Method for producing nanocomposite magnet using atomizing method

[0001] 1. Field of the Invention

[0002] The present invention relates to a method of making a nanocomposite magnet powder of an iron-based rare-earth alloy by an atomization process.

[0003] 2. Description of the Related Art

[0004] NdFeB based iron-based rare-earth magnet alloys are currently used extensively in sintered magnets and bonded magnets. These magnets are produced in different ways. More specifically, a sintered magnet is made by pulverizing a magnet alloy, obtained by an ingot casting process, a strip casting process or any other process, compacting the pulverized powder, and then sintering the powder compact. On the other hand, a bonded magnet is made by rapidly cooling and solidifying a molten alloy by a melt spinning process, for example, pulverizing the resultant rapidly solidified alloy into a powder, compounding the powder with a resin, and then molding the mixture into a desired shape. In this manner, no matter whether the magnet to be produced is a sintered magnet or a bonded magnet, its magnet powder is always obtained by pulverizing the material magnet alloy. That is to say, the manufacturing process of magnets normally includes a pulverizing process step as an indispensable process step.

[0005] However, there are some methods of making a magnet powder without performing such a pulverizing process step. A gas atomization process is one of such methods that are known in the art. In the gas atomization process, a melt of an alloy is sprayed through a nozzle, for example, into an inert gas, and is made to collide against the gas, thereby cooling the melt droplets. In this manner, spherical particles with particle sizes on the order of several tens of micrometers can be formed directly. In the gas atomization process, the droplets of the molten metal are solidified while being carried in the gas-flow, thus forming substantially spherical particles. The powder obtained by the gas atomization process (i.e., an atomized powder) has preferred shapes and particle sizes as a magnetic powder to make a bonded magnet.

[0006] If the atomization process is used to produce a bonded magnet, then the atomized powder can be used as it is as a magnet powder for a bonded magnet. Thus, no mechanical pulverizing process step is needed and the manufacturing cost can be reduced significantly. It should be noted, however, that the particle sizes of such an atomized powder are greater than those of a magnet powder to make a sintered magnet. Accordingly, it is difficult to use the atomized powder as it is as a magnet powder for a sintered magnet.

[0007] In a rapidly solidified rare-earth alloy magnet powder, which is currently used extensively to make a bonded magnet, an Nd₂Fe₁₄B based compound phase with a crystal grain size of about 20 nm to about 200 nm is finely dispersed in the powder particles. Such a nanocrystalline structure is formed by rapidly cooling a molten alloy with a particular composition by a melt spinning process, for example, to make an amorphous alloy thin strip and then thermally treating and crystallizing the amorphous alloy thin strip.

[0008] Meanwhile, high-performance magnets, having a quite different metal structure from that of the rapidly solidified magnet described above, are also under vigorous development. A typical example of those magnets is a composite magnet called a nanocomposite magnet (exchange spring magnet). The nanocomposite magnet has a metal structure in which hard and soft magnetic phases are finely dispersed and in which the respective constituent phases are magnetically coupled together through exchange interactions. The respective constituent phases of the nanocomposite magnet have nanometer-scale sizes and its nanocrystalline structure, defined by the sizes and dispersiveness of the respective constituent phases, has significant effects on its magnet performance.

[0009] Among those nanocomposite magnets, a magnet in which an Nd₂Fe₁₄B based compound phase (i.e., hard magnetic phase) and -Fe, iron-based boride and other soft magnetic phases are distributed in the same metal structure, attracts particularly much attention. In the prior art, such a nanocomposite magnet is also made by rapidly cooling a molten alloy by the melt spinning process and then thermally treating and crystallizing the rapidly solidified alloy. If the powder of such a rapidly solidified magnet could be made by the gas atomization process, then no other pulverizing process step would be needed and the manufacturing cost could be reduced significantly.

[0010] Actually, however, it is very difficult to make the rapidly solidified magnet powder by the atomization process. This is because the melt-quenching rate by the atomization process is lower than that by the melt spinning process by as much as one to two orders of magnitude. Thus, a sufficiently amorphized alloy structure cannot be formed by the conventional atomization process.

[0011] As for non-nanocomposite rapidly solidified magnets (i.e., rapidly solidified magnets including only the Nd₂Fe₁₄B based compound phase), a method of making an amorphous alloy producible even by the atomization process with such a low quenching rate by increasing the amorphous forming ability (i.e., quenchability) of the alloy with the addition of TiC, for example, was proposed.

