumarates, maleates, vinyl esters and/or vinyl ethers. The proportion of these groups based on copolymerizable monomers is preferably at most 30% by weight, more preferably at most 15% by weight, based on the weight of the repeat units derived from polyolefin-based macromonomers. In addition, the repeat units derived from polyolefin-based macromonomers may comprise start groups and/or end groups which serve for functionalization or are caused by the preparation of the repeat units derived from polyolefin-based macromonomers. The proportion of these start groups and/or end groups is preferably at most 30% by weight, more preferably at most 15% by weight, based on the weight of the repeat units derived from polyolefin-based macromonomers.

[0020] The number-average molecular weight of the repeat units which are derived from polyolefin-based macromonomers is preferably in the range from 500 to 50 000 g/mol, more preferably from 700 to 10 000 g/mol, in particular from 1500 to 4900 g/mol and most preferably from 2000 to 3000 g/mol.

[0021] In the case of preparation of the comb polymers via the copolymerization of low molecular weight and macromolecular monomers, these values arise through the properties of the macromolecular monomers. In the case of polymer-analogous reactions, this property arises, for example, from the macroalcohols and/or macroamines used taking account of the converted repeat units of the main chain. In the case of graft copolymerizations, the proportion of polyolefins formed which have not been incorporated into the main chain can be used to conclude the molecular weight distribution of the polyolefin.

[0022] The repeat units which are derived from polyolefin-based macromonomers preferably have a low melting point, which is measured by means of DSC. The melting point of the repeat units derived from the polyolefin-based macromonomers is preferably less than or equal to −10° C., especially preferably less than or equal to −20° C., more preferably less than or equal to −40° C. Most preferably, no DSC melting point can be measured for the repeat units which are derived from the polyolefin-based macromonomers.

[0023] In addition to the repeat units which are derived from the polyolefin-based macromonomers, the inventive comb polymers comprise repeat units which are derived from low molecular weight monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers. These monomers are widely known in the technical field.

[0024] The expression “low molecular weight” makes it clear that some of the repeat units of the backbone of the comb polymer have a low molecular weight. Depending on the preparation, this molecular weight may result from the molecular weight of the monomers used to prepare the polymers. The molecular weight of the low molecular weight repeat units or of the low molecular weight monomers is preferably at most 400 g/mol, more preferably at most 200 g/mol and most preferably at most 150 g/mol.

[0025] Examples of styrene monomers having from 8 to 17 carbon atoms are styrene, substituted styrenes having an alkyl substituent in the side chain, for example α-methylstyrene and α-ethylstyrene, substituted styrenes having an alkyl substituent on the ring, such as vinyltoluene and p-methylstyrene, halogenated styrenes, for example monochlorostyrenes, dichlorostyrenes, tribromostyrenes and tetrabromostyrenes.

[0026] The expression “(meth)acrylates” encompasses acrylates and methacrylates, and also mixtures of acrylates and methacrylates. The alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group include especially (meth)acrylates which derive from saturated alcohols, such as methyl(meth)acrylate, ethyl(meth)acrylate, n-propyl(meth)acrylate, isopropyl(meth)acrylate, n-butyl(meth)acrylate, tert-butyl(meth)acrylate, pentyl(meth)acrylate, hexyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, heptyl(meth)acrylate, 2-tert-butylheptyl(meth)acrylate, octyl(meth)acrylate, 3-isopropylheptyl(meth)acrylate, nonyl(meth)acrylate, decyl(meth)acrylate; (meth)acrylates which derive from unsaturated alcohols, for example 2-propynyl(meth)acrylate, allyl(meth)acrylate, vinyl(meth)acrylate, oleyl(meth)acrylate; cycloalkyl(meth)acrylates such as cyclopentyl(meth)acrylate, 3-vinylcyclohexyl(meth)acrylate.

[0027] Preferred alkyl(meth)acrylates include from 1 to 8, more preferably from 1 to 4 carbon atoms in the alcohol group. The alcohol group here may be linear or branched.

[0028] Examples of vinyl esters having from 1 to 11 carbon atoms in the acyl group include vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate. Preferred vinyl esters include from 2 to 9, more preferably from 2 to 5 carbon atoms in the acyl group. The acyl group here may be linear or branched.

[0029] Examples of vinyl ethers having from 1 to 10 carbon atoms in the alcohol group include vinyl methyl ether, vinyl ethyl ether, vinyl propyl ether, vinyl butyl ether. Preferred vinyl ethers include from 1 to 8, more preferably from 1 to 4 carbon atoms in the alcohol group. The alcohol group here may be linear or branched.

[0030] The notation “(di)ester” means that monoesters, diesters and mixtures of esters, especially of fumaric acid and/or of maleic acid, may be used. The (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group include monomethyl fumarate, dimethyl fumarate, monoethyl fumarate, diethyl fumarate, methyl ethyl fumarate, monobutyl fumarate, dibutyl fumarate, dipentyl fumarate and dihexyl fumarate. Preferred (di)alkyl fumarates comprise from 1 to 8, more preferably from 1 to 4 carbon atoms in the alcohol group. The alcohol group here may be linear or branched.

[0031] The (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group include monomethyl maleate, dimethyl maleate, monoethyl maleate, diethyl maleate, methyl ethyl maleate, monobutyl maleate, dibutyl maleate. Preferred (di)alkyl maleates comprise from 1 to 8, more preferably from 1 to 4 carbon atoms in the alcohol group. The alcohol group here may be linear or branched.

[0032] In addition to the repeat units detailed above, the inventive comb polymers may comprise further repeat units which are derived from further comonomers, their proportion being at most 20% by weight, preferably at most 10% by weight and more preferably at most 5% by weight, based on the weight of the repeat units.

