Method for hafnium nitride deposition

[0001] Field of the Invention

[0002] Embodiments of the present invention generally relate to methods to deposit materials on substrates, and more specifically, to methods for depositing metal oxides, metal nitrides, metal oxynitrides, metal silicates and metal silicon oxynitrides using atomic layer deposition processes.

[0003] In the field of semiconductor processing, flat-panel display processing or other electronic device processing, chemical vapor deposition has played an important role in forming films on substrates. As the geometries of electronic devices continue to shrink and the density of devices continues to increase, the size and aspect ratio of the features are becoming more aggressive, e.g., feature sizes of 0.07 microns and aspect ratios of 10 or greater are being considered. Accordingly, conformal deposition of materials to form these devices is becoming increasingly important.

[0004] While conventional chemical vapor deposition has proved successful for device geometries and aspect ratios down to 0.15 microns, the more aggressive device geometries require new, innovative deposition techniques. One technique that is receiving considerable attention is atomic layer deposition (ALD). In the scheme, reactants are sequentially introduced into a processing chamber where each reactant chemisorbs onto the surface of the substrate and a surface reaction occurs. A purge step is typically carried out between the delivery of each reactant gas. The purge step may be a continuous purge with the carrier gas or a pulse purge between the delivery of the reactant gases.

[0005] U.S. Pat. No. 6,287,965 describes a method of ALD to form a metal nitride layer having the structure of A-B-N, where A is a metal, B is an element to prevent crystallization and N is nitrogen. The preferred embodiment teaches a method to make TiAlN. No incorporation of oxygen into these films is disclosed; in fact, the invention teaches away from oxygen incorporation by sequentially stacking oxygen diffusion barrier layers between the metal nitride layers for oxygen protection.

[0006] U.S. Pat. No. 6,200,893, entitled Radical-assisted Sequential CVD, describes a method for CVD deposition on a substrate wherein radical species such as hydrogen and oxygen or hydrogen and nitrogen are used in an alternative step with a molecular precursor to form one cycle. A composite integrated film is produced by repetitive cycles of the method. In a preferred embodiment, the deposited material from the molecular precursor are metals and the radicals, in the alternate steps, are used to remove ligands left from the metal precursor reactions. The radicals oxidize or nitridize the metal surface in subsequent layers in order to respectively yield metal oxide or nitride. In various embodiments of the reference, metallic hafnium and hafnium oxide are made from a halogen-containing precursor. However, the reference does not address complex hafnium compounds (tertiary, quaternary or pentanary) produced from metal organic compounds. Furthermore, the reference requires the use of radicals to incorporate oxygen and/or nitrogen into the film.

[0007] Therefore, there is a need for a process for depositing hafnium compounds such as nitrides, silicates, oxynitrides, silicon nitrides, silicon oxynitrides, aluminum oxynitrides and aluminum silicon oxynitrides from organometallic compounds.

[0008] In one embodiment, the present invention is a method for forming a layer comprising hafnium on a substrate surface, sequentially comprising: a) exposing the substrate surface to a hafnium precursor to form a hafnium containing layer on the substrate surface; b) purging the chamber with a purge gas; c) reacting a second precursor with the hafnium containing layer; d) purging the chamber with the purge gas; e) reacting a third precursor with the hafnium containing layer; f) purging the chamber with the purge gas; g) reacting a fourth precursor with the hafnium containing layer; and h) purging the chamber with the purge gas.

[0009] In another embodiment, the present invention is a method for growing a layer comprising hafnium, comprising exposing a substrate sequentially to at least four precursors during an ALD cycle to deposit a compound film comprising hafnium and at least three elements selected from the group consisting of silicon, aluminum, oxygen and nitrogen.

[0010] In another embodiment, the present invention is a method for depositing a hafnium compound on a substrate in a chamber during an atomic layer deposition process, comprising conducting a first half reaction comprising a hafnium precursor, conducting a second half reaction comprising an oxygen precursor, conducting a third half reaction comprising a nitrogen precursor and conducting a fourth half reaction comprising a silicon precursor.

[0011] In another embodiment, the present invention is a composition of a semiconductor material, comprising HfSi_xO_yN_z, wherein x is at least about 0.2 and less than about 4, y is at least about 0.5 and less than about 4 and z is at least about 0.05 and less than about 2.

[0012] So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of the invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.

[0013] FIG. 1 is a scheme to show an example of half reactions that are used to grow a hafnium nitride film.

[0014] FIG. 2 is a scheme to show an example of half reactions that are used to grow a hafnium oxide film.

[0015] FIGS. 3A-3D are schemes to show an example of half reactions that are used to grow a hafnium silicate film.

[0016] FIGS. 4A-4D are schemes to show an example of half reactions that are used to grow a hafnium silicon oxynitride film.