[0012] However, as for an -Fe/R₂Fe₁₄B based nanocomposite magnet, it is difficult to produce an actually usable, high-performance magnet by the atomization process. The reason is that if the quenching rate is as low as in the atomization process, the soft magnetic -Fe phase easily nucleates and grows earlier than the R₂Fe₁₄B phase and increases its size so much that the exchange interactions among the respective constituent phases weaken and that the magnetic properties of the resultant nanocomposite magnet deteriorate significantly.

[0013] In order to overcome the problems described above, a primary object of the present invention is to make a powder of a nanocomposite magnet with excellent magnetic properties producible by the atomization process.

[0014] A nanocomposite magnet powder of an iron-based rare-earth alloy according to the present invention has a composition represented by the general formula: (Fe_1-mT_m)_100-x-y-zQ_xR_yTi_zM_n (where T is at least one element selected from the group consisting of Co and Ni; Q is at least one element selected from the group consisting of B and C; R is at least one element selected from the group consisting of the rare-earth metal elements and yttrium; and M is at least one element selected from the group consisting of Nb, Zr, Mo, Ta and Hf). The mole fractions x, y, z, m and n satisfy the inequalities of: 10 at %<x25 at %; 6 at %y<10 at %; 0.1 at %z12 at %; 0m0.5; and 0 at %n10 at %, respectively. The nanocomposite magnet powder includes at least two types of ferromagnetic crystalline phases, in which a hard magnetic phase has an average grain size of 10 nm to 200 nm and a soft magnetic phase has an average grain size of 1 nm to 100 nm.

[0015] In one preferred embodiment, an R₂Fe₁₄B type compound phase, a boride phase and an -Fe phase are present in the same metal structure.

[0016] In another preferred embodiment, the -Fe and boride phases have an average crystal grain size of 1 nm to 50 nm, which is smaller than the average crystal grain size of the R₂Fe₁₄B type compound phase, and are present on a grain boundary or sub-boundary of the R₂Fe₁₄B type compound phase.

[0017] In another preferred embodiment, the boride phase includes a ferromagnetic iron-based boride.

[0018] In another preferred embodiment, the iron-based boride includes Fe₃B and/or Fe₂₃B₆.

[0019] In another preferred embodiment, the magnet powder has a mean particle size of 1 m to 100 m.

[0020] In another preferred embodiment, the magnet powder exhibits hard magnetic properties including a coercivity H_cJ480 kA/m and a remanence B_r0.6 T.

[0021] A bonded magnet according to the present invention includes any of the iron-based rare-earth alloy nanocomposite magnet powders described above.

[0022] An inventive method of making an iron-based rare-earth alloy nanocomposite magnet powder includes the step of obtaining a rare-earth alloy magnet powder by rapidly cooling a melt of an alloy by an atomization process. The alloy has a composition represented by the general formula: (Fe_1-mT_m)_100-x-y-zQ_xR_yTi_zM_n (where T is at least one element selected from the group consisting of Co and Ni; Q is at least one element selected from the group consisting of B and C; R is at least one element selected from the group consisting of the rare-earth metal elements and yttrium; and M is at least one element selected from the group consisting of Nb, Zr, Mo, Ta and Hf). The mole fractions x, y, z, m and n satisfy the inequalities of: 10 at %<x25 at %, 6 at %y<10 at %, 0.1 at %z12 at %, 0m0.5, and 0 at %n10 at %, respectively. The method further includes the step of thermally treating the magnet powder, thereby forming a structure that includes at least two types of ferromagnetic crystalline phases, in which a hard magnetic phase has an average grain size of 10 nm to 200 nm and a soft magnetic phase has an average grain size of 1 nm to 100 nm.

[0023] In one preferred embodiment, the step of rapidly cooling the melt by the atomization process results in making a rapidly solidified alloy including at least 60 vol % of R₂Fe₁₄B type compound phase.

[0024] In another preferred embodiment, the soft magnetic phase includes a ferromagnetic iron-based boride.

[0025] In another preferred embodiment, the iron-based boride includes Fe₃B and/or Fe₂₃B₆.