[0033] These also include repeat units which are derived from alkyl(meth)acrylates having from 11 to 30 carbon atoms in the alcohol group, especially undecyl(meth)acrylate, 5-methylundecyl(meth)acrylate, dodecyl(meth)acrylate, 2-methyldodecyl(meth)acrylate, tridecyl(meth)acrylate, 5-methyltridecyl(meth)acrylate, tetradecyl(meth)acrylate, pentadecyl(meth)acrylate, hexadecyl(meth)acrylate, 2-methylhexa-decyl(meth)acrylate, heptadecyl(meth)acrylate, 5-isopropylheptadecyl(meth)acrylate, 4-tert-butyl-octadecyl(meth)acrylate, 5-ethyloctadecyl(meth)acrylate, 3-isopropyloctadecyl(meth)acrylate octadecyl(meth)acrylate, nonadecyl(meth)acrylate, eicosyl(meth)acrylate, cetyleicosyl(meth)acrylate, stearyleicosyl(meth)acrylate, docosyl(meth)acrylate and/or eicosyltetratriacontyl(meth)acrylate.

[0034] These also include repeat units which are derived from dispersing oxygen- and nitrogen-functionalized monomers, as listed below by way of example:

[0035] These include repeat units which are derived from aminoalkyl(meth)acrylates, such as

[0036] N,N-dimethylaminoethyl(meth)acrylate,

[0037] N,N-dimethylaminopropyl(meth)acrylate,

[0038] N,N-diethylaminopentyl(meth)acrylate,

[0039] N,N-dibutylaminohexadecyl(meth)acrylate.

[0040] These include repeat units which are derived from aminoalkyl(meth)acrylamides, such as

[0041] N,N-dimethylaminopropyl(meth)acrylamide.

[0042] These include repeat units which are derived from hydroxyalkyl(meth)acrylates, such as

[0043] 3-hydroxypropyl(meth)acrylate,

[0044] 3,4-dihydroxybutyl(meth)acrylate,

[0045] 2-hydroxyethyl(meth)acrylate,

[0046] 2-hydroxypropyl(meth)acrylate,

[0047] 2,5-dimethyl-1,6-hexanediol(meth)acrylate,

[0048] 1,10-decanediol(meth)acrylate.

[0049] These include repeat units which are derived from heterocyclic(meth)acrylates, such as

[0050] 2-(1-imidazolyl)ethyl(meth)acrylate,

[0051] 2-(4-morpholinyl)ethyl(meth)acrylate,

[0052] 1-(2-methacryloyloxyethyl)-2-pyrrolidone,

[0053] N-methacryloylmorpholine,

[0054] N-methacryloyl-2-pyrrolidinone,

[0055] N-(2-methacryloyloxyethyl)-2-pyrrolidinone,

[0056] N-(3-methacryloyloxypropyl)-2-pyrrolidinone.

[0057] These include repeat units which are derived from heterocyclic vinyl compounds, such as 2-vinylpyridine, 4-vinylpyridine, 2-methyl-5-vinylpyridine, 3-ethyl-4-vinylpyridine, 2,3-dimethyl-5-vinylpyridine, vinylpyrimidine, vinylpiperidine, 9-vinylcarbazole, 3-vinylcarbazole, 4-vinylcarbazole, 1-vinylimidazole, 2-methyl-1-vinylimidazole, N-vinylpyrrolidone, N-vinylpyrrolidine, 3-vinylpyrrolidine, N-vinylcaprolactam, N-vinylbutyrolactam, vinyloxolane, vinylfuran, vinyloxazoles and hydrogenated vinyloxazoles.

[0058] The aforementioned ethylenically unsaturated monomers may be used individually or as mixtures. It is additionally possible to vary the monomer composition during the polymerization of the main chain in order to obtain defined structures, for example block copolymers.

[0059] According to the invention, the comb polymers have a molar degree of branching in the range from 0.1 to 10 mol %, preferably from 0.8 to 6 mol %, more preferably from 0.8 to 3.4 mol % and especially preferably from 1.0 to 3.1 and most preferably from 1.4 to 2.8. The molar degree of branching of the comb polymers f_branch is calculated by the formula

$f_{\mathrm{branch}}=\frac{\sum _{a=1}^An_a}{\sum _{a=1}^An_a+\sum _{b=1}^Bn_b}$

[0060] where

• • [0061] A=number of types of repeat units which are derived from polyolefin-based macromonomers,
  • [0062] B=number of types of repeat units which are derived from low molecular weight monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers,
  • [0063] n_a=number of repeat units which are derived from polyolefin-based macromonomers of the type a in the comb polymer molecule
  • [0064] n_b=number of repeat units which are derived from low molecular weight monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers, of type b in the comb polymer molecule.

[0065] The molar degree of branching arises generally from the ratio of the monomers used if the comb polymer has been prepared by copolymerization of low molecular weight and macromolecular monomers. For the calculation, it is possible here to use the number-average molecular weight of the macromonomer.

[0066] In a particular aspect of the present invention, the comb polymer, especially the main chain of the comb polymer, may have a glass transition temperature in the range from −60 to 110° C., preferably in the range from −30 to 100° C, more preferably in the range from 0 to 90° C. and most preferably in the range from 20 to 80° C. The glass transition temperature is determined by DSC. The glass transition temperature can be estimated via the glass transition temperature of the corresponding homopolymers taking account of the proportions of the repeat units in the main chain.

[0067] If the comb polymer has been obtained by polymer-analogous reaction or by graft copolymerization, the molar degree of branching is found by known methods of determining the conversion.

[0068] The proportion of at least 80% by weight, preferably at least 90% by weight, of low molecular weight repeat units which are derived from monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers, and of repeat units which are derived from polyolefin-based macromonomers, is based on the weight of the repeat units. In addition to the repeat units, polymers generally also comprise start groups and end groups which can form through initiation reactions and termination reactions. In a particular aspect of the present invention, the statement of at least 80% by weight, preferably at least 90% by weight, of low molecular weight repeat units which are derived from monomers selected from the group consisting of styrene monomers having from 8 to 17 carbon atoms, alkyl(meth)acrylates having from 1 to 10 carbon atoms in the alcohol group, vinyl esters having from 1 to 11 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl fumarates having from 1 to 10 carbon atoms in the alcohol group, (di)alkyl maleates having from 1 to 10 carbon atoms in the alcohol group, and mixtures of these monomers, and of repeat units which are derived from polyolefin-based macromonomers, is based on the total weight of the comb polymers. The polydispersity of the comb polymers is obvious to the person skilled in the art. These data are therefore based on a mean value over all comb polymers.