[0017] The present invention provides methods for preparing hafnium compounds used in a variety applications including high k dielectric materials. The methods use atomic layer deposition (ALD) to have elemental control of the composition of hafnium compounds. The elemental control is generally separated by half reactions.

[0018] Half reactions are abstractly demonstrated via the reaction:

[0019] wherein AB is the product compound and CD is the secondary compound or secondary product.

[0020] For example, a half reaction is demonstrated by each of the following steps:

[0021] (1) *NH₂(Et₂N)₄Hf*NHf(NEt₂)₂2HNEt₂

[0022] (2) *NHf(NEt₂)₂NH₃*NHfNH2HNEt₂,

[0023] wherein the half reaction of step 1 is initiated by the functional group NH₂ and * is an atom or molecule that is part of the substrate, film or surface group. The hafnium precursor reacts with the NH₂ group and forms a HfN bond. Ligands are protonated from the hafnium precursor to form a secondary product. During the half reaction in step 2, ammonia reacts with the hafnium complex bound to the surface. The remaining ligands are protonated and removed while another HfN bond and another functional group (NH) are formed as the product compound. In each half reaction of steps 1 and 2, diethyl amine (HNEt₂) can be made as a secondary compound. Other secondary compounds are amines and hydrazines and include radicals, ions and variations to ligands, such as Et₂N, (Et₂N)₂, EtNH and (EtNH)₂. Generally, these secondary compounds are readily removable, such as by vacuum and/or purge. The reaction schemes are not necessarily stoichiometric, but have a wide range of atomic ratios. Throughout the disclosure, reaction examples lack specific stoichiometry, bonding order and bonding connectivity of the product compounds and secondary compounds.

[0024] Another example of a half reaction is demonstrated by each of the following steps:

[0025] (3) *OH(Et₂N)₄Hf*OHf(NEt₂)_xHNEt₂

[0026] (4) *OHf(NEt₂)_xH₂O*OHf(OH)HNEt₂,

[0027] wherein the half reaction of step 3 is initiated by the functional OH group and forms a HfO bond. Step 4 proceeds to form another HfO bond as well as the terminus and functional OH group.

[0028] Therefore, in general, a first half reaction initiates with the reaction of a first functional group, establishes at least one product compound bond and establishes a second functional group. The second half reaction initiates with a reaction of the second functional group, establishes at least one product compound bond and establishes a third functional group. The third functional group, in many examples, is the same or similar to the first functional group. However, the second half reaction is still complete even when the third functional group is different. Examples with tertiary, quaternary and higher product compounds require half reactions with more than two precursors. Therefore, half reactions are not limited to only binary product compounds and may contain any number of half reactions. Most half reactions are sequentially separated by gas and/or vacuum purges.

[0029] Embodiments of the processes described herein deposit hafnium-containing materials on many substrates and surfaces. Substrates on which embodiments of the invention may be useful include, but are not limited to semiconductor wafers, such as crystalline silicon (e.g., Si<100> or Si<111>), silicon oxide, silicon germanium, doped or undoped polysilicon, doped or undoped silicon wafers silicon nitride and patterned or non-patterned wafers. Surfaces include bare silicon wafers, films, layers and materials with dielectric, conductive and barrier properties and include aluminum oxide and polysilicon. Pretreatment of surfaces includes polishing, etching, reduction, oxidation, hydroxylation, annealing and baking.

[0030] A substrate can be pretreated to be terminated with a variety of functional groups such as hydroxyls (OH), alkoxy (OR, where RMe, Et, Pr or Bu), haloxyls (OX, where XF, Cl, Br or 1), halides (F, Cl, Br or 1), oxygen radicals, aminos (NH or NH₂) and amidos (NR or NR₂, where RMe, Et, Pr or Bu). A pretreatment can be accomplished by administering a reagent, such as NH₃, B₂H₆, SiH₄, SiH₆, H₂O, HF, HCl, O₂, O₃, H₂O₂, H₂, atomic-H, atomic-N, atomic-O, alcohols or amines.

[0031] Once the surface of the substrate is pretreated, an ALD cycle is started. For many of the hafnium compounds, the hafnium precursor adsorption is self-limiting under certain process conditions, and generally must be at low temperatures (<500 C.) to exhibit this behavior. Some examples of half reactions that are self-limiting for the hafnium precursor include:

[0032] wherein, hafnium is added to produce either *OHf(NEt₂)_x or *NHf(NEt₂)_x. An atom, such as a nitrogen or oxygen, can anchor the hafnium atom to the substrate or surface. *Hf(NEt₂)_x is self-limiting because the hafnium precursor will not react further; therefore, this is the first half reaction. To proceed with other half reactions, either an oxygen source (e.g., water) or a nitrogen source (e.g., ammonia) is added.