[0026] In a preferred embodiment, an inventive method for producing a bonded magnet includes the steps of: preparing a magnet powder by any of the methods described above; and processing the magnet powder into the bonded magnet.

[0027] FIG. 1(a) is a view showing the configuration of a gas atomization system for use in an embodiment of the present invention, and FIG. 1(b) is a perspective view illustrating a gas nozzle for use in this system.

[0028] FIG. 2 is a graph showing a demagnetization curve (i.e., the second quadrant of a hysteresis curve) for an example of the present invention.

[0029] According to the present invention, an iron-based rare-earth alloy nanocomposite magnet powder is obtained by rapidly cooling a melt of an alloy, having a composition represented by the general formula: (Fe_1-mT_m)_100-x-y-zQ_xR_yTi_zM_n by an atomization process.

[0030] In this general formula, T is at least one element selected from the group consisting of Co and Ni, Q is at least one element selected from the group consisting of B and C, R is at least one element selected from the group consisting of the rare-earth metal elements and yttrium, and M is at least one element selected from the group consisting of Nb, Zr, Mo, Ta and Hf. The mole fractions x, y, z, m and n satisfy the inequalities of: 10 at %<x25 at %, 6 at %y<10 at %, 0.1 at %z12 at %, 0m0.5, and 0 at %n10 at %, respectively.

[0031] A 2-14-1 type hard magnetic compound, represented by the general formula R₂(Fe_1-mT_m)₁₄Q, will be simply referred to herein as an R₂Fe₁₄B based compound (or R₂Fe₁₄B phase). That is to say, the R₂Fe₁₄B based compound or the R₂Fe₁₄B phase includes an R₂Fe₁₄B compound or phase in which a portion of Fe is replaced with Co and/or Ni or in which a portion of B is replaced with C. It should be noted that the R₂Fe₁₄B based compound may further include additive elements such as Ti and M.

[0032] The present inventors carried out extensive researches to make a nanocomposite magnet by an atomization process. As a result, the present inventors discovered that the nucleation and growth of the -Fe phase while the melt was rapidly quenched could be minimized by adding Ti to the material alloy. The present inventors acquired the basic idea of the present invention from this discovery.

[0033] According to the present invention, even at the relatively low quenching rate achievable by the atomization process, the R₂Fe₁₄B phase as a main phase can be nucleated earlier than the -Fe phase and yet the size of the R₂Fe₁₄B phase is not allowed to reach such a size as to produce multiple magnetic domains in the R₂Fe₁₄B phase (i.e., 300 nm). As a result, a magnet powder exhibiting excellent magnetic properties as a nanocomposite magnet can be obtained.

[0034] An -Fe/R₂Fe₁₄B based nanocomposite magnet to which the present invention is applied has a higher coercivity than an Fe₃B/Nd₂Fe₁₄B based nanocomposite magnet. However, the former nanocomposite magnet has a relatively low B mole fraction of about 7 at % to about 10 at % and a relatively high Nd mole fraction of about 10 at % to about 12 at %. Thus, its alloy has very low ability to from amorphous phases. Accordingly, if the atomization process is applied without adding any Ti thereto, then just a powder in which the soft magnetic -Fe phase has grown coarsely can be obtained and the magnetic properties thereof are insufficient. On the other hand, the Fe₃B/Nd₂Fe₁₄B based nanocomposite magnet has a relatively high B mole fraction of about 18 at % to about 20 at % and has high ability to form amorphous phases. However, the magnet has a relatively low Nd mole fraction of about 3 at % to about 5 at % and exhibits low coercivity. Also, if the Fe₃B/Nd₂Fe₁₄B based nanocomposite magnet is produced by the atomization process, powder particles with a relatively fine structure and amorphous phases can be obtained due to its high amorphous forming ability. Nevertheless, if the magnet is thermally treated and crystallized after that, the magnet itself generates some heat due to the crystallization and its crystal growth advances non-uniformly. Thus, the resultant nanocomposite magnet cannot exhibit high magnet performance.

[0035] As used herein, the Fe₃B includes Fe_3.5B which is hard to distinguish from Fe₃B.