[0069] The inventive comb polymers can be prepared in various ways. A preferred process consists in the free-radical polymerization, which is known per se, of low molecular weight monomers and macromolecular monomers.

[0070] For instance, these polymers can be effected especially by free-radical polymerization, and also related processes for controlled free-radical polymerization, for example ATRP (=Atom Transfer Radical Polymerization) or RAFT (=Reversible Addition Fragmentation Chain Transfer).

[0071] Customary free-radical polymerization is explained, inter alia, in Ullmanns's Encyclopedia of Industrial Chemistry, Sixth Edition. In general, a polymerization initiator and a chain transfer are used for this purpose.

[0072] The usable initiators include the azo initiators well known in the technical field, such as AIBN and 1,1-azo-biscyclohexanecarbonitrile, and also peroxy compounds such as methyl ethyl ketone peroxide, acetylacetone peroxide, dilauryl peroxide, tert-butyl per-2-ethyl-hexanoate, ketone peroxide, tert-butyl peroctoate, methyl isobutyl ketone peroxide, cyclohexanone peroxide, dibenzoyl peroxide, tert-butyl peroxybenzoate, tert-butyl peroxyisopropylcarbonate, 2,5-bis(2-ethylhexanoylperoxy)-2,5-dimethylhexane, tert-butyl peroxy-2-ethylhexanoate, tert-butyl peroxy-3,5,5-trimethylhexanoate, dicumyl peroxide, 1,1-bis-(tert-butylperoxy)cyclohexane, 1,1-bis(tert-butyl-peroxy)-3,3,5-trimethylcyclohexane, cumyl hydro-peroxide, tert-butyl hydroperoxide, bis(4-tert-butyl-cyclohexyl)peroxydicarbonate, mixtures of two or more of the aforementioned compounds with one another, and also mixtures of the aforementioned compounds with compounds which have not been mentioned and can likewise form free radicals. Suitable chain transferers are especially oil-soluble mercaptans, for example n-dodecyl mercaptan or 2-mercaptoethanol, or else chain transferers from the class of the terpenes, for example terpinolene.

[0073] The ATRP process is known per se. It is assumed that this is a “living” free-radical polymerization, without any intention that this should restrict the description of the mechanism. In these processes, a transition metal compound is reacted with a compound which has a transferable atom group. This transfers the transferable atom group to the transition metal compound, which oxidizes the metal. This reaction forms a radical which adds onto ethylenic groups. However, the transfer of the atom group to the transition metal compound is reversible, so that the atom group is transferred back to the growing polymer chain, which forms a controlled polymerization system. The structure of the polymer, the molecular weight and the molecular weight distribution can be controlled correspondingly.

[0074] This reaction is described, for example, by J-S. Wang, et al., J. Am. Chem. Soc., vol. 117, p. 5614-5615 (1995), by Matyjaszewski, Macromolecules, vol. 28, p. 7901-7910 (1995). In addition, the patent applications WO 96/30421, WO 97/47661, WO 97/18247, WO 98/40415 and WO 99/10387, disclose variants of the ATRP explained above.

[0075] In addition, the inventive polymers may be obtained, for example, also via RAFT methods. This process is presented in detail, for example, in WO 98/01478 and WO 2004/083169, to which reference is made explicitly for the purposes of disclosure.

[0076] The polymerization may be carried out at standard pressure, reduced pressure or elevated pressure. The polymerization temperature too is uncritical. However, it is generally in the range of −20°-200° C., preferably 50°-150° C. and more preferably 80°-130° C.

[0077] The polymerization may be carried out with or without solvent. The term solvent is to be understood here in a broad sense. The solvent is selected according to the polarity of the monomers used, preference being given to using 100N oil, relatively light gas oil and/or aromatic hydrocarbons, for example toluene or xylene.

[0078] The low molecular weight monomers to be used to prepare the inventive comb polymers in a free-radical copolymerization are generally commercially available.

[0079] Macromonomers usable in accordance with the invention have exactly one double bond, which is preferably terminal.

[0080] The double bond may be present as a result of the preparation of the macromonomers. For example, a cationic polymerization of isobutylene forms a polyisobutylene (PIB) which has a terminal double bond.

[0081] In addition, functionalized polyolefinic groups may be converted to a macromonomer by suitable reactions.

[0082] For example, macroalcohols and/or macroamines based on polyolefins may be subjected to a transesterification or aminolysis with low molecular weight monomers which have at least one unsaturated ester group, for example methyl(meth)acrylate or ethyl(meth)acrylate.

[0083] This transesterification is widely known. For example, a heterogeneous catalyst system can be used for this purpose, such as lithium hydroxide/calcium oxide mixture (LiOH/CaO), pure lithium hydroxide (LiOH), lithium methoxide (LiOMe) or sodium methoxide (NaOMe) or a homogeneous catalyst system, such as isopropyl titanate (Ti(OiPr)₄) or dioctyltin oxide (Sn(Oct)₂O). The reaction is an equilibrium reaction. The low molecular weight alcohol released is therefore typically removed, for example, by distillation.

[0084] In addition, these macromonomers can be obtained by a direct esterification or direct amidation proceeding, for example, from methacrylic acid or methacrylic anhydride, preferably with acidic catalysis by p-toluenesulfonic acid or methanesulfonic acid or from free methacrylic acid by the DCC method (dicyclohexyl-carbodiimide).

[0085] In addition, the present alcohol or the amide can be converted to a macromonomer by reaction with an acid chloride, such as (meth)acryloyl chloride.

[0086] In addition, it is also possible to prepare a macroalcohol via the reaction of the terminal PIB double bond, as forms in cationically polymerized PIB, with maleic anhydride (ene reaction) and subsequent reaction with an α,ω-amino alcohol.