[0033] The first half reaction with a hafnium precursor initiates a series of many half reactions to make binary, tertiary, quaternary and more complex compounds. The first half reaction does not have to include a hafnium precursor, but can include any precursor to which a particular element is incorporated into the film. The following examples will portray hafnium precursors as the first half reaction in order to more clearly explain aspects of the invention.

[0034] One embodiment of the invention is directed to a process which proceeds with the half reaction of NH₃ to *Hf(NEt₂)_x to produce *HfNH. Hafnium nitride is synthesized by sequentially proceeding with a half reaction of the hafnium precursor and a half reaction of a nitrogen source. FIG. 1 depicts a half reaction which is initiated by dosing (Et₂N)₄Hf from about 0.01 second to about 10 seconds, preferably about 0.25 second and dosing an inert gas purge from about 0.01 second to about 20 seconds, preferably about 0.25 second. A second half reaction is then initiated by dosing NH₃ from about 0.01 second to about 10 seconds, preferably about 0.25 second and dosing an inert gas purge from about 0.01 second to about 20 seconds, preferably about 0.25 second. The two half reactions are cycled several times to grow a hafnium nitride film at the rate of about 50 ng/cm² per cycle. By varying the cycle time, temperature, pressure and/or concentration, stoichiometry of the product compound is controlled. Slight variations of the stoichiometry can have an impact on the electrical properties, e.g., Hf₃N₄ is an insulating material while HfN is a conducting material. In one embodiment, HfN is made from a nitrate-free hafnium precursor. Hafnium nitride films can have oxygen contamination, since nitrates contain an oxygen/nitrogen ratio of three.

[0035] In one embodiment, a method for forming a semiconductor material by atomic layer deposition includes pulsing a hafnium precursor and a nitrogen precursor sequentially and cyclically. The hafnium nitride is deposited to the substrate surface wherein the hafnium nitride has a formula HfN_x and x is at least about 1.1 and less than about 1.3. In one aspect, the hafnium precursor is TDEAH and the nitrogen precursor is NH₃. In another aspect, the hafnium precursor is HfCl4 and the nitrogen precursor is a radical nitrogen, such as atomic nitrogen.

[0036] Another embodiment of the invention is directed to a process which proceeds with the half reaction of H₂O to *Hf(NEt₂)_x and produce *HfOH. Hafnium oxide is synthesized by sequentially proceeding with a half reaction of the hafnium precursor and a half reaction of an oxygen source. FIG. 2 depicts a half reaction which is initiated by dosing (Et₂N)₄Hf from about 0.01 second to about 10 seconds and an inert gas purge dosed for about 0.01 second to about 20 seconds. A second half reaction is then initiated by dosing H₂O from about 0.01 second to about 10 seconds and an inert gas purge from about 0.01 second to about 20 seconds. The two half reaction are cycled several times to grow a hafnium oxide film at the rate of about 1.2 per cycle.

[0037] The processes to grow the hafnium nitride or hafnium oxide films, as described above, can be modified to achieve other materials, namely tertiary compounds. Hafnium nitride is porous and reacts with water to form hafnium oxynitride, HfON. Therefore, to the hafnium nitride cycle, a half reaction of an oxygen source (e.g., water) is added to synthesize hafnium oxynitride. The ratio of Hf:O:N is controlled and varied to the desired characteristics of the product compound. In one embodiment, an oxygen precursor half reaction is included into the half reaction cycle. Such a cycle comprises a hafnium precursor half reaction, a nitrogen precursor half reaction, another hafnium precursor half reaction and an oxygen precursor half reaction. The oxygen precursor half reaction can be added into the cycle at any ratio relative to the hafnium and nitrogen precursor half reactions. As an example, an oxygen precursor half reaction is added at every ten complete cycles of hafnium and nitrogen precursor half reactions. Furthermore, the ratio can be varied in order to control the oxygen stoichiometry by film depth. Hence, a graded film is formed. In one embodiment, the process conditions are as follows, pressure is about 1 Torr, temperature is about 225 C., argon carrier flow is about 200 sccm, H₂O and NH₃ are dosed into the argon carrier flow in the range from about 1 second to about 4 seconds and TDEAH is dosed at about 20 seconds.

[0038] Graded films can be used to transition between various materials. One embodiment uses the method to transition between hafnium nitride and hafnium oxide. Within the hafnium nitride film, the elemental ratios N:Hf:O start out at 10:10:0, progress to 10:10:1, progress to 5:10:5, progress to 1:10:10 and finally 0:10:10, such that the film at the exposed surface following deposition is hafnium oxide. Graded films have advantageous characteristics, such as allowing control of electrical properties throughout the depth of the film, as well as higher levels of film adhesion.

[0039] Additional embodiments include methods to synthesize hafnium oxynitride. Due to the porosity of hafnium nitride, multiple layers are susceptible to oxygen enrichment. Instead of incorporating oxygen into each surface layer via half reactions, an excess oxygen precursor (e.g., water) is used to penetrate multiple layers of hafnium nitride and form a hafnium oxynitride graded film such as:

[0040] Therefore, hafnium nitride can be formed by ALD, CVD, PVD or other techniques and thereafter oxygenated with an oxygen precursor.