[0036] According to the present invention, by defining the mole fractions of Ti and other elements within appropriate ranges, a nanocomposite magnet powder with a nanocrystalline structure (i.e., a structure including at least 60 vol % of Nd₂Fe₁₄B phase) can be obtained even by the atomization process. Thus, the heat treatment process for crystallization does not have to be carried out after that. However, to increase the uniformity of the alloy structure and further improve the magnet performance, the crystalline atomized powder is preferably thermally treated.

[0037] The structure of magnet powder particles according to the present invention includes at least two ferromagnetic crystalline phases, of which the hard magnetic phase has an average size of 10 nm to 200 nm and the soft magnetic phase has an average size of 1 nm to 100 nm. More particularly, the R₂Fe₁₄B based compound phase exhibiting hard magnetic properties is uniformly dispersed in the alloy and the soft magnetic boride and -Fe phases are present on the grain boundary or sub-boundary thereof. The average crystal grain size of the -Fe and boride phases is smaller than that of the R₂Fe₁₄B based compound phase, and is typically 1 nm to 50 nm. In a preferred embodiment, iron-based borides (such as Fe₃B and/or Fe₂₃B₆) with ferromagnetic properties nucleate as the boride phases and high magnetization can be maintained.

[0038] As the present inventors disclosed in Japanese Patent Application No. 2001-144076, the boride phase (i.e., iron-based boride) is believed to be present at least partially as a film on the grain boundary of the R₂Fe₁₄B based compound crystalline phase. When such a texture structure is obtained, the magnetic coupling (i.e., exchange interactions) between the ferromagnetic boride phase and the main phase further consolidates and the magnetization of the ferromagnetic boride phase is firmly maintained. As a result, even higher coercivity is believed to be achieved.

[0039] The magnet powder of the present invention having such a texture structure can be used effectively to make a bonded magnet. In making a bonded magnet, the magnet powder preferably has a mean particle size of 1 m to 100 m as measured by a scanning electron microscope.

[0040] To make a permanent magnet powder by an atomization process from a molten alloy having the composition described above, a gas atomization process, a centrifugal atomization process, a rotational electrode process, a vacuum process, an impact process or any other suitable process may be adopted. When the centrifugal atomization process or the rotational electrode process is adopted, the quenching rate is preferably increased by blowing a gas at a high pressure.

[0041] Hereinafter, an embodiment that adopts a gas atomization process will be described with reference to FIGS. 1(a) and 1(b).

[0042] FIG. 1(a) shows an exemplary configuration for a gas atomization system to be preferably used in this embodiment. The system shown in FIG. 1(a) includes: a melting vessel 2 to melt an alloy by a high frequency heating or resistance heating process and store the resultant molten alloy 1 therein; and a spray chamber 4 in which a magnet powder (or atomized powder) 3 is formed by a gas atomization process. The melting chamber, in which the melting vessel 2 is provided, and the spray chamber 4 are preferably filled with an inert atmosphere (of argon or helium).

[0043] At the bottom of the melting vessel 2, a melt nozzle (with a nozzle orifice diameter of 0.5 mm to 3.0 mm) 5 is provided such that the molten alloy 1 is ejected through the melt nozzle 5 into the spray chamber 2. A ringlike gas nozzle 6 such as that shown in FIG. 1(b) is provided under the melt nozzle 5. A cooling gas is ejected strongly toward the center of the ring through a plurality of holes of this ringlike gas nozzle 6. As a result, a great number of small droplets of the molten alloy are formed and rapidly quenched while being deprived of the heat by the surrounding gas. Then the rapidly quenched and solidified metal droplets are collected as the magnet powder 3 at the bottom of the gas atomization system.

[0044] When such a gas atomization system is used, the particle size distribution of the powder can be controlled by adjusting the viscosity of the molten alloy and the energy of the spray gas.

[0045] It should be noted that when a molten alloy having a poor ability to form amorphous phases is rapidly quenched and solidified by a gas atomization process, powder particles with an amorphous or nanocrystalline structure cannot be obtained unless the atomization process is carried out under such conditions as to form powder particles with particle sizes of 20 m or less, for example. This is because the smaller the particle sizes of the powder particles to be obtained, the greater the ratio of the surface area to the volume of the respective particles and the higher the cooling effects. In the prior art, the greater the particle size, the lower the quenching rate of inside portions of particles. As a result, a crystal structure with an excessively large size is formed and the resultant magnet performance deteriorates. When such a phenomenon occurs, the magnet performance deteriorates significantly in a nanocomposite magnet powder, in particular.