[0087] Moreover, suitable macromonomers can be obtained by reacting a terminal PIB double bond with methacrylic acid or by a Friedel-Crafts alkylation of the PIB double bond onto styrene.

[0088] In the preparations of the macromonomers detailed above, preference is given to using polymerization inhibitors, for example 4-hydroxy-2,2,6,6-tetramethyl-piperidine oxyl radical or hydroquinone monomethyl ether.

[0089] The macroalcohols and/or macroamines which are based on polyolefins and are to be used for the reactions detailed above can be prepared in a known manner.

[0090] In addition, some of these macroalcohols and/or macroamines are commercially available.

[0091] The commercially available macroamines include, for example, Kerocom® PIBA 03. Kerocom® PIBA 03 is a polyisobutylene (PIB) of M_n=1000 g/mol which has been NH₂-functionalized to an extent of about 75% by weight and is supplied as a concentrate of about 65% by weight in aliphatic hydrocarbons by BASF AG (Ludwigshafen, Germany).

[0092] A further product is Kraton Liquid® L-1203, a hydrogenated polybutadiene which has been OH-functionalized to an extent of about 98% by weight (also known as olefin copolymer OCP) and has about 50% each of 1.2 repeat units and 1.4 repeat units of M_n=4200 g/mol, from Kraton Polymers GmbH (Eschborn, Germany).

[0093] Further suppliers of suitable macroalcohols based on hydrogenated polybutadiene are Cray Valley (Paris), a daughter company of Total (Paris), and the Sartomer Company (Exton/Pa./USA).

[0094] The preparation of macroamines is described, for example, in EP 0 244 616 to BASF AG. The macroamines are prepared via hydroformylation and amination, preferably of polyisobutylene. Polyisobutylene offers the advantage of exhibiting no crystallization at low temperatures.

[0095] Advantageous macroalcohols may additionally be prepared according to the known patents to BASF AG, either via hydroboration (WO 2004/067583) of highly reactive polyisobutylene HR-PIB (EP 0 628 575), which contains an elevated proportion of terminal α-double bonds, or by hydroformylation followed by hydrogenation (EP 0 277 345). Compared to hydroformylation and hydrogenation, hydroboration affords higher alcohol functionalities.

[0096] Preferred macroalcohols based on hydrogenated polybutadienes can be obtained according to GB 2270317 to Shell International Research Maatschappij. A high proportion of 1.2 repeat units of about 60% and more can lead to significantly lower crystallization temperatures.

[0097] Some of the macromonomers detailed above are also commercially available, for example Kraton Liquid® L-1253, which is produced from Kraton Liquid® L-1203 and is a hydrogenated polybutadiene which has been methacrylate-functionalized to an extent of about 96% by weight and has about 50% each of 1.2 repeat units and 1.4 repeat units, from Kraton Polymers GmbH (Eschborn, Germany).

[0098] Kraton® L-1253 was synthesized according to GB 2270317 to Shell International Research Matschappij.

[0099] Macromonomers based on polyolefins and their preparation are also detailed in EP 0 621 293 and EP 0 699 694.

[0100] In addition to a free-radical copolymerization of macromonomers and low molecular weight monomers which has been detailed above, the inventive comb polymers may be obtained by polymer-analogous reactions.

[0101] In these reactions, a polymer is first prepared in a known manner from low molecular weight monomers and is then converted. In this case, the backbone of a comb polymer may be synthesized from a reactive monomer such as maleic anhydride, methacrylic acid or else glycidyl methacrylate and other unreactive short-chain backbone monomers. In this case, the initiator systems detailed above, such as t-butyl perbenzoate or t-butyl per-2-ethylhexanoate, and regulators such as n-dodecylmercaptan may find use.

[0102] In a further step, for example in an alcoholysis or aminolysis, the side chains, which are also referred to as arms, may be generated. In this reaction, the macroalcohols and/or macroamines detailed above may be used.

[0103] The reaction of the initially formed backbone polymer with macroalcohols and/or macroamines corresponds essentially to the reactions detailed above of the macroalcohols and/or macroamines with low molecular weight compounds.

[0104] For example, the macroalcohols and/or macroamines may be converted to the inventive comb polymers in grafting reactions known per se, for example onto the present maleic anhydride or methacrylic acid functionalities in the backbone polymer with catalysis, for example, by p-toluenesulfonic acid or methanesulfonic acid to give esters, amides or imides. Addition of low molecular weight alcohols and/or amines, such as n-butanol or N-(3-aminopropyl)morpholine, allows this polymer-analogous reaction to be conducted to complete conversions, especially in the case of maleic anhydride backbones.

[0105] In the case of glycidyl functionalities in the backbone, an addition of the macroalcohol and/or of the macroamine can be performed so as to form comb polymers.

[0106] In addition, the macroalcohols and/or the macroamines can be converted by a polymer-analogous alcoholysis or aminolysis with a backbone which contains short-chain ester functionalities in order to generate comb polymers.

[0107] In addition to the reaction of the backbone polymer with macromolecular compounds, suitably functionalized polymers which have been obtained by reacting low molecular weight monomers with further low molecular weight monomers to form comb polymers can be reacted. In this case, the initially prepared backbone polymer has a plurality of functionalities which serve as initiators of multiple graft polymerizations.

[0108] For instance, a multiple cationic polymerization of i-butene can be initiated, which leads to comb polymers with polyolefin side arms. Suitable processes for such graft copolymerizations are also the ATRP and/or RAFT processes detailed above in order to obtain comb polymers with a defined architecture.

[0109] In a particular aspect of the present invention, the comb polymer of the present invention has a low proportion of olefinic double bonds. The iodine number is preferably less than or equal to 0.2 g per g of comb polymer, more preferably less than or equal to 0.1 g per g of comb polymer. This proportion can be determined according to DIN 53241 after drawing off carrier oil and low molecular weight residual monomers at 180° C. under reduced pressure for 24 hours.