[0041] Other embodiments of the invention include methods to synthesize tertiary hafnium nitride compounds incorporating silicon. Preferred silicon precursor compounds include (Me₂N)₄Si and (Me₂N)₃SiH. In one embodiment, a silicon precursor half reaction is included into the half reaction cycle for hafnium nitride formation. The cycle includes a hafnium precursor half reaction, a nitrogen precursor half reaction, a silicon precursor half reaction and another nitrogen precursor half reaction. The silicon precursor half reaction is added into the cycle at any ratio relative to the hafnium and nitrogen precursor half reactions. As an example, a silicon precursor half reaction is added about at every two complete cycles of hafnium and nitrogen precursor half reactions. Furthermore, the ratio can be varied in order to control the ratio of the silicon incorporated by depth of the film. Similarly to hafnium oxynitride, the method enables control of the Hf:Si:N stoichiometry.

[0042] Other embodiments of the invention are methods to synthesize tertiary hafnium oxide compounds incorporating nitrogen. Similarly as discussed above, the method reverses to use of oxygen and nitrogen to synthesize hafnium oxynitride. In one embodiment, a nitrogen precursor half reaction is included into the half reaction cycle of hafnium oxide. The cycle comprises a hafnium precursor half reaction, an oxygen precursor half reaction, another hafnium precursor half reaction and a nitrogen precursor half reaction. The nitrogen precursor half reaction is added into the cycle at any ratio relative to the hafnium and oxygen precursor half reactions. As an example, a nitrogen precursor half reaction is added at every two complete cycles of hafnium and oxygen precursor half reactions. Furthermore, the ratio can be varied in order to control the ratio of the nitrogen incorporated by depth of the growing film.

[0043] Other embodiments of the invention include methods to synthesize tertiary hafnium oxide compounds incorporating silicon, namely hafnium silicate (HfSiO), as depicted in FIGS. 3A-3D. In one embodiment, a silicon source half reaction is included into the half reaction cycle of hafnium oxide. The cycle comprises a silicon precursor half reaction, an oxygen precursor half reaction, a hafnium precursor half reaction and another oxygen precursor half reaction. Purges occur between each half reaction. The silicon precursor half reaction can be added into the cycle at any ratio relative to the hafnium and oxygen precursor half reactions. As an example, a silicon precursor half reaction is added at every two complete cycles of hafnium and oxygen precursor half reactions. Furthermore, the ratio can be varied in order to control the ratio of the silicon incorporated by depth of the film.

[0044] Embodiments of the invention include multiple methods to synthesize quaternary compounds, especially hafnium silicon oxynitride (HfSiON), as depicted in FIGS. 4A-4D. Methods to synthesize two tertiary compounds (HfSiO and HfSiN) are modified to respectively nitridized or oxidized within the cycles to form the quaternary complex HfSiON. Half reactions of nitrogen, oxygen or silicon precursors are added at particular cycles, providing complete control to the N:O:Si ratios relative to hafnium.

[0045] In one embodiment, a nitrogen source half reaction is included into the half reaction cycle of hafnium silicate. Such a cycle comprises a silicon precursor half reaction, an oxygen precursor half reaction, a hafnium precursor half reaction and a nitrogen precursor half reaction. The nitrogen precursor half reaction can be added into the cycle at any ratio relative to the hafnium, silicon and oxygen precursor half reactions. As an example, a nitrogen precursor half reaction can be added at about every two complete cycles of hafnium, silicon and oxygen precursor half reactions. Furthermore, the cycle ratio can be varied in order to control the nitrogen ratio incorporated within film depth. Some embodiments grow hafnium silicon oxynitride graded films with higher concentrations of nitrogen near the top of the film.

[0046] In one aspect, the surface is terminated with a *SiOH group. The half reaction cycles are conducted with a hafnium precursor, a nitrogen precursor, a silicon precursor and an oxygen precursor, each separated with a purge. The respective precursors can be TDEAH, ammonia, Tris-DMAS and water. In another aspect, the respective precursors are HfCl₄, radical nitrogen, Si₂Cl₆ and O₃. The composition is controlled to form a semiconductor material, comprising HfSi_xO_yN_z, wherein x is at least about 0.2 and less than about 4, y is at least about 0.5 and less than about 4 and z is at least about 0.05 and less than about 2.

[0047] Embodiments of the invention include multiple methods to synthesize pentanary compounds, especially hafnium aluminum silicon oxynitride (HfAlSiON). Half reactions of hafnium, aluminum, nitrogen, oxygen and silicon precursors are added at particular cycles, providing complete control to the Al:N:O:Si ratios relative to hafnium. In one aspect of the process, one cycle of half reaction pulses will include, in the respective order, water, TDEAH, ammonia, Tris-DMAS, water and TMA. In another aspect of the process, one cycle of half reaction pulses will include, in the respective order, water, HfCl₄, ammonia, Tris-DMAS, water and TMA.