[0046] In contrast, according to the present invention, even if the powder particle sizes are as large as 20 m to 100 m, the inside portions of the powder particles can also be rapidly quenched uniformly and at a sufficiently high rate. Thus, a nanocomposite magnet powder exhibiting excellent magnetic properties can be obtained.

[0047] Thereafter, the magnet powder, obtained by using the gas atomization system described above, is preferably thermally treated within an inert atmosphere of argon (Ar), for example. The temperature increase rate of the heat treatment process is preferably 0.08 C./s to 15 C./s. Specifically, the magnet powder is preferably maintained at a temperature of 500 C. to 800 C. for a period of time of 30 seconds to 60 minutes, and then cooled to room temperature. By carrying out this heat treatment process, an almost completely crystalline structure can be obtained even if some amorphous phases are left in the powder particles as a result of the gas atomization process.

[0048] The heat treatment atmosphere is preferably an inert gas such as Ar gas or N₂ gas to minimize the oxidation of the alloy. Alternatively, the heat treatment may also be carried out within a vacuum of 1.3 kPa or less.

[0049] It should be noted that if carbon is added to the material alloy, the oxidation resistance of the magnet powder can be increased. If a sufficient amount of carbon has been added to the material alloy, then the atomized powder may be heat-treated in the air. Also, the magnet powder of this embodiment already has a spherical shape when crystallized by the atomization process, and is not subjected to any mechanical pulverization process thereafter. Accordingly, the surface area of the powder per unit mass is far smaller than that of a known mechanically pulverized powder. Thus, the magnet powder is not oxidizable so easily even when exposed to the air during the heat treatment process or any other process.

[0050] In making a bonded magnet from this magnet powder, the magnet powder is compounded with an epoxy resin or a nylon resin and then molded into a desired shape. In this case, a magnet powder of any other type (e.g., a rapidly solidified alloy type magnet powder other than nanocomposite magnets, an SmTN based magnet powder and/or hard ferrite magnet powder) may be mixed with the magnet powder of the present invention.

[0051] Q is either B (boron) only or a combination of B and C (carbon). If the mole fraction x of Q is 10 at % or less, then the amorphous forming ability will be too low to obtain the desired nanocrystalline structure easily at a normal quenching rate (of about 10² C./s to about 10⁴ C./s) for a gas atomization process. On the other hand, if the mole fraction x of Q exceeds 25 at %, then the percentage of the -Fe phase, which has a higher saturation magnetization than any other constituent phase, decreases excessively and the remanence B_r drops. In view of these considerations, the mole fraction x of Q is preferably adjusted such that 10 at %<x25 at %. A more preferable x range is 10 at %<x20 at % and an even more preferable x range is 13 at %x18 at %.

[0052] C decreases the size of the metal structure in the rapidly solidified alloy, and therefore, plays an important role when the melt quenching rate is as low as in the gas atomization process. Also, by adding C, the nucleation of TiB₂ is minimized, thus decreasing the solidification start temperature of the molten alloy. As a result, the teeming temperature can be lowered. In that case, the alloy can be melted in a shorter time, and the quenching rate can be increased. However, if the atomic ratio of C to the total amount of Q exceeds 0.5, then the -Fe will be produced noticeably, the constituent phases will change, and the magnetic properties will deteriorate. This is why the atomic ratio of C to the total amount of Q is preferably 0.01 to 0.5. A more preferable range is 0.05 to 0.3 and an even more preferable range is 0.08 to 0.20.

[0053] R is at least one element selected from the group consisting of the rare-earth elements and yttrium. R is an indispensable element for R₂Fe₁₄B, which is a hard magnetic phase that cannot be omitted to achieve permanent magnet properties. Specifically, R preferably includes Pr or Nd as an indispensable element, a portion of which may be replaced with Dy and/or Tb. If the mole fraction y of R is less than 6 at %, then the compound phase having the R₂Fe₁₄B type crystal structure, which contribute to expressing coercivity, do not crystallize sufficiently and a coercivity H_cJ of 480 kA/m or more cannot be obtained. On the other hand, if the mole fraction y of R is equal to or greater than 10 at %, then the percentages of the iron-based borides and -Fe with ferromagnetic properties both decrease. For these reasons, the mole fraction y of the rare-earth element R is preferably 6 at %y<10 at %. A more preferable range for R is 7 at %y9 at %, and an even more preferable range for R is 7.5 at %y8.5 at %.