[0110] In a particular aspect of the present invention, the comb polymer preferably has repeat units which are derived from styrene, and repeat units which are derived from n-butyl methacrylate. The weight ratio of styrene repeat units and n-butyl methacrylate repeat units is preferably in the range of 90:10 to 10:90, more preferably 80:20 to 20:80.

[0111] In a further preferred embodiment of the present invention, the comb polymer preferably has repeat units which are derived from styrene, and repeat units which are derived from n-butyl acrylate. The weight ratio of styrene repeat units and n-butyl acrylate repeat units is preferably in the range of 90:10 to 10:90, more preferably 80:20 to 20:80.

[0112] In a further preferred feature of the present invention, the comb polymer preferably has repeat units which are derived from methyl methacrylate and repeat units which are derived from n-butyl methacrylate. The weight ratio of methyl methacrylate repeat units and n-butyl methacrylate repeat units is preferably in the range of 50:50 to 0:100, more preferably 30:70 to 0:100.

[0113] The inventive comb polymer can preferably be used in a lubricant oil composition. A lubricant oil composition comprises at least one lubricant oil.

[0114] The lubricant oils include especially mineral oils, synthetic oils and natural oils.

[0115] Mineral oils are known per se and commercially available. They are generally obtained from mineral oil or crude oil by distillation and/or refining and optionally further purification and finishing processes, the term mineral oil including in particular the higher-boiling fractions of crude or mineral oil. In general, the boiling point of mineral oil is higher than 200° C., preferably higher than 300° C., at 5000 Pa. The production by low-temperature carbonization of shale oil, coking of bituminous coal, distillation of brown coal with exclusion of air, and also hydrogenation of bituminous or brown coal is likewise possible. Mineral oils are also produced in a smaller proportion from raw materials of vegetable (for example from jojoba, rapeseed) or animal (for example neatsfoot oil) origin. Accordingly, mineral oils have, depending on their origin, different proportions of aromatic, cyclic, branched and linear hydrocarbons.

[0116] In general, a distinction is drawn between paraffin-base, naphthenic and aromatic fractions in crude oils or mineral oils, in which the term paraffin-base fraction represents longer-chain or highly branched isoalkanes, and naphthenic fraction represents cyclo-alkanes. In addition, mineral oils, depending on their origin and finishing, have different fractions of n-alkanes, isoalkanes having a low degree of branching, known as mono-methyl-branched paraffins, and compounds having heteroatoms, in particular O, N and/or S, to which a degree of polar properties are attributed. However, the assignment is difficult, since individual alkane molecules may have both long-chain branched groups and cycloalkane radicals, and aromatic parts. For the purposes of the present invention, the assignment can be effected to DIN 51 378, for example. Polar fractions can also be determined to ASTM D 2007.

[0117] The fraction of n-alkanes in preferred mineral oils is less than 3% by weight, the fraction of O—, N— and/or S-containing compounds less than 6% by weight. The fraction of the aromatics and of the mono-methyl-branched paraffins is generally in each case in the range from 0 to 40% by weight. In one interesting aspect, mineral oil comprises mainly naphthenic and paraffin-base alkanes which have generally more than 13, preferably more than 18 and most preferably more than 20 carbon atoms. The fraction of these compounds is generally ≧60% by weight, preferably ≧80% by weight, without any intention that this should impose a restriction. A preferred mineral oil contains from 0.5 to 30% by weight of aromatic fractions, from 15 to 40% by weight of naphthenic fractions, from 35 to 80% by weight of paraffin-base fractions, up to 3% by weight of n-alkanes and from 0.05 to 5% by weight of polar compounds, based in each case on the total weight of the mineral oil.

[0118] An analysis of particularly preferred mineral oils, which was effected by means of conventional processes such as urea separation and liquid chromatography on silica gel, shows, for example, the following constituents, the percentages relating to the total weight of the particular mineral oil used:

[0119] n-alkanes having from approx. 18 to 31 carbon atoms:

[0120] 0.7-1.0%,

[0121] slightly branched alkanes having from 18 to 31 carbon atoms:

[0122] 1.0-8.0%,

[0123] aromatics having from 14 to 32 carbon atoms:

[0124] 0.4-10.7%,

[0125] iso- and cycloalkanes having from 20 to 32 carbon atoms:

[0126] 60.7-82.4%,

[0127] polar compounds:

[0128] 0.1-0.8%,

[0129] loss:

[0130] 6.9-19.4%.

[0131] Valuable information with regard to the analysis of mineral oils and a list of mineral oils which have a different composition can be found, for example, in Ullmann's Encyclopedia of Industrial Chemistry, 5th Edition on CD-ROM, 1997, under “lubricants and related products”.

[0132] Synthetic oils include organic esters, for example diesters and polyesters, polyalkylene glycols, polyethers, synthetic hydrocarbons, especially polyolefins, among which preference is given to polyalphaolefins (PAO), silicone oils and perfluoro-alkyl ethers. They are usually somewhat more expensive than the mineral oils, but have advantages with regard to their performance.

[0133] Natural oils are animal or vegetable oils, for example neatsfoot oils or jojoba oils.

[0134] These lubricant oils may also be used as mixtures and are in many cases commercially available.

[0135] The concentration of the comb polymer in the lubricant oil composition is preferably in the range from 0.1 to 40% by weight, more preferably in the range from 1 to 20% by weight, based on the total weight of the composition.

[0136] In addition to the aforementioned components, a lubricant oil composition may comprise further additives.

[0137] These additives include antioxidants, corrosion inhibitors, antifoams, antiwear components, dyes, dye stabilizers, detergents, pour point depressants and/or DI additives.

[0138] In addition, these additives comprise viscosity index improvers, dispersing assistants and/or friction modifiers, which are more preferably based on a linear polyalkyl(meth)acrylate having from 1 to 30 carbon atoms in the alcohol group. These linear polyalkyl(meth)acrylates are described especially in the prior art discussed by way of introduction, and these polymers may have dispersing monomers.

[0139] Preferred lubricant oil compositions have a viscosity, measured at 40° C. to ASTM D 445, in the range from 10 to 120 mm²/s, more preferably in the range from 22 to 100 mm²/s.