[0048] Therefore, any stoichiometry of the following compounds is made by methods of the process: HfO, HfN, HfON, HfSiO, HfSiN, HfSiON, HfAlO, HfAlN, HfAlON, HfSiAlO, HfSiAlN, HfSiAlON. Therefore, ALD provides stoichiometric control during the deposition of product compounds. The stoichiometry may be altered by various procedures following the deposition process, such as when Hf₃N₄ is thermally annealed to form HfN. Stoichiometry is also controlled by altering the precursor ratios during deposition.

[0049] Many industrial applications exist for the product compounds synthesized by the various embodiments of the invention. Within the microelectronics industry, the product compounds are used as high-k transistor gate dielectric materials, transistor gate interface engineering, high-k capacitor dielectric materials (DRAMs), seed layers, diffusion barrier layers, adhesion layers, insulator layers, conducting layers and functionalized surface groups for patterned surfaces (e.g., selective deposition). In the realm of microelectromechanical systems (MEMS), the materials formed by the claimed invention are used as insulating, conducting or structural films. The materials can also serve as functionalized surface groups to reduce stiction. Additional functionality of surface groups is used in gas or liquid chromatography, chemical sensors and active sites for chemical attachment, patterned surfaces (e.g., combinatorial chemistry). Silicon nitride is also used as a hardening coating on tools and within optical devices.

[0050] Many precursors are within the scope of the invention. One important precursor characteristic is to have a favorable vapor pressure. Precursors may be a plasma, gas, liquid or solid at ambient temperature and pressure. However, within the ALD chamber, precursors are volatilized. Organometallic compounds or complexes include any chemical containing a metal and at least one organic group, such as alkyls, alkoxyls, alkylamidos and anilides. Precursors comprise of organometallic and halide compounds.

[0051] Exemplary hafnium precursors include hafnium compounds containing ligands such as alkylamidos, cyclopentadienyls, halides, alkyls, alkoxides and combinations thereof. Alkylamido hafnium compounds used as hafnium precursors include (RRN)₄Hf, where R or R are independently hydrogen, methyl, ethyl, propyl or butyl. Specific hafnium precursors include: (Et₂N)₄Hf, (Me₂N)₄Hf, (EtMeN)₄Hf), (^tBuC₅H₄)₂HfCl₂, (C₅H₅)₂HfCl₂, (EtC₅H₄)₂HfCl₂, (Me₅C₅)₂HfCl₂, (Me₅C₅)HfCl₃, (ⁱPrC₅H₄)₂HfCl₂, (ⁱPrC₅H₄)HfCl₃, (^tBuC₅H₄)₂HfMe₂, (acac)₄Hf, (hfac)₄Hf, (tfac)₄Hf, (thd)₄Hf, Br₄Hf, Cl₄Hf, 1₄Hf, (NO₃)₄Hf, (^tBuO)₄Hf, (ⁱPrO)₄Hf, (EtO)₄Hf and (MeO)₄Hf.

[0052] Exemplary silicon precursors include: alkylamidosilanes (e.g, (Me₂N)₄Si, (Me₂N)₃SiH, (Me₂N)₂SiH₂, (Me₂N)SiH₃, (Et₂N)₄Si, (Et₂N)₃SiH), Si(NCO)₄, MeSi(NCO)₃, SiH₄, Si₂H₆, SiCl₄, Si₂Cl₆, MeSiCl₃, HSiCl₃, Me₂SiCl₂, H₂SiCl₂, silanols (e.g., MeSi(OH)₃, Me₂Si(OH)₂), (EtO)₄Si and various alkoxy silanes (e.g., (RO)_4-nSiL_n, where Rmethyl, ethyl, propyl and butyl and LH, OH, F, Cl, Br or I and mixtures thereof). Also, higher silanes are used as silicon precursors by processes of the invention. Higher silanes are disclosed in U.S. provisional patent application 60/419,426, 60/419,376 and 60/419,504, each filed on Oct. 18, 2002, assigned to Applied Material, Inc., and each entitled, Low temperature deposition with silicon compounds and are incorporated herein by reference in entirety for the purpose of describing silicon precursors.

[0053] Exemplary nitrogen precursors include: NH₃, N₂, hydrazines (e.g., N₂H₄ or MeN₂H₃), amines (e.g., Me₃N, Me₂NH or MeNH₂), anilines (e.g., C₆H₅NH₂), organic azides (e.g., MeN₃ or Me₃SiN₃), inorganic azides (e.g., NaN₃ or Cp₂CoN₃) and radical nitrogen compounds (e.g., N₃, N₂, N, NH or NH₂). Radical nitrogen compounds can be produced by heat, hot-wires and/or plasma.