[0054] Ti is an indispensable element for a nanocomposite magnet according to the present invention. By adding Ti, high hard magnetic properties are achieved, and the loop squareness of the demagnetization curve is improved. As a result, the maximum energy product (BH)_max can also be increased.

[0055] Unless Ti is added, the -Fe easily nucleates and grows before the R₂Fe₁₄B phase nucleates and grows. Accordingly, when the atomized alloy is thermally treated and crystallized, the soft magnetic -Fe phase will have grown excessively.

[0056] In contrast, if Ti is added, the nucleation and growth kinetics of the -Fe phase is slowed down, i.e., it would take a longer time for the -Fe phase to nucleate and grow. Thus, the present inventors believe that the R₂Fe₁₄B phase starts to nucleate and grow before the -Fe phase has nucleated and grown. Thus, the R₂Fe₁₄B phase can be grown sufficiently and distributed uniformly before the -Fe phase has grown too much.

[0057] Also, Ti has a strong affinity for B and is easily condensed in an iron-based boride. Thus, the present inventors believe that Ti stabilizes an iron-based boride by producing a strong bond to B in the iron-based boride.

[0058] Furthermore, by adding Ti, the viscosity of the molten alloy decreases to 510⁶ m²/s or less. As a result, a preferred melt viscosity for the atomization process is obtained.

[0059] If the mole fraction of Ti exceeds 12 at %, then the production of the -Fe is reduced significantly, thus decreasing the remanence Br unintentionally. On the other hand, if the mole fraction of Ti is lower than 0.1 at %, then the R₂Fe₁₄B phase, which cannot be omitted to express the coercivity, will not crystallize sufficiently. Also, even if the R₂Fe₁₄B phase has crystallized sufficiently, the desired uniform nanocrystalline structure cannot be obtained, either, and high coercivity cannot be achieved. In view of these considerations, a preferable z range is 0.1 at %z12 at %, and a more preferable z range is 1 at %z7 at %.

[0060] The element M is an element that increases the amorphous forming ability of the alloy. If M is added, the amorphous forming ability of the alloy increases and the growth of the crystalline phases can be minimized while the molten alloy is being quenched. And a magnet with good loop squareness in its demagnetization curve can be obtained as a result of the subsequent heat treatment process. In addition, by adding M, the intrinsic coercivity can also be increased.

[0061] If the mole fraction of M exceeds 10 at %, then the grain growth of the respective constituent phases advances remarkably in a relatively high temperature range in which the -Fe phase grows rapidly, the exchange coupling among the respective constituent phases weakens, and the loop squareness of the demagnetization curve decreases significantly. For that reason, the mole fraction n of the element M preferably satisfies 0 at %n10 at %. A more preferable n range is 0.5 at %n8 at % and an even more preferable n range is 1 at %n6 at %. It should be noted that Al, Si, Mn, Cu, Ga, Ag, Pt, Au and/or Pb, as well as M, may also be added as an element that reduces the size of the metal structure.

[0062] The balance of the material alloy, other than the elements described above, may be Fe alone. Alternatively, at least one transition metal element T, selected from the group consisting of Co and Ni, may be substituted for a portion of Fe, because the desired hard magnetic properties are achievable in that case also. However, if the percentage m of Fe replaced with T exceeds 50%, then a high remanence Br cannot be obtained. For that reason, the percentage m of Fe replaced is preferably 50% or less (i.e., 0m0.5). A more preferable highest allowable replacement percentage m is 40%. Also, by substituting Co for a portion of Fe, the hard magnetic properties improve and the Curie temperature of the R₂Fe₁₄B phase increases, thus increasing the thermal resistance.

[0063] To make a permanent magnet powder by an atomization process from a molten alloy having the composition described above, a gas atomization process, a centrifugal atomization process, a rotational electrode process, a vacuum process, an impact process or any other suitable process may be adopted.

[0064] If a gas atomization process is adopted, the melt may be sprayed into the inert gas through a nozzle with a nozzle orifice diameter of 0.5 mm to 3.0 mm. In this case, the melt may be sprayed on a high-velocity inert gas flow. This gas may have a pressure of 0.1 MPa to 7 MPa, for example. According to the gas atomization method, the particle size distribution of the powder can be controlled by adjusting the viscosity of the molten alloy and the energy of the spray gas.