[0140] In a particular aspect of the present invention, preferred lubricant oil compositions have a viscosity index, determined to ASTM D 2270, in the range from 100 to 400, more preferably in the range from 150 to 350 and most preferably in the range from 200 to 300.

[0141] The invention will be illustrated in detail hereinafter with reference to examples, without any intention that this should impose a restriction.

[0142] A) Preparation of Macromonomers

[0143] Various macromonomers were prepared or obtained commercially. Table 1 shows a summary of the properties of the macroalcohols and/or macroamines used to prepare macromonomers.

[0144] The macroamine 1 is the polyisobutylene-based macroamine in Kerocom® PIBA 03, which was obtained commercially from BASF AG.

[0145] The macroalcohol 2 is a polyisobutylene-based macroalcohol which has been obtained according to EP 0 277 345.

[0146] The macroalcohols 3 and 4 are polyisobutylene-based macroalcohols which have been obtained according to WO 2004/067583.

[0147] The macroalcohol 5 is a macroalcohol which is based on hydrogenated polybutadiene and has been obtained according to GB 2270317.

[0148] M_n is the number-average molecular weight, which can be determined by GPC against polyolefin standards of the same chemistry or by osmotic methods such as vapor pressure or membrane osmosis. The kinematic viscosity is described by ν and the dynamic viscosity by η (ASTM D445). The proportion of 1.2 repeat units (vinyl repeat units) over the sum of 1.2 repeat units and 1.4 repeat units, as can be determined for (hydrogenated) polybutadiene by ¹H NMR spectroscopy, is given by f_vinyl. The melting point correlating to f_vinyl by DSC is reported as T_m.

	TABLE 1
		ν40°C	ν100°C	η25°C	η50°C	η75°C	fvinyl
	Mn [g/mol]	[mm2/s]	[mm2/s]	[mPas]	[mPas]	[mPas]	[%]	Tm [%]
Macro-	1000	4650	190				n.a.	n.a.
amine 1
Macro-	2300	48 000	1500				n.a.	n.a.
alcohol 2
Macro-	2300	48 000	1500				n.a.	n.a.
alcohol 3
Macro-	4800						n.a.	n.a.
alcohol 4
Macro-	4300			56 000			58	−29
alcohol 5
Kraton ®	4200			35 000	4800	1300	50	−17
L-1203
The abbreviation “n.a.” means that it was not possible to measure a melting point.

[0149] The macromonomer derived from macroamine is prepared by aminolysis of MMA. For this purpose, 1850 g of Kerocom® PIBA 03 (contains 35% aliphatic hydrocarbons) are dissolved in 1200 g of MMA with stirring at 60° C. 0.6 g of hydroquinone monomethyl ether and 0.12 g of 4-hydroxy-2,2,6,6-tetramethylpiperidino oxyl radical are added to the solution. After heating to MMA reflux (about 100° C.) with stabilized passage of air, about 30 g of MMA are distilled off for azeotropic drying. After cooling, 24 g of Sn(Oct)₂O are added and the mixture is heated to MMA reflux. At this temperature, the mixture is allowed to react for three hours. After cooling, 1000 g of water are added for catalyst precipitation and the mixture is stirred for 4 h. The biphasic mixture is separated in a separating funnel and the lower water phase is discarded. The upper organic phase is stirred with 10 g of kieselguhr (Celatom® FW-80) and filtered through a pressure filter (Seitz K800). Excess MMA and aliphatic hydrocarbons are drawn off on a vacuum rotary evaporator and the product is degassed. 1300 g of macromonomer are obtained.

[0150] The macromonomers derived from macroalcohols are prepared by transesterifying MMA. For this purpose, about 350 g of macroalcohol in each case are dissolved in 350 g of MMA with stirring at 60° C. for 12 hours. 200 mg of hydroquinone monomethyl ether and 20 mg of 4-hydroxy-2,2,6,6-tetramethylpiperidino oxyl radical are added to the solution. After heating to MMA reflux (about 100° C.) with stabilized passage of air, about 30 g of MMA are distilled off for azeotropic drying. After cooling, 2.7 g of LiOMe are added and heated to reflux of the methanol/MMA azeotrope (about 64° C.). The methanol/MMA azeotrope is distilled off constantly until a constant top temperature of about 100° C. is established. At this temperature, the mixture is allowed to continue to react for a further hour. After cooling, insoluble catalyst residues are removed under hot conditions by pressure filtration (Seitz T1000 depth filter). The product is finally degassed on a vacuum rotary evaporator. 350 g of macromonomer are obtained.

[0151] In the case of macroalcohols of relatively high molecular weights, the addition of KPE 100N oil at the start of the macromonomer synthesis may be helpful. The content of KPE 100N oil entrained into the comb polymer syntheses described below should be taken into account appropriately.

[0152] Kraton Liquid® L-1253 is a methacrylate-functionalized hydrogenated polybutadiene which is prepared from the OH-functionalized hydrogenated polybutadiene Kraton Liquid® L-1203, and has been obtained commercially from Kraton Polymers GmbH (Eschborn, Germany).

[0153] The macromonomer functionality f_MM of each and every macromonomer was derived from the GPC curves of the comb polymers themselves. The GPC method for determining the mass-average molecular weight M_w and the polydispersity index PDI of the comb polymers is described below. The measurements were effected in tetrahydrofuran at 35° C. against a polymethyl methacrylate calibration curve from a set of ≧25 standards (Polymer Standards Service or Polymer Laboratories) whose M_peak was in a uniform logarithmic distribution over the range from 5·10⁶ to 2·10² g/mol. A combination of six columns (Polymer Standards Service SDV 100 Å/2× SDV LXL/2× SDV 100 Å/Shodex KF-800D) was used. To record the signal, an RI detector (Agilent 1100 Series) was used. The macromonomer functionality f_MM was then determined by simple calculation from the ratio f between remaining integral area under the GPC trace of the macromonomer to the total integral under macromonomer and actual comb polymer as f_MM=1−f/w_MM. In this formula, w_MM specifies the weight fraction of macromonomer weighed in based on all monomers. The values determined for the macromonomer functionality f_MM are compiled in table 2. The same response factors for all repeat units were assumed. The polymerizations of the comb polymer syntheses were performed up to complete conversion of low molecular weight backbone monomers (nBMA, Sty, nBA, MMA and DiBF) with conversions of >99% (HPLC).