[0054] Exemplary oxygen precursors include: H₂O, H₂O₂, O₃, O₂, NO, N₂O, NO₂, N₂O₅, alcohols (e.g., ROH, where RMe, Et, Pr and Bu), peroxides (organic and inorganic) carboxylic acids and radical oxygen compounds (e.g., O, O₂, O₃ and OH radicals). Radical oxygen compounds can be produced by heat, hot-wires and/or plasma.

[0055] Exemplary aluminum precursors include: aluminum alkyls such as: Me₃Al, Et₃Al, Pr₃Al, Bu₃Al, Me₂AlH, Et₂AlH, Me₂AlCl, Et₂AlCl, aluminum alkoxyls such as: (MeO)₃Al, (EtO)₃Al, (PrO)₃Al and (BuO)₃Al, aluminum dimmers, aluminum halides and aluminum hydrides.

[0056] The processes of the invention can be carried out in equipment known in the art of ALD. The apparatus brings the sources into contact with a heated substrate on which the films are grown. Hardware that can be used to deposit films is an ALD apparatus as disclosed in U.S. patent application Ser. No. 10/251,715, filed Sep. 20, 2002, assigned to Applied Material, Inc., Santa Clara, Calif. and entitled An Apparatus for the Deposition of High Dielectric Constant Films, and is incorporated herein by reference in entirety for the purpose of describing the apparatus. Carrier gases or purge gases include N₂, Ar, He, H₂, forming gas and mixtures thereof.

[0057] In one embodiment, hydrogen gas is applied as a carrier gas, purge and/or a reactant gas to reduce halogen contamination from the film. Precursors that contain halogen atoms (e.g., HfCl₄, SiCl₄ and Si₂Cl₆) readily contaminate the film. Hydrogen is a reductant and will produce hydrogen chloride as a volatile and removable by-product. Therefore, hydrogen is used as a carrier gas or reactant gas when combined with a precursor compound (i.e., hafnium, silicon, aluminum, oxygen or nitrogen precursors) and can include another carrier gas (e.g., Ar or N₂). In one aspect, a water/hydrogen mixture, at a temperature in the range from about 250 C. to about 650 C., is used to reduce the halogen concentration and increase the oxygen concentration of the film.

[0058] The present invention provides methods for preparing the following compounds. The subscripts (w, x, y, z) imply that stoichiometry is intentionally varied (i.e., compositionally controlled) via ALD dosing sequences to form the following product compounds:

hafnium aluminate:	HfAlxOy
hafnium oxide:	HfO2 and HfOx
hafnium nitride:	Hf3N4, HfN and HfNx
hafnium oxynitride:	HfOxNy
hafnium aluminum oxynitride:	HfAlxOyNz
hafnium silicate:	HfSiO4, Hf4SiO10, Hf3SiO8, Hf2SiO6,
	HfSiO2, HfxSiyO2(xy) and HfxSiyO
aluminum silicate:	Al6Si2O13 and AlxSiyO
hafnium aluminum silicate:	Hf2Al6Si4O21 and HfxAlySizO
hafnium silicon nitride:	HfxSiyN
hafnium silicon oxynitride:	Hf2Si2N2O5 and HfSixOyNz
aluminum silicon oxynitride:	AlSixOyNz
hafnium aluminum silicon	HfAlwSixOyNZ
oxynitride:

[0059] The list of product compounds is only partial and other materials are prepared with the methods of the invention. Other elements, such as carbon, titanium, tungsten, ruthenium, tantalum, zirconium, molybdenum, iridium, nickel, copper, tin, boron or phosphorus may be incorporated into the films as product compounds. Therefore, a product compound may comprise hafnium silicon oxynitride and carbon. Examples of half reactions are listed below. Note, that *surface species.

[0060] Reactivity of Precursors with Surface Hydroxyl Groups (OH)

[0061] Reactivity of Surface Products with H₂O_(g) to Regenerate Surface Hydroxyl (OH) Groups.

[0062] Reactivity of Surface Products with NH_3(g) to Generate Surface Amine (NH₂, NH) Groups.

[0063] Reactivity of Precursors with Surface Amine Groups (NH or NH₂)

[0064] Reactivity of Surface products with NH₃ to Regenerate Surface Amine Groups.

[0065] Reactivity of Surface Products With H₂O_(g) to Generate Surface Hydroxyl Groups.