[0065] When a molten alloy having a poor ability to form amorphous phases is rapidly quenched and solidified by a gas atomization process, powder particles with an amorphous or nanocrystalline structure cannot be obtained unless the atomization process is carried out under such conditions as to form powder particles with particle sizes of 20 m or less, for example. This is because the smaller the particle sizes of the powder particles to be obtained, the greater the ratio of the surface area to the volume of the respective particles and the higher the cooling effects. In the prior art, the greater the particle size, the lower the quenching rate of inside portions of particles. As a result, a crystal structure with an excessively large size is formed and the resultant magnet performance deteriorates. When such a phenomenon occurs, the magnet performance deteriorates significantly in a nanocomposite magnet powder, in particular.

[0066] In contrast, according to the present invention, even if the powder particle sizes are as large as 20 m to 100 m, the inside portions of the powder particles can also be rapidly quenched uniformly and at a sufficiently high rate. Thus, a nanocomposite magnet powder exhibiting excellent magnetic properties can be obtained.

[0067] For each of Samples Nos. 1 through 4 having the compositions shown in the following Table 1, respective materials thereof. Nd, Pr, Fe, Co, B, C, Ti, Nb, Zr, Si and Cu having purities of 99.5% or more were weighed so that the mixture had a total weight of 1 kg (kilogram). The mixture was subjected to a gas atomization process under the following conditions, thereby making a powder with a mean particle size of about 50 m. Thereafter, the powder particles were classified to obtain a powder with particle sizes of 63 m or less.

[0068] Gas used: argon (Ar);

[0069] Gas pressure: 40 kgf/cm² (3.92 MPa);

[0070] Spraying temperature: 1,400 C.; and

[0071] Melt feeding rate: 2.0 kg/min.

	TABLE 1
		Heat
		Treat-
		ment
	Alloy	Temp-
	composition (at %)	erature
	No.	R	T	Q	Ti	M	Other	( C.)
E	1	Nd9	Fe as	B12.6	3	Nb1		740
X			balance	C1.4
A	2	Nd7.4	Fe as	B11	3	Nb1	Si0.5	720
M			balance	C2
P	3	Nd7.6	Co5	B12.5	4	Nb0.3	Cu0.2	740
L			Fe as	C2.5		Zr0.1
E			balance
S	4	Nd8.4	Fe as	B12	1	Zr2.6		720
		Pr0.5	balance	C1

[0072] In Table 1, Nd7.8Pr0.6 included in the column R indicates that 7.8 at % of Nd and 0.6 at % of Pr were added, and B12C1 included in the column Q indicates that 12 at % of B (boron) and 1 at % of C (carbon) were added.

[0073] Next, this atomized powder was heated to, and maintained at, any of the heat treatment temperatures shown in Table 1 for five minutes within an Ar gas atmosphere and then cooled to room temperature. The magnetic properties of the thermally treated atomized powder were measured with a vibrating sample magnetometer (VSM). The results obtained from powders with particle sizes of 25 m or less are shown in the following Table 2 and the demagnetization curve of the thermally treated atomized powder is shown in FIG. 1.

	TABLE 2
	EXAMPLES	Br (T)	HcJ (kA/m)	(BH)max (kJ/m3)
	1	0.74	901	81.2
	2	0.79	605	84
	3	0.77	629	79.6
	4	0.70	933	75.8

[0074] As can be seen, a nanocomposite magnet powder exhibiting hard magnetic properties including a coercivity H_cJ480 kA/m and a remanence B_r0.6 T can be obtained according to this example.

[0075] According to the present invention, even though an atomization process, which results in a lower quenching rate than a melt spinning process or any other rapid quenching process, is adopted, the R₂Fe₁₄B phase can be nucleated earlier than the -Fe phase by optimizing the alloy composition and adding Ti thereto. As a result, a magnet powder with a nanocrystalline structure that can exhibit excellent magnetic properties as a nanocomposite magnet can be obtained. In addition, according to the present invention, spherical particles for an alloy magnet can be directly produced by the atomization process. Thus, no pulverizing process step is needed, and the manufacturing cost of magnets can be reduced significantly.