[0154] The properties of the compounds obtained are shown in table 2.

	TABLE 2
			fMM
	Compound obtained	Compound used	[%]
	Macromonomer 1	Macroamine 1	75
	Macromonomer 2	Macroalcohol 2	59
	Macromonomer 3	Macroalcohol 3	77
	Macromonomer 4	Macroalcohol 4	54
	Macromonomer 5	Macroalcohol 5	83
	Kraton ® L-1253	Kraton ® L-1203	96

[0155] B) Syntheses of the Comb Polymers

[0156] An apparatus with 4-neck flask and precision glass saber stirrer is initially charged with a 150 g mixture of low molecular weight monomers and macromonomer whose composition is shown in table 3, and also 65 g of Shell Risella 907 oil and 35 g of KPE 100N oil. After heating to 120° C. under nitrogen, 0.9 g of t-butyl perbenzoate is added and the temperature is maintained. 3 h and 6 h after the first initiator addition, another 0.3 g of t-butyl perbenzoate each time is supplied and the mixture is stirred at 120° C. overnight. The next day, the mixture is diluted with 125 g of KPE 100 oil. 375 g of a 40% solution of comb polymers in mineral oil are obtained.

[0157] An apparatus with 4-neck flask and precision glass saber stirrer is initially charged with a 150 g mixture of low molecular weight monomers and macromonomer whose composition is shown in table 3, and also 65 g of Shell Risella 907 oil and 35 g of KPE 100N oil. After heating to 90° C. under nitrogen, 0.3 g of t-butyl per-2-ethyl hexanoate is added and the temperature is maintained. 3 h and 6 h after the first initiator addition, another 0.3 g of t-butyl per-2-ethylhexanoate each time is supplied and the mixture is stirred at 90° C. overnight. The next day, the mixture is diluted with 125 g of KPE 100 oil. 375 g of a 40% solution of comb polymers in mineral oil are obtained.

[0158] An apparatus with 4-neck flask and precision glass saber stirrer is initially charged with a 150 g mixture of low molecular weight monomers and macromonomer whose composition is shown in table 3, and also 100 g of toluene. After heating to 90° C. under nitrogen, 0.3 g of t-butyl per-2-ethyl hexanoate is added and the temperature is maintained. 2 h, 4 h, 6 h and 8 h after the first initiator addition, another 0.3 g of t-butyl per-2-ethylhexanoate each time is supplied and the mixture is stirred at 90° C. overnight. The next day, the mixture is diluted with 225 g of KPE 100 oil and the toluene is removed by degassing on a vacuum rotary evaporator. 375 g of a 40% solution of comb polymers in mineral oil are obtained.

[0159] Taking account of the net composition of macromonomer and low molecular weight monomers which form the 150 g and the macromonomer functionality f_MM, the net composition in terms of mass proportions and additionally, taking account of the molar masses of the monomers, the molar degree of branching f_branch was determined for each comb polymer. The resulting values are shown in table 3. Moreover, the molecular weights and PDIs by GPC in tetrahydrofuran, which is a good solvent for all segments of the comb polymers, according to the method described above are reported.

[0160] Moreover, after drawing off carrier oil and low molecular weight residual monomers at 180° C. under reduced pressure for 24 hours, the comb polymers were analyzed by DSC. To this end, a sample amount of 10 mg was analyzed in a perforated DSC pan in the range from −80° C. to +130° C. at 10 K/min (Pyris 1, Perkin-Elmer). The glass transition T_G of the backbone was determined from the second heating curve in each case (table 3).

	TABLE 3
		Net polymer
	Monomer mixture	composition
	Net composition [% by wt.]	[% by wt.]
Example 1	Kraton ® L-1253	Sty	nBMA	44	41	15
	45.0	40.0	15.0
Example 2	Macromonomer 2	Sty	nBMA	31	52	17
	43.1	42.6	14.3
Example 3	Macromonomer 2	Sty	nBMA	31	44	24
	37.2	40.6	22.0
Example 4	Kraton ® L-1253	Sty	nBMA	44	36	20
	45.0	35.6	19.4
Example 5	Macromonomer 4	Sty	nBMA	38	40	22
	53.3	30.4	16.3
Example 6	Macromonomer 5	Sty	nBMA	36	13	52
	40.0	12.0	48.0
Example 7	Macromonomer 2	Sty	DiBF	32	44	24
	44.0	36.0	20.0
Comparative	Macromonomer 2	Sty	nBMA	73	17	9
example 1	82.2	11.6	6.2
Comparative	Macromonomer2	Sty	nBMA	1	64	35
example 2	2.5	63.0	34.5
Comparative	Macromonomer 2	Sty	C12-	28	24	48
example 3	40.0	20.0	15MA
			40.0
Comparative	Macromonomer 2	Sty	C12-	13	44	44
example 4	20.0	40.0	15MA
			40.0
Example 8	Macromonomer 2	nBMA	MMA	37	51	13
	49.4	40.5	10.1
Example 9	Kraton ® L-1253	nBMA	MMA	44	50	6
	45.0	49.5	5.5
Example 10	Macromonomer 1	nBMA		41	59
	48.1	51.9
Example 11	Macromonomer 2	nBMA		27	73
	39.0	61.0
Example 12	Kraton ® L-1253	Sty	nBA	44	43	13
	45.0	42.1	12.9
Example 13	Macromonomer 2	Sty	nBA	35	49	15
	48.1	39.6	12.3
Comparative		C12-
example 5		15MA
		100.0
Comparative		C12/14/	MMA
example 6		16/18MA	25.0
		75.0
					Backbone
		fbranch	Mw [g/mol]	PDI	TG [° C.]
	Example 1	2.0%	281 000	3.7	+50
	Example 2	2.0%	132 000	5.2	+59
	Example 3	2.1%	144 000	5.0
	Example 4	2.1%	270 000	5.5
	Example 5	1.4%	142 000	6.3
	Example 6	1.6%	183 000	3.9
	Example 7	2.4%			+54
	Comparative	11.5%	83 500	6.9
	example 1
	Comparative	0.07%
	example 2
	Comparative	2.8%			if
	example 3				present
					<−60
	Comparative	0.9%			if
	example 4				present
					<−60
	Example 8	3.1%	187 000	9.8	+38
	Example 9	2.4%	402 000	4.6
	Example 10	8.2%	353 000	13.4
	Example 11	2.2%	354 000	16.6
	Example 12	2.0%	181 000	3.8	+46
	Example 13	2.4%	79 100	4.1
	Comparative	n.a.	24 000	1.9
	example 5
	Comparative	n.a.	43 000	2.0
	example 6
	In table 3:
	Sty: styrene
	MMA: methyl methacrylate
	nBMA: n-butyl methacrylate
	nBA: n-butyl acrylate
	DiBF: diisobutyl fumarate
	C12-15MA: alkyl methacrylate mixture having from 12 to 15 carbon atoms in the alcohol radicals
	C12/14/16/18MA: alkyl methacrylate mixture having 12, 14, 16 and 18 carbon atoms in the alcohol radicals