[0066]

	TDEAH tetrakisdiethylamidohafnium	(Et2N)4Hf
	TDMAS tetrakisdimethlaminosilicon	(Me2N)4Si
	TrisDMAS trisdimethylaminosilicon	(Me2N)3SiH
	TMA trimethyl aluminum	Me3Al

[0067] The ALD processes are maintained in a temperature range from about 20 C. to about 650 C., preferably from about 150 C. to about 300 C., more preferably at about 225 C. Materials grown may be similar throughout a wider temperature range assuming that saturating ALD behavior is maintained. The ALD processes are conducted with a pressure in the range from about 0.1 Torr to about 100 Torr, preferably in the range from about 1 Torr to about 10 Torr. Materials grown may be similar from high vacuum to high pressures assuming saturating ALD behavior is maintained. The flow is maintained viscous to encourage reactant separation. Carrier gas (e.g., N₂) is maintained in the range from about 50 sccm to about 1,000 sccm, preferably at about 300 sccm with a speed of about 1 m/s. Higher speeds may create particle transport issues while lower speeds could allow particle formation due to inefficient purging, affecting electrical behavior of thin films. Films are deposited with thickness in the range from about 2 to about 1,000 , preferably, from about 5 to about 100 , and more preferably in the range from about 10 to about 50 .

[0068] In one example, a hafnium oxide film is grown by ALD in the presence of hydrogen gas. Hydrogen is used to reduce levels of halogen contaminates (e.g., F or Cl) within hafnium-containing films. Flow A, containing hafnium tetrachloride and at least one carrier gas (e.g., Ar, N₂ and H₂), is pulsed sequentially with Flow B, containing water, hydrogen and an optional carrier gas. Flows A and B are each pulsed for about 1 second and purge flows of argon are pulsed for about 1 second between each pulse of Flows A and B. The temperature is maintained in the range from about 250 C. to about 650 C.

[0069] In another example, a hafnium silicate film is grown by ALD in the presence of hydrogen gas. Flow A, containing hafnium tetrachloride and at least one carrier gas (e.g., Ar, N₂ and H₂), is pulsed sequentially with Flow B, containing water, hydrogen and an optional carrier gas and Flow C, containing Tris-DMAS and at least one carrier gas. Flows A, B and C are each pulsed for about 1 second and purge flows of argon are pulsed for about 1 second between each pulse of Flows A, B and C. The temperature is maintained in the range from about 450 C. to about 650 C.

[0070] In another example, a hafnium silicon oxynitride film is grown by ALD in the presence of hydrogen gas. Flow A, containing hafnium tetrachloride and at least one carrier gas (e.g., Ar, N₂ and H₂), is pulsed sequentially with Flow B, containing water, hydrogen and an optional carrier gas and Flow C, containing Tris-DMAS and at least one carrier gas and Flow D, containing a nitrogen plasma and an optional carrier gas. Flows A, B, C and D are each pulsed for about 1 second and purge flows of argon are pulsed for about 1 second between each pulse of Flows A, B, C and D. The temperature is maintained in the range from about 450 C. to about 650 C.

[0071] Materials are deposited by dosing chemicals separately in an alternating fashion to achieve the desired film composition or characteristics with selected half reactions. The above half reactions, however, do not dictate the exact bonding connectivity or the stoichiometry of the resulting film. Stoichiometry is largely controlled by thermodynamics; however, kinetically controlled films may be achieved. Thus, the dosing sequence may be modified to effect the overall composition and qualities of the film. The types of thin-film materials that can be grown with ALD half reactions generally are:

[0072] 1. Binary Materials: Repetitive cycles of reactants AB: e.g., Hf₃N₄

[0073] 2. Direct Alloys: Repetitive cycles of reactants ABCD: e.g., HfSiO₄

[0074] 3. Compositionally Controlled Alloys: Repetitive cycles of reactants y(AB)z(CD) (where either y or z1 and either z or y is >1, respectively): e.g., Hf_xSi_(2-x)O₄

[0075] 4. Compositionally Controlled Gradient Materials: Similar to 3, however, y or z is varied during deposition.

[0076] 5. Layered or laminate materials: Deposition of two different materials in discrete physical layers. Repetitive cycles of reactants y(ABCD)z(EF) (where y and z are typically 4): e.g., nanolaminates of hafnia and alumina

[0077] ALD of Hafnium Aluminates (Hf_XAl_YO)

[0078] Direct: 1 cycle(TDEAHH₂OTMAH₂O)

[0079] half reactions (s)4.035.034.085.08

[0080] Compositionally Controlled: 1 cyclen(TDEAHH₂O)m(TMAH₂O) where typically n is one and m is varied or m is one and n is varied.

[0081] half reactions (second) (e.g., n3, m1)4.035.034.075.074.075.074.085.08

[0082] Layered: 1 layerp(TDEAHH₂O)q(TMAH₂O) where p and q are typically 4 half reactions (second) (e.g., n4, m4)4.035.03(4.075.074.075.074.075.07)4.085.08(4.045.044.045.054.045.04)

[0083] ALD of Hafnium Nitrides (Hf₃N₄ or HfN)

[0084] Direct: 1 cycle(TDEAHNH₃).