[0161] Evaluation of the Comb Polymers

[0162] The comb polymer additives obtained are characterized via VI measurements to ASTM D2270 and via PSSI measurements to ASTM D2603 Ref. B (12.5 min ultrasound) or to DIN 51381 (30 cycles of a Bosch pump) of a solution of established kinematic viscosity at 100° C. KV100=14.0 mm²/s (ASTM D445) in a 150N base oil (KV40=31.68 mm²/s, KV100=5.42 mm²/s, VI=105).

[0163] It is shown clearly that the inventive comb polymers have a significantly better relationship of VI, PSSI and solids content than the polymers detailed in the prior art according to EP 0699694. The results of the evaluation detailed are shown in table 4.

TABLE 4
				PSSI to
				DIN
	Net polymer		PSSI to	51382
	content [%]		ASTM D2603	(30
	in 150N test		Ref. B	cycles
Polymer	oil for	VI at	(12.5	of
according	KV100 =	KV100 =	min	Bosch
to	14 mm2/s	14 mm2/s	ultrasound)	pump)
Example 1	5.05	249	23.4	2.1
Example 2	9.24	254	4
Example 3	7.96	255	6.5	0.0
Example 4	5.83	245	15.1	1.6
Example 7	11.34	224
Example 9	4.4	263	29.4	3.8
Example 11	5.81	284		4.7
Comparative	7.41	169	36.9
example 1
Comparative	insoluble
example 2
Comparative	6.21	173		11.3
example 3
Comparative	5.95	164		18.2
example 4

[0164] In addition, comb polymers according to the present invention were compared with linear, exceptionally shear-stable PAMA (comparative example 5). In this case, the solids contents of the polymers were adjusted to a solution viscosity of KV100=13.15 mM²/s in a VII-free D/I package-containing API group III base oil composed of polyalphaolefin and hydrocrack oil (KV100=5.15 mm²/s, KV40=25.30 mm²/s, VI=137, pour point −45° C. to ASTM D97). Here too, significant advantages in the polymer content and also VI are found with comparable or even better PSSI to DIN 51350 part 6 (20 h or 192 h, tapered roller bearing). In the dynamic low-temperature viscosity at −40° C. to DIN 51398 and the pour point to ASTM D97 too, exceptionally advantageous values are found for the comb polymers. The comparison of example 6 with example 12 shows additionally that comb polymers which are based on OCP macromonomers of elevated proportion of 1.2 repeat units are significantly better in their low-temperature properties. The results obtained from the analyses detailed above are shown in table 5.

TABLE 5
	Net polymer
	content [%]
	in D/I		PSSI to	PSSI to
	package-		DIN 51350	DIN 51350
	containing		part 6	part 6
	group III		(20 h,	(192 h,
Polymer	base oil for	VI at	tapered	tapered
according	KV100 =	KV100 =	roller	roller
to	13.15 mm2/s	12.15 mm2/s	bearing)	bearing)
Example 2	11.2	266	12.2
Example 5	10.2	259	20.2	46.1
Example 6	7.6	261
Example 8	10.0	242	24.8
Example 12	7.9	239	16.1	43.5
Example 13	10.4	213	10.6
Comparative	22.1	176	19.0	45.0
example 5
		Dynamic viscosity
		at −40° C. to DIN	Pour point to
	Polymer	51398 in a liquid	ASTM D97
	according to	bath [mPas]	[° C.]
	Example 2	19 600	−45
	Example 5	25 900
	Example 6	34 000	−45
	Example 8	29 300	−45
	Example 12	solid	−27
	Example 13	37 500

[0165] Moreover, a comb polymer was used as a VII in an ISO46/VI160 hydraulic oil formulation based on API group I 100 N/600N oils and, in the PSSI to DIN 51350 (part 6, 20 h, tapered roller bearing), compared to a linear PAMA (comparative example 6). It was found that an exceptionally high reduction in the necessary solids content to less than 33% with equal to slightly better PSSI is possible. The compositions of the hydraulic oil formulations and the results obtained from the analysis are shown in table 6.

TABLE 6
		Oronite
	Net polymer	Oloa 4992
	content [%]	antiwear
	in	hydraulic
Polymer	ISO46/VI160	additive	600N	100N
according to	formulation	[%]	[% by wt.]	[% by wt.]
Example 12	8.3	0.6	18.5	72.6
Comparative	2.6	0.6	34.4	62.4
example 6
					PSSI to
					DIN51350
					part 6
					(20 h,
					tapered
	Polymer	KV100	KV40		roller
	according to	[mm2/s]	[mm2/s]	VI	bearing
	Example 12	8.48	46.41	161	19.2
	Comparative	8.51	46.8	161	17.4
	example 6