[0085] half reactions (second)7.028.02

[0086] In this case, deposition at these temperatures may produce Hf₃N₄. Annealing to higher temperatures may produce HfN.

[0087] ALD of hafnium oxynitrides (HfO_xN_y)

[0088] Direct: 1 cycle(TDEAHH₂OTDEAHNH₃)

[0089] half reactions (second)7.029.024.076.07

[0090] Compositionally Controlled: 1 cyclen(TDEAHH₂O)m(TDEAHNH₃) where typically n is one and m is varied or m is one and n is varied.

[0091] Layered: 1 layerp(TDEAHH₂O)q(TDEAHNH₃) where p and q are typically 4

[0092] ALD of Hafnium Aluminum Oxynitrides (Hf_wAl_xO_yN_z)

[0093] Direct: 1 cycle(TDEAHNH₃TMAH₂O) hafnium oxynitride/alumina oxynitride alloy

[0094] Variations possible: 1 cycle(TDEAHNH₃TDEAHH₂OTMAH₂O)

[0095] Note: The different dosing sequence effects the bonding connectivity, especially when grown at lower temperatures <300 C. and without a higher-temperature anneal. In the top example, one might predict OHfNAlO connectivity. This may be thought of as a hafnium oxynitride/aluminum oxynitride alloy. In the bottom example, one might predict OHfNHfOAlO connectivity. This may be thought of as a hafnium oxynitride/alumina alloy.

[0096] ALD of Hafnium Silicates (HfSiO₄ and Hf_xSi_yO)

[0097] Direct: 1 cycle(TDEAHH₂OTrisDMASH₂O)HfSiO₄

[0098] Silica-rich hafnium silicates: 1 cycle(TDEAHH₂O)3(TrisDMASH₂O)Hf₂Si₅O₁₄

[0099] Compositional control (Hf:Si) from pure HfO₂ to silica-rich (>70%) hafnium silicates are possible.

[0100] ALD of Aluminum Silicate (Al₆Si₂₁₃ and Al_xSi_yO)

[0101] Direct: 1 cycle(TMAH₂OTrisDMASH₂O)Al₆Si₂O₁₃

[0102] Silica-rich aluminum silicates: 1 cycle(TMAH₂O)3(TrisDMASH₂O)Al₂Si₂O₇

[0103] Compositional control (Al:Si) from pure Al₂O₃ to silica-rich (>50%) aluminum silicates are possible.

[0104] ALD of Hafnium Aluminum Silicate (Hf₂Al₆Si₄O₂₁ and Hf_xAl_ySi_zO)

[0105] e.g., 1 cycle(TDEAHH₂OTrisDMASH₂OTMAH₂OTrisDMASH₂O)Hf₂Al₆Si₄O₂₁

[0106] ALD of Hafnium Silicon Nitride (HfSi_xO_yN_z)

[0107] Direct: 1 cycle(TDEAHNH₃TrisDMASNH₃)

[0108] ALD of Hafnium Silicon Oxynitride (HfSi_xO_yN_z)

[0109] e.g., (TDEAHH₂OTrisDMASNH₃)

[0110] e.g., (TDEAHNH₃TDEAHH₂OTrisDMASH₂OTrisDMASNH₃)

[0111] ALD of Aluminum Silicon Oxynitride (AlSi_xO_yN_z)

[0112] e.g., (TMAH₂OTrisDMASNH₃)

[0113] ALD of Hafnium Aluminum Silicon Oxynitride (HfAl_wSi_xO_yN_z)

[0114] e.g., (TDEAHNH₃TMAH₂OTrisDMASH₂O)

[0115] e.g., (TDEAHNH₃TDEAHH₂OTrisDMASNH₃TMAH₂O)

[0116] Continuous ALD of silica (SiO₂)

[0117] e.g., Direct: 1 cycleSi(NCO)₄H₂O

[0118] This process may allow laminate layers of pure SiO₂ or more easy control of Si concentration in mixed allows. Si(NCO)₄ is very reactive with HfOH* groups making silica incorporation easy (since TDEAH is reactive with SiOH*).

[0119] e.g., Consider several (TrisDMASH₂O) cycles with an occasional (TDEAHH₂O) or (TMAH₂O) cycle or (flash anneal>700 C.H₂O) to reform surface hydroxal groups to reinitiate growth.

[0120] Si₃N₄, (e.g. Non-Continuous Seed Layer or Capping Layer)

[0121] e.g., Direct: 1 cycle(TrisDMASNH₃)

[0122] Si_xO_yN, (e.g., Non-Continuous Seed Layer or Capping Layer)

[0123] e.g., Direct: 1 cycle(TrisDMASNH₃TrisDMASH₂O)

[0124] AlN

[0125] e.g., 1 cycle(TMANH₃)

[0126] Al_xSi_yN:

[0127] Al_xO_yN:

[0128] Hf_xAl_yN:

[0129] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.